Patent Application
20120171429
This invention relates to molded magnesium oxychloride composite products, moldable magnesium oxychloride composite materials for manufacture of the molded products, and methods of producing the molded products.
Decorative products are one of the ancient and elaborately artistic manifestations. Materials such as wood, rock, wrought iron, steel and silver are most conventional materials used for the production of decorative products. However, processing said conventional materials to produce decorative products with intricate carvings, inlayed works and embossed shape is time consuming and requires skillful labors. To tackle the problem, instead of using said conventional materials to produce decorative products, moldable materials, including ordinary Portland cement, plastics and polyresins, are used to produce decorative products nowadays.
However, there are also shortcomings for these moldable materials. Ordinary Portland cement, hereinafter referred to as OPC, is not a good choice for small to medium products that involve intricate carvings, inlayed works and embossed shape. Patterns such as wood grains are very difficult to be made by using OPC. Furthermore, decorative products produced by OPC are comparatively heavy. Plastics and polyresins are the most popular moldable materials which can be molded into different product shapes and textures. Moreover, both plastics and polyresins are comparatively lighter than said conventional materials. However, the production of plastics and polyresins involves the use of organic solvents which would pollute the environment. The residual organic solvents in decorative products may even be hazardous to human health. Furthermore, the combustibility and fire toxicant emission of plastics and polyresins on encountering fire make plastics and polyresins not the good choices for being the raw materials of decorative products.
In light of the foregoing background, it is an object of the present invention to provide an alternate material for production of decorative molded products.
According to a first aspect of the present invention, a moldable material is disclosed comprising a mixture of calcined magnesium oxide, magnesium chloride, phosphoric acid, sodium dihydrogenphosphate, calcium silicate, iron II sulphate, tributyl phosphate, activated silicon oxides, and fiber. In one exemplary embodiment, the moldable material has no internal voids with an enhanced fluidity property of a slump test value of at least 120 mm. In another exemplary embodiment, the fiber is E class glass fiber, plastic fibers, vegetal fibers, or a combination thereof; the silicon oxide is coal fly ash. In yet another exemplary embodiment, the composition of the moldable material is described in Table 1.
In yet another aspect, the moldable material described in paragraph [0005] is obtained by mixing the components of calcined magnesium oxide, magnesium chloride hexahydrate, water, phosphoric acid, sodium dihydrogenphosphate monohydrate, calcium silicate, iron II sulphate heptahydrate, tributyl phosphate, activated silicon oxides, polycarboxylate, and fiber at vacuum condition. In an exemplary embodiment, the composition of the moldable material is described in Table 1.
A moldable material is disclosed in another aspect of the present invention which comprises a mixture of calcined magnesium oxide, magnesium chloride, phosphoric acid, sodium dihydrogenphosphate, calcium silicate, iron II sulphate, tributyl phosphate, activated silicon oxides, fiber, polymethylhydrogensiloxane-polydimethylsiloxane and polycarboxylate. In an exemplary embodiment, the moldable material has an enhanced fluidity property with a slump test value of at least 160 mm. In another exemplary embodiment, the fiber is E class glass fiber, plastic fibers, vegetal fibers, or a combination thereof; the silicon oxide is coal fly ash. In yet another exemplary embodiment, the composition of the moldable material is described in Table 3.
In yet another aspect, the moldable material described in paragraph [0007] is obtained by mixing the components of calcined magnesium oxide, magnesium chloride hexahydrate, water, phosphoric acid, sodium dihydrogenphosphate monohydrate, calcium silicate, iron II sulphate heptahydrate, tributyl phosphate, polymethylhydrogensiloxane-polydimethylsiloxane mixture, activated silicon oxides, polycarboxylate, and fiber at vacuum condition. In an exemplary embodiment, the composition of the moldable material is described in Table 3.
In yet another aspect of the present invention, a moldable material comprising a mixture of calcined magnesium oxide, magnesium chloride, sodium dihydrogenphosphate, calcium silicate, iron II sulphate, activated silicon oxides, fiber, and a foaming agent is disclosed. In one exemplary embodiment, the moldable material has an ability to expand the volume thereof by at least 50% and to decrease the density thereof by at least 25% and within a range of 0.8-1.5 kg/L.
In another exemplary embodiment, the fiber is E class glass fiber, plastic fibers, vegetal fibers, or a combination thereof; the silicon oxides is coal fly ash; the foaming agent is an inorganic foaming agent selected from a group consisting of hydrogen peroxide, aluminum powder, and sodium bicarbonate.
In yet another exemplary embodiment, the moldable material is obtained by a process comprising mixing the components of calcined magnesium oxide, magnesium chloride hexahydrate, water, phosphoric acid, sodium dihydrogenphosphate monohydrate, calcium silicate, iron II sulphate heptahydrate, activated silicon oxides, fiber, and foaming agent at atmospheric condition. In an exemplary embodiment, the composition of the moldable material is described in Table 2.
In a further aspect of the present invention, a paste shaping tool is disclosed in which it is used for minimizing the width of seam lines of molded products using at least two mold parts, comprising a panel with at least one hole having a contour matching the contour of the parting line of each of the two mold parts. In one exemplary embodiment, the width of the seam lines is less than 2 mm.
A molded product is disclosed in another aspect of the present invention, comprising seam lines of less than 2 mm after curing, a plurality of rigid shells comprising compacted fiber reinforced magnesium oxychloride composite, and at least a core. In one exemplary embodiment, the density of the core is selected for achieving a predetermined weight of the product.
In a further exemplary embodiment, the compacted fiber reinforced magnesium oxychloride comprises crystalline phase of 5Mg(OH)2.MgCl2.8H2O compacted at vacuum condition and stabilized by tributyl phosphate and calcium silicate; the seam lines are foamed fiber reinforced magnesium oxychloride composite; and the core is wood, stones, metals, paper , gas, or foamed fiber reinforced magnesium oxychloride composite.
In another exemplary embodiment, the rigid shells further comprise intricate carvings, inlayed works and embossed shape. The dimensions of said intricate carvings, inlayed works and embossed shape can be as small as 2 mm. In yet another exemplary embodiment, the molded product is incombustible according to ASTM E136, is free of volatile organic compound emission according to ASTM D5116 and is good to resist weathering according to ASTM C666 and ASTM G154.
In one exemplary embodiment, the molded product is able to absorb carbon dioxide from the atmosphere through the carbonation of said rigid shells. In yet another exemplary embodiment, at least one core is a porous core and seam lines provide a pathway for carbon dioxide in the atmosphere to reach the high surface area of said porous core; the porous core absorbs carbon dioxide at a faster rate than said rigid shells.
According to another aspect of the present invention, a method of producing a molded product is disclosed which comprises the steps of: (a) vacuuming a first paste of the moldable material described in any one of the embodiments in paragraph [0005]; (b) casting the vacuumed first paste onto a female mold of a mold assembly; (c) casting the vacuumed first paste onto a male mold of the mold assembly; (d) mixing a second paste of the moldable material described in any one of the embodiments in paragraph [0009]; (e) casting the second paste onto the first paste casted on the female mold obtained from step (b); (f) assembling the male mold obtained from step (c) and the female mold obtained from step (e); (g) allowing the second paste to expand and squeeze out from a gap between the assembled male and female molds; and (h) curing the first paste and the second paste inside the assembled male and female molds obtained from step (g) to from the molded product.
In an exemplary embodiment, the method further comprises the steps of: (i) clearing the excess second paste squeezed out from said gap of step (g) on the mixed paste; (j) demolding to obtain the molded product; (k) fixing surface defects on the molded product obtained from step (j); and (l) providing painting onto the molded product obtained from step (k) to yield desired surface finishing effects.
A method for producing a molded product is disclosed in a further aspect of this invention, comprising the steps of: (a) casting a first paste onto a core; (b) applying a fiber mat onto the casted first paste; (c) casting a second paste onto the casted first paste and the fiber mat to form a casted core; (d) assembling the mold parts around the casted core; (e) vacuuming a third paste; (f) filling the remaining cavity of the assembled mold obtained from step (d) with the third paste obtained from step (e) to form a filled assembled mold; (g) vacuuming the filled assembled mold; (h) curing and setting the filled assembled mold at atmospheric condition; and (i) demolding the filled assembled mold to form the molded product.
In an exemplary embodiment, the first paste is the moldable material as described in any one of the embodiments in paragraph [0005] or paragraph [0007]; the second paste is the moldable material as described in any one of the embodiments in paragraph [0005] or paragraph [0007]; the third paste is the moldable material as described in any one of the embodiments in paragraph [0005] or paragraph [0007].
In another aspect of this invention, a method for producing a molded product is provided comprising the steps of: (a) assembling the paste shaping tool as described in paragraph [0012]; (b) casting a first paste onto the assembled first mold part; (c) applying a fiber mat onto the casted first paste obtained from step (b); (d) casting a second paste onto the casted first paste obtained from step (c); (e) removing the paste shaping tool from the assembled first mold part to form a casted first mold part; (f) assembling the paste shaping tool as described in paragraph [0012] and a second mold part, wherein said second mold part is adapted to couple with said first mold part; (g) casting the first paste onto the assembled second mold part; (h) applying a fiber mat onto the casted first paste obtained from step (g); (i) casting the second paste onto the casted first paste obtained from step (h) to form a casted second mold part; (j) assembling the casted first mold part obtained from step (e) and the casted second mold part obtained from step (i); (k) curing and setting the filled assembled mold obtained from step (j) at atmospheric condition; and demolding the filled assembled mold to form the molded product.
In one exemplary embodiment, the first paste is the moldable material as described in any one of the embodiments in paragraph [0005] or paragraph [0007]; the second paste is the moldable material as described in any one of the embodiments in paragraph [0005] or paragraph [0007]. In yet another exemplary embodiment, the first paste and/or said second paste is vacuumed.
A preferred embodiment of the present invention will now be described, by way of an example only, in conjunction with the accompanying figures wherein like reference numerals designate like parts throughout, in which:
a-1b shows a mold for making a decorative molded product, as is a minor frame as illustrated, according to a preferred embodiment of the present invention;
a-3i are graphical illustrations of the utilization of a mold in a production method of decorative molded products according to a preferred embodiment of the present invention;
a-4c illustrate a production method of an ornamental molded product according to a preferred embodiment of the present invention; and
a-5h show a method for minimizing the width of seam lines of decorative products by using a paste shaping tool according to a preferred embodiment of the present invention.
As used herein and in the claims, “comprising” means including the following elements but not excluding others.
The terms “molded product”, “molded magnesium oxychloride composite product”, “decorative products”, or “decorative molded products” used herein and in the claims mean including interior home decorative products, garden ornaments, building decorative products and the like.
Any chemical as used herein and in the claims is interpreted as any specific hydrate form thereof. As such, any hydrate form or even the anhydrous form of such chemical should also be considered to be included therein. The term “hydrate” referred herein and in the claims includes water molecule(s) either bound to or crystallized with the chemical associated therewith. For example, “sodium dihydrogenphosphate” should be interpreted to include the anhydrous sodium dihydrogenphosphate, sodium dihydrogenphosphate monohydrate, or any other hydrate forms thereof.
The term “vacuuming” or “vacuumed” used herein and in the claims bears the meaning of treating or mixing the specified object at vacuum conditions.
The term “seam line(s)” of a molded product as used herein and in the claims refer to the “scar” remains on the molded products where the mold parts join during the assembling of the mold parts.
As afore-described, the present invention uses fiber reinforced magnesium oxychlorides as main components to produce decorative products with intricate carvings, inlayed works and embossed shape by using molding technique.
Magnesium oxychloride (MOC) is a type of hydraulic cement produced by mixing powdered magnesium oxide with a solution of magnesium chloride. If the ratio of magnesium oxide and magnesium chloride is within a certain range of ratios, when cured, MOC comprises mainly crystalline phase of 5Mg(OH)2.MgCl2.8H2O (hereinafter referred to as F-5 MOC). Having a high content of F-5 MOC, MOC possesses high fire resistance, low thermal conductivity, good abrasion resistance and good organic solvent resistance. In addition, MOC is environmental friendly as it requires comparatively lower energy in the production process than ordinary Portland cement, and F-5 MOC can absorb carbon dioxide in the atmosphere through carbonation according to Maravelaki-Kalaitzaki and Moraitou 1999.
A number of inventions have previously disclosed the application of MOC in different aspects. For example, Chinese Patent No. 1126708A discloses a production method for producing fire-proof board using MOC as one of the main ingredients. The MOC used in this patent comprises magnesium oxide, magnesium chloride, urea formaldehyde and vegetal fiber. The MOC is pressed to form a board structure with fiber glass mat by using a roller press machine. Chinese Patent No. 1099366A also discloses the use of MOC paste to produce composite board with the property of fire-proofing. The MOC used in this patent comprises magnesium oxide, magnesium chloride, activated silicon dioxide, vegetal fiber and a mixture of organic glue and ionic salts. The MOC paste is pressed to form a compressed board structure using a cold press machine.
In addition, Chinese Patent Publication Nos. 101429001A, 101016214A, 201086437Y, 101538141A, 101429801A, 101148062A, 101148064A, 101565294A, 101423349A, 101492279A, 101492278A, U.S. Patent Nos. 5004505, 5110361, 3963849, 4772654, and PCT International Publication No. 2009141325A1 disclose different formulations and production methods of MOC composites. Each of these publications uses formulations of MOC with single set of selected properties to produce the targeting products.
The utilization of MOC to produce decorative products with intricate carvings, inlayed works and embossed shape has not been disclosed in aforementioned publications.
Further, Chinese Patent Publication No. 200958257Y discloses a composite board that comprises two selected formulations of MOC cement with different densities so as to lower the weight of the products and keep the surface of the products with enough strength.
However, the utilization of two selected formulations of MOC cement with different densities to produce decorative products that requires the assembly of molds has not been disclosed in this publication.
To ensure a high content of F-5 MOC, the tuning of the ratio of raw materials of MOC is essential and has been previously disclosed. For instance, U.S. Pat. No. 7,658,795B2 discloses ways to produce MOC with at least 80% F-5 MOC by tuning the ratio and species of the raw materials. However, despite the right composition, the production method also plays a key role in achieving MOC with a stable structure. MOCs are often casted onto the molds in random motion by hand casting and spray casting. Hand casting is a method to apply the moldable materials onto the molds by brushing the moldable materials onto the molds. Spray casting is a method to apply the moldable materials onto the molds by spraying the moldable materials. Chinese Patent Number 1111709A discloses a method to produce composite door by coating a layer of MOC paste onto a wooden door frame by hand casting. Chinese Patent Number 1252377A discloses a method to produce cover of a well by pouring MOC paste into a steel framework. Further, Chinese Patent Number 1900006A discloses the production method of a colored composite material by casting of MOC paste and coupling agent solution alternatively using hand casting method.
Unlike hand casting and spray casting, pressing is a way to cast MOC paste for the purpose of producing better structured MOC. For example, Chinese Patent Numbers 1126708A, 1099366A and 1468753A utilize presses to form a composite material. However, press casting is not an efficient method to eliminate the possible gas bubbles and voids inside the MOC paste.
Vacuum casting and low-pressure filling are used in metal and resins casting in which vacuum casting eliminates turbulence, increases density, repeatability, tolerances, and grain uniformity. Moreover, as the feedstock is drawn from below to the top of the pool, the feedstock is free from dross and slag. The pressure differential helps the feedstock to flow into every intricacy of the mold. However, the application of vacuum casting on the casting of MOC paste has not been found because, conventionally, vacuum casting of MOC induces several technical problems and unfavorable product qualities. Some of the technical problems include the relative low fluidity of common MOC pastes, the technical difficulties in handling the mortar that contains certain amount of fiber, aggregates and sands and the deferred setting time of vacuum treated high-fluidity MOC pastes. Examples of unfavorable product qualities are high mass and low dimensional strength. As the feedstock is fed into the mold cavity by suction in a vacuum condition, products that produced by vacuum casting are always associated with high mass. Furthermore, there is no way to apply fiber mat under vacuum condition for conventional vacuum casting process. Thus, the strength and dimensional stability of the products are worse than that produced by hand casting and spray casting.
To the best knowledge of the inventors of the instant invention, the molds are always pre-assembled prior to the injection of moldable materials. The moldable materials are then injected into the mold cavity through a port; thus, the products will have a scar at the port location. In order to make light product, blow molding or spin molding has to be used. However, due to the long setting time of OPC and MOC pastes, blow molding and spin molding are impossible for OPC and MOC. As a result, decorative products made from OPC and MOC are seldom hollow. The current hollow products available in the market comprise obvious seam lines at the location where different pieces of mold assemble.
Summarizing the existing art, treating MOC paste under vacuum to generate compacted fiber reinforced MOC products as described in this invention has not been previously disclosed. The decorative products as described in this invention and resulted from this production method possess all the afore-discussed advantages that conventional MOC products may lack. Furthermore, none of the existing art has described methods to minimize the width of seam lines on the final products.
The present invention is directed to a category of novel decorative products characterized in having rigid shells of compacted fiber reinforced magnesium oxychloride composite, seam lines of less than two millimeters and cores in which densities thereof can be adjustable. In one embodiment, the density of the core is adjusted according to the preferred weight of the products during the product design stage. The afore-said compacted fiber reinforced magnesium oxychloride composite is characterized in comprising compacted structures of F-5 MOC phase magnesium oxychloride. With the rigid shell, the novel decorative products are non-combustible, volatile emission free, heavy metal leaching free, mold and insect resistant, and carbon dioxide absorbing.
a-1b show a mold for making minor frames as an example of the decorative product according to one embodiment of the instant invention. Said mold comprises a male mold (101) made from conventional molding material, including silicon rubber, polyurethane, resins and polyvinylchloride, preferably a rigid mold using polyresins. Said male mold (101) is also preferred to be a plate-like structure. Said male mold (101) is supported by a backing frame (102) which prevents the male mold (101) from distortion and fixes the position of said male mold (101) by providing a male hole (103) for any means to adjust and fix the position of male mold (101) when assembling with a female mold (105). Said male mold (101) also comprises fixing positions (104) for immersing the fixing fittings of the mirror frame. The female mold (105) comprises complicated intricate carvings (106), inlayed works (107) and embossed shape (108). Molding material including silicon rubber, polyurethane, resins and polyvinylchloride, can be used for the female mold (105), while flexible and soft material like silicon rubber or polyurethane is preferred. As soft material is used as the building material of said female mold (105), it is essential to have a support (109) for the female mold (105). The female mold (105) also comprises an extended section (110) and a female hole (111) corresponding to the male hole (103) on the male mold (101) is provided thereon. Unlike conventional molds, after assembling of the male mold (101) and female mold (105), the gap in between the male mold and the female molds are intended to be larger than 0.2 millimeters and smaller than 2 millimeters, preferably around 0.5 millimeters, in the current mold design as shown in
Another selected formulation of fiber reinforced MOC paste (MOC2) is prepared and mixed at atmospheric condition for 10-15 minutes. In one exemplary embodiment, the composition of said MOC2 is listed in Table 2 below. Hydrogen peroxide or aluminium powder is introduced to the pastes to provide the self-expanding property of MOC2. In one preferred embodiment, MOC2 is characterized in having an ability to expand its volume by at least 1.5 times, and the resulting density decreases about 25 percent without any external force exerted thereon within two hours after the mixing process. The extent of reduction of density can be adjusted within the range of 0.8-1.5 kilograms per liter by altering the dosage of hydrogen peroxide or aluminium powder in another preferred embodiment. The said expansion stops within three hours after the mixing process in one preferred embodiment. MOC2 is casted on top of the casted MOC1 paste of the female mold (105) and fills up at least 75 percent of the remaining cavity of the female mold (105) after said mixing at the atmospheric condition. Prior to the complete expansion of MOC2, the male mold (101) and female mold (105) are assembled. The positions of the male mold (101) and female mold (105) can be adjusted accordingly during the mold assembling period. Excess MOC pastes, including excess MOC1 and MOC2 pastes, are cleaned up by scraping after the assembly of male mold and female mold and prior to the curing process. The pastes are then allowed to cure at atmospheric condition. During the curing process, the self-expanding paste (i.e MOC2) expands and escapes the mold cavity through the gaps between the male mold (101) and the female mold (105). After final setting of both said selected formulation of MOC pastes, the expanded paste forms foamed MOC with density of at least 75% of the non-foamed paste. The excess foamed MOC paste which squeezed out from the mold cavity is scraped. The paste squeezed from the gap is foamed MOC and the foamed MOC paste forms seam lines of 0.2-2 millimeters; thus, it is easy to be scrapped. Finally, any surface deflects identified after demolding of the mirror frame is fixed and the fixed minor frame is painted according to the preferred surface finishing.
a-3i demonstrates the utilization of a segment (301) of the male mold (101) (not shown in
As the mirror frame, an example of the decorative product of the present invention, possesses rigid shells which are formed by vacuum treatment of a selected MOC paste, the shells of the mirror frame possess high strength and the ability to prevent water and chemical penetrations that would otherwise deteriorate the quality of the mirror frame. In addition, it is found that the rate of carbonation of the vacuum treated MOC paste is slower than that of MOC paste with the same formulation which is mixed under atmospheric condition. The reason would be related to the elimination of air, and thus the carbon dioxide, from the MOC paste in the vacuum mixing process and the compacted phase structure formed during the vacuum treatment of the MOC pastes. The gas permeable parting lines allow the air from the atmosphere to reach the porous core, thus providing high surface area for the carbon dioxide absorbing MOC to absorb carbon dioxide through carbonation. As said porous core made of MOC paste does not contribute much to the strength of the mirror frame, said carbonation of the porous core does not pose any durability problem to the mirror frame. Furthermore, because of the properties of non-combustibility in accordance with ASTM E136, free of volatile organic compound emission in accordance with ASTM D5116, free of heavy metal leaching and resistance of mold and insect of the selected formulations of MOC, the minor frame possesses environmentally friendly, safe and durable features.
a-4c illustrate a production method of an ornamental molded product, such as a garden ornament, as another example of the decorative product of the instant invention according to one embodiment of the present invention. This production method is carried out by casting the moldable material into the mold by vacuum casting, as contrasted to the hand or spray casting process employed in the production method described above. The core of garden ornament (401) is manufactured prior to the casting of moldable materials. The density of the said core (401) can be selected according to the preferred final product weight; for example, a stainless steel core can be used if a heavy final product weight is preferred; in contrast, a hollow paper box can be used if light final product weight is preferred. One of the choices of said core (401) is cured MOC2 as afore-described. As said core (401) does not comprise intricate carvings, inlayed works and embossed shape, using wood, stones, metals, paper or gas to make the core (401) is not time consuming and preferred in one embodiment of the instant invention. Products with gas core are conventionally referred to be hollow products. Said core (401) is characterized in having geometry similar to the final garden ornament. The core (401) is fixed to a bar (404) using screws (405, 406) and said bar (404) will then be fixed to the mold by screws (407, 408) after assembly of the mold parts. Thus, the core (401) is fixed onto the bar (404) at the position that, after assembly of mold parts, the core (401) will not be in contact with the mold and the clearance between the core (401) and the mold parts (402, 403) will be kept at above 5 millimeters. A selected formulation of fiber reinforced MOC paste (409) is casted on the core (401) by hand casting or spray casting prior to the assembly of the mold parts. Said fiber reinforced MOC can be MOC1 paste as afore-described in a preferred embodiment. With the said fiber reinforced MOC paste (409) casted onto the core (401), a fiber mat (410) can be applied on to the core (401). Another layer of said fiber reinforced MOC paste (411) is casted on to the casted MOC paste (409) and the fiber mat (410) thereon to ensure the fiber mat (410) is attached to the core (401). The mold parts (402, 403) are then assembled (408).
In a preferred embodiment of the instant invention, another selected formulation of the fiber reinforced MOC paste (MOC3) is first treated under vacuum. In one exemplary embodiment. the composition of said MOC3 is listed in Table 3 below. As MOC3 is intended to be used in vacuum casting, thus, the fluidity of said MOC3 should be good. With the utilization of high-activity calcined magnesium oxide and the addition of polycarboxylate, the fluidity of said MOC3 paste is larger than that of the conventional MOC paste. The slump test value of MOC3 should be above 160 mm. Said MOC3 is then filled into the remaining cavity (413) of the assembled mold (408) via the filling port (414) of the mold (408) at vacuum or atmospheric condition. The fully filled mold is then treated at low pressure or at vacuum prior to the final setting of MOC3 at atmospheric condition. Demolding time at atmospheric condition would be shorter than 8 hours. After demolding, screws (405, 406) are unscrewed, thus, leaving two holes in the products. Vacuum treated MOC3 can be used to fill the holes. When the MOC3 inside the said holes is cured, the final decorative product possesses a rigid shell of compacted F-5 MOC.
As the molds are assembled prior to the casting of moldable materials, seam lines of the products can be easily kept at less than 2 millimeters. With the incorporation of the core (401), the product weight can be controlled and the dimensional stability of the product can be ensured by the application of the fiber mat (410). The co-existence of tributyl phosphate and polymethylhydrogensiloxane-polydimethylsiloxane mixture in MOC3 enhances the weathering resistance, durability and the formation of compacted F-5 MOC; thus, said MOC3 is more suitable than other MOC for outdoor garden ornament.
a-5h shows a paste shaping method that can minimize the width of seam lines of the decorative products of the instant invention when hand casting or spray casting of moldable materials is used. A Buddha's head, as an example of the decorative product illustrated in
The invention is exemplified by the following, non-limiting, examples.
1.5 kilograms of MOC1 was mixed at vacuum condition. The resulting MOC1 paste was casted onto the female mold (101) and male mold (105) as shown in
The combustibility of the painted mirror frame was tested according to ASTM E136 and BS476 part 4 and the result showed that the minor frame was non-combustible. Said painted minor frame was also tested for the volatile organic compound emission according to the standard test method ASTM D5116 and it was found that the mirror frame is free of volatile organic compound emission. The durability of the mirror frame is tested according to ASTM G154 and it was found that the minor frame is of excellent durability under UV exposure. The in-house carbon dioxide absorption test was conducted by checking on the carbonation depth of the porous core and the rigid shell. The result showed that the depth of carbonation of the porous core was deeper than that of the rigid shell.
Conventionally, it is impossible to make a Buddha's head decoration of weight heavier than 10 kilograms using MOC paste and the mold shown in
The final weight of the finished Buddha's head decoration was around 10 kilograms. The combustibility of the Buddha's head was tested according to ASTM E136 and BS476 part 4 and the result showed that the Buddha's head decoration was non-combustible. Said Buddha's head decoration was also tested for the volatile organic compound emission according to the standard test method ASTM D5116 and it was found that the Buddha's head decoration is free of volatile organic compound emission. The durability of the Buddha's head decoration was tested according to ASTM G154, it was found that the Buddha's head decoration has even better durability than the mirror frame manufactured in Example 1. This should be due to the differences in the MOC formulations thereof. MOC3 formulation in the Buddha's head decoration comprises Polymethylhydrogensiloxane-Polydimethylsiloxane mixture which improves the stability and water resistance of the resulting MOC3 formulation, whereas MOC1 formulation in the minor flame lacks this ingredient and so it has a weaker stability and water resistance relative to the Buddha's head decoration.
Paste shaping tool (503) was used to minimize the seam lines of decorative products that are manufactured according to the process illustrated in
Different MOC pastes, namely MOC1 paste without the addition of calcium silicate and tributyl phosphate (P1), MOC1 paste without the addition of tributyl Phosphate (P2), MOC1 paste with ingredients and compositions as shown in Table 1 (P3), MOC2 paste with ingredients and compositions as shown in Table 2 (P4) and MOC3 paste with ingredients and compositions as shown in Table 3 (P5) were prepared. Part of the pastes P1, P3 and P4 were not treated at vacuum condition, while other pastes were all treated at vacuum condition. Then all pastes were used to make specimens for different tests. The test results of different cured MOC pastes are summarized in Table 4 below.
Water Resistance of the sample was assessed by first immersing the specimens into water in which the number of days at which the flexural strength of the specimens falls below 80% of its original value was recorded. Thus, the result of a larger number of days implies a better water resistance. The flexural strength of the samples was tested according to ASTM C947 which is a standard method (as set forth by the ASTM International) for testing the flexural properties of a material. The durability factor of the samples was tested according to ASTM C666 which is a standard method (as set forth by the ASTM International) for testing the freeze thaw resistance of materials. The durability of the specimens was tested according to ASTM G154 which is a method (as set forth by the ASTM International) for testing the UV and weathering resistances of materials.
As shown in the Table 4 above, vacuum treatment on MOC pastes increases the density of MOC pastes, and the addition of tributyl phosphate and polymethylhydrogensiloxane-polydimethylsiloxane mixture enlarges the extent of such density increment. Thus, vacuum treatment with the addition of tributyl phosphate and polymethylhydrogensiloxane-polydimethylsiloxane mixture made the MOC structure more compact.
Moreover, the addition of tributy phosphate and polymethylhydrogensiloxane-polydimethylsiloxane mixture improves the water resistance and weathering resistance of MOC paste. Such addition even leads to an enhanced improvement in these two properties as compared to the traditional improvement method of MOC, in which ionic phosphates and activated silicon oxide are used.
The addition of calcium silicate also showed a dramatic improvement on the product's strength, water resistance and durability. It was also found that the efflorescence can be greatly reduced by using calcium silicate as additive of MOC pastes.
It should also be understood that certain features of the invention, which are, for clarity, described in the context of separate embodiments, may be provided in combination in a single embodiment. Conversely, various features of the invention which are, for brevity, described in the context of a single embodiment, may also be provided separately or in any appropriate sub-combinations.
For example, a bar (404) as shown in
Also, steps for refinement of the final product, such as steps involving hole-filling described in the production method illustrated in
This application claims benefit under 35 U.S.C. §119(e) of U.S. Provisional Application having Ser. No. 61/428,220 filed Dec. 29, 2010, which is hereby incorporated by reference herein in its entirety.