Abstract

The present Application relates to pigment colorants of formula 1

Description

[0001] The present invention relates to novel pigment colourants, to their preparation and to their use in the mass-colouring of synthetic materials.

[0002] Pigment colourants and their use in the mass-colouring of synthetic materials are known. It has been found, however, that such colourants do not always fully meet the highest demands, especially in respect of fastness to light, thermostability and/or colour strength. Accordingly, there is a need for new pigment colourants which yield coloured materials that are fast to light, thermostable and of good tinctorial strength, and which exhibit good all-round properties.

[0003] Surprisingly, it has now been found that the pigment colourants according to the invention meet the above-mentioned criteria to a considerable degree.

[0004] Accordingly, the present invention relates to pigment colourants of formula 4

[0005] wherein

[0006] R1 is C1-C6alkyl, C1-C6alkoxy, phenoxy or halogen,

[0007] R2 is hydrogen, C1-C6alkyl, C1-C6alkoxy, phenoxy, halogen, acylamino, —CH2NHacyl or the radical 5

[0008] and

[0009] R3 is C1-C6alkyl, C1-C6alkoxy, phenoxy or halogen, the ring A may be further substituted by —SO3−M+, wherein M+is a cation, and the rings B and C may be unsubstituted or further mono- or poly-substituted by halogen, hydroxy, —SH, amino, C1-C6alkylamino, C1-C6alkyl, C1-C6alkoxy, phenoxy, acylamino, C1-C6thioalkyl or by thiophenyl, and the ring B may be substituted in the 5- or 8-position by a radical of formula 6

[0010] wherein R1, R2 and R3 are as defined above.

[0011] R1, R2 and R3 as C1-C6alkyl are, for example, methyl, ethyl, propyl, isopropyl, n-butyl, iso-butyl, sec-butyl, tert-butyl, amyl, tert-amyl (1,1-dimethylpropyl), 1,1,3,3-tetramethylbutyl, hexyl, 1-methylpentyl, neopentyl, cyclopentyl, cyclohexyl, as well as the associated isomers.

[0012] R1, R2 and R3 as C1-C4alkoxy are, for example, methoxy, ethoxy, propoxy or butoxy.

[0013] R1, R2 and R3 as halogen are, for example, chlorine, bromine or iodine, and preferably chlorine.

[0014] Acyl in acylamino or in the formula —CH2NHacyl is preferably formyl, acetyl, chloroacetyl, acryl or propionyl.

[0015] C1-C6Thioalkyl as a substituent of ring B and/or C is, for example, methylthio, ethylthio, propylthio or butylthio.

[0016] R1 is preferably ethyl or bromine, and especially methyl.

[0017] R2 is preferably hydrogen, ethyl, phenoxy, and especially methyl.

[0018] R3 is preferably ethyl or bromine, and especially methyl.

[0019] The cation M+ is, for example, Na+, Li+, K+, Ca2+, Mg2+, Sr2+, Al3+ or the cation of an organic amine such as, for example, ethylenediamine, diethylenetriamine, triethanolamine, tri-isopropanolamine, cyclohexylamine, hexamethylenediamine, Rosin Amine D and Primene 81R.

[0020] Preference is given to pigment colourants of formula (1) wherein the ring B is substituted by chlorine, and special preference is given to those wherein the ring B is unsubstituted or is substituted in the 5- or 8-position by a radical of formula 7

[0021] (2), wherein R1, R2 and R3 have the definitions and preferred meanings mentioned above.

[0022] Also preferred are pigment colourants of formula (1) wherein the ring C is unsubstituted or is substituted by bromine.

[0023] Special preference is given to the pigment colourants of formula (1) wherein the ring B is unsubstituted or is substituted in the 5- or 8-position by a radical of formula 8wherein R1, R2 and R3 are methyl, and the ring C is unsubstituted.

[0024] Very special preference is given to pigment colourants of formula (1) wherein the ring B is unsubstituted or is substituted in the 5-position by a radical of formula 9

[0025] wherein R1, R2 and R3 are methyl, and the ring C is unsubstituted.

[0026] The pigment colourants of formula (1) according to the invention are prepared, for example, by reacting 1-chloro-, 1-nitro- or 1-sulfo-anthraquinone with one equivalent of a compound of formula 10

[0027] wherein R1, R2 and R3 are as defined for formula (1), in the presence of alkali acetate, copper and/or a copper salt and optionally in an organic solvent, or by reacting 1,5- or 1,8-dichloro-, 1,5- or 1,8-dinitro- or 1,5- or 1,8-disulfo-anthraquinone with two equivalents of a compound of formula (2a) in the presence of alkali acetate, copper and/or a copper salt and optionally in an organic solvent, and, where appropriate, introducing further substituents into the resulting compound according to conventional methods.

[0028] The compounds of formula (2a) are known or can be prepared according to known methods.

[0029] The present invention relates also to a method of preparing coloured plastics or polymeric coloured particles, which method comprises mixing together a high molecular weight organic material and at least one pigment colourant of formula (1) in an amount having a colouring effect.

[0030] Colouring of high molecular weight organic substances with the pigment colourant of formula (1) is carried out, for example, by mixing such a pigment colourant with the substrates using rolling mills, mixing or grinding apparatuses, as a result of which the pigment colourant is dissolved or finely divided in the high molecular weight material. The high molecular weight material with the admixed pigment colourant is subsequently processed by methods known per se, for example calendering, compression moulding, extrusion, coating, spinning, casting or by injection moulding, whereby the coloured material acquires its final form. The admixture of the pigment colourant may also be carried out immediately prior to the actual processing step, for example by continuously feeding a solid pigment colourant, for example a pulverulent pigment colourant, and, at the same time, a granulated or powdered high molecular weight organic material, and optionally also additional ingredients, for example additives, directly into the intake zone of an extruder, where mixing takes place immediately before processing. In general, however, it is preferred to mix the pigment colourant with the high molecular weight organic material beforehand, since more uniformly coloured substrates can be obtained.

[0031] In order to produce mouldings that are not rigid or to reduce their brittleness, it is often desirable to incorporate so-called plasticisers into the high molecular weight compounds prior to shaping. There may be used as plasticisers, for example, esters of phosphoric acid, phthalic acid or sebacic acid. In the method according to the invention, the plasticisers may be incorporated into the polymers before or after the incorporation of the colourant. It is also possible, in order to achieve different colour shades, to add to the high molecular weight organic substances, in addition to the pigment colourant of formula (1), also further pigments or other colourants in any desired amounts, optionally together with further additional ingredients, for example fillers or siccatives.

[0032] Preference is given to the colouring of thermoplastic plastics especially in the form of fibres. Preferred high molecular weight organic materials that can be coloured according to the invention are, very generally, polymers having a dielectric constant ≧2.5, especially polyester, polycarbonate (PC), polystyrene (PS), polymethyl methacrylate (PMMA), polyamide, polyethylene, polypropylene, styrene/acrylonitrile (SAN) or acrylonitrile/butadiene/styrene (ABS). Special preference is given to polyester and polyamide. Very special preference is given to linear aromatic polyesters, which can be obtained by polycondensation of terephthalic acid and glycols, especially ethylene glycol, or condensation products of terephthalic acid and 1,4-bis(hydroxymethyl)cyclohexane, for example polyethylene terephthalate (PET) or polybutylene terephthalate (PBTP); also polycarbonates, for example those of α, α-dimethyl-4,4-dihydroxy-diphenylmethane and phosgene, or polymers based on polyvinyl chloride and on polyamide, for example polyamide 6 or polyamide 6.6.

[0033] The pigment colourants according to the invention impart to the above-mentioned materials, especially to the polyester and polyamide materials, tinctorially strong, level colour shades which have very good fastness properties in use, especially good fastness to light and good thermostability.

[0034] The Examples which follow serve to illustrate the invention. In the Examples, unless indicated to the contrary, parts are parts by weight and percentages are percentages by weight.

[0035] Temperatures are given in degrees Celsius. The relationship between parts by weight and parts by volume is the same as that between grams and cubic centimeters.

EXAMPLE 1

[0036] 12.1 parts by weight of 1-chloroanthraquinone are stirred together with 13.5 parts by weight of mesidine, 5.0 parts by weight of potassium acetate, 0.1 part by weight of copper and 0.1 part by weight of copper(I) chloride in 60.0 parts by weight of 1-pentanol for 6 hours at 130° C. The reaction mixture is cooled and the precipitated product is filtered off with suction and washed with a small amount of 1-pentanol, yielding 13.0 parts by weight of the colourant of formula 11

[0037] The colourant mass-colours polyester and polyamide in brilliant, lightfast red shades.

[0038] If in Example 1 the 13.5 parts by weight of mesidine are replaced by equivalent amounts of an amine indicated in column 3 of Table 1 and/or if the 12.1 parts by weight of 1-chloro-anthraquinone are replaced by equivalent amounts of an anthraquinone derivative indicated in column 2 of Table 1, colourants having good properties are likewise obtained.

TABLE 1
	Anthraquinone			Shade on
Ex.	derivative	Amine	Colourant	PES/PA
2	12	13	14	yellowish red
3	″	15	16	yellowish red
4	″	17	18	yellowish red
5	″	19	20	yellowish red
6	″	21	22	yellowish red
7	23	24	25	yellowish red
8	″	26	27	yellowish red
9	″	28	29	yellowish red
10	″	30	31	yellowish red
11	″	32	33	yellowish red

EXAMPLE 12

[0039] 12.1 parts by weight of 1 -chloroanthraquinone are stirred together with 12.0 parts by weight of 2,4-xylidine, 5.0 parts by weight of potassium acetate, 0.1 part by weight of copper and 0.1 part by weight of copper(I) chloride in 60.0 parts by weight of 1-pentanol for 6 hours at 130° C. The reaction mixture is cooled and the precipitated product is filtered off with suction and washed with a small amount of 1-pentanol, yielding 13.5 parts by weight of the compound of formula 34

[0040] 4.5 parts by weight of bromine are added to 8.2 parts by weight of the compound of formula (4) in 100.0 parts by weight of chlorobenzene at 35° C. Stirring is carried out for 12 hours at 35° C., the reaction product is filtered off with suction, and the residue is washed with a small amount of chlorobenzene, yielding 10.0 parts by weight of the colourant of formula 35

[0041] The colourant mass-colours polyester and polyamide in brilliant, lightfast red shades.

[0042] The products listed in Table 2 are prepared analogously to Example 12.

TABLE 2
	Anthraquinone			Shade on
Ex.	derivative	Amine	Colourant	PES/PA
13	36	37	38	yellowish red
14	39	40	41	yellowish red
15	″	42	43	yellowish red

EXAMPLE 16

[0043] 12.1 parts by weight of 1-chloroanthraquinone are stirred together with 10.7 parts by weight p-toluidine, 5.0 parts by weight of potassium acetate, 0.1 part by weight of copper and 0.1 part by weight of copper(I) chloride in 60.0 parts by weight of 1-pentanol for 6 hours at 130° C. The reaction mixture is cooled and the precipitated product is filtered off with suction and washed with a small amount of 1-pentanol, yielding 12.0 parts by weight of the compound of formula 44

[0044] 13.0 parts by weight of bromine are added to 7.8 parts by weight of the compound of formula (6) in 100.0 parts by weight of chiorobenzene at 35° C. Stirring is carried out for 12 hours at 35° C., the reaction product is filtered off with suction, and the residue is washed with a small amount of chiorobenzene, yielding 13.0 parts by weight of the colourant of formula 45

[0045] The colourant mass-colours polyester and polyamide in brilliant, lightfast red shades.

[0046] The products listed in Table 3 can be obtained analogously to Example 16.

TABLE 3
	Anthraquinone			Shade on
Ex.	derivative	Amine	Colourant	PES/PA
17	46	47	48	yellowish red
18	″	49	50	yellowish red
19	51	52	53	yellowish red
20	″	54	55	yellowish red
21	″	56	57	yellowish red

EXAMPLE 22

[0047] 13.9 parts by weight of 1,5-dichloroanthraquinone are stirred together with 21.0 parts by weight of mesidine, 10.0 parts by weight of potassium acetate, 0.2 part by weight of copper and 0.2 part by weight of copper(I) chloride in 100.0 parts by weight of o-dichlorobenzene for 6 hours at 170° C. The reaction mixture is cooled and the precipitated product is filtered off with suction and washed with a small amount of o-dichlorobenzene, yielding 19.0 parts by weight of the colourant of formula 58

[0048] The colourant mass-colours polyester and polyamide in brilliant, lightfast red shades.

[0049] If in Example 22 the 21.0 parts by weight of mesidine are replaced by equivalent amounts of an amine indicated in column 3 of Table 4 and/or if the 13.9 parts by weight of 1,5-dichloro-anthraquinone are replaced by equivalent amounts of an anthraquinone derivative indicated in column 2 of Table 4, colourants having good properties are likewise obtained.

TABLE 4
	Anthraquinone			Shade on
Ex.	derivative	Amine	Colourant	PES/PA
23	59	60	61	red
24	″	62	63	red
25	″	64	65	red
26	″	66	67	red
27	″	68	69	red
28	70	71	72	bluish red
30	″	73	74	bluish red
31	″	75	76	bluish red
32	″	77	78	bluish red
33	″	79	80	bluish red

EXAMPLE 34

[0050] 17.0 parts by weight of the compound according to Example 1 are dissolved in portions at 5-10° C. in 100% sulfuric acid. 7.0 parts by weight of N-hydroxymethylchloroacetamide are then added at 5-10° C. Stirring is carried out for 12 hours at 5-10° C., and the reaction mixture is poured onto ice. The precipitate is filtered off with suction, washed neutral with water and dried, yielding 23.0 parts by weight of the colourant of formula 81

[0051] The colourant mass-colours polyester and polyamide in brilliant, lightfast red shades.

EXAMPLE 35

[0052] If in Example 34 the 7.0 parts by weight of N-hydroxymethylchloroacetamide are replaced by 14.0 parts by weight of N-hydroxymethylchloroacetamide, 29.0 parts by weight of the colourant of formula 82

[0053] are obtained. The colourant mass-colours polyester and polyamide in brilliant, lightfast red shades.

EXAMPLE 36

[0054] If in Example 35 the 17.0 parts by weight of the compound according to Example 1 are replaced by 23.7 parts by weight of the compound according to Example 22, 35.0 parts by weight of the colourant of formula 83

[0055] are obtained. The colourant mass-colours polyester and polyamide in brilliant, lightfast red shades.

[0056] The colourants listed in Table 5 are obtained analogously to Example 36.

TABLE 5
	Anthraquinone	N-Hydroxymethyl		Shade on
Ex.	derivative	compound	Colourant	PES/PA
37	84	85	86	yellowish red
38	″	87	88	yellowish red
39	″	89	90	yellowish red
40	″	91	92	yellowish red
41	″	93	94	yellowish red
42	″	95	96	yellowish red
43	″	97	98	yellowish red
44	99	100	101	red
45	102	″	103	bluish red

EXAMPLE 46

[0057] 19.9 parts by weight of sodium thiophenolate are dissolved in 225.0 parts by weight of dimethylformamide (DMF) at 25° C.; 25.7 parts by weight of 1-amino-4-chloroanthraquinone are added thereto in portions. The mixture is stirred for 20 hours at 25° C. and diluted with water. The resulting reaction product is filtered off with suction, washed with a small amount of methanol and dried, yielding 30.0 parts by weight of the compound of formula 104

[0058] 16.5 parts by weight of the compound of formula (12) are boiled at reflux for 4 hours with 11.0 parts by weight of bromomesitylene, 2.5 parts by weight of sodium carbonate, 0.1 part by weight of copper and 0.1 part by weight of copper(I) chloride in 50.0 parts by weight of nitrobenzene. The reaction mixture is cooled and the nitrobenzene is distilled off with water vapour. The precipitated product is filtered off with suction and dried, yielding 24.0 parts by weight of the colourant of formula 105

[0059] The colourant mass-colours polyester and polyamide in lightfast, reddish blue shades.

[0060] The colourants listed in Table 6 are obtained analogously to Example 46.

TABLE 6
	Anthraquinone			Shade on
Ex.	derivative		Colourant	PES/PA
47	106	thiophenolate	107	reddish blue
48	108	1) thiophenolate 2) mesidine	109	reddish blue
49	110	1) thiophenolate 2) mesidine	111	blue

EXAMPLE 50

[0061] 4.8 parts by weight of the compound of Example 22 are dissolved in portions at 0-5° C. in 30.0 parts by weight of 5% oleum. The reaction mixture is stirred for 4 hours at 10° C. and poured into 200 parts by weight of ice. The precipitate is filtered off with suction, washed with water, made into a slurry in 100 parts by weight of water, neutralised with 1.5 parts by weight of hexamethylenediamine, and filtered off with suction again, yielding 6.6 parts by weight of the compound of formula 112

[0062] The colourant mass-colours polyamide in brilliant, lightfast red shades.

[0063] The colourants listed in Table 7 are obtained analogously to Example 50.

TABLE 7
	Anthraquinone		Shade on
Ex.	derivative	Colourant	PA
51	113	114	scarlet
52	115	116	bluish red

Colouring Example 1

[0064] 1200.00 g of polyester granules (PET Arnite D04-300, DSM) are pre-dried for 4 hours at 130° C. and then mixed homogeneously with 0.24 g of the pigment colourant of formula 117

[0065] in a “Roller rack” mixing apparatus for 15 minutes at 60 revolutions per minute. The homogeneous mixture is extruded in an extruder (twin screw 25 mm from Collin, D-85560 Ebersburg) having 6 heating zones at a maximum temperature of 275° C., cooled with water, granulated in a granulator (Turb Etuve TE 25 from MAPAG AG, CH-3001 Bern), and then dried for 4 hours at 130° C.

[0066] There are obtained red-coloured polyester granules having good all-round properties, especially very good light fastness and high temperature light fastness.

Colouring Example 2

[0067] 1200.00 g of polyamide 6 granules (Ultramid B3K, BASF) are pre-dried for 4 hours at 75° C. and then mixed homogeneously with 2.40 g of the pigment colourant of formula 118

[0068] in a “Roller rack” mixing apparatus for 15 minutes at 60 revolutions per minute. The homogeneous mixture is extruded in an extruder (twin screw 25 mm from Collin, D-85560 Ebersburg) having 6 heating zones at a maximum temperature of 220° C., cooled with water, granulated in a granulator (Turb Etuve TE 25 from MAPAG AG, CH-3001 Bern), and then dried for 4 hours at 75° C.

[0069] There are obtained violet-red-coloured polyamide granules having good all-round properties, especially very good light fastness and high temperature light fastness.

Claims

1. A pigment colourant of formula 119

2. A pigment colourant according to claim 1 of formula 122wherein R1 is C1-C6alkyl, C1-C6alkoxy, phenoxy or halogen, R2 is hydrogen, C1-C6alkyl, C1-C6alkoxy, phenoxy, halogen, acylamino, —CH2NHacyl or the radical 123and R3 is C1-C6alkyl, C1-C6alkoxy, phenoxy or halogen, and the rings B and C may be unsubstituted or further mono- or poly-substituted by halogen, hydroxy, —SH, amino, C1-C6-alkylamino, C1-C6alkyl, C1-C6alkoxy, phenoxy, acylamino, C1-C6thioalkyl or by thiophenyl, and the ring B may be substituted in the 5- or 8-position by a radical of formula 124 wherein R1, R2 and R3 are as defined above.

3. A pigment colourant according to either claim 1 or claim 2, wherein R1 is methyl, ethyl or bromine.

4. A pigment colourant according to either claim 1 or claim 2, wherein R2 is hydrogen, methyl, ethyl or phenoxy.

5. A pigment colourant according to either claim 1 or claim 2, wherein R3 is methyl, ethyl or bromine.

6. A pigment colourant according to either claim 1 or claim 2, wherein the ring B is unsubstituted or is substituted in the 5- or 8-position by a radical of formula 125wherein R1, R2 and R3 are methyl, and the ring C is unsubstituted.

7. A process for the preparation of a pigment colourant of formula (1) according to claim 1, which process comprises reacting 1-chloro-, 1-nitro- or 1-sulfo-anthraquinone with one equivalent of a compound of formula 126

8. A method of mass-colouring synthetic materials, which method comprises incorporating a pigment colourant of formula (1) into the substance of such materials.

9. The use of a pigment colourant of formula (1) according to claim 1 in the mass-colouring of synthetic materials.

10. A synthetic material coloured according to claim 8 with a pigment colourant of formula (1) according to claim 1.