Patent Application
20090247782
The present invention relates to a novel polymerizable compound useful as a synthetic intermediate for a polymerizable liquid crystal compound and the like.
It is possible to prepare a polymeric material in which the oriented structure of liquid crystal molecules is fixed, by first orienting, in the liquid crystal state, a liquid crystal compound having a polymerizable functional group (hereafter, may also be referred to as a “polymerizable liquid crystal compound”) or a liquid crystal composition containing at least one kind of the polymerizable liquid crystal composition (hereafter, may also be referred to as a “polymerizable liquid crystal composition”), and then irradiating the liquid crystal compound or the liquid crystal composition with an active energy ray such as ultraviolet light. The polymeric material thus obtained has anisotropies in physical properties such as a refractive index, a dielectric constant, magnetic susceptibility, an elastic modulus, a coefficient of thermal expansion and others, and thus may be used as an optical anisotropic material such as a retardation plate, a polarizing plate, a polarizing prism, a brightness improvement film, a low-pass filter, various light filters, a coating material for an optical fiber, and the like. With regard to the optical anisotropic material (polymer) obtained by polymerization, there are other important characteristics than anisotropies, including the rate of polymerization, transparency of the polymer, mechanical strength, coating properties, solubility, degree of crystallinity, shrinkage properties, permeability, hygroscopic degree, melting point, glass transition temperature, clearing point, chemical resistance, thermal resistance, and the like.
As the polymerizable liquid crystal compound, there has been proposed a polymerizable compound having a (meth)acryl group. Since the polymerizable liquid crystal compound whose polymerizable functional group is a (meth)acryl group has high polymerization reactivity and the obtained polymer shows high transparency, intensive investigations are conducted on application thereof as an optical anisotropic material (see, for example, Patent Documents 1 to 10).
In contrast, the present inventors have developed a polymerizable liquid crystal compound which provides an optical anisotropic material (polymer) which is excellent in the aforementioned characteristics and filed for the patent (Japanese Patent Application No. 2005-315699). The compound has excellent characteristics as a polymerizable liquid crystal material, and thus an intermediate which serves as a raw material is required.
Furthermore, a compound having a reactive functional group in addition to the polymerizable functional group is in demand as a monomer or an intermediate for various functional materials, because such compound is easy to react with various functional compounds.
Patent Document 1: Japanese Patent Laid-Open Publication No. H11-116534
Patent Document 2: Japanese Patent Application Laid-Open No. H11-130729
Patent Document 3: Japanese Patent Application Laid-Open No. H11-513360
Patent Document 4: Japanese Patent No. 3228348
Patent Document 5: Japanese Patent Laid-Open Publication No. 2005-015473
Patent Document 6: Japanese Patent Laid-Open Publication No. 2005-206579
Patent Document 7: Japanese Patent Laid-Open Publication No. 2002-265421
Patent Document 8: Japanese Patent Laid-Open Publication No. 2002-308831
Patent Document 9: Japanese Patent Laid-Open Publication No. 2002-308832
Patent Document 10: Japanese Patent Laid-Open Publication No. 2005-263789
Accordingly, an object of the present invention is to provide a novel polymerizable compound which is useful as an intermediate for a polymerizable liquid crystal material.
The present inventors conducted diligent research in order to solve the above-mentioned problems and, as a result, found a novel polymerizable compound.
Specifically, the present invention is to provide a novel polymerizable compound represented by the following general formula (I).
wherein R1 is a hydrogen atom, a methyl group or a halogen atom; R2 is an optionally substituted alkyl group having 1 to 6 carbon atoms, an optionally substituted alkoxy group having 1 to 6 carbon atoms, a halogen atom or a cyano group; an alkylene group of each of the alkyl and the alkoxy group may be interrupted by an unsaturated bond, an ether bond, a thioether bond or an ester bond; n is an integer from 0 to 14; and m is 0 or 1.
The present invention is also to provide the novel polymerizable compound which is a synthetic intermediate for a polymerizable liquid crystal compound.
Hereafter, the novel polymerizable compound of the present invention, represented by the general formula (I), will be described in further detail.
In the general formula (I), examples of halogen atoms represented by R1 and R2 include a fluorine atom, a chlorine atom, a bromine atom, and an iodine atom; examples of R2 that represents an optionally substituted alkyl group having 1 to 6 carbon atoms, include methyl, chloromethyl, trifluoromethyl, cyanomethyl, ethyl dichloroethyl, propyl, isopropyl, butyl, sec-butyl, tert-butyl, isobutyl, amyl, isoamyl, tert-amyl, hexyl, 2-hexyl, 3-hexyl, cyclohexyl, 1-methylcyclohexyl, and the like; examples of R2 that represents an optionally substituted alkoxy group having 1 to 6 carbon atoms, include methoxy, chloromethoxy, trifluoromethoxy, cyanomethoxy, ethoxy, dichloroethoxy, propoxy, isopropoxy, butoxy, sec-butoxy, tert-butoxy, isobutoxy, amyloxy, isoamyloxy, tert-amyloxy, hexyloxy, cyclohexyloxy, and the like. The alkyl and alkoxy group taken as examples above may be interrupted by an unsaturated bond, ether bond, thioether bond, or ester bond.
As specific examples of the novel polymerizable compound of the present invention, represented by the foregoing general formula (I), there may be mentioned the following Compound Nos. 1 to 22. However, the present invention is not limited by the following compounds.
As regards the synthetic method for the compound of the present invention, represented by the general formula (I), there may be mentioned the following method.
As a raw material for the compound represented by the general formula (I), there may be mentioned compounds represented by the following general formulae (II) and (III).
In the general formula (II), R1 is a hydrogen atom, a methyl group, or a halogen atom; n is an integer from 0 to 14; A may be any one of groups which form an ester bond by an esterification reaction with an —OH group of a compound represented by the following general formula (III). Examples of A include a carboxyl group (—COOH), an acyl halide group (—COX, where X represents a halogen such as F, Cl, Br, I, and the like), a carboxylate group (—COOM, where M represents an alkali metal such as Na, K, Li, and the like), and, further include a p-toluenesulfonic acid ester (—CO—O-TS, where TS represents a tosyl group), a methanesulfonic acid ester (—CO—O-MS, where MS represents a mesyl group) and the like. R1 and n in the general formula (II) correspond to R1 and n of the compound represented by the general formula (I), respectively.
In the general formula (III), R2 is an optionally substituted alkyl group having 1 to 6 carbon atoms, an optionally substituted alkoxy group having 1 to 6 carbon atoms, a halogen atom, or a cyano group, where an alkylene group in the alkyl and alkoxy group may be interrupted by an unsaturated bond, ether bond, thioether bond, or ester bond. R2 in the general formula (III) corresponds to R2 in the general formula (I).
In the general formula (III), B represents a protecting group for a phenolic hydroxyl group. The protecting group for the phenolic hydroxyl group may be one which is commonly used, with examples including a benzyl group, a p-methoxybenzyl (MPM) group, a trimethylsilyl (TMS) group, a tert-butyldimethylsilyl (TBDMS) group, a methoxymethyl (MOM) group, a methoxyethoxymethyl (MEM) group, and the like, and the benzyl group is especially preferable.
The reaction steps for preparing the compound represented by the general formula (I) include Step 1, where an esterification reaction is carried out between the compound represented by the general formula (II) and a compound represented by the general formula (III) to afford a compound represented by the general formula (IV). This is followed by Step 2, where the protecting group B is removed to afford a compound represented by the general formula (I). R1 and R2 in the general formula (IV) are derived from the general formulae (II) and (III), respectively, and correspond to those of the resultant compound represented by the general formula (I). B is derived from the general formula (III). The method for removing the protecting group in Step 2 may be selected appropriately depending on the nature of the protecting group.
The novel polymerizable compound of the present invention is characterized by the presence of a reactive phenolic hydroxyl group at the end of the molecule. By reacting this phenolic hydroxyl group with another compound, various polymerizable liquid crystal compounds may be obtained, which makes the novel polymerizable compound of the present invention useful as an intermediate for various polymerizable liquid crystal compounds.
Examples of the polymerizable liquid crystals to be obtained include those represented by the general formulae (V), (VI) and the like, but the polymerizable liquid crystals are not limited to these.
In the general formula (V), R1, R2 and n are the same as those in the compounds represented by the general formula (I); R3 is a hydrogen atom, a methyl group or a halogen atom; m is 0 or 1; and p is an integer from 1 to 14.
in the general formula (VI), R1, R2 and n are the same as those in the compounds represented by the general formula (I); R4 is a hydrogen atom, a methyl group or a halogen atom; m is 0 or 1; and q is an integer from 1 to 14.
The polymerizable liquid crystal compound thus obtained can be polymerized or copolymerized into a (co)polymer (optical anisotropic material). The (co)polymer may be used as an optical element such as a retardation film for a liquid crystal display, an optical compensation plate (retardation plate) for a liquid crystal display, an alignment layer for a liquid crystal display, a polarizing plate, a wide viewing angle plate, a reflection film, a color filter, a holographic element, a light polarizing prism, an optical head and the like; and as an optical anisotropic material for a low-pass filter, a brightness enhancement film, a polarizing beam splitter, and the like.
Furthermore, the novel polymerizable compound of the present invention has a reactive phenolic hydroxyl group at the end of the molecule and can be reacted easily with various functional groups. Thus, the novel polymerizable compound of the present invention is useful not only as an intermediate for the aforementioned liquid crystal compound but also as a monomer and an intermediate for various functional materials such as an optical anisotropic material, a color calibration plate, a wavelength conversion element, a nonlinear optical material, an organic semiconductor, an adhesive, a high-performance ink, a paint, a semiconductor resist, a color resist for a color filter, a photosensitive element, a membrane material with a high dielectric constant, various shielding materials, a resin substrate material, and the like.
Hereafter, the present invention will be further described in terms of Examples (Synthesis Examples). However, the present invention is not limited by these Examples.
In the following Examples (Synthesis Examples), the structure of a compound was confirmed by nuclear magnetic resonance (1H-NMR) spectra, infrared (IR) absorption spectra, and the like.
Furthermore, the thermal transition behavior of the polymerizable liquid crystal compound was observed with DSC and a polarizing microscope. C stands for crystals, N for a nematic phase, and I for an isotropic liquid phase, respectively.
Compound No. 2 of the present invention was synthesized according to the procedures of the following Steps 1 and 2.
<Step 1>
A benzyl ether compound was synthesized according to the following reaction equation and by the procedures described below.
Specifically, 1.90 g (7.86 mmol) of 6-acryloyloxy-2-naphthoic acid was dissolved in 10 g of THF, to which 0.99 g (8.65 mmol) of methanesulfonyl chloride was added with ice-water bath cooling, and further 1.91 g (18.87 mmol) of triethylamine (TEA) was added dropwise. After stirring for 1 hour, 10 mg (0.08 mmol) of 4-dimethylaminopyridine (DMAP) was added, to which a solution of 2.00 g (8.25 mmol) of 4-benzyloxy-2-n-propylphenol dissolved in 7 g of THF was added dropwise. After stirring for 1 hour, the reaction mixture was allowed to warm to room temperature, the precipitates were removed by filtration, and the filtrate was washed with water. After removing the solvent by evaporation, the residue was purified by column chromatography (developing solvent: dichloromethane, SiO2) and recrystallized from acetone. Thus the target benzyl ether was obtained as a white solid (2.27 g, 61.9% yield).
<Step 2>
Using the benzyl ether compound obtained in Step 1, Compound No. 2 was synthesized according to the following reaction equation and by the procedures described below.
Specifically, 2.01 g (15.08 mmol) of anhydrous aluminum chloride was dissolved in 9 g of anisole, to which a solution of 2.27 g (4.87 mmol) of the benzyl ether compound obtained in Step 1 and dissolved in 9 g of anisole was added dropwise with ice-water bath cooling. After 1 hour of stirring, the reaction mixture was allowed to warm to room temperature and aqueous hydrochloric acid was added dropwise to dissolve the precipitate. The reaction mixture was washed with water and the solvent was removed by distillation. The residue was purified by column chromatography (developing solvent: ethyl acetate/toluene=⅕, SiO2) and recrystallized from a mixed solvent, acetone/methanol, to afford a white solid (1.20 g, 65.6% yield).
Analysis of the white solid obtained confirmed that the white solid was the target material, Compound No. 2. The results of analysis are shown in the following.
(Results of Analysis)
(1) IR (KBr pellet method) (cm−1)
3379, 2954, 2927, 2870, 1724, 1628, 1601, 1501, 1474, 1450, 1400, 1373, 1339, 1277, 1172, 1142, 1111, 1057
(2) 1H-NMR [CDCl3] (ppm)
0.9 (t, 3H), 1.5-1.8 (m, 2H), 2.4-2.6 (t, 2H), 4.9 (s, 1H), 6.0-7.4 (m, 7H), 7.7-8.3 (m, 4H), 8.8 (s, 1H)
(3) Melting point
149.3° C. (DSC, 5° C./min)
Using Compound No. 2 obtained in Example 1 as an intermediate raw material, Polymerizable liquid crystal compound-1 was synthesized according to the following reaction equation.
Specifically, 1.04 g (3.04 mmol) of 6-(6-acryloyloxy-hexyloxy)-2-naphthoic acid was dissolved in 12 g of THF, to which 0.38 g (3.34 mmol) of methanesulfonyl chloride was added with ice-water bath cooling, and further 0.74 g (7.29 mmol) of triethylamine was added dropwise. After 1 hour of stirring, 4 mg (0.03 mmol) of DMAP was added, and a solution of 1.20 g (3.19 mmol) of Compound No. 2 obtained in Example 1 and dissolved in 8 g of THF was added dropwise. After 1 hour of stirring, the reaction mixture was allowed to warm to room temperature and precipitates were removed by filtration. The filtrate was washed with water and the solvent was removed by evaporation. The residue was purified by column-chromatography (developing solvent: ethyl acetate/toluene=⅕, SiO2) and then, recrystallized from a mixed solvent of ethyl acetate/hexane to give a white solid (0.67 g, 31.5% yield). Analysis of the white solid obtained confirmed that the white solid was the target material, Polymerizable liquid crystal compound-1. The results of analysis are shown in the following.
(Results of Analysis)
(1) IR (cm−1)
2936, 2866, 1624, 1474, 1404, 1339, 1273, 1246, 1200, 1169, 1150, 1065, 1022
(2) 1H-NMR (ppm)
0.9 (t, 3H), 1.5-1.9 (m, 10H), 2.6 (q, 2H), 3.9-4.3 (m, 4H), 5.7-6.6 (m, 6H), 7.1-7.5 (m, 6H), 7.7-8.3 (m, 7H), 8.7 (s, 1H), 8.9 (s, 1H)
(3) Thermal transition behavior
The novel polymerizable compound of the present invention is useful as a synthetic intermediate, which can provide a polymerizable liquid crystal compound. Furthermore, due to the presence of a reactive phenolic hydroxyl group at the end of the molecule, the novel polymerizable compound of the present invention can be reacted easily with various functional compounds and are useful as a monomer and an intermediate for various functional materials.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2006-003724 | Jan 2006 | JP | national |
| Filing Document | Filing Date | Country | Kind | 371c Date |
|---|---|---|---|---|
| PCT/JP2006/322597 | 11/14/2006 | WO | 00 | 6/9/2008 |