Claims
- 1. In a thermoplastic polyurethane elastomer which is the product of reaction of 4,4'-methylenebis(phenyl isocyanate), difunctional extender and a polymeric diol selected from the class consisting of (a) polyoxypropylene-polyoxyethylene copolymers having a molecular weight of from about 1000 to about 3000, and having a minimum content of ethylene oxide (E.O.) residues by weight for any given molecular weight (MW) corresponding to: ##EQU2## (b) polyester diols having a molecular weight of from about 1000 to about 4000, and mixtures of (a) and (b), the equivalent proportions of polymeric diol to extender being within the range of about 1:2 to about 1:20 and the ratio of equivalents of said isocyanate to total hydroxyl equivalents being within the range of about 0.99:1 to 1.06:1, the improvement which comprises replacing at least about 15 percent by weight of said polymeric diol by a replacement polyol selected from the class consisting of:
- (i) polyoxypropylene-polyoxyethylene glycols having a molecular weight of about 3500 to about 4500 and an ethylene oxide content of about 10 to about 60 percent by weight;
- (ii) polyoxypropylene-polyoxyethylene triols having a molecular weight from about 5000 to about 7000 and an ethylene oxide content of about 10 to about 40 percent by weight; and
- (iii) mixtures of (i) and (ii).
- 2. A thermoplastic polyurethane according to claim 1 wherein said polymeric diol is a polyoxypropylene-polyoxyethylene copolymer (a) defined in claim 1.
- 3. A thermoplastic polyurethane according to claim 2 wherein said diol is a 2000 molecular weight polyoxypropylene-polyoxyethylene glycol having about 45 percent by weight of ethylene oxide residues.
- 4. A thermoplastic polyurethane according to claim 1 wherein said polymeric diol is a polyester diol (b) defined in claim 1.
- 5. A thermoplastic polyurethane according to claim 4 wherein said polyester diol is a polyalkylene ester diol.
- 6. A thermoplastic polyurethane according to claim 5 wherein the polyester diol is a 2000 molecular weight polybutylene adipate.
- 7. A thermoplastic polyurethane according to claim 1 wherein said polymeric diol is a mixture of said polyoxypropylene-polyoxyethylene copolymer (a) and said polyester diol (b) defined respectively in claim 1.
- 8. A thermoplastic polyurethane according to claim 1 wherein said replacement polyol is a polyoxypropylene-polyoxyethylene glycol having a molecular weight of about 3500 to about 4500 and an ethylene oxide content of about 10 to about 60 percent by weight.
- 9. A thermoplastic polyurethane according to claim 1 wherein said replacement polyol is a polyoxypropylene-polyoxyethylene triol having a molecular weight about 5000 to about 7000 and an E.O. content of about 10 to about 40 percent by weight.
- 10. A thermoplastic polyurethane according to claim 1 wherein said replacement polyol comprises mixtures of a polyoxypropylene-polyoxyethylene glycol having a molecular weight about 3500 to about 4500 and an E.O. content of about 10 to about 60 percent by weight and a polyoxypropylene-polyoxyethylene triol having a molecular weight about 5000 to about 7000 and an E.O. content of about 10 to about 40 percent by weight.
- 11. In a thermoplastic polyurethane elastomer which is the product of reaction of 4,4'-methylenebis(phenyl isocyanate), difunctional extender and a polymeric diol selected from the class consisting of (a) a 2000 MW polyoxypropylene-polyoxyethylene glycol having about 45 percent by weight of E.O. residues, (b) a 2000 MW polybutylene adipate, and mixtures of (a) and (b), the equivalent proportions of polymeric diol to extender being within the range of about 1:2 to about 1:20 and the ratio of equivalents of said isocyanate to total hydroxyl equivalents being within the range of about 0.99:1 to 1.06:1, the improvement which comprises replacing at least about 15 percent by weight of said polymeric diol by a polyoxypropylene-polyoxyethylene glycol having a molecular weight of about 3500 to about 4500 and an E.O. content of about 10 to about 60 percent by weight.
- 12. A thermoplastic polyurethane according to claim 11 wherein said difunctional extender comprises (i) from about 75 to 100 percent on an equivalent basis of an aliphatic straight chain extender diol having from 2 to 6 carbon atoms, inclusive, and (ii) from 25 to 0 percent by equivalents of a polyethylene glycol having a molecular weight from about 200 to about 600.
- 13. A thermoplastic polyurethane according to claim 11 wherein said polymeric diol is a 2000 MW polyoxypropylene-polyoxyethylene glycol having about 45 percent by weight of E.O. residues.
- 14. A thermoplastic polyurethane according to claim 11 wherein said polymeric diol is a 2000 MW polybutylene adipate.
- 15. A thermoplastic polyurethane according to claim 11 wherein said polymeric diol is a mixture of a 2000 MW polyoxypropylene-polyoxyethylene glycol having about 45 percent by weight of E.O. residues and a 2000 MW polybutylene adipate.
- 16. A thermoplastic polyurethane according to claim 11 wherein said replacement glycol is a polyoxypropylene-polyoxyethylene glycol of MW about 4000 and E.O. content of about 20 percent by weight.
- 17. A thermoplastic polyurethane according to claim 11 wherein said replacement glycol is a polyoxypropylene-polyoxyethylene glycol of MW about 3700 and E.O. content of about 45 percent by weight.
- 18. A thermoplastic polyurethane according to claim 11 wherein said polymeric diol comprises a mixture of about 50 percent by weight of a 2000 MW polybutylene adipate and the balance a polyoxypropylene-polyoxyethylene glycol MW about 3700 and E.O. content of about 45 percent by weight.
- 19. A thermoplastic polyurethane according to claim 11 wherein said polymeric diol comprises a mixture of about 82 percent by weight of a 33/67 weight percent mixture of a 2000 MW polybutylene adipate and a 2000 MW polyoxypropylene-polyoxyethylene diol having about 45 percent by weight E.O. and the balance a polyoxypropylene-polyoxyethylene glycol MW about 4000 and E.O. content of about 20 percent by weight.
- 20. A thermoplastic polyurethane according to claim 18 or 19 wherein said extender is 1,4-butanediol.
CROSS-REFERENCE TO RELATED APPLICATION
This application is a continuation-in-part of pending application Ser. No. 348,324 filed Feb. 12, 1982 which latter is a continuation of Ser. No. 209,862 filed Nov. 24, 1980 both of which are now abandoned. The disclosure of said Ser. No. 348,324 is hereby incorporated by reference in its entirety.
US Referenced Citations (11)
Continuations (1)
|
Number |
Date |
Country |
Parent |
209862 |
Nov 1980 |
|
Continuation in Parts (1)
|
Number |
Date |
Country |
Parent |
348324 |
Feb 1982 |
|