Claims
- 1. A deep stretch forming process for preparing biaxially oriented, heat set, hermetically sealable, hollow containers with cylindrical sidewall and bottom sections measuring approximately the same thickness, from high molecular weight polyester, said process comprising the steps of
- (A) injection molding a contoured preform of high molecular weight polyester, said contoured preform consisting of a thick peripheral clamping section and immediately interiorly thereof a tapered central section which radially increases in thickness from about one-fourth the thickness of the peripheral clamping section at a point immediately adjacent to said clamping section to about the same thickness as that of the peripheral clamping section at about the center axis of said contoured preform;
- (B) heatng the contoured preform at a temperature ranging from about 10.degree. C. below to about 30.degree. C. above the glass transition temperature of the polyester comprising said contoured preform and clamping said preform exteriorly to and above a hollow die comprising a chamber or cavity having an annular flange forming recess in the upper portion thereof;
- (C) forcing the tapered central section of the contoured preform through the entrance aperture of and into the chamber or cavity of said hollow die by means of a forming plunger having a flange forming annular ring affixed to the upper portion thereof, said plunger being heated to a temperature ranging from about 10.degree. C. below to about 30.degree. C. above the glass transition temperature of the polyester comprising the contoured preform;
- (D) increasing the temperature of the forming plunger to a temperature sufficient to induce rapid crystallization of the polyester in the hollow container formed from the contoured preform to anneal or heat set the polyester in the formed container; and
- (E) cooling the formed container in the hollow die to a temperature below the glass transition temperature of the polyester in the hollow container prior to finally removing the container from the hollow die.
- 2. The process of claim 1 wherein the injection molded contoured preform is heated to a temperature ranging from about 60.degree. C. to about 100.degree. C.
- 3. The process of claim 1 wherein the forming plunger used to force the tapered central section of the heated contoured preform through the entrance aperture of and into the cavity or chamber of the hollow die is heated to a temperature ranging from about 60.degree. C. to about 100.degree. C.
- 4. The process of claim 1 wherein the temperature of the forming plunger is increased to a temperature ranging from about 150.degree. C. to about 200.degree. C. to anneal or heat set the polyester in the hollow container formed from the contoured preform.
- 5. The process of claim 1 wherein the formed container is cooled in the hollow die to a temperature below the glass transition temperature of the polyester in said container.
- 6. The process of claim 1 wherein the high molecular weight polyester employed in the process is polyethylene terephthalate.
- 7. The process of claim 6 wherein the polyethylene terephthalate has a density of 1.361 grams per cubic centimeter or less and an intrinsic viscosity ranging from about 0.5 to 1.10 as measured in a 60/40 mixed solvent of phenol and tetrachloroethane at 30.degree. C.
- 8. The process of claim 7 wherein the intrinsic viscosity of the polyethylene terephthalate ranges from about 0.70 to about 1.0.
- 9. A deep stretch forming process for preparing biaxially oriented, heat set, hermetically sealable, hollow containers with cylindrical sidewall and bottom sections measuring approximately the same thickness, from high molecular weight polyester, said process comprising the steps of
- (A) heating a contoured preform of high molecular weight polyester, said contoured preform consisting of a thick peripheral clamping section and immediately interiorly thereof a tapered central section which radially increases in thickness from about one-fourth the thickness of the peripheral clamping section at a point immediately adjacent to said clamping section to about the same thickness as that of the peripheral clamping section at about the center axis of said contoured preform wherein said heating is at a temperature ranging from about 10.degree. C. below to about 30.degree. C. above the glass transition temperature of the polyester comprising said contoured preform and clamping said preform exteriorly to and above a hollow die comprising a chamber or cavity having an annular flange forming recess in the upper portion thereof;
- (B) forcing the tapered central section of the contoured preform through the entrance aperature of and into the chamber or cavity of said hollow die by means of a forming plunger having a flange forming annular ring affixed to the upper portion thereof, said plunger being heated to a temperature ranging from about 10.degree. C. below to about 30.degree. C. above the glass transition temperature of the polyester comprising the contoured preform;
- (C) increasing the temperature of the polyester in the hollow container to induce rapid crystallization to anneal or heat set said polyester.
Parent Case Info
This is a division of application Ser. No. 199,139 filed Oct. 22, 1980, now U.S. Pat. No. 4,358,492.
US Referenced Citations (11)
Foreign Referenced Citations (1)
Number |
Date |
Country |
8004049 |
Jan 1981 |
NLX |
Divisions (1)
|
Number |
Date |
Country |
Parent |
199139 |
Oct 1980 |
|