Novel tetrablock copolymer and compositions containing same

Abstract

A novel tetrablock copolymer having the general configuration of A1-B1-A 2-B2 is claimed, where the A1 and A2 blocks are blocks of mono alkenyl arene and the B1 and B2 blocks are blocks of hydrogenated butadiene, having a 1,2-vinyl content of between 25% and 60%. The blocks have well defined molecular weight ranges, resulting in a polymer having a unique set of property advantages. Also disclosed and claimed are elastomeric compositions containing the linear hydrogenated block copolymer, a styrene polymer, an ethylene polymer and a tackifying resin. These elastomeric compositions have particular utility in injection molded parts and in extruded parts such as extruded films and fibers.

Description

FIELD OF THE INVENTION

[0002] The present invention relates to a novel tetrablock copolymer and to compositions containing such tetrablock copolymer. More particularly the tetrablock copolymer is a selectively hydrogenated SBSB block copolymer having a particular molecular weight distribution and microstructure, resulting in a polymer having a unique set of property advantages. Also claimed are blends of the tetrablock copolymer and other constituents including styrene polymers, olefin polymers and tackifying resins

BACKGROUND OF THE INVENTION

[0003] The preparation of block copolymers of mono alkenyl arenes and conjugated dienes is well known. One of the first patents on linear ABA block copolymers made with styrene and butadiene is U.S. Pat. No. 3,149,182. These polymers in turn could be hydrogenated to form more stable block copolymers, such as those described in U.S. Pat. No. 3,595,942 and Re. 27,145. A number of other variations for block copolymer structures have been found since then. One of the types of block copolymers that has found limited utility in the past have been tetrablock copolymers having the structure ABAB or BABA, where the A block is a styrene block and the B block is a conjugated diene block, typically either an isoprene block or a butadiene block. These polymers in turn have sometimes been hydrogenated. Such tetrablock copolymers are disclosed in a variety of patents, including U.S. Pat. Nos. 4,874,821; 5,378,760; 5,492,967; 5,549,964; 5,554,697; 6,106,011; and 6,239,218.

[0004] One of the many end uses for block copolymers and tetrablock copolymers is in fibers and films. See, for example, U.S. Pat. Nos. 5,549,964 and 5,705,556. However, during film and fiber formation, breaks are a common problem for highly elastic rubber compounds. Many of the existing block copolymers and formulations based on such block copolymers continue to have problems with breaks. What is needed is a polymer and compound that possesses enhanced strength to produce tougher films and fibers that are much less likely to break during processing. In addition, highly elastic compounds have a tendency to orient during injection molding in long or complex molds. This orientation leads to warpage and non-uniform shrinkage during de-molding or heating. What is needed then is a material with good elastic properties that can be easily injection molded into a part with isotropic properties. It is also desirable to produce a polymer with a higher modulus thus providing a stiffer rubber. A stiffer, stronger rubber allows the use of less polymer to achieve a desired stretching force, and is therefore, more economical.

SUMMARY OF THE INVENTION

[0005] The inventors have discovered a linear hydrogenated block copolymer possessing a unique balance of properties. In particular, the inventors have discovered a linear hydrogenated block copolymer consisting of four alternating blocks having the block arrangement of A1-B1-A2-B2 wherein:

[0006] a. the two polymer blocks B1 and B2 comprise hydrogenated butadiene monomer units in which at least 90% of the olefinically unsaturated double bonds contained in the unhydrogenated polymer block are hydrogenated, and in which the unhydrogenated polymer block have a 1,2-vinyl bond content of greater than 25% and less than 60%;

[0007] b. the two polymer blocks A1 and A2 comprise mono alkenyl arene monomer units;

[0008] c. the number average molecular weights of the blocks are between 6,000 and 8,000 for the S1 block, between 55,000 and 70,000 for the B1 block, between 7,500 and 9,000 for the S2 block and between 5,000 and 12,000 for the B2 block; and

[0009] d. wherein said linear hydrogenated block copolymer has an order-disorder temperature of less than 240° C., a melt flow rate of less than 2.0 g/10 minutes as measured at 200° C. under a load of 5 kg in accordance with ASTM D1238 and a melt flow rate of between 4.0 and 20.0 g/10 minutes as measured at 250° C. under a load of 5kg in accordance with ASTM 1238D.

[0010] The B1 and B2 blocks resemble ethylene/butylene copolymers due to the control of the 1,2-content of the butadiene polymer. These are therefore alternatively termed “EB” blocks.

[0011] The inventors have found that the particular combinations of molecular weights for the blocks claimed herein leads to outstanding elastic properties, and that the molecular weight of the B2 block, or the “EB-tail”, can be used to control the processability of the polymer.

[0012] In another aspect, the inventors have discovered that such linear hydrogenated block copolymers may be compounded with other components into certain elastomeric compositions that have great utility for injection molding and extrusion. Injection molding can be used to make articles such as overmolded handles and soft panels. Extrusion can be used to prepare films, ribbons, tapes and fibers. These compositions comprise the linear hydrogenated block copolymer, a styrene polymer, an ethylene polymer and a tackifying resin. The tetrablock copolymer of the present invention allows a balance of processability, strength and elasticity not achievable in any other film and fiber compound. Compounds for these film and fiber applications normally have strengths in the range of 2,000 to 3,000 psi. The combination of this particular tetrablock copolymer with tackifying resin, polyethylene, and polystyrene yields strengths in the range of 4,500 to 6,000 psi while retaining the balance of processability and elasticity of existing compounds. It is commonly accepted in the art that addition of commercial polystyrene to block copolymers does not affect the end-blocks of these polymers. However, the inventors have found that the addition of between 5 and 10% commercial polystyrene strikingly increases the tensile strength and modulus of these compounds, far beyond the small effect that would arise if the polystyrene were present as filler. The compounds of the present invention are much stiffer than previous compounds with comparable elasticity.

BRIEF DESCRIPTION OF THE DRAWINGS

[0013] FIG. 1 shows stress-strain curves for various compounds of one of the tetrablock copolymers of the present invention with varying amounts and types of polystyrene. FIG. 2 shows stress-strain curves for various compounds of the present invention, including tetrablock copolymer, polystyrene, polyethylene and tackifying resin. FIG. 3 shows stress-strain curves comparing compounds of the present invention against a compound based on a selectively hydrogenated styrene-isoprene tetrablock copolymer.

DETAILED DESCRIPTION OF THE INVENTION

[0014] The tetrablock copolymers of the present invention are linear polymers prepared by contacting the monomers to be polymerized sequentially with an organoalkali metal compound in a suitable solvent at a temperature within the range from about −150° C. to about 300° C., preferably at a temperature within the range from about 0° C. to about 100° C. Particularly effective anionic polymerization initiators are organolithium compounds having the general formula RLin where R is an aliphatic, cycloaliphatic, aromatic, or alkyl-substituted aromatic hydrocarbon radical having from 1 to 20 carbon atoms; and n is an integer of 1 to 4. Preferred initiators include n-butyl lithium and sec-butyl lithium. See generally, U.S. Pat. Nos. 4,039,593 and Re 27,145 for typical synthesis.

[0015] The tetrablock is a selectively hydrogenated A1-B1-A2-B2 block copolymer where the A blocks are polymer blocks of mono alkenyl arenes, preferably polymer blocks of styrene. The B blocks prior to hydrogenation are polymer blocks of 1,3-butadiene, where between about 25 and 60 percent of the units have a 1,2-vinyl bond content, preferably between about 30 and about 55 1,2-vinyl bond content. The control of microstructure in the synthesis of the polymer is through the addition of a control agent during polymerization of the butadiene. A typical agent is diethyl ether. See U.S. Pat. No. Re 27,145 and U.S. Pat. No. 5,777,031, the disclosure of which is hereby incorporated by reference.

[0016] The tetrablock copolymer is selectively hydrogenated using any of the several hydrogenation processes know in the art. For example the hydrogenation may be accomplished using methods such as those taught, for example, in U.S. Pat. Nos. 3,494,942; 3,634,594; 3,670,054; 3,700,633; and Re. 27,145, the disclosures of which are hereby incorporated by reference. The methods known in the prior art and useful in the present invention for hydrogenating polymers containing ethylenic unsaturation and for selectively hydrogenating polymers containing aromatic and ethylenic unsaturation, involve the use of a suitable catalyst, particularly a catalyst or catalyst precursor comprising an iron group metal atom, particularly nickel or cobalt, and a suitable reducing agent such as an aluminum alkyl. Also useful are titanium based catalyst systems. In general, the hydrogenation will be accomplished in a suitable solvent at a temperature within the range from about 20° C. to about 100° C., and at a hydrogen partial pressure within the range from about 100 psig to about 5,000 psig. Catalyst concentrations within the range from about 10 ppm wt to about 500 ppm wt of iron group metal based on total solution are generally used and contacting at hydrogenation conditions is generally continued for a period of time with the range from about 60 to about 240 minutes. After the hydrogenation is completed, the hydrogenation catalyst and catalyst residue will, generally, be separated from the polymer.

[0017] An important aspect of the present tetrablock copolymer is control of the molecular weights of the individual blocks. This is accomplished by controlling the monomer and the initiator ratios according to known techniques. The following are the preferred and more preferred molecular weights of the blocks:

Block	Preferred Range	More Preferred Range
A1	6,000 to 8,000	6,500 to 7,250
B1	55,000 to 70,000	55,000 to 65,000
A2	7,500 to 9,000	8,000 to 9,000
B2	5,000 to 12,000	5,000 to 8,000

[0018] Molecular weights of linear block copolymers are conveniently measured by Gel Permeation Chromatography (GPC) in tetrahydrofuran, where the GPC system has been appropriately calibrated. Polymers of known molecular weight are used to calibrate the GPC and these must be of the same molecular structure and chemical composition as the unknown linear polymers that are to be measured.

[0019] Another important aspect of the tetrablock copolymers is the melt flow, measured at 200° C. and at 250° C. The measurement is according to ASTM D-1238. The melt flow for the neat polymer must be between 4.0 and 20.0 grams per 10 minutes as measured at 250° C. under a load of 5 kg, preferably between 5.0 and 15 grams per 10 minutes. In addition the melt flow must be less than 2.0 grams per 10 minutes as measured at 200° C. under a load of 5 kg, preferably under 1.5. These melt flow rates are important because they are measures of the rheological properties that control the balance of performance and processability for these polymers. Products that have melt flow rates at 200° C. greater than 2.0 grams per 10 minutes will have poor mechanical properties in the application. Products that have melt flow rates at 250° C. that are less than 4.0 grams per 10 minutes will be difficult to melt fabricate into a useful article. Preparing polymers having the desired melt flow rates will allow the preparation of compounds having good melt processing characteristics and excellent performance in the final fabricated article.

[0020] Still further, the order-disorder temperature (ODT) must be less than 240° C., preferably between 210° C. and 240° C. This is important because when the ODT is below 210° C. the polymer will exhibit excessive creep. Polymers with ODT's above 240° C. may not be easily formulated into effective elastic compounds with common ingredients. The order-disorder temperature is defined as the temperature above which a zero shear viscosity can be measured by capillary rheology or dynamic rheology.

[0021] As mentioned above, another aspect of the present invention relates to blends or compounds of the tetrablock copolymers of the present invention with other polymers selected from the group consisting of certain styrene polymers, certain olefin polymers, and certain tackifying resins.

[0022] The styrene polymers are selected from crystal polystyrene and anionic polystyrene, and are included to increase strength and modulus of the compound. High impact polystyrene is not useful because the rubber dispersed in the HIPS would reduce the strength of the compound. It is preferred that the anionic polystyrene have a molecular weight of about 5,000 to about 100,000, since lower molecular weights would be too volatile and higher molecular weights could be obtained as easily from commercial polymers. As for the crystal polystyrene, it is preferred that it have a melt flow greater than 8 and about 15. Preferred polystyrenes include anionic polystyrene having a molecular weight of 7,000, and crystal polystyrene having a melt flow of about 15. Suitable polystyrenes are available from many manufacturers such as Nova Chemicals.

[0023] The olefin polymers include both crystalline and elastomeric polyolefins. Polyolefins utilized in the present invention must be those that form a mechanically compatible blend when blended with the tetrablock copolymers of the present invention. The olefin polymer is added to the compound in order to increase the modulus (stiffness) of the compound and improve the flow properties. In particular, preferred olefin polymers include polyethylene, polypropylene, and polybutylene, including ethylene copolymers, propylene copolymers and butylene copolymers. Also useful are metallocene catalyzed olefin polymers, such as those available from Dow Chemical Company under the trademark AFFINITY or ENGAGE and from Exxon/Mobil Chemical Company under the trademark EXACT. Blends of two or more of the polyolefins may be utilized. Much preferred polyolefins include low density polyethylene and linear low density polyethylene having densities less than 0.93 grams per cubic centimeter. In addition it is preferred that the LDPE or LLDPE have a high melt flow, preferably greater than about 100. A much preferred polyolefin is Petrothene NA 601 from Quantum Chemical, having a density of about 0.903 grams per cubic centimeter and a Melt index of 2,000 grams per 10 minutes when measured in accordance with ASTM D 1238. Waxes, such as Epolenes, available from Eastman Chemical are also suitable polyolefins. The waxes may be branched ethylene waxes or copolymer waxes.

[0024] Various tackifying resins can be used in the present invention in order to 1 0 increase tack and reduce viscosity. Any tackifying resin can be used which is compatible with the tetrablock copolymer and the polyolefin, and can withstand the processing temperatures. Generally, hydrogenated hydrocarbon resins are preferred tackifying resins, because of their better temperature stability. Suitable resins are available from a number of companies such as Arkon resins from Arakawa, Rextac from Huntsman Chemical, Escorez from Exxon Chemical and Estotac , Regalite, and Regalrez resins from Eastman.

[0025] Preferred tackifying resins are hydrogenated α-methyl styrene, low molecular weight hydrocarbon resin, such as REGALREZ® resins 1126 and 1139 from Eastman Chemical.

[0026] The compounds of the present invention include those having the following formulations, where the total of the various components in any one formulation equals 100 percent:

Component	Preferred Range, % w	More Preferred Range, % w
Tetrablock	50 to 80%	65 to 75%
Styrene Polymer	4 to 15%	5 to 10%
Olefin Polymer	5 to 20%	5 to 15%
Tackifying Resin	0 to 25%	10 to 25%

[0027] While the principal components of the extrudable, elastomeric composition have been described in the foregoing, such composition is not limited thereto, and can include other components not adversely affecting the composition attaining the stated objectives. Exemplary materials which could be used as additional components would include, without limitation, pigments, antioxidants, stabilizers, surfactants, waxes, flow promoters, solvents, particulates, and materials added to enhance processability and handling of the composition.

[0028] Any of the techniques known in the art for blending polymeric components may be used to combine the components of the composition of this invention. Suitable blending techniques include roll milling, screw extrusion and the like.

[0029] The compositions of the present invention may be used in a variety of applications such as molded and extruded goods. Preferred applications are overmolding on various polymer substrates and extrusion into elastic films and fibers having improved processing and/or bonding properties. Molded products provide a soft, high friction surface either alone or overmolded onto polymer substrates to improve the surface feel of a wide range, of products.

[0030] The following examples are intended to be illustrative only, and are not intended to be, nor should they be construed as being, limiting in any way of the scope of the present invention.

[0031] Illustrative Embodiment #1

[0032] In Illustrative Embodiment #1 various tetrablock copolymers were prepared—some according to the present invention, and some outside the present invention. In all cases the tetrablock copolymers were prepared according to the following process scheme:

[0033] 1. In the first step styrene was polymerized in a reactor in the presence of a cyclohexane diluent and a sec-butyl lithium initiator to form the S1 block;

[0034] 2. in the second step, 1,3-butadiene was added to the reactor along with diethyl ether as a microstructure modifier to form the B1 block;

[0035] 3. in the third step styrene was added to form the S2 block;

[0036] 4. in the fourth step 1,3-butadiene was added to form the B2 block;

[0037] 5. methanol was then added to terminate the polymerization;

[0038] 6. the resulting S1-B1-S2-B2 polymer was then hydrogenated under standard conditions with a nickel octoate/aluminum triethyl catalyst to selectively hydrogenate the butadiene units. The residual unsaturation of the olefin portion of the block copolymer was under 0.3 millequivalents per gram, equivalent to a conversion of over 95% of the olefin unsaturation.

[0039] The 1,2-vinyl content of the butadiene blocks prior to hydrogenation was about 38% for all the polymers.

[0040] The various polymers prepared in Illustrative Embodiment #1 are listed in Table #1. The polymers marked with an asterisk are those according to the present invention. —those not marked with an asterisk are outside the present invention.

[0041] Illustrative Embodiment #2

[0042] In Illustrative Embodiment #2 Polymer 1000 from Illustrative Embodiment #1 was compounded with varying amounts and types of polystyrene. The various polystyrenes tested include:

[0043] PS 6700, an anionic polystyrene having a molecular weight of 6700

[0044] Nova 555, a crystal polystyrene having a melt flow of 15

[0045] PS 15000, an anionic polystyrene having a molecular weight of 15,000

[0046] Nova EA 3000, a crystal polystyrene having a melt flow of 1.5

[0047] In all cases the compound contained 0.2 percent of an antioxidant.

[0048] It is well known in the industry that high molecular weight polystyrene is not effective in improving the properties of block copolymers because it does not interact with the polystyrene domains of the block copolymers. With the polymer of the present invention, however, the inventors have found that the addition of 5% to 10% polystyrene provides a very large improvement in tensile strength and 500% modulus. Table 2 and FIG. 1 details the formulations and properties of various compounds. These compounds were melt mixed in a small Brabender mixing head at 225° C. for 5 minutes. The resulting mixture was removed and compression molded into a film for testing. Table 2 and FIG. 1 show that the addition of 5% to 10% polystyrene produces a significant improvement in tensile strength, but more importantly in the modulus values at 300% and 500% strain. This provides the compound with a more linear stress strain curve and less of a rubbery plateau from 150-500% elongation. Typical block copolymers have a relatively slow increase in stiffness from 150-500% elongation. This slow increase in stiffness allows typical block copolymers to be stretched to high elongation without the use of significantly greater forces. In injection molded parts, the stiffer elastomer will provide better tear and bite resistance.

[0049] Illustrative Embodiment #3

[0050] In Illustrative Embodiment #3 Polymer 1000 from Illustrative Embodiment #1 was compounded with a tackifying resin and a low-density polyethylene. The tackifying resin was Regalrez 1126, which is a fully hydrogenated a-methyl styrene hydrocarbon resin having a softening point of 125° C. The low-density polyethylene was NA-601, having a density of 0.903. Samples D-1 through D-5 were compounded in a similar manner to that of Illustrative Embodiment #2. The benefit of increased strength and modulus can be see from Table #3 and FIG. #2. Sample D-3, which contains polystyrene, tackifying resin and polyethylene has a substantially improved tensile strength and modulus at 500% elongation over any of the other formulations, without sacrificing other properties such as permanent set and hysteresis.

[0051] The formulation of Sample D-3 was compounded in larger volumes on a Berstorff twin screw extruder, then cast on a Davis Standard cast film line. The formulation is labeled F-1in Table 3 and FIG. 2. The film version has substantially improved tensile strength and modulus at high elongations compared to formulations without polystyrene. The improvement is particularly noted in the machine direction (“md”) of the extruded film, compared to the transverse (“td”) direction. For applications where elongation is in the machine direction, such as fibers and some films, this is highly advantageous. The properties shown in Table 3 are relatively isotropic compared to traditional compounds where the difference in properties between the MD and TD directions is often more than a factor of 2. This is advantageous for molding thin parts with long flow paths. A material such as the F-1 compound would show very little tendency to warp or shrink non-uniformly because the properties are very similar in all directions.

[0052] Illustrative Embodiment #4

[0053] In Illustrative Embodiment #4 formulation F-1 from Illustrative Embodiment #3 is compared with other similar formulations with varying amounts of polymer and other ingredients. As shown in Table #4 the variation in tackifying level and polystyrene level results in materials which can have a range of modulus and surface tack without losing their high strength. Table 4 shows that this formulation can be very tacky and can be adjusted as desired.

[0054] In addition, formulations with KRATON™ polymers G-1657 and G-1730 were prepared in a similar manner to the F-1 formulation, and the particular formulations are shown in Table 5. G-1657 is a selectively hydrogenated SBS block copolymer having a styrene content of about 13% w and also containing about 30% uncoupled diblock copolymer. G-1730 is a selectively hydrogenated S-I-S-I tetrablockcopolymer having a styrene content of about 22% w. As shown by comparing the results in Tables 4 and 5 and in FIG. 3, the ultimate tensile strength of the current invention is substantially improved over the existing commercial compounds. The modulus at all elongation levels is improved resulting in a more powerful elastic.

TABLE #1
Tetrablock Copolymers-Block Sizes, Melt Flow and Order-Disorder
Temperatures
	Actual Block Size (×1000)	Melt flow	ODT
Polymer	S1	EB1	S2	EB2	@ 250° C.	@ 200° C.	(° C.)
1000*	6.7	65.2	8.4	6.7	5.0	0.5	210
1001*	6.8	59.2	8.1	6.6	8.4		210
1002*	6.9	61.0	8.4	6.6	8.4		220
1003	23.4	83.4	25.0	8.8			300+
1004	27.0	90.4	27.4	12.1			300+
1005	21.4	83.5	28.7	11.0			300+
1006	7.4	67.7	9.6	6.9	2.0		250
1007	7.3	65.8	9.2	7.7	2.9		240
1008	7.4	64.8	9.1	6.7	2.9		240
1009	6.7	59.2	8.6	7.3	5.0		240
1010	6.8	58.4	8.6	6.5	7.0	0.7	240
B-6	6.6	66.1	9.5	6.6	4.7		250
B-7	6.9	60.7	9.5	6.0	5.3		240
B-8*	6.9	60.3	8.9	5.8	9.5	0.7	230
B-9*	6.8	59.4			14.3	1.7	210
B-10*	6.8	59.9	7.8	6.3	12.8	1.3	210
B-11*	6.8	59.7	8.8	5.8	7.7		230
B-12*	6.8	60.6	8.2	6.1	9.4	1.1	230

[0055]

TABLE #2
Sample No.	D11	D12	D13	D17	D14	D15	D16	D18
Formulation
1000, %	99	95	90	95	99	95	90	95
PS 6700, %	1	5	10	0	0	0	0	0
Nova 555, %	0	0	0	0	1	5	10	0
PS 1500, %	0	0	0	5	0	0	0	0
EA 3000, %	0	0	0	0	0	0	0	5
Properties
Stress-Strain
Max Stress, psi	4792	5561	5433	5773	4896	5734	6035	5719
Strain at Break,	921	915	843	882	989	905	860	877
%
Stress at 50%,	172	151	183	165	159	165	179	170
psi
Stress at 100%,	218	193	241	212	203	209	229	216
psi
Stress at 200%,	290	264	342	286	271	286	324	301
psi
Stress at 300%,	392	362	482	398	364	402	472	426
psi
Stress at 500%,	799	806	1176	921	713	919	1249	1059
psi
ODT (° C.)	210-	>280	>280	200-	200-	200-	>280	200-
	260			280	260	280		280

[0056]

TABLE #3
Sample No.	D1	D2	D3	D4	D5	F-1	F-1
1000, %	68	80	75	63	74	75	75
PE 601, %	12	7	7	20	13	7	7
Regalrez 1126,	20	13	13	17	13	13	13
%
Nova 555, %	0	0	5	0	0	5	5
Properties
	Stress-Strain	md	trans
Max Stress at	4461	4482	5648	4771	4758	5628	5834
Break, psi
Strain at Break,	1019	1008	969	1064	1019	787	914
%
Stress at 50%,	166	176	179	199	173	182	176
psi
Stress at 100%,	208	221	224	242	215	233	216
psi
Stress at 200%,	272	288	305	313	281	336	284
psi
Stress at 300%,	360	382	423	409	371	485	380
psi
Stress at 500%,	688	732	951	745	704	1262	817
psi
ODT (° C.)	225	230	240	225	240	240

[0057]

TABLE #4
Sample No	F-1-1	F-1-2	F-1-3
Polymer	1000	1000	1000
Formulation
Polymer, %	75	68	60
PE 601, %	7	7	7
Reg. 1126, %	13	20	23
PS 555, %	5	5	10
Tack	Very slight	Slightly tacky	Tacky
Properties
Stress-Strain	md	td	md	td
Max Stress at Break, psi	5628	5834	5700	5400	4360
Strain at Break, %	787	914	830	985	945
Stress at 50%, psi	182	176	170	140	135
Stress at 100%, psi	233	216	220	170	180
Stress at 200%, psi	336	284	310	230	260
Stress at 300%, psi	485	380	430	300	390
Stress at 500%, psi	1262	817	980	560	1050

[0058]

TABLE #5
Sample No	F-2	F-3	F-4
Polymer Type	G-1657	G-1730	G-1730
Formulation
Polymer, %	63	68	80
PE 601, %	20	12	7
Reg. 1126, %	17	20	13
PS 555, %	0	0	0
Tack	Very slight	Very slight	Very slight
Properties
Stress-Strain	md	td	md	td	md	Td
Max Stress at Break, psi	2037	2050	3213	1924	2100	1990
Strain at Break, %	1000	1066	888	787	930	900
Stress at 50%, psi	146		122	106
Stress at 100%, psi	190	222	158	139	150	154
Stress at 200%, psi	236		211	189		276
Stress at 300%, psi	294		281	255	270	554
Stress at 500%, psi	478		535	498	563
Sample No	F-5	F-6
Polymer Type	G-1730	G-1730
Formulation
Polymer, %	70	85
PE 601, %	30	15
Reg. 1126, %	0	0
PS 555, %	0	0
Tack	Very slight	Very slight
Properties
Stress-Strain	Md	Td	Md	Td
Max Stress at Break, psi	1970	1840	2485	2310
Strain at Break, %	795	788	830	800
Stress at 50%, psi
Stress at 100%, psi	330	284	263	260
Stress at 200%, psi
Stress at 300%, psi	520	520	485	480
Stress at 500%, psi	950	1020	1040	1020

Claims

1. A linear hydrogenated block copolymer consisting of four alternating blocks having the block arrangement of A1-B1-A2-B2 wherein: a. the two polymer blocks B1 and B2 comprise hydrogenated butadiene monomer units in which at least 90% of the olefinically unsaturated double bonds contained in the unhydrogenated polymer block are hydrogenated, and in which the unhydrogenated polymer block have a 1,2-vinyl bond content of greater than 25% and less than 60%; b. the two polymer blocks A1 and A2 comprise mono alkenyl arene monomer units; c. the number average molecular weights of the blocks are between 6,000 and 8,000 for the S1 block, between 55,000 and 70,000 for the B1 block, between 7,500 and 9,000 for the S2 block and between 5,000 and 12,000 for the B2 block; and d. wherein said linear hydrogenated block copolymer has an order-disorder temperature of less than 240° C., a melt flow rate of less than 2.0 g/10 minutes as measured at 200° C. under a load of 5 kg in accordance with ASTM D1238 and a melt flow rate of between 4.0 and 20.0 g/10 minutes as measured at 250° C. under a load of 5 kg in accordance with ASTM 1238D.

2. The linear hydrogenated block copolymer of claim 1 wherein said mono alkenyl arene is styrene.

3. The linear hydrogenated block copolymer of claim 2 wherein the number average molecular weights of the blocks are between 6,550 and 7,250 for the A1 block, between 55,000 and 65,000 for the B1 block, between 8,000 and 9,000 for the A2 block, and between 5,000 and 8,000 for the B2 block.

4. The linear hydrogenated block copolymer of claim 3 wherein the melt flow rate at 250° C. under 5 kg load is between 5 and 15 g/10 minutes.

5. The linear hydrogenated block copolymer of claim 4 wherein said order-disorder temperature is between 210 and 240° C.

6. The linear hydrogenated block copolymer of claim 4 wherein the 1,2-vinyl bond content of the unhydrogenated butadiene blocks is between 30% and 55%.

7. An elastomeric composition comprising: a. about 50 to about 80 weight percent of the linear hydrogenated block copolymer of claim 1;b. about 4 to about 15 weight percent of a styrene polymer selected from the group consisting of crystal polystyrene and anionically polymerized polystyrene; c. about 5 to about 20 weight percent of an olefin polymer selected from the group consisting of ethylene polymers and copolymers, propylene polymers and copolymers, and butylene polymers and copolymers; and d. about 0 to about 25 weight percent of a tackifying resin.

8. The elastomeric composition of claim 7 wherein said mono alkenyl arene is styrene, and wherein the number average molecular weights of the blocks are between 6,550 and 7,250 for the A1 block, between 55,000 and 65,000 for the B1 block, between 8,000 and 9,000 for the A2 block, and between 5,000 and 8,000 for the B2 block.

9. The elastomeric composition of claim 8 wherein the melt flow rate at 250° C. under 5 kg load of said linear hydrogenated block copolymer is between 5 and 15 g/10 minutes and wherein said order-disorder temperature is between 210 and 240° C.

10. The elastomeric composition of claim 9 wherein the amount of linear hydrogenated block copolymer is between about 60 and 80 weight percent, the amount of styrene polymer is between about 5 and 10 weight percent, the amount of olefin polymer is between about 5 and 15 weight percent, and the amount of tackifying resin is between about 10 and 25 weight percent.

11. The elastomeric composition of claim 7 wherein said styrene polymer is selected from the group consisting of anionic polystyrene having a molecular weight of about 5,000 to about 100,000 and crystal polystyrene having a melt flow above 8 gm/10 min at 200° C. under 5 kg load.

12. The elastomeric composition of claim 11 wherein said styrene polymer is crystal polystyrene having a melt flow of about 15gm/10 min at 200° C. under 5 kg load.

13. The elastomeric composition of claim 7 wherein said olefin polymer is selected from the group consisting of ethylene polymers and ethylene copolymers.

14. The elastomeric composition of claim 13 wherein said ethylene polymer is selected from the group consisting of low density polyethylene and linear low density polyethylene having a density less than 0.93 grams per cubic centimeter.

15. The elastomeric composition of claim 7 wherein said tackifying resin is a hydrogenated hydrocarbon resin.

16. The elastomeric composition of claim 15 wherein said tackifying resin is a hydrogenated α-methyl styrene resin.

17. The elastomeric composition of claim 7 also containing one or more additives selected from the group consisting of uv stabilizers, antioxidants, optical brighteners and pigments.

18. A film extruded from the elastomeric composition of claim 7.

19. A fiber extruded from the elastomeric composition of claim 7.

20. The elastomeric composition of claim 7 where the polyolefin is a polypropylene polymer or copolymer.

21. An injection molded article prepared from the elastomeric composition of claim 7.

22. A linear hydrogenated block copolymer consisting of four alternating blocks having the block arrangement of A1-B1-A2-B2 wherein: a. each polymer block B1 and B2 comprises polymerized, hydrogenated butadiene monomer units in which at least 90% of the olefinically unsaturated double bonds contained in the unhydrogenated polymer block are hydrogenated, and in which the unhydrogenated polymer block have a 1,2-vinyl bond content of greater than 25% and less than 60%; b. each polymer block A1 and A2 comprises polymerized mono alkenyl arene monomer units; c. the number average molecular weights of the blocks are between 6,000 and 8,000 for the S1 block, between 55,000 and 70,000 for the B1 block, between 7,500 and 9,000 for the S2 block and between 5,000 and 12,000 for the B2 block; and d. wherein said linear hydrogenated block copolymer has an order-disorder temperature of less than 240° C., a melt flow rate of less than 2.0 g/10 minutes as measured at 200° C. under a load of 5kg in accordance with ASTM D1238 and a melt flow rate of between 4.0 and 20.0 g/10 minutes as measured at 250° C. under a load of 5 kg in accordance with ASTM 1238D.

23. The linear hydrogenated block copolymer of claim 22 wherein said mono alkenyl arene is styrene.

24. The linear hydrogenated block copolymer of claim 23 wherein the number average molecular weights of the blocks are between 6,550 and 7,250 for the A1 block, between 55,000 and 65,000 for the B1 block, between 8,000 and 9,000 for the A2 block, and between 5,000 and 8,000 for the B2 block.

25. The linear hydrogenated block copolymer of claim 24 wherein the melt flow rate at 250° C. under 5 kg load is between 5 and 15 g/10 minutes.

26. The linear hydrogenated block copolymer of claim 25 wherein said order-disorder temperature is between 210 and 240° C.

27. The linear hydrogenated block copolymer of claim 25 wherein the 1,2-vinyl bond content of the unhydrogenated butadiene blocks is between 30% and 55%.

28. An elastomeric composition comprising: a. 50 to 80 weight percent of the linear hydrogenated block copolymer as claimed in claim 22;b. 4 to 15 weight percent of a styrene polymer selected from crystal polystyrene and anionically polymerized polystyrene; c. 5 to 20 weight percent of an olefin polymer selected from ethylene polymers and copolymers, propylene polymers and copolymers, and butylene polymers and copolymers; and d. 0 to 25 weight percent of a tackifying resin.

29. A film or fiber or an injection molded article prepared from the elastomeric composition of claim 28.