The present invention is directed towards a paperboard laminate useful for making containers for citrus juices and beverages, as well as dried food products. In addition, the paperboard laminate is useful for making containers for liquid non-food products such as fabric softeners. The present invention uses two layers of Nylon 6 separated by a low density polyethylene layer to provide a resulting laminated structure having good oxygen barrier properties, abuse resistance, and protection of products packaged therein against the loss of vitamins, flavor, and essential oils. The innermost layer of Nylon 6 is applied directly to the board substrate and provides an oxygen barrier which also protects against overactivation of the board. An additional layer of Nylon 6 provides an anti-scalping layer and is placed adjacent the skin coat layer. The skin coat layer and the adjacent Nylon 6 layer are joined by an adhesive tie layer. The resulting laminate provides for a board structure and carton which are resistant to the creation of pin holes in the laminated layers which may occur through overactivation of the board. Further, the resulting cartons have excellent resistance to scalping. The resulting laminate structure also provides for an assembled carton which, when filled with an aqueous liquid, has good resistance to carton bulge over the life of the carton.
This invention relates to coated paperboard which may be used within the beverage industry to provide containers for citrus and fruit juices, milk, and other liquid and non-liquid food products. A variety of coating layers are known to be used to provide useful properties to the resulting paperboard laminate. For instance, within the citrus juice industry paperboard cartons have coatings designed to provide an oxygen barrier. The incorporation of oxygen barriers into a laminate structure helps preserve Vitamin C content against oxidative loss and contributes to a longer product shelf life.
In addition, juice cartons are prone to scalping of essential oils in the carton's contents by the skin or product contact layer of the laminated board. As such, barrier coatings which provide increased resistance to scalping are also desirable.
Extruded nylon has been used as one layer of a multi-component laminated structure for a barrier board. One such barrier board which provides for oxygen barrier properties and reduces essential oil loss is disclosed in Thompson et al, U.S. Pat. No. 4,777,088.
Brown et al, U.S. Pat. No. 4,753,832, also discloses a nylon oxygen barrier layer as part of a laminated structure. The Brown et al layer provides a skin layer of glycol-modified polyethylene terephathalate (PET-G).
Parks et al, U.S. Pat. No. 6,149,993, discloses a layer of amorphous nylon as an oxygen barrier structure. Amorphous nylon has relatively low strength as compared to Nylon-6 and other semi-crystalline nylon structures. The Park et al reference proposes that the oxygen barrier properties of amorphous nylon are equivalent to the barrier properties of laminated structures containing ethylene vinyl alcohol (EVOH).
An EVOH barrier laminated structure may be seen in reference to the Gibbons et al, U.S. Pat. No. 4,701,360, in which EVOH is provided as a heat-sealable oxygen barrier that offers resistance to scalping when present as the skin layer of a board laminate.
While the art provides for a variety of laminated barriers for cartons, there remains for room for variation and improvement within the art.
It is one aspect of at least one of the present embodiments of the invention to provide an improved, heat-sealable laminated board structure for a juice carton which exhibits excellent oxygen barrier properties. The oxygen barrier properties provide for the retention of high Vitamin C levels. Juice cartons constructed from the laminate board structure also offer good resistance to scalping of essential oils.
It is yet another object of at least one of the present embodiments to provide a heat-sealable paperboard laminated structure which may be used for fruit or citrus juices, other beverages, dry food products, and non-food liquid products such as fabric softeners. The multi-layer laminated structure contains two distinct, separated layers of a high melting temperature polyamide such as Nylon 6 applied to the product side of a paperboard substrate. The innermost layer of Nylon 6 provides an oxygen barrier which is resistant to overactivation.
The outermost layer of Nylon 6 provides a barrier against scalping of essential oils which further protects the extruded, laminated layers during heat sealing steps associated with the folding and filling of cartons.
It is yet another aspect of at least one of the present embodiments of the invention to provide a laminated board structure in which the extruded polymer layer prevents blistering and pinholing of the laminated layers (overactivation) during heat sealing of the cartons. In accordance with this invention, it has been found that when a carton is heat sealed, the paperboard substrate is often raised to a temperature in excess of the boiling point of water. As such, moisture in the paperboard layer turns to steam, the release of which may compromise the structural integrity of the various laminated layers (board overactivation). The damaged lamination layers provide undesirable pathways through the laminated structure for oxygen and moisture. Several of the embodiments described herein provide for laminated structures which are resistant to overactivation.
Thus, in one embodiment of the present invention a paperboard, coated with an outer heat-sealable polyolefin layer, is provided as a coated base substrate upon which an inner, laminated structure is extruded. The extruded, laminated structure, from the exterior (gloss side) of the laminated structure to the interior of the structure, comprises the following layers:
It is yet another embodiment of at least one of the present inventions to provide a laminated structure for paperboard cartons in which an outer skin layer of a polyolefin or other heat-sealable material is attached to an anti-scalping layer such as Nylon 6, Nylon 6/6, amorphous nylon, or other polar polymer material using an adhesive tie layer. The anti-scalping layer, when a high melting polar polymer is used, also provides additional protection to the paperboard against overactivation.
Cartons can be constructed from the laminates of the present invention which provide excellent gas-barrier protection for food and non-food products. Further, the resulting carton has been found to offer a significant reduction in scalping of essential oils which further extends the shelf life and quality of a juice product.
These and other features, aspects, and advantages of the present invention will become better understood with reference to the following description and appended claims.
A fully and enabling disclosure of the present invention, including the best mode thereof, to one of ordinary skill in the art is set forth more particularly in the remainder of the specification, including reference to the accompanying drawings.
Reference now will be made in detail to the embodiments of the invention, one or more examples of which are set forth below. Each example is provided by way of explanation of the invention, not limitation of the invention. In fact, it will be apparent to those skilled in the art that various modifications and variations can be made in the present invention without departing from the scope or spirit of the invention. For instance, features illustrated or described as part of one embodiment can be used on another embodiment to yield a still further embodiment. Thus, it is intended that the present invention cover such modifications and variations as come within the scope of the appended claims and their equivalents. Other objects, features, and aspects of the present invention are disclosed in the following detailed description. It is to be understood by one of ordinary skill in the art that the present discussion is a description of exemplary embodiments only and is not intended as limiting the broader aspects of the present invention, which broader aspects are embodied in the exemplary constructions.
In describing the various figures herein, the same reference numbers are used throughout to describe the same material, apparatus or process pathway. To avoid redundancy, detailed descriptions of much of the apparatus once described in relation to a figure is not repeated in the descriptions of subsequent figures, although such apparatus or process is labeled with the same reference numbers.
An embodiment of the present invention may be provided by a paperboard laminate having the structure as seen in reference to
The laminated structure 1, as seen in reference to
As seen in
The LDPE used on the gloss 12 and skin coat layer 26 is a Chevron 4517 LDPE which may be extruded onto the board at a temperature of about 600° F. The possible operative extrusion temperatures of LDPE are well known to one having ordinary skill in the art and may be varied within the known acceptable temperature ranges. The Nylon 6 is a B85QP (Honeywell) material extruded at 580° F., though a lower extrusion temperature of about 500° F. is recommended. The respective tie layers are low density polyethylene Plexar® 175 (Quantum Corp.) and may be extruded at a temperature of about 600° F.
The resulting laminate may be scored and cut into blanks which may be subsequently folded. The side seams may be heat sealed as is conventional within the art. The prepared blanks are then ready to be filled with juice or other product and sealed using conventional equipment and techniques.
While the structure seen in reference to
Positioned between the oxygen barrier layer 14 and the anti-scalping layer 20 is a relatively thick 20 lb. layer of LDPE (layer 18). The inclusion of a relatively thick layer of LDPE within the laminated structure has been found useful in that the added bulk material further minimizes the overactivation of board during heat sealing. Additionally, the LDPE layer 18 also limits water vapor loss of carton contents which is particularly important for non-refrigerated liquids such as fabric softeners which must have extended shelf lives in low humidity storage environments. The bulk and density of the LDPE helps insulate the board substrate during heat sealing operations and provides for a more rigid carton which resists bulge. While a 20 lb. coating weight is used in the example set forth below, the coating weight of the LDPE may range from between about 10 to about 24 lbs/ream. Additionally, the various polyolefins described above may also be used in place of the low density polyethylene within layer 18. Likewise, similar properties may be achieved by using multiple layers of polyolefin, along with any necessary adhesive tie layers, so as to achieve the similar benefits and attributes of the bulk polyolefin layer 18.
Paperboards suitable for use with the present invention may include a range of paperboard stock having a basis weight of between about 150 to about 300 lbs/ream.
The oxygen barrier layer 14, represented in
The tie resins suitable for co-extrusion with the individual laminated layers may include a variety of conventional tie resins such as anhydride modified co-polymers available under the trade name of Bynel® (DuPont Corp.) along with the Plexar® resins noted above. Useful coating levels of tie layers include about 2 to about 6 lbs/ream coating weight.
The anti-scalping layer, represented in
Amorphous nylon may also be used as the anti-scalping layer 22. Amorphous nylon provides excellent oxygen barrier properties to the overall structure and works well in high humidity environments such as those encountered in refrigerated juice cartons.
As set forth in the examples which follow, a structure as seen in
A laminate according to the embodiment seen in reference to
As seen in reference to
As seen in reference to the data set forth in
Additionally, the use of a high semi-crystalline nylon as discussed in some embodiments as oxygen barrier layers and/or an anti-scalping layer, imparts additional stiffness to the laminated structure which also contributes to the overall bulge resistance of the carton.
As set forth in Applicant's co-pending application having Ser. No. 60/428,293, entitled Improved Flavor Barrier, and which is incorporated herein by reference in its entirety, calcium carbonate and other organic and inorganic fillers described may be incorporated into skin coat 26 and tie layer 24 at a percent by weight loading of at least about 10 to 20 percent. The inclusion of a filler into the skin coat and tie layer resins will further reduce the amount of d-limonene which is scalped by the polyolefin polymers.
Although preferred embodiments of the invention have been described using specific terms, devices, and methods, such description is for illustrative purposes only. The words used are words of description rather than of limitation. It is to be understood that changes and variations may be made by those of ordinary skill in the art without departing from the spirit or the scope of the present invention, which is set forth in the following claims. In addition, it should be understood that aspects of the various embodiments may be interchanged, both in whole or in part. Therefore, the spirit and scope of the appended claims should not be limited to the description of the preferred versions contained therein.
Number | Date | Country | Kind |
---|---|---|---|
PCT/US2004/014305 | May 2004 | US | national |
This application claims the benefit of U.S. application Ser. No. 10/431,955 filed on May 8, 2003, and PCT Application PCT/US2004/014305 filed on May 7, 2004, both of which are incorporated herein by reference.
Number | Date | Country | |
---|---|---|---|
Parent | 10431955 | May 2003 | US |
Child | 11895457 | Aug 2007 | US |