Patent Application
20080285422
1. Field of the Invention
The present invention relates to an optical pickup apparatus to record and/or reproduce information by a beam of light emitted from a light source, and an objective lens for the optical pickup apparatus.
2. Description of Related Art
Recently, the recording density of the optical pickup apparatuses have been getting higher, and thus numeric aperture of the optical elements such as objective lenses have been getting larger and wavelength of the laser light has been getting shorter. Larger numeric aperture causes larger curvature of an objective lens, which results larger incident angle of a laser beam at a peripheral part of the objective lens. For example, an optical pick up apparatus using laser light of nm wavelength has an objective lens of numeric aperture as large as 0.6 to 0.9, and the largest incident angle of the laser light to the objective lens is 50 to 70°.
Since larger incident angle causes larger reflection of laser light at a peripheral part of an objective lens, the amount of transmitted light at the peripheral part decreases, and thereby a signal-to-noise ratio (S/N ratio) in signal reproduction decreases. To cope with this problem, recent objective lenses are provided with antireflection coating to expand low-reflection band, so as to reduce the decrease of transmittance at peripheral parts of the objective lenses (for example, see Japanese patent application publication laid-open No. H10-160906).
However, multi-layered antireflection coating to achieve more effective expansion of the low-reflection band results higher production cost.
It is one of objects of the present invention to provide an objective lens having improved total transmittance while the production cost thereof is kept low, and to provide an optical pickup apparatus provided with the objective lens.
In order to solve the above problem, according to a first aspect of the present invention, an objective lens for an optical pickup apparatus which records and/or reproduces information with a light beam emitted from a light source, comprises: a substrate; and an anti-reflection coating comprising at least one layer, formed on a surface of the substrate at a side of the light source, wherein a refractive index of the anti-reflection coating at a peripheral part where an outer edge of an effective light beam transmits is smaller than a refractive index of the anti-reflection coating at a center part where a light beam on an optical axis transmits.
By the above feature, it becomes possible to suppress reflection at the peripheral part of the objective lens having large curvature while the number of layers of the antireflection coating and the resulting production cost are kept as low as before.
According to a second aspect of the invention, an objective lens for an optical pickup apparatus which records and/or reproduces information with a light beam emitted from a light source, comprises: a substrate; and an anti-reflection coating comprising at least one layer, formed on a surface of the substrate at a side of the light source, wherein a packing density of the anti-reflection coating at a peripheral part where an outer edge of an effective light beam transmits is smaller than a packing density of the anti-reflection coating at a center part where a light beam on an optical axis transmits.
Preferably, a wavelength X of the light beam emitted from the light source is within a range of 350 nm≦λ≦450 nm.
Preferably, the objective lens has a numeral aperture of 0.6 to 0.9 inclusive.
Preferably, the objective lens has a numeral aperture of 0.8 to 0.9 inclusive.
Preferably, an angle between a normal line of a surface at the peripheral part and the optical axis is 48° to 72° inclusive.
Preferably, the angle between the normal line of the surface at the peripheral part and the optical axis is 60° to 72° inclusive.
Preferably, the anti-reflection coating is composed of one to three layers.
Preferably, at least one layer of the anti-reflection coating is formed of a low-refractive index material having a refractive index n of 1.3≦n≦1.5 for a light of 500 nm wavelength.
Preferably, the low-refractive index material is SiO2-based material.
Preferably, the refractive index at the peripheral part is 0.8 to 0.98 times inclusive of the refractive index at the center part.
Preferably, the refractive index at the peripheral part is 0.85 to 0.92 times inclusive of the refractive index at the center part.
Preferably, the packing density at the peripheral part is 0.38 to 0.94 times inclusive of the packing density at the center part.
Preferably, the packing density at the peripheral part is 0.53 to 0.75 times inclusive of the packing density at the center part.
Preferably, the substrate is formed of a plastic material.
According to a third aspect of the present invention, an optical pickup apparatus comprises the objective lens of the first or second aspect.
The above and other objects, advantages and features of the present invention will become more fully understood from the detailed description given hereinbelow and the appended drawings which are given by way of illustration only, and thus are not intended as a definition of the limits of the present invention, and wherein:
Hereinafter, embodiments of the present invention will be described with reference to the drawings.
As shown in this figure, the optical pickup apparatus 1 comprises a laser diode 1, and is to record information onto an information recording surface A of an information recording medium R and to read and reproduce information recorded on the information recording surface A. As the information recording medium R, a BD (Blu-ray disk), HD-DVD or the like can be given. In the present embodiment, the information recording medium R is a BD. Further, the information recording medium R has a protective layer of 0.1 mm thickness.
The laser diode 11 is a laser source of the present embodiment, and emits laser light of wavelength λ1 (350≦λ1≦450 nm) at the time of recording/reproducing information with the information recording medium R. In the embodiment, wavelength λ1 is 405 nm.
A collimator lens 12, a polarization beam splitter 13, a quarter wavelength plate 14, and an objective lens 15 are disposed in alignment in a direction from bottom to top in
Accompanied with the polarization beam splitter 13, a convex lens 16 and an optical detector 17 are mounted in alignment on the right side in
Next, operation and action of the optical pickup apparatus 1 will be briefly described.
At the time of recording information onto the information recording medium R and reproducing information in the information recording medium R, the laser diode 11 emits laser light of wavelength λ1. The laser light is firstly converted into parallel light by the collimator lens 12, and thereafter the polarization beam splitter 13 lets only P-polarization component of the light transmit so as to convert the light into linear polarized light (P-polarized light).
Next, this P-polarized laser light is converted into right-hand circularly polarized light by the quarter wavelength plate 14, and thereafter is focused by the objective lens 15, enters on the information recording surface A of the information recording medium R at various incident angles, and forms a focused spot. The objective lens 15 also performs focusing and tracking by means of the two-dimensional actuator disposed around the lens.
Next, the laser light, which is circularly polarized light and forms the focused spot, is reflected on the information recording surface A of the information recording medium R and thereby converted into left-hand circularly polarized light. The reflected laser light then passes through the objective lens 15 again, and is converted into linear polarized light composed of a S-polarized component only (S-polarized light). Next, this S-polarized laser light is totally reflected by the polarization beam splitter 13, and is focused to the optical detector 17 by the convex lens 16. The information in the information recording medium R is reproduced by using output signal of the optical detector 17.
Next, configuration of the objective lens 15 will be described.
The objective lens 15 is an optical element of the present invention, and as shown in
Two optical surfaces of the substrate 150 of the present embodiment are both aspherical. The optical surfaces may have diffraction structures known in the art.
The substrate 150 is formed of plastic material having superior resistance to short wavelength blue-violet laser and superior heat resistance. For such plastic material, a resin composition comprising a copolymer resin of α-olefin and cyclic olefin and a light-resistance stabilizer, or the like can be given.
Anti-reflection coating is provided on a surface of the substrate 150 to form an optically functional surface, at a side of the light source, i.e. at an incident side in
The anti-reflection coating 151 is formed such that a ratio Rn=nD/nC fulfills Rn<1.0, where nD is refractive index at a peripheral part D where an outer edge of an effective light beam transmits, and nC is refractive index at a center part C where a light beam on the light axis transmits. The peripheral part D locates at a position corresponding to an open angle of light axis and light beam which define NA.
The anti-reflection coating 151 is formed such that a ratio RP=PD/PC fulfills RP<1.0, where PD is packing density at the peripheral part D, and PC is packing density at the center part C.
The packing density is a substantial volume of a coating divided by a sum of the substantial volume and pore volume of the coating, and for example, is calculated from the following formula by utilizing absorption of vapor at wavelength of 2.97 μm, as described in “Optical coating and coating technique” by Li Zheng zhong, translated by Ulvac, Inc. and issued by Agne Gijutsu Center Co., Ltd. which is incorporated by reference.
where: P is packing density; T0 is transmittance when vapor is fully absorbed in vacuum; T is transmittance when vapor is fully absorbed in air; αW is absorption coefficient of water (=1.27×10−4 cm−1) ; and df is thickness of coating (cm).
At least one layer of the anti-reflection coating 151 is formed of low refractive index material having refractive index n for light of 500 nm wavelength of 1.3≦n≦1.55.
It is particularly preferable the low refractive index material is SiO2-based material.
Such anti-reflection coating 151 may be formed by means of vapor deposition, sputtering, CVD, application or the like. In the present embodiment, vacuum vapor deposition is employed. The method of the employed vapor deposition will be summarized. The objective lens 15 of the invention is not limited to the one made by the following method.
At the time of vapor deposition, a plurality of substrates 150 are attached to the rotation plate 23 in a manner that the surfaces to be subjected to deposition face downward. While the substrates 150 are rotated by the rotation shaft 22 via the rotation plate 23, vapor deposition material is evaporated from the crucible 24 to deposit onto the deposited surfaces of the substrates 150.
According to the above-described vacuum vapor deposition device 2, refractive index n at the peripheral part D of the anti-reflection coating 151 to be formed can be controllably changed by changing an angle θ1 of a line between a peripheral part G of the substrate 150, which corresponds to the peripheral part D of the anti-reflection coating 151, and a tip F of the plate-shaped member 25A with respect to the optical axis of the parallel light (see
Table 1 shows refractive indexes n at the center part C and peripheral part D and a ratio of the peripheral part D to the central part C with respect to each of three values of θ1 in the case of SiO2 single layer. According to the table, refractive index n at the peripheral part D can be increased by increasing θ1 while leaving refractive index n at the central part C to be constant.
An undercoat layer known in the art may be intermediated between the substrate 150 and anti-reflection coating 151 to improve adhesion of the anti-reflection coating 151 onto the substrate 150. Further, the anti-reflection coating 151 may be provided with an antifouling layer, a water-shedding layer, and an antistatic layer in the surface side thereof to prevent adhesion of dust etc. due to static electricity.
Hereinafter, the present invention will be described in more detail by giving examples and comparative examples.
<Configuration of Objective Lens>
As for the examples of the objective lens 15 of the present invention, five types of the lens substrate 150 each having different NA as shown in the following table 2 were prepared and the anti-reflection coating 151 composed of three layers as shown in Table 3 was formed on an incident surface of each substrate. As for shape of the substrate 150, one known in the art was employed.
As for the anti-reflection coating 151, five types of examples which have ratio Rn of refractive index n at the peripheral part D to refractive index n at the center part C within a range from 0.8 to 0.98, and additionally, one comparative example of Rn=1 known in the art, thus six types in total, were formed (see Table 4).
The “plane angle” in Table 2 represents an angle θ in
The coating was formed by vacuum vapor deposition. In the present example, precision vacuum thin film deposition device ACE-1350 produced by Shincron Co., Ltd. was used as the vacuum vapor deposition device 2.
<Evaluation of Transmittance>
Each of the examples of the objective lens 15, where the lens substrate 150 shown in Table 2 was coated with the anti-reflection coating 151 shown in Table 3 at the incident surface thereof, was measured for transmittance of overall lens. The result of the measurement is shown in an area framed by bold lines of Table 4. In the table, the results are associated with the ratio Rn of the refractive index n at the peripheral part D to the refractive index n at the center part C and the corresponding ratio RP of the packing density P.
According to the measurement result shown in Table 4, substrates (1) to (4) (NA=0.6 to 0.9) with inventive coating have transmittances larger than those with comparative coating. In particular, substrates (1) to (3) (NA=0.8 to 0.9) show much larger transmittances. These ranges of NA correspond to plane angle ranges of 48 to 72° and 60 to 72° respectively.
Further, substrates (1) to (4) (NA=0.6 to 0.9) show equal or larger transmittance within a range of Rn=0.8 to 0.98 (RP=0.38 to 0.94) compared to the comparative example of Rn=1.0. In particular, samples having Rn=0.85 to 0.92 (RP=0.53 to 0.75) show much larger transmittances.
As for the examples of the objective lens 15 of the present invention, five types of the lens substrate 150 each having different NA as shown in table 2 were prepared and the anti-reflection coating 151 composed of two layers as shown in Table 5 was formed on an incident surface of each substrate.
The other conditions were as same as example 1.
<Evaluation of Transmittance>
Each of the examples of the objective lens 15, where the lens substrate 150 shown in Table 2 was coated with the anti-reflection coating 151 shown in Table 5 at the incident surface thereof, was measured for transmittance of overall lens. The result of the measurement is shown in an area framed by bold lines of Table 6. In the table, the results are associated with the ratio Rn of the refractive index n at the peripheral part D to the refractive index n at the center part C and the corresponding ratio RP of the packing density P.
According to the measurement result shown in Table 6, substrates (1) to (4) (NA=0.6 to 0.9) with inventive coating have transmittances almost larger than those with comparative coating. In particular, substrates (1) to (3) (NA=0.8 to 0.9) show much larger transmittances. These ranges of NA correspond to plane angle ranges of 48 to 72° and 60 to 72° respectively.
Further, substrates (1) to (4) (NA=0.6 to 0.9) show larger transmittance almost within an entire range of Rn=0.8 to 0.98 (RP=0.38 to 0.94) than the comparative example of Rn=1.0. In particular, samples having Rn=0.85 to 0.92 (RP=0.53 to 0.75) show completely larger transmittances.
Comparing the measurement result of example 2 with that of example 1, example 1 shows broader range of NA, Rn or RP where transmittance of the sample is larger than the comparative example of Rn=1.0. Further, example 1 shows larger difference of refractive index to the comparative example of Rn=1.0. Therefore, the anti-reflection coating 151 of example 1 composed of three layers is superior to the anti-reflection coating 151 of example 2 composed of two layers in the point of the higher transmittance.
As described above, according to the objective lens 15 of the present invention, the ratio Rn of the anti-reflection coating, which is a ratio of the refractive index n at the peripheral part D to the refractive index n at the center part C, is less than 1.0. Thus, it is possible to suppress effectively increase of reflectance of light beam at the peripheral part D so as to improve the transmittance. This advantage may be explained by the following reasons.
General anti-reflection coating has characteristics of reflectance as shown in
On the other hand, as show in
The entire disclosure of Japanese Patent Application No. 2007-127954 filed on May 14, 2007 including description, claims, drawings, and abstract are incorporated herein by reference.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2007-127954 | May 2007 | JP | national |