Patent Application
20210257526
Semiconductor devices are found in nearly every piece of consumer and commercial electronics made today. Their wide-spanning uses include single discrete devices such as diodes and transistors, as well as integrated circuits which can include many millions of semiconductor devices interconnected on a single semiconductor substrate. The discovery of new materials for use in semiconductor device manufacturing, as well as the development of new semiconductor device manufacturing methods, continues to improve the efficiency of these devices, as well as to expand the already broad range of their practical application.
Light emitting diodes (LEDs) are one example of a semiconductor device widely used in consumer and commercial applications. LEDs contain several semiconductor materials, including a p-doped semiconductor material, an n-doped semiconductor material, and a junction between the two materials. As in a normal diode, current flows easily from the p-side, or anode, to the n-side, or cathode, but not in the reverse direction. When a voltage is applied with the correct polarity to the semiconductor structure, the junction is forward-biased, and the charge-carriers, electrons and holes, flow into the junction. When an electron meets a hole as it moves out of the n-doped region and into the junction, it falls to a lower energy level, and releases energy in the form of emitted light. The wavelength of the light emitted, and therefore its color, depends on the band gap energy of the materials forming the junction. Sometimes the n- and p-doped semiconductor material can include multiple layers of different semiconductor materials. Sometimes an active layer is sandwiched between the n-doped semiconductor material and the p-doped semiconductor material, allowing further control over both the wavelength of the photons emitted (e.g. color) and the number of photons emitted (e.g. brightness) when electrons move through the junction. Active layers can themselves include several layers of various semiconductor materials, and sometimes can contain several light emitting layers. LEDs with active layers comprising more than one light emitting layer are commonly called either multi-(MW) LEDs or multiple quantum well (MQW) LEDs. In contrast, LEDs having a single light emitting layer in the active layer are commonly called either double heterostructure (DH) LEDs, or single quantum well (SQW) LEDs.
In order to utilize a semiconductor structure as a semiconductor device, electricity must be able to get to the structure; e.g., one must be able to apply a voltage across the structure. Since electrical potential and corresponding electrical current is generally transferred through a metallic medium, a connection between the metallic medium and the semiconductor structure is necessary to enable the application of voltage to the structure. Contacts are regions of a semiconductor structure that have been prepared to act as connections between the semiconductor structure and a metallic medium. Contacts that have low resistance, that are stable at various temperatures over time, and also that are stable when subjected to various electrical conditions over time, are critical for the performance and reliability of semiconductor devices. Other desirable properties include smooth surface morphology, simple manufacturing, high production yield, good corrosion resistance, and good adhesion to semiconductors. An ideal contact has no effect on the performance of the semiconductor structure, meaning that it has zero resistance and delivers the required current with no voltage drop between the semiconductor structure and the metal, and also meaning that the relationship between the voltage applied to the contact and the current generated in the structure is perfectly linear. In practice, a contact generally must have some resistance, but contacts that provide an approximately linear voltage-current relationship and that exhibit low resistance are desirable. These are referred to as ohmic contacts.
When two solids are placed in contact with one another, unless each solid has the same electrochemical potential, also called the work function, electrons will flow from one solid to the other until equilibrium is reached, forming a potential between the two solids, called the contact potential. A contact potential can give insulating properties to the connection between the two solids, and is the underlying cause of phenomena such as rectification in diodes. The contact potential causes the voltage-current relationship to be non-linear, and thus the connection between the two solids departs from ideal ohmic contact properties. In general, to create ohmic contacts with the lowest resistances and with the most linear and symmetric voltage-current relationship, materials with a work function near to the work function of the particular semiconductor material on which the ohmic contact is to be formed are sought.
Traditional methods of fabricating ohmic contacts on semiconductor structures, including structures that are to become LEDs, involve deposition of one or more various materials on the structure, such that the one or more materials only touch a specific part of the semiconductor structure. Generally, the materials as deposited on the semiconductor do not yet form an ohmic contact, because relationship between the work function of each material is such that undesirable contact potentials are formed. Therefore, the deposition step is followed by an annealing process to chemically alter the materials, which can correspondingly alter their work functions. During the anneal, diffusion of the atoms of the deposited lavers and the contiguous portion of the semiconductor structure occurs, causing the materials to mix to varying degrees, essentially making the deposited layers part of the semiconductor structure while still allowing them to retain their basic physical shape. By allowing the relocation of atoms, annealing enables the formation of new chemical species with different properties than the originally deposited layers or the contiguous portion of the structure, and preferably results in the newly formed portion of the semiconductor structure having the desired ohmic contact properties. While annealing is generally essential for formation of an ohmic contact, high temperatures can introduce thermal defects into the semiconductor structure, leading to negative effects in the resulting semiconductor device, such as poor performance and poor operating lifespan. Additionally, high temperatures can cause undesirable changes in the surface characteristics (surface morphology) of the contact, such as beading and mottling, tending to make an electrical connection to the ohmic contact more difficult and less efficient. The negative effects of high temperature are compounded by a longer exposure to those temperatures. Therefore, compositions and methods for formation of ohmic contacts on semiconductor structures that can handle shorter anneals and that don't require high temperature anneals are sought.
For example, a common semiconductor used in LED semiconductor devices, and in other semiconductor devices, is gallium nitride (GaN), frequently found as layers of n-doped and/or p-doped material in the semiconductor structure. An ohmic contact is often sought to be formed with a specific layer of GaN, for example n-doped GaN (n-GaN). A stable metal-n-GaN system is imperative for the achievement of n-GaN-containing semiconductor devices, including LEDs. Contacts made by depositing titanium (Ti) followed by aluminum (Al) on the semiconductor structure are the most popular in n-GaN-containing semiconductor devices (Ti/Al-bilayer). However, the Ti/Al-bilayer system is easily prone to converting to an undesirable high-resistance contact after thermal annealing at an intermediate temperature range. This could be due to the formation of an aluminum oxide (Al2O3) on the Al, leading to an increase in the contact resistance. This change can be due to the formation of titanium nitride (TiN) during the annealing process. The Ti/Al-bilayer system can convent to an ohmic contact and exhibit a specific contact resistance that can be about 10−5˜10−6 Ωcm− when annealed at higher temperatures. However, annealing at high temperatures can cause degradation in semiconductor device performance and reliability because Al has a low melting point (˜660 degrees C.) and tends to ball up during annealing. Thus, the surface morphology of most Ti/Al-bilayer based contacts is quite rough. In addition, application of high temperature to the semiconductor structure introduces thermal defects, which also can cause degradation in the performance of the semiconductor device.
In the drawings, which are not necessarily drawn to scale, like numerals can describe substantially similar components throughout the several views. The figures illustrate generally, by way of example, but not by way of limitation, various embodiments and examples discussed in the present document.
The present invention provides a composition for formation of an ohmic contact on a semiconductor structure. The composition includes a TiAlxNy material. The TiAlxNy material is at least partially contiguous with the semiconductor structure. The semiconductor structure includes at least one semiconductor material. The variables x and y do not simultaneously equal zero. When the variable y equals zero, x does not equal one.
The present invention provides a method for formation of an ohmic contact on a semiconductor structure. The method includes providing a semiconductor structure. The semiconductor structure includes an n-doped GaN material. The method also includes depositing a TiAlxNy material. The TiAlxNy material is deposited contiguous to at least part of the n-doped GaN material. The TiAlxNy material is approximately 200 to 2000 angstroms thick. The variables x and y do not simultaneously equal zero. When the variable y equals zero, the variable x does not equal one. The method also includes annealing the semiconductor structure and the TiAlxNy material. The annealing takes place at or less than approximately 660 to 880 degrees C. The annealing takes place for a duration of approximately 30 to 60 seconds.
The present invention provides a method for formation of an ohmic contact on a semiconductor structure. The method includes providing a semiconductor structure. The semiconductor structure includes an n-doped GaN material. The method includes depositing a TiAlxNy material. The TiAlxN), material is deposited contiguous to at least part of the n-doped GaN material. the TiAlxNy material is approximately 50 to 200 angstroms thick. The variables x and y do not simultaneously equal zero. When the variable y equals zero, the variable x does not equal one. The method also includes depositing an aluminum material. The aluminum material is deposited contiguous to at least part of the TiAlxNy material. The aluminum material is deposited such that the TiAlx material is between the aluminum material and the n-doped GaN material. The aluminum material is approximately 1000 angstroms thick. The method also includes annealing the semiconductor structure and the TiAlxNy material and the aluminum material. The annealing takes place at or less than approximately 660 degrees C. The annealing takes place for a duration of approximately 30 to 60 seconds.
The present invention provides in various embodiments a composition and method for formation of ohmic contacts on a semiconductor structure. In various embodiments, the composition includes TiAlxAy material. The TiAlxNy material is at least partially contiguous with the semiconductor structure. The TiAlxNv can be TiAl3. The composition can include aluminum. The aluminum can be contiguous to at least part of the TiAlxNy, such that the TiAlxNy is between the aluminum and the semiconductor structure. The method includes annealing the composition to form an ohmic contact on the semiconductor structure.
The invention relates to a composition and method for formation of an ohmic contact on a semiconductor structure. When describing the composition and the method, the following terms have the following meanings, unless otherwise indicated.
As used herein, the term “contiguity” refers to an area of physical touching or contacting.
As used herein, the term “contiguous” refers to physically touching or in contact with, to any degree.
As used herein, the term “ohmic contact” refers to a contact that provides an approximately linear voltage-current relationship and that exhibits low resistance. An ohmic contact can be used for connecting an electrical potential to a semiconductor structure or semiconductor device. An ohmic contact can be considered to be on a semiconductor structure, and it can also be considered to be part of a semiconductor structure.
As used herein, the term “semiconductor device” refers to a semiconductor structure that is ready for its intended use, such as ready for use as an electronics component, and also such as ready to function as a component in an integrated circuit. The term can refer to, but is not limited to, a state of manufacturing wherein all layers of semiconductor material necessary for the intended operation of the semiconductor device are in place and have been annealed as necessary, necessary passivation has been performed, and the necessary contacts have been formed on the semiconductor structure to enable the application of a desired electrical potential across the structure. The term can refer to multiple semiconductor devices, and to multiple semiconductor structures ready for their intended use.
As used herein, the term “semiconductor material” refers to a material that includes but need not be exclusively a chemical compound or chemical compounds, said chemical compound or compounds when pure having an electrical conductivity between that of a conductor and an insulator. Semiconductor materials can be undoped, n-doped, or p-doped, and include but are not limited to, in their pre- or post-doped state, at least one of: GaN, InGaN, AlGaN, AlGaInN, InN, GaAs, AlGaAs, AlGaAs, GaAsP, AlGaInP, GaP, AlGaP, ZnSe, SiC, Si, diamond, BN, AlN, MgO, SiO, ZnO, LiAlO2, SiC, Ge, InAs, InAt, InP, C, Ge, SiGe, AlSb, AlAs, AlP, BP, BAs, GaSb, InSb, AlzGa1-zAs, InGaAs, InzGa1-zAs, InGaP, AlInAs, AlInSb, GaAsN, AlGaP, AlGaP, InAsSb, InGaSb, AlGaAsP, AlInAsP, AlGaAsN, InGaAsN, InAlAsN, GaAlAsN, GaAsSbN, GaInNAsSb, or GaInAsSbP.
As used herein, the term “semiconductor structure” refers to but is not limited to at least one layer of semiconductor material, but can also refer to multiple layers of semiconductor material, that is or are to become a semiconductor device. The state of becoming a semiconductor device can occur once a manufacturing process is complete. The term “semiconductor structure” can also refer to one or more semiconductor devices at an intermediate stage of manufacture. The term can refer to but is not limited to a layer or layers of semiconductor material that is or are to become multiple semiconductor devices. The term also encompasses a structure or structures that is or are to become a semiconductor device when the structure or structures include at least one layer of semiconductor material, or multiple layers of semiconductor material, and the structure or structures also include layers of other materials contiguous with at least one layer of semiconductor material for the purpose of formation of an ohmic contact.
As used herein, the chemical formula “TiAlxNy” refers to but is not limited to a compound or compounds with a molar ratio of titanium (Ti to aluminum (Al) to nitrogen (N) of 1:x:y, where x and y can each independently equal zero. The chemical formula can also additionally or alternatively refer to, but is not limited to, a mixture of the elements titanium, aluminum, and nitrogen with a molar ratio of Ti to Al to N of 1:x:y, wherein the atoms of titanium, aluminum, and nitrogen are not bonded together as a compound or compounds with a chemical formula of TiAlxNy, but rather exist as a homogenous, semi-:homogenous, or heterogenous mixture; in this case, the atoms of titanium, aluminum, and/or nitrogen can be but are not necessarily chemically bonded together as a compound or compounds, the compound or compounds of which are not necessarily the same, the compound or compounds of which can but do not necessarily contain all three of these elements in the same proportions, the compound or compounds of which can be but are not necessarily intentionally formed, and the compound or compounds of which can but do not necessarily exist for transient or permanent duration. In some embodiments, x and additionally or alternatively y are not of a consistent value throughout the TiAlxNy material. Thus, in some embodiments, in some locations of the TiAlxNy material versus other locations of the TiAlxNy material, x or y can have values that fall within ranges rather than have values that are exact. In some embodiments for which values of x or y are specified, the specification of value not only encompasses embodiments where x or y are consistently equal to the specified values throughout a material, but also encompasses embodiments where the value of x or y averages to about the specified values as the composition of the TiAlxNy material is sampled throughout its entirety. Correspondingly, in embodiments for which a specific pair of values for x and y are forbidden, embodiments are not forbidden in which samples of TiAlxNy with the forbidden pair of values can be found within a TiAlxNy material, but rather embodiments are only forbidden for which a TiAlxNy material has the forbidden pair of values for x and y throughout the material consistently, or for which a TiAlxNy material has the forbidden pair of values of x and y as average values of x and y as the composition of the TiAlxNy material is sampled throughout its entirety.
Reference will now be made in detail to certain embodiments of the invention, examples of which are illustrated in the accompanying structures and formulas. While the invention will be described in conjunction with the enumerated claims, it will be understood that they are not intended to limit the invention to those claims. On the contrary, the invention is intended to cover all alternatives, modifications, and equivalents, which can be included within the scope of the invention as defined by the claims.
References in the specification to “one embodiment,” “an embodiment,” “an example embodiment,” etc., indicate that the embodiment described can include a particular feature, structure, or characteristic, but every embodiment can not necessarily include the particular feature, structure, or characteristic. Moreover, such phrases are not necessarily referring to the same embodiment. Further, when a particular feature, structure, or characteristic is described in connection with an embodiment it is submitted that it is within the knowledge of one skilled in the art to affect such feature, structure, or characteristic in connection with other embodiments whether or not explicitly described.
In some embodiments the present invention provides a composition for formation of an ohmic contact on a semiconductor structure, comprising TiAlxNy material at least partially contiguous with the semiconductor structure, wherein x and y do not simultaneously equal zero. Some embodiments of the present invention can be semiconductor structures that include at least one semiconductor material. Some embodiments of the present invention can be semiconductor structures that are to become one or more semiconductor devices for use in circuits, including integrated circuits, and for any application for a semiconductor device. In some embodiments of the present invention, the types of semiconductor devices which the claimed semiconductor structures are to become are unlimited, and include but are not limited to: any transistor or transistors including MOSFETs (metal oxide semiconductor field effect transistors), any MOS device, any diode (a device which, in general, only conducts current in one direction) including all types of LEDs, integrated circuits (miniaturized electronic circuits containing multiple semiconductor devices), microprocessors, and memory including RAM (random access memory) and ROM (read only memory) memory.
In some embodiments of the present invention, the TiAlxNy and alternatively or additionally the semiconductor structure can contain some chemical impurities, such that in those embodiments the TiAlxNy can or can not contain some chemical elements that are not Ti, Al, or N, and the semiconductor structure can or can not contain some chemical elements that are not semiconductor materials, and the aluminum (if present) can or can not contain some chemical elements that are not aluminum. In these embodiments, the presence of the impurities need not be specified in order to refer to the TiAlxNy or to the semiconductor material that is at least part of the semiconductor structure or to the aluminum (if present). In these embodiments, the level of impurities present is not sufficient to prevent the intended formation of an ohmic contact or contacts, nor is it sufficient to prevent the operation of the semiconductor device or devices into which the semiconductor structure is to be formed. In some embodiments, the presence of certain compounds in the semiconductor material that, can be called chemical impurities is intended and sometimes can cause the semiconductor material to be doped, in which cases generally the presence of impurities enables the intended operation of the semiconductor device.
Some embodiments of the present invention include but are not limited to compositions and methods for the formation of multiple contacts, and are not restricted to compositions and methods for the formation of one contact or for the formation of one contact at a time. Thus, some embodiments of the present invention include compositions and methods for the formation of multiple contacts, and additionally embodiments of the present invention encompass compositions and methods for the formation of multiple contacts at one time.
One embodiment of the present invention includes compositions and methods for the formation of one or more ohmic contacts that extend across a semiconductor structure, which can then, after annealing, and sometimes after other steps, be cut or chopped or broken or sliced into many separate semiconductor structures or semiconductor devices. In
Some embodiments of the present invention encompass any degree of contiguity between the semiconductor structure and the TiAlxNy, including contiguity of only a few atoms, or contiguity of the majority of the surfaces of semiconductor structure and the TiAlxNy. Some embodiments of the present invention encompass contiguity that is between the TiAlxNy and one specific portion of semiconductor material that is at least part of the semiconductor structure; some embodiments of the present invention additionally or alternatively encompass contiguity between the TiAlxNy and multiple specific portions of semiconductor material that is at least part of the semiconductor structure.
One embodiment of the invention is a composition for formation of an ohmic contact on a semiconductor structure, comprising a TiAlxNy material at least partially contiguous with the semiconductor structure, wherein x and y do not simultaneously equal zero. In some embodiments, when y equals zero, x does not equal one. In some embodiments, the contiguity between the TiAlxNy material and the semiconductor structure includes at least partial contiguity with n-doped GaN. In some embodiments, the contiguity between the TiAlxNy material and the semiconductor structure includes at least partial contiguity with a p-doped GaN. In some embodiments, the contiguity between the TiAlxNy material and the semiconductor structure includes at least partial contiguity with at least one portion of the semiconductor structure. In some embodiments of the present invention, the contiguity between the TiAlxNy material and the semiconductor structure includes at least partial contiguity with more than one portion of the semiconductor structure.
An embodiment of the invention is a composition for formation of an ohmic contact on a semiconductor structure, comprising a TiAlxNy material at least partially contiguous with the semiconductor structure, wherein the contiguity between the TiAlxNy material and the semiconductor structure includes at least partial contiguity with at least one portion of semiconductor material which can be undoped, n-doped, or p-doped, wherein the undoped, n-doped, or p-doped material includes in either or both its pre- or post-doped state at least one of: GaN, InGaN, AlGaN, AlGaInN, InN, GaAs, AlGaAs, AlGaAs, GaAsP, AlGaInP, GaP, AlGaP, ZnSe, SiC, Si, diamond, BN, AlN, MgO, SiO, ZnO, LiAlO2, SiC, Ge, InAs, InAt, InP, C, Ge, SiGe AlSb, AlAs, AlP, BP, BAs, GaSb, InSb, AlzGa1-zAs, InGaAs, InzGa1-zAs, InGaP, AlInAs, AlInSb, GaAsN, AlGaP, AlGaP, InAsSb, InGaSb, AlGaAsP, AlInAsP, AlGaAsN, InGaAsN, InAlAsN, GaAlAsN, GaAsSbN, GaInNAsSb, or GaInAsSbP.
Another embodiment of the invention is a composition for formation of an ohmic contact on a semiconductor structure, comprising TiAlxNy material at least partially contiguous with the semiconductor structure. In some embodiments, the TiAlxNy material is at least partially contiguous with the semiconductor structure prior to or during at least part of an annealing process. In some embodiments, the TiAlxNy material is added using at least one of the following: atomic layer deposition, physical vapor deposition (PVD), or chemical vapor deposition (CVD).
In one embodiment, the present invention provides a composition for formation of an ohmic contact on a semiconductor structure, comprising a TiAlxNy material at least partially contiguous with the semiconductor structure, wherein x is equal to about 3 and y is equal to about zero. In another embodiment, the TiAl3 material is between approximately 5 and 4000 angstroms thick. In another embodiment, the TiAl3 material is between approximately 50 and 4000 angstroms thick. In another embodiment, the TiAl3 material is between approximately 50 and 2000 angstroms thick. In another embodiment, the TiAl3 material is between approximately 100 and 1000 angstroms thick. In another embodiment, the TiAl3 is material approximately 200 angstroms thick. In another embodiment, the TiAl3 material is approximately 150 angstroms thick. In another embodiment, the TiAl3 material is approximately 100 angstroms thick.
In one embodiment, the present invention provides a composition for formation of an ohmic contact on a semiconductor structure, comprising Ti material at least partially contiguous with the semiconductor structure, wherein the composition further includes an aluminum material, wherein the aluminum material is contiguous to at least part of the TiAlxNy material. In a related embodiment, the TiAlxNy is between the semiconductor structure and the aluminum. In another related embodiment, the aluminum is added using at least one of the following: atomic layer deposition, physical vapor deposition (PVD), or chemical vapor deposition (CVD). In another related embodiment, the aluminum is between about 5 and 4000 angstroms thick. In another related embodiment, the aluminum is between about 250 and 2000 angstroms thick. In another related embodiment, the aluminum is between about 750 and 1250 angstroms thick. In another related embodiment, the aluminum is approximately 1000 angstroms thick.
In some embodiments the present invention provides a composition for formation of an ohmic contact on a semiconductor structure, comprising TiAlxNy material at least partially contiguous with the semiconductor structure, wherein the TiAlxNy material is between about 5 and 4000 angstroms thick. In another embodiment, the TiAlxNy material is between approximately 50 and 4000 angstroms thick. In another embodiment, the TiAlxNy is between approximately 50 and 2000 angstroms thick. In another embodiment, the TiAlxNy material is between approximately 100 and 1000 angstroms thick. In another embodiment, the TiAlxNy material is approximately 200 angstroms thick. In another embodiment, the TiAlxNy material is approximately 150 angstroms thick. In another embodiment, the TiAlxNy material is approximately 100 angstroms thick
Another embodiment of the present invention provides a composition for formation of an ohmic contact on a semiconductor structure, comprising a TiAlxNy material at least partially contiguous with the semiconductor structure, wherein x is between about zero and 10. In another embodiment, x is between about 1 and 10. In another embodiment, x is between about zero and 5. In another embodiment, x is between about zero and 1. In another embodiment, x is between zero and 0.5.
In some embodiments the present invention provides a composition for formation of an ohmic contact on a semiconductor structure, comprising a TiAlxNy material at least partially contiguous with the semiconductor structure, wherein y is between about zero and 10. In another embodiment, y is between about zero and 5. In another embodiment, y is between about zero and 1. In another embodiment, y is between about zero and 0.5.
Embodiments of the present invention include a method for formation of an ohmic contact on a semiconductor structure, comprising the step of annealing a composition for formation of an ohmic contact on a semiconductor structure, the composition comprising a TiAlxNy material at least partially contiguous with the semiconductor structure. In some embodiments, the semiconductor structure can be annealed at a temperature of less than 500 degrees C. to 1500 degrees C.; at less than about 1000 to 1500 degrees C.; at about 800 degrees C.; at less than about 660 degrees C.; or at less than about 500 degrees C.
Embodiments of the present invention include a method for formation of an ohmic contact on a semiconductor structure, comprising the step of annealing a composition for formation of an ohmic contact on a semiconductor structure, the composition comprising a TiAlxNy, material at least partially contiguous with the semiconductor structure. In some embodiments, the semiconductor structure can be annealed for approximately 0.001 to 10 minutes; for approximately 5 to 10 minutes; for approximately 1 to 5 minutes; for approximately 1 minute; for approximately 30 to 60 seconds; or for approximately 0.001 to 1 minute.
In some embodiments the present invention provides a method for formation of an ohmic contact on a semiconductor structure, comprising the steps of: providing a semiconductor structure, wherein the semiconductor structure includes an n-doped GaN material; depositing a TiAlxNy material contiguous to at least part of the n-doped GaN, wherein x and y do not simultaneously equal zero; and, annealing the semiconductor structure and the TiAlxNy. In a related embodiment, x is equal to about 3 and y is equal to about zero. In another related embodiment, the TiAlxNy material is about 200-2000 angstroms thick. In another related embodiment, the TiAlxNy material is about 200 angstroms thick. In another related embodiment, the annealing process takes place at about 800 degrees C. In another related embodiment, the annealing process takes place at less than 660 degrees C. In another related embodiment, the annealing process takes place for approximately 0.1 to 10 minutes. 0.1n another related embodiment, the annealing process takes place for approximately 30 to 60 seconds.
Another embodiment of the present invention provides a method for formation of an ohmic contact on a semiconductor structure, comprising the steps of: providing a semiconductor structure, wherein the semiconductor structure includes an n-doped GaN material, depositing a TiAlxNy material contiguous to at least part of the n-doped GaN, wherein x and y do not simultaneously equal zero, depositing Al contiguous to at least part of the TiAlxNy, such that the TiAlxNy is between the Al and the n-doped GaN, and annealing the semiconductor structure and the TiAlxNy material and the Al material. In a related embodiment, x is equal to about 3 and y is equal to about zero. In another related embodiment, the TiAlxNy material is about 50-200 angstroms thick and the Al material is about 1000 angstroms thick. In another related embodiment, the annealing process takes place at less than 660 degrees C. In another related embodiment, the annealing process takes place for approximately 0.1 to 10 minutes. In another related embodiment, the annealing process takes place for approximately 30 to 60 seconds.
Various embodiments of the present invention provide a method of manufacturing an LED comprising: use of a composition for formation of an ohmic contact on a semiconductor structure, comprising a TiAlxNy material at least partially contiguous with the semiconductor structure, wherein x and v do not simultaneously equal zero; or comprising a method for formation of an ohmic contact on a semiconductor structure, comprising the step of annealing a composition for formation of an ohmic contact on a semiconductor structure, comprising a TiAlxNy material at least partially contiguous with the semiconductor structure, wherein x and y do not simultaneously equal zero; or comprising a method for formation of an ohmic contact on a semiconductor structure, comprising the steps of providing a semiconductor structure, wherein the semiconductor structure includes an n-doped GaN material, depositing a TiAlxNy material contiguous to at least part of the n-doped GaN, wherein x and y do not simultaneously equal zero, and annealing the semiconductor structure and TiAlxNy material; or comprising a method for formation of an ohmic contact on a semiconductor structure comprising the steps of providing a semiconductor structure, wherein the semiconductor structure includes an n-doped GaN material, depositing a TiAlxNy material contiguous to at least part of the n-doped GaN, wherein x and y do not simultaneously equal zero; depositing aluminum material contiguous to at least part of the TiAlxNy, such that the TiAlxNy is between the aluminum and the n-doped GaN; and, annealing the semiconductor structure and the TiAlxNy material and the aluminum material.
Various embodiments of the present invention provide a composition or product formed by any one of the methods comprising: a method for formation of an ohmic contact on a semiconductor structure, comprising the step of annealing a composition for formation of an ohmic contact on a semiconductor structure, comprising a TiAlxNy material at least partially contiguous with the semiconductor structure, wherein x and y do not simultaneously equal zero; or comprising a method for formation of an ohmic contact on a semiconductor structure, comprising the steps of providing a semiconductor structure, wherein the semiconductor structure includes an n-doped GaN material, depositing a TiAlxNy material contiguous to at least part of the n-doped GaN material, wherein x and y do not simultaneously equal zero, and annealing the semiconductor structure and the TiAlxNy material; or comprising a method for formation of an ohmic contact on a semiconductor structure comprising the steps of providing a semiconductor structure, wherein the semiconductor structure includes an n-doped GaN material, depositing TiAlxNy contiguous to at least part of the n-doped GaN, wherein x and y do not simultaneously equal zero; depositing an aluminum material contiguous to at least part of the TiAlxNy, such that the TiAlxNy is between the aluminum and the n-doped GaN; and, annealing the semiconductor structure and the TiAlxNy material and the aluminum material.
Various embodiments of the present invention provide an LED comprising: a composition for formation of an ohmic contact on a semiconductor structure, comprising a TiAlxNy material at least partially contiguous with the semiconductor structure, wherein x and y do not simultaneously equal zero; or an LED prepared by any one of the methods comprising: a method for formation of an ohmic contact on a semiconductor structure, comprising the step of annealing a composition for formation of an ohmic contact on a semiconductor structure, comprising a TiAlxNy material at least partially contiguous with the semiconductor structure, wherein x and y do not simultaneously equal zero; or comprising a method for formation of an ohmic contact on a semiconductor structure, comprising the steps of providing a semiconductor structure, wherein the semiconductor structure includes an n-doped GaN material, depositing a TiAlxNy material contiguous to at least part of the n-doped GaN, wherein x and y do not simultaneously equal zero, and annealing the semiconductor structure and the TiAlxNy material; or comprising a method for formation of an ohmic contact on a semiconductor structure comprising the steps of providing a semiconductor structure, wherein the semiconductor structure includes an n-doped GaN Material, depositing a TiAlxNy material contiguous to at least part of the n-doped GaN material, wherein x and y do not simultaneously equal zero; depositing an aluminum material contiguous to at least part of the TiAlxNy, such that the TiAlxNy is between the aluminum and the n-doped GaN; and, annealing the semiconductor structure and the TiAlxNy material and the aluminum material.
An example of a disadvantageous method of forming ohmic contacts on n-doped GaN (n-GaN) semiconductor structures which is not an embodiment of the present invention is shown in
Some embodiments of the present invention provide advantages over known compositions and methods for the formation of ohmic contacts on semiconductor structures, including semiconductor structures that are to become LED semiconductor devices. Advantages can include, but are not limited to, the use of lower heat during the annealing process, the use of a shorter annealing process, and the use of materials that are more resilient to a high temperature annealing process.
An embodiment of the present invention is shown in
Another embodiment of the present invention is shown in
Another embodiment of the present invention is shown in
Another embodiment of the present invention is shown in
All publications, patents, and patent applications are incorporated herein by reference. While in the foregoing specification this disclosed subject matter has been described in relation to certain preferred embodiments thereof, and many details have been set forth for purposes of illustration, it will be apparent to those skilled in the art that the disclosed subject matter is susceptible to additional embodiments and that certain of the details described herein can be varied considerably without departing from the basic principles of the disclosed subject matter.
This application is a continuation of U.S. application Ser. No. 16/592,425, filed Oct. 3, 2019, which is a continuation of U.S. application Ser. No. 15/399,372, filed Jan. 5, 2017, now issued as U.S. Pat. No. 10,446,727, which is a continuation of U.S. application Ser. No. 14/261,901, filed Apr. 25, 2014, now issued as U.S. Pat. No. 9,608,185, which is a divisional of U.S. application Ser. No. 12/787,211, filed May 25, 2010, all of which are incorporated herein by reference in their entirety.
| Number | Date | Country | |
|---|---|---|---|
| Parent | 12787211 | May 2010 | US |
| Child | 14261901 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 16592425 | Oct 2019 | US |
| Child | 17223732 | US | |
| Parent | 15399372 | Jan 2017 | US |
| Child | 16592425 | US | |
| Parent | 14261901 | Apr 2014 | US |
| Child | 15399372 | US |