1. Field of the Invention
The present invention relates to an oil-impregnant sintered bearing in which a bearing main body is impregnated with lubricating oil for improving lubrication with a rotating axis member which runs through an internal diameter of the bearing, and the manufacturing method thereof.
2. Related Art
An oil-impregnant sintered bearing is composed of a porous sintered metal, and is impregnated with lubricating oil prior to use. Consequently, the oil-impregnant sintered bearing can be used for a long period of time without being further oiled, has superior durability at high temperatures and low noise levels. For these reasons, it is widely used instead of a ball-bearing as a bearing for a rotating axis member.
This type of oil-impregnant sintered bearing comprises a cylindrical bearing main body of porous sintered metal, which an internal face is provided therein. A rotating axis member has a smaller diameter than the diameter of the internal face, and is inserted therein. Lubricating oil, which is sucked out from the great number of small pores which are buried in the bearing main body or opened in the surface of the internal face by the pump action accompanying the rotation of the rotating axis member, and a lubricating oil, which has been exuded by expansion caused by frictional heating, form an oil film at the section of the oil-impregnant sintered bearing which slides against the rotating axis member; this oil film supports the rotating axis member and protects it from damage such as burning.
However, in such an oil-impregnant sintered bearing, since even the sliding face, which the rotating axis member contacts while sliding, has a great number of pores which the lubricating oil is impregnated in, even when the oil film is formed between the rotating axis member and the sliding face, some of the lubricating oil leaks from the pores, reducing the oil pressure and allowing local contact between the rotating axis member and the sliding face. As a consequence, there are drawbacks in that the frictional coefficient with the rotating axis member increases, and burns on the like may occur.
An oil-impregnant sintered bearing 101 shown in
However, as for the example disclosed in Japanese Patent Application, First Publication No. 4-307111, even when pores are closed in the inner peripheral face of a pressed powder body, obtained by pressure-forming of raw material powder, the pores sometimes re-open during sintering since tin and the like is included in the raw material powder. Consequently, oil seeps from the holes to the inside, and oil pressure decreases. Further, Japanese Patent Application, First Publication No. 5-180229 discloses technology for closing the pores in the inner peripheral face when plugging in a rod for forming the bearing at the time of post-sintering correction. However, this technology basically involves closing the pores which have appeared in the inner face, and cannot preserve the oil film since the surface layer may be broken by the oil pressure, allowing the oil to seep to the inside.
Further, Japanese Patent Application, First publication No. 8-28567 discloses technology which uses a welded material having no pores in one section of its inner peripheral face. However, since the welded material cannot contain lubricating oil, the capacity of lubricating oil which can be contained in the oil-impregnant sintered bearing is reduced.
The present invention has been realized in consideration of the above problems, and aims to provide an oil-impregnant sintered bearing which can reliably secure the oil film, formed on the sliding face, and a method for manufacturing the oil-impregnant sintered bearing.
A first aspect of the present invention provides an oil-impregnant sintered bearing comprising an internal diameter, in which a rotating axis member is inserted therethrough, provided in a bearing main body, formed by a porous sintered alloy having internal pores, and a sliding face, provided in one region of the inner peripheral face of the internal diameter. The sliding face is obtained by closing the pores which have been opened in the inner peripheral face. The density in a section preserving oil pressure, which extends from the sliding face of the bearing main body toward the outer side of the diameter, is higher than in other sections of the bearing main body.
According to this constitution, the density of the section preserving oil pressure, extending from the sliding face of the bearing main body to the outer side of the diameter, is higher than other sections of the bearing main body. Therefore, the pores in the internal area of the section preserving oil pressure are closed more greatly than the other section, with the result that oil does not seep from the sliding face to the inside, thus enabling the oil film to be secured over the sliding face.
A second aspect of the present invention provides a method for manufacturing the oil-impregnant sintered bearing, comprising the steps of pressure-forming a raw material powder to obtain a pressed powder body, sintering the pressed powder body, obtaining a bearing main body, formed by a porous sintered alloy having internal pores, and providing a sliding face in one region of the inner peripheral face of the internal diameter, the sliding face being provided by closing the pores which have been opened in the inner peripheral face; and making the density in a section preserving oil pressure, which extends from the sliding face of the bearing main body toward the outer side of the diameter, higher than in other sections of the bearing main body.
In this invention, the oil-impregnant sintered bearing is manufactured so that the density of the section preserving oil pressure, extending from the sliding face of the bearing main body to the outer side of the diameter, is higher than other sections of the bearing main body. Therefore, the pores in the internal area of the section preserving oil pressure are more greatly closed than in the other sections, with the result that oil does not seep from the sliding face to the inside, enabling the oil film to be secured over the sliding face.
According to a third aspect of the present invention, in the method of the second aspect, more raw material powder is filled in a part of a cavity for pressure-forming the pressed powder body where the section preserving oil pressure is to be provided than in other parts, and the compression rate of the raw material powder in the part during pressure-forming is made greater than in the other parts, thereby making the density in the section preserving oil pressure higher than in other sections of the bearing main body.
In this invention, in a cavity for pressure-forming a pressed powder body, more raw material powder is filled in a part where the section preserving oil pressure is to be provided than in other parts, and the compression rate of the raw material powder in the part during pressure-forming is greater than in the other parts. Therefore, when the pressed powder body is corrected after sintering to obtain the oil-impregnant sintered bearing, the density in the section preserving oil pressure can be made higher than in other sections of the bearing main body.
According to a fourth aspect of the present invention, in the method of the third aspect, the raw material powder is filled in a cavity comprised of a die for forming an outer peripheral face of the pressed powder body, which is made substantially cylindrical, a round-ended column-like core rod for forming an inner peripheral face, a first lower punch and a second lower punch for forming a bottom end face of the pressed powder body. More raw material powder is filled in a place where the section preserving oil pressure is to be provided, by bringing the first lower punch lower down than the second lower punch. In addition, the raw material powder is enclosed by the first lower punch, the second lower punch, and an upper punch, and is compressed until the first lower punch and the second lower punch are set at the same height, thereby increasing the density in the place on the pressed-powder body where the section preserving oil pressure is to be provided.
In this invention, the raw material powder is filled from above into a cavity comprised of a die for forming an outer peripheral face of the pressed powder body, which is made substantially cylindrical, a round-ended column-like core rod for forming an inner peripheral face, a first lower punch and a second lower punch for forming a bottom end face of the pressed powder body. Since the first lower punch is brought lower down than the second lower punch, more raw material powder is filled in the place where the section preserving oil pressure is to be provided. The first lower punch and the second lower punch are moved upwards in the space enclosed by the die and the core rod, and the upper punch for forming the top face of the pressed powder body is inserted from above into the space enclosed by the die and the core rod and moved downwards, whereby the raw material powder is enclosed and compressed by the first lower punch, the second lower punch, and the upper punch. Since the pressed powder body is made so that the first lower punch and the second lower punch finally become the same height, the raw material powder which is filled above the first lower punch is compressed at a high compression rate. Therefore, when the pressed powder body is corrected after sintering to obtain the oil-impregnant sintered bearing, the density in the section which is filled with more raw material powder is increased, and the internal pores are more greatly closed than in other sections.
In this way, the lower punch is divided in alignment with the place where the section preserving oil pressure will be provided, the first lower punch for forming the section which will become the section preserving oil pressure being brought down lower than the second lower punch. The compression rate of the raw material powder is higher in the section which is enclosed by the first lower punch and the upper punch than in other sections. Therefore, when the pressed powder body is corrected after sintering to obtain the oil-impregnant sintered bearing, the density in the section preserving oil pressure is higher than in other sections of the bearing main body.
According to a fifth aspect of the present invention, in the method of the second aspect, the inside diameter of the inner peripheral face of the pressed powder body, which is made substantially cylindrical, is made smaller in a region where the sliding face will be provided than in other regions, and the region where the sliding face will be provided is extended toward the outer side of the diameter during correction to obtain the internal diameter, thereby compressing the section which extends to the outer side of the diameter from the region where the sliding face will be provided, and making the density of the section preserving oil pressure higher than the density in other sections of the bearing main body.
In this invention, the inside diameter of the pressed powder body in the region where the sliding face is to be provided so as to be smaller than in other regions, and, during post-sintering correction, this section is corrected and compressed so as to expand toward the outer side of the diameter. Therefore, the density in the section preserving oil pressure can be made higher than in other sections.
A sixth aspect of this invention provides a motor equipped with a rotator having a rotating axis member which protrudes at one end, the motor comprising a worm, provided around the outer periphery of the protruding rotating axis member; and a worm wheel which meshes with the worm and has a decelerator unit provided to an output axis member protruding at a rotation core of the worm wheel. The protruding rotating axis member of the rotator is inserted into the internal diameter of the oil-impregnant sintered bearing of the first aspect, and the sliding face of the oil-impregnant sintered bearing is provided so as to slidingly contact one part of the outer peripheral face of the rotating axis member which is provided on the opposite side of the axis member line of the rotating axis member to the side which meshes with the worm wheel.
According to the constitution, the oil film, which is provided on the sliding face, is reliably preserved, guaranteeing that the rotating axis member rotates smoothly.
The oil-impregnant sintered bearing and manufacturing method of the present invention will be explained based on the drawings.
More specifically, the pores which contain the lubricating oil are provided in the whole area of the bearing main body 3 along the peripheral direction thereof. As a result, the lubricating oil can be freely moved along the peripheral direction, and therefore, the lubricating oil can diffuse in the whole area without stagnating. Furthermore, the porosity of the section preserving oil pressure 6 becomes relatively low since most of the pores are closed and the average diameter of the holes is decreased. Otherwise, the porosity of the other section 7 of the bearing main body 3 becomes relatively high since most of the pores are not closed and the average diameter of the holes is enlarged.
Next, an embodiment of a method for manufacturing the oil-impregnant sintered bearing 1 having the constitution described above will be explained mainly with reference to
As shown in
The raw material powder M is enclosed and compressed by the first lower punch 12, the second lower punch 13, and the upper punch 14. That is, the first lower punch 12 and the second lower punch 13 are moved upwards toward the die 10 and the core rod 11, and the upper punch 14 is inserted into the space between the die 10 and the core rod 11 and moved downwards therein, whereby the raw material powder M is enclosed and compressed by the first lower punch 12, the second lower punch 13, and the upper punch 14. In this way, as shown in
In a subsequent process, when the core rod 11 is pulled out, the rough face 11a, which is provided on the outer peripheral face of the core rod 11, closes the pores in the inner peripheral face of the pressed powder body P and thereby obtains the region which will become the sliding face 5.
Since the compression rate in the section of the raw material powder M which is enclosed and compressed by the first lower punch 12 and the upper punch 14 is higher than the compression rate in the section of the raw material powder M which is enclosed and compressed by the second lower punch 13 and the upper punch 14, the pores in this section are more greatly closed than the other section. When the pressed powder body P in this state is sintered and corrected, achieving the oil-impregnant sintered bearing 1 as shown in
In the oil-impregnant sintered bearing 1 which has been made in this way, not only the pores on the sliding face 5 but also the pores in the section preserving oil pressure 6 which extend from the sliding face 5 toward the outer side of the diameter are more greatly closed than the other sections. For this reason, even when holes are created in the sliding face 5 due to sintering, since the internal pores are closed, the oil on the sliding face 5 is unlikely to seep into the bearing main body 3.
Therefore, according to the oil-impregnant sintered bearing 1 shown in
Incidentally, in the embodiment described above, the stage of making the pressed powder body P in order to obtain the sliding face 5 comprises a step of closing the pores on the inner peripheral face, but it is acceptable to use a method, disclosed in Japanese Patent Application, First Publication No. 5-180229, of providing a bump protruding to the inner side of the diameter in the region where the sliding face 5 is to be provided, shaving away this bump during correction after sintering, and pressingly-inserting a correction rod, thereby closing the pores on the inner peripheral face and making the sliding face.
In creating the section preserving oil pressure, it is important not only to close the pores on the sliding face, but to close the pores in the section of the bearing main body which extends from the sliding face toward the outer side of the diameter.
Furthermore, a method for manufacturing the oil-impregnant sintered bearing according to another embodiment of the present invention will be explained using
Subsequently, as shown in
In this way, the pores in the inner section are closed by post-sintering compression of the section which extends from the sliding face 5 toward the outer side of the diameter, and finally the section preserving oil pressure 6 having higher density than the other sections is made.
According to this method, the section preserving oil pressure can be made merely by slightly changing the shape of the correction rod, and there is no need to greatly change the die set.
The oil-impregnant sintered bearing 1 shown in
According to this constitution, the sliding face 105 supports the load which the worm wheel imposes on the rotating axis member 102. By reliably preserving the oil film, which is provided on the sliding face 105, smooth rotation of the rotating axis member 102 can be guaranteed.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2000-241618 | Aug 2000 | JP | national |
| 2001-222858 | Jul 2001 | JP | national |
| Number | Name | Date | Kind |
|---|---|---|---|
| 2615766 | Wallace | Oct 1952 | A |
| 2625452 | Haller | Jan 1953 | A |
| 2763519 | Thompson | Sep 1956 | A |
| 2864792 | Groote et al. | Dec 1958 | A |
| 2894792 | Brilli | Jul 1959 | A |
| 3140131 | Tann | Jul 1964 | A |
| 3445148 | Harris et al. | May 1969 | A |
| 3580106 | Wiehl et al. | May 1971 | A |
| 4026657 | Chmura | May 1977 | A |
| 4059879 | Chmura et al. | Nov 1977 | A |
| 4608085 | Eudier et al. | Aug 1986 | A |
| 4830820 | Itoh et al. | May 1989 | A |
| 5120091 | Nakagawa | Jun 1992 | A |
| 5282688 | Kanezaki et al. | Feb 1994 | A |
| 5433294 | Walker | Jul 1995 | A |
| 5529401 | Gabelli et al. | Jun 1996 | A |
| 5540883 | Jones et al. | Jul 1996 | A |
| 6023114 | Mori et al. | Feb 2000 | A |
| 6082903 | Saneshige | Jul 2000 | A |
| 6120188 | Fujinaka et al. | Sep 2000 | A |
| 6225265 | Shibuya et al. | May 2001 | B1 |
| 6270259 | Burton | Aug 2001 | B1 |
| 6338747 | Kosco | Jan 2002 | B1 |
| 6361737 | Miyasaka et al. | Mar 2002 | B1 |
| 6505971 | Sugimoto et al. | Jan 2003 | B2 |
| 6599018 | Maruyama et al. | Jul 2003 | B2 |
| 20040136858 | Woolf | Jul 2004 | A1 |
| Number | Date | Country |
|---|---|---|
| 280149 | Jun 1990 | DE |
| 0 097 027 | Dec 1983 | EP |
| 4-307111 | Oct 1992 | JP |
| 5-180229 | Jul 1993 | JP |
| 8-28567 | Feb 1996 | JP |
| Number | Date | Country | |
|---|---|---|---|
| 20030206670 A1 | Nov 2003 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 09923356 | Aug 2001 | US |
| Child | 10441005 | US |