1. Field of the Invention
The present invention relates to the field of photoprotective compounds, and more particularly to photoprotective compounds from plant oil processing.
2. Background Art
Pesticides, herbicides, xenobiotics and other useful chemicals are commonly applied to fields, forests, roadsides and other locations where they may be degraded by exposure to light. Similarly, living organisms including bacteria, bacterial spores, fungi, fungal spores, viruses and viral spores are increasingly being applied in the environment for their beneficial effects. Exposure of these materials and beneficial organisms to light often decreases their effectiveness by altering their chemical structures or diminishing their biological activity. Photoprotective strategies can be employed to maintain or increase the effectiveness of these compounds and organisms.
Wood, plastic, fabric and many other construction materials are also degraded by visible and ultraviolet light. Over time exposure to light will fade or discolour such materials and decrease their integrity. Photoprotective strategies may also be employed to maintain the integrity and appearance of these materials.
Virus particles may be mixed with opaque solids such as carbon black to maintain viability by protection from white light in the method of U.S. Pat. No. 3,541,203. U.S. Pat. No. 5,939,089 teaches methods of coating viral spores with kraft lignin. The coated virus spores possess enhanced resistance to ultraviolet light.
Insecticide compositions containing pyrethinoids are highly susceptible to light degradation. According to U.S. Pat. No. 3,264,176 insecticide powders may be stabilised against light degradation by absorption onto charcoal. The disadvantage of this method is the tendency of dark materials to heat in the environment. Heat as well as light exacerbates the processes involved in degradation and inactivation. Reflective pigments including titanium dioxide can be used in place of carbon black according to U.S. Pat. No. 2,168,064 but the added cost of these materials limits their application. Dextrins and gums also provide protection to pyrethinoids. (U.S. Pat. No. 3,130,121). Strong UV absorbing compounds may be mixed with pyrethinoids to maintain activity. Diisophorone, for example, may be mixed with pyrethinoids to protect them from light wavelengths between 210 and 350 nm according to U.S. Pat. No. 3,839,561. Pyrethinoids may also be stabilized by the addition of amyl-paradimethylamino benzoate and a suitable antioxidant (U.S. Pat. No. 3,560,613).
Endosulfan and chlorpyriphos are also noted to be unstable to light exposure. U.S. Pat. No. 5,549,903 teaches of the use of urea encapsulation and light absorbing compounds to produce a stabilized insecticide product.
Petroleum spray oils may be used to control a number of fungi and insects (U.S. Pat. No. 3,098,000) but these oils are subject to harmful oxidation catalyzed by ultraviolet light. Degradation of the oils causes them to become phytotoxic.
Combinations of anti-oxidants and light absorbents may be added to the oils to prevent degradation and phytoxicity.
Synthetic light absorbing compounds may be highly effective but they are produced from non-renewable resources and they may have undesirable side effects. For example, U.S. Pat. No. 2,772,198 demonstrates that 4-amino-azo-benzene provides excellent protection of pyrethinoids but this compound is a potent carcinogen. Acidulated soybean and other acidulated vegetable oils are commonly used as adjuvants for herbicidal compounds. Gednalske reported that blends of a non-ionic surfactant and acidulated soapstock were effective in preparing a carrier solution for the application of herbicides (U.S. Pat. No. 5,260,260). U.S. Pat. No. 5,521,144 teaches that mixed tocopherols may be added to acidulated soapstock to improve the environmental stability of active ingredients applied with the adjuvant. Acidulated soapstock may also be used in herbicidal compositions to decrease odours as taught by Gednalske and Herzfeld (U.S. Pat. Nos. 5,463,180 and 5,719,102).
Soapstock is a co-product obtained in the manufacture of vegetable oil. It is commonly used in wide-ranging applications including animal feed and road dust control. Industrial soapstock is a highly variable product, which contains significant amounts of pigments, colour bodies and other compounds. Acidulated soapstock is prepared by adding acid to soapstock and recovering oil from the acidified solution. The acidulated oil solution is a concentrated source of plant pigments.
The instant invention discloses the surprising discovery that acidulated soapstock may be prepared to maximize and standardize the content of light absorbing compounds. When appropriately processed the soapstock has sufficient light absorbance to be used as a photoprotective adjuvant for pesticides, herbicides, xenobiotics, other useful chemicals, bacteria, bacterial spores, fungi, fungal spores, viruses and viral spores.
The present invention teaches methods of preparing soapstock to enhance and standardize the light absorbance characteristics. Furthermore, it also teaches the application of acidulated oils as natural photoprotective agents. Acidulated oils with strong light absorbance between 190 and 700 nm wavelength may be used to protect environmentally applied pesticides, herbicides, xenobiotics, other useful chemicals, bacteria, bacterial spores, fungi, fungal spores, viruses and viral spores. Similarly acidulated oils may be able to maintain wood, plastics, fabrics and construction materials that are exposed to visible and ultraviolet light.
These and other attributes of the invention will become more clear upon a thorough study of the following description of the best mode for carrying out the invention, particularly when reviewed in conjunction with the drawings, wherein:
The present invention includes methods of preparing acidulated oils with strong light absorbing characteristics. The light absorbance is due to the presence of specific compounds that may be preferentially concentrated during soapstock preparation or during acidulation. The light absorbing oil soluble compounds include but are not limited to naturally occurring oil soluble protein, tocopherol, phaeophytin, carotenoid, quinone, quinol, phenolic, and ferulate ester. The light absorbing oil also includes chemically modified compounds where the modification is controlled by extraction and acidulation conditions.
The invention also teaches that although all acidulated soapstock has some light absorbance the absorbance characteristics are too variable for the reliable production of a useful light adsorbing oil. The light adsorbing quality of the oil is subject to wide ranging factors. Compounds present in the acidulated oil vary considerably depending on the species and genetic factors. The utilisation of soapstock from the processing of soy, canola, rapeseed, palm, sunflower, peanut, cottonseed, flax, rice bran is included in the current invention. In a preferred embodiment acidulated soapstock derived from the manufacture of soybean oil is utilized for its photoprotective effects. In another preferred embodiment acidulated soapstock are blended to minimise differences in light absorbance and to produce a consistent product.
Furthermore, conditions used in oil extraction by different commercial operations greatly affect the light absorbance properties of the soapstock. For example, in one industrial process soapstock is prepared such that it includes phospholipids and glycolipids as a major component while other soapstock has only minor amounts of these compounds. Phospholipids significantly affect the light absorbance of the acidulated oil. The current invention includes but is not restricted to acidulated oils that are produced from soapstock materials that include phospholipids and glycolipids.
Oil extrusion, tempering conditions, expeller pressing and solvent extraction methods vary between manufacturers of vegetable oil. These processing methods alter the light absorbance characteristics of the soapstock. It is also part of the current invention to utilize extraction protocols such as modified extrusion methods, expeller pressing and solvent extraction to enhance the light absorbance of the acidulated oil. In a preferred embodiment of the current invention the soapstock is derived from expeller pressed oils. In another embodiment the soapstock is derived from solvent extracted oils. The soapstock may also be recovered from mixtures of solvent extracted oils and expeller pressed oils.
Conditions employed during acidulation also affect the absorbance of the oil. For example, the temperature of acidulation, the type of acid used for acidulation and duration of the acidulation treatment significantly affect oil light absorbance properties. The current invention includes conditions that occur during acidulation that enhance or alter oil absorbance properties. In a preferred embodiment the acidulation occurs at a pH of less than 2.0. In another preferred embodiment the acidulation occurs at a pH of 1.5 and a temperature of 90-110 C. In another preferred embodiment sulfuric acid is used to acidulate the oil. It is known to those skilled in the art that any of a number of mineral and organic acids may be used for acidulation. Due to the price of the acid used it may be preferred to utilize sulfuric acid.
Normally the major components of acidulated oils are fatty acids, partial glycerides and triglycerides. The fatty acids and glycerides themselves have only limited light absorbance characteristics, with a strong absorbance due to their carbonyl functionality at wavelengths less than 210 nm. Therefore, the glycerides act to dilute the light absorbing compounds. Selectively removing fatty acids and glycerides can concentrate the light absorbance of the oil producing intensely absorptive oil. In particular, it is possible to selectively remove fatty and mono glycerides from acidulated oils by distillation. It is an embodiment of this invention where fatty acids and glycerides are removed from acid oil to increase the concentration of light absorbance. In a preferred embodiment fatty acids are removed from the acid oil by distillation. In another preferred embodiment fatty acids are removed from the acid oil by short path distillation.
The light absorbance characteristics of acidulated oils are not equal at all wavelengths. It is possible to augment the light absorbance characteristics by the addition of oil soluble pigments. Pigments from naturally occurring sources are preferred but the use of synthetic pigments is an embodiment of the current invention.
The photoprotective acidulated fatty acids may be used in any application for protection of light exposed materials. In a preferred embodiment the photoprotective action is utilised in herbicide spray mixtures to maintain the biological activity of the herbicide. In another preferred embodiment the photoprotective action is used to stabilise wood against chemical attack.
Canola soapstock was obtained from a commercial manufacturer of vegetable oil. Four hundred grams of the soapstock were blended with 24 grams of sulfuric acid in a 4-liter glass beaker using a stainless steel spatula. The mixture was heated 95 C then held at that temperature for 15 minutes on a hot plate equipped with a teflon coated magnetic stirrer bar. After acidulation the contents of the beaker were cooled. The beaker contents were transferred to a separatory funnel where, after settling, the lower water layer was removed (221 g—water). An intermediate layer of viscous material was then taken from the funnel (12 g—emulsion) followed by an upper layer of black coloured oil (181 g—of acidulated soapstock). The extracted oil was dissolved to a concentration of 10%, 1.0%, 0.1% and 0.01 w/w in spectrophotometry grade n-hexane.
Visible and ultraviolet light spectra of all dilutions of acidulated soapstock were measured using a dual beam UV/visible spectrophotometer. The spectrum of the 1.0% dilution is shown in
Soybean soapstock was obtained from a commercial manufacturer of vegetable oil. Four thousand pounds of sulfuric acid was added to eighty thousand pounds of soapstock with continuous agitation in a fiberglass resin reactor tank. The temperature of the mixture was increased to 95 C by injection of steam while maintaining continuous agitation. After addition of acid and heat treatment the mixture was subject to 2 additional hours of agitation at 95 C the contents of the reactor tank were transferred to a settling tank. After 24 hours 35,000 pounds of acidulated oil were removed from the top of the tank. The oil possessed strong UV absorbance characteristics.
Spray mixtures of the herbicides (+/−) 2-{(E)-1-{3-chloroallyloxyimino]propyl]-5-{2-(ethylthio)propyl}-hydroxycyclohexen-2-one (Select) and 2-{1-(ethoxyimino)butyl}-5-[2-(ethylthio)propyl]-3-hydroxy-2-cyclohexen-1-one (Poast) were prepared with an non-ionic surfactant adjuvant including acidulated soybean oil and without the acidulated oil. The non-ionic surfactants were added to a water spray solution at a concentration of 0.25% v/v ai and applied to yellow foxtail plants in the greenhouse. The application rate of Select and Poast was 2 fl. and 6 fl. Oz/Acre, respectively. Control of grassy weeds was assessed as reduction in dry weight of the plants compared to untreated control plants 27 days after application. Control data was statistically analyzed using analysis of variance methods. Differences between means reported in the Table I were determined at p=0.05 using the Student-Newman-Keuls method.
Spray mixtures of the herbicide (+/−) 2-{(E)-1-{3-chloroallyloxyimino]propyl]-5-{2-(ethylthio)propyl}-hydroxycyclohexen-2-one (Select) was prepared with a non-ionic surfactant adjuvant including acidulated soybean oil and without the acidulated oil. The nonionic surfactants were used at a concentration of 0.25% v/v ai and applied to corn and wheat plants in the field. The application rate was 2 fl. oz./Acre. Percent control of the corn and hard red spring wheat was visually assessed compared to untreated control plants 17 and 31 days after treatment. Control data was statistically analyzed using analysis of variance methods. Differences between means reported in the Table II were determined at p=0.05 using the Student-Newman-Keuls method.
Table II shows that when Select was applied without an adjuvant weed control was poor. Inclusion of an adjuvant improved control of the corn while inclusion of a non-ionic surfactant with the acidulated oil increased control even more.
Although only an exemplary embodiment of the invention has been described in detail above, those skilled in the art will readily appreciate that many modifications are possible without materially departing from the novel teachings and advantages of this invention. Accordingly, all such modifications are intended to be included within the scope of this invention as defined in the following claims.
This application contains disclosure from and claims the benefit under Title 35 United States Code § 119(e) of U.S. Provisional Application Ser. No. 60/367,585, filed Mar. 26, 2002 and entitled “Oil Soluble Photoprotective Compounds and Compositions from Plant Oil Processing”.
| Number | Name | Date | Kind |
|---|---|---|---|
| 3425938 | Bloomberg et al. | Feb 1969 | A |
| 4280962 | Watanabe et al. | Jul 1981 | A |
| 5521144 | Farr et al. | May 1996 | A |
| Number | Date | Country | |
|---|---|---|---|
| 20030186818 A1 | Oct 2003 | US |
| Number | Date | Country | |
|---|---|---|---|
| 60367585 | Mar 2002 | US |