Claims
- 1. A method of making a one-package and substantially acid-free room temperature vulcanizable composition curable to the solid elastomeric state, which method comprises agitating under substantially anhydrous conditions at a temperature in the range of from 0.degree. C. to 180.degree. C., a room temperature vulcanizable material selected from
- (i) a mixture comprising
- (a) 100 parts of a silanol-terminated polydiorganosiloxane consisting essentially of chemically combined units of the formula ##STR14## (b) a stabilizing amount of a silane scavenger for hydroxy functional groups of the formula ##STR15## (c) 0.01 to 10 parts of cross-linking silane of the formula ##STR16## (d) an effective amount of a condensation catalyst, and (e) 0 to 5 parts of a curing accelerator selected from the group consisting of substituted guanidines, amines and mixtures thereof; and
- (ii) a mixture comprising
- (a) 100 parts of a polyalkoxy-terminated polydiorganosiloxane of the formula ##STR17## (iii) 0 to 10 parts of a cross-linking silane of the formula, ##STR18## (iv) an effective amount of a condensation catalyst (v) a stabilizing amount of a silane scavenger for hydroxy functional groups having the formula ##STR19## and (vi) 0 to 5 parts of a curing accelerator selected from the group consisting of substituted guanidines, amines and mixtures thereof,
- where R is selected from C.sub.(1-13) monovalent substituted or unsubstituted hydrocarbon radicals, R.sup.1 is a C.sub.(1-8) aliphatic organic radical selected from the group consisting of alkyl, alkylether, alkylester, alkylketone and alkylcyano radicals, or a C.sub.(7-13) alkaryl radical, R.sup.2 is a C.sub.(1-13) monovalent substituted or unsubstituted hydrocarbon radical, X is a hydrolyzable leaving group selected from the group consisting of amido, amino, carbamato, enoxy, imidato, isocyanato, oximato, thioisocyanato and ureido radicals and, a is an integer equal to 1 or 2, b is a whole number equal to 0 or 1, and the sum of a+b is equal to 1 or 2, c is a whole number equal to 0 to 3 inclusive, d is an integer equal to 1 to 4 inclusive, and the sum of c+d is equal to 3 or 4, e is a whole number equal to 0 or 1 and the sum of b+e is equal to 0 to 1, n is an integer having a value of from about 50 to about 2500 inclusive, c is a whole number equal to 0 to 3 inclusive, f is an integer equal to 1 to 4 inclusive and the sum of c+f is equal to 1 to 4 inclusive, and in either mixture where X is enoxy, there is also added, before or with the scavenger, 0.1 to 5 parts of a curing accelerator selected from the group consisting of substituted guanidines, amines and mixtures thereof.
- 2. A method in accordance with claim 1, where R, R.sup.1 and R.sup.2 are methyl.
- 3. A method in accordance with claim 1, where the curing accelerator is selected from the group consisting of silylated guanidine and alkyl guanidine.
- 4. A method in accordance with claim 1, where the scavenging silane is a polymethoxyacetamidosilane.
- 5. A method in accordance with claim 1, where the cross-linking silane is methyltrimethoxysilane.
- 6. A method in accordance with claim 1, where the condensation catalyst is a tin compound.
- 7. A method in accordance with claim 4, where the silane scavenger is methyldimethoxy(N-methylacetamido)silane.
- 8. A mixture comprising
- (a) 100 parts of a silanol-terminated polydiorganosiloxane consisting essentially of chemically combined units of the formula ##STR20## (b) a stabilizing amount of a silane scavenger for hydroxy functional groups of the formula ##STR21## (c) 0.01 to 10 parts of cross-linking silane of the formula ##STR22## (d) an effective amount of a condensation catalyst, and (e) 0 to 5 parts of a curing accelerator selected from the group consisting of substituted guanidines, amines and mixtures thereof,
- where R is selected from C.sub.(1-13) monovalent substituted or unsubstituted hydrocarbon radicals, R.sup.1 is a C.sub.(1-8) aliphatic organic radical selected from the group consisting of alkyl, alkylether, alkylester alkylketone and alkylcyano radicals, or a C.sub.(7-13) aralkyl radical, R.sup.2 is a C.sub.(1-13) monovalent substituted or unsubstituted hydrocarbon radical, X is a hydrolyzable leaving group selected from the group consisting of amido, amino, carbamato, enoxy, imidato, isocyanato, oximato, thioisocyanato and ureido radicals and, a is an integer equal to 1 or 2, c is a whole number equal to 0 to 3 inclusive, d is an integer equal to 1 to 4 inclusive, and the sum of c+d is equal to 3 or 4, b is a whole number equal to 0 or 1, and the sum of a+b is equal to 1 or 2; and where X is enoxy, 0.1 to 5 parts of a curing accelerator selected from the group consisting of substituted guanidines, amines and mixtures thereof.
- 9. In the method of making a substantially acid-free room temperature vulcanizable organopolysiloxane composition under substantially anhydrous conditions utilizing an effective amount of a condensation catalyst with a silanol-terminated organopolysiloxane and a polyalkoxysilane cross-linking agent, the improvement which comprises adding to the silanol-terminated organopolysiloxane a stabilizing amount of scavenger for hydroxy functional groups of the formula ##STR23## where R.sup.1 is a C.sub.(1-8) aliphatic organic radical selected from the group consisting of alkyl, alkylether, alkylester, alkylketone and alkylcyano, or a C.sub.(7-13) aralkyl radical, R.sup.2 is a C.sub.(1-13) monovalent substituted or unsubstituted hydrocarbon radical, X is a hydrolyzable leaving group selected from the group consisting of amido, amino, carbamato, enoxy, imidato, isocyanato, oximato, thioisocyanato and ureido radicals and, c is an integer equal to 0 to 3 inclusive, f is an integer equal to 1 to 4 inclusive, and the sum of c+f is equal to 1 to 4 inclusive, and thereafter adding an effective amount of a condensation catalyst, whereby improved stability is achieved in the resulting room temperature vulcanizable organopolysiloxane composition, and where X is enoxy, adding before or with the scavenger an effective amount of a curing accelerator selected from the group consisting of substituted guanidines, amines and mixtures thereof.
- 10. A method in accordance with claim 9, where the silane scavenger is methyldimethoxy-N-methylacetamidosilane.
- 11. A method in accordance with claim 9, where the silane scavenger is methyldimethoxyisopropenoxysilane.
- 12. A method in accordance with claim 9, where the silane scavenger is methyltriisopropenoxysilane.
- 13. A method in accordance with claim 9 using an effective amount of dibutyltindiacetate as the condensation catalyst.
CROSS REFERENCE TO RELATED APPLICATIONS
This application is a division of application Ser. No. 277,524, filed June 26, 1981, now U.S. Pat. No. 4,395,526.
Reference is made to copending application RD-13421, of John E. Hallgren, for Dialkoxysilylenolethers and method for making.
US Referenced Citations (14)
Divisions (1)
|
Number |
Date |
Country |
Parent |
277524 |
Jun 1981 |
|