This application claims the priority benefit of China application serial no. 202210543986.1, filed on May 19, 2022. The entirety of the above-mentioned patent application is hereby incorporated by reference herein and made a part of this specification.
The present disclosure belongs to the technical field of preparation of nano-structured functional materials and environmental materials, and specifically relates to a one-step method for preparing magnetic magnesium-iron layered double hydroxide (LDH)-biochar composite material and use thereof.
Phosphorus is an essential element for life. But if the phosphorus in phosphorus-containing wastewater is not treated well and the phosphorus enters an aquatic system, negative effects, such as eutrophication of the aquatic system, will be caused. Therefore, there is a great potential to develop an efficient and sustainable method to remove the phosphorus from the phosphorus-containing wastewater and recover it as a resource. Currently, biological treatment, membrane separation, chemical precipitation, electrolysis, adsorption, etc. have been studied. Among these technologies, adsorption is considered as a promising method due to its low cost, high selectivity, eco-friendliness and ease of operation.
Biochar has obvious advantages of consuming low production energy and reducing carbon emission in environmental application. In addition, a large amount of a low-cost waste is used as a raw material for producing the biochar, thus the biochar is an ideal sustainable adsorbent for water treatment. The surface of the biochar can be modified by chemical activation or a biochar-based composite material can be manufactured to further improve an adsorption capacity of the biochar. Hydrotalcite, layered double hydroxide (LDH), has gained a wide attention in many fields such as water treatment due to a strong ion exchange capacity. The LDH has a general form of [M2+1−xM3+x(OH)2]·[An−x/n·mH2O], wherein M2+ and M3+ are divalent and trivalent metal cations separately, x is a molar ratio of the trivalent metal cations, and An− is an anion in an interlayer. A synergistic effect of the LDH and the biochar obviously improves physicochemical properties, such as a specific surface area, surface functional groups, structural heterogeneity, stability and adsorption characteristics, of a biochar/LDH composite material. Besides, due to sustainability, low cost and great potential of effectively removing various pollutants, more and more researchers pay attention to loading the LDH on the biochar to remove the pollutants.
At present, the LDH-biochar composite material is mainly prepared by three methods, namely hydrothermal synthesis, coprecipitation of an LDH salt on a surface of biochar and co-pyrolysis after coprecipitation of an LDH salt on a surface of a biomass. Since the coprecipitation is economic and high-yield, it is most commonly used for preparing the LDH-biochar composite material. However, the coprecipitation usually requires a long aging time and a relatively strict control of pH. Besides, a formation of a large number of crystallization nuclei also results in LDH particles with a low crystallinity. The low cost of the LDH-biochar composite material is relative, thus it is difficult to be really applied and popularized in the environmental protection industry with a low economic benefit.
In 2019, Lee, et al. added magnesium nitrate and aluminum nitrate into sodium hydroxide to adjust pH, magnesium-aluminum LDH was coprecipitated on a surface of rice hull powder, and magnesium-aluminum LDH-rice hull biochar composite material was synthesized by co-pyrolysis, specifically as follows: 1) 1 g of rice hull powder was put into 80 ml of a solution containing a certain concentration of magnesium nitrate hexahydrate and aluminum nitrate nonahydrate, and an obtained mixture was vibrated for one hour at a room temperature and at a rotating speed of 300 r/min; 2) during the vibration, sodium hydroxide with a concentration of 5 M was dripped in to keep a pH of the solution constant at 10.0; 3) an obtained mixture was aged at 50° C. for 72 h; 4) a sample was collected, washed with deionized water, and dried at 80° C. overnight; 5) the dried sample was put into a tubular quartz furnace for pyrolysis at a heating rate of 10° C./min within a temperature range (300-700° C.), and nitrogen was continuously introduced during the pyrolysis; 6) prepared biochar was collected and washed with deionized water; and 8) the washed material was dried at 80° C. In the technology, rice hulls were used as a biomass raw material, magnesium nitrate and aluminum nitrate were added, pH was adjusted by sodium hydroxide, magnesium aluminum hydrotalcite was preloaded on rice hull powder, and pyrolysis was carried out to prepare the magnesium-aluminum LDH-rice hull biochar composite adsorbing material. The preparation is complex, has a relatively high requirement on experiment operations, and requires a long aging time (72 h), the material after adsorption is difficult to recover, thus the technology is not suitable for practical application.
Aiming at problems in the prior art, the present disclosure provides a simple one-step method for preparing a layered double hydroxide (LDH)-biochar composite material by carrying out a series of improvements on pretreatment, medicine use and the like. A material precursor magnesium-iron LDH-biomass prepared by the method is aged in a shorter time to obtain an LDH with a higher yield and crystallinity, pyrolysis is carried out at a certain temperature to obtain a magnetic magnesium-iron LDH-biochar composite material, the material contains magnesium-iron LDH particles on a surface, an LDH layered structure can be reconstructed after phosphate in water is adsorbed, and a recovery rate can 98% or more using a strong magnet. Based on characteristics of insolubility and complete ionization of Mg(OH)2 in an aqueous solution, the method realizes controllable coprecipitation and pH control, and does not need to carry out long-time crystallization and pH control.
The present disclosure is specifically realized by the following technical solutions.
A one-step method for preparing a magnetic magnesium-iron LDH-biochar composite material includes the following steps:
Furthermore, the biomass is selected from corn stalk and the corn stalk is dried to a moisture content ≤5%; and the dried corn stalk is crushed to be capable of passing through a 20-40 mesh sieve.
Furthermore, in step 2), the ferric salt is one or more of FeCl3, Fe(NO3)3, and Fe2(SO4)3.
Furthermore, in step 2), the magnesium hydroxide and the ferric salt have a molar ratio of (2-4):1.
Furthermore, in step 2), the aging is performed at 60±10° C. for 2-4 h.
Furthermore, in step 2), an adding amount of the biomass and the ferric salt solution is that 5-10 g of the biomass is added into every 100 ml of the ferric salt solution.
Furthermore, in step 3), the drying is performed in an oven at a temperature of 50±5° C.
Furthermore, in step 4), the pyrolyzing is performed in the inert gas of nitrogen and at a temperature of 500±200° C. for 2±0.5 h.
Use of the composite material prepared by any of the above methods in phosphate adsorption in water treatment is provided.
The adsorbing material is recycled by the following steps: performing solid-liquid separation and recovery on the adsorbing material in wastewater within 5 s using a strong magnet.
The present disclosure utilizes characteristics of insolubility and complete ionization of Mg(OH)2 in an aqueous solution, a magnetic magnesium-iron LDH-biochar is prepared in one step, and the preparation is simple and convenient, and has a wide raw material source and a low cost; and the prepared material is composed of biochar embedded (wrapped) by magnesium-iron LDH and a magnesium-iron oxide, the attached magnesium-iron LDH and magnesium-iron oxide can effectively remove phosphorus in an aqueous solution, and the magnetic material is easy to separate and recycle.
A magnetic magnesium-iron LDH-biochar composite material was prepared in one step: a specific preparation route was compared with a traditional preparation route shown in
the dried solid was pyrolyzed at 500° C. for 2 h under a nitrogen atmosphere to obtain an LDH biochar-loaded composite material.
A scanning electron microscope image of the magnetic magnesium-iron LDH-biochar composite material prepared in the example was shown in
The LDH-biochar composite material was proved to be magnetic by using a strong magnet for recovery in an aqueous solution. A recovery effect was shown in
An adsorption test of removing phosphate radicals in water using the magnetic magnesium-iron LDH-biochar composite material prepared by the method of the present example was specifically as follows:
Preparation of stock solution: 1,000 mg/L of a PO43−solution: 1.4315 g of KH2PO4 was weighed and dissolved in 1 L of deionized water to prepare the solution.
Preparation of adsorption solution: the PO43− stock solution was diluted with deionized water to prepare an adsorption solution of a corresponding concentration.
0.04 g of the magnetic magnesium-iron LDH-biochar composite material was weighed and placed in a 50-ml centrifuge tube, 40 ml of the PO43−solution with concentrations of 50/100/200 mg/L was separately added, shaking and adsorption were performed at 25° C. and 200 rpm for 24 h, a supernatant was extracted and filtered with a 45-μm microporous membrane, a concentration of phosphate radicals in the supernatant was determined by ultraviolet spectrophotometry, and the adsorption capacity and a removal rate were calculated.
The concentration of phosphate radicals in the solution was determined by a national standard method of ascorbic acid-molybdenum blue colorimetry, and ascorbic acid-molybdate was used as a color developer to generate a blue compound which was determined by an ultraviolet spectrophotometer at a wavelength of 700 nm.
“67.625 g (0.25 mol) FeCl3·6H2O was weighed” and “29 g (0.5 mol) of Mg(OH)2 was finally slowly added” in step 2) of example 1, and “pyrolyzed at 500° C. for 2 h under a nitrogen atmosphere” in step 4) were separately modified to observe an effect of different modifications on removing phosphorus from the magnetic magnesium-iron LDH-biochar composite material. The modifications were shown in Table 1.
An experiment was carried out under the method and conditions in example 1, and the adsorption test was carried out on the PO43−solution of 50-200 mg/L. The obtained results were shown in Table 2.
The magnesium hydroxide in step 2) of example 1 was replaced with magnesium chloride, and the remaining was the same as in example 1.
Magnesium-aluminum LDH-biochar composite material Preparation method: sodium hydroxide (NaOH) was added into magnesium nitrate hexahydrate (Mg(NO3)2·6H2O) and aluminum nitrate nonahydrate (Al(NO3)3·9H2O) at a molar ratio of 2:1, magnesium-aluminum LDH was generated on a surface of rice hull powder by coprecipitation and co-pyrolysis was performed at 500° C. for 2 h.
0.1 g of the magnesium-aluminum LDH-biochar composite material was placed in a 100-ml conical flask, and 80 ml of a phosphate solution with a concentration of 50-100 mg/L was added to conduct an adsorption test.
Iron-magnesium LDH material Preparation method: the iron-magnesium LDH material was prepared by adding sodium hydroxide (NaOH) to a solution of magnesium chloride hexahydrate (MgCl2·6H2O) and ferric chloride (FeCl3) at a molar ratio of 2:1 for precipitation.
0.025 g of the material obtained in example 1 and 0.025 g of the material obtained in comparative examples 1-3 were separately taken and placed in a 50-ml conical tube, 25 ml of a phosphate solution (pH=7.4) with a concentration of 50 mg/L was added into each conical tube, and an adsorption test was performed under the same condition. The test results were shown in Table 3.
It can be seen from Table 3 that the magnetic magnesium-iron LDH-biochar composite material prepared by the innovative synthesis method of the present disclosure had the highest removal rate and adsorption capacity of phosphorus in a phosphate solution with a concentration of 50 mg/L.