Optical amplifier glass

Abstract

An optical amplifier glass comprising a matrix glass containing Bi2O3 and at least one of Al2O3 and Ga2O3, and Er doped to the matrix glass, wherein from 0.01 to 10% by mass percentage of Er is doped to the matrix glass which has a total content of Al2O3 and Ga2O3 of at least 0.1 mol %, a content of Bi2O3 of at least 20 mol %, a refractive index of at least 1.8 at a wavelength of 1.55 μm, a glass transition temperature of at least 360° C. and an optical basicity of at most 0.49.

Description

BACKGROUND OF THE INVENTION

[0001] 1. Field of the Invention

[0002] The present invention relates to an optical amplifier glass, particularly a broadband optical amplifier glass which is operable in a wavelength range of from 1.55 to 1.65 μm.

[0003] 2. Discussion of Background

[0004] For the purpose of application to the optical communication field, there have been research and development of an optical fiber amplifier using as an optical amplification medium an optical fiber having a rare earth element doped to the core, and an Er (erbium)-doped optical fiber amplifier (EDFA), and their application to an optical communication system is being actively pursued. On the other hand, to cope with diversification of communication services expected in future, a wavelength division multiplexing communication system (WDM) has been proposed to increase the transmission capacity. As the number of wavelength division multiplexing channels increases, the transmission capacity will increase. Application of EDFA to such a wavelength division multiplexing transmission system is also being studied. As EDFA so far proposed, an Er-doped quartz type fiber and an Er-doped fluoride fiber are known.

[0005] In the case of a conventional Er-doped quartz type fiber, the wavelength dependency of the gain is sharp, and the wavelength width wherein an adequate gain is obtainable, is as narrow as from about 10 to 30 nm. Consequently, so far as such conventional EDFA is employed, the number of wavelength division multiplexing channels is limited to a level of from 30 to 40 channels.

[0006] If EDFA showing a flat gain within a wider wavelength range, is realized, it is expected to be able to broaden the useful signal wavelength and thereby to substantially improve the transmission capacity. Accordingly, development of such EDFA is desired.

[0007] In order to solve such problems, an optical amplifier which can be used in a wide wavelength range has been proposed wherein amplifiers having different amplification gain characteristics to wavelengths, are arranged in series or in parallel, but there has been a problem such that the structure tends to be cumbersome, or in the vicinity of the center of the wavelength range, there is a region where no amplification is possible. Further, JP-A-8-110535 proposes a tellurite type glass as a glass capable of amplification in a broadband range. However, such tellurite type glass usually has a low glass transition point and is thermally unstable. In order to improve the amplification gain of an optical amplifier, it is necessary to let a high intensity excited laser beam enter into the glass, but such glass was likely to be thermally damaged by the strong laser beam.

SUMMARY OF THE INVENTION

[0008] It is an object of the present invention to solve the above-mentioned problems and to provide an optical amplifier glass having a high glass transition point and having a wide wavelength width wherein the gain is obtainable.

[0009] The present invention provides an optical amplifier glass comprising a matrix glass containing Bi2O3 and at least one of Al2O3 and Ga2O3, and Er doped to the matrix glass, wherein from 0.01 to 10% by mass percentage of Er is doped to the matrix glass which has a total content of Al2O3 and Ga2O3 of at least 0.1 mol %, a content of Bi2O3 of at least 20 mol %, a refractive index of at least 1.8 at a wavelength of 1.55 μm, a glass transition temperature of at least 360° C. and an optical basicity of at most 0.49.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0010] With an optical amplifier glass having Er-doped to a matrix glass, optical amplification is carried out by means of stimulated emission transition from the 4I{fraction (13/2)} level to the 4I{fraction (15/2)} level of Er. The present inventors have found that the wavelength width wherein the optical amplification gain is obtainable, is dependent on the optical basicity which will be described hereinafter, and have thus arrived at present invention. The wavelength width within which the optical amplification gain is obtainable, will hereinafter be referred to as “the gain wavelength width”.

[0011] The gain wavelength width has heretofore been considered to be as follows. Namely, the gain wavelength width is dependent on the refractive index of the matrix glass, i.e. the gain wavelength width increases as the refractive index increases. This has been explained such that the electric field which Er receives in the matrix glass increases as the refractive index increases, and consequently, the energy level of Er is broadened, whereby the emission spectrum becomes broad.

[0012] However, the present inventors have found that the gain wavelength width Δλ is not only dependent on the refractive index of the matrix glass but also strongly dependent on the optical basicity Λ of the matrix glass, which will be described hereinafter, i.e. Δλ becomes large as Λ becomes small.

[0013] With respect to a glass composition represented by mol % of oxide components, the optical basicity Λ is defined as follows. Namely, with a glass containing Ci mol % of an oxide of component i,

Λ=1−Θ[zi·ri(γi−1)/2γi]

[0014] Σ indicates summing up with respect to subscript i

γi=1.36(xi−0.26)

[0015] zi: valency of the cation in the oxide of component 1,

[0016] ri: the ratio of the number of cations in the oxide of component i to the total number of oxygen in the above “glass composition represented by mol % of oxide components”,

[0017] xi: the Pauling's electronegativity of an atom bonded to oxygen in the oxide of component i.

[0018] For reference, the Pauling's electronegativities of main atoms are shown below.

[0019] Li:1.0, Na:0.9, K:0.8, Mg:1.2, Ca:1.0, Sr:1.0, Zn:1.6, Ba:0.9, B:2.0, Al:1.5, Si:1.8, P:2.1, Ge:1.8, Ga:1.6, Te:2.1, Sn:1.8, Sb:1.9, W:1.7, Pb:1.8, Bi:1.9, and Ti:1.5.

[0020] For example, with respect to a glass wherein the oxide of the first component is Bi2O3, and the oxide of the second component is SiO2, and the composition represented by mol % is 20Bi2O3/80SiO2,

[0021] z1=3, z2=4

[0022] Total number of oxygen=0.2×3+0.8×2=2.2,

[0023] r1=0.2×2/2.2, r2=0.8×1/2.2,

[0024] x1=1.9, x2=1.8,

[0025] Λ=0.47.

[0026] The optical basicity is one which Duffy et al. have proposed as an index of the basicity of glass in J. Am. Chem. Soc., 93 (1971) 6448, and it is one obtainable by a simple calculation from the glass composition without necessity of carrying out the measurement or complex analysis or calculation.

[0027] Now, the relation between Λ and Δλ will be described based on data.

[0028] Glasses A to I having Er doped to a matrix glass having a composition shown by mol % in lines for from Bi2O3 to ZnO in Table 1, were prepared. The amount of Er doped, is shown in the line for Er in Table 1 by mass % based on the matrix glass being 100%. With respect to these glasses, the refractive index n at a wavelength of 1.55 um, the glass transition point Tg (unit: ° C.) and the gain wavelength width Δλ (unit: nm) were measured. Further, the optical basicity Λ was calculated from the composition. The measuring methods for n, Tg and Δλ were as follows.

[0029] n: measured by an Ellipsometer.

[0030] Tg: measured by a differential thermal analysis (DTA).

[0031] Δλ: excited by a laser beam with a wavelength of 980 nm, and it was obtained from the emission spectrum obtained by this excitation.

BRIEF DESCRIPTION OF THE DRAWINGS

[0032] FIG. 1 is a graph showing the relation between the optical basicity Λ of glass and the wavelength width Δλ (unit: nm) wherein the optical amplification gain is obtainable.

[0033] FIG. 2 is a graph showing the relation between the optical basicity Λ of an optical amplifier glass of the present invention and the wavelength width Δλ (unit: nm) wherein the optical amplification gain is obtainable.

[0034]

	TABLE 1
	A	B	C	D	E	F	G	H	I
Bi2O3	—	—	40	—	—	—	20	—	—
B2O3	—	—	20	—	20	—	—	—	—
SiO2	—	70	20	—	70	—	50	—	97.9
Al2O3	—	—	—	—	—	—	—	—	0.1
GeO2	—	—	—	—	—	—	—	—	2
TiO2	—	—	—	—	—	—	10	—	—
TeO2	75	—	—	75	—	75	—	75	—
Na2O	5	20	20	20	10	15	10	7	—
CaO	—	10	—	—	—	—	—	—	—
BaO	—	—	—	—	—	—	10	—	—
ZnO	20	—	—	5	—	10	—	18	—
Er	0.5	0.5	0.5	2.5	1.0	1.0	0.5	0.5	0.05
n	2	1.5	2	1.9	1.5	1.92	1.8	1.97	1.49
Tg	299	550	370	270	490	285	470	292	1010
Λ	0.438	0.587	0.505	0.490	0.495	0.455	0.547	0.445	0.478
Δλ	69	18	30	35	32	48	22	59	3838

[0035] FIG. 1 is a graph wherein the relation between Λ and Δλ in Table 1, was plotted.

[0036] As is evident from FIG. 1, Δλ increases as Λ becomes small. The reason is not clearly understood, but it is considered that in a matrix glass having small Λ, the polarizability of O (oxygen) ions surrounding Er ions tends to decrease, whereby the electrical shielding effect of Er ions tends to be large, and consequently, the proportion of the electric dipole transition to the magnetic dipole transition of Er tends to be large.

[0037] Further, as is evident from Table 1, even with glasses having substantially the same refractive index n, Δλ is not necessarily the same. For example, n of each of glass A and glass C is 2, Δλ of glass A is 69 nm, and Δλ of glass C is 30 nm, and thus, the difference in Δλ of the two is substantial. Such a difference can not be expected by the conventional concept such that Δλ is dependent largely on n, and can be expected for the first time by the discovery relating to Λ and Δλ by the present inventors.

[0038] The optical amplifier glass of the present invention is used usually in the form of a fiber.

[0039] In the optical amplifier glass of the present invention, from 0.01 to 10% by mass percentage of Er is doped in the matrix glass. Here, the matrix glass is regarded as 100%. The matrix glass in the optical amplifier glass of the present invention will be referred to hereinafter simply as the matrix glass of the present invention.

[0040] If the amount of Er is less than 0.01%, the desired optical amplification can not be obtained. Preferably, it is at least 0.1%, more preferably at least 0.3%. If it exceeds 10%, optical quenching by concentration tends to occur, whereby the optical amplification tends to decrease. It is preferably at most 5%, more preferably at most 1%. When the optical amplifier glass of the present invention is used in the form of a fiber, the amount of Er is preferably adjusted depending upon the length of the fiber. Namely, it is preferred that when the fiber is long, the amount is adjusted to be small, and when the fiber is short, the amount is adjusted to be large.

[0041] The refractive index at a wavelength of 1.55 μm of the matrix glass of the present invention is at least 1.8. If it is less than 1.8, the electric dipole transition of Er tends to hardly take place, whereby Δλ tends to be too small. It is preferably at least 1.9, more preferably at least 2.0.

[0042] The glass transition point of the matrix glass of the present invention is at least 360° C. If it is less than 360° C., when the temperature of glass becomes locally high by the use of a laser beam of high intensity as an excitation light, the glass tends to be thermally damaged, and the desired optical amplification tends to hardly be obtained. It is preferably at least 380° C., more preferably at least 400° C.

[0043] The optical basicity of the matrix glass of the present invention is at most 0.49. If it exceeds 0.49, Δλ tends to be too small. It is preferably at most 0.485, more preferably at most 0.48.

[0044] To reduce the optical basicity, it is preferred to introduce into the glass atoms having large values of the above-mentioned zi (valency of the cation) and/or the above-mentioned xi (the Pauling's electronegativity of atoms). As such atoms, Bi, Si, Al or Ga may, for example, be mentioned. Accordingly, it is preferred that the matrix glass of the present invention is a Bi2O3/SiO2/M2O3 type glass. Here, M2O3 is Al2O3 and/or Ga2O3.

[0045] Now, the composition of the matrix glass of the present invention will be described, wherein mol % will be represented simply as %.

[0046] Bi2O3 is an essential component. If it is less than 20%, the electric dipole transition of Er tends to hardly occur, whereby Δλ tends to be too small. It is preferably at least 25%, more preferably at least 30%. Further, its content is preferably at most 80%. If it exceeds 80%, vitrification tends to be difficult, or devitrification tends to take place during processing into a fiber, or the glass transition point tends to be too low. Preferably, it is at most 70%, more preferably at most 65%. Here, devitrification is meant for distinct precipitation of crystals, which causes breakage of the fiber during the fiber processing or the breakage of the fiber during use as an optical amplifier glass fiber.

[0047] At least one of Al2O3 and Ga2O3 must be contained. If the total content thereof is less than 0.1%, crystallization of glass is likely to take place. It is preferably at least 1%. Further, the total content is preferably at most 30%. If it exceeds 30%, vitrification tends to be difficult, or the glass transition point tends to be too low. It is more preferably at most 25%.

[0048] The content of Al2O3 is preferably at most 10%. If it exceeds 10%, the optical amplification is likely to deteriorate. It is more preferably at most 8%, particularly preferably at most 6%. When Al2O3 is contained, the content is preferably at least 0.1%, more preferably at least 1%.

[0049] The content of Ga2O3 is preferably at most 30%. If it exceeds 30%, the optical amplification is likely to deteriorate, or the glass transition point is likely to be too low. It is more preferably at most 20%. When Ga2O3 is contained, the content is preferably at least 0.1%, more preferably at least 1%.

[0050] B2O3 is not an essential component, but it is a network former and is preferably contained in a range of up to 75% in order to facilitate formation of glass by suppressing precipitation of crystals during the preparation of glass. It is more preferably at most 50%, particularly preferably at most 30%. When B2O3 is contained, the content is preferably at least 1%.

[0051] Further, in some cases, it is preferred that the B2O3 content is less than 15%. For example, such is preferred when the total content of Al2O3 and Ga2O3 exceeds 1%.

[0052] SiO2 is not an essential component, but it is a network former and is preferably contained in a range of up to 79.9% in order to facilitate formation of glass by suppressing precipitation of crystals during the preparation of glass. It is more preferably at most 50%, particularly preferably at most 40%. When SiO2 is contained, the content is preferably at least 1%.

[0053] Further, the total content of Bi2O3 and SiO2 is preferably at least 50%.

[0054] In order to facilitate formation of glass by suppressing precipitation of crystals during the preparation of glass, it is preferred to incorporate at least one of B2O3 and SiO2. The total content thereof is preferably within a range of from 5 to 60%. If it is less than 5%, vitrification is likely to be difficult, or the optical amplification tends to be inadequate, or devitrification is likely to occur during the fiber processing. It is more preferably at least 10%, particularly preferably at least 15%. If it exceeds 60%, the optical amplification is likely to be inadequate. It is more preferably at most 55%, particularly preferably at most 50%.

[0055] GeO2 is not essential, but it facilitates formation of glass and has an effect to increase the refractive index. Thus, it may be doped up to 30%. If it exceeds 30%, the glass tends to crystallize. It is preferably at most 10%, more preferably at most 5%. When GeO2 is contained, the content is preferably at least 0.1%, more preferably at least 1%.

[0056] Each of Li2O, TiO2, ZrO2 and SnO2 is not essential, but each of them may be doped within a range of up to 50% in order to suppress devitrification during fiber processing. Each content is preferably at most 10%.

[0057] WO3 is not essential but may be doped up to 30% in order to increase Δλ. If the content exceeds 30%, the optical amplification is likely to deteriorate. It is more preferably at most 20%, particularly preferably at most 10%.

[0058] TeO2 is not essential but may be doped up to 30% in order to increase Δλ. If the content exceeds 30%, the optical amplification is likely to deteriorate. It is more preferably at most 20%, particularly preferably at most 17%.

[0059] The total content of WO3 and TeO2 is preferably at most 27%. If the total content exceeds 27%, crystals are likely to precipitate, whereby vitrification or fiber processing tends to be difficult. It is more preferably at most 20%, particularly preferably at most 15%.

[0060] CeO2 is not essential, but it has an effect to suppress reduction of Bi2O3 in the glass composition during melting of glass to precipitate metal bismuth thereby to lower the transparency of glass and may be doped up to 10%. If it exceeds 10%, vitrification tends to be difficult. It is more preferably at most 1%, particularly preferably at most 0.5%.

[0061] Further, if CeO2 is contained, it may happen that yellow or orange coloring tends to increase, whereby the transmittance of glass tends to decrease, and the background loss at an excitation light wavelength (such as 980 nm) or a signal light wavelength tends to increase. From this viewpoint, the content of CeO2 is preferably less than 0.15%, particularly preferably substantially zero.

[0062] It is preferred that the matrix glass of the present invention consists essentially of the above described components, but components other than the above described components (“other components”) may be contained within a range not to impair the purpose of the present invention. For example, to facilitate vitrification or to suppress devitrification during fiber processing, BeO, MgO, CaO, SrO, BaO, Na2O, K2O, Cs2O, La2O3, ZnO, CdO, In2O3 or PbO may, for example, be contained. The total content of such other components is preferably not more than 10%.

[0063] As a preferred composition of the matrix glass of the present invention, the following may be mentioned, as represented by mol % based on the following oxides:

Oxides Mol %
Bi2O3  20 to 80,
B2O3   0 to 75,
SiO2   0 to 79.9,
Al2O3  0 to 10,
Ga2O3  0 to 30,
GeO2   0 to 30,
Li2O   0 to 50,
TiO2   0 to 50,
ZrO2   0 to 50,
SnO2   0 to 50,
WO3    0 to 30,
TeO2   0 to 30, and
CeO2   0 to 10,

[0064] wherein at least one of B2O3 and SiO2 is contained, and the total content of Al2O3 and Ga2O3 is at least 0.1 mol %.

[0065] The method for preparing the optical amplifier glass of the present invention is not particularly limited, and it can be prepared by mixing the prescribed starting materials, putting the mixture into a platinum crucible, an alumina crucible, a quartz crucible or an iridium crucible, melting it in air at a temperature of from 800 to 1,300° C., and casting the obtained melt in a prescribed mold. Otherwise, it may be prepared by a method other than the melting method, such as a sol gel method or a gas phase vapor deposition method.

[0066] From the glass thus prepared, a preform may be prepared and formed into a fiber, or such a glass may be formed into a fiber by a double crucible method, to obtain an optical amplifier fiber.

[0067] Now, the present invention will be described in further detail with reference to Examples. However, it should be understood that the present invention is by no means restricted to such specific Examples.

EXAMPLES

[0068] Glasses 1 to 10 were prepared which had Er doped to the matrix glasses having the compositions shown by mol % in lines from Bi2O3 to CeO2 in Table 2. The amount of Er doped is represented by mass %, based on the matrix glass being 100%. With respect to each of these glasses, the refractive index n at a wavelength of 1.55 μm, the glass transition point Tg (unit: ° C.) and the gain wavelength width Δλ (unit: nm) were measured by the above-mentioned methods. Further, from the composition, the optical basicity Λ was calculated. Glasses 1 to 9 represent Working Examples of the present invention. Glass 10 is an Er-doped quartz type glass which is the same as glass 1 in Table 1 and represents a Comparative Example.

[0069] FIG. 2 is a graph wherein the relation between Λ and Δλ in Table 2 was plotted. As is evident from this Figure, Δλ increases as Λ becomes small. Here, Δλ is preferably at least 40 nm.

	TABLE 2
	1	2	3	4	5	6	7	8	9	10
Bi2O3	43	43	43	45	40	43	43	43	62.8	—
B2O3	—	—	—	5	1	27	28	28	30	—
SiO2	29	36	22	20	20	20	21	14	4	97.9
Al2O3	3	3	3	2	2	1	—	1	—	0.1
Ga2O3	18	18	18	8	19	—	1	—	3	2
GeO2	—	—	—	—	—	2	—	—	—	—
TiO2	—	—	—	—	6	—	—	—	—	—
SnO2	—	—	—	6	—	—	—	—	—	—
WO3	—	—	—	2	2	7	—	—	—	—
TeO2	7	—	14	12	10	—	7	14	—	—
CeO2	—	—	—	—	—	—	—	—	0.2	—
Er	0.5	0.5	0.5	2.5	1.0	1.0	0.5	0.5	0.5	0.05
n	2.02	2.01	2.01	2.10	2.05	2.01	2.01	2.02	2.21	1.49
Tg	450	475	420	440	445	420	415	410	370	1010
Λ	0.478	0.482	0.473	0.462	0.482	0.452	0.443	0.440	0.444	0.478
Δλ	42	40	45	50	50	58	69	74	68	38

[0070] By employing the optical amplifier glass of the present invention, optical amplification within a broader band will be possible, and transmission of information of a large capacity by a wavelength division multiplexing transmission system will be possible. Further, the thermal damage scarcely occurs even if a high intensity laser beam is used as the excitation light.

[0071] Obviously, numerous modifications and variations of the present invention are possible in light of the above teachings. It is therefore to be understood that within the scope of the appended claims, the invention may be practiced otherwise than as specifically described herein.

[0072] The entire disclosure of Japanese Patent Application No. 2000-17448 filed on Jan. 26, 2000 including specification, claims, drawings and summary are doped herein by reference in its entirety.

Claims

1. An optical amplifier glass comprising a matrix glass containing Bi2O3 and at least one of Al2O3 and Ga2O3, and Er doped to the matrix glass, wherein from 0.01 to 10% by mass percentage of Er is doped to the matrix glass which has a total content of Al2O3 and Ga2O3 of at least 0.1 mol %, a content of Bi2O3 of at least 20 mol %, a refractive index of at least 1.8 at a wavelength of 1.55 μm, a glass transition temperature of at least 360° C. and an optical basicity of at most 0.49.

2. The optical amplifier glass according to claim 1, wherein the matrix glass consists essentially of the following, as represented by mol % based on the following oxides:

3. The optical amplifier glass according to claim 1 or 2, wherein the matrix glass contains B2O3 in a content of less than 15 mol %.

4. The optical amplifier glass according to claim 1, 2 or 3, wherein the matrix glass contains GeO2 in a content of from 0.1 to 30 mol %.

5. The optical amplifier glass according to any one of claims 1 to 4, wherein the matrix glass contains CeO2 in a content of less than 0.15 mol %.

6. The optical amplifier glass according to any one of claims 1 to 4, wherein the matrix glass contains substantially no CeO2.