The invention relates to an optical article comprising a base lens substrate covered with an abrasion-resistant coating and having at least one optical element such as a microlens, a Fresnel structure, etc. The invention also relates to a manufacturing method of said optical article.
Optical articles such as lenses generally comprise a base-lens substrate which is shaped in order to provide a desired optical power, and an anti-abrasion coating covering at least one surface of the base-lens substrate to prevent the latter from being damaged by scratches.
An anti-abrasion coating, also known as hard coating, provides, according to a favorite embodiment with a bi-layered structure, a hardness gradient from the base-lens substrate to the free surface of the anti-abrasion coating. The upper layer of the coating defines the hardest part of the coating at the free surface thereof and allows a protection against thin particles and thin scratches, while the lower layer of the coating defines the less hard part underneath can absorb shocks provided by bigger particles and prevent formation of larger scratches. It also provides a transition with the hardness of the base-lens substrate to prevent formation of cracks at the interface between the substrate and the abrasion-resistant coating.
For a number of applications, it has been found desirable to provide on the base-lens substrate a plurality of microlenses, providing a local change of the power of the optical article. For instance, it is known from US 2017/0131567 a lens comprising a plurality of microlenses formed on a surface of the lens, the local change of power provided by the microlenses enabling to suppress or slow down the progress of myopia.
It is also known from document WO2016/168746 a lens having a first optical power, the lens comprising an array of microlenses having a second optical power, the microlenses allowing to increase the correction provided by the lens even though the curvature of the lens is limited, or allowing forming multifocal lenses with large areas of different optical powers while not exhibiting sharp steps that are visible at a micro-scale.
With reference to
As shown on
A solution has been proposed consisting of reducing the thickness of the abrasion-resistant coating to reduce this alteration of the microlenses power. However, it has been measured that there still remains an alteration of the power since the local power P′ of the microlenses covered with this coating is about P-0,5 (P being the initial power of the microlenses without coating). Furthermore, the properties of protection against scratching of the coating are highly reduced, so this solution is not satisfactory.
The same kind or problem arises for other optical structures which are made in relief from a base-lens substrate. For instance, structures such as Fresnel rings also undergo a perturbation of power when covered by an abrasion-resistant coating.
Another issue arises with some technical permanent markings which are performed on multi-focal lenses to distinguish between a top and a bottom of a lens for later insertion in a frame by an optician. Upon forming an abrasion-resistant coating, the material used to form the coating fills in the groove and makes it invisible.
The purpose of the invention is to provide a solution to the defects in the prior art.
In particular, one aim of the invention is to provide an optical article comprising a base-lens substrate, an abrasion-resistant coating protecting said substrate, and an optical element, wherein the abrasion-resistant coating does not reduce or suppress the optical effect of the optical element.
The above-mentioned purpose is achieved by a combination of the characteristics described in the independent claims, and subordinate claims provide for specific advantageous examples of the invention.
An optical article and a method of manufacturing the same are disclosed.
In an embodiment, an optical article is disclosed, comprising:
In an embodiment, the thickness of a layer composed of the abrasion resistant coating and the at least one optical element protruding thereof is maximal at the optical element.
In an embodiment, the abrasion resistant coating may be formed of the same material as the one of which is composed the optical element.
In an embodiment, the optical element protrudes from the second surface of the abrasion resistant coating.
In an embodiment, the optical element protrudes from the first surface of the abrasion resistant coating towards the base lens substrate, and the base lens substrate comprises at least one recess in the surface at the interface with the abrasion resistant coating, said recess having a shape complementary to the shape of the optical element so that each optical element is received in a respective recess.
In an embodiment, the optical element defines a local change of optical power of the optical device, the material forming the optical element has an optical index nM, and the base lens substrate has at least one layer in which each recess is formed, said layer being made in a material having an optical index nS such that the optical index nM is different from the optical index nS.
In an embodiment, the layer of the base substrate in which each recess is formed has an optical index nS nS<nM, and the base substrate further comprises a second layer assembled to the first layer on a surface opposite the surface on which is formed each recess, the second layer having a refraction index NHI greater than the refraction index nS of the first layer.
In an embodiment, the optical index nS of the layer of the base lens substrate in which each recess is formed is such that nS−nM≥0.1, and the optical article further comprises a quarter-wave layer interposed between the abrasion resistant coating and the base substrate.
In an embodiment, the optical element is chosen among the following group:
In an embodiment, the optical device further comprises an anti-reflection coating over said second surface of the abrasion-resistant coating.
In an embodiment, the base lens substrate comprises at least a plano wafer or a base lens having optical power.
A method for manufacturing an optical article, comprising:
In an embodiment, the abrasion-resistant coating is formed on the front or back surface of the base lens substrate by dipping or spin-coating or additive manufacturing, and the step of forming the at least one microelement is made by additive manufacturing or by photolithography or by thermal embossing a base lens substrate covered by an abrasion resistant coating or by injection of a melt polymer on an abrasion resistant film pushing the later on the inner surface of an injection mold comprising at least a recess having a shape complementary to the shape of an optical element to be formed.
In an embodiment, the abrasion-resistant coating and the optical element are composed of a same material and formed simultaneously by molding.
In an embodiment, the molding step comprises:
In an embodiment, the molding step further comprises steps of:
the base lens substrate is also formed by molding, in a mold comprising two walls of given respective curvatures chosen with respect to the respective front and back surface of the base lens substrate to be formed, one of the walls having at least one protruding element of the shape of the optical element to be formed, such that the base lens substrate comprises, on a front or back surface thereof, at least one recess having a shape complementary to the shape of the optical element to be formed, and the subsequent step of molding the abrasion resistant coating and the optical element comprises:
In an embodiment, the method further comprising forming an anti-reflection coating over the abrasion-resistant coating.
The optical article according to an embodiment of the invention comprises a base-lens substrate and an abrasion-resistant coating, wherein at least one optical element is made protruding from a surface of the abrasion-resistant coating, and formed in a material adapted to compose an abrasion-resistant coating.
Thus, in one embodiment, the abrasion-resistant coating and the optical elements can be formed integrally. Thus the shape of the optical element and its optical power are not impaired by the later deposition of a coating, since it belongs to said coating and therefore the detrimental effects disclosed before related to the deposition of the coating do not happen.
According to an embodiment, the optical elements are protruding from a surface of the abrasion-resistant coating towards the base-lens substrate, in which are performed complementary recesses in which the protruding elements can be received. According to this embodiment, the optical elements are completely contained within the optical article and the outer surfaces of the optical article do not have any relief, which is preferable for subsequent deposition of other functional coatings such as anti-reflective, anti-soiling, or anti-fogging coatings, aesthetic and comfort.
For a more complete understanding of the description provided herein and the advantages thereof, reference is now made to the brief descriptions below, taken in connection with the accompanying drawings and detailed description, wherein like reference represent like parts.
With reference to
The base lens substrate 10 may comprise a single layer or may be formed of a laminate. The base lens substrate 10 preferably comprises at least a plano wafer 11, or a base lens 12 providing optical power, or both, i.e. a base lens 12 providing optical power and a wafer 11 complementing the base lens 12 with an optical function as described below.
A plano wafer 11 has no optical power and hence provides no correction to the wearer, but acts as a mechanical support for other layers, and optionally also provides one or more functional properties to the finished optical article, such as at least one among the following optical functions:
A plano wafer 11 refers to a film structure formed by either a single film layer or a film laminate structure formed of multiple film layers attached to one another. More precisely, the plano wafer 11 may be formed by one or several ophthalmic-grade function film (with for example polar or photochromic properties), optionally having an ophthalmic-grade protective film on one or both sides of the ophthalmic grade functional film.
A plano wafer 11 may exhibit a thickness in the range of 20 to 700 micrometers, preferably 30 to 600 μm. The protective layer(s), if any, may have a thickness of about 50 μm.
Suitable transparent resin film or sheet materials for forming the plano wafer (including functional and protective films) include poly(vinyl alcohol) (PVA) or cellulose acylate-based materials, for example, cellulose diacetate and cellulose triacetate (TAC). Other usable wafer materials can include polycarbonate, polysulfone, cellulose acetate buturate (CAB) or cyclic oleofin copolymer (COC), polyacrylate, polyester, polystyrene, copolymers of acrylate and styrene, and poly(vinylalcohol) (PVA). Polycarbonate-based materials include, for example, polybisphenol-A carbonate; homopolycarbonate such as 1,1′ dihroxydiphenyl-phenylmethylmethane, 1,1′-dihroxydiphenyl-diphenylmethane, 1,1′-dihydroxy-3,3′-dimethyl diphenyl-2,2-propane, their mutual copolymer polycarbonate and copolymer polycarbonate with bisphenol-A.
The base lens 12 may be formed in organic eyeglass, for example made of thermoplastic or thermosetting plastic. In particular, thermoplastic materials may be selected from, for instance: polyamides, polyimide, polysulfones, polycarbonates and copolymers thereof, poly(ethylene terephtalate) and polymethylmethacrylate (PMMA).
Thermosetting materials may be selected from, for instance: cycloolefin copolymers such as ethylene/norbornene or ethylene/cyclopentadiene copolymers; homo- and copolymers of allyl carbonates of linear or branched aliphatic or aromatic polyols, such as homopolymers of diethylene glycol bis(allyl carbonate) (CR 39®); homo- and copolymers of (meth)acrylic acid and esters thereof, which may be derived from bisphenol A; polymer and copolymer of thio(meth)acrylic acid and esters thereof, polymer and copolymer of allyl esters which may be derived from Bisphenol A or phtalic acids and allyl aromatics such as styrene, polymer and copolymer of urethane and thiourethane, polymer and copolymer of epoxy, and polymer and copolymer of sulphide, disulfide and episulfide, and combinations thereof. As used herein, a (co)polymer is intended to mean a copolymer or a polymer. As used herein, a (meth)acrylate is intended to mean an acrylate or a methacrylate.
Examples of substrates to be suitably used in the present invention include those obtained from MR6®, MR7®, MR8®, MR174 ® and MR10® resins (thermosetting polythiourethane resins). The various substrates based on polythiourethane resins are marketed by the Mitsui Toatsu Chemicals company and these substrates as well as the monomers used for their preparation are especially described in the patents U.S. Pat. Nos. 4,689,387, 4,775,733, 5,059,673, 5,087,758 and 5,191,055.
The base lens 12 is preferably shaped to provide optical power suitable for correcting a wearer ametropia, for instance myopia or hyperopia. The base lens 12 may be monofocal or multifocal such as a multifocal progressive lens.
The base substrate 10 may comprise other layers in addition to the base lens 12 and/or plano wafer 11, such as for instance photochromic Trans-Bonding® layer on a front surface of a base lens 12, or any additional layer which can be deposited on the base lens or plano wafer and which incorporates an optical function such that:
As shown in
The abrasion resistant coating 20 is preferably formed on the front surface 101 of the base lens substrate 10. The abrasion resistant coating 20 has the role of protecting the base lens substrate 10 from scratches and abrasion. It is also conventionally called Hard-Multilayer coating, HC or HMC.
The abrasion-resistant coating can be any layer conventionally used as abrasion-resistant coating in the field of ophthalmic lenses.
Hard abrasion-resistant and/or scratch-resistant coatings are preferably prepared from compositions comprising at least one alkoxysilane and/or one hydrolyzate of the latter obtained, for example, by hydrolysis with a hydrochloric acid solution. After the hydrolysis stage, the duration of which is generally between 2 h and 24 h, preferably between 2 h and 6 h, catalysts can optionally be added. A surface-active compound is preferably also added in order to promote the optical quality of the deposit.
Mention may be made, among the coatings recommended in the present invention, of coatings based on epoxysilane hydrolyzates, such as those described in the patents EP 0 614 957, U.S. Pat. Nos. 4,211,823 and 5,015,523.
A preferred composition for an abrasion-resistant coating is that disclosed in the patent FR 2 702 486 on behalf of the applicant. It comprises an epoxytrialkoxysilane and dialkyldialkoxysilane hydrolyzate, colloidal silica and a catalytic amount of aluminum-based curing catalyst, such as aluminum acetylacetonate, the remainder being essentially composed of solvents conventionally used for the formulation of such compositions. Preferentially, the hydrolyzate used is a γ-glycidoxypropyltrimethoxysilane (GLYMO) and dimethyldiethoxysilane (DMDES) hydrolyzate or else a γ-glycidoxypropyltrimethoxysilane (GLYMO) and triethyl orthosilicate (TEOS) hydrolyzate.
The abrasion resistant coating 20 can be a bi-layered structure forming a hardness gradient from the base-lens substrate 10 to the free surface of the anti-abrasion coating. The upper layer of the coating defines the hardest part of the coating at the free surface thereof and allows a protection against thin particles and thin scratches, while the lower layer of the coating defines the less hard part underneath, able to absorb shocks provided by bigger particles and prevent formation of larger scratches.
Such bi-layered structure of hard coat can be the one of the structures disclosed in the document EP 2 092 377 incorporated therein by reference.
Compositions of materials suitable for forming abrasion resistant coating and which can be used in additive manufacturing or inkjet printing may be found in document US2007238804.
The abrasion resistant coating 20 comprises a front surface 21 and a back surface 22, one of the surfaces being at the interface with the base-lens substrate 10. In the case where the abrasion resistant coating 20 covers the front surface 201 of the base-lens substrate 10, the interface between the coating 20 and the base lens substrate 10 thus comprises the back surface 22 of the coating 20 and the front surface 101 of the base lens substrate.
As shown in
In one embodiment, each optical element 30 is formed of the same material as the abrasion resistant coating 20 and may be formed integral with the latter.
The optical element can be any kind of microelement, i.e. a microelement forming a discrete island or slot of the microscopic scale, or a rib of any form such as a ring, the width and/or the height of which being of the microscopic scale, protruding from the base surface of the abrasion-resistant coating.
The optical elements can be dimensioned, formed and organized to constitute any kind of optical functions, such as microlenses as disclosed in US2017/0131567 and WO2016/168746, Fresnel microstructures such as disclosed in EP 2 787 385 or WO 2014060552 and/or technical or non technical marking such as the ones disclosed in EP2604415, all references being incorporated therein.
In embodiments, the optical elements induce a local change in optical power of the optical device.
The optical elements are configured so that at least along one section of the lens the mean sphere of the optical elements increases from a point of said section towards the peripheral of said section.
According to an embodiment of the invention the optical elements are configured so that at least along one section of the lens, for example at least the same section as the one along which the mean sphere of the optical elements increases, the mean cylinder increases from a point of said section, for example the same point as for the mean sphere, towards the peripheral part of said section.
According to an embodiment of the invention, the at least one, for example all, of the optical element having is, for example are, micro-lens.
A microlens may be spherical, toric, or have an aspherical shape. A microlens may have a single focus point, or cylindrical power, or non-focusing point. In preferred embodiments, microlenses can be used to prevent progression of myopia or hyperopia. In that case, the base lens substrate comprises a base lens 12 providing an optical power for correcting myopia or hyperopia, and the microlenses may provide respectively an optical power greater than the optical power of the base lens 12 if the wearer has myopia, or an optical power lower than the optical power of the base lens 12 is the wearer has hyperopia.
In the sense of the invention, a “micro-lens” has a contour shape being inscribable in a circle having a diameter greater than or equal to 0.8 mm and smaller than or equal to 3.0 mm.
The optical elements may be configured so that along the at least one section of the lens the mean sphere and/or the mean cylinder of optical elements increases from the center of said section towards the peripheral part of said section.
For example, the optical elements may be regularly distributed along circles centered on the optical center of the refraction area.
The optical elements on the circle of diameter 10 mm and centered on the optical center of the refraction area may be micro lenses having a mean sphere of 2.75 D.
The optical elements on the circle of diameter 20 mm and centered on the optical center of the refraction area may be micro lenses having a mean sphere of 4.75 D.
The optical elements on the circle of diameter 30 mm and centered on the optical center of the refraction area may be micro lenses having a mean sphere of 5.5 D.
The optical elements on the circle of diameter 40 mm and centered on the optical center of the refraction area may be micro lenses having a mean sphere of 5.75 D.
The mean cylinder of the different micro lenses may be adjusted based on the shape of the retina of the person.
According to an embodiment of the invention, the refraction area comprises a far vision reference point, a near vision reference, and a meridian line joining the far and near vision reference points. For example, the refraction area may comprise a progressive additional lens design adapted to the prescription of the person or adapted to slow down the progression of the abnormal refraction of the eye of the person wearing the lens element.
The meridian line corresponds to the locus of the intersection of the main gaze direction with the surface of the lens.
Preferably, according to such embodiment, the optical elements are configured so that in standard wearing conditions along any horizontal section of the lens the mean sphere and/or the mean cylinder of the optical elements increases from the intersection of said horizontal section with the meridian line towards the peripheral part of the lens.
The mean sphere and/or the mean cylinder increase function along the sections may be different depending on the position of said section along the meridian line.
In particular, the mean sphere and/or the mean cylinder increase function along the sections are unsymmetrical. For example, the mean sphere and/or the mean cylinder increase function are unsymmetrical along vertical and/or horizontal section in standard wearing conditions.
At least one of the optical element, has an optical function of not focusing an image on the retina of the eye of the person when the lens element is worn in standard wearing conditions.
Advantageously, such optical function of the optical element combined with a refractive area having at least one refractive power different from the refractive power of the prescription allows slowing down the progression of the abnormal refraction of the eye of the person wearing the lens element.
The optical elements may be non-contiguous optical elements.
In the sense of the invention two optical elements are non-contiguous if for all the paths linking the two optical elements one may measure at least along part of each path the refractive power based on a prescription for the eye of the person.
When the two optical elements are on a spherical surface, the two optical elements are non-contiguous if there for all the paths linking the two optical elements one may measure at least along part of each path the curvature of said spherical surface.
According to an embodiment of the invention, at least one of the optical elements has an optical function of focusing an image on a position other than the retina.
Preferably, at least 50%, for example at least 80%, for example all, of the optical elements have an optical function of focusing an image on a position other than the retina.
According to an embodiment of the invention, at least one of the optical elements has a non-spherical optical function.
Preferably at least 50%, for example at least 80%, for example all, of the optical elements have a non-spherical optical function.
In the sense of the invention, a “non-spherical optical function” is to be understood as not having a single focus point.
The at least one element having a non-spherical optical function is transparent.
One can add these optical elements on a defined array like square or hexagonal or random or other.
The optical element may cover specific zones of the lens element, like at the center or any other area.
The optical element density or the quantity of power may be adjusted depending on zones of the lens element. Typically, the optical element may be positioned in the periphery of the lens element, in order to increase the effect of the optical element on myopia control, so as to compensate peripheral defocus due to the peripheral shape of the retina for example.
According to an embodiment of the invention, at least one, for example all, of the optical elements has a shape configured so as to create a caustic in front of the retina of the eye of the person. In other words, such optical element is configured so that every section plane where the light flux is concentrated if any, is located in front of the retina of the eye of the person.
According to an embodiment of the invention, the at least one, for example all, of the optical element having a non-spherical optical function is a multifocal refractive micro-lens.
In the sense of the invention, an optical element is “multifocal refractive micro-lens” includes bifocals (with two focal powers), trifocals (with three focal powers), progressive addition lenses, with continuously varying focal power, for example aspherical progressive surface lenses.
According to an embodiment of the invention, the at least one multifocal refractive micro-lens has a toric surface. A toric surface is a surface of revolution that can be created by rotating a circle or arc about an axis of revolution (eventually positioned at infinity) that does not pass through its center of curvature.
Toric surface lenses have two different radial profiles at right angles to each other, therefore producing two different focal powers.
Toric and spheric surface components of toric lenses produce an astigmatic light beam, as opposed to a single point focus.
According to an embodiment of the invention, the at least one of the optical element having a non-spherical optical function, for example all, of the optical elements is a toric refractive micro-lens. For example, a toric refractive micro-lens with a sphere power value greater than or equal to 0 diopter (δ) and smaller than or equal to +5 diopters (δ), and cylinder power value greater than or equal to 0.25 Diopter (δ).
As a specific embodiment, the toric refractive microlens may be a pure cylinder, meaning that minimum meridian line power is zero, while maximum meridian line power is strictly positive, for instance less than 5 Diopters.
According to an embodiment of the invention, at least one, for example all of the optical element, has discontinuities, such as a discontinuous surface, for example Fresnel surfaces and/or having a refractive index profile with discontinuities.
At least one, for example all, of the diffractive lenses may comprise a metasurface structure as disclosed in WO2017/176921.
The diffractive lens may be a Fresnel lens whose phase function ψ(r) has π phase jumps at the nominal wavelength. One may give these structures the name “π-Fresnel lenses” for clarity's sake, as opposition to unifocal Fresnel lenses whose phase jumps are multiple values of 2π. The π-Fresnel lens whose phase function is displayed in
According to an embodiment of the invention, at least one, for example all of the optical element, is a multifocal binary component.
According to an embodiment of the invention, at least one, for example all of the optical element, is a pixelated lens. An example of multifocal pixelated lens is disclosed in Eyal Ben-Eliezer et al, APPLIED OPTICS, Vol. 44, No. 14, 10 May 2005.
According to an embodiment of the invention, at least one, for example all of the optical elements, has an optical function with high order optical aberrations. For example, the optical element is a micro-lens composed of continuous surfaces defined by Zernike polynomials.
According to other embodiments, the optical elements do not induce a local change in optical power of the optical device but provide other optical functions.
For instance, an optical element can be a technical marking formed as a bump for on the top of bottom of the optical article comprising a progressive base lens 12, said technical marking enabling an optician to distinguish between the top and bottom of the optical article and hence to position properly the optical article in a frame.
According to still another example shown schematically in
As shown in
Each of concave and convex microlens/microelement can have a maximum height, e.g., measured in a direction perpendicular to first film surface 46a or second film surface that is less than or equal to 0.1 millimeters (mm), such as, for example, less than or equal to or between any two of 100 micrometers (μm), 90 μm, 80 μm, 70 μm, 60 μm, 50 μm, 40 μm, 30 μm, 20 μm, 10 μm, 5 μm, 1 μm, or smaller. Each of concave and convex microelement/microlenses can have a diameter, respectively, that is less than or equal to 2.0 mm, such as, for example, less than or equal to or between any two of 2.0 mm, 1.5 mm, 1.0 mm, 0.5 mm, 0.1 mm, 80 μm, 60 μm, 40 μm, 20 μm, or smaller.
With reference to
As the optical elements protrude from the abrasion resistant coating 20, there is only one diffraction of the ray of lights incoming on the optical elements, which is the diffraction caused by the different refraction indices of air and of the material forming the abrasion resistant coating 20. When the optical elements provide an optical power, this diffraction is well controlled and the design of the microelements can be easily adapted accordingly to achieve the desired optical power.
With reference to
In this embodiment, the optical elements 30 are fully encapsulated within the optical article 1, which provides the advantage that the outer surfaces of the optical article are devoid of any bumps or local changes of curvature relative to the overall curvature of the outer surfaces, which is more aesthetic, more comfortable and makes it easier to provide any desired additional coating on the outer surfaces of the optical article 1.
In this embodiment, an optical diopter is created by the difference of refraction indices between the material of the base lens substrate 10 at the interface, and the material forming the optical elements 30. As this difference of index is lower than the difference between the optical element material and air (case of the previous embodiment), if the optical elements are microlenses, this difference needs to be compensated by increasing the curves of the microlenses to increase their surfacic power. This can be easily calculated knowing the bases and indexes of materials. Thus in this embodiment as well the optical power of microlenses can be well controlled. If the abrasion-resistant coating is formed as a bi-layered structure as disclosed above, the optical elements could be constituted in the material of the upper harder layer of the bi-layered structure and be made integral with the latter, either on the interface with the lower less hard layer that would be provided with complementary recesses, or on the opposite surface of the upper harder layer of the bi-layered structure. Alternatively, the optical elements could be constituted in the material of the lower less hard layer, and protrude toward the main surface of the base lens substrate.
If the optical elements form a Fresnel structure, the optical power of the Fresnel structure can be well controlled for the same reasons in the two embodiments disclosed above. The Fresnel microstructure thus obtained can be similar to one of those disclosed in the document EP 2 287 385 or WO2014060552 that are incorporated therein by reference and defines phase shifting microelements typical of a Fresnel microstructure.
One can notice that the layer formed by the abrasion-resistant coating 20 wearing the optical elements 30 (be they formed of the same abrasion-resistant material as the coating or a distinct one) exhibits two kinds of outer surfaces: a first one constituted by the outer surfaces of the microelements, comprises local curvature variations due to the shape of the optical elements, whereas the second one constituted by the surfaces of the abrasion-resistant coating 20 disposed between the optical elements exhibits fewer or even no local curvature variations. Preferably, the difference induced by a local curvature variation of a microelement compared to the surrounding second kind of surface is at least 1 D.
Such a layer therefore exhibits a thickness in average greater at the optical element than away from them, and the maximum thickness of the layer is reached at the point of maximum thickness of the optical elements.
Back to the embodiment in which the optical elements 30 protrude from a surface of the abrasion-resistant coating 20 at the interface with the base lens substrate 10, in the case where the optical elements induce a local change of optical power of the optical device (microlenses, Fresnel structure), the indices of refraction of the microelements nM and of the layer 10i of the base lens substrate 10 at the interface with the microelements nS are distinct in order to allow said local change of optical power.
According to a first embodiment, the index nS of the substrate at the interface with the microelements can be lower than the index nM of the microelements, or it can be slightly superior but not beyond a given threshold T:
n
S
−n
M
<T
T is for instance about 0.1
In this case, as shown in
According to another embodiment shown in figure B, the index nS of the substrate at the interface with the microelements is greater than the index nM of the microelements beyond the above threshold:
n
S
−n
M
≥T
In that case the difference in refraction index between the base lens substrate 10 and the optical elements 30 may induce reflections at the interface. The optical article 1 then preferably comprises a quarter-wave layer 40 at the interface between the base lens substrate 10 and the optical elements 30, suitable for reducing the amount of reflections. A quarter wave layer (also noted as λ/4 layer) having a refraction index RI=(nS·nM)1/2 may for instance be used.
A detailed example of λ/4 layer is disclosed in U.S. Pat. No. 7,008,690 of the applicant.
Last the optical article 1 can comprise one or more coating(s) on each of the front surface and back surface thereof. For instance, the front surface of the optical article 1 may be coated with an anti-reflection coating 50 (shown in dotted line in
The optical article 1 described above, which incorporates optical elements 30 in a material suitable for forming an abrasion resistant coating, may be produced according to a number of various manufacturing methods.
First of all, the optical elements may be formed on the base-lens substrate 10 during the manufacturing of the optical elements. However, optical elements may also be formed on a layer of abrasion resistant material of a finished optical article, in the embodiment where the optical elements protrude from an outer surface of the abrasion resistant layer.
With reference to
According to this embodiment, an even abrasion resistant coating 20 is first formed an a surface of the base-lens substrate 10 by spin coating, dipping, or spraying or inkjet or by additive manufacturing, followed by curing/polymerization.
Then, optical elements are formed according to a desired patterned on the abrasion-resistant coating by technique such as inkjet or spraying as disclosed in the document WO2018010809A1. To this end, an installation comprises a plurality of nozzles N which are fed with a material suitable for forming the optical elements. The mesh size of the nozzles can be determined in accordance with the density, viscosity and surface tension of the material used for the inkjet printing. The positioning of the nozzles relative to the abrasion resistant coating 20 is programmed.
In order to obtain good adhesion between the optical elements and the abrasion resistant coating, different techniques can be used such as surface treatments (physical: corona or plasma treatment for example or chemical with appropriate adhesion promoters according to the material forming the optical elements and the abrasion resistant coating).
The nozzles deposit droplets of material at the desired positions and between each deposition a UV flash light or a thermic flash light may be used to start the polymerization in order to fix the droplets shape and position until the next deposition. Additive can also be added in the material for forming the optical elements, such as colors or filters.
Compositions of materials suitable for forming abrasion resistant coating and which can be used in inkjet printing may be found in document US2007238804.
According to another manufacturing method embodiment shown in
During a first step (
Regarding any of the two previous embodiments of the manufacturing method, if the optical elements are added to the abrasion resistant layer of a finished optical article, the addition of the optical elements can require a surface treatment of the abrasion resistant layer to allow adhesion between the deposited optical elements and the abrasion resistant layer.
With reference to
According to a first embodiment shown in
According to this method, a mold 8 is provided (
Material suitable for forming abrasion resistant material is deposited in a malleable state on the surface 80. A support layer 16 is then inserted in the mold and applied on the material in order for the material to spread between the surface 80 and the support layer, the material thus filing the recesses formed in the surface 80 (
In an embodiment, the support layer 16 may be an optical lens previously formed. In another embodiment, the support layer may be a wafer such as the one described above. In another embodiment, the support layer may be the base lens substrate.
The material filling the recesses 81 is then cured (
In case where the support layer is the base lens substrate, the optical article 1 is obtained once the mold is removed.
According to another embodiment, the support layer may be for instance a wafer 11, and the method may further comprise (
Upon removal of the mold, the obtained optical article 1 then comprises the base lens substrate 10 comprising the wafer 11 having an abrasion resistant coating in which are formed the optical elements 30, and the optical lens 12 on the opposite side of the wafer.
According to another embodiment shown in
According to a first step shown in
Then the layer of the base lens substrate is put inside another mold 9′ having two surfaces 94, 95 of the same respective curvatures as the walls 90, 91 of the previous mold, but the two surfaces being devoid of any protruding element. Material suitable for forming abrasion resistant coating is provided in a malleable state between the surface of the layer of base lens substrate comprising the recesses 13 and the opposite surface 95 of the mold (
The material is then cured and the mold is removed to obtain an optical article 1 comprising the layer of base lens substrate 10 having an abrasion resistant coating 20 and optical elements 30 formed integral with the abrasion resistant coating and encapsulated within the article.
Once the optical article comprising the base lens substrate and the abrasion resistant coating with protruding optical elements is obtained, it may further be coated on any one or both opposite main surfaces with an additional coating such as an anti-reflective coating.
With reference to
According to this method, as illustrated on the
The resulting varnished substrate is then embossed with a thermal embossing technology involving pressure and temperature. An embossing mold comprising an insert 103 whose internal surface 104 is provided with at least one recess 105 is made facing the layer of abrasion resistant coating 102 of the substrate 101. The varnished substrate is applied by its abrasion resistant coating on the internal surface 104 of the insert. The mold is closed and a predetermined temperature and pressure are applied during a time allowing at least the abrasion resistant coating or even in some case also a part of the substrate to take the form of the recess of the mold 103.
The temperature, pressure and time will be chosen at least in function of the abrasion resistant coating thermal properties and/or thickness to allow at least the abrasion resistant coating or even in some case also a part of the substrate, to take the form of the recess of the mold 103. Ideally, the thermal properties of the substrate will also be taken into account. For example, an abrasion resistant coating and the corresponding substrate can be chosen so as to have similar thermal properties i.e. similar glass transition temperature or equivalent. Or, if the abrasion resistant coating and the corresponding substrate have different thermal properties i.e. glass transition temperature or equivalent separated from more than 10° C., preferably 20° C. or even more preferably 30° C., the thickness of the abrasion resistant coating, the form of the recess and/or the pressure, time and temperature of the embossing method will be adapted in order to allow at least the abrasion resistant coating or even in some case also a part of the substrate.
Preferably the kind of abrasion resistant coating and/or its thickness, will be chosen in function of the thermal properties of the substrate to allow at least the abrasion resistant coating or even in some case also a part of the substrate, to take the form of the recess of the mold 103.
Even if the substrate and the abrasion resistant coating are not of the thermoplastic kind, the experiments provided showed that they can be heated to allow at least the abrasion resistant coating or even in some case also a part of the substrate to take the recess form of the mold 103.
Specifically for the illustrated example, a substrate MR8 was coated with a 3-6 μm thickness of a Mithril HI abrasion resistant coating, and, according to the
After cooling the resulting embossed varnished substrate 106, a lens on the surface of which an optical element made from abrasion resistant coating 107 and of a form complementary to the recess 105 is obtained (see
The substrate ideally has to present the same radius as the insert.
Said substrate can be constituted by a semifinished lens i.e. a lens whose at least one surface (the one opposite to the abrasion resistant coating) will have to be processed at a predetermined form to define a particular optical design, or by a finished lens. The substrate can also be constituted by a functional wafer or film, that will be varnished with an abrasion resistant coating, and then embossed to form the optical elements according to the present embodiment of the invention.
The
According to yet another embodiment, not illustrated, optical elements constituted from abrasion resistant material, can be obtained by injection, by inserting an abrasion resistant film into a cavity of an injection mold comprising an inner surface provided with at least a recess having a shape complementary to the shape of an optical element to be formed, the abrasion resistant film being pushed along said inner surface to match the form of the recess when the melt polymer is injected into the mold cavity.
| Number | Date | Country | Kind |
|---|---|---|---|
| 18306353.6 | Oct 2018 | EP | regional |
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/EP2019/077905 | 10/15/2019 | WO | 00 |