Optical CdO and ThO.sub.2 -free glass with refractive indices of 1.73-1.78 abbe numbers of 30-34, and high devitrification stability

Abstract

A new, CdO-and ThO.sub.2 -free optical glass with refractive indices of 1.73-1.78 and Abbe numbers of 30-34 and with particularly good devitrification stability comprises (in weight %):______________________________________SiO.sub.2 12-20, B.sub.2 O.sub.3 10-18, PbO 50-60Al.sub.2 O.sub.3 2-7, ZnO 0-4, ZrO.sub.2 0.5-3La.sub.2 O.sub.3 2-10, Cs.sub.2 O 0-5, M.sub.2 O 0-1(M.sub.2 O.dbd. Na.sub.2 O, K.sub.2 O, Li.sub.2 O) TiO.sub.2 0-5with the SiO.sub.2 /B.sub.2 O.sub.3 -ratio being about 1.0 to______________________________________1.5.

Description

BACKGROUND OF THE INVENTION

This invention relates to a new optical glass having good devitrification stability, good transmission, a good optical quality, refractive indices of 1.73-1.78 and Abbe numbers of 30-34.

Glasses with a simlar optical position have already been described in several publications. German AS No. 12 607 12 describes glasses with n.sub.d .ltoreq.1.86 and v.sub.d> 26, which are mainly within the system SiO.sub.2 -B.sub.2 O.sub.3 -BaO-ZnO. The optical position and the good chemical stability of these glasses can only be achieved by addition of up to 25% TiO.sub.2 and of up to 7% ZrO.sub.2. This entails a deterioration of transmission in the short-wave length spectral range (around 400 nm) as well as of devitrification stability.

The PbO-ZnO glasses known from JP-OS No. 78037886 require, for crystallization-stabilization and improved chemical resistance, up to 12 wt % Al.sub.2 O.sub.3, which in turn detracts from the meltability of these glasses.

The glasses produced within the system SiO.sub.2 -BaO-La.sub.2 O.sub.3 -PbO, which are known from Japanese Pat. Nos. 75 73914 and 77 84211, require up to 25% Ta.sub.2 O.sub.5 +ZrO.sub.2 or up to 15% TiO.sub.2 and up to 20% Nb.sub.2 O.sub.5 in order to achieve the desired optical position, crystallization stablity and chemical stability. With these glasses, high costs in the first case and transmission losses as well as stronger devitrification in the second case must be expected.

SUMMARY OF THE INVENTION

It is thus an object of this invention to provide a glass composition range which enables the production of high-reflective index optical glasses with good devitrification stability, good transmission and good optical quality without the environmentally hostile components CdO and ThO.sub.2.

Upon further study of the specification and appended claims, further objects and advantages of this invention will become apparent to those skilled in the art.

These objects have been achieved by providing optical, substantially CdO-and ThO.sub.2 -free glass with refractive indices of 1.73-1.78, Abbe numbers of 30-34, particularly good devitrification stability, good transmission in the visible range and low raw material costs, having the following composition (in weight per cent):

______________________________________SiO.sub.2 12-20B.sub.2 O.sub.3 10-18PbO 50-60Al.sub.2 O.sub.3 2-7ZnO 0-4ZrO.sub.2 0.5-3La.sub.2 O.sub.3 2-10Cs.sub.2 O 0-5M.sub.2 O 0-1 (M.sub.2 O = Na.sub.2 O, K.sub.2 O, Li.sub.2 O)TiO.sub.2 0-5______________________________________

Preferred compositions are in wt. %:

______________________________________ SiO.sub.2 15-18 B.sub.2 O.sub.3 13-15 PbO 52-60 Al.sub.2 O.sub.3 4.5-6 ZnO 1.5-3 ZrO.sub.2 1.5-3 La.sub.2 O.sub.3 2-10 Cs.sub.2 O 0-2______________________________________

Also preferred are glasses wherein the ratio SiO.sub.2 /B.sub.2 O.sub.3 is about 1.0 to 1.5.

The glass can also include other ingredients, e.g., in wt. %:

______________________________________SnO.sub.2 0-1.5F.sup.- (replacing O.sup.=) 0-2Y.sub.2 O.sub.3 0-2Bi.sub.2 O.sub.3 0-2Gd.sub.2 O.sub.3 0-2MO (MgO, CaO, SiO, BaO) 0-10Ta.sub.2 O.sub.5 0-2Nb.sub.2 O.sub.5 0-1______________________________________

DETAILED DISCUSSION

In the glasses according to this inventon, the high refractive indices are achieved primarily by the use of PbO and La.sub.2 O.sub.3, and partly by means of ZrO.sub.2. Good crystallization stability in turn is achieved by balanced amounts of SiO.sub.2 and B.sub.2 O.sub.3 (especially preferred ratio SiO.sub.2 :B.sub.2 O.sub.3 =1.14 to 1.24), ZnO (optionally), Al.sub.2 O.sub.3 and small optional additions of Cs.sub.2 O, SnO.sub.2, Y.sub.2 O.sub.3, Gd.sub.2 O.sub.3 and/or Bi.sub.2 O.sub.3.

The glasses according to this invention satisfy not only the demand for good transmission, low light scattering and good optical quality, but also for excellent crystallization stability and very low production costs. These thus are very useful to form optical elements.

When one of the optional elements is used in the glass, it typically is used in amounts of at least 0.1, 0.3, 0.5, 0.7, 1.0, 1.3, 1.5 etc. depending on its generic range above.

The glasses according to the invention can be produced as follows. The raw materials (e.g. oxides, carbonates, nitrates, fluorides) are weighed out; a conventional refining agent such as As.sub.2 O.sub.3 in amounts of 0.1 to 0.5 wt % is added and subsequently the whole is well mixed. The batch is melted down at about 1140.degree. to 1180.degree. C. in a ceramic or platinum crucible, refined at 1240.degree. C.-1280.degree. C. and well homogenized by means of an agitator. With a casting temperature of about 1050.degree. C. and a viscosity of approximately 10 dPas, the glass is then poured into metal dies.

Sample melt for 100 kg calculated glass

______________________________________ weight quantityOxide weight % raw material (kg)______________________________________SiO.sub.2 16.40 quartz powder 16.42B.sub.2 O.sub.3 14.00 H.sub.3 BO.sub.3 24.87PbO 56.13 Pb.sub.3 O.sub.4 57.47ZnO 1.90 ZnO 1.91Al.sub.2 O.sub.3 5.30 AlO(OH) 6.68La.sub.2 O.sub.3 4.57 La.sub.2 O.sub.3 4.57ZrO.sub.2 1.70 ZrO.sub.2 1.70 +As.sub.2 O.sub.3 113.62 0.10 (ref. agent) 113.72 kg batch______________________________________

The properties of this glass are specified in Table 1, example 1.

Without further elaboration, it is believed that one skilled in the art can, using the preceding description, utilize the present invention to its fullest extent. The following preferred specific embodiments are, therefore, to be construed as merely illustrative, and not limitative of the remainder of the disclosure in any way whatsoever. In the preceding text and the following examples, all temperatures are set forth uncorrected in degrees Celsius and all parts and percentages are by weight, unless otherwise indicated.

TABLE 1__________________________________________________________________________1 2 3 4 5 6 7 8 9 10 11__________________________________________________________________________SiO.sub.2 16.40 15.50 15.20 15.00 17.50 16.50 16.50 16.50 16.50 16.15 16.50B.sub.2 O.sub.3 14.00 13.40 13.30 13.00 15.00 13.30 14.00 13.30 14.00 13.50 14.00PbO 56.13 59.75 53.40 60.00 52.20 56.50 56.50 55.70 56.50 56.50 56.50ZnO 1.90 1.70 1.50 1.50 2.50 1.70 1.70 1.70 1.70 1.70 1.70Al.sub.2 O.sub.3 5.30 5.30 5.30 4.95 5.50 5.20 5.20 5.20 5.20 5.20 5.30La.sub.2 O.sub.3 4.57 2.50 9.50 3.45 6.50 4.30 3.00 4.30 3.50 4.30 4.30ZrO.sub.2 1.70 1.75 1.70 2.00 0.70 1.60 1.60 1.60 1.60 1.60 1.60Cs.sub.2 O 0.70Y.sub.2 O.sub.3 1.30Bi.sub.2 O.sub.3 1.50Gd.sub.2 O.sub.3 0.80SnO.sub.2 0.85F.sup.- 0.30As.sub.2 O.sub.3 0.10 0.10 0.10 0.10 0.10 0.20 0.20 0.20 0.20 0.20 0.20SiO.sub.2 1.17 1.16 1.14 1.15 1.17 1.24 1.18 1.24 1.18 1.20 1.18B.sub.2 O.sub.3n.sub.d 1.7575 1.7675 1.7698 1.7793 1.7342 1.7530 1.7515 1.7590 1.7524 1.7577 1.7507v.sub.d 31.86 30.6 31.80 30.00 33.50 31.60 31.90 31.50 31.8 31.5 32.0Ti* 0.74 0.73 0.75 0.73 0.75 0.79 0.76 0.73 0.78 0.74 0.78400/25__________________________________________________________________________ *Ti 400 nm/25 mm; net transmission at wavelength 400 nm and layer thickness o 25 mm.

The preceding examples can be repeated with similar success by substituting the generically or specifically described reactants and/or operating conditions of this invention for those used in the preceding examples.

From the foregoing description, one skilled in the art can easily ascertain the essential characteristics of this invention, and without departing from the spirit and scope thereof, can make various changes and modifications of the invention to adapt it to various usages and conditions.

Example 1 is a typical example of a glass according to the invention. This glass is used as an optical glass and replaces the well-known optical glass LaF11 which is widely used in optical lens systems, and which contains CdO and ThO.sub.2.

Claims

1. An optical, substantially CdO-and ThO.sub.2 -free glass having a refractive index of 1.73-1.78, an Abbe number of 30-34, good devitrification stability, good transmission in the visible range and low raw material cost, consisting essentially of in weight percent:

______________________________________SiO.sub.2 12-20B.sub.2 O.sub.3 10-18PbO 52-60Al.sub.2 O.sub.3 2-7ZnO 0-3ZrO.sub.2 0.5-3La.sub.2 O.sub.3 2-9.5Cs.sub.2 O 0-5M.sub.2 O(M.sub.2 O.dbd. Na.sub.2 O, K.sub.2 O, Li.sub.2 O) 0-1TiO.sub.2 0-5,SnO.sub.2 0-1.5F.sup.- (replacing O.sup.=) 0-2Y.sub.2 O.sub.3 0-2Bi.sub.2 O.sub.3 0-2Nb.sub.2 O.sub.5 0-1.______________________________________

2. A glass of claim 1 wherein the ratio of SiO.sub.2 /B.sub.2 O.sub.3 is in the range of 1.0 to 1.5.

3. A glass of claim 1, consisting essentialy of (in wt. %):

______________________________________ SiO.sub.2 15-18 B.sub.2 O.sub.3 13-15 PbO 52-60 Al.sub.2 O.sub.3 4.5-6 ZnO 1.5-3 ZrO.sub.2 1.5-3 La.sub.2 O.sub.3 2-10 Cs.sub.2 O 0-2.______________________________________

4. A glass of claim 3 wherein the ratio of SiO.sub.2 /B.sub.2 O.sub.3 is in the range of 1.0 to 1.5.

5. A glass of claim 1 wherein the ratio of SiO.sub.2 /B.sub.2 O.sub.3 is in the range of about 1.14 to 1.24.

6. A glass of claim 3 wherein the ratio of SiO.sub.2 /B.sub.2 O.sub.3 is in the range of 1.14 to 1.24.

7. A glass of claim 1 containing SnO.sub.2.

8. A glass of claim 1 containing F.sup.-.

9. A glass of claim 1 containing Y.sub.2 O.sub.3.

10. A glass of claim 1 containing Bi.sub.2 O.sub.3.

11. A glass of claim 1 containing Cs.sub.2 O.

12. A glass of claim 1 containing Nb.sub.2 O.sub.5.

13. An optical element consisting essentially of a glass of claim 1.

14. A glass of claim 1 having a ZnO content of 0-2.5% in weight.

15. A glass of claim 1 having a ZnO content of 0-1.7% in weight.