Patent Application
20140233104
This invention relates to an optical element that can suppress a change in color tone, a window material, a fitting and a solar shading device.
In recent years, there have been increasing cases in which a layer for absorbing or reflecting one portion of solar light is attached to building-use glass and vehicle window glass of a high-rise building, a house or the like. This is one of energy-saving countermeasures to be carried out for preventing global warming, and its purpose is to reduce the load imposed on cooling facilities, caused by light energy that is applied from the sun and enters the inside of a housing through a window to cause a temperature rise of the inside of the housing. In the optical energy applied from the sun, a visible light region having wavelengths of 380 to 780 nm and a near infrared ray region having wavelengths of 780 to 2100 nm occupy a great ratio thereof. Of these, since the transmittance of the window in the wavelength region of the latter has nothing to do with the visibility of the human, it forms an essential factor by which functions of the window having high transparency and a high heat-shading function are determined.
As a method for shading near infrared rays while maintaining transparency in the visible light region, a method for attaching an optical element having a high transmittance in the near infrared ray region to window glass is proposed. With respect to this method, a technique has been disclosed in which an optical multi-layer film is used as a reflection layer (for example, see Patent Document 1). However, since such a reflection layer is formed on a flat-shaped film or a window glass, it is only possible to regularly reflect incident solar light. For this reason, light rays applied from the sky and regularly reflected therefrom are allowed to reach another building outside and the ground, and absorbed and converted to heat, thereby causing a rise in the ambient temperature. As a result, on the periphery of a building in which this reflection layer is bonded to the entire windows, a temperature rise is locally generated, with the result that such problems as to cause an increased heat island phenomenon in a city district and as to suppress lawn from growing only on an irradiated surface by the reflected light.
However, conventionally, a heat-ray shading film has been designed by film-forming a multi-layer film on a flat plate. In the case when the multi-layer film is designed by using this conventional method, since the refractive index on the multi-layer film and the incident light angle on the interface of incident light rays are varied, a designed spectrum is deviated from an optimal value to cause a change in color tones, resulting in bluish or reddish light rays.
Therefore, an object of the present invention is to provide an optical element that can suppress a change in color tones due to a change in an incident angle, and a window material, a fitting and a solar shading device for such an optical element.
In order to solve the above-mentioned problems, a first aspect of the invention relates to an optical element that is provided with:
a first optical layer having a concave-convex surface;
a wavelength-selective reflection layer formed on the concave-convex surface; and
a second optical layer formed on the wavelength-selective reflection layer, and in this structure, the wavelength-selective reflection layer has a five-layer structure in which a high-refractive-index layer and a metal layer are alternately stacked, and in the case when the entire wavelength-selective reflection layer has a geometric film thickness L of 80 nm, a ratio α (=db/da) of an optical film thickness db of the entire metal layer relative to an optical film thickness da of the entire high-refractive-index layer and a ratio β (=d3/d1) of an optical film thickness d3 of a third high-refractive-index layer relative to an optical film thickness d1 of a first high-refractive-index layer, when viewed from either the first optical layer side or the second optical layer side, are included in a first region surrounded by the following formulas (1) to (4), while in the case when the entire wavelength-selective reflection layer has a geometric film thickness L of 90 nm, the ratio α and the ratio β are included in a second region surrounded by the following formulas (5) to (8), and in the case when the entire wavelength-selective reflection layer has a geometric film thickness L of 80 nm<L<90 nm,
supposing that each of minute sides formed by dividing a periphery C1 of the first region into n-equal portions, with an intersection between the formula (1) and formula (3) being set as a starting point, is represented as ΔC1i (where i represents a natural number of 0 to n), that each of minute sides formed by dividing a periphery C2 of the second region into n-equal portions, with an intersection between the formula (5) and formula (7) being set as a starting point, is represented as ΔC2i and that each of minute regions having a rectangular shape, with ΔC1i and ΔC2i being formed as the two short sides, is defined as ΔSi, the ratio α and the ratio β are surrounded by a circumferential surface S composed of a group of minute regions ΔSi.
α=−0.0004β2+0.0053β+0.0065 (1)
α=−1×10−5β2+0.0007β+0.0066 (2)
α=−1×10−5β2+0.0005β+0.0119 (3)
α=0.012114 (4)
α=−0.0002β2+0.0039β+0.0087 (5)
α=−3×10−5β2+0.0014β+0.0038 (6)
α=−2×10−5β2+0.0006β+0.0112 (7)
α=0.010589 (8)
A second aspect of the invention relates to an optical element that is provided with:
a first optical layer having a concave-convex surface;
a wavelength-selective reflection layer formed on the concave-convex surface; and
a second optical layer formed on the wavelength-selective reflection layer, and in this structure, the wavelength-selective reflection layer has a five-layer structure in which a high-refractive-index layer and a metal layer are alternately stacked, and in the case when the entire wavelength-selective reflection layer has a geometric film thickness L of 90 mm, a ratio α (=db/da) of an optical film thickness db of the entire metal layer relative to an optical film thickness da of the entire high-refractive-index layer and a ratio β (=d3/d1) of an optical film thickness d3 of a third high-refractive-index layer relative to an optical film thickness d1 of a first high-refractive-index layer, when viewed from either the first optical layer side or the second optical layer side, are included in a first region surrounded by values represented by the following formulas (5) to (8), while in the case when the entire wavelength-selective reflection layer has a geometric film thickness L of 100 nm, the ratio α and the ratio β are included in a second region surrounded by values represented by the following formulas (9) to (12), and in the case when the entire wavelength-selective reflection layer has a geometric film thickness L of 90 nm<L<100 nm,
supposing that each of minute sides formed by dividing a periphery C1 of the first region into n-equal portions, with an intersection between the formula (5) and formula (7) being set as a starting point, is represented as ΔC1i (where i represents a natural number of 0 to n), that each of minute sides formed by dividing the periphery C2 of the second region into n-equal portions, with an intersection between the formula (9) and formula (11) serving as a starting point, is represented as ΔC2i and that each of minute regions having a rectangular shape, with ΔC1i and ΔC2i being formed as the two short sides, is defined as ΔSi, the optical element is designed such that the ratio α and the ratio β are surrounded by a circumferential surface S composed of a group of minute regions ΔSi.
α=−0.0002β2+0.0039β+0.0087 (5)
α=−3×10−5β2+0.0014β+0.0038 (6)
α=−2×10−5β2+0.0006β+0.0112 (7)
α=0.010589 (8)
α=−0.0002β2+0.0055β+0.0057 (9)
α=−0.0002β2+0.0045β−0.0067 (10)
α=−4×10−5β2+0.001β+0.0099 (11)
α=0.009403 (12)
A third aspect of the present invention relates to an optical element that is provided with:
a first optical layer having a concave-convex surface;
a wavelength-selective reflection layer formed on the concave-convex surface; and
a second optical layer formed on the wavelength-selective reflection layer, and in this structure, the wavelength-selective reflection layer has a five-layer structure in which a high-refractive-index layer and a metal layer are alternately stacked, and in the case when the entire wavelength-selective reflection layer has a geometric film thickness L of 100 nm, a ratio α (=db/da) of an optical film thickness db of the entire metal layer relative to an optical film thickness da of the entire high-refractive-index layer and a ratio β (=d3/d1) of an optical film thickness d3 of a third high-refractive-index layer relative to an optical film thickness d1 of a first high-refractive-index layer, when viewed from either the first optical layer side or the second optical layer side, are included in a first region surrounded by the following formulas (9) to (12), while in the case when the entire wavelength-selective reflection layer has a geometric film thickness L of 120 nm, the ratio α and the ratio β are included in a second region surrounded by the following formulas (13) to (16), and in the case when the entire wavelength-selective reflection layer has a geometric film thickness L of 100 nm<L<120 nm,
supposing that each of minute sides formed by dividing a periphery C1 of the first region into n-equal portions, with an intersection between the formula (9) and formula (11) being set as a starting point, is represented as ΔC1i (where i represents a natural number of 0 to n), that each of minute sides formed by dividing the periphery C2 of the second region into n-equal portions, with an intersection between the formula (13) and formula (15) serving as a starting point, is represented as ΔC2i and that each of minute regions having a rectangular shape, with ΔC1i and ΔC2i being formed as the two short sides, is defined as ΔSi, the ratio α and the ratio β are surrounded by a circumferential surface S composed of a group of the minute regions ΔSi.
α=−0.0002β2+0.0055β+0.0057 (9)
α=−0.0002β2+0.0045β−0.0067 (10)
α=−4×10−5β2+0.001β+0.0099 (11)
α=0.009403 (12)
α=−0.0003β2+0.0074β+0.0033 (13)
α=−0.0014β2+0.0191β−0.0422 (14)
α=−9×10−5β2+0.0015β+0.0084 (15)
α=0.007709 (16)
A fourth aspect of the invention relates to an optical element that is provided with:
a first optical layer having a concave-convex surface;
a wavelength-selective reflection layer formed on the concave-convex surface; and
a second optical layer formed on the wavelength-selective reflection layer has a five-layer structure in which a high-refractive-index layer and a metal layer are alternately stacked, and in the case when the entire wavelength-selective reflection layer has a geometric film thickness L of 120 nm, a ratio α (=db/da) of an optical film thickness db of the entire metal layer relative to an optical film thickness da of the entire high-refractive-index layer and a ratio β (=d3/d1) of an optical film thickness d3 of a third high-refractive-index layer relative to an optical film thickness d1 of a first high-refractive-index layer, when viewed from either the first optical layer side or the second optical layer side, are included in a first region surrounded by the following formulas (13) to (16), while in the case when the entire wavelength-selective reflection layer has a geometric film thickness L of 140 nm, the ratio α and the ratio β are included in a second region surrounded by the following formulas (17) to (20), and in the case when the entire wavelength-selective reflection layer has a geometric film thickness L of 120 nm<L<140 nm,
supposing that each of minute sides formed by dividing a periphery C1 of the first region into n-equal portions, with an intersection between the formula (13) and formula (15) being set as a starting point, is represented as ΔC1i (where i represents a natural number of 0 to n), that each of minute sides formed by dividing the periphery C2 of the second region into n-equal portions, with an intersection between the formula (17) and formula (19) serving as a starting point, is represented as ΔC2i and that each of minute regions having a rectangular shape, with ΔC1i and ΔC2i being formed as the two short sides, is defined as ΔSi, the ratio α and the ratio β are surrounded by a circumferential surface S composed of a group of minute regions ΔSi.
α=−0.0003β2+0.0074β+0.0033 (13)
α=−0.0014β2+0.0191β−0.0422 (14)
α=−9×10−5β2+0.0015β+0.0084 (15)
α=0.007709 (16)
α=−0.0014β2+0.0136β−0.0027 (17)
β=10132α2−241.39α+4.747 (18)
α=−0.0001β2+0.002β+0.0074 (19)
α=0.006523 (20)
A fifth aspect of the invention relates to an optical element that is provided with:
a first optical layer having a concave-convex surface;
a wavelength-selective reflection layer formed on the concave-convex surface; and
a second optical layer formed on the wavelength-selective reflection layer has a five-layer structure in which a high-refractive-index layer and a metal layer are alternately stacked, and in the case when the entire wavelength-selective reflection layer has a geometric film thickness L of 140 nm, a ratio α (=db/da) of an optical film thickness db of the entire metal layer relative to an optical film thickness da of the entire high-refractive-index layer and a ratio β (=d3/d1) of an optical film thickness d3 of a third high-refractive-index layer relative to an optical film thickness d1 of a first high-refractive-index layer, when viewed from either the first optical layer side or the second optical layer side, are included in a first region surrounded by the following formulas (17) to (20), while in the case when the entire wavelength-selective reflection layer has a geometric film thickness L of 160 nm, the ratio α and the ratio β are included in a second region surrounded by the following formulas (21) to (25), and in the case when the entire wavelength-selective reflection layer has a geometric film thickness L of 140 nm<L<160 nm,
supposing that each of minute sides formed by dividing a periphery C1 of the first region into n-equal portions, with an intersection between the formula (17) and formula (19) being set as a starting point, is represented as ΔC1i (where i represents a natural number of 0 to n), that each of minute sides formed by dividing the periphery C2 of the second region into n-equal portions, with an intersection between the formula (21) and formula (24) serving as a starting point, is represented as ΔC2i and that each of minute regions having a rectangular shape, with ΔC1i and ΔC2i being formed as the two short sides, is defined as ΔSi, the ratio α and the ratio β are surrounded by a circumferential surface S composed of a group of minute regions ΔSi.
α=−0.0014β2+0.0136β−0.0027 (17)
β=10132α2−241.39α+4.747 (18)
α=−0.0001β2+0.002β+0.0074 (19)
α=0.006523 (20)
α=−0.005β2+0.0273β−0.0145 (21)
α=0.0043β2−0.0332β+0.07 (22)
β=2.875 (23)
α=−0.0001β2+0.0025β+0.0062 (24)
α=0.005676 (25)
A sixth aspect of the invention relates to an optical element that is provided with:
a first optical layer having a concave-convex surface;
a wavelength-selective reflection layer formed on the concave-convex surface; and
a second optical layer formed on the wavelength-selective reflection layer has a five-layer structure in which a high-refractive-index layer and a metal layer are alternately stacked, and in the case when the entire wavelength-selective reflection layer has a geometric film thickness L of 160 nm, a ratio α (=db/da) of an optical film thickness db of the entire metal layer relative to an optical film thickness da of the entire high-refractive-index layer and a ratio β (=d3/d1) of an optical film thickness d3 of a third high-refractive-index layer relative to an optical film thickness d1 of a first high-refractive-index layer, when viewed from either the first optical layer side or the second optical layer side, are included in a first region surrounded by the following formulas (21) to (25), while in the case when the entire wavelength-selective reflection layer has a geometric film thickness L of 180 nm, the ratio α and the ratio β are included in a second region surrounded by the following formulas (26) to (29), and in the case when the entire wavelength-selective reflection layer has a geometric film thickness L of 160 nm<L<180 nm,
supposing that each of minute sides formed by dividing a periphery C1 of the first region into n-equal portions, with an intersection between the formula (21) and formula (24) being set as a starting point, is represented as ΔC1i (where i represents a natural number of 0 to n), that each of minute sides formed by dividing the periphery C2 of the second region into n-equal portions, with an intersection between the formula (26) and formula (28) serving as a starting point, is represented as ΔC2i and that each of minute regions having a rectangular shape, with ΔC1i and ΔC2i being formed as the two short sides, is defined as ΔSi, the ratio α and the ratio β are surrounded by a circumferential surface S composed of a group of minute regions ΔSi.
α=−0.005β2+0.0273β−0.0145 (21)
α=0.0043β2−0.0332β+0.07 (22)
β=2.875 (23)
α=−0.0001β2+0.0025β+0.0062 (24)
α=0.005676 (25)
α=−0.0103β2+0.047β−0.0322 (26)
α=0.0093β2−0.0677β+0.1212 (27)
α=−0.0003β2+0.0036β+0.0046 (28)
α=0.00498 (29)
In the first to sixth aspects of the present invention, by determining the film thicknesses of the respective layers of the wavelength-selective reflection layer so as to allow the ratio α and the ratio β to be included by a predetermined region, it becomes possible to suppress a change in color tones.
As described above, in accordance with the present invention, it is possible to suppress a color tone change caused by an incident angle.
Referring to Figures, the following description will discuss embodiments of the present invention in the following order.
1. First Embodiment (example in which structural elements are one-dimensionally arranged)
2. Second Embodiment (example in which a region is defined by an approximation straight line)
3. Third Embodiment (example in which structural elements are two-dimensionally arranged)
4. Fourth Embodiment (example of a reflection layer of a louver type)
5. Fifth Embodiment (example in which a light-scattering body is attached to an optical film)
6. Sixth Embodiment (example in which a reflection layer is exposed)
7. Seventh Embodiment (example in which a self-washing effect layer is installed)
8. Eighth Embodiment (example in which an optical film is applied to a blind device)
9. Ninth Embodiment (example in which an optical film is applied to a roll screen device)
10. Tenth Embodiment (example in which an optical film is applied to fittings)
The optical film 1 may be further provided with a first substrate 4a attached to the light-releasing surface S2 of the optical layer 2, if necessary. Moreover, the optical film 1 may be further provided with a second substrate 5a attached to the light incident surface S1 of the optical layer 2, if necessary. Additionally, in the case when the first substrate 4a and/or the second substrate 5a are attached to the optical film 1, optical characteristics, such as transparency and color transmittance, shown below, are preferably satisfied, with the first substrate 4a and/or the second substrate 5a being attached to the optical film 1.
The optical film 1 may be further provided with a bonding layer 6, if necessary. Of the light-incident surface S1 and the light-releasing surface S2 of the optical film 1, this bonding layer 6 is formed on the surface that is bonded to a window material 10. Through this bonding layer 6, the optical film 1 is bonded to the indoor side or the outdoor side of the window material 10 serving as an adherent member. As the bonding layer 6, for example, an adhesive layer (for example, a UV-setting resin, or a two-liquid mixing type resin) mainly composed of an adhesive, or a sticker layer (for example, Pressure Sensitive Adhesive (PSA)) mainly composed of a sticker may be used. In the case when the bonding layer 6 is a sticker layer, a separation layer 7 formed on the bonding layer 6 is further preferably provided thereon. With this structure, the optical film 1 is easily bonded onto the adherent member, such as the window material 10, with the bonding layer 6 interposed therebetween, by simply separating the separation layer 7.
From the viewpoint of improving the joining property of the second substrate 5a and the bonding layer 6 and/or the second optical layer 5, the optical film 1 may be further provided with a primer layer (not shown) between the second substrate 5a and the bonding layer 6 and/or the second optical layer 5. Moreover, from the viewpoint of improving the joining property of the same portion, in place of the primer layer, or together with the primer layer, a known physical preliminarily treatment is preferably carried out thereon. As the known physical preliminarily treatment, for example, a plasma process, a corona process, or the like is proposed.
The optical film 1 may be further provided with a barrier layer (not shown) on the light-incident surface S1 or the light-releasing surface S2, or between each of the surfaces and the reflection layer 3, to which the adherent member such as the window material 10 or the like is bonded. By installing the barrier layer in this manner, moisture dispersion from the light-incident surface S1 or the light-releasing surface S2 to the reflection layer 3 is reduced so that degradation of metal or the like contained in the reflection layer 3 is suppressed. Therefore, the durability of the optical film 1 can be improved.
From the viewpoint of providing a scratch resistance or the like to its surface, the optical film 1 may be further provided with a hard coat layer 8. The hard coat layer 8 is preferably formed on a face of the light-incident surface S1 and the light-releasing surface S2 on the side opposite to the face to be bonded to an adherent member such as the window material 10 or the like. From the viewpoint of providing an antifouling property or the like to the light-incident surface S1 of the optical film 1, a layer having a water-repellent property or a hydrophilic property may be further formed thereon. The layer having these functions may be directly formed, for example, on the optical layer 2, or may be formed on a functional layer of various kinds, such as the hard coat layer 8.
From the viewpoint of easily bonding the optical film 1 onto an adherent member such as the window material 10 or the like, the optical film 1 is preferably designed to have flexibility. In this case, the films may include sheets. That is, the optical film 1 includes an optical sheet.
The optical film 1 is provided with transparency. The transparency is preferably set within a range of degree of transmission image clearness, which will be described below. The difference of refractive indexes between the first optical layer 4 and the second optical layer 5 is preferably set to 0.010 or less, more preferably, to 0.008 or less, most preferably, to 0.005 or less. When the difference in refractive indexes exceeds 0.010, the transmission image tends to become a blurred image. In the case when it is in a range from 0.008 to 0.010 or less, no problems are raised for use in daily life although it also depends on external brightness. In the case when it is in a range from 0.005 to 0.008 or less, although a diffraction pattern tends to cause an adverse effect only when a very bright object, such as a light source, is viewed, outside scenes can be clearly viewed. In the case when it is 0.005 or less, the diffraction pattern no longer causes an adverse effect. Of the first optical layer 4 and the second optical layer 5, the optical layer forming the side which is bonded to the window material 10 or the like may be mainly composed of a sticker. By using this structure, the optical film 1 can be bonded to the window material 10 or the like by the first optical layer 4 or the second optical layer 5 mainly composed of the sticker. Additionally, in the case when this structure is used, the difference in the refractive indexes of the stickers is preferably set within the above-mentioned range.
The first optical layer 4 and the second optical layer 5 are preferably designed to have the same optical properties such as the refractive index or the like. More specifically, the first optical layer 4 and the second optical layer 5 are preferably made of the same material, for example, the same resin material, having transparency within a visible range. In the case when the first optical layer 4 and the second optical layer 5 are formed by using the same material, since the two layers have the same refractive index, it becomes possible to improve the transparency of visible light rays. However, even in the case of using the same material as the starting sources, the refractive indexes of the resulting generated layers sometimes differ from each other due to the curing condition or the like in the film-forming process; therefore, this point needs to be taken into consideration. In contrast, in the case when the first optical layer 4 and the second optical layer 5 are made of different materials, since the refractive indexes of the two members are different from each other, light is refracted, with the reflection layer 3 serving as the border, with the result that a blurred transmission image tends to be generated. In particular, when an object that is close to a point light source, such as a distant light bulb or the like, is observed, a diffraction pattern tends to be remarkably observed. Additionally, in order to adjust the value of a refractive index, an additive agent may be mixed in the first optical layer 4 and/or the second optical layer 5.
The first optical layer 4 and the second optical layer 5 are preferably designed to have transparency in a visible range. In this case, the definition of transparency has two kinds of meanings, that is, no light absorption is caused and no light scattering occurs. In the case when transparency is generally mentioned, it sometimes indicates only the former; however, the optical film 1 relating to the first embodiment is preferably provided with both of the properties. In case of the currently utilized retroreflection members, such as traffic signs and clothes for night-time workers, since their purposes are to visually recognize their reflected light display, even when they have, for example, a light scattering property, their reflected light can be visually recognized as long as they are tightly made in contact with a base reflective member. This is based upon the same principle as that even when an antiglare treatment having a scattering property is carried out on the front surface of an image display device so as to give an antiglare property thereto, its image can be visually recognized. However, since the optical film 1 relating to the first embodiment is characterized by the fact that it can transmit light rays other than light having a specific wavelength that is directionally reflected, and since it is bonded to a transmission member that mainly transmits this transmission wavelength so as to observe its transmitted light, it preferably has no scattering property. However, depending on its applications, the second optical layer 5 may be intentionally allowed to have a scattering property.
The optical film 1 is bonded to a rigid member that mainly has a transmitting property relative to light rays other than transmitted light having a specific wavelength, that is, for example, the window material 10, with a sticker or the like interposed therebetween, and utilized. As the window material 10, examples thereof include: window materials for use in buildings, such as high-rise buildings and houses, and window materials for use in vehicles. In the case when the optical film 1 is used for the window material for use in buildings, the optical film 1 is preferably applied to the window material 10 that is disposed in any of directions facing the east, south or west directions (for example, a south-east or south-west direction). By applying the optical film 1 to the window material 10 disposed at such a position, it becomes possible to more effectively reflect heat rays. The optical film 1 may be applied not only to a window glass of a single layer, but also to a special glass such as a multi-layered glass. Moreover, the window material 10 is not limited by those made of glass, and those made of a polymeric material having transparency may be used. The optical layer 2 preferably has transparency in a visible light range. By allowing it to have transparency in this manner, when the optical film 1 is bonded to the window material 10 such as window glass, visible light rays can be transmitted to properly ensure lighting by solar light. Moreover, with respect to the bonding surface, not only the inner surface of glass, but also the outer surface may be used.
Furthermore, the optical film 1 may be used in combination with another heat ray-cutting film, and for example, a light-absorption coat film may be formed on an interface (that is, the outermost surface of the optical film 1), for example, between air and the optical film 1. The optical film 1 may be used in combination with another layer, such as a hard coat layer, an ultraviolet-ray cutting layer, a surface reflection preventive layer, or the like. In the case when these functional layers are used in combination, these functional films are preferably formed on an interface between the optical film 1 and air. However, with respect to the ultraviolet-ray cutting layer, since this layer needs to be disposed on the sun side from the optical film 1, the ultraviolet-ray cutting layer is preferably placed between the window glass surface and the optical film 1, in particular, upon application of this for inside bonding use of an indoor window glass surface. In this case, an ultraviolet-ray absorbing agent may be kneaded into a bonding layer between the window glass face and the optical film 1.
Moreover, depending on the application of the optical film 1, a coloring process may be carried out on the optical film 1 so that a designing property may be given thereto. In the case when the designing property is applied in this manner, at least one of the first optical layer 4 and the second optical layer 5 is preferably designed so as to mainly absorb light having a specific wavelength band in a visible light range, within a region not impairing the transparency.
The light ray having a specific wavelength band that is directionally reflected selectively and the specific light ray that is allowed to transmit are different depending on the application of the optical film 1. For example, in the case when the optical film 1 is applied to the window material 10, the light ray having a specific wavelength band that is directionally reflected selectively is preferably a near infrared light ray, and the specific light ray that is allowed to transmit is preferably a visible light ray. More specifically, the light ray having a specific wavelength band that is directionally reflected selectively is preferably a near infrared light ray mainly having a wavelength range from 780 nm to 2100 nm. By reflecting the near infrared light ray, the optical element is allowed to suppress a temperature rise inside a building when it is bonded to the window material such as a glass window. Therefore, the cooling load can be lowered so as to save energy. In this case, the directional reflection refers to a reflection in a certain specific direction other than a regular reflection, and indicates that it is sufficiently strong in comparison with a diffusion reflection intensity having no directivity. In this case, with respect to the reflection, a reflectance in a specific wavelength range, for example, in a near infrared light region, is preferably set to 30% or more, more preferably, to 50% or more, and most preferably, to 80% or more. With respect to the transmission, a transmittance in a specific wavelength range, for example, in a visible light region, is preferably set to 30% or more, more preferably, to 50% or more, and most preferably, to 70% or more.
In the optical film 1, a direction φo in which the reflection is directionally made is preferably set to −90° or more to 90° or less. This is because in the case when the optical film 1 is bonded to the window material 10, of light rays made incident thereon from the sky, the light ray having the specific wavelength band can be returned in the upward sky direction. In the case when there are no high-rise buildings on the periphery, the optical film 1 in this range is effectively used. Moreover, the direction in which the reflection is directionally made is preferably set in the vicinity of (θ, −φ). The vicinity means a deviation preferably set within 5 degrees from (θ, −φ), more preferably, within 3 degrees from (θ, −φ), and most preferably, within 2 degrees therefrom. This is because in the case when the optical film 1 is bonded to the window material 10, by setting this range, of light rays made incident thereon from the sky above buildings having about the same height that stand side by side, the light ray having the specific wavelength band can be effectively returned to the sky above the buildings. In order to achieve the directional reflection of this type, a three-dimensional structural element, for example, having a shape of one portion of a spherical face or a hyperboloid, a trigonal pyramid, a pyramid, a cone, or the like, is preferably used. A light ray made incident in the (θ, φ) direction (−90°<φ<90°) is reflected in the (θo, φo) direction (0°<θo<90°, −90°<φo<90°) based upon the corresponding shape. Alternatively, a pillar shape extending in one direction is preferably used. A light ray made incident in the (θ, φ) direction (−90°<φ<90°) is reflected in the (θo, −φ) direction (0°<θo<90°) based upon the inclination angle of the pillar shape.
In the optical film 1, the directional reflection of a light ray of a specific wavelength band is preferably set in a direction in the vicinity of retroreflection, that is, the reflection direction of the light ray of the specific wavelength band relative to a light ray made incident on the incident surface S1 at the incident angle (θ, φ) is preferably set to the vicinity of (θ, φ). Thus, in the case when the optical film 1 is bonded to the window material 10, of light rays made incident thereon from the sky, the light ray having the specific wavelength band can be returned in the upward sky direction. In this case, the vicinity refers to an angle range within 5 degrees, more preferably, within 3 degrees, and most preferably, within 2 degrees. By setting this range, in the case when the optical film 1 is bonded to the window material 10, of light rays made incident thereon from the sky, the light ray having the specific wavelength band can be effectively returned to the sky. Moreover, as in the case of an infrared-ray sensor and an infrared-ray image pick-up process, when the infrared-ray irradiation unit and the light-receiving unit are adjacent to each other, the retroreflection direction has to be made equal to the incident direction; however, as in the case of the present invention, when it is not necessary to carry out a sensing process in a specific direction, it is not necessary to make the directions precisely equal to each other.
In the optical film 1, with respect to the degree of transmission image clearness relative to a wavelength band having a transmitting property, the value at the time of using an optical comb of 0.5 mm is preferably set to 50 or more, more preferably, to 60 or more, and most preferably, to 75 or more. In the case when the value of the degree of transmission image clearness is less than 50, the transmission image tends to become a blurred image. In the case when it is from 50 or more to less than 60, no problems are raised for use in daily life, although it also depends on external brightness. In the case when it is from 60 or more to less than 75, although a diffraction pattern tends to cause an adverse effect only when a very bright object, such as a light source, is viewed, outside scenes can be clearly viewed. In the case when it is 75 or more, the diffraction pattern no longer causes an adverse effect. Moreover, the total value of values obtained by measurements by the use of optical combs of 0.125 mm, 0.5 mm, 1.0 mm and 2.0 mm is preferably set to 230 or more, more preferably, to 270 or more, and most preferably, to 350 or more. In the case when the total value of the degree of transmission image clearness is less than 230, the transmission image tends to become a blurred image. In the case when it is from 230 or more to less than 270, no problems are raised for use in daily life, although it also depends on external brightness. In the case when it is from 270 or more to less than 350, although a diffraction pattern tends to cause an adverse effect only when a very bright object, such as a light source, is viewed, outside scenes can be clearly viewed. In the case when it is 350 or more, the diffraction pattern no longer causes an adverse effect. In this case, the value of the degree of transmission image clearness is measured by using an ICM-1T made by Suga Test Instruments Co., Ltd. in accordance with JIS K7105. However, in the case when the wavelength to be preferably transmitted is different from a D65 light source wavelength, measurements are preferably carried out after a calibration process has been carried out by using a filter for the wavelength to be preferably transmitted.
In the optical film 1, haze relative to the wavelength band having a transmitting property is preferably set to 6% or less, more preferably, to 4% or less, and most preferably, to 2% or less. When the haze exceeds 6%, the transmission light is diffused to cause a foggy view. In this case, the haze is measured by using an HM-150 made by Murakami Color Research Laboratory by using a measuring method defined by JIS K7136. However, in the case when the wavelength to be preferably transmitted is different from a D65 light source wavelength, measurements are preferably carried out after a calibration process has been carried out by using a filter for the wavelength to be preferably transmitted. An incident surface S1 of the optical film 1, preferably, the incident surface S1 and a light-releasing surface S2, have such a degree of smoothness as not to lower the degree of transmission image clearness. More specifically, an arithmetic mean roughness Ra of the incident surface S1 and the light-releasing surface S2 is preferably set to 0.08 μm or less, more preferably, 0.06 μm or less, and most preferably, to 0.04 μm or less. Additionally, the above-mentioned arithmetic mean roughness Ra is calculated as a roughness parameter through processes in which the surface roughness of the incident surface is measured, and a roughness curve is obtained from a two-dimensional cross-sectional curve. Additionally, the measuring conditions are based upon JIS B0601: 2001. The measuring device and the measuring conditions are shown below.
Measuring device: fully automatic micro-shape measuring device, Surf-Coder ET4000A (made by Kosaka Laboratory Ltd.)
λc=0.8 mm, Evaluation length 4 mm, cut-off×5
Data sampling interval: 0.5 μm
The transmission color of the optical film 1 is preferably made as close to neutral color as possible, and even when colored, a faint color tone, such as blue, bluish green, green or the like, which gives a cool impression, is preferably used. From the viewpoint of obtaining such a color tone, chromaticity coordinates x, y of a transmission light ray released from the light-releasing surface S2 derived from an incident light ray on the incident surface S1 that is transmitted through the optical layer 2 and the reflection layer 3 are preferably set in a range of 0.20<x<0.35 and 0.20<y<0.40, more preferably in a range of 0.25<x<0.32 and 0.25<y<0.37, and most preferably in a range of 0.30<x<0.32 and 0.30<y<0.35, relative to irradiation from, for example, a D65 light source. Moreover, in order to prevent the color tone from becoming reddish, the relationship of y>x−0.02 is preferably satisfied, and more preferably, the relationship of y>x is satisfied. Moreover, in the case when a reflection color tone is varied depending on the incident angle, for example, in the case of the application as the window of a building, since the color tone becomes different depending on places or since the color looks differently when viewed while walking, these states are not preferable. From the viewpoint of suppressing these changes in color tone, the absolute value of a difference in the color coordinate x and the absolute value of a difference in the color coordinate y of an incident light ray that is made incident on the incident surface S1 or the light-releasing surface S2 at an incident angle θ in a range from 5° or more to 60° or less and that of a regular reflected light ray from the optical film 1 is preferably set to 0.05 or less, more preferably, to 0.03 or less, and most preferably, to 0.01 or less, in each of the two main surfaces of the optical film 1. These limitations in the numeric value range relative to the color coordinates x and y given to the reflected light ray are preferably satisfied on both of the surfaces of the incident surface S1 and the light-releasing surface S2.
The following description will successively discuss the first optical layer 4, the second optical layer 5 and the reflection layer 3 constituting the optical film 1.
The first optical layer 4 is, for example, used for supporting and also protecting the reflection layer 3. From the viewpoint of applying flexibility to the optical film 1, the first optical layer 4 is, for example, made of a layer mainly composed of a resin. Of the two main surfaces of the first optical layer 4, for example, one of the surfaces is a smoothed surface and the other surface is a concave-convex surface (first surface). The reflection layer 3 is formed on the concave-convex surface.
The second optical layer 5 is allowed to enclose and bury the first surface (concave-convex surface) of the first optical layer 4 on which the reflection layer 3 is formed so that it is used for protecting the reflection layer 3. From the viewpoint of applying flexibility to the optical film 1, the second optical layer 5 is made of, for example, a layer mainly composed of a resin. Of the two main surfaces of the second optical layer 5, for example, one of the surfaces is a smoothed surface and the other surface is a concave-convex surface (second surface). The concave-convex surface of the first optical layer 4 and the concave-convex surface of the second optical layer 5 have such a relationship that their mutual concave-convex shapes are inverted to each other.
The concave-convex surface of the first optical layer 4 is made of, for example, a plurality of structural elements 4c that are one-dimensionally arranged. The concave-convex surface of the second optical layer 5 is made of, for example, a plurality of structural elements 5c that are one-dimensionally arranged (see
In the optical film 1, the pitch P of the structural elements 4c is preferably set to 5 μm or more to 5 mm or less, more preferably, to 5 μm or more to less than 250 μm, and most preferably, to 20 μm or more to 200 μm or less. In the case when the pitch of the structural elements 4c is less than 5 μm, since it becomes difficult to form the shape of the structural elements 4c into a desired shape, and since it is generally difficult to make the wavelength selection characteristic of the reflection layer 3 abruptly changed, one portion of the transmission wavelength tends to be reflected. In the case when such a reflection occurs, a diffraction is generated so that a reflection up to a high-order reflection is visually recognized, with the result that the transparency tends to be felt worse. On the other hand, in the case when the pitch of the structural elements 4c exceeds 5 mm, in an attempt to take into consideration the shape of the structural elements 4c required for directional reflection, the required film thickness becomes too thick, with the result that the flexibility is lost, thereby making it difficult to be bonded to a rigid member such as the window material 10. Moreover, by setting the pitch of the structural elements 4c to less than 250 μm, the flexibility is further increased so that a manufacturing process in roll-to-roll operations is easily carried out, with the necessity of a batch production being eliminated. In order to apply the optical film 1 of the present invention to fittings, such as a window or the like, a length of about several meters is required so that the roll-to-roll manufacturing operations rather than the batch process are suitable. Moreover, when the pitch is set to 20 μm or more to 200 μm or less, the productivity is further improved.
Moreover, the shape of the structural elements 4c to be formed on the surface of the first optical layer 4 is not limited to one kind, and the structural elements 4c having shapes of a plurality of kinds may be formed on the first optical layer 4. In the case when the structural elements 4c having shapes of a plurality of kinds are formed on the surface, a predetermined pattern composed of the shapes of the plural kinds of the structural elements 4c may be periodically repeated. Moreover, depending on a desired characteristic, the plural kinds of the structural elements 4c may be formed at random (non-periodically).
The shapes of the structural elements 4c include, for example, a prism shape shown in
Moreover, as shown in
Preferably, the first optical layer 4 is mainly composed of a resin which is less susceptible to reduction in the storage elastic modulus at 100° C. and in which the storage elastic modulus is not varied so much between that at 25° C. and that at 100° C. More specifically, a resin in which the storage elastic modulus at 25° C. is set to 3×109 Pa or less and the storage elastic modulus at 100° C. is set to 3×107 Pa or more is preferably contained therein. Additionally, although the first optical layer 4 is preferably made of one kind of a resin, it may contain two or more kinds of resins. Moreover, an additive agent may be mixed therein, if necessary.
When the first optical layer 4 is mainly composed of a resin which is less susceptible to reduction in the storage elastic modulus at 100° C. and in which the storage elastic modulus is not varied so much between that at 25° C. and that at 100° C., even in the case of carrying out processes applying heat or heat and pressure after the formation of the concave-convex surface (first surface) of the first optical layer 4, a designed interface shape can be virtually maintained. In contrast, in the case when it is mainly composed of a resin that has a great reduction in the storage elastic modulus at 100° C. and in which the storage elastic modulus is varied greatly between that at 25° C. and that at 100° C., the interface shape is greatly deformed from the designed shape, with the result that a curling or the like tends to occur in the optical film 1.
In this case, those processes applying heat include not only a process such as an annealing process or the like in which heat is directly applied to the optical film 1 or its constituent member, but also a process in which upon film-forming a thin film and upon curing a resin composition, or the like, a temperature-rise occurs locally on the film-forming surface and the resulting heat is indirectly applied to those members, and a process in which the temperature of a metal mold is raised by irradiation with an energy ray so that heat is indirectly applied to the optical film. Moreover, the effects to be obtained by limiting the numeric value range of the above-mentioned storage elastic modulus are not particularly limited by the kinds of resins, and can be obtained by any of thermoplastic resins, thermosetting resins and energy-ray irradiation-type resins.
The storage elastic modulus of the first optical layer 4 can be confirmed, for example, by using the following method. In the case when the surface of the first optical layer 4 is exposed, the storage elastic modulus of the exposed surface can be confirmed by using a minute hardness meter. Moreover, in the case when the first substrate 4a or the like is formed on the surface of the optical layer 4, after separating the first substrate 4a or the like therefrom so that the surface of the first optical layer 4 is exposed, the storage elastic modulus of the exposed surface can be confirmed by measurements by the use of a minute hardness meter.
As a method for suppressing a reduction of the elastic modulus under high temperatures, for example, in the case of the thermoplastic resin, a method for adjusting the length, kind or the like of a side chain is proposed, and in the case of the thermosetting resin and energy-ray irradiation-type resin, a method for adjusting the amount of cross-linking points and the molecule structure of the cross-linking member is proposed. In this case, however, it is preferable to prevent the characteristic required for the resin material itself from being impaired by this structural change. For example, depending on the kinds of cross-linking agents, the elastic modulus becomes higher in the vicinity of room temperature to sometimes cause the resin to become brittle, or the shrinkage becomes greater to sometimes cause the resulting film to be curved or curled so that the kind of the cross-linking agent needs to be preferably selected on demand in accordance with desired characteristics.
In the case when the first optical layer 4 contains a crystalline polymeric material as its main component, it is also mainly composed of a resin which has a glass transition point higher than the maximum temperature within manufacturing processes and is less susceptible to a reduction of the storage elastic modulus under the maximum temperature in the manufacturing processes. On the other hand, in the case of using a resin which has a glass transition point that is higher than room temperature 25° C. and within a range lower than the maximum temperature in the manufacturing processes, and is susceptible to a great reduction of the storage elastic modulus under the maximum temperature in the manufacturing processes, it becomes difficult to maintain an optimally designed interface shape during the manufacturing processes.
In the case when the first optical layer 4 contains an amorphous polymeric material as its main component, it is also mainly composed of a resin which has a melting point higher than the maximum temperature within manufacturing processes and is less susceptible to a reduction of the storage elastic modulus under the maximum temperature in the manufacturing processes. In contrast, in the case of using a resin which has a glass transition point that is higher than room temperature 25° C. and is located within a range lower than the maximum temperature in the manufacturing processes, and is susceptible to a great reduction of the storage elastic modulus under the maximum temperature in the manufacturing processes, it becomes difficult to maintain an optimally designed interface shape during the manufacturing processes.
In this case, the maximum temperature in the manufacturing processes refers to the maximum temperature of the concave-convex surface (first surface) of the first optical layer 4 in the manufacturing processes. It is preferable for the second optical layer 5 to also satisfy the above-mentioned numeric value range of the storage elastic modulus and the temperature range of the glass transition point.
That is, at least one of the first optical layer 4 and the second optical layer 5 preferably contains a resin that has a storage elastic modulus at 25° C. of 3×109 Pa or less. Since it becomes possible to give flexibility to the optical film 1 at 25° C., the manufacturing process of the optical film 1 by using the roll-to-roll operation is achieved.
The first substrate 4a and the second substrate 5a have, for example, transparency. From the viewpoint of giving flexibility to the optical film 1, the shape of the substrate is preferably formed into a film shape; however, it is not limited only by this shape. As the material for the first substrate 4a and the second substrate 5a, for example, known polymeric materials may be used, and examples of the known polymeric materials include: triacetyl cellulose (TAC), polyester (TPEE), polyethylene terephthalate (PET), polyimide (PI), polyamide (PA), aramid, polyethylene (PE), polyacrylate, polyether sulfone, polysulfone, polypropylene (PP), diacetyl cellulose, polyvinyl chloride, acrylic resin (PMMA), polycarbonate (PC), epoxy resin, urea resin, urethane resin, melamine resin, and the like; however, the materials are not particularly limited by these. From the viewpoint of productivity, the thickness of the first substrate 4a and the second substrate 5a is preferably set to 38 to 100 μm; however, it is not particularly limited by this range. The first substrate 4a and the second substrate 5a are preferably provided with an energy-ray transmitting property. With this arrangement, as will be described later, an energy-ray is applied to an energy-ray setting-type resin interposed between the first substrate 4a or the second substrate 5a and the reflection layer 3 from the first substrate 4a or second substrate 5a side so that the energy-ray setting-type resin can be cured.
The first optical layer 4 and the second optical layer 5 has, for example, transparency. The first optical layer 4 and the second optical layer 5 are obtained, for example, by curing a resin composition. As the resin composition, from the viewpoint of easiness in production, an energy-ray setting-type resin that is cured by light, an electron beam, or the like, and a thermosetting type resin that is cured by heat are preferably used. With respect to the energy-ray setting-type resin, a photosensitive resin composition that is cured by light is preferably used, and an ultraviolet-ray setting resin composition that is cured by ultraviolet rays is most preferably used. From the viewpoint of improving the adhesion between the first optical layer 4 or the second optical layer 5 and the reflection layer 3, the resin composition preferably further contains a compound containing a phosphoric acid, a compound containing a succinic acid and a compound containing butyrolactone. As the compound containing a phosphoric acid, for example, (meth)acrylate containing a phosphoric acid, more preferably, (meth)acrylic monomer or oligomer having a phosphoric acid in its functional group may be used. As the compound containing a succinic acid, for example, (meth)acrylate containing a succinic acid, more preferably, (meth)acrylic monomer or oligomer containing a succinic acid in its functional group may be used. As the compound containing butyrolactone, for example, (meth)acrylate containing butyrolactone, more preferably, (meth)acrylic monomer or oligomer containing butyrolactone in its functional group may be used.
The ultraviolet-ray setting-type resin composition contains, for example, (meth)acrylate and a photo-polymerization initiator. Moreover, the ultraviolet-ray setting-type resin composition may further contains a photo-stabilizer, a flame retardant, a leveling agent, an antioxidant or the like, if necessary.
With respect to the acrylate, a monomer and/or an oligomer containing two or more (meth)acryloyl groups may be preferably used. As this monomer and/or oligomer, for example, urethane (meth)acrylate, epoxy(meth)acrylate, polyester(meth)acrylate, polyol(meth)acrylate, polyether(meth)acrylate, melamine(meth)acrylate, or the like may be used. In this case, the (meth)acryloyl group refers to either one of an acryloyl group and a methacryloyl group. In this case, the oligomer refers to a molecule having a molecular weight in a range from 500 or more to 60000 or less.
As the photo-polymerization initiator, one selected from known materials on demand can be used. As the known materials, for example, a benzophenone derivative, an acetophenone derivative, an anthraquinone derivative, and the like may be used alone, or in combination. The compounding amount of the polymerization initiator is preferably set in a range from 0.1 mass % or more to 10 mass % or less in solid components. When the amount is less than 0.1 mass %, the photo-setting property deteriorates, failing to be actually applied to the industrial production. In contrast, when the amount exceeds 10 mass %, odor tends to remain in the coated film in the case when the quantity of light irradiation is small. In this case, the solid components mean all the components constituting a hard coat layer 12 after its curing process. More specifically, for example, acrylate and the photo-polymerization initiator, etc. are referred to as solid components.
With respect to the resin, one that is capable of transferring a structure by irradiation with an energy ray, heat, or the like is preferably used, and any kind of resins, such as a vinyl-based resin, an epoxy-based resin, a thermoplastic resin or the like, may be used as long as it satisfies the requirement for the aforementioned refractive index.
In order to reduce the curing shrinkage, an oligomer may be added thereto. As the curing agent, polyisocyanate or the like may be contained therein. Moreover, when the adhesion between the first optical layer 4 and the second optical layer 5 is taken into consideration, a monomer having a hydroxyl group, a carboxylic group, or a phosphoric acid group, a coupling agent, such as polyhydric alcohols, carboxylic acid, silane, aluminum, titanium or the like, and various kinds of chelate agents may be added thereto.
The resin composition preferably further contains a cross-linking agent. As this cross-linking agent, a cyclic cross-linking agent is in particular preferably used. By using the cross-linking agent, it is possible to make the resin heat resistant without changing the storage elastic modulus greatly at room temperature. Additionally, in the case when the storage elastic modulus at room temperature is greatly varied, the optical film 1 tends to become brittle, making it difficult to manufacture the optical film 1 by the use of the roll-to-roll process, or the like. As the cyclic cross-linking agent, for example, dioxane glycol diacrylate, tricyclodecane dimethanol diacrylate, tricyclodecane dimethanol dimethacrylate, ethylene oxide modified isocyanurate diacrylate, ethylene oxide modified isocyanurate triacrylate, caprolactone modified tris(acryloxyethyl)isocyanurate, or the like are proposed.
The first substrate 4a or the second substrate 5a is preferably designed to have a water vapor permeability that is lower than that of the first optical layer 4 or the second optical layer 5. For example, in the case when the first optical layer 4 is formed by using an energy-ray setting-type resin, such as urethane acrylate, it is preferable to form the first substrate 4a by using a resin, such as polyethylene terephthalate (PET) or the like, which has a water vapor permeability that is lower than that of the first optical layer 4, and also has an energy-ray transmitting property. With this arrangement, moisture diffusion from the light-incident surface S1 or the light-releasing surface S2 toward the reflection layer 3 is reduced so that metal or the like contained in the reflection layer 3 is prevented from deteriorating. Therefore, the durability of the optical film 1 can be improved. Additionally, the water vapor permeability of the PET having a thickness of 75 μm is about 10 g/m2/day (40° C., 90% RH).
It is preferable to allow at least one of the first optical layer 4 and the second optical layer 5 to contain a functional group having a high polarity, with its contents being preferably different between the first optical layer 4 and the second optical layer 5. Both of the first optical layer 4 and the second optical layer 5 contain a phosphoric acid compound (for example, phosphate), and the contents of the phosphoric acid compound are preferably made different between the first optical layer 4 and the second optical layer 5. The contents of the phosphoric acid compound between the first optical layer 4 and the second optical layer 5 are preferably made different by two times or more, more preferably by five times or more, and most preferably by 10 times or more.
In the case when at least one of the first optical layer 4 and the second optical layer 5 contains a phosphoric acid compound, the reflection layer 3 preferably contains an oxide, a nitride or an oxynitride on its surface that is made in contact with the first optical layer 4 or the second optical layer 5 that contains the phosphoric acid compound. The reflection layer 3 is, in particular, preferably provided with a layer containing zinc oxide (ZnO) or niobium oxide on the surface that is made in contact with the first optical layer 4 or the second optical layer 5 containing the phosphoric acid compound. With this structure, the adhesion between these optical layer and the reflection layer 3 can be improved. Moreover, in the case when the reflection layer 3 contains metal, such as Ag or the like, its corrosion preventive effect can be improved. Furthermore, the reflection layer 3 may contain a dopant such as Al, Ga or the like. This structure makes it possible to improve the film quality and smoothness when a metal oxide layer is formed by sputtering or the like.
From the viewpoint of allowing at least one of the first optical layer 4 and the second optical layer 5 to give a designing property to the optical film 1, the window material 10, and the like, the layer preferably has a characteristic for absorbing light having a specific wavelength band within a visible light range. A pigment to be dispersed in a resin may be either an organic-based pigment or an inorganic-based pigment; however, an inorganic-based pigment that particularly has high weatherabillity in the pigment itself is preferably used. More specifically, inorganic pigments, such as Zircon Gray (Co, Ni doped ZrSiO4), Praseodymium Yellow (Pr doped ZrSiO4), Chromium Titanium Yellow (Cr, Sb doped TiO2 or Cr, W doped TiO2), Chromium Green (Cr2O3 or the like), Peacock Blue ((CoZn)O(AlCr)2O3), Victoria Green ((Al, Cr)2O3), Prussian Blue (CoO—Al2O3—SiO2), Vanadium Zirconium Blue (V doped ZrSiO4), Chrome Tin Pink (Cr doped CaO—SnO2—SiO2), Manganese Pink (Mn doped Al2O3) and Salmon Pink (Fe doped ZrSiO4) and organic-based pigments, such as azo-based pigments and phthalocyanine-based pigments, are proposed.
The reflection layer 3 is a wavelength-selective reflection layer of a laminated film in which of light rays made incident on the incident surface, for example, at an incident angle (θ, φ), a light ray having a specific wavelength band is directionally reflected, while light rays other than the light ray having the specific wavelength band are transmitted. The average layer thickness of the reflection layer 3 is preferably set to 20 μm, more preferably, to 5 μm or less, and most preferably, to 1 μm or less. When the average layer thickness of the reflection layer 3 exceeds 20 μm, a light path in which a transmitted light ray is refracted becomes longer, and a transmission image tends to be viewed in a distorted state. The formation method of the reflection layer may be carried out, for example, by using a sputtering method, a vapor deposition method, a dip coating method, a die-coating method, or the like.
The laminated film has a configuration of at least five layers in which, for example, metal layers, each having a high reflectance in an infrared light region, and high-refractive-index layers, each having a high refractive index relative to the metal layer in a visible light region and functioning as an antireflection layer, are alternately stacked. As the high-refractive-index layers, optical transparent layers or transparent conductive layers may be used.
The metal layers having a high reflectance in an infrared light region are mainly composed of a simple substance, for example, selected from the group consisting of Au, Ag, Cu, Al, Ni, Cr, Ti, Pd, Co, Si, Ta, W, Mo and Ge, or an alloy containing two or more kinds of these simple substances. From the viewpoint of practical use, among these, an Ag-based, Cu-based, Al-based, Si-based or Ge-based material is preferably used. Moreover, in the case of using an alloy as the metal layer, the metal layer is preferably mainly composed of AlCu, AlTi, AlCr, AlCo, AgNdCu, AlMgSi, AgBi, AgNdCu, AgPdCu, AgPdTi, AgCuTi, AgPdCa, AgPdMg, AgPdFe, Ag or SiB. Moreover, in order to suppress corrosion in the metal layer, another material, such as Ti, Nd or the like, is preferably added to the metal layer. In particular, in the case when Ag is used for the material of the metal layer, the above-mentioned material is preferably added thereto.
The optical transparent layer is an optical transparent layer having a high refractive index in the visible light region and serving as an antireflection layer. The optical transparent layer is mainly composed of a high dielectric material, such as, for example, niobium oxide, tantalum oxide, titanium oxide, or the like. The transparent conductive layer is mainly composed of, for example, a ZnO-based oxide, an indium-doped tin oxide, or the like. Additionally, as the ZnO-based oxide, for example, at least one kind of materials selected from the group consisting of zinc oxide (ZnO), gallium (Ga), zinc oxide (AZO) doped with aluminum (Al), zinc oxide (GZO) doped with aluminum (Al) and zinc oxide (GZO) doped with gallium (Ga) may be used.
Moreover, the refractive index of the high-refractive-index layer contained in the laminated film is preferably set in a range from 1.7 or more to 2.6 or less. More preferably, it is set in a range from 1.8 or more to 2.6 or less, and most preferably, it is set in a range from 1.9 or more to 2.6 or less. With this structure, it is possible to realize an antireflection property in the visible light region by using a thin film in such a degree as not to cause cracks. In this case, the refractive index is taken at a wavelength of 550 nm. The high-refractive-index layer is a layer mainly composed of, for example, a metal oxide. As the metal oxide, for example, at least one kind of materials selected from the group consisting of niobium oxide, zinc oxide, titanium oxide and tantalum oxide may be used, and from the viewpoint of alleviating the stress of the layer and suppressing the occurrence of cracks, in some cases, a metal oxide other than zinc oxide is more preferably used. In particular, at least one kind of materials selected from the group consisting of niobium oxide (for example, niobium pentoxide), tantalum oxide (for example, tantalum pentoxide) and titanium oxide is preferably used. The film thickness of the high-refractive-index layer is preferably set in a range from 10 nm or more to 120 nm or less, more preferably, from 10 nm or more to 100 nm or less, and most preferably, from 10 nm or more to 80 nm or less. In the case when the film thickness is less than 10 nm, the visible light tends to be easily reflected. In contrast, when the film thickness exceeds 120 nm, the transmittance tends to be lowered, and cracks tend to be generated.
The layer structure of the reflection layer 3 is not limited to this, and for example, each of the high-refractive-index layers may be separated into a plurality of layers so that each of them forms a single layer.
Moreover, in the example shown in
Additionally, the laminated film is not limited to a thin film made of an inorganic material, and may be formed as a thin film made of a polymeric material, or may be formed by stacking layers in which fine particles or the like are dispersed in a polymer. Moreover, in order to prevent degradation by oxidation of lower layer metal during a film-forming process of the optical transparent layer, a thin buffer layer made of Ti or the like having a thickness of about several nms may be formed on the interface of the optical transparent layer to be film-formed. In this case, the buffer layer refers to a layer which suppresses oxidation of a metal layer or the like serving as the lower layer by being oxidized itself at the time of film-forming an upper layer.
In the embodiment of the present invention, by determining an index value indicating a color tone such as a blue tone and a red tone and by forming a laminated film in a manner so as to satisfy the index value, a change in the color tone is suppressed. In this example, as the index value for color tones, a blue index and a red index are determined.
The blue index is an index value for use in determining whether or not transmission light is viewed with a blue tone. The blue index value is calculated through processes in which in a wavelength range from 620 nm to 750 nm, a light-source spectrum is respectively multiplied by a reflectance and a degree of visual sense, and the resulting products are integrated and the value thus obtained is divided by a value obtained by integrating the product of the light-source spectrum and the degree of visual sense.
The blue index value is preferably set to less than 0.152, and more preferably, to less than 0.111. This is because in the case when the blue index value is from 0 or more to less than 0.111, a blue tone hardly causes any adverse effect to feeling, and in the case when it is from 0.111 or more to less than 0.152, the blue tone is in such a degree as not to cause any adverse effect to feeling although it depends on external brightness. In contrast, in the case when the blue index value is from 0.152 or more to less than 0.2, transmission light tends to be viewed with a slightly blue tone when seen in a specific angle direction, while in the case when it is 0.2 or more, the transmission light tends to be viewed with a deep blue tone when seen in a specific angle direction.
The red index is an index value for use in determining whether or not transmission light is viewed with a red tone. In the same manner as in the blue index value, the red index value is calculated through processes in which in a wavelength range from 620 nm to 750 nm, a light-source spectrum is respectively multiplied by a reflectance and a degree of visual sense, and the resulting products are integrated and the value thus obtained is divided by a value obtained by integrating the product of the light-source spectrum and the degree of visual sense.
The red index value is preferably set to less than 0.258, and more preferably, to less than 0.175. This is because in the case when the red index value is from 0 or more to less than 0.175, a red tone hardly causes any adverse effect to feeling, and in the case when it is from 0.175 or more to less than 0.258, the red tone is in such a degree as not to cause any adverse effect to feeling although it depends on external brightness. In contrast, in the case when the red index value is from 0.258 or more to less than 0.3, transmission light tends to be viewed with a slightly red tone when seen in a specific angle, while in the case when it is 0.3 or more, the transmission light tends to be viewed with a deep red tone when seen in a specific angle direction.
Moreover, as shown in
Supposing that the light incident angle is δ, the refractive index of the first optical layer 4 is n and the reflectance of the reflection layer 3 is R, the ratio x of component LA to be reflected toward the sky relative to the entire incident light components is represented by the following formula (1).
x=(sin(45−δ′)+cos(45−δ′)/tan(45+δ′))/(sin(45−δ′)+cos(45−δ′))×R2 (1)
In this case, however, σ′=sin−1(sin σ/n) is satisfied.
In the case when the ratio of the component LB that is not reflected toward the sky is increased, the ratio of the incident light to be reflected toward the sky is reduced. In order to increase the ratio of the reflection toward the sky, the shape of the reflection layer 3 is changed, that is, it is effective to devise the shape of the structural element 4c of the first optical layer 4. For example, in order to increase the ratio of the reflection toward the sky, the shape of the structural element 4c is preferably formed into a lenticular shape shown in
The laminate rolls 41 and 42 are designed so as to nip the optical layer 9 with a reflection layer and a second substrate 5a. In this case, the optical layer 9 with the reflection layer has a structure in which the reflection layer 3 is film-formed on one of the main surfaces of the first optical layer 4. Additionally, as the optical layer 9 with the reflection layer, a first substrate 4a may be formed on the other main surface on the side opposite to the surface on which the reflection layer 3 of the first optical layer 4 is formed. In this example, the reflection layer 3 is film-formed on the one of the main surfaces of the first optical layer 4, and the first substrate 4a is formed on the other main surface. The guide rolls 43 are disposed on a transporting path inside the manufacturing device so as to transport a band-shaped optical film 1. The materials for the laminate rolls 41 and 42 and the guide rolls 43 are not particularly limited, and in accordance with desired roll characteristics, metal such as stainless steel, rubber, silicone and the like are selected on demand and may be used.
As the coating device 45, for example, a device provided with a coating means such as a coater or the like may be used. As the coater, for example, by taking into consideration physical properties or the like of the resin composition to be coated, a desired coater, such as a gravure coater, a wire bar coater or a die coater, may be selected and used on demand. The irradiation device 46 is an irradiation device that applies an ionizing ray, such as, for example, an electron beam, an ultraviolet ray, a visible ray or a gamma ray. In this example, as the irradiation device 46, a UV lamp for applying an ultraviolet ray is illustrated.
Referring to
First, as shown in
Moreover, as shown in
Next, as shown in
Next, as shown in
The following description will discuss a formation method of the optical film 1 by the use of the manufacturing device shown in
Next, the second substrate 5a thus transported and the optical layer 9 with the reflection layer are sandwiched by the laminate rolls 41 and 42 in a manner so as not to allow bubbles to be mingled between the second substrate 5a thus transported and the optical layer 9 with the reflection layer, so that the optical layer 9 with the reflection layer is laminated onto the second substrate 5a. Next, the second substrate 5a laminated with the optical layer 9 with the reflection layer is transported along the outer circumferential face of the laminate roll 41, with an ionizing ray being applied onto the ionizing ray setting resin 44 from the second substrate 5a side by the irradiation device 46 so that the ionizing ray setting resin 44 is cured. Thus, the second substrate 5a and the optical layer 9 with the reflection layer are bonded to each other, with the ionizing ray setting resin 44 being interposed therebetween, so that a target elongated optical film 1 is produced. Next, the band-shaped optical film 1 thus produced is wound around a winding roll, not shown. Thus, a material roll formed by winding the band-shaped optical film 1 therearound is obtained.
The cured first optical layer 4 is preferably set so as to have a storage elastic modulus of 3×107 Pa or more at (t−20) ° C. supposing that a process temperature at the time of the above-mentioned second optical layer formation is t ° C. In this case, for example, the process temperature t refers to a heating temperature of the laminate roll 41. The first optical layer 4 is formed, for example, on the first substrate 4a, and transported along the laminate roll 41 with the first substrate 4a interposed therebetween; therefore, it has been known from experience that the temperature to be actually applied onto the first optical layer 4 is about (t−20) ° C. For this reason, by setting the storage elastic modulus of the first optical layer 4 at 3×107 Pa or more at (t−20) ° C., it is possible to prevent the concave-convex shape on the interface inside the optical layer from being deformed by heat or heat and pressure.
Moreover, in the first optical layer 4, its storage elastic modulus at 25° C. is preferably set to 3×109 Pa or less. Thus, it is possible to impart flexibility at room temperature to the optical film. Therefore, the optical film 1 can be manufactured by using a manufacturing process such as a roll-to-roll process, or the like.
Additionally, the process temperature t is preferably set to 200° C. or less when the heat resistance of a resin for use in the optical layer or the substrate is taken into consideration. However, by using a resin having a high heat resistance, the process temperature t may be set to 200° C. or more.
As described earlier, the blue index value and the red index value indicating blue and red color tones are varied depending on the film thickness of each layer of the laminated film of the reflection layer 3. Therefore, in the embodiment of the present invention, by using the blue index value and the red index value as parameters, the film thickness of the laminated film is set so as to satisfy the conditions of these parameters.
Moreover, in this example, in addition to the blue index and the red index, a visible light-ray transmittance and a shading coefficient are used as parameters so as to set the film thickness of the laminated film. The visible light-ray transmittance is a parameter indicating transmittance of light, and preferably set to 70% or more. The shading coefficient is a parameter indicating an efficiency for shading heat, and preferably set to 0.6 or less. The visible light-ray transmittance and the shading coefficient are also varied in accordance with the film thickness of the laminated film in the same manner as in the blue index and the red index.
The film thickness of each of layers in the laminated film, which satisfies the conditions of the respective parameters, can be calculated, for example, by simulation. For example, by finding the distribution of each of the parameters by simulation, the film thickness that satisfies conditions of the respective parameters can be determined.
Upon carrying out a simulation, a ratio α and a ratio β that are determined in accordance with the film thickness of each of the layers of the laminated film of the reflection layer 3 are utilized. The ratio α indicates a ratio of the optical film thickness of the entire metal layer relative to the optical film thickness of the entire high-refractive-index layer. The ratio β indicates a ratio of an optical film thickness of the third high-refractive-index layer relative to an optical film thickness of the first high-refractive-index layer, when viewed on either one of the first optical layer side and the second optical layer side. Additionally, the optical film thickness indicates a film thickness obtained by multiplying the geometric film thickness by a refractive index.
In this case, the following explanation will be given by exemplifying a case in which the film thicknesses of the first and fifth high-refractive-index layers are virtually the same and the film thicknesses of the second and fourth metal layers are virtually the same when viewed on either one of the first optical layer side and the second optical layer side. In this case, the high-refractive-index layer is supposed to have a high refractive index relative to the metal layer. Supposing that the optical film thickness of the first and fifth high-refractive-index layers is X1, that the optical film thickness of the third high-refractive-index layer is X2, and that the optical film thickness of the second and fourth metal layers is Y, the total film thickness (geometric film thickness) L in the optical film thickness, the ratio α and the ratio β are calculated by the following formulas (2) to (4).
L=X1+Y+X2+Y+X1 (2)
α=2Y/(2X1+X2) (3)
β=X2/X1 (4)
By finding the total film thickness L, the ratio α and the ratio β, based upon the above-mentioned formulas (2) to (4), the film thicknesses of the respective layers in the laminated film of the reflection layer 3 that satisfy the conditions of the respective parameters can be set.
In the embodiment of the present invention, as shown in
Referring to a flowchart shown in
In step S6, a simulation is carried out based upon the conditions determined in steps S1 to S5, respective parameter values at the determined ratio α and ratio β are calculated. In step S7, visible light-ray transmittances at the determined ratio α and ratio β are calculated. In step S8, shading coefficients at the determined ratio α and ratio β are calculated. In step S9, a blue index at the determined ratio α and ratio β is calculated. In step S10, a red index at the determined ratio α and ratio β is calculated.
In step S11, by changing the ratio α and ratio β, the film thicknesses of the respective layers are changed, and the simulations of step S6 to step S10 are repeatedly carried out so that the respective parameter values are calculated.
In step S12, the respective parameter values calculated in steps S7 to S10 are mapped on an α-β plane, and as shown in
Next, in step S13, based upon the α-β correlation diagram relative to the respective parameters shown in
Blue index: less than 0.152, Red index: less than 0.258, Shading coefficient: 0.6 or less, Visible light-ray transmittance: 70% or more.
By overlapping the α-β correlation diagrams shown in
In step S14, these border lines are represented by mathematical formulas. For example, a specific value on a border line is extracted, and an approximation line of the border line between regions that satisfy the conditions of the respective parameters and regions that do not satisfy those conditions thereof is obtained based upon the value so that the border line is represented by a mathematical formula. Thus, the region that satisfies the conditions of the respective parameters is determined.
The following description will specifically explain the region that satisfies the conditions of the respective parameters relative to the ratio α and ratio β. First, with respect to a case in which the visible light-ray transmittance, the blue index and the red index are used as parameters, an explanation will be given for each of the total film thicknesses L of the reflection layer 3.
Based upon the points on the border line of the respective parameters plotted on the α-β correlation diagram, approximation curves of the border line based upon the respective parameters as indicated by the following formulas (5) to (7) are obtained.
α=−0.0004β2+0.0053β+0.0065 (5)
α=−1×10−5β2+0.0007β+0.0066 (6)
α=−1×10−5β2+0.0005β+0.0119 (7)
In this case, a region, which is indicated by half-tone dot meshing (hereinafter, referred to as “first region R1”) surrounded by the approximation curves indicated by formulas (5) to (7) and a straight line indicated by the following formula (8), corresponds to a region satisfying the conditions of the respective parameters. That is, by allowing the ratio α and ratio β to be included in the first region R1, the conditions of the respective parameters can be satisfied. In this case, it is supposed that the first region R1 includes the above-mentioned approximation lines and the straight line. Formula (8) is determined so as to prevent the film thickness of the metal layer from becoming 5 nm or less. This is because the film thickness of the metal layer of 5 nm or less causes physical values of the material for use in the metal layer to change, resulting in an increased possibility of deviation from the simulation value.
α=0.012114 (8)
In the following description, of the plane of L=80 nm, a portion defined by the first region R1 is referred to as “first plane Sp1” on demand.
α=−0.0002β2+0.0039β+0.0087 (9)
α=−3×10−5β2+0.0014β+0.0038 (10)
α=−2×10−5β2+0.0006β+0.0112 (11)
In this case, a region, which is indicated by half-tone dot meshing (hereinafter, referred to as “second region R2”) surrounded by the approximation curves indicated by formulas (9) to (11) and a straight line indicated by the following formula (12), corresponds to a region satisfying the conditions of the respective parameters. That is, by allowing the ratio α and ratio β to be included in the second region R2, the conditions of the respective parameters can be satisfied. In this case, it is supposed that the second region R2 includes the above-mentioned approximation lines and the straight line. Formula (12) is determined so as to prevent the film thickness of the metal layer from becoming 5 nm or less.
α=0.010589 (12)
In the following description, of the plane of L=90 nm, a portion defined by the second region R2 is referred to as “second plane Sp2” on demand.
α=−0.0002β2+0.0055β+0.0057 (13)
α=−0.0002β2+0.0045β−0.0067 (14)
α=−4×10−5β2+0.001β+0.0099 (15)
In this case, a region, which is indicated by half-tone dot meshing (hereinafter, referred to as “third region R3”) surrounded by the approximation curves indicated by formulas (13) to (15) and a straight line indicated by the following formula (16), corresponds to a region satisfying the conditions of the respective parameters. That is, by allowing the ratio α and ratio β to be included in the third region R3, the conditions of the respective parameters can be satisfied. In this case, it is supposed that the third region R3 includes the above-mentioned approximation lines and the straight line. Formula (16) is determined so as to prevent the film thickness of the metal layer from becoming 5 nm or less.
α=0.009403 (16)
In the following description, of the plane of L=100 nm, a portion defined by the third region R3 is referred to as “third plane Sp3” on demand.
α=−0.0003β2+0.0074β+0.0033 (17)
α=−0.0014β2+0.0191β−0.0422 (18)
α=−9×10−5β2+0.0015β+0.0084 (19)
In this case, a region, which is indicated by half-tone dot meshing (hereinafter, referred to as “fourth region R4”) surrounded by the approximation curves indicated by formulas (17) to (19) and a straight line indicated by the following formula (20), corresponds to a region satisfying the conditions of the respective parameters. That is, by allowing the ratio α and ratio β to be included in the fourth region R4, the conditions of the respective parameters can be satisfied. In this ease, it is supposed that the fourth region R4 includes the above-mentioned approximation lines and the straight line. Formula (20) is determined so as to prevent the film thickness of the metal layer from becoming 5 nm or less.
α=0.007709 (20)
In the following description, of the plane of L=120 nm, a portion defined by the fourth region R4 is referred to as “fourth plane Sp4” on demand.
α=−0.0014β2+0.0136β−0.0027 (21)
β=10132α2−241.39α+4.747 (22)
α=−0.0001β2+0.002β+0.0074 (23)
In this case, a region, which is indicated by half-tone dot meshing (hereinafter, referred to as “fifth region R5”) surrounded by the approximation curves indicated by formulas (21) to (23) and a straight line indicated by the following formula (24), corresponds to a region satisfying the conditions of the respective parameters. That is, by allowing the ratio α and ratio β to be included in the fifth region R5, the conditions of the respective parameters can be satisfied. In this case, it is supposed that the fifth region R5 includes the above-mentioned approximation lines and the straight line. Formula (24) is determined so as to prevent the film thickness of the metal layer from becoming 5 nm or less.
α=0.006523 (24)
In the following description, of the plane of L=140 nm, a portion defined by the fifth region R5 is referred to as “fifth plane Sp5” on demand.
α=−0.005β2+0.0273β−0.0145 (25)
α=0.0043β2−0.0332β+0.07 (26)
β=2.875 (27)
α=−0.0001β2+0.0025β+0.0062 (28)
In this case, a region, which is indicated by half-tone dot meshing (hereinafter, referred to as “sixth region R6”) surrounded by the approximation curves indicated by formulas (25) to (28) and a straight line indicated by the following formula (29), corresponds to a region satisfying the conditions of the respective parameters. That is, by allowing the ratio α and ratio β to be included in the sixth region R6, the conditions of the respective parameters can be satisfied. In this case, it is supposed that the sixth region R6 includes the above-mentioned approximation lines and the straight line. Formula (29) is determined so as to prevent the film thickness of the metal layer from becoming 5 nm or less.
α=0.005676 (29)
In the following description, of the plane of L=160 nm, a portion defined by the sixth region R6 is referred to as “sixth plane Sp6” on demand.
α=−0.0103β2+0.047β−0.0322 (30)
α=0.0093β2−0.0677β+0.1212 (31)
α=−0.0003β2+0.0036β+0.0046 (32)
In this case, a region, which is indicated by half-tone dot meshing (hereinafter, referred to as “seventh region R7”) surrounded by the approximation curves indicated by formulas (30) to (32) and a straight line indicated by the following formula (33), corresponds to a region satisfying the conditions of the respective parameters. That is, by allowing the ratio α and ratio β to be included in the seventh region R7, the conditions of the respective parameters can be satisfied. In this case, it is supposed that the seventh region R7 includes the above-mentioned approximation lines and the straight line. Formula (33) is determined so as to prevent the film thickness of the metal layer from becoming 5 nm or less.
α=0.00498 (33)
In the following description, of the plane of L=180 nm, a portion defined by the seventh region R7 is referred to as “seventh plane Sp7” on demand.
With respect to a case in which in addition to the above-mentioned visible light-ray transmittance, blue index and red index, a shading coefficient is also used as parameters, an explanation will be given for each of the total film thicknesses L of the reflection layer 3.
In addition to the approximation curves of the border line indicated by the aforementioned formulas (5) to (7), based upon the points on the border line of the shading coefficient plotted on the α-β correlation diagram, an approximation curve of the border line indicated by the following formula (34) is obtained.
α=−6×10−6β2+0.0002β+0.0141 (34)
In this case, a region, which is indicated by half-tone dot meshing (hereinafter, referred to as “first region R11”) surrounded by the approximation curves indicated by the formulas (6), (7) and (34), corresponds to a region satisfying the conditions of all the parameters. That is, by allowing the ratio α and ratio β to be included in the first region R11, the conditions of the respective parameters can be satisfied. In this case, it is supposed that the first region R11 includes the above-mentioned approximation curves. Additionally, of the plane of L=80 nm, a portion defined by the first region R11 is referred to as “first plane Sp11” on demand.
α=−1×10−5β2+0.0002β+0.0125 (35)
In this case, a region, which is indicated by half-tone dot meshing (hereinafter, referred to as “second region R12”) surrounded by the approximation curves indicated by the formulas (10), (11) and (35), corresponds to a region satisfying the conditions of all the parameters. That is, by allowing the ratio α and ratio β to be included in the second region R12, the conditions of the respective parameters can be satisfied. In this case, it is supposed that the second region R12 includes the above-mentioned approximation curves. Additionally, of the plane of L=90 nm, a portion defined by the second region R12 is referred to as “second plane Sp12” on demand.
α=−3×10−5β2+0.0004β+0.0113 (36)
In this case, a region, which is indicated by half-tone dot meshing (hereinafter, referred to as “third region R13”) surrounded by the approximation curves indicated by the formulas (14), (15) and (36), corresponds to a region satisfying the conditions of all the parameters. That is, by allowing the ratio α and ratio β to be included in the third region R13, the conditions of the respective parameters can be satisfied. In this case, it is supposed that the third region R13 includes the above-mentioned approximation curves. Additionally, of the plane of L=100 nm, a portion defined by the third region R13 is referred to as “third plane Sp13” on demand.
α=−7×10−5β2+0.0007β+0.0097 (37)
In this case, a region, which is indicated by half-tone dot meshing (hereinafter, referred to as “fourth region R14”) surrounded by the approximation curves indicated by the formulas (18), (19) and (37), corresponds to a region satisfying the conditions of all the parameters. That is, by allowing the ratio α and ratio β to be included in the fourth region R14, the conditions of the respective parameters can be satisfied. In this case, it is supposed that the fourth region R14 includes the above-mentioned approximation curves. Additionally, of the plane of L=120 nm, a portion defined by the fourth region R14 is referred to as “fourth plane Sp14” on demand.
α=−0.0001β2+0.0011β+0.0083 (38)
In this case, a region, which is indicated by half-tone dot meshing (hereinafter, referred to as “fifth region R15”) surrounded by the approximation curves indicated by the formulas (22), (23) and (38), corresponds to a region satisfying the conditions of all the parameters. That is, by allowing the ratio α and ratio β to be included in the third region R15, the conditions of the respective parameters can be satisfied. In this case, it is supposed that the fifth region R15 includes the above-mentioned approximation curves. Additionally, of the plane of L=140 nm, a portion defined by the fifth region R15 is referred to as “fifth plane Sp15” on demand.
α=−0.0002β2+0.0016β+0.0067 (39)
In this case, a region, which is indicated by half-tone dot meshing (hereinafter, referred to as “sixth region R16”) surrounded by the approximation curves indicated by the formulas (25) to (28), and (39), corresponds to a region satisfying the conditions of all the parameters. That is, by allowing the ratio α and ratio β to be included in the sixth region R16, the conditions of the respective parameters can be satisfied. In this case, it is supposed that the third region R16 includes the above-mentioned approximation curves. Additionally, of the plane of L=160 nm, a portion defined by the sixth region R16 is referred to as “sixth plane Sp16” on demand.
α=−0.0003β2+0.0021β+0.0055 (40)
In this case, a region, which is indicated by half-tone dot meshing (hereinafter, referred to as “seventh region R17”) surrounded by the approximation curves indicated by the formulas (30) to (32) and (40), corresponds to a region satisfying the conditions of all the parameters. That is, by allowing the ratio α and ratio β to be included in the seventh region R17, the conditions of the respective parameters can be satisfied. In this case, it is supposed that the seventh region R17 includes the above-mentioned approximation curves. Additionally, of the plane of L=180 nm, a portion defined by the seventh region R17 is referred to as “seventh plane Sp17” on demand.
Next, the following description will discuss a method for determining a region that satisfies the conditions of the respective parameters in the case when the total film thickness L is other than a specific film thickness.
As shown in
First, the following description will discuss a case in which by using the visible light-ray transmittance, the blue index and the red index as the parameters, the total film thickness L is set to a value between predetermined total film thicknesses L (=80 nm, 90 nm, . . . , 180 nm) so as to satisfy the conditions of the parameters.
(80 nm<L<90 nm)
In the case when the total film thickness L is represented by 80 nm<L<90 nm, as shown in
As shown in
Supposing that each of minute sides formed by dividing a periphery C1 of the first region R1 into n-equal portions, with an intersection P between formula (5) and formula (7) being set as a starting point, is represented as ΔC1i and that each of minute sides formed by dividing a periphery C2 of the second region R2 into n-equal portions, with an intersection P between formula (9) and formula (11) being set as a starting point, is represented as ΔC2i, each of minute regions having a rectangular shape, with ΔC1i and ΔC2i being defined as the two short sides, is defined as ΔSi. In this case, i represents a natural number from 0 to n, with n→∞ being preferably set. Moreover, suppose that i increases in a clockwise direction when the first region R1 and the second region R2 are viewed from the L axis direction (that is, in an increasing direction of the total film thickness L). A circumferential surface, which is composed of a group of minute regions ΔSi defined in this manner, is defined as the circumferential surface S1.
α=−0.0004β2+0.0053β+0.0065 (5)
α=−1×10−5β2+0.0005β+0.0119 (7)
α=−0.0002β2+0.0039β+0.0087 (9)
α=−2×10−5β2+0.0006β+0.0112 (11)
(90 nm<L<100 nm)
In the case when the total film thickness L is represented by 90 nm<L<100 nm, as shown in
As shown in
Supposing that each of minute sides formed by dividing a periphery C2 of the second region R2 into n-equal portions, with an intersection P between formula (9) and formula (11) being set as a starting point, is represented as ΔC2i and that each of minute sides formed by dividing a periphery C3 of the third region R3 into n-equal portions, with an intersection P between formula (13) and formula (15) being set as a starting point, is represented as ΔC3i, each of minute regions having a rectangular shape, with ΔC2i and ΔC3i being defined as the two short sides, is defined as ΔSi. In this case, i represents a natural number from 0 to n, with n→∞ being preferably set. Moreover, suppose that i increases in a clockwise direction when the second region R2 and the third region R3 are viewed from the L axis direction (that is, in an increasing direction of the total film thickness L). A circumferential surface, which is composed of a group of minute regions ΔSi defined in this manner, is defined as the circumferential surface S2.
α=−0.0002β2+0.0039β+0.0087 (9)
α=−2×10−5β2+0.0006β+0.0112 (11)
α=−0.0002β2+0.0055β+0.0057 (13)
α=−4×10−5β2+0.001β+0.0099 (15)
(100 nm<L<120 nm)
In the case when the total film thickness L is represented by 100 nm<L<120 nm, as shown in
As shown in
Supposing that each of minute sides formed by dividing a periphery C3 of the third region R3 into n-equal portions, with an intersection P between formula (13) and formula (15) being set as a starting point, is represented as ΔC3i and that each of minute sides formed by dividing a periphery C4 of the fourth region R4 into n-equal portions, with an intersection P between formula (17) and formula (19) being set as a starting point, is represented as ΔC4i, each of minute regions having a rectangular shape, with ΔC3i and ΔC4i being defined as the two short sides, is defined as ΔSi. In this case, i represents a natural number from 0 to n, with n→∞ being preferably set. Moreover, suppose that i increases in a clockwise direction when the third region R3 and the fourth region R4 are viewed from the L axis direction (that is, in an increasing direction of the total film thickness L). A circumferential surface, which is composed of a group of minute regions ΔSi defined in this manner, is defined as the circumferential surface S3.
α=−0.0002β2+0.0055β+0.0057 (13)
α=−4×10−5β2+0.001β+0.0099 (15)
α=−0.0003β2+0.0074β+0.0033 (17)
α=−9×10−5β2+0.0015β+0.0084 (19)
(120 nm<L<140 nm)
In the case when the total film thickness L is represented by 120 nm<L<140 nm, as shown in
As shown in
Supposing that each of minute sides formed by dividing a periphery C4 of the fourth region R4 into n-equal portions, with an intersection P between formula (17) and formula (19) being set as a starting point, is represented as ΔC4i and that each of minute sides formed by dividing a periphery C5 of the fifth region R5 into n-equal portions, with an intersection P between formula (21) and formula (23) being set as a starting point, is represented as ΔC5i, each of minute regions having a rectangular shape, with ΔC4i and ΔC5i being defined as the two short sides, is defined as ΔSi. In this case, i represents a natural number from 0 to n, with n→∞ being preferably set. Moreover, suppose that i increases in a clockwise direction when the fourth region R4 and the fifth region R5 are viewed from the L axis direction (that is, in an increasing direction of the total film thickness L). A circumferential surface, which is composed of a group of minute regions ΔSi defined in this manner, is defined as the circumferential surface S4.
α=−0.0003β2+0.0074β+0.0033 (17)
α=−9×10−5β2+0.0015β+0.0084 (19)
α=−0.0014β2+0.0136β−0.0027 (21)
α=−0.0001β2+0.002β+0.0074 (23)
(140 nm<L<160 nm)
In the case when the total film thickness L is represented by 140 nm<L<160 nm, as shown in
As shown in
Supposing that each of minute sides formed by dividing a periphery C5 of the fifth region R5 into n-equal portions, with an intersection P between formula (21) and formula (23) being set as a starting point, is represented as ΔC5i and that each of minute sides formed by dividing a periphery C6 of the sixth region R6 into n-equal portions, with an intersection P between formula (25) and formula (28) being set as a starting point, is represented as ΔC6i, each of minute regions having a rectangular shape, with ΔC5i and ΔC6i being defined as the two short sides, is defined as ΔSi. In this case, i represents a natural number from 0 to n, with n→∞ being preferably set. Moreover, suppose that i increases in a clockwise direction when the fifth region R5 and the sixth region R6 are viewed from the L axis direction (that is, in an increasing direction of the total film thickness L). A circumferential surface, which is composed of a group of minute regions ΔSi defined in this manner, is defined as the circumferential surface S5.
α=−0.0014β2+0.0136β−0.0027 (21)
α=−0.0001β2+0.002β+0.0074 (23)
α=−0.005β2+0.0273β−0.0145 (25)
α=−0.0001β2+0.0025β+0.0062 (28)
(160 nm<L<180 nm)
In the case when the total film thickness L is represented by 160 nm<L<180 nm, as shown in
As shown in
Supposing that each of minute sides formed by dividing a periphery C6 of the sixth region R6 into n-equal portions, with an intersection P between formula (25) and formula (28) being set as a starting point, is represented as ΔC6i and that each of minute sides formed by dividing a periphery C7 of the seventh region R7 into n-equal portions, with an intersection P between formula (30) and formula (32) being set as a starting point, is represented as ΔC7i, each of minute regions having a rectangular shape, with ΔC6i and ΔC7i being defined as the two short sides, is defined as ΔSi. In this case, i represents a natural number from 0 to n, with n→∞ being preferably set. Moreover, suppose that i increases in a clockwise direction when the sixth region R6 and the seventh region R7 are viewed from the L axis direction (that is, in an increasing direction of the total film thickness L). A circumferential surface, which is composed of a group of minute regions ΔSi defined in this manner, is defined as the circumferential surface S6.
α=−0.005β2+0.0273β−0.0145 (25)
α=−0.0001β2+0.0025β+0.0062 (28)
α=−0.0103β2+0.047β−0.0322 (30)
α=−0.0003β2+0.0036β+0.0046 (32)
Therefore, a region that satisfies the conditions of the parameters of the visible light-ray transmittance, the blue index and the red index is determined in the following mariner for each of ranges of the respective total film thicknesses L.
(80 nm≦L≦90 nm)
In the case when the total film thickness L is represented by 80 nm≦L≦90 nm, a region (space) V1, which is surrounded by the first plane Sp1 defined by the first region R1, the second plane Sp2 defined by the second region R2 and a circumferential surface S1, with these planes serving as two end faces thereof, forms a region that satisfies the conditions of the respective parameters. That is, by allowing the ratio α and ratio β to be included in the region (space) V1 surrounded by the plane Sp1, the plane Sp2 and the circumferential surface S1 having these two planes as its two end faces, the conditions of the respective parameters can be satisfied. In this case, it is supposed that the region (space) V1 includes the plane Sp1, the plane Sp2 and the circumferential surface S1.
(90 nm≦L≦100 nm)
In the case when the total film thickness L is represented by 90 nm≦L≦100 nm, a region (space) V2, which is surrounded by the second plane Sp2 defined by the second region R2, the third plane Sp3 defined by the third region R3 and a circumferential surface S2, with these planes serving as two end faces thereof, forms a region that satisfies the conditions of the respective parameters. That is, by allowing the ratio α and ratio β to be included in the region (space) V2 surrounded by the plane Sp2, the plane Sp3 and the circumferential surface S2 having these two planes as its two end faces, the conditions of the respective parameters can be satisfied. In this case, it is supposed that the region (space) V2 includes the plane Sp2, the plane Sp3 and the circumferential surface S2.
(100 nm≦L≦120 nm)
In the case when the total film thickness L is represented by 100 nm≦L≦120 nm, a region (space) V3, which is surrounded by the third plane Sp3 defined by the third region R3, the fourth plane Sp4 defined by the fourth region R4 and a circumferential surface S3, with these planes serving as two end faces thereof, forms a region that satisfies the conditions of the respective parameters. That is, by allowing the ratio α and ratio β to be included in the region (space) V3 surrounded by the plane Sp3, the plane Sp4 and the circumferential surface S3 having these two planes as its two end faces, the conditions of the respective parameters can be satisfied. In this case, it is supposed that the region (space) V3 includes the plane Sp3, the plane Sp4 and the circumferential surface S3.
(120 nm≦L≦140 nm)
In the case when the total film thickness L is represented by 120 nm≦L≦140 nm, a region (space) V4, which is surrounded by the fourth plane Sp4 defined by the fourth region R4, the fifth plane Sp5 defined by the fifth region R5 and a circumferential surface S4, with these planes serving as two end faces thereof, forms a region that satisfies the conditions of the respective parameters. That is, by allowing the ratio α and ratio β to be included in the region (space) V4 surrounded by the plane Sp4, the plane Sp5 and the circumferential surface S4 having these two planes as its two end faces, the conditions of the respective parameters can be satisfied. In this case, it is supposed that the region (space) V4 includes the plane Sp4, the plane Sp5 and the circumferential surface S4.
(140 nm≦L≦160 nm)
In the case when the total film thickness L is represented by 140 nm≦L≦160 nm, a region (space) V5, which is surrounded by the fifth plane Sp5 defined by the fifth region R5, the sixth plane Sp6 defined by the sixth region R6 and a circumferential surface S5, with these planes serving as two end faces thereof, forms a region that satisfies the conditions of the respective parameters. That is, by allowing the ratio α and ratio β to be included in the region (space) V5 surrounded by the plane Sp5, the plane Sp6 and the circumferential surface S5 having these two planes as its two end faces, the conditions of the respective parameters can be satisfied. In this case, it is supposed that the region (space) V5 includes the plane Sp5, the plane Sp6 and the circumferential surface S5.
(160 nm≦L≦180 nm)
In the case when the total film thickness L is represented by 160 nm≦L≦180 nm, a region (space) V6, which is surrounded by the sixth plane Sp6 defined by the sixth region R6, the seventh plane Sp7 defined by the seventh region R7 and a circumferential surface S6, with these planes serving as two end faces thereof, forms a region that satisfies the conditions of the respective parameters. That is, by allowing the ratio α and ratio β to be included in the region (space) V6 surrounded by the plane Sp6, the plane Sp7 and the circumferential surface S6 having these two planes as its two end faces, the conditions of the respective parameters can be satisfied. In this case, it is supposed that the region (space) V6 includes the plane Sp6, the plane Sp7 and the circumferential surface S6.
Next, the following description will discuss a case in which by also using a shading coefficient as the parameters in addition to the visible light-ray transmittance, the blue index and the red index, the total film thickness L is set to a value between predetermined total film thicknesses L (=80 nm, 90 nm, . . . , 180 nm).
In the case when as shown in
(80 nm<L<90 nm)
In the case when the total film thickness L is represented by 80 nm<L<90 nm, as shown in
As shown in
Supposing that each of minute sides formed by dividing a periphery C11 of the first region R11 into n-equal portions, with an intersection P between formula (7) and formula (34) being set as a starting point, is represented as ΔC11i and that each of minute sides formed by dividing a periphery C12 of the second region R12 into n-equal portions, with an intersection P between formula (11) and formula (35) being set as a starting point, is represented as ΔC2i, each of minute regions having a rectangular shape, with ΔC11i and ΔC12i being defined as the two short sides, is defined as ΔSi. In this case, i represents a natural number from 0 to n, with n→∞ being preferably set. Moreover, suppose that i increases in a clockwise direction when the first region R11 and the second region R12 are viewed from the L axis direction (that is, in an increasing direction of the total film thickness L). A circumferential surface, which is composed of a group of minute regions ΔSi defined in this manner, is defined as the circumferential surface S11.
α=−1×10−5β2+0.0005β+0.0119 (7)
α=−6×10−6β2+0.0002β+0.0141 (34)
α=−2×10−5β2+0.0006β+0.0112 (11)
α=−1×10−5β2+0.0002β+0.0125 (35)
(90 nm<L<100 nm)
In the case when the total film thickness L is represented by 90 nm<L<100 nm, as shown in
As shown in
Supposing that each of minute sides formed by dividing a periphery C12 of the second region R12 into n-equal portions, with an intersection P between formula (11) and formula (35) being set as a starting point, is represented as, ΔC12i and that each of minute sides formed by dividing a periphery C13 of the third region R13 into n-equal portions, with an intersection P between formula (15) and formula (36) being set as a starting point, is represented as ΔC13i, each of minute regions having a rectangular shape, with ΔC12i and ΔC13i being defined as the two short sides, is defined as ΔSi. In this case, i represents a natural number from 0 to n, with n→∞ being preferably set. Moreover, suppose that i increases in a clockwise direction when the second region R12 and the third region R13 are viewed from the L axis direction (that is, in an increasing direction of the total film thickness L). A circumferential surface, which is composed of a group of minute regions ΔSi defined in this manner, is defined as the circumferential surface S12.
α=−2×10−5β2+0.0006β+0.0112 (11)
α=−1×10−5β2+0.0002β+0.0125 (35)
α=−4×10−5β2+0.001β+0.0099 (15)
α=−3×10−5β2+0.0004β+0.0113 (36)
(100 nm<L<120 nm)
In the case when the total film thickness L is represented by 100 nm<L<120 nm, as shown in
As shown in
Supposing that each of minute sides formed by dividing a periphery C13 of the third region R13 into n-equal portions, with an intersection P between formula (15) and formula (36) being set as a starting point, is represented as ΔC13i and that each of minute sides formed by dividing a periphery C14 of the fourth region R14 into n-equal portions, with an intersection P between formula (19) and formula (37) being set as a starting point, is represented as ΔC14i, each of minute regions having a rectangular shape, with ΔC13i and ΔC14i being formed as the two short sides, is defined as ΔSi. In this case, i represents a natural number from 0 to n, with n→∞ being preferably set. Moreover, suppose that i increases in a clockwise direction when the third region R13 and the fourth region R14 are viewed from the L axis direction (that is, in an increasing direction of the total film thickness L). A circumferential surface, which is composed of a group of minute regions ΔSi defined in this manner, is defined as the circumferential surface S13.
α=−4×10−5β2+0.001β+0.0099 (15)
α=−3×10−5β2+0.0004β+0.0113 (36)
α=−9×10−5β2+0.0015β+0.0084 (19)
α=−7×10−5β2+0.0007β+0.0097 (37)
(120 nm<L<140 nm)
In the case when the total film thickness L is represented by 120 nm<L<140 nm, as shown in
As shown in
Supposing that each of minute sides formed by dividing a periphery C14 of the fourth region R14 into n-equal portions, with an intersection P between formula (19) and formula (37) being set as a starting point, is represented as ΔC14i and that each of minute sides formed by dividing a periphery C15 of the fifth region R15 into n-equal portions, with an intersection P between formula (23) and formula (38) being set as a starting point, is represented as ΔC15i, each of minute regions having a rectangular shape, with ΔC14i and ΔC15i being defined as the two short sides, is defined as ΔSi. In this case, i represents a natural number from 0 to n, with n→∞ being preferably set. Moreover, suppose that i increases in a clockwise direction when the fourth region R14 and the fifth region R15 are viewed from the L axis direction (that is, in an increasing direction of the total film thickness L). A circumferential surface, which is composed of a group of minute regions ΔSi defined in this manner, is defined as the circumferential surface S14.
α=−9×10−5β2+0.0015β+0.0084 (19)
α=−7×10−5β2+0.0007β+0.0097 (37)
α=−0.0001β2+0.002β+0.0074 (23)
α=−0.0001β2+0.0011β+0.0083 (38)
(140 nm<L<160 nm)
In the case when the total film thickness L is represented by 140 nm<L<160 nm, as shown in
As shown in
Supposing that each of minute sides formed by dividing a periphery C15 of the fifth region R15 into n-equal portions, with an intersection P between formula (23) and formula (38) being set as a starting point, is represented as ΔC15i and that each of minute sides formed by dividing a periphery C16 of the sixth region R16 into n-equal portions, with an intersection P between formula (28) and formula (39) being set as a starting point, is represented as ΔC16i, each of minute regions having a rectangular shape, with ΔC15i and ΔC16i being defined as the two short sides, is defined as ΔSi. In this case, i represents a natural number from 0 to n, with n→∞ being preferably set. Moreover, suppose that i increases in a clockwise direction when the fifth region R15 and the sixth region R16 are viewed from the L axis direction (that is, in an increasing direction of the total film thickness L). A circumferential surface, which is composed of a group of minute regions ΔSi defined in this manner, is defined as the circumferential surface S15.
α=−0.0001β2+0.002β+0.0074 (23)
α=−0.0001β2+0.0011β+0.0083 (38)
α=−0.005β2+0.0273β−0.0145 (28)
α=−0.0002β2+0.0016β+0.0067 (39)
(160 nm<L<180 nm)
In the case when the total film thickness L is represented by 160 nm<L<180 nm, as shown in
As shown in
Supposing that each of minute sides formed by dividing a periphery C16 of the sixth region R16 into n-equal portions, with an intersection P between formula (28) and formula (39) being set as a starting point, is represented as ΔC16i and that each of minute sides formed by dividing a periphery C17 of the seventh region R17 into n-equal portions, with an intersection P between formula (32) and formula (40) being set as a starting point, is represented as ΔC17i, each of minute regions having a rectangular shape, with ΔC16i and ΔC17i being defined as the two short sides, is defined as ΔSi. In this case, i represents a natural number from 0 to n, with n→∞ being preferably set. Moreover, suppose that i increases in a clockwise direction when the sixth region R16 and the seventh region R17 are viewed from the L axis direction (that is, in an increasing direction of the total film thickness L). A circumferential surface, which is composed of a group of minute regions ΔSi defined in this manner, is defined as the circumferential surface S16.
α=−0.005β2+0.0273β−0.0145 (28)
α=−0.0002β2+0.0016β+0.0067 (39)
α=−0.0103β2+0.047β−0.0322 (32)
α=−0.0003β2+0.0021β+0.0055 (40)
Therefore, a region that satisfies the conditions of the parameters of the visible light-ray transmittance, the blue index, the red index and the shading coefficient is determined in the following manner for each of ranges of the respective total film thicknesses L.
(80 nm≦L≦90 nm)
In the case when the total film thickness L is represented by 80 nm≦L≦90 mm, a region (space) V11, which is surrounded by the first plane Sp11 defined by the first region R11, the second plane Sp12 defined by the second region R12 and a circumferential surface S11, with these planes serving as two end faces thereof, forms a region that satisfies the conditions of the respective parameters. That is, by allowing the ratio α and ratio β to be included in the region (space) V11 surrounded by the plane Sp11, the plane Sp12 and the circumferential surface S11 having these two planes as its two end faces, the conditions of the respective parameters can be satisfied. In this case, it is supposed that the region (space) V11 includes the plane Sp11, the plane Sp12 and the circumferential surface S11.
(90 nm≦L≦100 nm)
In the case when the total film thickness L is represented by 90 nm≦L≦100 nm, a region (space) V12, which is surrounded by the second plane Sp12 defined by the second region R12, the third plane Sp13 defined by the third region R13 and a circumferential surface S12, with these planes serving as two end faces thereof, forms a region that satisfies the conditions of the respective parameters. That is, by allowing the ratio α and ratio β to be included in the region (space) V12 surrounded by the plane Sp12, the plane Sp13 and the circumferential surface S12 having these two planes as its two end faces, the conditions of the respective parameters can be satisfied. In this case, it is supposed that the region (space) V12 includes the plane Sp12, the plane Sp13 and the circumferential surface S12.
(100 nm≦L≦120 nm)
In the case when the total film thickness L is represented by 100 nm≦L≦120 nm, a region (space) V13, which is surrounded by the third plane Sp13 defined by the third region R13, the fourth plane Sp14 defined by the fourth region R14 and a circumferential surface S13, with these planes serving as two end faces thereof, forms a region that satisfies the conditions of the respective parameters. That is, by allowing the ratio α and ratio β to be included in the region (space) V13 surrounded by the plane Sp13, the plane Sp14 and the circumferential surface S13 having these two planes as its two end faces, the conditions of the respective parameters can be satisfied. In this case, it is supposed that the region (space) V13 includes the plane Sp13, the plane Sp14 and the circumferential surface S13.
(120 nm≦L≦140 nm)
In the case when the total film thickness L is represented by 120 nm≦L≦140 nm, a region (space) V14, which is surrounded by the fourth plane Sp14 defined by the fourth region R14, the fifth plane Sp15 defined by the fifth region R15 and a circumferential surface S14, with these planes serving as two end faces thereof, forms a region that satisfies the conditions of the respective parameters. That is, by allowing the ratio α and ratio β to be included in the region (space) V14 surrounded by the plane Sp14, the plane Sp15 and the circumferential surface S14 having these two planes as its two end faces, the conditions of the respective parameters can be satisfied. In this case, it is supposed that the region (space) V14 includes the plane Sp14, the plane Sp15 and the circumferential surface S14.
(140 nm≦L≦160 nm)
In the case when the total film thickness L is represented by 140 nm≦L≦160 nm, a region (space) V15, which is surrounded by the fifth plane Sp15 defined by the fifth region R15, the sixth plane Sp16 defined by the sixth region R16 and a circumferential surface S15, with these planes serving as two end faces thereof, forms a region that satisfies the conditions of the respective parameters. That is, by allowing the ratio α and ratio β to be included in the region (space) V15 surrounded by the plane Sp15, the plane Sp16 and the circumferential surface S15 having these two planes as its two end faces, the conditions of the respective parameters can be satisfied. In this case, it is supposed that the region (space) V15 includes the plane Sp15, the plane Sp16 and the circumferential surface S15.
(160 nm≦L≦180 nm)
In the case when the total film thickness L is represented by 160 nm≦L≦180 nm, a region (space) V16, which is surrounded by the sixth plane Sp16 defined by the sixth region R16, the seventh plane Sp17 defined by the seventh region R17 and a circumferential surface S16, with these planes serving as two end faces thereof, forms a region that satisfies the conditions of the respective parameters. That is, by allowing the ratio α and ratio β to be included in the region (space) V16 surrounded by the plane Sp16, the plane Sp17 and the circumferential surface S16 having these two planes as its two end faces, the conditions of the respective parameters can be satisfied. In this case, it is supposed that the region (space) V16 includes the plane Sp16, the plane Sp17 and the circumferential surface S16.
In this manner, the total film thickness L is determined, and by setting the film thicknesses of the respective layers within a region indicated by half-tone dot meshing so as to satisfy the ratio α and the ratio β, a laminated film that satisfies the conditions of the respective parameters can be manufactured.
In the above-mentioned description, a region that satisfies the conditions of respective parameters in a structure other than the structure having a specific total film thickness L is prepared as a region surrounded by a circumferential surface S with adjacent regions having specific total film thicknesses L being allowed to form two end faces thereof; however, the region that satisfies the conditions of the respective parameters is not limited to this example. For example, a region that satisfies the conditions of respective parameters in a case other than the case in which the total film thickness L has a specific value may be prepared as a region in which regions of adjacent specific film thicknesses L are overlapped with each other with respect to the values.
First, an explanation will be given by exemplifying a case in which the visible light-ray transmittance, the blue index and the red index are used as the parameters. In
As shown in
(80 nm<L<90 nm)
In the case when the total film thickness L exceeds 80 nm and is less than 90 nm, based upon regions that satisfy the conditions of the respective parameters shown in
α=0.012114 (8)
α=−3×10−5β2+0.0014β+0.0038 (10)
α=−2×10−5β2+0.0006β+0.0112 (11)
(90 nm<L<100 nm)
In the case when the total film thickness L exceeds 90 nm and is less than 100 nm, based upon regions that satisfy the conditions of the respective parameters shown in
α=−2×10−5β2+0.0006β+0.0112 (11)
α=0.010589 (12)
α=−0.0002β2+0.0055β+0.0057 (13)
α=−0.0002β2+0.0045β−0.0067 (14)
α=−4×10−5β2+0.001β+0.0099 (15)
(100 nm<L<120 nm)
In the case when the total film thickness L exceeds 100 nm and is less than 120 nm, based upon regions that satisfy the conditions of the respective parameters shown in
α=−4×10−5β2+0.001β+0.0099 (15)
α=0.009403 (16)
α=−0.0003β2+0.0074β+0.0033 (17)
α=−0.0014β2+0.0191β−0.0422 (18)
α=−9×10−5β2+0.0015β+0.0084 (19)
(120 nm<L<140 nm)
In the case when the total film thickness L exceeds 120 nm and is less than 140 nm, based upon regions that satisfy the conditions of the respective parameters shown in
α=0.007709 (20)
α=−0.0014β2+0.0136β−0.0027 (21)
β=10132α2−241.39α+4.747 (22)
α=−0.0001β2+0.002β+0.0074 (23)
(140 nm<L<160 nm)
In the case when the total film thickness L exceeds 140 nm and is less than 160 nm, based upon regions that satisfy the conditions of the respective parameters shown in
α=−0.0001β2+0.002β+0.0074 (23)
α=0.006523 (24)
α=−0.005β2+0.0273β−0.0145 (25)
α=0.0043β2−0.0332β+0.07 (26)
β=2.875 (27)
α=−0.0001β2+0.0025β+0.0062 (28)
(160 nm<L<180 nm)
In the case when the total film thickness L exceeds 160 nm and is less than 180 nm, based upon regions that satisfy the conditions of the respective parameters shown in
α=−0.0001β2+0.0025β+0.0062 (28)
α=0.005676 (29)
α=−0.0103β2+0.047β−0.0322 (30)
α=0.0093β2−0.0677β+0.1212 (31)
α=−0.0003β2+0.0036β+0.0046 (32)
First, an explanation will be given by exemplifying a case in which in addition to the visible light-ray transmittance, the blue index and the red index, a shading coefficient is also included as the parameters. In
As shown in
Additionally, in the case when the total film thickness L exceeds 80 nm and is less than 90 nm, even when regions that satisfy the conditions of the respective parameters shown in
(90 nm<L<100 nm)
In the case when the total film thickness L exceeds 90 nm and is less than 100 nm, based upon regions that satisfy the conditions of the respective parameters shown in
α=−2×10−5β2+0.0006β+0.0112 (11)
α=−0.0002β2+0.0045β−0.0067 (14)
α=−4×10−5β2+0.001β+0.0099 (15)
α=−1×10−5β2+0.0002β+0.0125 (35)
(100 nm<L<120 nm)
In the case when the total film thickness L exceeds 100 nm and is less than 120 nm, based upon regions that satisfy the conditions of the respective parameters shown in
α=−4×10−5β2+0.001β+0.0099 (15)
α=−0.0014β2+0.0191β−0.0422 (18)
α=−9×10−5β2+0.0015β+0.0084 (19)
α=−3×10−5β2+0.0004β+0.0113 (36)
(120 nm<L<140 nm)
In the case when the total film thickness L exceeds 120 nm and is less than 140 nm, based upon regions that satisfy the conditions of the respective parameters shown in
α=−9×10−5β2+0.0015β+0.0084 (19)
β=10132α2−241.39α+4.747 (22)
α=−0.0001β2+0.002β+0.0074 (23)
α=−7×10−5β2+0.0007β+0.0097 (37)
(140 nm<L<160 nm)
In the case when the total film thickness L exceeds 140 nm and is less than 160 nm, based upon regions that satisfy the conditions of the respective parameters shown in
α=−0.0001β2+0.002β+0.0074 (23)
α=0.0043β2−0.0332β+0.07 (26)
α=−0.0001β2+0.0025β+0.0062 (28)
β=2.875 (27)
α=−0.0001β2+0.0011β+0.0083 (38)
(160 nm<L<180 nm)
In the case when the total film thickness L exceeds 160 nm and is less than 180 nm, based upon regions that satisfy the conditions of the respective parameters shown in
α=−0.0001β2+0.0025β+0.0062 (28)
α=−0.0103β2+0.047β−0.0322 (30)
α=−0.0003β2+0.0036β+0.0046 (32)
α=−0.0002β2+0.0016β+0.0067 (39)
α=0.0093β2−0.0677β+0.1212 (31)
In accordance with the first embodiment, by determining a region that satisfies the conditions of respective parameters relative to the ratio α and ratio β that are determined in accordance with the film thicknesses of the respective layers of the reflection layer 3, the film thicknesses of the reflection layer 3 are set so as to allow the ratio α and ratio β to be included within this region so that a change in color tone can be suppressed.
The following description will discuss modified examples of the above-mentioned embodiment.
The second embodiment differs from the first embodiment in that in place of regions that are defined by approximation curves, the regions that are required to be satisfied by the respective parameters are determined by using regions that are defined by approximation straight lines. The approximation straight lines are obtained from the approximation curves found in the first embodiment.
First, referring to
As shown in
From an approximation curve indicated by formula (21), an approximation straight line indicated by formula (21a) can be found, for example, in the following manner. For example, coordinates of intersections A and B between a straight line (24) that intersects with an approximation curve indicated by formula (21) and an approximation curve (23) are found. Next, a straight line that passes through the coordinates of these two intersections A and B is found, and this straight line is defined as an approximation straight line (21a).
From the approximation curve indicated by formula (23), the approximation straight line indicated by formula (23a) is found, for example, in the following manner. First, coordinates of intersections B and C between a curved line (21) that intersects with an approximation curved line indicated by formula (23) and an approximation curved line (22) are found. Next, a straight line that passes through the coordinates of these two intersections B and C is found, and this straight line is defined as an approximation straight line (23a).
From an approximation curve indicated by formula (22), an approximation straight line indicated by formula (22a) can be found, for example, in the following manner. First, coordinates of intersections C and D between a curved line (23) that intersects with an approximation curved line indicated by formula (22) and a straight line (24) are found. Next, a straight line 22m that passes through the coordinates of these two intersections C and D is found. Next, a straight line (tangential line) that is in parallel with this straight line 22m and is also inscribed in the approximation curve 22 is found, and this straight line is defined as an approximation straight line (22a).
First, with respect to a case in which the visible light-ray transmittance, the blue index and the red index are used as parameters, an explanation will be given on regions satisfying the conditions of these parameters for each of the total film thicknesses L of the reflection layer 3.
From formulas (5) to (7) of the approximation curves that define the region R1 (
ab:α=0.004236β+0.007158 (5a)
bd:α=0.000172β+0.012238 (7a)
dc:α=0.000317β+0.009179 (6a)
ca:α=0.012114 (8)
In this case, a region (hereinafter, referred to as “first region R1a”), which is defined by the approximation straight lines indicated by these formulas (5a) to (7a) and the straight line indicated by formula (8), corresponds to a region satisfying the conditions of the respective parameters of the visible light-ray transmittance, the blue index and the red index. That is, by allowing the ratio α and ratio β to be included in the first region R1a, the conditions of the respective parameters can be satisfied. In this case, it is supposed that the first region R1a includes the approximation straight lines indicated by formulas (5a) to (7a) and the straight line indicated by formula (8). Additionally, in the following description, of the plane of L=80 nm, a portion defined by the first region R1a is referred to as “first plane Sp1a” on demand.
ab:α=0.003388β+0.008895 (9a)
bd:α=0.000371β+0.011309 (11a)
dc:α=0.000934β+0.005454 (10a)
ca:α=0.010589 (12)
A region (hereinafter, referred to as “second region R2a”), which is defined by the approximation straight lines indicated by these formulas (9a) to (11a) and the straight line indicated by formula (12), corresponds to a region satisfying the conditions of the respective parameters of the visible light-ray transmittance, the blue index and the red index. That is, by allowing the ratio α and ratio β to be included in the second region R2a, the above-mentioned conditions of the respective parameters can be satisfied. In this case, it is supposed that the second region R2a includes the approximation straight lines indicated by formulas (9a) to (11a) and the straight line indicated by formula (12). Additionally, in the following description, of the plane of L=90 nm, a portion defined by the second region R2a is referred to as “second plane Sp2a” on demand.
ab:α=0.005083β+0.005845 (13a)
bc:α=0.000616β+0.010312 (15a)
cd:α=0.00234β−0.00089 (14a)
da:α=0.009403 (16)
A region (hereinafter, referred to as “third region R3a”), which is defined by the approximation straight lines indicated by these formulas (13a) to (15a) and the straight line indicated by formula (16), corresponds to a region satisfying the conditions of the respective parameters of the visible light-ray transmittance, the blue index and the red index. That is, by allowing the ratio α and ratio β to be included in the third region R3a, the above-mentioned conditions of the respective parameters can be satisfied. In this case, it is supposed that the third region R3a includes the approximation straight lines indicated by formulas (13a) to (15a) and the straight line indicated by formula (16). Additionally, in the following description, of the plane of L=100 nm, a portion defined by the third region R3a is referred to as “third plane Sp3a” on demand.
ab:α=0.006777β+0.003643 (17a)
bc:α=0.001062β+0.008786 (19a)
cd:α=0.008601β−0.02326 (18a)
da:α=0.007709 (20)
A region (hereinafter, referred to as “fourth region R4a”), which is defined by the approximation straight lines indicated by these formulas (17a) to (19a) and the straight line indicated by formula (20), corresponds to a region satisfying the conditions of the respective parameters of the visible light-ray transmittance, the blue index and the red index. That is, by allowing the ratio α and ratio β to be included in the fourth region R4a, the above-mentioned conditions of the respective parameters can be satisfied. In this case, it is supposed that the fourth region R4a includes the approximation straight lines indicated by formulas (17a) to (19a) and the straight line indicated by formula (20). Additionally, in the following description, of the plane of L=120 nm, a portion defined by the fourth region R4a is referred to as “fourth plane Sp4a” on demand.
ab:α=0.010843β−0.00161 (21a)
bc:α=0.001603β+0.00763 (23a)
cd:α=−0.01414β+0.056433 (22a)
da:α=0.006523 (24)
A region (hereinafter, referred to as “fifth region R5a”), which is defined by the approximation straight lines indicated by these formulas (21a) to (23a) and the straight line indicated by formula (24), corresponds to a region satisfying the conditions of the respective parameters of the visible light-ray transmittance, the blue index and the red index. That is, by allowing the ratio α and ratio β to be included in the fifth region R5a, the above-mentioned conditions of the respective parameters can be satisfied. In this case, it is supposed that the fifth region R5a includes the approximation straight lines indicated by formulas (21a) to (23a) and the straight line indicated by formula (24). Additionally, in the following description, of the plane of L=140 nm, a portion defined by the fifth region R5a is referred to as “fifth plane Sp5a” on demand.
ab:α=0.019766β−0.01211 (25a)
bc:α=0.002186β+0.006345 (28a)
cd:α=−0.00691β+0.029828 (26a)
da:α=0.005676 (29)
A region (hereinafter, referred to as “sixth region R6a”), which is defined by the approximation straight lines indicated by these formulas (25a), (26a) and (28a) and, the straight line indicated by formula (29), corresponds to a region satisfying the conditions of the respective parameters of the visible light-ray transmittance, the blue index and the red index. That is, by allowing the ratio α and ratio β to be included in the sixth region R6a, the above-mentioned conditions of the respective parameters can be satisfied. In this case, it is supposed that the sixth region R6a includes the approximation straight lines indicated by formulas (25a), (26a) and (28a) and the straight line indicated by formula (29). Additionally, in the following description, of the plane of L=160 nm, a portion defined by the sixth region R6a is referred to as “sixth plane Sp6a” on demand.
As shown in
The following description will discuss a case in which by using the visible light-ray transmittance, the blue index and the red index as the parameters, the total film thickness L is set to a value between predetermined total film thicknesses L (=80 nm, 90 nm, . . . , 160 nm) so as to satisfy the conditions of the parameters.
(80 nm<L<90 nm)
Based upon the positions of the respective apexes in the regions that satisfy the conditions of the respective parameters shown in
aa:(β−0.5)/0.67=(α=0.01059)/0.001524=(L−90)/(−10) (41)
bb:(β−0.8)/0.45=(α=0.01161)/0.000847=(L−90)/(−10) (42)
dd:(β−10.4)/10.6=(α−0.01516)/0.0006776=(L−90)/(−10) (43)
cc:(β−5.5)/3.75=(α−0.01059)/0.0015247=(L−90)/(−10) (44)
In the case when the total film thickness L is represented by 80 nm<L<90 nm, a region (space) V1a that is surrounded by the following four surfaces forms a region that satisfies the conditions of the respective parameters. That is, by allowing the ratio α and ratio β to be included in the region (space) V1a, the conditions of the respective parameters can be satisfied.
Surface in which the approximation straight lines of formula (41) and formula (42) form two opposed sides . . . s1
Surface in which the approximation straight lines of formula (42) and formula (43) form two opposed sides . . . s2
Surface in which the approximation straight lines of formula (43) and formula (44) form two opposed sides . . . s3
Surface in which the approximation straight lines of formula (44) and formula (41) form two opposed sides . . . s4
In this case, it is supposed that the region (space) V1a includes the approximation straight lines of formulas (41) to (44) themselves.
The surface in which the approximation straight lines of formula (41) and formula (42) form two opposed sides corresponds to a surface formed in the following manner. That is, the surface is formed by moving a line segment ab in an L-axis direction (direction in which the total film thickness L increases), while its positional relationship is kept in parallel with the first plane Sp1a, with its two end points being shifted along a line segment aa (line segment represented by formula (41)) and a line segment bb (line segment represented by formula (42)). In this case, the moving range of the line segment ab is in a range of 80 nm<L<90 nm.
The surface in which the approximation straight lines of formula (42) and formula (43) form two opposed sides corresponds to a surface formed in the following manner. That is, the surface is formed by moving a line segment bd in the L-axis direction (direction in which the total film thickness L increases), while its positional relationship is kept in parallel with the first plane Sp1a, with its two end points being shifted along a line segment bb (line segment represented by formula (42)) and a line segment dd (line segment represented by formula (43)). In this case, the moving range of the line segment bd is in a range of 80 nm<L<90 nm.
The surface in which the approximation straight lines of formula (43) and formula (44) form two opposed sides corresponds to a surface formed in the following manner. That is, the surface is formed by moving a line segment dc in the L-axis direction (direction in which the total film thickness L increases), while its positional relationship is kept in parallel with the first plane Sp1a, with its two end points being shifted along a line segment dd (line segment represented by formula (43)) and a line segment cc (line segment represented by formula (44)). In this case, the moving range of the line segment dc is in a range of 80 nm<L<90 nm.
The surface in which the approximation straight lines of formula (44) and formula (41) form two opposed sides corresponds to a surface formed in the following manner. That is, the surface is formed by moving a line segment ca in the L-axis direction (direction in which the total film thickness L increases), while its positional relationship is kept in parallel with the first plane Sp1a, with its two end points being shifted along a line segment cc (line segment represented by formula (44)) and a line segment aa (line segment represented by formula (41)). In this case, the moving range of the line segment ca is in a range of 80 nm<L<90 nm.
(90 nm<L<100 nm)
Based upon the positions of the respective apexes in the regions that satisfy the conditions of the respective parameters shown in
aa:(β−0.7)/(−0.2)=(α−0.0094)/0.001185=(L−100)/(−10) (51)
bb:(β−1)/(−0.2)=(α−0.01093)/0.0006776=(L−100)/(−10) (52)
dc:(β−6.5)/3.9=(α−0.01432)/0.000847=(L−100)/(−10) (53)
cd:(β−4.4)/1.1=(α−0.0094)/0.001186=(L−100)/(−10) (54)
In the case when the total film thickness L is represented by 90 nm<L<100 nm, a region (space) V2a that is surrounded by the following four surfaces forms a region that satisfies the conditions of the respective parameters. That is, by allowing the ratio α and ratio β to be included in the region (space) V2a, the conditions of the respective parameters can be satisfied.
Surface in which the approximation straight lines of formula (51) and formula (52) form two opposed sides . . . s1
Surface in which the approximation straight lines of formula (52) and formula (53) form two opposed sides . . . s2
Surface in which the approximation straight lines of formula (53) and formula (54) form two opposed sides . . . s3
Surface in which the approximation straight lines of formula (54) and formula (51) form two opposed sides . . . s4
In this case, it is supposed that the region (space) V2a includes the approximation straight lines of formulas (51) to (54) themselves.
The surface in which the approximation straight lines of formula (51) and formula (52) form two opposed sides corresponds to a surface formed in the following manner. That is, the surface is formed by moving a line segment ab in an L-axis direction (direction in which the total film thickness L increases), while its positional relationship is kept in parallel with the second plane Sp2a, with its two end points being shifted along a line segment aa (line segment represented by formula (51)) and a line segment bb (line segment represented by formula (52)). In this case, the moving range of the line segment ab is in a range of 90 nm<L<100 nm.
The surface in which the approximation straight lines of formula (52) and formula (53) form two opposed sides corresponds to a surface formed in the following manner. That is, the surface is formed by moving a line segment bd in the L-axis direction (direction in which the total film thickness L increases), while its positional relationship is kept in parallel with the second plane Sp2a, with its two end points being shifted along a line segment bb (line segment represented by formula (52)) and a line segment dc (line segment represented by formula (53)). In this case, the moving range of the line segment bd is in a range of 90 nm<L<100 nm.
The surface in which the approximation straight lines of formula (53) and formula (54) form two opposed sides corresponds to a surface formed in the following manner. That is, the surface is formed by moving a line segment dc in the L-axis direction (direction in which the total film thickness L increases), while its positional relationship is kept in parallel with the second plane Sp2a, with its two end points being shifted along a line segment dc (line segment represented by formula (53)) and a line segment cd (line segment represented by formula (54)). In this case, the moving range of the line segment dc is in a range of 90 nm<L<100 nm.
The surface in which the approximation straight lines of formula (54) and formula (51) form two opposed sides corresponds to a surface formed in the following manner. That is, the surface is formed by moving a line segment ca in the L-axis direction (direction in which the total film thickness L increases), while its positional relationship is kept in parallel with the second plane Sp2a, with its two end points being shifted along a line segment cd (line segment represented by formula (54)) and a line segment aa (line segment represented by formula (51)). In this case, the moving range of the line segment ca is in a range of 90 nm<L<100 nm.
(100 nm<L<120 nm)
Based upon the positions of the respective apexes in the regions that satisfy the conditions of the respective parameters shown in
aa:(β−0.6)/0.1=(α−0.00771)/0.001694=(L−120)/(−20) (61)
bb:(β−0.9)/0.1=(α−0.00974)/0.001185=(L−120)/(−20) (62)
cc:(β−4.25)/2.25=(α−0.0133)/0.0010165=(L−120)/(−20) (63)
dd:(β−3.6)/0.8=(α−0.00771)/0.0016942=(L−120)/(−20) (64)
In the case when the total film thickness L is represented by 100 nm<L<120 nm, a region (space) V3a that is surrounded by the following four surfaces forms a region that satisfies the conditions of the respective parameters. That is, by allowing the ratio α and ratio β to be included in the region (space) V3a, the conditions of the respective parameters can be satisfied.
Surface in which the approximation straight lines of formula (61) and formula (62) form two opposed sides . . . s1
Surface in which the approximation straight lines of formula (62) and formula (63) form two opposed sides . . . s2
Surface in which the approximation straight lines of formula (63) and formula (64) form two opposed sides . . . s3
Surface in which the approximation straight lines of formula (64) and formula (61) form two opposed sides . . . s4
In this case, it is supposed that the region (space) V3a includes the approximation straight lines of formulas (61) to (64) themselves.
The surface in which the approximation straight lines of formula (61) and formula (62) form two opposed sides corresponds to a surface formed in the following manner. That is, the surface is formed by moving a line segment ab in an L-axis direction (direction in which the total film thickness L increases), while its positional relationship is kept in parallel with the third plane Sp3a, with its two end points being shifted along a line segment aa (line segment represented by formula (61)) and a line segment bb (line segment represented by formula (62)). In this case, the moving range of the line segment ab is in a range of 100 nm<L<120 nm.
The surface in which the approximation straight lines of formula (62) and formula (63) form two opposed sides corresponds to a surface formed in the following manner. That is, the surface is formed by moving a line segment be in the L-axis direction (direction in which the total film thickness L increases), while its positional relationship is kept in parallel with the third plane Sp3a, with its two end points being shifted along a line segment bb (line segment represented by formula (62)) and a line segment cc (line segment represented by formula (63)). In this case, the moving range of the line segment bc is in a range of 100 nm<L<120 nm.
The surface in which the approximation straight lines of formula (63) and formula (64) form two opposed sides corresponds to a surface formed in the following manner. That is, the surface is formed by moving a line segment cd in the L-axis direction (direction in which the total film thickness L increases), while its positional relationship is kept in parallel with the third plane Sp3a, with its two end points being shifted along a line segment cc (line segment represented by formula (63)) and a line segment dd (line segment represented by formula (64)). In this case, the moving range of the line segment cd is in a range of 100 nm<L<120 nm.
The surface in which the approximation straight lines of formula (64) and formula (61) form two opposed sides corresponds to a surface formed in the following manner. That is, the surface is formed by moving a line segment da in the L-axis direction (direction in which the total film thickness L increases), while its positional relationship is kept in parallel with the third plane Sp3a, with its two end points being shifted along a line segment dd (line segment represented by formula (64)) and a line segment aa (line segment represented by formula (61)). In this case, the moving range of the line segment da is in a range of 100 nm<L<120 nm.
(120 nm<L<140 nm)
Based upon the positions of the respective apexes in the regions that satisfy the conditions of the respective parameters shown in
aa:(β−0.75)/(−0.15)=(α−0.00652)/0.001185=(L−140)/(−20) (71)
bb:(β−1)/(−0.1)=(α−0.00923)/0.0005082=(L−140)/(−20) (72)
cc:(β−3.1)/1.15=(α−0.0216)/0.0006994=(L−140)/(−20) (73)
dd:(β−3.53)/0.07=(α−0.00652)/0.0011859=(L−140)/(−20) (74)
In the case when the total film thickness L is represented by 120 nm<L<140 nm, a region (space) V4a that is surrounded by the following four surfaces forms a region that satisfies the conditions of the respective parameters. That is, by allowing the ratio α and ratio β to be included in the region (space) V4a, the conditions of the respective parameters can be satisfied.
Surface in which the approximation straight lines of formula (71) and formula (72) form two opposed sides . . . s1
Surface in which the approximation straight lines of formula (72) and formula (73) form two opposed sides . . . s2
Surface in which the approximation straight lines of formula (73) and formula (74) form two opposed sides . . . s3
Surface in which the approximation straight lines of formula (74) and formula (71) form two opposed sides . . . s4
In this case, it is supposed that the region (space) V4a includes the approximation straight lines of formulas (71) to (74) themselves.
The surface in which the approximation straight lines of formula (71) and formula (72) form two opposed sides corresponds to a surface formed in the following manner. That is, the surface is formed by moving a line segment ab in an L-axis direction (direction in which the total film thickness L increases), while its positional relationship is kept in parallel with the fourth plane Sp4a, with its two end points being shifted along a line segment aa (line segment represented by formula (71)) and a line segment bb (line segment represented by formula (72)). In this case, the moving range of the line segment ab is in a range of 120 nm<L<140 nm.
The surface in which the approximation straight lines of formula (72) and formula (73) form two opposed sides corresponds to a surface formed in the following manner. That is, the surface is formed by moving a line segment be in the L-axis direction (direction in which the total film thickness L increases), while its positional relationship is kept in parallel with the fourth plane Sp4a, with its two end points being shifted along a line segment bb (line segment represented by formula (72)) and a line segment cc (line segment represented by formula (73)). In this case, the moving range of the line segment bc is in a range of 120 nm<L<140 nm.
The surface in which the approximation straight lines of formula (73) and formula (74) form two opposed sides corresponds to a surface formed in the following manner. That is, the surface is formed by moving a line segment cd in the L-axis direction (direction in which the total film thickness L increases), while its positional relationship is kept in parallel with the fourth plane Sp4a, with its two end points being shifted along a line segment cc (line segment represented by formula (73)) and a line segment dd (line segment represented by formula (74)). In this case, the moving range of the line segment cd is in a range of 120 nm<L<140 nm.
The surface in which the approximation straight lines of formula (74) and formula (71) form two opposed sides corresponds to a surface formed in the following manner. That is, the surface is formed by moving a line segment da in the L-axis direction (direction in which the total film thickness L increases), while its positional relationship is kept in parallel with the fourth plane Sp4a, with its two end points being shifted along a line segment dd (line segment represented by formula (74)) and a line segment aa (line segment represented by formula (71)). In this case, the moving range of the line segment da is in a range of 120 nm<L<140 nm.
(140 nm<L<160 nm)
Based upon the positions of the respective apexes in the regions that satisfy the conditions of the respective parameters shown in
aa:(β−0.9)/(−0.15)=(α−0.00568)/0.0008471=(L−160)/(−20) (81)
bb:(β−1.05)/(−0.05)=(α−0.00864)/0.00059297=(L−160)/(−20) (82)
cc:(β−2.582)/0.518=(α−0.01199)/0.00061=(L−160)/(−20) (83)
dd:(β−3.496)/0.034=(α−0.00568)/0.0008471=(L−160)/(−20) (84)
In the case when the total film thickness L is represented by 140 nm<L<160 nm, a region (space) V5a that is surrounded by the following four surfaces forms a region that satisfies the conditions of the respective parameters. That is, by allowing the ratio α and ratio β to be included in the region (space) V5a, the conditions of the respective parameters can be satisfied.
Surface in which the approximation straight lines of formula (81) and formula (82) form two opposed sides . . . s1
Surface in which the approximation straight lines of formula (82) and formula (83) form two opposed sides . . . s2
Surface in which the approximation straight lines of formula (83) and formula (84) form two opposed sides . . . s3
Surface in which the approximation straight lines of formula (84) and formula (81) form two opposed sides . . . s4
In this case, it is supposed that the region (space) V5a includes the approximation straight lines of formulas (81) to (84) themselves.
The surface in which the approximation straight lines of formula (81) and formula (82) form two opposed sides corresponds to a surface formed in the following manner. That is, the surface is formed by moving a line segment ab in an L-axis direction (direction in which the total film thickness L increases), while its positional relationship is kept in parallel with the fifth plane Sp5a, with its two end points being shifted along a line segment aa (line segment represented by formula (81)) and a line segment bb (line segment represented by formula (82)). In this case, the moving range of the line segment ab is in a range of 140 nm<L<160 nm.
The surface in which the approximation straight lines of formula (82) and formula (83) form two opposed sides corresponds to a surface formed in the following manner. That is, the surface is formed by moving a line segment bc in the L-axis direction (direction in which the total film thickness L increases), while its positional relationship is kept in parallel with the fifth plane Sp5a, with its two end points being shifted along a line segment bb (line segment represented by formula (82)) and a line segment cc (line segment represented by formula (83)). In this case, the moving range of the line segment bc is in a range of 140 nm<L<160 nm.
The surface in which the approximation straight lines of formula (83) and formula (84) form two opposed sides corresponds to a surface formed in the following manner. That is, the surface is formed by moving a line segment cd in the L-axis direction (direction in which the total film thickness L increases), while its positional relationship is kept in parallel with the fifth plane Sp5a, with its two end points being shifted along a line segment cc (line segment represented by formula (83)) and a line segment dd (line segment represented by formula (84)). In this case, the moving range of the line segment cd is in a range of 140 nm<L<160 nm.
The surface in which the approximation straight lines of formula (84) and formula (81) form two opposed sides corresponds to a surface formed in the following manner. That is, the surface is formed by moving a line segment da in the L-axis direction (direction in which the total film thickness L increases), while its positional relationship is kept in parallel with the fifth plane Sp5a, with its two end points being shifted along a line segment dd (line segment represented by formula (84)) and a line segment aa (line segment represented by formula (81)). In this case, the moving range of the line segment da is in a range of 140 nm<L<160 nm.
Therefore, a region that satisfies the conditions of the parameters of the visible light-ray transmittance, the blue index and the red index is determined in the following manner for each of ranges of the respective total film thicknesses L.
(80 nm≦L≦90 nm)
In the case when the total film thickness L is represented by 80 nm≦L≦90 nm, a region (space) V1b, which is surrounded by the following six planes, forms a region that satisfies the conditions of the respective parameters. That is, by allowing the ratio α and ratio β to be included in the region (space) V1b, the conditions of the respective parameters can be satisfied.
Plane in which the approximation straight lines and straight line of formula (5a), formula (7a), formula (6a) and formula (8) form four sides . . . Sp1a
Plane in which the approximation straight lines and straight line of formula (9a), formula (11a), formula (10a) and formula (12) form four sides . . . Sp2a
Surface in which the approximation straight lines of formula (5a), formula (9a), formula (41) and formula (42) form four sides . . . s1a
Surface in which the approximation straight lines of formula (7a), formula (11a), formula (42) and formula (43) form four sides . . . s2a
Surface in which the approximation straight lines of formula (6a), formula (10a), formula (43) and formula (44) form four sides . . . s3a
Surface in which the approximation straight lines of formula (8), formula (12), formula (44) and formula (41) form four sides . . . s4a
In this case, it is supposed that the region (space) V1b includes the respective approximation straight lines themselves that define the respective surfaces. Moreover, the surfaces s1a to s4a are surfaces that are formed in the same manner as in surfaces s1 to s4 within the range of 80 nm<L<90 nm in the total film thickness L, except that the moving ranges of the respective line segments are set within the range of 80 nm≦L≦90 nm.
(90 nm≦L≦100 nm)
In the case when the total film thickness L is represented by 90 nm≦L≦100 nm, a region (space) V2b, which is surrounded by the following six planes, forms a region that satisfies the conditions of the respective parameters. That is, by allowing the ratio α and ratio β to be included in the region (space) V2b, the conditions of the respective parameters can be satisfied.
Plane in which the approximation straight lines and straight line of formula (9a), formula (11a), formula (10a) and formula (12) form four sides . . . Sp2a
Plane in which the approximation straight lines and straight line of formula (13a), formula (15a), formula (14a) and formula (16) form four sides . . . Sp3a
Surface in which the approximation straight lines of formula (9a), formula (13a), formula (51) and formula (52) form four sides . . . s1a
Surface in which the approximation straight lines of formula (11a), formula (15a), formula (52) and formula (53) form four sides . . . s2a
Surface in which the approximation straight lines of formula (10a), formula (14a), formula (53) and formula (54) form four sides . . . s3a
Surface in which the approximation straight lines of formula (12), formula (16), formula (54) and formula (51) form four sides . . . s4a
In this case, it is supposed that the region (space) V2b includes the respective approximation straight lines and straight lines themselves that define the respective surfaces. Moreover, the surfaces s1a to s4a are surfaces that are formed in the same manner as in surfaces s1 to s4 within the range of 90 nm<L<100 nm in the total film thickness L, except that the moving ranges of the respective line segments are set within the range of 90 nm≦L≦100 nm.
(100 nm≦L≦120 nm)
In the case when the total film thickness L is represented by 100 nm≦L≦120 nm, a region (space) V3b, which is surrounded by the following six planes, forms a region that satisfies the conditions of the respective parameters. That is, by allowing the ratio α and ratio β to be included in the region (space) V3b, the conditions of the respective parameters can be satisfied.
Plane in which the approximation straight lines and straight line of formula (13a), formula (15a), formula (14a) and formula (16) form four sides . . . Sp3a
Plane in which the approximation straight lines and straight line of formula (17a), formula (19a), formula (18a) and formula (20) form four sides . . . Sp4a
Surface in which the approximation straight lines of formula (13a), formula (17a), formula (61) and formula (62) form four sides . . . s1a
Surface in which the approximation straight lines of formula (15a), formula (19a), formula (62) and formula (63) form four sides . . . s2a
Surface in which the approximation straight lines of formula (14a), formula (18a), formula (63) and formula (64) form four sides . . . s3a
Surface in which the approximation straight lines of formula (16), formula (20), formula (64) and formula (61) form four sides . . . s4a
In this case, it is supposed that the region (space) V3b includes the respective approximation straight lines and straight lines themselves that define the above-mentioned respective surfaces. Moreover, the surfaces s1a to s4a are surfaces that are formed in the same manner as in surfaces s1 to s4 within the range of 100 nm<L<120 nm in the total film thickness L, except that the moving ranges of the respective line segments are set within the range of 100 nm≦L≦120 nm.
(120 nm≦L≦140 nm)
In the case when the total film thickness L is represented by 120 nm≦L≦140 nm, a region (space) V4b, which is surrounded by the following six planes, forms a region that satisfies the conditions of the respective parameters. That is, by allowing the ratio α and ratio β to be included in the region (space) V4b, the conditions of the respective parameters can be satisfied.
Plane in which the approximation straight lines and straight line of formula (17a), formula (19a), formula (18a) and formula (20) form four sides . . . Sp4a
Plane in which the approximation straight lines and straight line of formula (21a), formula (23a), formula (22a) and formula (24) form four sides . . . Sp5a
Surface in which the approximation straight lines of formula (17a), formula (21a), formula (71) and formula (72) form four sides . . . s1a
Surface in which the approximation straight lines of formula (19a), formula (23a), formula (72) and formula (73) form four sides . . . s2a
Surface in which the approximation straight lines of formula (18a), formula (22a), formula (73) and formula (74) form four sides . . . s3a
Surface in which the approximation straight lines of formula (20), formula (24), formula (74) and formula (71) form four sides . . . s4a
In this case, it is supposed that the region (space) V4b includes the respective approximation straight lines and straight lines themselves that define the above-mentioned respective surfaces. Moreover, the surfaces s1a to s4a are surfaces that are formed in the same manner as in surfaces s1 to s4 within the range of 120 nm<L<140 nm in the total film thickness L, except that the moving ranges of the respective line segments are set within the range of 120 nm≦L≦140 nm.
(140 nm≦L≦160 nm)
In the case when the total film thickness L is represented by 140 nm≦L≦160 nm, a region (space) V5b, which is surrounded by the following six planes, forms a region that satisfies the conditions of the respective parameters. That is, by allowing the ratio α and ratio β to be included in the region (space) V5b, the conditions of the respective parameters can be satisfied.
Plane in which the approximation straight lines and straight line of formula (21a), formula (23a), formula (22a) and formula (24) form four sides . . . Sp5a
Plane in which the approximation straight lines and straight line of formula (25a), formula (28a), formula (26a) and formula (29) form four sides . . . Sp6a
Surface in which the approximation straight lines of formula (21a), formula (25a), formula (81) and formula (82) form four sides . . . s1a
Surface in which the approximation straight lines of formula (23a), formula (28a), formula (82) and formula (83) form four sides . . . s2a
Surface in which the approximation straight lines of formula (22a), formula (26a), formula (83) and formula (84) form four sides . . . s3a
Surface in which the approximation straight lines of formula (24), formula (29), formula (84) and formula (81) form four sides . . . s4a
In this case, it is supposed that the region (space) V5b includes the respective approximation straight lines and straight lines themselves that define the above-mentioned respective surfaces. Moreover, the surfaces s1a to s4a are surfaces that are formed in the same manner as in surfaces s1 to s4 within the range of 140 nm<L<160 nm in the total film thickness L, except that the moving ranges of the respective line segments are set within the range of 140 nm≦L≦160 nm.
Next, with respect to a case in which in addition to the above-mentioned visible light-ray transmittance, blue index and red index, the shading coefficient is also used as parameters, an explanation will be given thereto for each of the total film thicknesses L of the reflection layer 3.
ed:α=2.95×10−5β+0.01522 (7b)
df:α=0.000199β+0.011655 (6b)
ef:α=−1.2×10−5β+0.015739 (34b)
A region (hereinafter, referred to as “first region R11a”), which is defined by the approximation straight lines indicated by these formulas (6b), (7b) and (34b), corresponds to a region satisfying the conditions of the respective parameters of the visible light-ray transmittance, the blue index, the red index and the shading coefficient. That is, by allowing the ratio α and ratio β to be included in the first region R11a, the above-mentioned conditions of the respective parameters can be satisfied. In this case, it is supposed that the first region R11a includes the approximation straight lines indicated by formulas (6b), (7b) and (34b). Additionally, in the following description, of the plane of L=80 nm, a portion defined by the first region R11a is referred to as “first plane Sp11a” on demand.
ed:α=0.000308β+0.01196 (11b)
df:α=0.000791β+0.006941 (10b)
ef:α=0.000127β+0.012846 (35b)
A region (hereinafter, referred to as “second region R12a”), which is defined by the approximation straight lines indicated by these formulas (10b), (11b) and (35b), corresponds to a region satisfying the conditions of the respective parameters of the visible light-ray transmittance, the blue index, the red index and the shading coefficient. That is, by allowing the ratio α and ratio β to be included in the second region R12a, the above-mentioned conditions of the respective parameters can be satisfied. In this case, it is supposed that the second region R12a includes the approximation straight lines indicated by formulas (10b), (11b) and (35b). Additionally, in the following description, of the plane of L=90 nm, a portion defined by the second region R12a is referred to as “second plane Sp12a” on demand.
ec:α=0.000572β+0.010596 (15b)
cf:α=0.00242β−0.00142 (14b)
ef:α=0.000141β+0.011803 (36b)
A region (hereinafter, referred to as “third region R13a”), which is defined by the approximation straight lines indicated by these formulas (14b), (15b) and (36b), corresponds to a region satisfying the conditions of the respective parameters of the visible light-ray transmittance, the blue index, the red index and the shading coefficient. That is, by allowing the ratio α and ratio β to be included in the third region R13a, the above-mentioned conditions of the respective parameters can be satisfied. In this case, it is supposed that the third region R13a includes the approximation straight lines indicated by formulas (14b), (15b) and (36b). Additionally, in the following description, of the plane of L=100 nm, a portion defined by the third region R13a is referred to as “third plane Sp13a” on demand.
ec:α=0.000997β+0.009064 (19b)
cf:α=0.007454β−0.01838 (18b)
ef:α=0.000295β+0.010257 (37b)
A region (hereinafter, referred to as “fourth region R14a”), which is defined by the approximation straight lines indicated by these formulas (18b), (19b) and (37b), corresponds to a region satisfying the conditions of the respective parameters of the visible light-ray transmittance, the blue index, the red index and the shading coefficient. That is, by allowing the ratio α and ratio β to be included in the fourth region R14a, the above-mentioned conditions of the respective parameters can be satisfied. In this case, it is supposed that the fourth region R14a includes the approximation straight lines indicated by formulas (18b), (19b) and (37b). Additionally, in the following description, of the plane of L=120 nm, a portion defined by the fourth region R14a is referred to as “fourth plane Sp14a” on demand.
ec:α=0.001599β+0.007644 (23b)
cf:α=−0.0109β+0.0464 (22b)
ef:α=0.000462β+0.008895 (38b)
A region (hereinafter, referred to as “fifth region R15a”), which is defined by the approximation straight lines indicated by these formulas (22b), (23b) and (38b), corresponds to a region satisfying the conditions of the respective parameters of the visible light-ray transmittance, the blue index, the red index and the shading coefficient. That is, by allowing the ratio α and ratio β to be included in the fifth region R15a, the above-mentioned conditions of the respective parameters can be satisfied. In this case, it is supposed that the fifth region R15a includes the approximation straight lines indicated by formulas (22b), (23b) and (38b). Additionally, in the following description, of the plane of L=140 nm, a portion defined by the fifth region R15a is referred to as “fifth plane Sp15a” on demand.
ec:α=0.002463β+0.005631 (28b)
cf:α=−0.00693β+0.029895 (26b)
ef:α=0.000773β+0.007406 (39b)
A region (hereinafter, referred to as “sixth region R16a”), which is defined by the approximation straight lines indicated by these formulas (26b), (28b) and (39b), corresponds to a region satisfying the conditions of the respective parameters of the visible light-ray transmittance, the blue index, the red index and the shading coefficient. That is, by allowing the ratio α and ratio β to be included in the sixth region R16a, the above-mentioned conditions of the respective parameters can be satisfied. In this case, it is supposed that the sixth region R16a includes the approximation straight lines indicated by formulas (26b), (28b) and (39b). Additionally, in the following description, of the plane of L=160 nm, a portion defined by the sixth region R16a is referred to as “sixth plane Sp16a” on demand.
As shown in
The following description will discuss a case in which by using the visible light-ray transmittance, the blue index, the red index and the shading coefficient as the parameters, the total film thickness L is set to a value between predetermined total film thicknesses L (=80 nm, 90 nm, . . . , 160 nm) so as to satisfy the conditions of the parameters.
(80 nm<L<90 nm)
Based upon the positions of the respective apexes in the regions that satisfy the conditions of the respective parameters shown in
dd:(α−10.4)/10.6=(β−0.01516)/0.0006776=(L−90)/(−10) (43)
ee:(α−4.9)/7.5=(β−0.01347)/0.00211775=(L−90)/(−10) (45)
ff:(α−8.9)/10.4=(β−0.01398)/0.0015247=(L−90)/(−10) (46)
In the case when the total film thickness L is represented by 80 nm<L<90 nm, a region (space) V11a that is surrounded by the following three surfaces forms a region that satisfies the conditions of the respective parameters. That is, by allowing the ratio α and ratio β to be included in the region (space) V11a, the conditions of the respective parameters can be satisfied.
Surface in which the approximation straight lines of formula (43) and formula (45) form two opposed sides . . . s5
Surface in which the approximation straight lines of formula (45) and formula (46) form two opposed sides . . . s6
Surface in which the approximation straight lines of formula (46) and formula (43) form two opposed sides . . . s7
In this case, it is supposed that the region (space) V11a includes the approximation straight lines of formulas (43), (45) and (46) themselves.
The surface in which the approximation straight lines of formula (43) and formula (45) form two opposed sides corresponds to a surface formed in the following manner. That is, the surface is formed by moving a line segment de in an L-axis direction (direction in which the total film thickness L increases), while its positional relationship is kept in parallel with the first plane Sp11a, with its two end points being shifted along a line segment dd (line segment represented by formula (43)) and a line segment ee (line segment represented by formula (45)). In this case, the moving range of the line segment de is in a range of 80 nm<L<90 nm.
The surface in which the approximation straight lines of formula (45) and formula (46) form two opposed sides corresponds to a surface formed in the following manner. That is, the surface is formed by moving a line segment ef in the L-axis direction (direction in which the total film thickness L increases), while its positional relationship is kept in parallel with the first plane Sp11a, with its two end points being shifted along a line segment ee (line segment represented by formula (45)) and a line segment ff (line segment represented by formula (46)). In this case, the moving range of the line segment ef is in a range of 80 nm<L<90 nm.
The surface in which the approximation straight lines of formula (46) and formula (43) form two opposed sides corresponds to a surface formed in the following manner. That is, the surface is formed by moving a line segment fd in the L-axis direction (direction in which the total film thickness L increases), while its positional relationship is kept in parallel with the first plane Sp11a, with its two end points being shifted along a line segment ff (line segment represented by formula (46) and a line segment dd (line segment represented by formula (43)). In this case, the moving range of the line segment fd is in a range of 80 nm<L<90 nm.
(90 nm<L<100 nm)
Based upon the positions of the respective apexes in the regions that satisfy the conditions of the respective parameters shown in
dc:(α−6.5)/3.9=(β−0.01432)/0.000847=(L−100)/(−10) (53)
ee:(α−2.8)/2.1=(β−0.0122)/0.00127=(L−100)/(−10) (55)
ff:(α−5.8)/3.1=(β−0.01262)/0.00135536=(L−100)/(−10) (56)
In the case when the total film thickness L is represented by 80 nm<L<90 nm, a region (space) V12a that is surrounded by the following three surfaces forms a region that satisfies the conditions of the respective parameters. That is, by allowing the ratio α and ratio β to be included in the region (space) V12a, the conditions of the respective parameters can be satisfied.
Surface in which the approximation straight lines of formula (53) and formula (55) form two opposed sides . . . s5
Surface in which the approximation straight lines of formula (55) and formula (56) form two opposed sides . . . s6
Surface in which the approximation straight lines of formula (56) and formula (53) form two opposed sides . . . s7
In this case, it is supposed that the region (space) V12a includes the approximation straight lines of formulas (53), (55) and (56) themselves.
The surface in which the approximation straight lines of formula (53) and formula (55) form two opposed sides corresponds to a surface formed in the following manner. That is, the surface is formed by moving a line segment de in an L-axis direction (direction in which the total film thickness L increases), while its positional relationship is kept in parallel with the second plane Sp12a, with its two end points being shifted along a line segment dc (line segment represented by formula (53)) and a line segment ee (line segment represented by formula (55)). In this case, the moving range of the line segment de is in a range of 90 nm<L<100 nm.
The surface in which the approximation straight lines of formula (55) and formula (56) form two opposed sides corresponds to a surface formed in the following manner. That is, the surface is formed by moving a line segment ef in the L-axis direction (direction in which the total film thickness L increases), while its positional relationship is kept in parallel with the second plane Sp12a, with its two end points being shifted along a line segment ee (line segment represented by formula (55)) and a line segment ff (line segment represented by formula (56)). In this case, the moving range of the line segment ef is in a range of 90 nm<L<100 nm.
The surface in which the approximation straight lines of formula (56) and formula (53) form two opposed sides corresponds to a surface formed in the following manner. That is, the surface is formed by moving a line segment fd in the L-axis direction (direction in which the total film thickness L increases), while its positional relationship is kept in parallel with the second plane Sp12a, with its two end points being shifted along a line segment ff (line segment represented by formula (56)) and a line segment dc (line segment represented by formula (53)). In this case, the moving range of the line segment fd is in a range of 90 nm<L<100 nm.
(100 nm<L<120 nm)
Based upon the positions of the respective apexes in the regions that satisfy the conditions of the respective parameters shown in
cc:(α−4.25)/2.25=(β−0.0133)/0.0010165=(L−120)/(−20) (63)
ee:(α−1.7)/1.1=(β−0.01076)/0.00144=(L−120)/(−20) (65)
ff:(α−4)/1.8=(β−0.01144)/0.001186=(L−120)/(−20) (66)
In the case when the total film thickness L is represented by 100 nm<L<120 nm, a region (space) V13a that is surrounded by the following three surfaces forms a region that satisfies the conditions of the respective parameters. That is, by allowing the ratio α and ratio β to be included in the region (space) V13a, the conditions of the respective parameters can be satisfied.
Surface in which the approximation straight lines of formula (63) and formula (65) form two opposed sides . . . s5
Surface in which the approximation straight lines of formula (65) and formula (66) form two opposed sides . . . s6
Surface in which the approximation straight lines of formula (66) and formula (63) form two opposed sides . . . s7
In this case, it is supposed that the region (space) V13a includes the approximation straight lines of formulas (63), (65) and (66) themselves.
The surface in which the approximation straight lines of formula (63) and formula (65) form two opposed sides corresponds to a surface formed in the following manner. That is, the surface is formed by moving a line segment ce in an L-axis direction (direction in which the total film thickness L increases), while its positional relationship is kept in parallel with the third plane Sp13a, with its two end points being shifted along a line segment cc (line segment represented by formula (63)) and a line segment ee (line segment represented by formula (65)). In this case, the moving range of the line segment ce is in a range of 100 nm<L<120 nm.
The surface in which the approximation straight lines of formula (65) and formula (66) form two opposed sides corresponds to a surface formed in the following manner. That is, the surface is formed by moving a line segment ef in the L-axis direction (direction in which the total film thickness L increases), while its positional relationship is kept in parallel with the third plane Sp13a, with its two end points being shifted along a line segment ee (line segment represented by formula (65)) and a line segment ff (line segment represented by formula (66)). In this case, the moving range of the line segment ef is in a range of 100 nm<L<120 nm.
The surface in which the approximation straight lines of formula (66) and formula (63) form two opposed sides corresponds to a surface formed in the following manner. That is, the surface is formed by moving a line segment fc in the L-axis direction (direction in which the total film thickness L increases), while its positional relationship is kept in parallel with the third plane Sp13a, with its two end points being shifted along a line segment ff (line segment represented by formula (66)) and a line segment cc (line segment represented by formula (63)). In this case, the moving range of the line segment fc is in a range of 100 nm<L<120 nm.
(120 nm<L<140 nm)
Based upon the positions of the respective apexes in the regions that satisfy the conditions of the respective parameters shown in
cc:(α−3.1)/1.15=(β−0.0216)/0.0006994=(L−140)/(−20) (73)
ee:(α−1.1)/0.6=(β−0.0094)/0.0013553=(L−140)/(−20) (75)
ff:(α−3.3)/0.7=(β−0.01042)/0.001016=(L−140)/(−20) (76)
In the case when the total film thickness L is represented by 120 nm<L<140 nm, a region (space) V14a that is surrounded by the following three surfaces forms a region that satisfies the conditions of the respective parameters. That is, by allowing the ratio α and ratio β to be included in the region (space) V14a, the conditions of the respective parameters can be satisfied.
Surface in which the approximation straight lines of formula (73) and formula (75) form two opposed sides . . . s5
Surface in which the approximation straight lines of formula (75) and formula (76) form two opposed sides . . . s6
Surface in which the approximation straight lines of formula (76) and formula (73) form two opposed sides . . . s7
In this case, it is supposed that the region (space) V14a includes the approximation straight lines of formulas (73), (75) and (76) themselves.
The surface in which the approximation straight lines of formula (73) and formula (75) form two opposed sides corresponds to a surface formed in the following manner. That is, the surface is formed by moving a line segment ce in an L-axis direction (direction in which the total film thickness L increases), while its positional relationship is kept in parallel with the fourth plane Sp14a, with its two end points being shifted along a line segment cc (line segment represented by formula (73)) and a line segment ee (line segment represented by formula (75)). In this case, the moving range of the line segment ce is in a range of 120 nm<L<140 nm.
The surface in which the approximation straight lines of formula (75) and formula (76) form two opposed sides corresponds to a surface formed in the following manner. That is, the surface is formed by moving a line segment ef in the L-axis direction (direction in which the total film thickness L increases), while its positional relationship is kept in parallel with the fourth plane Sp14a, with its two end points being shifted along a line segment ee (line segment represented by formula (75)) and a line segment ff (line segment represented by formula (76)). In this case, the moving range of the line segment ef is in a range of 120 nm<L<140 nm.
The surface in which the approximation straight lines of formula (76) and formula (73) form two opposed sides corresponds to a surface formed in the following manner. That is, the surface is formed by moving a line segment fc in the L-axis direction (direction in which the total film thickness L increases), while its positional relationship is kept in parallel with the fourth plane Sp14a, with its two end points being shifted along a line segment ff (line segment represented by formula (76)) and a line segment cc (line segment represented by formula (73)). In this case, the moving range of the line segment fc is in a range of 120 nm<L<140 nm.
(140 nm<L<160 nm)
Based upon the positions of the respective apexes in the regions that satisfy the conditions of the respective parameters shown in
cc:(α−2.582)/0.518=(β−0.01199)/0.00061=(L−160)/(−20) (83)
ee:(α−1.05)/0.05=(β−0.00822)/0.0011859=(L−160)/(−20) (85)
ff:(α−2.918)/0.382=(β−0.00966)/0.0007593=(L−160)/(−20) (86)
In the case when the total film thickness L is represented by 140 nm<L<160 nm, a region (space) V15a that is surrounded by the following three surfaces forms a region that satisfies the conditions of the respective parameters. That is, by allowing the ratio α and ratio β to be included in the region (space) V15a, the conditions of the respective parameters can be satisfied.
Surface in which the approximation straight lines of formula (83) and formula (85) form two opposed sides . . . s5
Surface in which the approximation straight lines of formula (85) and formula (86) form two opposed sides . . . s6
Surface in which the approximation straight lines of formula (86) and formula (83) form two opposed sides . . . s7
In this case, it is supposed that the region (space) V15a includes the approximation straight lines of formulas (83), (85) and (86) themselves.
The surface in which the approximation straight lines of formula (83) and formula (85) form two opposed sides corresponds to a surface formed in the following manner. That is, the surface is formed by moving a line segment ce in an L-axis direction (direction in which the total film thickness L increases), while its positional relationship is kept in parallel with the fifth plane Sp15a, with its two end points being shifted along a line segment cc (line segment represented by formula (83)) and a line segment ee (line segment represented by formula (85)). In this case, the moving range of the line segment ce is in a range of 140 nm<L<160 nm.
The surface in which the approximation straight lines of formula (85) and formula (86) form two opposed sides corresponds to a surface formed in the following manner. That is, the surface is formed by moving a line segment ef in the L-axis direction (direction in which the total film thickness L increases), while its positional relationship is kept in parallel with the fifth plane Sp15a, with its two end points being shifted along a line segment ee (line segment represented by formula (85)) and a line segment ff (line segment represented by formula (86)). In this case, the moving range of the line segment ef is in a range of 140 nm<L<160 nm.
The surface in which the approximation straight lines of formula (86) and formula (83) form two opposed sides corresponds to a surface formed in the following manner. That is, the surface is formed by moving a line segment fc in the L-axis direction (direction in which the total film thickness L increases), while its positional relationship is kept in parallel with the fifth plane Sp15a, with its two end points being shifted along a line segment ff (line segment represented by formula (86)) and a line segment cc (line segment represented by formula (83)). In this case, the moving range of the line segment fc is in a range of 140 nm<L<160 nm.
Therefore, a region that satisfies the conditions of the parameters of the visible light-ray transmittance, the blue index, the red index and the shading coefficient is determined in the following manner for each of ranges of the respective total film thicknesses L.
(80 nm≦L≦90 nm)
In the case when the total film thickness L is represented by 80 nm≦L≦90 nm, a region (space) V11b, which is surrounded by the following five planes, forms a region that satisfies the conditions of the respective parameters. That is, by allowing the ratio α and ratio β to be included in the region (space) V11b, the conditions of the respective parameters can be satisfied.
Plane in which the approximation straight lines of formula (6b), formula (7b), and formula (34b) form three sides . . . Sp11a
Plane in which the approximation straight lines of formula (10b), formula (11b) and formula (35b) form three sides . . . Sp12a
Surface in which the approximation straight lines of formula (7b), formula (11b), formula (43) and formula (45) form four sides . . . s5a
Surface in which the approximation straight lines of formula (6b), formula (10b), formula (43) and formula (46) form four sides . . . s7a
Surface in which the approximation straight lines of formula (34b), formula (35b), formula (45) and formula (46) form four sides . . . s6a
In this case, it is supposed that the region (space) V11b includes the respective approximation straight lines themselves that define the respective surfaces. Moreover, the surfaces s5a to s7a are surfaces that are formed in the same manner as in surfaces s5 to s7 within the range of 80 nm<L<90 nm in the total film thickness L, except that the moving ranges of the respective line segments are set within the range of 80 nm≦L≦90 nm.
(90 nm≦L≦100 nm)
In the case when the total film thickness L is represented by 90 nm≦L≦100 nm, a region (space) V12b, which is surrounded by the following five planes, forms a region that satisfies the conditions of the respective parameters. That is, by allowing the ratio α and ratio β to be included in the region (space) V12b, the conditions of the respective parameters can be satisfied.
Plane in which the approximation straight lines of formula (10b), formula (11b) and formula (35b) form three sides . . . Sp12a
Plane in which the approximation straight lines of formula (14b), formula (15b) and formula (36b) form three sides . . . Sp13a
Surface in which the approximation straight lines of formula (11b), formula (15b), formula (53) and formula (55) form four sides . . . s5a
Surface in which the approximation straight lines of formula (10b), formula (14b), formula (53) and formula (56) form four sides . . . s7a
Surface in which the approximation straight lines of formula (35b), formula (36b), formula (55) and formula (56) form four sides . . . s6a
In this case, it is supposed that the region (space) V12b includes the respective approximation straight lines themselves that define the respective surfaces. Moreover, the surfaces s5a to s7a are surfaces that are formed in the same manner as in surfaces s5 to s7 within the range of 90 nm<L<100 nm in the total film thickness L, except that the moving ranges of the respective line segments are set within the range of 90 nm≦L≦100 nm.
(100 nm≦L≦120 nm)
In the case when the total film thickness L is represented by 100 nm≦L≦120 nm, a region (space) V13b, which is surrounded by the following five planes, forms a region that satisfies the conditions of the respective parameters. That is, by allowing the ratio α and ratio β to be included in the region (space) V13b, the conditions of the respective parameters can be satisfied.
Plane in which the approximation straight lines of formula (14b), formula (15b) and formula (36b) form three sides . . . Sp13a
Plane in which the approximation straight lines of formula (18b), formula (19b), and formula (37b) form three sides . . . Sp14a
Surface in which the approximation straight lines of formula (15b), formula (19b), formula (63) and formula (65) form four sides . . . s5a
Surface in which the approximation straight lines of formula (14b), formula (18b), formula (63) and formula (66) form four sides . . . s7a
Surface in which the approximation straight lines of formula (36b), formula (37b), formula (65) and formula (66) form four sides . . . s6a
In this case, it is supposed that the region (space) V13b includes the respective approximation straight lines themselves that define the above-mentioned respective surfaces. Moreover, the surfaces s5a to s7a are surfaces that are formed in the same manner as in surfaces s5 to s7 within the range of 100 nm<L<120 nm in the total film thickness L, except that the moving ranges of the respective line segments are set within the range of 100 nm≦L≦120 nm.
(120 nm≦L≦140 nm)
In the case when the total film thickness L is represented by 120 nm≦L≦140 nm, a region (space) V14b, which is surrounded by the following five planes, forms a region that satisfies the conditions of the respective parameters. That is, by allowing the ratio α and ratio β to be included in the region (space) V14b, the conditions of the respective parameters can be satisfied.
Plane in which the approximation straight lines of formula (18b), formula (19b) and formula (37b) form three sides . . . Sp14a
Plane in which the approximation straight lines of formula (22b), formula (23b) and formula (38b) form three sides . . . Sp15a
Surface in which the approximation straight lines of formula (19b), formula (23b), formula (73) and formula (75) form four sides . . . s5a
Surface in which the approximation straight lines of formula (18b), formula (22b), formula (73) and formula (76) form four sides . . . s7a
Surface in which the approximation straight lines of formula (37b), formula (38b), formula (75) and formula (76) form four sides . . . s6a
In this case, it is supposed that the region (space) V14b includes the respective approximation straight lines themselves that define the above-mentioned respective surfaces. Moreover, the surfaces s5a to s7a are surfaces that are formed in the same manner as in surfaces s5 to s7 within the range of 120 nm<L<140 nm in the total film thickness L, except that the moving ranges of the respective line segments are set within the range of 120 nm≦L≦140 nm.
(140 nm≦L≦160 nm)
In the case when the total film thickness L is represented by 140 nm≦L≦160 nm, a region (space) V15b, which is surrounded by the following five planes, forms a region that satisfies the conditions of the respective parameters. That is, by allowing the ratio α and ratio β to be included in the region (space) V15b, the conditions of the respective parameters can be satisfied.
Plane in which the approximation straight lines of formula (22b), formula (23b) and formula (38b) form three sides . . . Sp15a
Plane in which the approximation straight lines of formula (26b), formula (28b) and formula (39b) form three sides . . . Sp16a
Surface in which the approximation straight lines of formula (23b), formula (28b), formula (83) and formula (85) form four sides . . . s5a
Surface in which the approximation straight lines of formula (22b), formula (26b), formula (83) and formula (86) form four sides . . . s7a
Surface in which the approximation straight lines of formula (38b), formula (39b), formula (85) and formula (86) form four sides . . . s6a
In this case, it is supposed that the region (space) V15b includes the respective approximation straight lines themselves that define the above-mentioned respective surfaces. Moreover, the surfaces s5a to s7a are surfaces that are formed in the same manner as in surfaces s5 to s7 within the range of 140 nm<L<160 nm in the total film thickness L, except that the moving ranges of the respective line segments are set within the range of 140 nm≦L≦160 nm.
As shown in
Moreover, by two-dimensionally arranging the structural elements 4c having, for example, a spherical shape or a corner cubic shape, on the one main surface of the first optical layer 4, in the most closely packed filling state, a close-packed array, such as a square close-packed array, a delta close-packed array and a hexagonal close-packed array, may be formed thereon. For example, as shown in
Each of the structural elements 4c is formed as a convex portion or a concave portion having, for example, a corner cubic shape, a hemispherical shape, a semi-elliptical shape, a prism shape, a cylindrical shape, a free-curved face shape, a polygonal shape, a cone shape, a polygonal pyramid-like shape, a truncated cone shape, a paraboloidical surface shape, or the like. The bottom face of each structural element 4c has, for example, a round shape, an elliptical shape, or a polygonal shape, such as a triangular shape, a quadrangular shape, a hexagonal shape, an octagonal shape or the like. Moreover, the pitches P1 and P2 of the structural elements 4c are preferably selected on demand in accordance with desired optical characteristics. Furthermore, in the case when the main axis of the structural element 4c is tilted relative to a perpendicular line that is perpendicular to the incident surface of the optical film 1, the main axis of the structural element 4c is preferably tilted in at least one of the arrangement directions of the two-dimensional arrangement of the structural elements 4c. In the case when the optical film 1 is bonded to a window material that is disposed virtually perpendicularly to the ground, the main axis of the structural elements 4c is preferably tilted downward (ground side) from the window material based upon the perpendicular line.
In the case of the structural elements 4c having the corner cubic shape, when the ridge line portion R is great, the main axis thereof is preferably tilted in the upward sky direction and from the viewpoint of suppressing downward reflection, it is preferably tilted toward the ground side. Since solar light rays are diagonally made incident on the film, light rays are hardly made incident onto the inside of the structure so that the shape on the incident side becomes very important. That is, in the case when the R of the ridge line portion is large, since retroreflection light is reduced, by tilting the main axis thereof in the upward sky direction, this phenomenon can be suppressed. Moreover, in the corner cubic body, the retroreflection is realized by being reflected on the reflection surface three times; however, one portion of light rays is leaked in directions other than the retroreflection direction because of reflections of two times. By tilting the corner cube toward the ground side, most of this leakage light can be returned to the upward sky direction. In this manner, depending on the shape and object, the tilted angle may be made in any direction.
In accordance with the fourth embodiment, the plural reflection layers 3 are arranged in parallel with one another inside an optical layer 5. Thus, the number of reflections by the reflection layers 3 can be reduced in comparison with that of the structure in which the structural element 4c having the corner cubic shape or the prism shape is formed. Therefore, it is possible to increase the reflectance and also to reduce the light absorption by the reflection layers 3.
The fifth embodiment differs from the first embodiment in that while a light ray having a predetermined wavelength is directively reflected, light rays having wavelengths other than the predetermined wavelength are scattered. The optical film 1 is provided with a light scattering body for scattering incident light rays. This scattering body is installed on at least one portion of for example, the surface of the optical layer 2, the inside of the optical layer 2 and a portion between the reflection layer 3 and the optical layer 2. The light scatting body is preferably installed on at least one portion of a portion between the reflection layer 3 and the first optical layer 4, the inside of the first optical layer 4 and the surface of the first optical layer 4. In the case when the optical film 1 is bonded to a support body such as the window material or the like, the light scattering body may be applied to either the indoor side or the outdoor side. In the case when the optical film 1 is bonded to the outdoor side, the light scattering body for scattering light rays having wavelengths other than the predetermined wavelength is preferably installed only between the reflection layer 3 and the support body such as the window material or the like. This is because when the light scattering body exists between the reflection layer 3 and the incident surface, the directive reflection property tends to be lost. Moreover, in the case when the optical film 1 is bonded to the indoor side, the light scattering body is preferably installed between the light-releasing surface on the side opposite to the bonding surface and the reflection layer 3.
In accordance with the fifth embodiment, a light ray having a predetermined wavelength such as an infrared ray or the like can be directively reflected, while light rays having wavelengths other than the predetermined wavelength, such as visible light-rays or the like, can be scattered. Therefore, the optical film 1 is allowed to become foggy so that it is possible to impart a designing property to the optical film 1.
The optical film 1 may be further provided with a substrate 2b on the light-releasing surface S2 of the optical layer 2a, if necessary. Moreover, the optical film 1 may be further provided with a bonding layer 6 and a separation layer 7 on the light-releasing surface S2 of the optical layer 2a or on the substrate 2b, if necessary. As the optical layer 2a and the substrate 2b, those that are the same as those of the first optical layer 4 and the substrate 4a of the aforementioned first embodiment may be used.
In accordance with the sixth embodiment, since the concave-convex surface of the optical layer 2a with the reflection layer 3 formed thereon is used as the incident surface S1, one portion of incident light rays is scattered by the incident surface S1, while one portion of light rays that have not been scattered is transmitted through the optical film 1. Therefore, it is possible to obtain an optical film 1 that allows brightness of light to be felt by the incident light rays, although it is opaque. The optical film 1 having such a characteristic is preferably applicable to interior members, exterior members, solar shading members, or the like for use in such places where privacy is required, that is, more specifically, to window materials, blinds, roll screens, pleated screens, and the like.
As described above, the optical film 1 has such a characteristic as to semi-transmit the incident light rays. In the case when the optical film 1 is used outdoors, or in a room or the like with lots of contaminants, since light is scattered by contaminants adhering to the surface to cause reduction in transmitting and reflecting properties, the surface is preferably always kept transparent optically. For this reason, the surface is preferably provided with superior water repellency, hydrophilicity, or the like, with the surface being preferably allowed to exert a washing effect automatically.
In accordance with the seventh embodiment, since the optical film 1 is provided with the self-washing effect layer 51, it is possible to impart water repellency, hydrophilicity, or the like to the incident surface. Therefore, it is possible to suppress contaminants or the like from adhering to the incident surface, and consequently to suppress a reduction of directive reflecting property.
The aforementioned first embodiment has been explained by exemplifying a case in which the present invention is applied to the window material or the like; however, the present invention is not intended to be limited by this example, and may be applied to members other than the window material, such as interior members and exterior members. Moreover, not limited only to immovable fixed interior members and exterior members, such as walls, roofs, or the like, the present invention can be applied to a device that can be taken into an indoor space, by moving the interior member or the exterior member so as to adjust the transmission amount and/or reflection amount of solar light in accordance with a change in the amount of solar light caused by seasons and time variations. In the eighth embodiment, as one example of such a device, a solar shading device (blind device), which is capable of adjusting the shading amount of incident light rays by the use of a group of solar shading members by altering the angle of the group of solar shading members composed of a plurality of solar shading members, will be explained.
The head box 203 serves as a driving means that adjusts the amount of light to be taken into a space such as the inside of a room, by rotation-driving the group of slats 202 composed of the plural slats 202a in response to an operation by the operation means such as the rod. Moreover, the head box 203 also functions as a driving means (raising and lowering means) that raises and lowers the group of slats 202 on demand in accordance with the operation of the operation means such as raising and lowering operation codes 207 or the like.
As the shape of the base member 211, for example, a sheet shape, a film shape, a plate shape or the like may be used. As the material for the base member 211, for example, glass, a resin material, a paper material, a cloth material or the like may be used, and from the viewpoint of taking visible light into a predetermined space such as the inside of a room, a resin material having a transparent property is preferably used. As the glass, resin material, paper material and cloth material, known materials as the conventional roll screen may be used. As the optical film 1, one kind of the optical films 1 relating to the aforementioned first to seventh embodiments may be used, or two or more kinds of them may be used in combination.
In the ninth embodiment, explanations will be given to a roll screen device that is one example of a solar shading device capable of adjusting the shading amount of incident light rays by the use of a solar shading member by winding-up or feeding the solar shading member.
As the shape of the base member 311, for example, a sheet shape, a film shape, a plate shape or the like may be used. As the material for the base member 311, for example, glass, a resin material, a paper material, a cloth material or the like may be used, and from the viewpoint of taking visible light into a predetermined space such as the inside of a room, a resin material having a transparent property is preferably used. As the glass, resin material, paper material and cloth material, known materials as the conventional roll screen may be used. As the optical film 1, one kind of the optical films 1 relating to the aforementioned first to seventh embodiments may be used, or two or more kinds of them may be used in combination.
In the tenth embodiment, explanations will be given to an example in which the present invention is applied to a fitting (interior member or exterior member) in which an optical element having a directional reflection performance is used as a lighting unit.
The base member 411 may be formed as, for example, a sheet, a film, a substrate having flexibility. As the material for the base member 411, for example, glass, a resin material, a paper material, a cloth material or the like may be used, and from the viewpoint of taking visible light into a predetermined space such as the inside of a room, a resin material having a transparent property is preferably used. As the glass, resin material, paper material and cloth material, known materials as the conventional optical element for use as fittings may be used. As the optical film 1, one kind of the optical films 1 relating to the aforementioned first to seventh embodiments may be used, or two or more kinds of them may be used in combination.
The present invention is described in greater detail below by referring to the examples, however, the present invention should not be construed as being limited only to these examples.
In the following examples, optical characteristics of a laminated film in the case of changing the film thicknesses of the respective layers of a reflection layer 3 are found by simulation. The simulation is carried out on the laminated film shown in each of the following sample 1-1 to sample 7-5, by using optical simulation software (Light Tools) made by ORA (Optical Research Associates), so that values of the visible light-ray transmittance, shading coefficient, blue index and red index are obtained in the case when the ratio α and ratio β are changed.
First, it is assumed that high-refractive-index layers and metal layers are stacked to form a laminated film having a five-layer structure. The configuration of this laminated film is shown below.
Layer configuration: high-refractive-index layer/metal layer/high-refractive-index layer/metal layer/high-refractive-index layer
Total film thickness L: 80 nm
High-refractive-index layer:
Metal layer:
Ratio α: 0.0121
Ratio β: 8.4
It is assumed that a laminated film is formed by using the same conditions as those of sample 1-1 except that the film thicknesses of the respective layers are changed so as to satisfy the ratio α: 0.0138 and the ratio β: 12.4.
It is assumed that a laminated film is formed by using the same conditions as those of sample 1-1 except that the film thicknesses of the respective layers are changed so as to satisfy the ratio α: 0.0138 and the ratio β: 17.9.
It is assumed that a laminated film is formed by using the same conditions as those of sample 1-1 except that the film thicknesses of the respective layers are changed so as to satisfy the ratio α: 0.0155 and the ratio β: 17.4.
It is assumed that a laminated film is formed by using the same conditions as those of sample 1-1 except that the film thicknesses of the respective layers are changed so as to satisfy the ratio α: 0.0172 and the ratio β: 14.6.
It is assumed that a laminated film is formed by using the same conditions as those of sample 1-1 except that the total film thickness of the laminated film L: 90 nm is satisfied and that the film thicknesses of the respective layers are changed so as to satisfy the ratio α: 0.0106 and the ratio β: 4.
It is assumed that a laminated film is formed by using the same conditions as those of sample 2-1 except that the film thicknesses of the respective layers are changed so as to satisfy the ratio α: 0.0123 and the ratio β: 10.6.
It is assumed that a laminated film is formed by using the same conditions as those of sample 2-1 except that the film thicknesses of the respective layers are changed so as to satisfy the ratio α: 0.014 and the ratio β: 7.6.
It is assumed that a laminated film is formed by using the same conditions as those of sample 2-1 except that the film thicknesses of the respective layers are changed so as to satisfy the ratio α: 0.0157 and the ratio β: 1.6.
It is assumed that a laminated film is formed by using the same conditions as those of sample 2-1 except that the film thicknesses of the respective layers are changed so as to satisfy the ratio α: 0.0157 and the ratio β: 9.
It is assumed that a laminated film is formed by using the same conditions as those of sample 1-1 except that the total film thickness of the laminated film L: 100 nm is satisfied and that the film thicknesses of the respective layers are changed so as to satisfy the ratio α: 0.0095 and the ratio β: 4.2.
It is assumed that a laminated film is formed by using the same conditions as those of sample 3-1 except that the film thicknesses of the respective layers are changed so as to satisfy the ratio α: 0.0122 and the ratio β: 6.6.
It is assumed that a laminated film is formed by using the same conditions as those of sample 3-1 except that the film thicknesses of the respective layers are changed so as to satisfy the ratio α: 0.0129 and the ratio β: 4.8.
It is assumed that a laminated film is formed by using the same conditions as those of sample 3-1 except that the film thicknesses of the respective layers are changed so as to satisfy the ratio α: 0.0129 and the ratio β: 7.4.
It is assumed that a laminated film is formed by using the same conditions as those of sample 3-1 except that the film thicknesses of the respective layers are changed so as to satisfy the ratio α: 0.0146 and the ratio β: 4.8.
It is assumed that a laminated film is formed by using the same conditions as those of sample 1-1 except that the total film thickness of the laminated film L: 120 nm is satisfied and that the film thicknesses of the respective layers are changed so as to satisfy the ratio α: 0.0094 and the ratio β: 3.
It is assumed that a laminated film is formed by using the same conditions as those of sample 4-1 except that the film thicknesses of the respective layers are changed so as to satisfy the ratio α: 0.0111 and the ratio β: 4.6.
It is assumed that a laminated film is formed by using the same conditions as those of sample 4-1 except that the film thicknesses of the respective layers are changed so as to satisfy the ratio α: 0.0128 and the ratio β: 4.
It is assumed that a laminated film is formed by using the same conditions as those of sample 4-1 except that the film thicknesses of the respective layers are changed so as to satisfy the ratio α: 0.0128 and the ratio β: 5.8.
It is assumed that a laminated film is formed by using the same conditions as those of sample 4-1 except that the film thicknesses of the respective layers are changed so as to satisfy the ratio α: 0.0145 and the ratio β: 3.
It is assumed that a laminated film is formed by using the same conditions as those of sample 1-1 except that the total film thickness of the laminated film L: 140 nm is satisfied and that the film thicknesses of the respective layers are changed so as to satisfy the ratio α: 0.0065 and the ratio β: 2.4.
It is assumed that a laminated film is formed by using the same conditions as those of sample 54 except that the film thicknesses of the respective layers are changed so as to satisfy the ratio α: 0.0082 and the ratio β: 3.8.
It is assumed that a laminated film is formed by using the same conditions as those of sample 5-1 except that the film thicknesses of the respective layers are changed so as to satisfy the ratio α: 0.0099 and the ratio β: 1.6.
It is assumed that a laminated film is formed by using the same conditions as those of sample 5-1 except that the film thicknesses of the respective layers are changed so as to satisfy the ratio α: 0.0099 and the ratio β: 4.2.
It is assumed that a laminated film is formed by using the same conditions as those of sample 5-1 except that the film thicknesses of the respective layers are changed so as to satisfy the ratio α: 0.0116 and the ratio β: 1.6.
It is assumed that a laminated film is formed by using the same conditions as those of sample 1-1 except that the total film thickness of the laminated film L: 160 nm is satisfied and that the film thicknesses of the respective layers are changed so as to satisfy the ratio α: 0.0057 and the ratio β: 2.2.
It is assumed that a laminated film is formed by using the same conditions as those of sample 6-1 except that the film thicknesses of the respective layers are changed so as to satisfy the ratio α: 0.0074 and the ratio β: 3.6.
It is assumed that a laminated film is formed by using the same conditions as those of sample 6-1 except that the film thicknesses of the respective layers are changed so as to satisfy the ratio α: 0.0091 and the ratio β: 1.6.
It is assumed that a laminated film is formed by using the same conditions as those of sample 6-1 except that the film thicknesses of the respective layers are changed so as to satisfy the ratio α: 0.0108 and the ratio β: 1.2.
It is assumed that a laminated film is formed by using the same conditions as those of sample 6-1 except that the film thicknesses of the respective layers are changed so as to satisfy the ratio α: 0.0125 and the ratio β: 3.2.
It is assumed that a laminated film is formed by using the same conditions as those of sample 1-1 except that the total film thickness of the laminated film L: 180 nm is satisfied and that the film thicknesses of the respective layers are changed so as to satisfy the ratio α: 0.005 and the ratio β: 1.8.
It is assumed that a laminated film is formed by using the same conditions as those of sample 7-1 except that the film thicknesses of the respective layers are changed so as to satisfy the ratio α: 0.0067 and the ratio β: 3.4.
It is assumed that a laminated film is formed by using the same conditions as those of sample 7-1 except that the film thicknesses of the respective layers are changed so as to satisfy the ratio α: 0.0101 and the ratio β: 2.
It is assumed that a laminated film is formed by using the same conditions as those of sample 7-1 except that the film thicknesses of the respective layers are changed so as to satisfy the ratio α: 0.0118 and the ratio β: 1.6.
It is assumed that a laminated film is formed by using the same conditions as those of sample 7-1 except that the film thicknesses of the respective layers are changed so as to satisfy the ratio α: 0.0135 and the ratio β: 2.
Table 1 and Table 2 show the results of simulation processes carried out on the laminated films shown in sample 1-1 to sample 7-5.
From Table 1 and Table 2, the following facts are confirmed.
In the case when the visible light-ray transmittance, the blue index and the red index are used as the parameters, since sample 1-1, sample 1-2 and sample 1-4 satisfy the conditions of the respective parameters, the set ratio α and ratio β are located within a region shown in
Moreover, in the case when the shading coefficient is further used as parameters in addition to the visible light-ray transmittance, the blue index and the red index, since sample 1-4 also satisfies the condition of the shading coefficient, the set ratio α and ratio β are located within a region shown in
In the case when the visible light-ray transmittance, the blue index and the red index are used as the parameters, since sample 2-1 and sample 2-3 satisfy the conditions of the respective parameters, the set ratio α and ratio β are located within a region shown in
Moreover, in the case when the shading coefficient is further used as parameters in addition to the visible light-ray transmittance, the blue index and the red index, since sample 2-3 also satisfies the condition of the shading coefficient, the set ratio α and ratio β are located within a region shown in
In the case when the visible light-ray transmittance, the blue index and the red index are used as the parameters, since sample 3-1 and sample 3-3 satisfy the conditions of the respective parameters, the set ratio α and ratio β are located within a region shown in
Moreover, in the case when the shading coefficient is further used as parameters in addition to the visible light-ray transmittance, the blue index and the red index, since sample 3-3 also satisfies the condition of the shading coefficient, the set ratio α and ratio β are located within a region shown in
In the case when the visible light-ray transmittance, the blue index and the red index are used as the parameters, since sample 4-1 and sample 4-3 satisfy the conditions of the respective parameters, the set ratio α and ratio β are located within a region shown in
Moreover, in the case when the shading coefficient is further used as parameters in addition to the visible light-ray transmittance, the blue index and the red index, since sample 4-3 also satisfies the condition of the shading coefficient, the set ratio α and ratio β are located within a region shown in
In the case when the visible light-ray transmittance, the blue index and the red index are used as the parameters, since sample 5-1 and sample 5-3 satisfy the conditions of the respective parameters, the set ratio α and ratio β are located within a region shown in
Moreover, in the case when the shading coefficient is further used as parameters in addition to the visible light-ray transmittance, the blue index and the red index, since sample 5-3 also satisfies the condition of the shading coefficient, the set ratio α and ratio β are located within a region shown in
In the case when the visible light-ray transmittance, the blue index and the red index are used as the parameters, since sample 6-1 and sample 6-3 satisfy the conditions of the respective parameters, the set ratio α and ratio β are located within a region shown in
Moreover, in the case when the shading coefficient is further used as parameters in addition to the visible light-ray transmittance, the blue index and the red index, since sample 6-3 also satisfies the condition of the shading coefficient, the set ratio α and ratio β are located within a region shown in
In the case when the visible light-ray transmittance, the blue index and the red index are used as the parameters, since sample 7-1 and sample 7-3 satisfy the conditions of the respective parameters, the set ratio α and ratio β are located within a region shown in
Moreover, in the case when the shading coefficient is further used as parameters in addition to the visible light-ray transmittance, the blue index and the red index, since sample 7-3 also satisfies the condition of the shading coefficient, the set ratio α and ratio β are located within a region shown in
Explanation has been given specifically to embodiments of the present invention; however, the present invention is not intended to be limited by the above-mentioned embodiments, and various modifications may be made therein based upon technical ideas of the present invention.
For example, although the configurations, methods, shapes, materials and numeric values are used in the above-mentioned embodiments, they are exemplary only, and configurations, methods, shapes, materials, numeric values and the like, different from those may be used, on demand.
Moreover, the respective configurations of the above-mentioned embodiments may be combined with one another on demand within the scope not departing from the gist of the present invention.
In the above-mentioned embodiments, explanations have been given by exemplifying the driving system of the blind device and the roll screen device as a manual driving system; however, an electric driving system may be used as the driving system of the blind device and the roll screen device.
Moreover, in the above-mentioned embodiment, explanations have been given by exemplifying a configuration in which an optical film is bonded to an adherent member such as a window material or the like; however, another configuration may be adopted in which the adherent member such as the window material or the like is prepared as a first optical layer or a second optical layer itself of the optical film. Thus, the optical element such as the window material or the like may be preliminarily prepared with a function for a directional reflection.
Moreover, in the above-mentioned embodiments, explanations have been given by exemplifying a configuration in which the optical element is prepared as an optical film; however, the shape of the optical element is not intended to be limited by a film shape, and a plate shape, a block shape or the like may be used.
In the above-mentioned embodiments, explanation have been given by exemplifying a structure in which the present invention is applied to an interior member or an exterior member, such as a window material, fittings, slats of a blind device, and a screen or the like of a roll screen device; however, the present invention is not intended to be limited by these, and may be applicable to an interior member and an exterior member other than those described above.
As the interior member or the exterior member to which the optical element relating to the present invention is applied, for example, an interior member or an exterior member constituted by an optical element itself, an interior member or an exterior member constituted by a transparent substrate to which a directional reflection body is bonded, or the like, is proposed. By installing such an interior member or exterior member in the vicinity of a window inside a room, for example, only infrared rays can be directionally reflected outside the room, while visible light rays can be taken into the room. Therefore, in the case when the interior member or the exterior member is installed, it becomes possible to reduce the necessity of indoor illumination. Moreover, since there is hardly any diffused reflection into the indoor side by the interior member or the exterior member, it is possible to suppress an ambient temperature rise. Furthermore, in accordance with required purposes, such as visibility control, intensity improvement and the like, the present invention may be applied to a bonding member other than the transparent substrate.
In the above-mentioned embodiments, explanations have been given by exemplifying a case in which the present invention is applied to a blind device and a roll screen device; however, the present invention is not intended to be limited by these, and may be applicable to various solar shading devices to be installed indoors or outdoors.
Moreover, in the above-mentioned embodiments, explanations have been given by exemplifying a case in which the present invention is applied to a solar shading device (for example, roll screen device) capable of adjusting the shading amount of incident light rays by the use of a solar shading member by winding a solar shading member up or by feeding the solar shading member out; however, the present invention is not intended to be limited by this example. For example, the present invention may be applied to a solar shading device capable of adjusting the shading amount of incident light rays by folding the shading member up. As the solar shading device of this type, for example, a pleated screen device which is capable of adjusting the shading amount of incident light rays by folding up a screen serving as the shading member like bellows is proposed.
Furthermore, in the above-mentioned embodiments, explanations have been given by exemplifying a case in which the present invention is applied to a horizontal blind device (Venetian blind device); however, the present invention may also be applicable to a longitudinal blind device (vertical blind device).
In the above-mentioned second embodiment, by defining a minute region ΔSi between the respective adjacent regions in the same manner as in the first embodiment, the ratio α and the ratio β may be set within a region surrounded by a circumferential surface S composed of a group of the minute regions ΔSi.
The present technique may have the following configurations.
(1)
An optical element including: a first optical layer having a concave-convex surface;
a wavelength-selective reflection layer formed on the concave-convex surface; and
a second optical layer formed on the wavelength-selective reflection layer, and in this structure, the wavelength-selective reflection layer has a five-layer structure in which a high-refractive-index layer and a metal layer are alternately stacked, and in the case when the entire wavelength-selective reflection layer has a geometric film thickness L of 80 nm, a ratio α (=db/da) of an optical film thickness db of the entire metal layer relative to an optical film thickness da of the entire high-refractive-index layer and a ratio β (=d3/d1) of an optical film thickness d3 of the third high-refractive-index layer relative to an optical film thickness d1 of the first high-refractive-index layer, when viewed from either the first optical layer side or the second optical layer side, are included in a first region surrounded by the following formulas (1) to (4), while in the case when the entire wavelength-selective reflection layer has a geometric film thickness L of 90 nm, the ratio α and the ratio β are included in a second region surrounded by the following formulas (5) to (8), and in the case when the entire wavelength-selective reflection layer has a geometric film thickness L of 80 nm<L<90 nm,
supposing that each of minute sides formed by dividing a periphery C1 of the first region into n-equal portions, with an intersection between the formula (1) and formula (3) being set as a starting point, is represented as ΔC1i (where i represents a natural number from 0 to n) and that each of minute sides formed by dividing a periphery C2 of the second region into n-equal portions, with an intersection between the formula (5) and formula (7) being set as a starting point, is represented as ΔC2i, and that each of minute regions having a rectangular shape, with ΔC1i and ΔC2i being formed as the two short sides, is defined as ΔSi, the optical element is designed such that the ratio α and the ratio β are surrounded by a circumferential surface S composed of a group of minute regions ΔSi.
α=−0.0004β2+0.0053β+0.0065 (1)
α=−1×10−5β2+0.0007β+0.0066 (2)
α=−1×10−5β2+0.0005β+0.0119 (3)
α=0.012114 (4)
α=−0.0002β2+0.0039β+0.0087 (5)
α=−3×10−5β2+0.0014β+0.0038 (6)
α=−2×10−5β2+0.0006β+0.0112 (7)
α=0.010589 (8)
(2)
An optical element including: a first optical layer having a concave-convex surface;
a wavelength-selective reflection layer formed on the concave-convex surface; and
a second optical layer formed on the wavelength-selective reflection layer, and in this structure, the wavelength-selective reflection layer has a five-layer structure in which a high-refractive-index layer and a metal layer are alternately stacked, and in the case when the entire wavelength-selective reflection layer has a geometric film thickness L of 90 nm, a ratio α (=db/da) of an optical film thickness db of the entire metal layer relative to an optical film thickness da of the entire high-refractive-index layer and a ratio β (=d3/d1) of an optical film thickness d3 of the third high-refractive-index layer relative to an optical film thickness d1 of the first high-refractive-index layer, when viewed from either the first optical layer side or the second optical layer side, are included in a first region surrounded by the following formulas (5) to (8), while in the case when the entire wavelength-selective reflection layer has a geometric film thickness L of 100 nm, the ratio α and the ratio β are included in a second region surrounded by the following formulas (9) to (12), and in the case when the entire wavelength-selective reflection layer has a geometric film thickness L of 90 nm<L<100 nm,
supposing that each of minute sides formed by dividing a periphery C1 of the first region into n-equal portions, with an intersection between the formula (5) and formula (7) being set as a starting point, is represented as ΔC1i (where i represents a natural number of 0 to n), that each of minute sides formed by dividing a periphery C2 of the second region into n-equal portions, with an intersection between the formula (9) and formula (11) being set as a starting point, is represented as ΔC2i and that each of minute regions having a rectangular shape, with ΔC1i and ΔC2i being formed as the two short sides, is defined as ΔSi, the optical element is designed such that the ratio α and the ratio β are surrounded by a circumferential surface S composed of a group of minute regions ΔSi.
α=−0.0002β2+0.0039β+0.0087 (5)
α=−3×10−5β2+0.0014β+0.0038 (6)
α=−2×10−5β2+0.0006β+0.0112 (7)
α=0.010589 (8)
α=−0.0002β2+0.0055β+0.0057 (9)
α=−0.0002β2+0.0045β−0.0067 (10)
α=−4×10−5β2+0.001β+0.0099 (11)
α=0.009403 (12)
(3)
An optical element including: a first optical layer having a concave-convex surface;
a wavelength-selective reflection layer formed on the concave-convex surface; and
a second optical layer formed on the wavelength-selective reflection layer, and in this structure, the wavelength-selective reflection layer has a five-layer structure in which a high-refractive-index layer and a metal layer are alternately stacked, and in the case when the entire wavelength-selective reflection layer has a geometric film thickness L of 100 nm, a ratio α (=db/da) of an optical film thickness db of the entire metal layer relative to an optical film thickness da of the entire high-refractive-index layer and a ratio β (=d3/d1) of an optical film thickness d3 of the third high-refractive-index layer relative to an optical film thickness d1 of the first high-refractive-index layer, when viewed from either the first optical layer side or the second optical layer side, are included in a first region surrounded by the following formulas (9) to (12), while in the case when the entire wavelength-selective reflection layer has a geometric film thickness L of 120 nm, the ratio α and the ratio β are included in a second region surrounded by the following formulas (13) to (16), and in the case when the entire wavelength-selective reflection layer has a geometric film thickness L of 100 nm<L<120 nm,
supposing that each of minute sides formed by dividing a periphery C1 of the first region into n-equal portions, with an intersection between the formula (9) and formula (11) being set as a starting point, is represented as ΔC1i (where i represents a natural number of 0 to n), that each of minute sides formed by dividing the periphery C2 of the second region into n-equal portions, with an intersection between formula (13) and formula (15) serving as a starting point, is represented as ΔC2i and that each of minute regions having a rectangular shape, with ΔC1i and ΔC2i being formed as the two short sides, is defined as ΔSi, the optical element is designed such that the ratio α and the ratio β are surrounded by a circumferential surface S composed of a group of the minute regions ΔSi.
α=−0.0002β2+0.0055β+0.0057 (9)
α=−0.0002β2+0.0045β−0.0067 (10)
α=−4×10−5β2+0.001β+0.0099 (11)
α=0.009403 (12)
α=−0.0003β2+0.0074β+0.0033 (13)
α=−0.0014β2+0.0191β−0.0422 (14)
α=−9×10−5β2+0.0015β+0.0084 (15)
α=0.007709 (16)
(4)
An optical element including: a first optical layer having a concave-convex surface;
a wavelength-selective reflection layer formed on the concave-convex surface; and
a second optical layer formed on the wavelength-selective reflection layer, and in this structure, the wavelength-selective reflection layer has a five-layer structure in which a high-refractive-index layer and a metal layer are alternately stacked, and in the case when the entire wavelength-selective reflection layer has a geometric film thickness L of 120 nm, a ratio α (=db/da) of an optical film thickness db of the entire metal layer relative to an optical film thickness da of the entire high-refractive-index layer and a ratio β (=d3/d1) of an optical film thickness d3 of the third high-refractive-index layer relative to an optical film thickness d1 of the first high-refractive-index layer, when viewed from either the first optical layer side or the second optical layer side, are included in a first region surrounded by the following formulas (13) to (16), while in the case when the entire wavelength-selective reflection layer has a geometric film thickness L of 140 nm, the ratio α and the ratio β are included in a second region surrounded by the following formulas (17) to (20), and in the case when the entire wavelength-selective reflection layer has a geometric film thickness L of 120 nm<L<140 nm,
supposing that each of minute sides formed by dividing a periphery C1 of the first region into n-equal portions, with an intersection between the formula (13) and formula (15) being set as a starting point, is represented as ΔC1i (where i represents a natural number of 0 to n), that each of minute sides formed by dividing the periphery C2 of the second region into n-equal portions, with an intersection between formula (17) and formula (19) serving as a starting point, is represented as ΔC2i and that each of minute regions having a rectangular shape, with ΔC1i and ΔC2i being formed as the two short sides, is defined as ΔSi, the optical element is designed such that the ratio α and the ratio β are surrounded by a circumferential surface S composed of a group of minute regions ΔSi.
α=−0.0003β2+0.0074β+0.0033 (13)
α=−0.0014β2+0.0191β−0.0422 (14)
α=−9×10−5β2+0.0015β+0.0084 (15)
α=0.007709 (16)
α=−0.0014β2+0.0136β−0.0027 (17)
β=10132α2−241.39α+4.747 (18)
α=−0.0001β2+0.002β+0.0074 (19)
α=0.006523 (20)
(5)
An optical element including: a first optical layer having a concave-convex surface;
a wavelength-selective reflection layer formed on the concave-convex surface; and
a second optical layer formed on the wavelength-selective reflection layer, and in this structure, the wavelength-selective reflection layer has a five-layer structure in which a high-refractive-index layer and a metal layer are alternately stacked, and in the case when the entire wavelength-selective reflection layer has a geometric film thickness L of 140 nm, a ratio α (=db/da) of an optical film thickness db of the entire metal layer relative to an optical film thickness da of the entire high-refractive-index layer and a ratio β (=d3/d1) of an optical film thickness d3 of the third high-refractive-index layer relative to an optical film thickness d1 of the first high-refractive-index layer, when viewed from either the first optical layer side or the second optical layer side, are included in a first region surrounded by the following formulas (17) to (20), while in the case when the entire wavelength-selective reflection layer has a geometric film thickness L of 160 nm, the ratio α and the ratio β are included in a second region surrounded by the following formulas (21) to (25), and in the case when the entire wavelength-selective reflection layer has a geometric film thickness L of 140 nm<L<160 nm,
supposing that each of minute sides formed by dividing a periphery C1 of the first region into n-equal portions, with an intersection between the formula (17) and formula (19) being set as a starting point, is represented as ΔC1i (where i represents a natural number of 0 to n), that each of minute sides formed by dividing the periphery C2 of the second region into n-equal portions, with an intersection between the formula (21) and formula (24) serving as a starting point, is represented as ΔC2i and that each of minute regions having a rectangular shape, with ΔC1i and ΔC2i being formed as the two short sides, is defined as ΔSi, the optical element is designed such that the ratio α and the ratio β are surrounded by a circumferential surface S composed of a group of minute regions ΔSi.
α=−0.0014β2+0.0136β−0.0027 (17)
β=10132α2−241.39α+4.747 (18)
α=−0.0001β2+0.002β+0.0074 (19)
α=0.006523 (20)
α=−0.005β2+0.0273β−0.0145 (21)
α=0.0043β2−0.0332β+0.07 (22)
β=2.875 (23)
α=−0.0001β2+0.0025β+0.0062 (24)
α=0.005676 (25)
(6)
An optical element including: a first optical layer having a concave-convex surface;
a wavelength-selective reflection layer formed on the concave-convex surface; and
a second optical layer formed on the wavelength-selective reflection layer, and in this structure, the wavelength-selective reflection layer has a five-layer structure in which a high-refractive-index layer and a metal layer are alternately stacked, and in the case when the entire wavelength-selective reflection layer has a geometric film thickness L of 160 nm, a ratio α (=db/da) of an optical film thickness db of the entire metal layer relative to an optical film thickness da of the entire high-refractive-index layer and a ratio β (=d3/d1) of an optical film thickness d3 of the third high-refractive-index layer relative to an optical film thickness d1 of the first high-refractive-index layer, when viewed from either the first optical layer side or the second optical layer side, are included in a first region surrounded by the following formulas (21) to (25), while in the case when the entire wavelength-selective reflection layer has a geometric film thickness L of 180 nm, the ratio α and the ratio β are included in a second region surrounded by the following formulas (26) to (29), and in the case when the entire wavelength-selective reflection layer has a geometric film thickness L of 160 nm<L<180 nm,
supposing that each of minute sides formed by dividing a periphery C1 of the first region into n-equal portions, with an intersection between the formula (21) and formula (24) being set as a starting point, is represented as ΔC1i (where i represents a natural number of 0 to n), that each of minute sides formed by dividing the periphery C2 of the second region into n-equal portions, with an intersection between the formula (26) and formula (28) serving as a starting point, is represented as ΔC2i and that each of minute regions having a rectangular shape, with ΔC1i and ΔC2i being formed as the two short sides, is defined as ΔSi, the optical element is designed such that the ratio α and the ratio β are surrounded by a circumferential surface S composed of a group of minute regions ΔSi.
α=−0.005β2+0.0273β−0.0145 (21)
α=0.0043β2−0.0332β+0.07 (22)
β=2.875 (23)
α=−0.0001β2+0.0025β+0.0062 (24)
α=0.005676 (25)
α=−0.0103β2+0.047β−0.0322 (26)
α=0.0093β2−0.0677β+0.1212 (27)
α=−0.0003β2+0.0036β+0.0046 (28)
α=0.00498 (29)
(7)
The optical element according to (1) in which in the case when the entire wavelength-selective reflection layer has a geometric film thickness L of 80 nm, the ratio α and the ratio β are included in a third region surrounded by the above-mentioned formulas (2) and (3) as well as the following formula (30), in the case when the entire wavelength-selective reflection layer has a geometric film thickness L of 90 nm, the ratio α and the ratio β are included in a fourth region surrounded by the above-mentioned formulas (6) and (7) as well as the following formula (31), and in the case when the entire wavelength-selective reflection layer has a geometric film thickness L of 80 nm<L<90 nm,
supposing that each of minute sides formed by dividing a periphery C3 of the third region into n-equal portions, with an intersection between the above-mentioned formula (3) and the following formula (30) being set as a starting point, is represented as ΔC3i (where i represents a natural number of 0 to n), that each of minute sides formed by dividing a periphery C4 of the fourth region into n-equal portions, with an intersection between the above-mentioned formula (7) and the following formula (31) serving as a starting point, is represented as ΔC4i and that each of minute regions having a rectangular shape, with ΔC3i and ΔC4i being formed as the two short sides, is defined as ΔSi, the optical element is designed such that the ratio α and the ratio β are surrounded by a circumferential surface S composed of a group of the minute regions ΔSi.
α=6×10−6β2+0.0002β+0.0141 (30)
α=−1×10−5β2+0.0002β+0.0125 (31)
(8)
The optical element according to (2) in which in the case when the entire wavelength-selective reflection layer has a geometric film thickness L of 90 nm, the ratio α and the ratio β are included in a third region surrounded by the above-mentioned formulas (6) and (7) as well as the following formula (31), in the case when the entire wavelength-selective reflection layer has a geometric film thickness L of 100 nm, the ratio α and the ratio β are included in a fourth region surrounded by the above-mentioned formulas (10) and (11) as well as the following formula (32), and in the case when the entire wavelength-selective reflection layer has a geometric film thickness L of 90 nm<L<100 nm,
supposing that each of minute sides formed by dividing a periphery C3 of the third region into n-equal portions, with an intersection between the above-mentioned formula (7) and the following formula (31) being set as a starting point, is represented as ΔC3i (where i represents a natural number of 0 to n), that each of minute sides formed by dividing a periphery C4 of the fourth region into n-equal portions, with an intersection between the above-mentioned formula (11) and the following formula (32) serving as a starting point, is represented as ΔC4i and that each of minute regions having a rectangular shape, with ΔC3i and ΔC4i being formed as the two short sides, is defined as ΔSi, the optical element is designed such that the ratio α and the ratio β are surrounded by a circumferential surface S composed of a group of the minute regions ΔSi.
α=−1×10−5β2+0.0002β+0.0125 (31)
α=−3×10−5β2+0.0004β+0.0113 (32)
(9)
The optical element according to (3) in which in the case when the entire wavelength-selective reflection layer has a geometric film thickness L of 100 nm, the ratio α and the ratio β are included in a third region surrounded by the above-mentioned formulas (10) and (11) as well as the following formula (32), in the case when the entire wavelength-selective reflection layer has a geometric film thickness L of 120 nm, the ratio α and the ratio β are included in a fourth region surrounded by the above-mentioned formulas (14) and (15) as well as the following formula (33), and in the case when the entire wavelength-selective reflection layer has a geometric film thickness L of 100 nm<L<120 nm,
supposing that each of minute sides formed by dividing a periphery C3 of the third region into n-equal portions, with an intersection between the above-mentioned formula (11) and the following formula (32) being set as a starting point, is represented as ΔC3i (where i represents a natural number of 0 to n), that each of minute sides formed by dividing a periphery C4 of the fourth region into n-equal portions, with an intersection between the above-mentioned formula (15) and the following formula (33) serving as a starting point, is represented as ΔC4i and that each of minute regions having a rectangular shape, with ΔC3i and ΔC4i being formed as the two short sides, is defined as ΔSi, the optical element is designed such that the ratio α and the ratio β are surrounded by a circumferential surface S composed of a group of the minute regions ΔSi.
α=−3×10−5β2+0.0004β+0.0113 (32)
α=−7×10−5β2+0.0007β+0.0097 (33)
(10)
The optical element according to (4) in which in the case when the entire wavelength-selective reflection layer has a geometric film thickness L of 120 nm, the ratio α and the ratio β are included in a third region surrounded by the above-mentioned formulas (14) and (15) as well as the following formula (33), in the case when the entire wavelength-selective reflection layer has a geometric film thickness L of 140 nm, the ratio α and the ratio β are included in a fourth region surrounded by the above-mentioned formulas (18) and (19) as well as the following formula (34), and in the case when the entire wavelength-selective reflection layer has a geometric film thickness L of 120 nm<L<140 nm,
supposing that each of minute sides formed by dividing a periphery C3 of the third region into n-equal portions, with an intersection between the above-mentioned formula (15) and the following formula (33) being set as a starting point, is represented as ΔC3i (where i represents a natural number of 0 to n), that each of minute sides formed by dividing a periphery C4 of the fourth region into n-equal portions, with an intersection between the above-mentioned formula (19) and the following formula (34) serving as a starting point, is represented as ΔC4i and that each of minute regions having a rectangular shape, with ΔC3i and ΔC4i being formed as the two short sides, is defined as ΔSi, the optical element is designed such that the ratio α and the ratio β are surrounded by a circumferential surface S composed of a group of the minute regions ΔSi.
α=−7×10−5β2+0.0007β+0.0097 (33)
α=−0.0001β2+0.0011β+0.0083 (34)
(11)
The optical element according to (5) in which in the case when the entire wavelength-selective reflection layer has a geometric film thickness L of 140 nm, the ratio α and the ratio β are included in a third region surrounded by the above-mentioned formulas (18) and (19) as well as the following formula (34), in the case when the entire wavelength-selective reflection layer has a geometric film thickness L of 160 nm, the ratio α and the ratio β are included in a fourth region surrounded by the above-mentioned formulas (21) to (24) as well as the following formula (35), and in the case when the entire wavelength-selective reflection layer has a geometric film thickness L of 140 nm<L<160 nm,
supposing that each of minute sides formed by dividing a periphery C3 of the third region into n-equal portions, with an intersection between the above-mentioned formula (19) and the following formula (34) being set as a starting point, is represented as ΔC3i (where i represents a natural number of 0 to n), that each of minute sides formed by dividing a periphery C4 of the fourth region into n-equal portions, with an intersection between the above-mentioned formula (21) and the following formula (35) serving as a starting point, is represented as ΔC4i and that each of minute regions having a rectangular shape, with ΔC3i and ΔC4i being formed as the two short sides, is defined as ΔSi, the optical element is designed such that the ratio α and the ratio β are surrounded by a circumferential surface S composed of a group of the minute regions ΔSi.
α=−0.0001β2+0.0011β+0.0083 (34)
α=−0.0002β2+0.0016β+0.0067 (35)
(12)
The optical element according to (6) in which in the case when the entire wavelength-selective reflection layer has a geometric film thickness L of 160 inn, the ratio α and the ratio β are included in a third region surrounded by the above-mentioned formulas (21) to (24) as well as the following formula (35), in the case when the entire wavelength-selective reflection layer has a geometric film thickness L of 180 nm, the ratio α and the ratio β are included in a fourth region surrounded by the above-mentioned formulas (26) to (28) as well as the following formula (36), and in the case when the entire wavelength-selective reflection layer has a geometric film thickness L of 160 nm<L<180 nm,
supposing that each of minute sides formed by dividing a periphery C3 of the third region into n-equal portions, with an intersection between the above-mentioned formula (21) and the following formula (35) being set as a starting point, is represented as ΔC3i (where i represents a natural number of 0 to n), that each of minute sides formed by dividing a periphery C4 of the fourth region into n-equal portions, with an intersection between the above-mentioned formula (26) and the following formula (36) serving as a starting point, is represented as ΔC4i and that each of minute regions having a rectangular shape, with ΔC3i and ΔC4i being formed as the two short sides, is defined as ΔSi, the optical element is designed such that the ratio α and the ratio β are surrounded by a circumferential surface S composed of a group of the minute regions ΔSi.
α=−0.0002β2+0.0016β+0.0067 (35)
α=−0.0003β2+0.0021β+0.0055 (36)
(13)
The optical element according to any one of (1) to (12) in which, when viewed from either the first optical layer side or the second optical layer side, the film thicknesses of the first and fifth high-refractive-index layers are virtually the same, and the film thicknesses of the second and fourth metal layers are virtually the same.
(14)
The optical element according to any one of (1) to (12) in which the high-refractive-index layer has a refractive index higher than that of the metal layer.
(15)
The optical element according to any one of (1) to (12) in which the high-refractive-index layer has a refractive index of 1.7 or more to 2.6 or less.
(16)
The optical element according to any one of (1) to (12) in which the high-refractive-index layer contains at least one element selected from the group consisting of niobium oxide, zinc oxide, titanium oxide and tantalum oxide, and the metal layer contains an Ag alloy.
(17)
A window material including an optical element according to any one of (1) to (16).
(18)
A fitting provided with an optical element according to any one of (1) to (16) installed in a lighting unit.
(19)
A solar shading device including one or a plurality of solar shading members for shading solar light, in which the solar shading member is provided with an optical element according to any one of (1) to (16).
| Number | Date | Country | Kind |
|---|---|---|---|
| 2011-225389 | Oct 2011 | JP | national |
| Filing Document | Filing Date | Country | Kind | 371c Date |
|---|---|---|---|---|
| PCT/JP2012/072085 | 8/24/2012 | WO | 00 | 4/11/2014 |