Related patent application is commonly assigned Japanese Patent Application No. 2003-61538 filed on Mar. 7, 2003, which is incorporated by reference into the present patent application.
1. Field of the Invention
The present invention relates to an optical element which polarizes transmitted light and reflected light and a method of manufacturing the same.
2. Description of the Related Art
A polarizing element is an optical element which is capable of transmitting or reflecting only a desired linear polarized light component. For example, such a polarizing element has been proposed which uses a two-dimensional periodic structure in which dielectric material layers having different refractive indexes from each other are stacked one atop the other in wavelength or shorter periods, namely, photonic crystals. When the periods of dielectric material layers are set appropriately, so-called photonic crystals exhibit a photonic band gap (PBG) which does not permit propagation of light. Using the PBG, it is possible to reflect one of mutually orthogonal polarized wave components having different propagation characteristics from each other, while transmitting the other one of the polarized wave components.
One example of a polarizing element using photonic crystals is a polarizing element in which two or more types of film-like materials having approximately periodic one-dimensional concave and convex portions are stacked one atop the other approximately periodically. To be specific, this is a multi-layer structure in which on a substrate which includes a periodic groove, an SiO2 film which is a transparent medium whose refractive index is low and an Si layer which is a transparent medium whose refractive index is high are alternately stacked one atop the other (JP, 3288976, B).
Such a polarizing element is fabricated by alternately forming an SiO2 layer and a Si layer on a substrate which seats periodic groove-like concave and convex portions while maintaining the shapes of the concave and convex portions, using a bias sputtering method. A bias sputtering method requires to execute deposition and etching at the same time, and was proposed as an automatic cloning method.
Also proposed as a similar polarizing element using photonic crystals is a polarizing element in which a groove is formed by RIE in a multi-layer film of repeatedly stacked Si/SiO2 and periodically repetitive structures are accordingly formed (Chuan C. Cheng et al., “New fabrication techniques for high quality photonic crystals” J. Vac. Sci. Technol. B 15(6), pp. 2764-2767 (1997)).
The first polarizing element above demands to control so as to achieve appropriate deposition and etching during automatic cloning, and therefore, it is difficult to set up conditions for bias sputtering. Further, there is a problem that a general-purpose sputtering apparatus cannot be used.
Meanwhile, with respect to the second polarizing element, it is extremely difficult to form a groove in periods which are equal to or shorter than the wavelength of light in a laminated structure in which the different materials of the Si layer and the SiO2 layer are alternately stacked one atop the other, and since this requires to use less laminations, a problem that a quenching rate becomes small arises.
The present invention aims at providing a laminated-type optical element which allows easy industrial fabrication and a method of manufacturing the same.
The present invention is directed to an optical element which polarizes light, including a substrate having a major surface with a first axis, the major surface being formed so as to include concave and convex portions arranged periodically in the direction of the first axis. The optical element further includes a laminated structure disposed on the major surface, in which a first dielectric layer and a second dielectric layer whose refractive index is different from that of the first dielectric layer are stacked one atop the other. The laminated structure includes a low-refraction area which is periodically disposed in the direction of said first axis. The refractive index of the low-refraction area is smaller than that of the first dielectric layer or the second dielectric layer which is adjacent to the low-refraction area.
The present invention is directed also to a method of manufacturing an optical element which polarizes light, including: a step of preparing a substrate having a major surface with a first axis; a step of forming concave and convex portions on the major surface arranged periodically in the direction of the first axis; and a stacking step of alternately depositing a first dielectric layer and a second dielectric layer whose refractive index is different from that of the first dielectric layer on the major surface. The stacking step is a step at which a corpuscular ray which is to impinge upon the major surface is allowed to impinge from a direction which is inclined with respect to the vertical direction to the major surface in such a manner that the convex portions will partially block the corpuscular ray. And thereby, a low-refraction area, whose refractive index is lower than that of the first dielectric layer or the second dielectric layer which is adjacent to the same, is formed within the first dielectric layer and the second dielectric layer.
First Preferred Embodiment
The optical element 100 includes the silicon substrate 10. Convexes 11 are disposed in predetermined periods along the direction of the x-axis, on the major surface of the silicon substrate 10. The convexes 11 extend as stripes along the direction of the y-axis.
On the silicon substrate 10, silicon layers 1 which are transparent dielectric layers and silicon oxide layers 2 which similarly are transparent dielectric layers are alternately stacked one atop the other. The refractive index of the silicon layers 1 is higher than that of the silicon oxide layers 2. The film thickness t1 and t2 along the direction of the z-axis of the silicon layers 1 and the silicon oxide layers 2 are 0.11 μm and 0.16 μm, respectively. The silicon layers 1 and the silicon oxide layers 2 are formed seven layers each, in total fourteen layers. The optical element 100 thus have a structure that layers having different refractive indexes from each other are stacked one atop the other in the direction of the z-axis.
The film thickness of only the top-most silicon oxide layer 2 is 0.35 μm. This is to prevent a variation in transmission characteristic which is called a “ripple.” Further, a back surface of the silicon substrate 10 is coated with a non-reflection film (not shown) such as SiON for example, which prevents reflection of incident light at the back surface.
In the optical element 100, since the silicon layers 1 and the silicon oxide layers 2 are stacked on the convexes 11, cavities 3 are created on the concaves 12. The cavities 3 are created as they are inclined at an angle θ with respect to the direction of the z-axis. As described later, the angle θ is dependent upon the angle of incidence of sputter particles which are used to form the silicon layers 1 and the silicon oxide layers 2.
As shown in
In this fashion, in the optical element 100, the major surface of the silicon substrate 10 is structured as stripes which run in the direction of the y-axis, and the high refractive index layers and the low refractive index layers are stacked one atop the other alternately in the predetermined periods. The optical element 100 therefore exhibits a polarization characteristic with respect to light which is along the direction of the z-axis.
It is preferable to set the periods P, the width WL and the height H of the convexes 11 as follows in
P<λ
0<WL≦k·P
0<H≦k·P
where the symbol λ denotes the wavelength of light and the symbol k denotes a coefficient. While the value k is 0.5 in this embodiment, the value k is preferably 0.3. Under the condition of k>0.5, the cavities 3 disappear as the number of the stacked layers increases, and the adjacent dielectric films on the convexes 11 become contiguous to each other and turn into a film which is continuous along the direction of the x-axis. Although such a structure exhibits a polarization characteristic, a polarization-dependent wavelength shift becomes small, and a quenching rate decreases.
In the optical element 100, with the periods (P) in the direction of the x-axis and the periods in the direction of the z-axis (film thickness t1, t2) controlled, a wavelength range which causes a photonic band gap (PBG) can be freely changed with respect to a TE wave and a TM wave contained in light along the direction of the z-axis.
A method of manufacturing the optical element 100 will now be briefly described. When the manufacturing method according to this embodiment is used, the silicon substrate 10 having a major surface is prepared. The silicon substrate 10 may be replaced with other semiconductor substrate of as GaAs or the like, a glass substrate of quartz, Pyrex (registered trademark) or the like, a substrate of a polymer material, etc.
The major surface of the silicon substrate 10 is then etched, thereby forming the stripe-shaped convexes 11 which are located in the predetermined periods.
At the step of forming the convexes 11, first, a resist pattern shaped as stripes which run in the direction of the y-axis at pitches of 0.4 μm is formed on the silicon substrate 10 at a photolithography step using EB exposure. Following this, through ECR etching using the resist pattern as an etching mask, a pattern as that shown in
Alternatively, isotropic etching such as wet etching may be executed after turning the striped pattern into a thermally oxidized film or a mask layer on the silicon substrate through ECR etching which uses the resist pattern as an etching mask while using the silicon substrate seating a thermally oxidized film or the silicon substrate on which a mask layer has been formed in advance, to thereby form convexes 13 as those shown in
Next, by a sputtering method, silicon particles and silicon oxide particles are deposited alternately on the major surface of the silicon substrate 10. The silicon layers 1 are formed by DC sputtering which uses silicon as a target, while the silicon oxide layers 2 are formed by RF sputtering which uses silicon oxide as a target.
During the sputtering, the direction of incidence of the sputter particles is the direction which is inclined at the predetermined angle with respect to the direction of the z-axis (vertical direction). To be more specific, the silicon substrate 10 is positioned approximately perpendicular to a substrate holder of a sputtering apparatus to thereby ensure that the sputter particles impinge at an angle upon the major surface of the silicon substrate 10.
As a result, the convexes 11 block some of the sputter particle thus impinging upon the major surface of the silicon substrate 10 (shadow effect), and the dielectric films accordingly fail to deposit on a part of the silicon substrate 10 and thus become the cavities 3.
Alternatively, a blocking plate (not shown) may be disposed between the sputter targets and the silicon substrate 10 and sputter particle components impinging upon the silicon substrate 10 from the direction of the z-axis (vertical direction) may be blocked. This prevents the adjacent dielectric layers from linking with each other.
As the silicon particles and the silicon oxide particles are supplied alternately, in the direction of incidence of these particles, that is, in the direction which is inclined with respect to the z-axis, the silicon layers 1 and the silicon oxide layers 2 are deposited. Further, during this, the cavities 3 are formed which run also in the direction which is inclined at the angle θ with respect to the z-axis.
Although silicon and silicon oxide are used as the materials of the dielectric layers which are formed on the convexes 11 in this embodiment, other materials may be used instead which are transparent to the wavelength which is used in the optical element 100. For example, semiconductor materials such as germanium and GaAs, oxides and nitrides such as TiO2, Ta2O5, SiN or the like may be used.
Through these steps, the optical element 100 is completed.
While the cavities 3 are formed between the adjacent dielectric layers (the silicon layers 1, the silicon oxide layers 2) in the optical element 100, when the angle of incidence of the sputter particles is appropriately selected, dielectric layers whose density is lower than those of the silicon layers 1 and the silicon oxide layers 2 can be formed instead of the cavities 3. In this structure, since the refractive index of the low density dielectric layers are also smaller than the refractive indexes of the silicon layers 1 and the silicon oxide layers 2, a similar effect to that obtained where the cavities 3 are formed is obtained.
In this manner, an optical element which exhibits an excellent polarization characteristic is obtained according to this embodiment.
Further, it is possible to fabricate a highly accurate optical element by a simple method as compared to conventional methods. In addition, it is possible to fabricate the optical element, using a general-purpose manufacturing apparatus. This realizes inexpensive manufacturing of optical elements at a high yield.
Second Preferred Embodiment
In the optical element 200, although a silicon substrate 20 is used which includes stripe-shaped concaves and convexes on a major surface as in the optical element 100 described above, the aspect ratios of the convexes 21 and the concaves 22 are higher than those in the optical element 100. The silicon layers 1 and the silicon oxide layers 2 are stacked three layers each, one atop the other on the convexes 21 approximately the direction of the z-axis.
In
The film thickness t1 and t2 of the silicon layers 1 and the silicon oxide layers 2 along the direction of the z-axis are 0.26 μm and 0.11 μm, respectively. Since the film thickness are set as such, a polarizing mirror used at the wavelength of 1.55 μm can be formed.
To prevent a variation in transmission characteristic which is called a “ripple,” the film thickness of only the top-most silicon oxide layer 2 is 0.35 μm.
While there are the cavities 3 on the concaves 22, as the number of the stacked layers increases, the widths of the silicon layers 1 and the silicon oxide layers 2 stacked on the convexes 21 become wider.
With the optical element 200, it is possible to obtain an excellent polarization characteristic.
A method of manufacturing the optical element 200 will now be briefly described. According to this manufacturing method, first, the silicon substrate 20 which includes a major surface is prepared. As in the first preferred embodiment, the silicon substrate 20 may be replaced with a semiconductor substrate, a glass substrate or the like.
The major surface of the silicon substrate 20 is then ECR-etched, whereby the stripe-shaped convexes 21 as those shown in
Next, using a sputtering method, the silicon particles and the silicon oxide particles are deposited alternately on the major surface of the silicon substrate 20. The silicon layers 1 are formed by DC sputtering which uses silicon as a target, while the silicon oxide layers 2 are formed by RF sputtering which uses silicon oxide as a target. However, unlike in the first preferred embodiment, the direction of incidence of the sputter particles needs not be a direction which is inclined at a particular angle, but may include such an inclined direction of incidence in which the shadow effect (inclined incident component) is obtained.
Since the aspect ratio (height/width) of the concaves 22 in particular is large in the silicon substrate 20, the convexes 21 block some of the sputter particle thus impinging upon the major surface of the silicon substrate 20 (shadow effect), and the volumes of the silicon layers 1 and the silicon oxide layers 2 deposited within the concaves 22 decrease. In consequence, as shown in
As the number of the stacked layers increases, the widths of the silicon layers 1 and the silicon oxide layers 2 deposited on the convexes 21 become gradually wider in the direction of the x-axis. However, since there are the cavities 3 formed on the concaves 22 in the optical element 200, the optical element 200 can exhibit a polarization characteristic along the direction of the z-axis.
In order to form the cavities 3 utilizing the shadow effect in this fashion, it is necessary that the width WG and height H of the concaves 22 satisfy the following relationship:
0.1WG≦H≦10WG
Further, in order to obtain an excellent polarization characteristic in the direction of the z-axis, it is preferable that the periods (pitches) of the convexes 21 (or the concaves 22) and the wavelength used μ satisfy the following relationship:
P≦λ
Alternatively, as in the first preferred embodiment, the materials of the dielectric layers formed on the convexes 21 may be other materials which are transparent to the wavelength which is used in the optical element 200.
Further, although there are the cavities 3 on the concaves 22 in the optical element 200, dielectric layers whose density is lower than those of the silicon layers 1 and the silicon oxide layers 2 may be formed.
Through these steps, the optical element 200 shown in
As described above, according to the second preferred embodiment, it is possible to obtain an optical element which exhibits an excellent polarization characteristic as in the first preferred embodiment. Further, it is possible to fabricate a highly accurate optical element by a simpler method than conventional methods. In addition, it is possible to fabricate an optical element using only a general-purpose manufacturing apparatus.
As is clear from the foregoing, it is possible to provide an optical element which is inexpensive, suitable to high-yield production and exhibits an excellent polarization characteristic, according to the present invention.