Optical fiber of high durability prepared from multicomponent glass

BACKGROUND OF THE INVENTION
This invention relates to a step-index type optical fiber for optical communication which is prepared from multicomponent glass.
This optical fiber is formed of core glass and cladding glass having a smaller refractive index than the core glass. Optical communication glass fiber is designed to conduct light information from one end to the other in a state completely enclosed in the core glass by utilizing the total reflection of light at the boundary between the core glass and cladding glass.
The above-mentioned type of optical fiber is demanded to meet the requirements listed below:
(1) Fiber, particularly cladding glass should have a high resistance to chemicals, such as water, acids, alkalis, and a high resistance to weathering, in other words, high durability.
(2) Neither core glass nor cladding glass should crystallize during manufacture. This requirement is indispensable.
(3) The core glass should minimize loss of light transmitted therethrough. Transmission loss of light should be smaller than 20 dB/km as measured from the whole fiber. Where fiber glass has a high melting point, impurities tend to be carried into the glass from, for example, a crucible. As a result, scattering of light undesirably arises in such defective glass, leading to higher transmission loss of light.
(4) The core glass should have a thermal expansion coefficient larger than that of the cladding glass by a difference .DELTA..alpha. of less than 3.times.10.sup.-6 cm/cm .degree. C. (at 0.degree. to 300.degree. C.). Where both thermal expansion coefficients have an unduly large difference, then the resultant fiber glass will decrease in reliability.
(5) The core glass should have a refractive index (n.sub.1) larger than that of the cladding glass (n.sub.2) by a larger ratio .DELTA.n (=n.sub.1 -n.sub.2 /n.sub.1) than 0.003.
Improvement on the known optical fiber has been primarily intended to decrease loss of light transmitted therethrough. It is reported that an optical fiber has been developed in which transmission loss of light is of the order of about 5 dB/km. Though favored by a small transmission loss of light, the optical fiber developed to date has the drawback that it is unsatisfactory in respect of resistance to chemicals and weathering. An optical fiber is generally demanded to have a long effective life. However, the above-mentioned prior art optical fiber, though improved in transmission loss of light, has insufficient durability and consequently low reliability, failing to be put into practical application.
A known multicomponent optical fiber favored by a low transmission loss of light is formed of a core glass member prepared from 20% by weight of Na.sub.2 O, 9% by weight of CaO and 71% by weight of SiO.sub.2 and a cladding glass member prepared from 22% by weight of Na.sub.2 O, 3.5% by weight of CaO and 74.5% by weight of SiO.sub.2. Though appreciably reduced in transmission loss of light, this optical fiber, particularly, the cladding glass member thereof contains a large amount of alkali. This alkali component tends to exude to the surface of the fiber and decrease its durability.
A step-index type optical fiber is generally manufactured by causing molten core glass and cladding glass simultaneously to flow downward respectively through the bottom openings of the inner and outer unit crucibles constituting a double crucible assembly, and later drawing both falling glass materials into a fine fibrous form. These core and cladding glass materials are preferred to have a viscosity ranging from 10.sup.5 to 10.sup.3 poises during the rundown through the bottom opening and subsequent drawing in the fibrous form. If the glass material crystallizes during the fibrous drawing, it gives rise to increased transmission loss of light and decreased tensile strength. Therefore, it is an indispensable requirement for the glass material to be saved from crystallization during the fibrous drawing.
SUMMARY OF THE INVENTION
It is accordingly an object of this invention to provide an optical fiber capable of meeting all the aforesaid requirements.
Another object of the invention is to provide an optical fiber characterized by small transmission loss of light and high durability.
To attain the above-mentioned objects, this invention provides an optical fiber, whose core glass member is prepared from 50 to 80% by weight or preferably 60 to 80% by weight of SiO.sub.2, 0.5 to 7% by weight of Al.sub.2 O.sub.3, 10 to 23% by weight of an alkali metal oxide, 0 to 10% by weight of CaO, 0 to 5% by weight of MgO and 0 to 15% by weight of B.sub.2 O.sub.3 ; and whose cladding member is formed of 60 to 80% by weight of SiO.sub.2, 0.5 to 10% weight of Al.sub.2 O.sub.3, 9 to 17% weight of an alkali metal oxide, 0 to 5% by weight of CaO, 0 to 4% by weight of MgO, 0 to 15% by weight of B.sub.2 O.sub.3 and 7% by weight or less of at least one component selected from the group consisting of ZnO, ZrO.sub.2 and TiO.sub.2.
An optical fiber according to a preferred embodiment of this invention consists of a core glass member prepared from 65 to 75% by weight of SiO.sub.2, 1 to 6% by weight of Al.sub.2 O.sub.3, 12 to 21% by weight of an alkali metal oxide, 2 to 10% by weight of CaO and 1 to 5% by weight of MgO; and a cladding glass member formed of 65 to 75% by weight of SiO.sub.2, 2 to 8% by weight of Al.sub.2 O.sub.3, 9 to 16% by weight of an alkali metal oxide, 0 to 5% by weight of CaO, 0 to 3% by weight of MgO, 1 to 12% by weight of B.sub.2 O.sub.3 and 0.5 to 3% by weight of at least one component selected from the group consisting of ZnO, ZrO.sub.2 and TiO.sub.2.
An optical fiber according to a more preferred embodiment of this invention consists of a core glass member prepared from 55 to 70% by weight of SiO.sub.2, 1 to 6% by weight of Al.sub.2 O.sub.3, 14 to 21% by weight of an alkali metal oxide, 2 to 8% by weight of CaO, 1 to 4% by weight of MgO and 3 to 12% by weight of B.sub.2 O.sub.3 ; and a cladding glass member formed of 65 to 75% by weight of SiO.sub.2, 2 to 8% by weight of Al.sub.2 O.sub.3, 9 to 16% by weight of an alkali metal oxide, 0 to 5% by weight of CaO, 0 to 3% by weight of MgO, 1 to 12% by weight of B.sub.2 O.sub.3 and 0.5 to 3% by weight of at least one component selected from the group consisting of ZnO, ZrO.sub.2 and TiO.sub.2.
DETAILED DESCRIPTION OF THE INVENTION
For the core glass member of this invention, SiO.sub.2, Al.sub.2 O.sub.3 and alkali metal oxide are indispensable ingredients. An optical fiber embodying this invention meets the requirements to minimize scattering of light and transmission loss of light and is also improved in resistance to chemicals due to the addtion of a proper amount of Al.sub.2 O.sub.3. CaO, MgO and B.sub.2 O.sub.3 may be omitted from the core glass member.
There will now be described the chemical composition of a core glass member included in an optical fiber embodying this invention.
(1) SiO.sub.2 is a network former of fiber glass. Where the content of SiO.sub.2 falls below 50% by weight, the resultant glass decreases in resistance to water. Where the content of SiO.sub.2 rises above 80% by weight, the resultant glass fails to have a desired large refractive index. For elevation of resistance to water, it is preferred to use more than 60% by weight of SiO.sub.2. Part of SiO.sub.2 may be replaced by GeO.sub.2 to control the viscosity of a core glass member at a temperature of fibrous drawing. In this case, however, the content of GeO.sub.2 is restricted to 30% at maximum (at this time the content of SiO.sub.2 ranges between 20 and 50% by weight). Where the content of GeO.sub.2 increases over said maximum level, the viscosity of the core glass at a temperature of fibrous drawing excessively falls, presenting difficulties in the fibrous drawing of the resultant core glass.
(29 Al.sub.2 O.sub.3 is an important ingredient to elevate the water resistance of glass and minimize its tendency toward crystallization. A smaller content of Al.sub.2 O.sub.3 than 0.5% by weight can not provide glass having a high resistance to water and a small tendency toward crystallization. Where, however, the content of Al.sub.2 O.sub.3 exceeds 7% by weight, then the core glass is ready to crystallize during the fibrous drawing. The content of Al.sub.2 O in the core glass member is preferred to range between 1 and 6% by weight.
(3) Alkali metal oxides used with an optical fiber embodying this invention chiefly include Na.sub.2 O, K.sub.2 O and Li.sub.2 O. It will well serve the purpose, if the glass contains at least one of these components or a mixture thereof. The alkali metal oxide is a glass network modifier. As the alkali metal oxide is used in a larger amount, the resultant glass tends to have a lower resistance to wear. An upper limit to the content of an alkali metal oxide in the core glass is chosen to be 23% by weight. Where, however, the content of an alkali metal oxide falls below 10% by weight, then the core glass tends to crystallize during the fibrous drawing. Therefore, the content of an alkali metal oxide in the core glass is preferred to range between 12% and 21% by weight. The percentage of the above mentioned Na.sub.2 O, K.sub.2 O and Li.sub.2 O can be properly adjusted within said range, depending on the property demanded of the core glass.
Where it is desired to decrease, for example, the viscosity of the core glass at a temperature of fibrous drawing, it is advised to reduce the percentage of K.sub.2 O. Where the core glass is desired to have a higher thermal expansion coefficient, then Li.sub.2 O is applied in a larger amount. Where the core glass is desired to have a higher refractive index, then Li.sub.2 O is applied similarly in an increased percentage.
(4) CaO contributes to the elevation of the water resistance and refractive index of glass. Where, however, CaO is contained in a larger amount than 10% by weight, the resultant glass is likely to crystallize. The content of CaO in the core glass is preferred to range between 2 and 10% by weight.
(5) MgO restricts the occurrence of haze in glass resulting from exudation of alkali components, and consequently improves resistance to weathering. Where, however, the content of MgO increases over 5% by weight, the resultant glass is ready to crystallize. The content of MgO in the core glass is preferred to range from 1 to 5% by weight.
(6) B.sub.2 O.sub.3 is effective to prevent glass from crystallization and decreasing in viscosity at high temperature. Where, however, the content of B.sub.2 O.sub.3 increases over 15% by weight, the resultant glass unduly drops in viscosity at a temperature of fibrous drawing, presenting difficultiesin carrying out said fibrous drawing. Where the content of B.sub.2 O.sub.3 in the core glass favorably ranges between 3 and 12% by weight, then the resultant core glass is saved from crystallization, making it possible to manufacture an optical fiber with a high reproducibility.
For the cladding glass member of this invention, it is indispensable to use SiO.sub.2, Al.sub.2 O.sub.3, alkali metal oxide and at least one component selected from the group consisting of ZnO, ZrO.sub.2 and TiO.sub.2. It is possible to omit CaO, MgO and B.sub.2 O.sub.3. To let the cladding glass member have a higher durability than the core glass member, the content of an alkali metal oxide is more restricted. Further, the cladding glass member is made to contain Al.sub.2 O.sub.3 and at least one component selected from the group consisting of ZnO, ZrO.sub.2 and TiO.sub.2.
There will now be described the respective ingredients of the cladding glass member.
(1) SiO.sub.2 is network formerof fiber glass. Where the content of SiO.sub.2 falls below 60% by weight, then the resultant cladding glass decreases in resistance to water. Where the content of SiO.sub.2 rises above 80% by weight, then the resultant cladding glass has an increased viscosity at high temperature, undesirably showing a larger viscosity difference between the core glass and the cladding glass. The content of SiO.sub.2 in the cladding glass is preferred to range between 65 and 75% by weight.
(2) Al.sub.2 O.sub.3 is effective to elevate the water resistance of the cladding glass and minimize its tendency toward crystallization. Where Al.sub.2 O.sub.3 is applied in a smaller amount than 0.5% by weight, the resultant cladding glass fails to have a satisfactory property. Conversely, where the content of Al.sub.2 O.sub.3 exceeds 10% by weight, then the resultant cladding glass tends to crystallize during the fibrous drawing. The content of Al.sub.2 O.sub.3 in the cladding glass is preferred to range between 2 and 8% by weight.
(3) Alkali metal oxides chiefly includeNa.sub.2 O, K.sub.2 O and Li.sub.2 O. It will well serve the purpose, if the cladding glass contains at least one of these components, or a mixture thereof. Since the cladding glass is demanded to have a higher durability than the core glass, the content of an alkali metal oxide in the cladding glass is controlled to be smaller than when applied in the core glass. It has been discovered that where the content of an alkali metal oxide rises above 17% by weight, the resultant cladding glass fails to have a sufficient resistance to water, and that where said content falls below 9% by weight, the resultant cladding glass is ready to crystallize during the fibrous drawing. The content of an alkali metal oxide is preferred to range between 9 and 16% by weight.
(4) CaO contributed to the elevation of the water resistance of the cladding glass. Where, however, CaO is used in a larger amount than 5% by weight, then the resultant cladding glass is likely to crystallize.
(5) MgO is effective to suppress the occurrence of haze in the cladding glass and elevate its resistance to weathering. Where, however, the content MgO increases over 4% by weight, the resultant cladding glass is ready to crystallize. The content of MgO in the cladding glass is preferred to range between 0 and 3% by weight.
(6) B.sub.2 O.sub.3 contributes to the elevation of water resistance of the cladding glass and its refractive index. Where, however, the content of B.sub.2 O.sub.3 exceeds 15% by weight, then the resulting cladding glass has too high a refractive index.
The content of B.sub.2 O.sub.3 is preferred to range between 1 and 12% by weight.
(7) Even a minute amount of ZnO, ZrO.sub.2 and TiO.sub.2 is very effective to increase the water resistance of the cladding glass. Where, however, the content of any of these components increases over 7%, then striae tend to be grown in the resultant cladding glass. The content of any of said oxides favorably falling within the range of 0.5 to 3% by weight is sufficiently effective to increase the water resistance of the resultant cladding glass.
An optical fiber embodying this invention can be manufactured by the ordinary spinning process such as the double crucible process, and rod-in-tube process. For example, where core glass and cladding glass are simultaneously drawn in the fibrous form by the double crucible process with temperature controlled to a level falling within the range of 800.degree. to 1100.degree. C. to ensure the proper viscosity of both glass materials, then it is possible to prepare an optical fiber from multicomponent glass, whose core glass member has a diameter of 80 microns and whose cladding glass memberhas a diameter of 150 microns.

There are shown in the following table some concrete examples of the compositions of core glass and cladding glass constituting optical fibers embodying this invention and those falling outside of the scope of the invention, and also the properties of the core glass members and cladding glass members. Resistance to water, resistance to weathering and tendency toward loss of transparence given in the following table were determined by the undermentioned tests.
(1) Resistance to water
5.0 g of the respective powder samples of the core and cladding glass materials which passed through the standard JIS (Japanese Industrial Standards) screen having 0.5 mm meshes but did not pass through the standard JIS screen having 0.3 mm meshes were dipped in distilled water of 100 ml. Each sample was heated one hour in a bath of boiling distilled water. Thereafter the distilled water was titrated with a 0.01 N HCl solution. An amount (ml) of the 0.01 N HCl solution required for titration is given in the row of the following table showing resistance to wear. With the prior art optical fiber prepared from multicomponent glass, even the cladding glass member which was demanded to have good resistance to wear gave rise to the prominent exudation of an alkali metal. Therefore, the above-mentioned 0.01 N HCl titration solution was used in as large an amount as scores of milliliters.
(2) Resistance to weathering
Haze produced on the surface of tested glass samples was measured by a hazemeter. Comparison was made between the tested glass samples and a standard optical glass specimen SK-16 with respect to the development of haze. The haze conditions of the tested glass samples were indicated by the following equation marks.
______________________________________Less liable to develop haze than SK-16 AAs ready to produce haze as SK-16 ABMore likely to develop haze thanSK-16 B(3) Tendency toward crystallization______________________________________
The tendency of tested glass samples toward crystallization was observed when heated 15 hours in an oven at 800.degree. C. and also when heated 15 hours in an oven at 1100.degree. C. The tendencies of the tested glass samples were indicated by the following evaluation marks.
______________________________________Completely saved from crystallization aLiable to indicate crystallizationon the surface bTendensy to show crystallization con the outside and in the inside______________________________________
Since complete freedom from crystallization is an indispensable requirement for an optical fiber, the tested glass samples whose tendency toward crystallization was indicated by the other evaluation marks than the above-mentioned mark a were considered as falling outside of the scope of this invention. An optical fiber prepared from the glass sample indicated by the evaluation mark a did not crystallize.
______________________________________ Example Example 1 Example 2 Clad- Clad-Composition Core ding Core dingand Properties glass glass glass glass______________________________________SiO.sub.2 (wt %) 78.5 79.5 77 78.0GeO.sub.2 (wt %) -- -- -- --Al.sub.2 O.sub.3 (wt %) 0.5 0.5 3 2.0Na.sub.2 O (wt %) 8 10 13 10Li.sub.2 O (wt %) 8 2 7 4K.sub.2 O (wt %) 5 4 -- 3CaO (wt %) -- -- -- --MgO (wt %) -- -- -- --B.sub.2 O.sub.3 (wt %) -- -- -- --ZnO (wt %) -- 2 -- 2ZrO.sub.2 (wt %) -- 1 -- 1TiO.sub.2 (wt %) -- 1 -- --Refractive index n 1.5170 1.5110 1.5170 1.5120Thermal expansion coefficient(.alpha. .times. 10.sup.-7) 110 95 111 100Resistance to water (ml) 24.5 2.8 24.3 4.1Resistance to weathering AB AB AB ABTemperature (.degree.C.) for viscosityof 10.sup.4 poises 930 1046 910 1043Temperature (.degree.C.) for viscosityof 10.sup.5 poises 821 903 801 899Temperature (.degree.C.) for viscosityof 10.sup.6 poises 732 793 708 789Tendencytoward crystallization(800.degree. C., 15hr) a a a aTendencytoward crystallization(1100.degree. C., 15hr) a a a a______________________________________ Example Example 3 Example 4 Clad- Clad-Composition Core ding Core dingand Properties glass glass glass glass______________________________________SiO.sub.2 (wt %) 77 78.5 77 78GeO.sub.2 (wt %) -- -- -- --Al.sub.2 O.sub.3 (wt %) 3 5 3 3Na.sub.2 O (wt %) 13 10 13 12Li.sub.2 O (wt %) 7 3 7 4K.sub.2 O (wt %) -- 3 -- --CaO (wt %) -- -- -- --MgO (wt %) -- -- -- --B.sub.2 O.sub.3 (wt %) -- -- -- --ZnO (wt %) -- -- -- 2ZrO.sub.2 (wt %) -- 0.5 -- 1TiO.sub.2 (wt %) -- -- -- --Refractive index n 1.5170 1.5040 1.5170 1.5110Thermal expansion coefficient(.alpha. .times. 10.sup.-7) 111 97 111 98Resistance to water (ml) 24.3 4.3 24.3 1.5Resistance to weathering AB AB AB ABTemperature (.degree.C.) for viscosityof 10.sup.4 poises 910 1056 910 1027Temperature (.degree.C.) for viscosityof 10.sup.5 poises 801 915 801 878Temperature (.degree.C.) for viscosityof 10.sup.6 poises 708 809 708 770Tendencytoward crystallization(800.degree. C., 15hr) a a a aTendencytoward crystallization(1100.degree. C., 15hr) a a a a______________________________________ Example Example 5 Example 6 Clad- Clad-Composition Core ding Core dingand Properties glass glass glass glass______________________________________SiO.sub.2 (wt %) 76 78.5 74 72.5GeO.sub.2 (wt %) -- -- -- --Al.sub.2 O.sub.3 (wt %) 2 6 2 5Na.sub.2 O (wt %) 3 6 10 7.5Li.sub.2 O (wt %) 7 3 3 3K.sub.2 O (wt %) 2 -- 2 5CaO (wt %) 6 5 6 3MgO (wt %) 4 -- 3 2B.sub.2 O.sub.3 (wt %) -- -- -- --ZnO (wt %) -- 1 -- 2.0ZrO.sub.2 (wt %) -- -- -- --TiO.sub.2 (wt %) -- 0.5 -- --Refractive index n 1.5149 1.4998 1.5139 1.5070Thermal expansion coefficient(.alpha. .times. 10.sup.-7) 101 92 101 93Resistance to water (ml) 0.8 0.1 1.9 0.7Resistance to weathering A AB A ATemperature (.degree.C.) for viscosityof 10.sup.4 poises 1081 1180 1038 1051Temperature (.degree.C.) for viscosityof 10.sup.5 poises 941 1041 904 912Temperature (.degree.C.) for viscosityof 10.sup.6 poises 834 932 799 798Tendencytoward crystallization(800.degree. C., 15hr) a a a aTendencytoward crystallization(1100.degree. C., 15hr) a a a a______________________________________ Example Example 7 Example 8 Clad- Clad-Composition Core ding Core dingand Properties glass glass glass glass______________________________________SiO.sub.2 (wt %) 77.6 72.5 61.5 65GeO.sub.2 (wt %) -- -- -- --Al.sub.2 O.sub.3 (wt %) 2 5 6 7Na.sub.2 O (wt %) 6 7.5 7 8Li.sub.2 O (wt %) 4 1 7 2K.sub.2 O (wt %) 5 7 7 6CaO (wt %) 2.5 4 8.5 4.5MgO (wt %) 2.9 -- 3 2B.sub.2 O.sub.3 (wt %) -- 1 -- 3.5ZnO (wt %) -- -- -- 2.0ZrO.sub.2 (wt %) -- 2 -- --TiO.sub.2 (wt %) -- -- -- --Refractive index n 1.5100 1.5038 1.5318 1.5074Thermal expansion coefficient(.alpha. .times. 10.sup.-7) 99 94 122 101Resistance to water (ml) 1.5 1.1 26.2 0.7Resistance to weathering A AB A ATemperature (.degree.C.) for viscosityof 10.sup.4 poises 1088 1087 959 1049Temperature (.degree.C.) for viscosityof 10.sup.5 poises 944 942 831 904Temperature (.degree.C.) for viscosityof 10.sup.6 poises 821 817 729 788Tendencytoward crystallization(800.degree. C., 15hr) a a a aTendencytoward crystallization(1100.degree. C., 15hr) a a a a______________________________________ Example Example 9 Example 10 Clad- Clad-Composition Core ding Core dingand Properties glass glass glass glass______________________________________SiO.sub.2 (wt %) 59.5 71.5 59 76.5GeO.sub.2 (wt %) -- -- -- --Al.sub.2 O.sub.3 (wt %) 2 5 5.5 2Na.sub.2 O (wt %) 14.9 7.5 9 5Li.sub.2 O (wt %) 2 3 1 2K.sub.2 O (wt %) 2.7 5 8 9CaO (wt %) 6.6 3 8.5 3MgO (wt %) 2.5 2 1 1B.sub.2 O.sub.3 (wt %) 9.8 2 8 --ZnO (wt %) -- 1 -- --ZrO.sub.2 (wt %) -- -- -- 1.5TiO.sub.2 (wt %) -- -- -- --Refractive index n 1.5358 1.5100 1.5432 1.5034Thermal expansion coefficient(.alpha. .times. 10.sup.-7) 110 94 118 96Resistance to water (ml) 4.8 0.8 3.7 0.8Resistance to weathering A A A ATemperature (.degree.C.) for viscosityof 10.sup.4 poises 818 990 1025 1044Temperature (.degree.C.) for viscosityof 10.sup.5 poises 741 860 884 904Temperature (.degree.C.) for viscosityof 10.sup.6 poises 678 760 761 790Tendencytoward crystallization(800.degree. C., 15hr) a a a aTendencytoward crystallization(1100.degree. C., 15hr) a a a a______________________________________ Example Example 11 Example 12 Clad- Clad-Composition Core ding Core dingand Properties glass glass glass glass______________________________________SiO.sub.2 (wt %) 68 65 65 72.5GeO.sub.2 (wt %) -- -- -- --Al.sub.2 O.sub.3 (wt %) 4.5 7 2 5Na.sub.2 O (wt %) 8 8 7 7.5Li.sub.2 O (wt %) -- 2 1 1K.sub.2 O (wt %) 10 6 7 7CaO (wt %) 5 4.5 8 4MgO (wt %) -- 2 -- --B.sub.2 O.sub.3 (wt %) 4.5 3.5 10 1ZnO (wt %) -- -- -- --ZrO.sub.2 (wt %) -- -- -- 2TiO.sub.2 (wt %) -- 2.0 -- --Refractive index n 1.5379 1.5074 1.5331 1.5038Thermal expansion coefficient(.alpha. .times. 10.sup.-7) 102 101 99 94Resistance to water (ml) 3.4 0.7 1.5 1.1Resistance to weathering AB A AB ABTemperature (.degree.C.) for viscosityof 10.sup.4 poises 1033 1049 1092 1087Temperature (.degree.C.) for viscosityof 10.sup.5 poises 891 904 950 942Temperature (.degree.C.) for viscosityof 10.sup.6 poises 773 788 827 817Tendencytoward crystallization(800.degree. C., 15hr) a a a aTendencytoward crystallization(1100.degree. C., 15hr) a a a a______________________________________ Example Example 13 Example 14 Clad- Clad-Composition Core ding Core dingand Properties glass glass glass glass______________________________________SiO.sub.2 (wt %) 64.5 66.5 65 72.5GeO.sub.2 (wt %) -- -- -- --Al.sub.2 O.sub.3 (wt %) 5.5 7 2.0 5Na.sub.2 O (wt %) 2 6 13 7.5Li.sub.2 O (wt %) 2 4 2 3K.sub.2 O (wt %) 10 3 2 5CaO (wt %) 4 4.5 8 3MgO (wt %) 2 2 1 2B.sub.2 O.sub.3 (wt %) 10 6 7 --ZnO (wt %) -- -- -- 2ZrO.sub.2 (wt %) -- -- -- --TiO.sub.2 (wt %) -- 1 -- --Refractive index n 1.5330 1.5070 1.5416 1.5070Thermal expansion coefficient(.alpha. .times. 10.sup.-7) 98 91 116 93Resistance to water (ml) 1.1 2.1 2.1 0.7Resistance to weathering A A A ATemperature (.degree.C.) for viscosityof 10.sup.4 poises 1099 1124 1046 1051Temperature (.degree.C.) for viscosityof 10.sup.5 poises 967 990 911 912Temperature (.degree.C.) for viscosityof 10.sup.6 poises 841 857 789 798Tendencytoward crystallization(800.degree. C., 15hr) a a a aTendencytoward crystallization(1100.degree. C., 15hr) a a a a______________________________________ Example Example 15 Example 16 Clad- Clad-Composition Core ding Core dingand Properties glass glass glass glass______________________________________SiO.sub.2 (wt %) 65 67.5 68.5 68.0GeO.sub.2 (wt %) -- -- -- --Al.sub.2 O.sub.3 (wt %) 3 5 2 6.0Na.sub.2 O (wt %) 10 7.5 15.2 7.4Li.sub.2 O (wt %) 1 3 4.8 3.0K.sub.2 O (wt %) 6 6.5 -- 4.7CaO (wt %) 6 4 6.7 --MgO (wt %) 2 -- 2.8 0.5B.sub.2 O.sub.3 (wt %) 7 1.5 -- 8.4ZnO (wt %) -- -- -- 2.0ZrO.sub.2 (wt %) -- 5.0 -- --TiO.sub.2 (wt %) -- -- -- --Refractive index n 1.5389 1.5183 1.5275 1.5144Thermal expansion coefficient(.alpha. .times. 10.sup.-7) 113 96 118 93Resistance to water (ml) 1.7 1.0 24.1 1.0Resistance to weathering A AB A ATemperature (.degree.C.) for viscosityof 10.sup. 4 poises 1069 1029 880 920Temperature (.degree.C.) for viscosityof 10.sup.5 poises 921 886 771 820Temperature (.degree.C.) for viscosityof 10.sup.6 poises 801 767 682 730Tendencytoward crystallization(800.degree. C., 15hr) a a a aTendencytoward crystallization(1100.degree. C., 15hr) a a a a______________________________________ Example Example 17 Clad-Composition Core dingand Properties glass glass______________________________________SiO.sub.2 (wt %) 59.5 68.0GeO.sub.2 (wt %) -- --Al.sub.2 O.sub.3 (wt %) 2 6.0Na.sub.2 O (wt %) 14.9 7.4Li.sub.2 O (wt %) 2 3.0K.sub.2 O (wt %) 2.7 4.7CaO (wt %) 6.6 --MgO (wt %) 2.5 0.5B.sub.2 O.sub.3 (wt %) 9.8 8.4ZnO (wt %) -- 2.0ZrO.sub.2 (wt %) -- --TiO.sub.2 (wt %) -- --Refractive index n 1.5358 1.5144Thermal expansion coefficient(.alpha. .times. 10.sup.-7) 110 93Resistance to water (ml) 4.8 1.0Resistance to weathering A ATemperature (.degree.C.) for viscosityof 10.sup.4 poises 818 920Temperature (.degree.C.) for viscosityof 10.sup.5 poises 741 820Temperature (.degree.C.) for viscosityof 10.sup.6 poises 678 730Tendencytoward crystallization(800.degree. C., 15hr) a aTendencytoward crystallization(1100.degree. C., 15hr) a a______________________________________ Example Control 1 Control 2 Clad- Clad-Composition Core ding Core dingand Properties glass glass glass glass______________________________________SiO.sub.2 (wt %) 66.7 72.5 68.5 73GeO.sub.2 (wt %) 5 -- -- --Al.sub.2 O.sub.3 (wt %) 0.3 5 2 3Na.sub.2 O (wt %) 5 7.5 15.2 17Li.sub.2 O (wt %) 3 1 4.8 3K.sub.2 O (wt %) 4 7 -- --CaO (wt %) 3 4 6.7 3MgO (wt %) 1 3 2.8 1B.sub.2 O.sub.3 (wt %) 12 -- -- --ZnO (wt %) -- -- -- --ZrO.sub.2 (wt %) -- -- -- --TiO.sub.2 (wt %) -- -- -- --Refractive index n 1.5324 1.5101 1.5275 1.5121Thermal expansion coefficient(.alpha. .times. 10.sup.-7) 96 95 118 111Resistance to water (ml) 0.9 3.8 24.1 18.4Resistance to weathering A A A ATemperature (.degree.C.) for viscosityof 10.sup.4 poises 1109 1075 880 850Temperature (.degree.C.) for viscosityof 10.sup.5 poises 968 931 771 761Temperature (.degree.C.) for viscosityof 10.sup.6 poises 854 820 682 680Tendencytoward crystallization(800.degree. C., 15hr) b a a aTendencytoward crystallization(1100.degree. C., 15hr) b a a a______________________________________
As mentioned above, the optical fiber of this invention prepared from multicomponent glass, particularly, the cladding glass member thereof gives rise to very little exudation of alkali metal, and consequently has a high resistance to chemicals such as resistance to water and a high resistance to weathering. In contrast, Control 2 in which the cladding glass contains an unduly large amount of an alkali metal oxide was proved to have a lower resistance to water than the optical fiber of this invention. Further, this invention prevents glass from crystallization during fibrous drawing, and provides with a high reproducibility an optical fiber which has a prominent dimensional stability, is free from the occurrence of striae, and allows for easy fibrous drawing. In contrast, Control 1 which contains too little Al.sub.2 O.sub.3 undesirably indicates a strong tendency toward crystallization. The optical fiber of the invention has as low a transmission loss of light as 5 to 10 dB/km with respect to light beams having a wavelength of 850 millimicrons. Further, with the product of the invention, the core glass has a thermal expansion coefficient larger than that of the gladding glass by a difference .DELTA..alpha. of less than 3.times.10.sup.-6 cm/cm..degree. C. (at 0.degree. to 300.degree. C.). The core glass of the present optical fiber has a refractive index (n.sub.1) larger than that of the cladding glass (n.sub.2) by a larger ratio .DELTA.n (=n.sub.1 -n.sub.2 /n.sub.1) than 0.003. The optical fiber of the invention having the above-mentioned excellent properties displays a high reliability and prominent practical effect.

Number	Name	Date
3013888	Lajarte	Dec 1961
3841882	Wolf	Oct 1974
3844801	Wolf	Oct 1974

Number	Date	Country
48-17814	Jun 1973	JPX
51-14915	May 1976	JPX

Optical fiber of high durability prepared from multicomponent glass

Information

Patent Number

Date Filed

Date Issued

Inventors

Original Assignees

Examiners

Agents

CPC

US Classifications

Field of Search

US

International Classifications

Abstract

Description

Claims

Priority Claims (1)

US Referenced Citations (3)

Foreign Referenced Citations (2)

Non-Patent Literature Citations (1)