Patent Application
20070258685
1. Technical Field
This invention relates to optical fiber tape cores in each of which plural optical fiber cores two-dimensionally arranged in parallel with each other are united together in the form of a tape with a coating layer, and also to their fabrication process.
2. Background Art
Optical fiber tape cores each of which is formed of a bundle of plural optical fiber cores united together are known for many years. Owing to the merit that a number of optical fibers can be connected all together, these optical fiber tape cores are widely used as optical transmission media in optical communications systems as a result of the rapid introduction of optical fiber cables in subscribers' systems in recent years.
An optical fiber tape core is required to have higher separability into single cores and higher strength, and active research and development work is under way in various companies. To provide optical fiber cores with both strength and separability into single cores, it is the common practice to form a coating layer in a two-layer construction—one being a primary coating layer uniting plural optical fiber cores together and the other a secondary coating layer uniting together such multi-core units covered with such primary coating layers, respectively—and to form the primary and secondary coating layers with UV curable resins different in strength and hardness.
In general, optical fiber tape cores coated with such UV curable resins are fabricated using acrylic materials. The resulting optical fiber tape cores are, however, accompanied by a problem in that they are not sufficient in hardness, durability and flexibility and tend to become loose or break, for example, when twisted. Concerning flexibility, on the other hand, these optical fiber tape cores also involve a problem in that they are extremely weak to bending in the direction of the cores and becomes loose or break although they have durability to folding.
Further, optical fiber tape cores coated with general UV curable resins are also accompanied by a further problem in that they are poor in shape restorability due to their plasticity attributable to the materials and, when wound on bobbins or the like upon storage, they continue to retain a wound shape, in other words, they develop curling and in actual work, for example, upon conducting connection to connectors or the like or performing installation work, this retention of a wound shape (curling) makes it difficult to handle them, resulting in poor workability.
Turning now to a process for the fabrication of optical fiber tape cores, the conventional fabrication of an optical fiber tape core has been conducted generally by the facilities illustrated in
According to this process, however, it is necessary to keep the interior of the coating jig always filled with the coating material, leading to a problem that the material is wasted. This problem involves another problem in that to change the thickness and/or width of an optical fiber tape, a new coating jig equipped with a different hole for feeding optical fiber cores therethrough is needed, thereby making it difficult to readily change the thickness and/or width of the optical fiber tape.
In the above-described process, it is also necessary to feed plural optical fiber cores, which are before their formation into a tape and are single cores in a loose state, through the aligner 17 while aligning them with each other and then to insert them into the very small holes (18a and 18c) of the coating jig 18. This setting of the optical fiber cores is troublesome and time-consuming, leading to a reduction in work efficiency. With respect to a demand for the fabrication of a short-distance optical fiber tape core or the formation of an optical fiber tape core into a tape only at a necessary position, the fabrication facilities are difficult to meet such a demand because the distance from the core feeder 16 to the curing unit 19 is long and fabrication conditions such as the coat thickness do not become constant shortly after an initiation of fabrication.
When fabricating a short-distance optical fiber tape core, forming an optical fiber tape core into a tape only at a necessary position or reinforcing an optical fiber tape core only at a part thereof, it is strongly required to provide the optical fiber tape core with a thicker coating layer, a wider coating layer or the like especially from the standpoint of protection of the optical fibers to be wired within a system. However, the above-described conventional process can by no means meet or is difficult to meet these requirements.
From the standpoint of protecting optical fibers drawn out of optical connectors or an optical component, it is strongly required to form them into a tape. The above-described process is, however, accompanied by a problem in that the tape formation can be hardly effected. The above-described process involves a further problem in that, when optical fibers are wired in a very narrow place, it cannot effect the tape formation.
The present invention has been completed to resolve such problems of the conventional technology as described above. Specifically, an object of the present invention is to provide an optical fiber tape core, which has excellent strength and good flexibility and hardly retains a wound shape (curling).
Another object of the present invention is to provide a process for the fabrication of an optical fiber tape core, which can coat plural optical fiber cores all together in a simple manner. A further object of the present invention is to provide a process for the fabrication of an optical fiber tape core, which can feed a coating material to optical fiber cores only as much as required, can feed a coating material even when the area to be coated extends over a short distance or is partial, can feed a coating material even when optical fiber cores to be coated are wired in a very narrow place, or can feed a coating material to optical fiber cores to form it into a tape while controlling the thickness and/or width of the coating of the tape. A still further object of the present invention is to provide a process for the fabrication of an optical fiber tape core, which can simplify the setting of plural optical fiber cores, can apply a coating over a short distance or on a partial area without wasting a coating material, or can also form into a tape plural optical fiber cores provided at one ends or both ends thereof with optical components such as optical connectors.
An optical fiber tape core according to the present invention comprises an optical fiber core assembly with plural optical fiber cores two-dimensionally arranged in parallel with each other and a coating layer formed of silicone rubber and arranged on at least one side of the optical fiber core assembly. In the optical fiber tape core according to the present invention, the silicone rubber forming the coating layer can preferably have a hardness of from 20 to 90 and a tensile strength of from 15 to 80 kgf/cm2.
In the present invention, the optical fiber core assembly may be provided on both upper and lower sides thereof with coating layers formed of the silicone rubber, and may also be provided on side walls thereof with additional coating layers formed of the silicone rubber. These coating layers can bring about further improvements in strength.
The term “hardness” as used herein means “durometer hardness” as measured following the procedure prescribed in JIS K6253. Specifically, the term (“hardness” means a value measured by preparing a specimen 6 mm thick of silicone rubber, pressing a needle of a Type A durometer against the specimen without any impact from a point right above an upper surface of the specimen, and reading graduations. A durometer is a testing machine for determining a hardness from a penetration depth of a needle when the needle is pressed by means of a spring.
On the other hand, the term “tensile strength” as used herein means “tensile strength at break” as measured following the procedure prescribed in JIS K6251. Specifically, the term “tensile strength” means a value [kgf/cm2] calculated by preparing a JIS No. 2 dumbbell-shaped specimen about 2 mm thick of silicone rubber, pulling the specimen at a pulling speed of 500 mm/min, and dividing a load value, when the specimen was broken, by a cross-sectional area of the specimen.
The optical fiber tape core according to the present invention can also be characterized in the use of a silicone rubber material, which has the above-described hardness and tensile strength, as a coating material, and owing to the excellent shape restorability of the silicone rubber, is extremely good in workability and handling without developing curling or retaining a wound shape even when wound on a bobbin or the like.
A process according to the present invention for the fabrication of an optical fiber tape core is a process for fabricating the optical fiber tape core by coating plural optical fiber cores all together, and in a first embodiment thereof, comprises bringing at least one nozzle close to the surfaces of the plural optical fibers aligned in parallel with each other on a two-dimensional flat surface; and then, while delivering silicone rubber from the nozzle, causing the nozzle to undergo a relative movement in a direction of axes of the optical fibers such that the plural optical fibers are coated all together to form a coating layer.
The process according to the present invention for the fabrication of the optical fiber tape core comprises, in a second embodiment thereof, applying silicone rubber onto the plural optical fiber cores arranged on a two-dimensional flat surface; and with a shaping jig having a shaping groove and being arranged such that the plural optical fiber cores are located in the shaping groove or are located underneath in proximity of the shaping groove, causing the forming jig to undergo a relative movement in a direction of axes of the optical fiber cores such that the silicone rubber is shaped to form a coating layer.
The process according to the present invention for the fabrication of the optical fiber tape core comprises, in a third embodiment thereof, arranging the optical fiber cores on a two-dimensional flat surface; and with a shaping jig having a shaping groove provided with a through-hole for feeding silicone rubber and being arranged such that the plural optical fiber cores are located in the shaping groove or are located underneath in proximity of the shaping groove, causing the shaping jig to undergo a relative movement in a direction of axes of the optical fiber cores such that with the silicone rubber fed into the shaping groove from the through-hole, the optical fiber cores are coated and shaped to form a coating layer.
The process according to the present invention for the fabrication of the optical fiber tape core comprises, in a fourth embodiment thereof, mounting the optical fiber cores in alignment with each other on a two-dimensional flat surface; applying silicone rubber onto the two-dimensional flat surface such that the two-dimensional surface with the plural optical fiber cores mounted therein is coated with the silicone rubber to form a coating layer; and peeling off the plural optical fiber cores from the two-dimensional flat surface to separate, from the coating layer on the two-dimensional flat surface, only a part thereof located on the optical fiber cores.
In these first to fourth embodiments of the present invention, it is preferred to use silicone rubber having a hardness of from 20 to 90 and a tensile strength of from 15 to 80 kgf/cm2.
(Legend)
The embodiments of the present invention will hereinafter be described in detail with reference to the drawings.
In
In the present invention, it is only necessary for the coating layer 3a that as illustrated in
As illustrated in
The silicone rubber forming the coating layer of the optical fiber tape core according to the present invention may preferably have a hardness of from 20 to 90 and a tensile strength of from 15 to 80 kgf/cm2. More preferred silicone rubber has a hardness of from 25 to 75 and a tensile strength of from 15 to 60 kgf/cm2. Still more preferred silicone rubber has a hardness of from 30 to 65 and a tensile strength of from 15 to 50 kgf/cm2.
Silicone rubber the hardness and tensile strength of which are lower than 20 and lower than 15 kgf/cm2, respectively, cannot provide the resulting optical fiber tape core with sufficient strength against lateral pressures, twisting and the like, so that during fabrication or installation, the optical fiber tape cores are susceptible to breakage even under a small strain. If the hardness is higher than 90 and the tensile strength is higher than 80 kgf/cm2, on the other hand, the resulting optical fiber tape core is sufficient neither in flexibility nor in separability into single cores.
In the present invention, no particular limitation is imposed on the silicone rubber insofar as its hardness and tensile strength fall within the above-described corresponding ranges. The addition reaction curing type, the condensation reaction curing type, and the vulcanizable type are all usable. Among these, silicone rubber of the addition reaction curing type or the condensation reaction curing type is preferred for its production of less byproducts and its good workability.
The thickness of the optical fiber tape core can be selectively determined as needed in accordance with its application purpose. In general, however, the thickness, including that of optical fiber cores, can be set within a range of from 300 μm to 480 μm, preferably from 330 μm to 430 μm, more preferably from 350 μm to 410 μm when the employed optical fiber cores have a thickness of 250 μm. Further, the width of the optical fiber tape core can also be selectively determined as needed in accordance with its application purpose. In general, however, the width, including that of optical fiber cores, can be set within a range of form 2,000 μm to 2,300 μm, preferably from 2,050 μm to 2,250 μm when eight optical fiber cores having a diameter of 250 μm are arranged in parallel with each other.
In addition, no particular limitation is imposed on the number of optical fiber cores in the optical fiber tape core according to the present invention, so that the optical fiber tape core can be a 2-core or 12-core optical-fiber tape core in addition to a 4-core optical-fiber tape core equipped with four optical fiber cores or an 8-core optical-fiber tape core equipped with eight optical fiber cores.
The optical fiber tape core according to the present invention, which has such a construction as described above, has sufficiently high strength and excellent flexibility and also sufficient anti-curling property, so that its optical fiber cores neither undergo breakage nor develop curling when handled upon connecting them to connectors or during installation work. Accordingly, the optical fiber tape core according to the present invention has high reliability and assures improvements in the safety and efficiency of work. Because the optical fiber tape core according to the present invention has excellent separability into single cores, the work to separate the optical fiber cores from each other can be performed easily without failure.
The optical fiber tape core according to the present invention is fabricated using silicone rubber as a coating material. It is preferred to fabricate the optical fiber tape core in accordance with the above-described first to fourth embodiments of the present invention.
Firstly, the first embodiment of the process of the present invention for the fabrication of an optical fiber tape core will be described with reference to the drawings. The first embodiment of the process for the fabrication of the optical fiber tape core firstly comprises, as illustrated in
In the present invention, the movement of the nozzle 4 can be effected by using any means, for example, can be effected either manually or automatically without any problem or inconvenience. It is, however, preferred to use such a system that permits control of the moving speed and also permits a movement at a constant speed and a stop. It is to be noted that the movement of the nozzle in the present invention is only required to be relative and either the nozzle or the optical fiber cores can be moved forwards each other, respectively. As the coating material is applied by the nozzle in the present invention, even optical fiber cores wired in a very narrow space can be formed into a tape insofar as there is a space sufficient to permit an insertion of the nozzle.
The nozzle for use in the present invention may preferably be in a tubular shape as depicted in
In the present invention, the nozzle for use in applying the coating material is not necessarily limited to a single nozzle, but can be in the form of plural nozzles.
In another example of the first embodiment of the fabrication process according to the present invention as illustrated in
In a further example of the first embodiment shown in
When applying the coating material to the optical fiber cores, the position of the nozzle relative to the plural optical fiber cores can be set so as to permit the application of the coating material onto all the optical fiber cores. It is to be noted that the clearance between the nozzle and the optical fiber cores can be selectively determined as needed to form the coating layer with desired shape and thickness. In the present invention, it is also possible to change the coating conditions in the course of the coating operation. Described specifically, the moving speed of the nozzle, the clearance between the nozzle and the optical fiber cores and the delivery rate of the coating material can be changed as needed, and therefore, can be selectively determined, for example, depending on the application purpose and the system construction. The stop of the delivery of the coating material from the nozzle at the coating end position and the movement of the nozzle can be selectively determined depending on the shape of the tape and the application purpose. For example, the delivery of the coating material from the moving nozzle can be stopped at the coating end position, and the nozzle can then be moved further such that the nozzle passes beyond the coating end position.
According to the above-described first embodiment of the process of the present invention for the fabrication of an optical fiber tape core, the coating material can be applied only as much as needed owing to the use of the nozzle so that the optical fiber tape core can be fabricated without waste of material. As the moving speed and distance of the nozzle can be controlled, it is also possible to feed the coating material to optical fiber cores even at parts thereof or over a short distance, and moreover, it is also possible to coat optical fiber cores all together with the coating material over a desired distance with desired tape width and thickness. Accordingly, optical fiber cores can be formed into a tape in order to improve mechanical strength, handling workability and the like. In addition, the use of the nozzle which is a very small coating jig makes it possible to coat plural optical fiber cores all together even if they are those drawn out of an optical component or optical connectors or those wired in a narrow place.
The second embodiment of the process of the present invention for the fabrication of an optical fiber tape core will next be described with reference to the drawings. The second embodiment of the process for the fabrication of the optical fiber tape core firstly comprises, as illustrated in
According to the above-described second embodiment, the setting of the optical fibers at the time of the initiation of the fabrication of the optical fiber tape core is completed by positioning the plural optical fiber cores on the flat surface in the shaping groove of the shaping jig or on the flat surface underneath the shaping groove of the shaping jig held in a proximity of the flat surface. The setting of the optical fibers for performing their formation into a tape can, therefore, be conducted very easily in a short time. Because the shaping of the coating material is effected by simply moving the shaping jig of the simple construction, which is provided only with the shaping groove, in the direction of the axes of the optical fiber cores, the formation into the tape can be conducted very easily.
The third embodiment of the process for the fabrication of an optical fiber tape core will next be described with reference to the drawings. As shown in
Examples of the shaping jig 7 employed in the above-described procedure can include those of the constructions shown in
As the coating material is fed to the shaping groove of the shaping jig in the above-described third embodiment, the coating and shaping of the coating material can be conducted in a single step by the single shaping jig. By controlling the feed position and feed rate of the coating material from a coating material feeder, it is also possible to avoid any over-feeding of the coating material to make an improvement in the material yield of the coating material and further, to set the width and thickness of the resulting tape as desired. By controlling the distance of a relative movement of the shaping jig, it is also possible to form optical fiber cores into a tape over a short distance thereof or to form parts of optical fiber cores into a tape at a desired position. It is to be noted that the term “relative” as used herein means that either the shaping jig or the arranged optical fiber cores can be moved forwards each other, respectively.
For use in the fabrication process of the second or third embodiment, any shaping jig can be selected depending upon the application object or the like of the optical fiber tape core insofar as it is equipped with a shaping groove. No particular limitation is imposed on the cross-sectional shape of the shaping jig because it can be selected as needed depending upon the shape of the applied coating material and its specification, but for example, a semielliptic, rectangular or semicircular cross-sectional shape or the like can be mentioned. The shaping jig can be of either a single-piece, unitary structure made of a single material or a structure of discrete parts assembled together. Further, the height, width and length of the shaping groove of the shaping jig can be selectively set as desired. The height is not required to be constant in the shaping jig, and may vary as needed. In addition, no particular limitation is imposed on the position of the shaping groove in the direction of the width of the shaping jig, and the shaping groove can be arranged at any position insofar as it is located within the width of the shaping jig. Furthermore, it is not necessary to limit to one (1) as the number of shaping groove(s) to be arranged in a shaping jig. For example, a single shaping jig can be provided with plural shaping grooves to fabricate plural optical fiber tape cores at once. A shaping groove of a shaping jig can be chamfered off at an upstream end portion thereof to facilitate the introduction of optical fiber cores into the shaping groove. As described above, it is also possible to use a shaping jig of the construction that two legs are arranged at an interval either equal to or wider than the width of the shaping groove to regulate optical fibers into alignment with each other (
No particular limitation is imposed on the size of the shaping jig, and the size can be selectively set as desired, for example, depending upon the number or the like of optical fiber tape cores. No particular limitation is imposed on its shape either. For example, a shape such as a quonset-shaped or parallelepipedal shape can be mentioned. Moreover, no particular limitation is imposed on the material which makes up the shaping jig, but preferred examples include materials having small friction coefficients such as polyacetal resins, materials having good mechanical properties such as materials resistant to thermal deformations, none-corrosive materials such as stainless steel, trifluoroethylene resin and tetrafluoroethylene resin, and materials having low resistance to chemical substances and solvents.
The shape of the through-hole arranged in the shaping jig to feed the coating material can be selectively set depending upon its application purpose, and therefore, the through-hole can have any shape. Illustrative are circular shape, elliptic shape, and rectangular shape. It is unnecessary to arrange only one through-hole, and plural through-holes may be arranged. No particular limitation is imposed on the size of the through-hole insofar as it can feed the coating material and can apply the coating material onto the optical fiber cores. Further, the through-hole can be located at any position insofar as it extends to the shaping groove. Moreover, the direction of the through-hole is not required to be perpendicular to the flat surface, and may have an inclination with respect to the flat surface.
To bring the optical fiber cores into alignment with each other by the shaping jig, the shaping jig is required to have, at a part thereof forward of the through-hole through which the coating material is fed, a construction that can regulate movements of the optical fiber cores and can put the optical fiber cores together side by side, as mentioned above. In this case, it is preferred to have such a construction that the optical fiber cores can be regulated not only in vertical movements but also in lateral movements. As an example of such a construction, one having a shaping groove of a rectangular shape in cross-section as mentioned above can be mentioned.
In the present invention, the shaping jig is required to be movable vertically and laterally relative to the optical fiber cores. Its operation can be effected manually. To precisely form a coating on the optical fiber tape core, however, it is more preferred to use a machine that performs the coating mechanically or automatically. As a means for moving the shaping jig in the direction of the axes of the optical fiber cores, any means can be used insofar as it can move the shaping jig at a constant speed in the direction of a single axis. It is, however, preferred to use such a means that can start and stop the shaping jig at desired positions and can also change its moving speed. For example, a moving system with the shaping jig secured on a 1-axis controlled robot can be used. With the moving system, the moving position and moving speed can be controlled.
To more precisely control the shape of a tape or the position of core parts to be formed into a tape, it is preferred to use a system that can control both of the feed rate of the coating material and the speed of a relative movement of the shaping jig. The use of such a system makes it possible to fabricate an optical fiber tape core different in shape at part or parts thereof or to increase the width and thickness of a tape at position or positions, where strength, protection or the like is needed, by changing the feed rate of the coating material or the speed of a relative movement of the shaping jig in the course of the formation into the tape. To more strictly control the shape of the tape or the position of core parts to be formed into the tape, it is preferred to use such a system that can also control the distance of a relative movement of the shaping jig in addition to the above-described control of the feed rate of the coating material and the speed of the relative movement of the shaping jig.
Further, the shaping jig can be one that allows to change the height of the shaping jig in the course of its movement in the direction of the axis of the optical fibers. Such a shaping jig makes it possible to fabricate an optical fiber tape core different in thickness or the like at part or parts thereof by changing its thickness or shape in the course of fabrication. More preferred is a system that permits automated movements of the shaping jig in the vertical direction.
For the feeding of the coating material, any means can be used. The feeding can be conducted manually, although mechanical or automated feeding is preferred from the viewpoint of control. For example, it is preferred that the initiation and termination of the feeding can be automatically controlled at desired positions. From the standpoint of improving the yield of coating layers made of silicone rubber and controlling the shape such as thickness, it is also preferred to control the feed rate.
The fourth embodiment of the process of the present invention for the fabrication of an optical fiber tape core will next be described with reference to the drawings. As shown in
According to the above-described fourth embodiment, it is only necessary to simply mount the optical fiber cores in alignment with each other on the two-dimensional flat surface and to apply the coating material over the optical fiber cores. It is, therefore, unnecessary to subject the optical fiber cores to two-dimensional alignment upon conducting the coating operation. Even if the number of cores is increased, an optical fiber tape core can still be fabricated stably without development of dimensional variations in the direction of the thickness of the optical fiber cores. The range of coating is not limited and, even when coating over a very short distance is desired, it is only necessary to simply apply the coating material to the surfaces of the optical fiber cores. Accordingly, the formation of connector-equipped optical fiber cores into a tape and the fabrication of a short-distance optical fiber tape core can be performed with ease.
In the above-described fourth embodiment, the step in which the two-dimensional flat surface is coated with silicone rubber requires only to apply the silicone rubber such that a silicone rubber coating layer is formed at a constant thickness over the surface of the optical fiber cores, and no limitations whatsoever are imposed on the manner of the coating. For example, plural optical fiber cores arranged on a two-dimensional flat surface of a substrate can be coated with a coating material in advance. A shaping jig with its bottom wall formed into a flat surface can then be moved from a coating start position to a coating end position such that the silicone rubber on the surfaces of the optical fiber cores can be shaped into a uniform thickness by the bottom wall of the shaping jig. This manner makes it possible to apply silicone rubber at a more uniform thickness. The thickness of the silicone rubber can also be controlled to a desired value by adjusting the height of the shaping jig. Further, the coating material can be spread over the two-dimensional flat surface of the substrate with the optical fiber cores arranged thereon by applying the coating material thick over the optical fiber cores beforehand and then moving the shaping jig. In addition, the application of the coating material and the movement of the shaping jig can be interlocked with each other. Furthermore, the coating and the shaping can be conducted at the same time by using a jig that can perform coating and shaping at the same time.
In the step that the plural optical fibers are peeled off from the two-dimensional flat surface, it is only necessary to set the moving speed and moving direction and the angle between the optical fiber cores and the substrate at the time of the peeling such that the peeling can be performed without deforming the shape of the coating layer, and therefore, no particular limitation is imposed on the manner of the peeling. For keeping the shape of the coating layer constant, however, it is preferred to control the moving speed constant during the peeling.
In the fourth embodiment, an optical fiber tape core maybe fabricated by coating the surfaces of plural optical fiber cores with silicone rubber as described above and then peeling some of the optical fiber cores. As illustrated in
The coated silicone rubber may be cured or dried as needed. This processing can be conducted either before or after peeling the optical fiber cores form the two-dimensional flat surface. These optical fiber cores may also be peeled off while the curing or drying is being conducted. In other words, the curing or drying processing can be conducted in any stage where the alignment of the optical fiber cores is not affected.
In the above-described fourth embodiment of the present invention, the coating of the optical fiber tape core may have a multilayer construction.
In the above-described first to fourth embodiments of the process of the present invention for the fabrication of an optical fiber tape core, an adhesive layer may be arranged on each two-dimensional flat surface. When optical fiber cores are mounted on the two-dimensional flat surface, they are temporarily held in place by the adhesive layer. The optical fiber cores, therefore, no longer require any positioning for alignment upon conducting coating or shaping so that the setting of the optical fiber cores can be easily conducted in a shorter time. In the fourth embodiment, the existence of the adhesive layer has led to greater adhesive force to the coating material so that the coating layer has been facilitated to fracture and separate along the direction of the axes of the optical fiber cores, thereby making it possible to improve the yield of products. In addition, it has also been facilitated to adjust the pitch intervals of the individual optical fiber cores.
Any adhesive can be used as an adhesive for use in the adhesive layer, insofar as it has adhesive force of such a degree as maintaining the shape of the optical fiber cores, keeping the optical fiber cores free from stress or strain and causing no damage on the optical fiber cores upon peeling them off. Usable examples of the adhesive can include various pressure-sensitive adhesives (adhesives) of the urethane, acrylic, epoxy, nylon, phenol, polyimide, vinyl, silicone, rubber, fluorinated epoxy and fluorinated acrylic types; thermoplastic adhesives, and thermosetting adhesives. From the ease in wiring the optical fire cores, pressure-sensitive adhesives thermoplastic adhesives can be used preferably. Any method can be used to bond the plural optical fiber cores on the adhesive layer. An automated wiring machine capable of bonding the optical fiber cores to the adhesive layer under constant pressure is also usable. A property can be imparted to the adhesive layer such that the adhesive layer is deactivated when the peeling is conducted. The peeling of the optical fiber cores form the adhesive layer can be facilitated, for example, by applying a solvent or irradiating light.
In the first to fourth embodiments, the substrate may be provided in the two-dimensional flat surface thereof with a groove for bringing optical fiber cores into alignment with each other.
The groove in the two-dimensional flat surface is required merely to permit aligning optical fiber cores and holding them in place, so that the width and depth of the groove can be dimensioned in conformity with those in the specification of an optical fiber tape core to be fabricated. Further, no particular limitation is imposed on the cross-sectional shape of the groove, and no problem or inconvenience arises with a groove in the form of a V letter or a series of semicircles instead of a rectangular shape.
It is to be noted that the expression “to bring optical fiber cores into alignment” as used herein means to arrange individual optical fiber cores side by side at a desired position. The spaces between the individual optical fiber cores may or may not be equal to each other, and can be set as needed depending upon the specification of an optical fiber tape core of an optical fiber tape core to be fabricated. Concerning the coating of optical fiber cores, no particular limitation is imposed on a range in which the optical fiber cores are to be coated, insofar as the optical fiber cores are coated with silicone rubber at the surfaces of at least parts of the optical fiber cores to be formed into a tape. It is also possible to mount plural bundles of optical fiber cores in parallel with each other and then to coat the bundles of optical fiber cores at the same time. Further, the expression “to peel off optical fiber cores” means that the optical fiber cores and their associated two-dimensional flat surface are caused to separate relative to each other, and the peeling-off of optical fiber cores can be effected by moving either the optical fiber cores or the two-dimensional flat surface. In the present invention, the individual optical fiber cores arranged in alignment with each other on a two-dimensional flat surface are required only that at least parts of them are arranged in alignment with each other on the same flat surface, and may include parts where the optical fiber cores are intersecting. In addition, no particular limitation is imposed on the number of optical fiber cores to be coated all together. It is, therefore, possible to fabricate 2-core tape cores, 4-core tape cores, 6-core tape cores, 8-core tape cores, 16-core tape cores, and so on.
The present invention will hereinafter be described more specifically based on examples and comparative examples. It should, however, be bone in mind that the present invention shall by no means limited to the following examples.
Each 8-core optical fiber tape core, which had such a construction as shown in
With respect to the thus-obtained optical fiber tape cores, the following tests were then conducted.
(Single-Core Separability Test)
Work was conducted on each optical fiber tape core (500 mm) to separate it into single optical fiber cores, and the ease of the work was ranked.
(Twist Property Test)
Each optical tape core (100 mm) was pulled under tension of 300 gf and, after the optical tape core was twisted 10 times or 20 times at one end thereof, the external appearance of the optical tape core was ranked. Specifically, the optical tape core was observed under a microscope for damages such as cleavage and coating layer peeling.
(Curl Property Test)
Each optical tape core (380 mm) was wound 2 full turns on a bobbin of 60 mm diameter. After the optical tape core was left over for 1 hour, the optical tape core was unwound and then, the degrees of its curling at both ends from a flat table surface were determined.
The test results so obtained are shown in Table 2.
* Optical fiber tape core making use of a UV curable resin (“8-CORE TAPE S 08/8T”, product of The Furukawa Electric Co., Ltd.)
As shown in Table 2, the optical fiber tape cores of Invention Examples 1-6 showed excellent single-core separability and exhibited sufficient tensile strength, and had been resolved to the maximum extent in the problem of development of curling due to the retention of a wound shape.
In the optical fiber tape core of Comparative Example 1, on the other hand, the single-core separability was good, but the strength was not sufficient and curling had been developed as a result of the winding.
An 8-core optical fiber tape core having the construction shown in
Using four optical fiber cores 2a-2d of 25 cm length (products of The Furukawa Electric Co., Ltd., quartz-based single-mode optical fibers, outer diameter: 0.25 mm), an optical fiber tape core of 20 cm length, 0.4 mm thickness and 1.1 mm width was fabricated by the coating machine shown in
The used coating machine was constructed of a 1-axis controlled robot and a coating material feeder for feeding a coating material to a nozzle. The 1-axis controlled robot had a flat substrate 10 for mounting optical fibers thereon. A ball screw shaft 11 was arranged along the longitudinal direction, is provided at an end thereof with a drive motor 14, and is supported at an opposite end thereof by a journal bearing 15. A movable unit 12 is arranged in threaded engagement with the ball screw, and is provided with a nozzle 4 such that the nozzle extends perpendicularly to the stage surface. On the movable unit, the nozzle was constructed such that it was movable not only in the vertical direction but also in the longitudinal direction and was fixable at a predetermined position. Further, a flexible pipe 8 was connected to the nozzle to feed the coating material from a coating material feeder 13. As the nozzle 4, a dispenser needle made of stainless steel (outer diameter: 1.2 mm, inner diameter: 0.9 mm) was used.
Firstly, the four optical fiber cores were aligned in parallel with each other on the substrate 10 along a line on which the movable unit of the 1-axis controlled robot 9 was movable, and at opposite end parts to which no coating was to be applied, were held in place by adhesive tapes 6 such that the same tension was applied to the individual optical fiber cores. As a coating material, a thermosetting silicone rubber resin having a hardness of 84 and a tensile strength of 45 gf/cm2 (“TSE3281-G”, product of GE Toshiba Silicones) was used. As the coating material feeder 13 for feeding the coating material to the nozzle, a dispenser was used.
The movable unit 12 of the 1-axis controlled robot 9 was next controlled to move the nozzle 4 to a coating start position A for the aligned four optical fiber cores (
Next, the moving speed of the movable unit 12 of the 1-axis controlled robot 9 and the delivery pressure of the coating material feeder 13 were set at 50 mm/sec and 5.0 kg/cm2, respectively. Concurrently with the initiation of a movement of the nozzle 4, a delivery of the coating material 3 was initiated. By moving the nozzle 4 in the direction of the axes of the optical fibers, the coating material was applied onto the optical fiber cores (
By coating and curing the coating material through the above operation, it was possible to apply the coating over the surfaces of the plural optical fibers all together. The thus-obtained optical fiber tape core was good in single-core separability, was not peeled off when twisted 10 times, and did not develop curling.
According to the above procedure, it was possible to fabricate optical fiber tape cores of 1.1 mm and less in width and 0.4 mm and less in thickness without developing any problem. Since it was possible to deliver the coating material only as much as needed to coat by moving the nozzle while delivering the coating material under constant pressure, the yield was good so that the cost of the coating material was successfully reduced.
An optical fiber tape core was fabricated in a similar manner as in Example 7 except that the moving speed was changed to 35 mm/sec in a range of 10 cm at central parts of the optical fibers. In the resulting optical fiber tape core, the width and thickness of its central part were 1.2 mm and 0.55 mm, respectively, and were greater than those of the remaining parts (width: 1 mm, thickness: 0.4 mm). The optical fiber tape core was good in single-core separability, was not peeled off when twisted 10 times, and did not develop curling. The optical fiber tape core was provided with increased strength, did not undergo breakage even when bent severely, and therefore, had sufficient strength.
Provided were four optical fiber cores of 25 cm length with MU connectors attached to one ends thereof. The four optical fiber cores with the MU connectors attached to the one ends thereof were formed at their central parts of 15 cm into a tape in a similar manner as in Example 7.
According to the above procedure, the optical fiber tape core was successfully fabricated at the predetermined position of the optical fiber cores with the MU connectors attached to the one ends thereof. By the formation into the tape, the optical fibers were united together and were increased in strength. The optical fibers, therefore, showed better handling ease in a system, leading to an improvement in workability.
To fabricate an optical fiber tape core of 60 cm length, 1.1 mm width and 0.4 mm thickness by using four optical fiber cores of 80 cm length (products of The Furukawa Electric Co., Ltd., quartz-based single-mode optical fibers, outer diameter: 0.25 mm), the procedure shown in the flow diagrams of
Firstly, the four optical fiber cores 2a-2d were aligned in parallel with each other on the substrate 5 in the optical fiber tape core fabrication facilities, and at their opposite end portions to which no coating was to be applied, were held in place by adhesive tapes 6. The coating material was then applied to the surfaces of the four optical fiber cores over a range of 60 cm where the optical fiber cores were to be formed into a tape, and the surface of the coating material was lightly leveled by a spatula (
Next, the shaping jig 7 was placed on the substrate such that the four optical fiber cores were located in the shaping grove 7a of the shaping jig (
In this example, the setting of the optical fiber cores required merely to bring the optical fiber cores, which had been mounted on the substrate, into the shaping groove of the shaping jig. Accordingly, the time required for the work was short and the operations were simple, resulting in improved working efficiency. Further, the thus-obtained optical fiber tape core was 1.2 mm in tape width and 0.35 mm in thickness, that is, was substantially of the preset dimensions, and the tape shape was substantially semielliptic in cross-section as desired.
Using four optical fiber cores of 90 cm length (products of The Furukawa Electric Co., Ltd., quartz-based single-mode optical fibers, outer diameter: 0.25 mm), an optical fiber tape core of 70 cm length, 1.1 mm width and 0.4 mm thickness was fabricated by the fabrication steps shown in
A shaping jig employed in this example had the same size as that used in Example 10, but at its free end part (on the forward side as viewed in the moving direction of the shaping jig), was provided with a circular through-hole having a diameter of 2 mm and extending to a shaping groove. A flexible pipe 8 is connected to the through-hole such that the coating material can be fed from the coating material feeder 13.
Firstly, the four optical fiber cores 2a-2d were aligned in parallel with each other on the flat substrate 10, and at their opposite end portions to which no coating was to be applied, were held in place by adhesive tapes 6. Next, the movable unit 12 was moved such that the through-hole of the shaping jig 7 was located at the coating start position A (
In this example, the setting of the optical fiber cores required merely to bring the optical fiber cores, which had mounted on the substrate, into the shaping groove of the shaping jig. Accordingly, the time required for the work was short and the operations were simple, resulting in improved working efficiency. By providing the shaping jig with the shaping groove and the through-hole and feeding the coating material, it was possible to perform both the coating and the shaping at the same time by the shaping jig of the very simple construction. Moreover, the feed rate of the coating material was controllable so that the coating material was not fed excessively, leading to an improvement in material yield. In addition, it was possible to coat, that is, to form a tape only at a predetermined position. Therefore, the thus-obtained optical fiber tape core was 1.1 mm in tape width and 0.4 mm in thickness, that is, was substantially of the preset dimensions, and the tape shape was substantially semielliptic in cross-section as desired.
Using four optical fiber cores of 35 cm length (products of The Furukawa Electric Co., Ltd., quartz-based single-mode optical fibers, outer diameter: 0.25 mm), an optical fiber tape core of 25 cm length, 1.1 mm width and 0.4 mm thickness was fabricated by the fabrication steps shown in
In this example, the setting of the optical fiber cores required merely to bring the optical fiber cores, which had mounted on the flat substrate, into the shaping groove of the shaping jig. Accordingly, the time required for the work was short and the operations were simple, resulting in improved working efficiency. By arranging the through hole at the longitudinal center of the shaping groove formed in the shaping jig and feeding a coating material, it was possible to perform both the coating and the shaping at the same time by the shaping jig of the very simple construction while aligning the optical fibers. As it was unnecessary to align the optical fibers together and in parallel with each other, a further improvement was achieved in working efficiency with respect to the setting of the optical fibers. Moreover, the feed rate of the coating material was controllable so that the coating material was not fed excessively, leading to an improvement in material yield. In addition, it was possible to coat, that is, to form a tape only at a predetermined position. Therefore, the thus-obtained optical fiber tape core was 1.1 mm in tape width and 0.4 mm in thickness, that is, was substantially of the preset dimensions, and the tape shape was substantially rectangular in cross-section as desired. The thus-obtained optical fiber tape core was good in single-core separability, was not peeled off when twisted 10 times, and did not develop curling.
Using four optical fiber cores of 40 cm length (products of The Furukawa Electric Co., Ltd., quartz-based single-mode optical fibers, outer diameter: 0.25 mm), an optical fiber tape core of 30 cm length was fabricated. A coating machine employed in this example was of the construction illustrated in
Firstly, the four optical fiber cores 2a-2d were aligned in parallel with each other on the substrate 5, and at their opposite end portions to which no coating was to be applied, were held in place by adhesive tapes 6, so that they were arranged above the flat base 10 (
The above-described procedure allowed to perform the shaping of the optical fiber tape cores very easily, and therefore, was able to make the fabrication time shorter than the conventional fabrication processes. Further, it was unnecessary to conduct any two-dimensional alignment adjustment. Therefore, optical fiber tape cores were fabricated without wasting, and the yields of the optical fiber cores and coating material were good. Moreover, the thus-obtained optical fiber tape cores had a uniform thickness of 0.35 mm.
A 30-cm long, 8-core optical fiber tape core of a unitary 2-layer construction was fabricated by using two of the optical fiber tape cores fabricated in Example 13, arranging the optical fiber tape cores side by side in parallel with each other, coating the optical fiber tape cores together with a thermosetting silicone rubber having a hardness of 84 and a tensile strength of 45 kgf/cm2 (“TSE3281-G”, product of GE Toshiba Silicones Co., Ltd.). As a shaping machine and forming jig, the same machine and jig as those employed in Example 13.
Firstly, two optical fiber tape cores obtained in a similar manner as in Example 13 were arranged in parallel with each other on a substrate. Next, the coating material was applied to the surfaces of the two optical fiber tape cores. A movable unit was then moved such that a bottom wall of a shaping jig was located at a height of 0.05 mm from the surfaces of the two optical fiber tape cores, and was moved at a moving speed of 50 mm/sec in the direction of the axes of the optical fiber cores. The thus-shaped coating material was then semi-cured under the conditions of a curing temperature of 150° C. and a curing time of 30 minutes. Next, the optical fiber cores were held at one ends thereof by a hand and then pulled in an upper direction, so that the optical fiber cores were peeled off from the substrate. The thus-obtained, 8-core optical fiber tape core was treated further under the conditions of 150° C. and 1 hour to completely cure the coating material, so that the 8-core optical fiber tape core of the two-layer construction was obtained. The thus-obtained optical fiber tape core was good in single-core separability, was not peeled off when twisted 10 times, and did not develop curling.
In the above-described example, the optical fiber tape core of the two-layer construction was successfully fabricated the same facilities and procedure as in Example 13. Unlike the conventional processes, it was unnecessary to replace the jig for use in the fabrication. The fabrication was, therefore, possible with good working efficiency and at low cost. The thus-obtained optical fiber tape core had a uniform thickness of 0.4 mm.
Using four optical fiber cores of 40 cm length, an optical fiber tape core was fabricated in a similar manner as in Example 13 except for the use of a substrate equipped with a groove which was 0.1 mm in depth and 1.1 mm in width and had a rectangular shape in cross-section. As the alignment of the optical fiber cores was successfully achieved by simply mounting the optical fiber cores in the groove, the setting of the optical fiber cores was feasible without any precise positional alignment. Accordingly, it was possible to shorten the time required for the work. It was also possible to conduct the work with ease, resulting in improved working efficiency.
Using four optical fiber cores of 40 cm length provided at opposite ends thereof with MT connectors, an MT-connector-equipped, 4-core optical fiber tape core was fabricated by forming them into a tape at their central parts of 35 cm length. As a substrate having a two-dimensional flat surface, a polyimide film of 500 mm×100 mm in size and 125 μm in thickness was used, and on one side of the substrate, an adhesive layer of 100 μm in film thickness was formed. The four optical fiber cores were bonded on the adhesive layer of the substrate such that they were held in place in alignment with each other. Subsequently, the procedure of Example 13 was followed likewise to fabricate the 4-core optical fiber tape core.
In this example, the optical fiber cores provided at the opposite ends thereof with the MT connectors was arranged and temporarily held in place beforehand on the adhesive layer. It was, therefore, possible to conduct the application and shaping of the coating material easily and uniformly. It was also possible to conduct with ease the positional alignment of the shaping jig. Accordingly, it was possible to shorten the time required for the work, resulting in improved working efficiency. Using the MT-connector-equipped optical fiber tape core, its connection to optical components in a system was performed. As the optical fiber tape core had been formed into the tape at the central part thereof, it was possible to easily handle its optical fiber cores and to readily connect them to the optical components, resulting in improved working efficiency.
The optical fiber tape core according to the present invention has extremely good characteristics that it is equipped with both sufficiently high strength and flexibility and hardly develops curling. Upon attachment of connectors or during installation work, its optical fiber cores neither break nor develop curling, thereby bringing above improvements in reliability, work safety and work efficiency. According to the fabrication process of the present invention for the optical fiber tape core, plural optical fiber cores can be readily formed into the tape by coating them together at a desired position and shaping the resulting coating layer with a nozzle and forming jig of simple constructions.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2002-205330 | Jul 2002 | JP | national |
| 2002-329030 | Nov 2002 | JP | national |
| 2003-28982 | Feb 2003 | JP | national |
This is a divisional application of Ser. No. 10/521,218, filed Jan. 13, 2005 which is presently allowed. The subject matter of the aforementioned prior application is hereby incorporated herein by reference.
| Number | Date | Country | |
|---|---|---|---|
| Parent | 10521218 | Jan 2005 | US |
| Child | 11827510 | Jul 2007 | US |