Optical glass and lens

Abstract

An optical glass which contains at least 20 mol % of TeO2 and has an internal transmittance of at least 80% in a thickness of 2 mm to a light having a wavelength of 405 nm and a refractive index of at least 1.85 to the same light, and which contains no alkali metal oxide or contains alkali metal oxides in a total amount of at most 15 mol %.

Description

BACKGROUND OF THE INVENTION

[0001] 1. Field of the Invention

[0002] The present invention relates to an optical glass and a lens suitable for e.g. an object lens to be used for recording on or reading out from an optical recording medium such as CD, CD-R, CD-RW, DVD or MO.

[0003] 2. Discussion of Background

[0004] Recording on an optical recording medium such as CD is carried out by condensing a laser beam by an object lens. It is common to employ a laser beam having a wavelength of 780 nm and an object lens having a numerical aperture of from 0.4 to 0.45. In a case where a higher recording density is desired, it is common to employ a laser beam having a wavelength of 650 nm and an object lens having a numerical aperture of 0.65.

[0005] In recent years, in order to further increase the recording density, it has been proposed to use a laser beam having a wavelength of from 400 to 415 nm, e.g. 405 nm and an object lens having a numerical aperture of from about 0.65 to 0.85. In order to increase the numerical aperture, the curvature or the refractive index of the object lens may be made large. However, if the curvature of the object lens is increased more than ever, there has been a problem that the thickness of the object lens will be so thick that the operation distance i.e. the distance between the object lens and the disk, cannot be secured. Accordingly, it is desired to increase the refractive index of the object lens.

[0006] As an optical glass having a large refractive index, which can be used as an object lens having such a large numerical aperture, a TeO2 type glass (hereinafter referred to as conventional glass) comprising 6 mass % of Na, 4 mass % of K, 12 mass % of Ba, 78 mass % of Te, and the rest being O (oxygen) is disclosed (JP-A-2001-180971). Further, the composition of the conventional glass represented by mol % comprises, based on the following oxides, 14.8% of Na2O, 5.8% of K2O, 9.9% of BaO and 69.4% of TeO2.

[0007] However, the object lens is required to have not only a large numerical aperture but also a large transmittance and high chemical durability. On the other hand, the above-mentioned conventional glass contains alkali metal oxides in a total amount of 20.6 mol % (=14.8+5.8), whereby it is possible that there will be a problem in chemical durability.

[0008] It is an object of the present invention to provide an optical glass and a lens which solve such problems.

SUMMARY OF THE INVENTION

[0009] The present invention provides an optical glass which contains at least 20 mol % of TeO2 and has an internal transmittance of at least 80% in a thickness of 2 mm to a light having a wavelength of 405 nm and a refractive index of at least 1.85 to the same light, and which contains no alkali metal oxide or contains alkali metal oxides in a total amount of at most 15 mol %.

[0010] Further, the present invention provides the above optical glass which consists essentially of, as represented by mol % based on the following oxides:

TeO2                     20 to 69%,
ZnO                      0 to 30%,
Na2O                     0 to 15%,
Y2O3                     0 to 20%,
GeO2                     0 to 50%,
B2O3                     0 to 50%,
La2O3                    0 to 30%,
BaO                      0 to 30%,
Ga2O3                    0 to 20%,
Nb2O5                    0 to 30%,
P2O5                     0 to 15%,
Ta2O5                    0 to 20%,
ZrO2                     0 to 20%,
Hf2O3                    0 to 20%,
Gd2O3                    0 to 20%,
In2O3                    0 to 20%,
Yb2O3                    0 to 20%,
MgO + CaO + SrO          0 to 20%,
Li2O + K2O + Rb2O + Cs2O 0 to 10%,
SiO2 + Al2O3             0 to 20%,

[0011] wherein the internal transmittance is at least 95%, and Na2O+Li2O+K2O+Rb2O+CS2O is from 0 to 15 mol %, and which contains no Fe or contains Fe in such an amount that the content calculated as Fe2O3 is at most 0.0001% as represented by mass percentage (glass A).

[0012] In glass A, in order to have the glass more stabilized, ZnO is preferably from 0.1 to 19 mol %.

[0013] Further, the present invention provides the above optical glass which contains no Er or contains Er in such an amount that the content calculated as Er2O3 is at most 0.01% as represented by mass percentage.

[0014] Further, the present invention provides a lens made of the above optical glass.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0015] Hereinafter, the contents of the respective components of glass will be represented by “%”, and this is meant for “mol %”. Further, for example, “glass X contains 20% of TeO2” means that “glass X contains Te, and the content on the assumption that such Te is present in the form of TeO2, is 20 mol %”.

[0016] The lens of the present invention is produced, for example, by press-forming the optical glass of the present invention (hereinafter referred to as the glass of the present invention). Namely, the glass of the present invention is processed to form a preform, and then, the preform is heated and softened and press-formed by means of a mold to form a lens. Further, the preform may also be prepared by forming a molten glass.

[0017] The lens of the present invention is suitable for use as an object lens in a case where recording on or reading out from an optical recording medium such as CD, CD-R, CD-RW, DVD or MO, is carried out by using a laser having a wavelength of from 400 to 415 nm, e.g. 405 nm.

[0018] If the internal transmittance T405 of the glass of the present invention in a thickness of 2 mm to a light having a wavelength of 405 nm, is less than 80%, it tends to be difficult to use such glass as the above-mentioned object lens. It is preferably at least 95%, more preferably at least 96%, particularly preferably at least 97%.

[0019] The above T405 may, for example, be measured as follows. Namely, with respect to two plate-shaped samples having thicknesses of 1 mm and 4 mm and a size of 2 cm×2 cm and having both sides mirror polished, the transmittances to a light having a wavelength of 405 nm are measured by means of a spectral photometer U-3500 (tradename, manufactured by Hitachi, Ltd.). The transmittances of the plate-shaped samples having thicknesses of 1 mm and 4 mm are represented by T1 and T4. respectively, and T405 is calculated by the following formula from the transmittance T1 at the thickness of 1 mm and the transmittance T4 at the thickness of 4 mm, obtained by the measurements.

T 405 =100×exp[(⅔)×loge(T4/T1)]

[0020] If the refractive index n of the glass of the present invention to a light having a wavelength of 405 nm, is less than 1.85, the numerical aperture of the object lens tends to be small. It is preferably at least 1.90, more preferably at least 1.95, particularly preferably at least 2.00, most preferably at least 2.05.

[0021] The glass transition point TG of the glass of the present invention is preferably at most 500° C. If it exceeds 500° C., press forming as mentioned above, tends to be difficult. It is more preferably at most 400° C., particularly preferably at most 370° C.

[0022] The glass of the present invention is preferably such that in an internal transmittance curve in a thickness of 2 mm to lights having wavelengths of from 300 to 800 nm, the internal transmittance in a thickness of 2 mm is 0% at a wavelength of 300 nm, and when the wavelength is increased beyond 300 nm, the internal transmittance becomes 0.1% for the first time, and the wavelength λe at which the internal transmittance becomes 0.1%, is 345 nm or less.

[0023] If λe exceeds 345 nm, coloration tends to be distinct when the glass is irradiated with a laser beam having a wavelength of e.g. 400 nm or 405 nm, and, for example, even when T405 was initially 97%, it would be less than 80% after 20 hours, whereby it would be difficult to use it as an object lens. λe is more preferably at most 342 nm, further preferably at most 330 nm, particularly preferably at most 325 nm.

[0024] The above internal transmittance may, for example, be measured in the same manner as measuring the internal transmittance at the time of measurement of T405, to lights having wavelengths of from 300 to 800 nm.

[0025] λe may, for example, be measured as follows. Namely, with respect to the same two plate-shaped samples (those having thicknesses of 1 mm and 4 mm) as used for the above measurement of T405, the transmittances to lights having wavelengths of from 300 to 800 nm are measured to obtain an internal transmittance curve for wavelengths of from 300 to 800 nm. The wavelength where the internal transmittance becomes 0.1% at the rising portion of this internal transmittance curve, is taken as λe.

[0026] The glass of the present invention is preferably such that when a blue purple light (406.7 nm and 413.1 nm) of Kr+ ion laser is irradiated under a condition of an energy density of 38 kW/m2, the reduction ratio L of the transmitted light intensity in a thickness of 2 mm in one hour after the irradiation is at most 16%. If it exceeds 16%, for example, in a case where the glass of the present invention is to be used as an object lens of DVD employing a blue purple laser diode, even if T405 was initially 97%, it would decrease to less than 80% after 20 hours, whereby it would be difficult to use it as the above-mentioned object lens. For example, in a case where even if T405 is initially 97%, T405 after 20 hours is desired to be at least 95%, L is more preferably at most 5%. L is particularly preferably at most 1%.

[0027] L may, for example, be measured as follows. Namely, with respect to a plate-shaped sample having a size of 1 cm×1 cm and a thickness of 2 mm and having both sides mirror polished, a blue purple light (wavelength: 406.7 nm, and 413.1 nm) of Kr+ ion laser INNOVA300 (tradename), manufactured by COHERENT, Inc. is irradiated for one hour under a condition of 38 kW/m2, whereby the transmitted light intensity I0 immediately after the irradiation and the transmitted light intensity I1, after irradiation for one hour, are measured by means of photodiode PD-300UV (tradename), manufactured by Ophir Optonics LTD., whereupon L is calculated by the following formula.

L =(I0−I1)×100/I0

[0028] If the TeO2 content in the. glass of the present invention is less than 20%, the glass tends to be instable, n tends to be small, or TG tends to be high. In order to make n large, the content is preferably at least 30%.

[0029] If the total content of alkali metal oxides in the glass of the present invention exceeds 15%, the chemical durability tends to be low, n tends to be small, the glass tends to be instable, or the hardness tends to be low. The total content is preferably at most 10%, more preferably at most 9%.

[0030] The glass of the present invention preferably contains at least one of GeO2, B2O3 and P2O5, wherein GeO2+B2O3+P2O5 is at most 50 mol %. If the glass does not contain any of GeO2, B2O3 and P2O5, the above-mentioned λe tends to be large, and L is likely to exceed 16%. The content is preferably at most 30%, particularly preferably at most 15%. If GeO2+B2O3+P2O5 exceeds 50%, n is likely to be small.

[0031] In a case where the glass of the present invention contains at least one of GeO2, B2O3 and P2O5, it is preferred that it contains either one of GeO2 and B2O3, and in a case where the chemical durability and/or the devitrification resistance is desired to be improved, it more preferably contains GeO2, and in a case where the melting temperature is desired to be lowered, it more preferably contains B2O3. Further, in such cases, GeO2+B2O3+P2O5 is preferably at least 1%, particularly preferably at least 2%.

[0032] The glass of the present invention preferably contains ZnO and/or BaO, wherein ZnO+BaO is at most 40 mol %. If it contains neither ZnO nor BaO, it tends to be difficult to make n large without increasing λe. If ZnO+BaO exceeds 40%, n is likely to be small. It is more preferably at most 25%.

[0033] Now, the composition of the above glass A as a preferred embodiment of the glass of the present invention, will be described. TeO2 is a component to form the glass skeleton, and it is also a component to make n large or to lower TG and is essential. If it is less than 20%, n tends to be small, or TG tends to be high. It is preferably at least 30%, more preferably at least 45%, particularly preferably at least 55%. If it exceeds 69%, T405 tends to be small. It preferably is at most 68%.

[0034] ZnO is not essential, but may be incorporated up to 30% to stabilize the glass. If it exceeds 30%, it becomes necessary to raise the temperature for melting the glass to a level exceeding 1000° C., whereby it tends to be difficult to melt the glass by means of a metal crucible (melting point: 1063° C.). In a case where the melting temperature is to be made lower, ZnO is preferably at most 19%.

[0035] If the above-mentioned temperature for melting the glass exceeds 1000° C., a crucible made of platinum or crucible made of a platinum alloy may, for example, be employed. However, if a glass containing TeO2 at the main component, is melted by using such a crucible, a crucible component such as platinum is likely to be dissolved in the glass, whereby the internal transmittance of the glass or T405 is likely to decrease.

[0036] In a case where ZnO is incorporated in order to e.g. facilitate vitrification or suppress devitrification at the time of forming, its content is preferably at least 0.1%. It is preferably at least 1%, more preferably at least 3%, particularly preferably at least 5%, most preferably at least 10%.

[0037] In the foregoing, a case of employing zinc oxide (melting point: 1975° C.) as the ZnO material to be used for melting glass, is assumed. However, even if a Zno material other than zinc oxide, is employed, if ZnO exceeds 19%, the following problems are likely to result.

[0038] For example, if zinc chloride, zinc fluoride, zinc bromide or zinc sulfate is used, chlorine, fluorine, bromine or sulfur is likely to remain, respectively, in the glass, whereby devitrification is likely to result. Further, it is conceivable to use zinc nitrate, but its deliquescence nature is very strong, whereby its handling tends to be difficult.

[0039] Na2O is not essential, but may be incorporated up to 15% in order to stabilize the glass or to lower TG or the melting temperature. If it exceeds 15%, n is likely to be small. It is preferably at most 11%, more preferably at most 8%. Further, when Na2O is incorporated, its content is preferably at least 0.1%, more preferably at least 1%, particularly preferably at least 3%.

[0040] Y2O3 is not essential, but may be incorporated up to 20% in order to suppress devitrification at the time of forming. If it exceeds 20%, the glass tends to be rather instable, or TG is likely to be high. It is preferably at most 10%, more preferably at most 7%, particularly preferably at most 4%. Further, in a case where Y2O3 is incorporated, its content is preferably at least 0.1%, more preferably at least 1%.

[0041] GeO2 is not essential, but may be incorporated up to 50% in order to suppress devitrification at the time of forming. If it exceeds 50%, the glass tends to be instable, or TG tends to be high. It is preferably at most 30%, more preferably at most 15%, particularly preferably at most 8%. Further, in a case where GeO2 is incorporated, its content is preferably at least 0.1%, more preferably at least 1%, particularly preferably at least 2%.

[0042] B2O3 is not essential, but may be incorporated up to 50% in order to stabilize the glass or to lower TG or the melting temperature. If it exceeds 50%, n is likely to be small. It is preferably at most 30%, more preferably at most 20%, particularly preferably at most 10%. Further, in a case where B2O3 is incorporated, its content is preferably at least 0.1%, more preferably at least 1%.

[0043] La2O3 is not essential, but may be incorporated up to 30% in order to suppress devitrification at the time of forming or to increase n or the hardness. If it exceeds 30%, vitrification tends to be difficult. It is more preferably at most 20%. particularly preferably at most 10%, most preferably at most 5%. In a case where La2O3 is incorporated, its content is preferably at least 0.1%, more preferably at least 1%, particularly preferably at least 3%.

[0044] BaO is not essential, but may be incorporated up to 30% in order to suppress devitrification at the time of forming or to increase n up to 30%. If it exceeds 30%, vitrification tends to be difficult. It is more preferably at most 20%, particularly preferably at most 10%. In a case where BaO is incorporated, its content is preferably at least 0.1%, more preferably at least 1%, particularly preferably at least 3%.

[0045] Ga2O3 is not essential, but may be incorporated up to 20% in order to increase the hardness. If it exceeds 20%, the glass is likely to be instable. It is preferably at most 5%.

[0046] Nb2O5 is not essential, but may be incorporated up to 30% in order to increase n or the hardness. If it exceeds 30%, the glass tends to be instable, or the internal transmittance or T405 tends to decrease. It is preferably at most 20%, more preferably at most 10%, particularly preferably at most 5%, most preferably at most 3%. In a case where Nb2O5 is incorporated, its content is preferably at least 0.1%, more preferably at least 1%. Further, in a case where it is desired to increase the internal transmittance or T405, it is preferred not to incorporate Nb2O5.

[0047] P2O5 is not essential, but may be incorporated up to 15% in order to stabilize the glass. If it exceeds 15%, chemical durability, particularly water resistance, tends to be low, or n is likely to be small. It is preferably at most 10%, particularly preferably at most 5%, most preferably at most 3%. In a case where P2O5 is incorporated, its content is preferably at least 0.1%, more preferably at least 1%, particularly preferably at least 3%. Here, in a case where it is desired to further increase water resistance, it is preferred not to incorporate P2O5.

[0048] Each of Ta2O5, ZrO2, Hf2O3, Gd2O3, In2O3 and Yb2O3 is not essential, but may be incorporated within a range of up to 20% each in order to increase n or the hardness without reducing the internal transmittance or T405. If each exceeds 20%, the glass is likely to be instable. Each of them is preferably at most 10%, more preferably at most 5%. For example, in a case where it is desired to increase T405, In2O3 is preferably at most 10%, more preferably at most 5%, particularly preferably at most 2%. In a case where any of these six components is contained, the content is preferably at least 0.1%, more preferably at least 1%. Further, the total content of Ta2O5, ZrO2, Hf2O3, Gd2O3, In2O3 and Yb2O3 is preferably at most 25%.

[0049] Each of MgO, CaO and SrO is not essential, but may be incorporated within a range of up to 20% in total in order to stabilize the glass or to adjust n. If the total exceeds 20%, the glass tends to be rather instable, or n tends to be small. It is preferably at most 10%, more preferably at most 5%.

[0050] Each of Li2O, K2O, Rb2O and Cs2O is not essential, but may be incorporated within a range of up to 10% in total in order to lower the melting temperature. If the total exceeds 10%, the glass tends to be instable, n or the hardness tends to be small, or the chemical durability tends to deteriorate. The total is preferably at most 5%. In a case where it is desired to increase the hardness or in a case where it is desired to improve the chemical durability, it is preferred not to incorporate any one of them.

[0051] The total content of Na2O, Li2O, K2O, Rb2O and Cs2O must be at most 15%. If it exceeds 15%, the chemical durability tends to decrease. The total amount is more preferably at most 12%, more preferably at most 9%.

[0052] Each of SiO2 and Al2O3 is not essential, but may be incorporated up to 20% in total in order to improve the water resistance. If the total exceeds 20%, TG or the melting temperature tends to be high, or n is likely to be small. The total is preferably at most 10%, more preferably at most 5%.

[0053] Glass A consists essentially of the above-mentioned components, but it may contain other components within a range not to impair the purpose of the present invention.

[0054] For example, in order to increase n or the hardness, MoO3, RuO2, Nd2O3, Pr2O3, CeO2, Sm2O3, Eu2O3, Tb2O3Ho203 or TM2O3 may be incorporated within such a range that the total content thereof is at most 10%. If the total content exceeds 10%, T405 tends to decrease. The total content is preferably at most 5%, more preferably at most 1%. Further, to improve the clarity, SO3, AS2O5 or Sb2O5 may be incorporated within such a range that the total content thereof is at most 2%.

[0055] Glass A contains no Fe,.or even if it contains Fe, the content calculated as Fe2O3 is at most 0.0001% as represented by mass percentage. If it exceeds 0.0001%, T405 tends to decrease.

[0056] As a preferred embodiment of glass A, one comprising from 55 to 68% of TeO2, from 10 to 19% of ZnO, from 3 to 15% of Na2O, from 1 to 4% of Y2O3 and from 2 to 8% of GeO2, may be exemplified.

[0057] For example, in a case where it is desired to bring λe to e.g. at most 342 nm, it is preferred that in glass A, TeO2 is from 30 to 67%, ZnO+BaO is from 0 to 40%, Na2O is from 0 to 10%, GeO2+B2O3+P2O5 is from 0 to 50%, Y2O3+La2O3+Ta2O5+ZrO2+Gd2O3+Yb2O3 is from 0 to 30%.

[0058] For example, in a case where it is desired to bring L to be e.g. at most 16%, it is preferred that in glass A, TeO2 is from 30 to 65%, ZnO+BaO is from 0 to 40%, Na2O is from 0 to 10%, GeO2+B2O3+P2O5 is from 0.1 to 50%, and Y2O3+La2O3+Ta2O5+ZrO2+Gd2O3+Yb2O3 is from 0 to 30%.

[0059] For example, in a case where it is desired to bring L to e.g. at most 5%, it is preferred that in glass A, TeO2 is from 30 to 60%, ZnO+BaO is from 0 to 40%, Na2O is from 0 to 8%, GeO2+B2O3+P2O5 is from 0.1 to 50%, and Y2O3+La2O3+Ta2O5+ZrO2+Gd2O3+Yb2O3 is from 0 to 30%, and Li2O+K2O+Rb2O+Cs2O is from 0 to 8%.

[0060] The glass of the present invention preferably contains no Er or even if Er is contained, its content calculated as Er2O3 is less than 0.01% as represented by mass percentage. If it exceeds 0.01%, T405 is likely to be small. It is more preferably at most 0.001%, particularly preferably at most 0.0001%.

[0061] The glass of the present invention preferably contains none of TiO2, Bi2O3 and WO3. If these components are contained, T405 is likely to be small.

[0062] Further, the glass of the present invention preferably contains none of PbO and Tl2O.

[0063] For the production of the glass of the present invention, tellurium dioxide, zinc oxide, lanthanum oxide, yttrium oxide, germanium oxide, boron oxide, gallium oxide, sodium carbonate, barium carbonate, etc., are used as starting materials, and the purities of these materials must be ones whereby the purpose of the present invention can be accomplished.

[0064] For example, tellurium dioxide is used as the material for TeO2, its purity is preferably at least 99.99%. If the purity is less than 99.99%, the Fe content is likely to be large. It is more preferably at least 99.999%. Further, the same applies also in a case where zinc oxide is used as the material for ZnO.

EXAMPLES

[0065] Materials were mixed to have the composition shown by mol % in the lines for TeO2 to Ga2O3 in Table 1, put into a crucible made of gold and melted for one hour at from 800 to 1000° C. At that time, the molten glass was homogenized by stirring for 0.5 hour by means of a stirrer made of gold. The homogenized molten glass was cast and formed into a plate shape, followed by annealing.

[0066] As the materials, in Examples 1 to 8, tellurium dioxide having a purity of at least 99.999% manufactured by Shinko Chemical Co., Ltd., zinc oxide having a purity of at least 99.999% manufactured by Kojundo Chemical Laboratory Co., Ltd., lanthanum oxide, yttrium oxide, germanium oxide, boron oxide and gallium oxide having a purity of at least 99.9%, manufactured by the same company, or super-high grades of sodium carbonate and barium carbonate, manufactured by Kanto Kagaku, were used. In Example 9, materials were selected for use from those listed above, except that tellurium dioxide having a purity of at least 99.9% manufactured by Kojundo Chemical Laboratory Co., Ltd. was used instead of the above-mentioned tellurium dioxide manufactured by Shinko Chemical Co., Ltd.

[0067] With respect to the obtained glass, the content of Fe calculated as Fe2O3 as represented by mass percentage (unit: 1×10−4%), the glass transition point TG (unit: °C.), the refractive index n′ to light having a wavelength of 633 nm, a refractive index n to light having a wavelength of 405 nm, the internal transmittance T405 (unit: %) in a thickness of 2 mm, λe (unit: nm) and L (unit: %) were measured.

[0068] Here, n was measured only with respect to Examples 8 and 9, and n in Examples 1 to 7 is values (=n′+0.10) results of measurement of n and n′ in Examples 8 and 9.

[0069] λe was measured only with respect to Examples 3 to 6 and 8, and λe in Examples 1, 2, 7 and 9 is values assessed from the compositions.

[0070] L in Examples 1 to 9 is all assessed values. With respect to ones where the measured values of λe were available, L was assessed from the interrelation between L and λe, and with respect to ones where no measured values of λe were available, λe was assessed from the compositions, and the respective L was assessed from the assessed value of λe.

[0071] Further, the content calculated as Fe2O3 in Example 9 being larger than in Examples 1 to 8, is considered to be attributable to the fact that tellurium dioxide having a low purity was used as the Te material. Further, the content of Fe calculated as Fe2O3 represented by mol % in Example 9 was 0.00021%.

[0072] Methods for measuring n′, n and TG will be described as follows.

[0073] n′: A plate-shaped sample having a size of 2 cm×2 cm and a thickness of 1 mm and having both sides mirror-polished, was measured by means of a refractive index measuring apparatus Model 2010 PRISMCOUPLER (tradename) manufactured by Metricon Corporation.

[0074] n: The glass was processed into a triangular shaped prism having one side of 30 mm and a thickness of 10 mm, which was measured by a precision spectrometer GMR-1 (tradename) manufactured by Kalnew Optical Company.

[0075] TG: A sample processed into a columnar shape having a diameter of 5 mm and a length of 20 mm, was measured at a temperature raising rate of 5° C./min by means of thermal mechanical analyzer TMA8140 (tradename) manufactured by Rigaku Corporation.

TABLE 1
	1	2	3	4	5	6	7	8	9
TeO2	69	67	65	65	63	63	63	63	69
ZnO	18	19	19	17	16.5	16.5	16.5	16.5	18
Na2O	5	5	5	5	4.9	4.9	4.9	4.9	5
Y2O3	3	3	3	3	2.9	2.9	2.9	2.9	3
GeO2	5	5	5	5	4.9	4.9	4.9	4.9	5
B2O3	0	1	3	5	4.8	4.8	4.8	7.8	0
La2O3	0	0	0	0	0	3	0	0	0
BaO	0	0	0	0	0	0	0	0	0
Ga2O3	0	0	0	0	0	0	3	0	0
Fe2O3	<1	<1	<1	<1	<1	<1	<1	<1	1.7
TG	340	340	340	340	340	360	350	340	340
n′	2.01	2.00	1.98	1.97	1.96	1.96	1.95	1.96	2.01
n	2.11	2.11	2.08	2.07	2.06	2.06	2.05	2.06	2.11
T405	95	96	97	97	97	98	98	99	85
λe	350	350	346	347	346	343	345	345	352
L	20	20	15	15	15	14	15	15	25

[0076] Glasses of Examples 10 to 16 having compositions represented by mol percentage in the lines for TeO2 to B2O3 in Table 2, were prepared in the same manner as glasses of Examples 1 to 8. However, the melting time was from 0.5 to 3 hours, and the stirring time by the stirrer was from 0.5 to 1 hour. The contents calculated as Fe2O3 in glasses of Examples 10 to 16 were not measured, but the same contents are considered to be less than 1×10−4%, since the same ones as in glasses of Examples 1 to 8 were used as the materials.

[0077] In Examples 10 to 16, n′, λe and L were measured, but n and T405 were assessed from the compositions, and the assessed values are shown in Table 2. Further, TG was measured with respect to Examples 11 to 16, but TG in Example 10 is a value assessed from the composition.

[0078] Here, assessment of n from n′ was carried out as follows taking into consideration the dispersion characteristic of the wavelength. Namely, in a case where n′≧1.95, n=n′+0.10 (Examples 10 to 13, the after-mentioned Examples 18, 20 to 22, 25 to 31 and 40), in a case where 90≦n′<1.95, n=n′+0.09 (Examples 14 and 15), in a case where 1.85≦n′<1.90, n=n′+0.07, in a case where 1.80≦n′<1.85, n=n′+0.06 (Example 16, and the after-mentioned Example 23), and in a case where 1.75≦n′<1.80, n=n′+0.05 (the after-mentioned Example 24).

TABLE 2
	10	11	12	13	14	15	16
TeO2	70	67	64	60	57	54	40
ZnO	17	20	23	27	27	30	30
Na2O	5	5	5	5	8	8	0
Y2O3	3	3	3	3	3	3	0
GeO2	5	5	5	5	5	5	0
B2O3	0	0	0	0	0	0	30
TG	330	340	345	345	335	335	405
n′	2.01	2.00	1.99	1.97	1.93	1.92	1.83
n	2.11	2.10	2.09	2.07	2.02	2.01	1.89
T405	95	96	97	97	97	98	98
λe	345	342	339	335	330	327	324
L	18.1	18.9	16.3	12.2	5.99	4.91	0.16

[0079] Glasses of Examples 17 to 40 having compositions represented by mol% in the lines for TeO2 to Al2O3 in Tables 3 to 5, were prepared in the same manner as the glasses of Examples 1 to 8. However, the melting time was from 1.5 to 3 hours, and the stirring time by the stirrer was from 0.5 to 1 hour. Example 24 is a Comparative Example.

[0080] The contents calculated as Fe2O3 in the obtained glasses of Examples 17 to 40 were not measured, but the same contents are considered to be less than 1×10−4%, respectively, since the same ones as for the glasses of Examples 1 to 8 were used as materials.

[0081] TG in Examples 18 and 29 to 38, and T405 in Examples 19 to 38 and 40 are values assessed from the compositions, respectively.

[0082] Further, n′in Examples 21 to 23, 28 to 31 and 40, n in Examples 18, 20 to 31 and 40, λe in Examples 19 to 38 and 40 and L in Examples 18 to 38 and 40, are assessed values, respectively.

TABLE 3
	17	18	19	20	21	22	23	24
TeO2	65	65	65	65	65	65	30	20
ZnO	17	15	17.5	15	12.5	17.5	40	50
Na2O	5	5	5	5	5	5	0	0
Y2O3	3	2.5	2.5	2.5	2.5	2.5	0	0
GeO2	5	5	5	5	5	5	0	0
B2O3	0	0	0	0	0	0	30	30
La2O3	5	7.5	0	0	0	0	0	0
BaO	0	0	5	7.5	10	0	0	0
In2O3	0	0	0	0	0	5	0	0
Al2O3	0	0	0	0	0	0	0	0
TG	370	390	335	335	335	370	440	460
n′	1.98	1.97	1.98	1.98	1.98	1.98	1.80	1.77
n	2.07	2.07	2.08	2.08	2.08	2.08	1.86	1.82
T405	97	97	97	97	97	94	99	99
λe	342	342	345	345	345	350	315	305
L	16	16	16	16	16	20	0	0

[0083]

TABLE 4
	25	26	27	28	29	30	31	32
TeO2	65	65	65	65	68.42	68.42	68.42	63.05
ZnO	17	17	17	17	17.9	17.9	12.9	16.5
Na2O	5.5	6	6.5	7	0	5.26	0	4.85
Y2O3	2.5	2	1.5	1	3.16	3.16	3.16	2.9
GeO2	5	5	5	5	5.26	0	5.26	4.85
B2O3	0	0	0	0	0	0	5	4.85
La2O3	5	5	5	5	5.26	5.26	5.26	0
BaO	0	0	0	0	0	0	0	0
In2O3	0	0	0	0	0	0	0	3
Al2O3	0	0	0	0	0	0	0	0
TG	360	350	355	340	370	350	380	385
n′	1.97	1.98	1.97	1.97	2.01	2.00	1.97	1.96
n	2.07	2.08	2.07	2.07	2.11	2.10	2.07	2.05
T405	97	97	97	97	95	95	95	95
λe	345	345	345	345	350	350	350	350
L	16	16	16	16	20	20	20	20

[0084]

TABLE 5
	33	34	35	36	37	38	39	40
TeO2	63.05	63.05	63.05	63.05	63.05	63.05	70	70
ZnO	16.5	16.5	16.5	16.5	16.5	16.5	0	0
Na2O	4.85	4.85	7.85	4.85	4.85	4.85	5.38	5.38
Y2O3	5.9	2.9	2.9	2.9	2.9	2.9	3.23	3.23
GeO2	4.85	7.85	4.85	4.85	4.85	4.85	5.38	5.38
B2O3	4.85	4.85	4.85	4.85	4.85	4.85	16	10
La2O3	0	0	0	0	0	0	0	0
BaO	0	0	0	0	0	0	0	0
Nb2O3	0	0	0	3	0	0	0	0
ZrO2	0	0	0	0	3	0	0	0
Al2O3	0	0	0	0	0	3	0	6
TG	390	385	340	390	390	390	415	425
n′	1.95	1.96	1.96	1.99	1.96	1.94	1.97	1.97
n	2.04	2.06	2.06	2.09	2.06	2.03	2.06	2.07
T405	99	99	99	94	99	99	94	93
λe	340	340	340	350	340	340	350	350
L	12	12	12	20	12	12	14.8	20

[0085] According to the present invention, it is possible to obtain an optical glass which has a small content of alkali metal oxides and which has a large refractive index and a large internal transmittance to light having a wavelength of 405 nm. Further, it is possible to obtain an optical glass which has no or little reduction in the transmitted light intensity by a blue purple light irradiation. By using the glass of the present invention, it is possible to obtain a lens such as an object lens suitable for recording on or reading out from an optical recording medium such as CD, CD-R, CD-RW, DVD or MO, by press forming.

[0086] The entire disclosures of Japanese Patent Application No. 2002-147849 filed on May 22, 2002 and Japanese Patent Application No. 2003-143617 filed on May 21, 2003 including specifications, claims and summaries are incorporated herein by reference in their entireties.

Claims

1. An optical glass which contains at least 20 mol % of TeO2 and has an internal transmittance of at least 80% in a thickness of 2 mm to a light having a wavelength of 405 nm and a refractive index of at least 1.85 to the same light, and which contains no alkali metal oxide or contains alkali metal oxides in a total amount of at most 15 mol %.

2. The optical glass according to claim 1, which contains at least one of GeO2, B2O3 and P2O5, wherein GeO2+B2O3+P2O5 is at most 50 mol %.

3. The optical glass according to claim 1, which contains ZnO and/or BaO, wherein ZnO+BaO is at most 40 mol %.

4. The optical glass according to claim 1, which consists essentially of, as represented by mol % based on the following oxides:

5. The optical glass according to claim 4, wherein TeO2 is from 55 to 68%, ZnO is from 10 to 19%, Na2O is from 3 to 15%, Y2O3 is from 1 to 4%, and GeO2 is from 2 to 8%.

6. The optical glass according to claim 4, wherein TeO2 is from 30 to 67%, ZnO+BaO is from 0 to 40%, Na2O is from 0 to 10%, GeO2+B2O3+P2O5 is from 0 to 50%, and Y2O3+La2O3+Ta2O5+ZrO2+Gd203+Yb2O3 is from 0 to 30%.

7. The optical glass according to claim 1, which contains no Er or contains Er in such an amount that the content calculated as Er2O3 is at most 0.01% as represented by mass percentage.

8. The optical glass according to claim 1, wherein, in an internal transmittance curve in a thickness of 2 mm to lights having wavelengths of from 300 to 800 nm, the internal transmittance in a thickness of 2 nun is 0% at a wavelength of 300 nm, and when the wavelength is increased beyond 300 nm, the internal transmittance becomes 0.1% for the first time, and the wavelength at which the internal transmittance becomes 0.1%, is 345 nm or less.

9. The optical glass according to claim 1, wherein when a blue purple light (406.7 nm and 413.1 nm) of Kr+ ion laser is irradiated under a condition of an energy density of 38 kW/m2, the reduction ratio L in one hour after the irradiation of the transmitted light intensity in a thickness of 2 mm is at most 16%.

10. The optical glass according to claim 9, wherein the reduction ratio L is at most 5%.

11. A lens made of the optical glass as defined in claim 1.