1. Field of the Invention
The present invention relates to an optical information recording medium, in particular, to an optical information recording medium including a transparent substrate, an optical recording layer absorbing a laser beam formed on the substrate, the optical recording layer containing at least, for example, a light-absorbing substance composed of a dye, and a light-reflective layer composed of materials such as a metal film, wherein writing and reading can be performed with high density and speed using a red laser beam having a wavelength of, for example, 640 to 680 nm.
2. Description of the Related Art
Recently, write-once optical information recording media such as DVD-R and DVD+R have been developed. These media use an organic dye compound corresponding to a semiconductor laser having a wavelength of 640 to 680 nm (for example, 650 to 665 nm) as an optical recording layer. A known CD-R has a track pitch of 1.6 μm and a storage capacity of 600 to 650 MB. In contrast, optical information recording media such as DVD-R and DVD+R have a track pitch of 0.74 μm which is smaller than that of the CD-R, and a storage capacity of 4.7 GB which enables a very high recording density. Furthermore, regarding the recording speed, the CD-R has a reference scanning velocity of 1.2 to 1.4 m/s, whereas the DVD-R/+R has a much higher reference scanning velocity of 3.49 m/s. For recording onto DVD-R/+R, recording instruments having a recording speed of eight times the reference scanning velocity (8× speed) are in practical use. However, at present, a recording instrument having a recording speed sixteen times the reference scanning velocity (16× speed) is not in practical use. In the optical information recording medium using an organic dye compound as the optical recording layer, recording and playback characteristics are required over a wide range of recording speeds, from low speed to high speed. Under the present situation, however, such an optical information recording medium that has recording and playback characteristics adequate to cover a wide range of recording speeds is not realized.
In high speed recording, a high recording power increases the amount of heat generated during recording or per unit time. This causes a problem of thermal strain to become obvious, resulting in variations in the recording pits. Furthermore, the output power of a semiconductor laser is limited. Therefore, a dye material with high sensitivity that can be compatible with high speed recording is desired.
Accordingly, regarding the characteristics of the organic dye material forming the optical recording layer, the complex refractive index (hereinafter referred to as “refractive index”) must be further increased to reduce the thickness of the optical recording layer, thus controlling the heat generated during recording. In addition, the dye in the optical recording layer must be decomposed with a recording power as low as possible. The trend for decreasing the thickness of the optical recording layer is, when the recording speed is represented based on a reference scanning velocity (corresponding to 1× speed) of 3.49 m/s (about 3.5 m/s), the average of 60 nm at 2× speed, 54 nm at 4× speed, 44 to 47 nm at 8× speed, and about 40 nm at 16× speed etc. However, even if the molecules of the organic dye material are designed to have a high refractive index, possible chemical structures are limited. Therefore, under the present situation, such a dye that can be compatible with high speed recording cannot sufficiently be designed. On the other hand, the recording power at low speed recording is too low. Therefore, when the thickness of the optical recording layer is decreased in order to provide characteristics for high speed recording, it is difficult to form sufficiently large pits.
As described above and will also be described later, in high speed recording, at the recording speed of 8× or more in particular, the amount of heat generated during recording is increased because of the high recording power. Accordingly, configuration factors and thermophysical properties must be designed so as to be suitable for thermal control during recording. The configuration factors include the shape of the optical recording layer in a pregroove on a substrate, the shape of the light reflective layer in the pregroove, and the shape of the substrate. The thermophysical properties include the decomposition temperature of the dye and the calorific value. In order to decrease the recording power, optical design of the dye, for example, increasing light absorption of the organic dye material is also required. In a media design suitable for high speed recording, the thickness of the optical recording layer is reduced. As a result, the physical size of the pits formed is decreased in low speed recording. In order to perform appropriate recording from low speed to high speed, the pits must be made optically larger using an organic dye material having high refractive index. Furthermore, a measure for heat dissipation in high speed recording is also required.
As described above, in order to perform the appropriate recording from low speed to high speed, in particular, recording at high speed recording, the configuration factors and thermophysical properties of the dye are preferable to be designed so as to be suitable for thermal control and the heat dissipation measure (see, domestic re-publication of PCT international publication for patent application No. 2001-59778).
One aspect of the invention provides an optical information recording medium that can record with high density and high speed using a laser beam, in particular, having a wavelength of about 640 nm to about 680 nm.
Another aspect of the invention provides an optical information recording medium wherein heat dissipation characteristics are improved in view of the regulation of heat generated by a recording power during recording on an optical recording layer.
Another aspect of the invention provides an optical information recording medium wherein configuration factors such as the shape of the optical recording layer, the shape of a light-reflective layer, and thermophysical properties of a dye are considered.
According to embodiments of the present invention, it is difficult to achieve a significant advantage by controlling the thermophysical properties of a dye, which is particularly related to the control of heat generation during recording. On the other hand, a significant advantage that improves the effect of the generated heat can be achieved by controlling the configuration factors, which is related to the control of heat dissipation. Embodiments of the present invention have been accomplished by paying attention to the following point, i.e., a phenomena in which the recording power of a laser beam heats a light-absorbing substance such as a dye in a pregroove while the heat is diffused through the optical recording layer and the light-reflective layer, thus improving the heat dissipation effect of the diffusing heat. According to one embodiment of the present invention, an optical information recording medium includes a transparent substrate having a pregroove thereon, an optical recording layer absorbing a laser beam and formed on the substrate, and a light-reflective layer reflecting the laser beam and formed on the optical recording layer. In the optical information recording medium, optically readable information is recorded by irradiating the laser beam on the optical recording layer through the substrate. According to a first aspect of the present invention, in the pregroove, the ratio of the cross-sectional area of the optical recording layer to the cross-sectional area of the pregroove in the direction of the diameter of the optical information recording medium is about 30% to about 63%.
According to another embodiment of the present invention, an optical information recording medium includes a transparent substrate having a pregroove thereon, an optical recording layer absorbing a laser beam and formed on the substrate, and a light-reflective layer reflecting the laser beam and formed on the optical recording layer. In the optical information recording medium, optically readable information is recorded by irradiating the laser beam on the optical recording layer through the substrate. According to a second aspect of the present invention, in the pregroove, the ratio of the cross-sectional area of the light-reflective layer to the cross-sectional area of the pregroove in the direction of the diameter of the optical information recording medium is about 37% to about 70%.
According to another embodiment of the present invention, an optical information recording medium includes a transparent substrate having a pregroove thereon, an optical recording layer absorbing a laser beam and formed on the substrate, and, a light-reflective layer reflecting the laser beam and formed on the optical recording layer. In the optical information recording medium, optically readable information is recorded by irradiating the laser beam on the optical recording layer through the substrate. According to a third aspect of the present invention, the light-reflective layer projects into the pregroove.
According to another embodiment of the present invention, an optical information recording medium includes a transparent substrate having a pregroove thereon; an optical recording layer absorbing a laser beam and formed on the substrate; and a light-reflective layer reflecting the laser beam and formed on the optical recording layer. In the optical information recording medium, optically readable information is recorded by irradiating the laser beam on the optical recording layer through the substrate. According to a forth aspect of the present invention, a thickness of the light-reflective layer in the pregroove is greater than a thickness of the recording layer in the pregroove.
The optical recording layer ratio in the pregroove is preferably about 30% to about 57%.
The light-reflective layer ratio in the pregroove is preferably about 43% to about 70%.
The projecting depth of the light-reflective layer in the pregroove is preferably about 83 nm to about 140 nm.
The projecting depth of the light-reflective layer in the pregroove is preferably about 93 nm to about 140 nm.
The optical recording layer preferably has a thickness of about 35 nm to about 90 nm in the pregroove.
The optical recording layer preferably has a thickness of about 35 nm to about 83 nm in the pregroove.
An inclination angle of the optical recording layer in the pregroove is preferably about 37.5 degrees to about 60 degrees.
The inclination angle of the optical recording layer in the pregroove is preferably about 38.5 degrees to about 60 degrees.
The optical recording layer preferably has a leveling value of about 0.15 to about 0.29.
The optical recording layer preferably has a leveling value of about 0.15 to about 0.26.
A reference scanning velocity during recording is preferably about 3.49 m/s. The optical information recording medium can be preferably compatible with a recording speed of S×n (wherein S represents the reference scanning velocity during recording, and n represents an integer of 8 or higher).
The optical information recording medium can be preferably compatible with a recording speed of S×n (wherein S represents the reference scanning velocity during recording, and n represents an integer of exceeding 8). The recording wavelength of the laser beam is preferably about 640 nm to about 680 nm.
In addition, above-mentioned each condition defined by each range includes a margin of error on each measurement.
An advantage according to an embodiment of the present invention is as follows: In an optical information recording medium, since the optical recording layer ratio in the pregroove is about 30% to about 63%, the calorific value during the formation of recording pits can be properly controlled. As a result, preferable recording characteristics can be maintained in a recording area compatible with higher speed recording. In one embodiment of the present invention, in addition to paying attention to the optical recording layer ratio in the pregroove, a projecting depth of the optical recording layer projecting toward the inside of the pregroove and a light-reflective layer ratio in the pregroove are also considered. As a result, the heat generated in the optical recording layer during recording can be immediately transmitted and diffused toward the light-reflective layer having a high thermal conductivity. Therefore, the heat dissipation can be controlled effectively and efficiently. In a very high speed recording such as 8× speed or even 16× speed, the optical information recording medium according to one embodiment of the present invention can improve the heat dissipation effect of the heat generated during recording to form appropriate recording pits.
According to an embodiment of the present invention, since the optical recording layer ratio in the pregroove is about 30% to about 63%, a media compatible with higher speed recording and high density recording can be realized.
An optical information recording medium according to an embodiment of the present invention will be described with reference to
The pregroove 7 forming a spiral shape is disposed on the substrate 2. A land 8, which is a part other than the pregroove 7, is disposed on both sides of the pregroove 7.
As shown in
The substrate 2 and the optical recording layer 3 are in contact with each other at a first boundary 11.
The optical recording layer 3 and the light-reflective layer 4 are in contact with each other at a second boundary 12. The light-reflective layer 4 and the protective layer 5 are in contact with each other at a third boundary 13. The protective layer 5 and the dummy substrate 6 are in contact with each other at a fourth boundary 14.
The transparent substrate 2 is composed of a material having a high transparency and a refractive index of, for example, about 1.5 to about 1.7 with a laser beam. The substrate 2 is chiefly composed of a resin plate having high impact resistance such as polycarbonate, acrylic resin, and epoxy resin, or a glass plate.
The optical recording layer 3 formed on the substrate 2 is composed of a light-absorbing substance containing, for example, a dye. Irradiation of the laser beam 9 causes heat generation, melting, sublimation, deformation, or alteration of the optical recording layer 3. For example, the optical recording layer 3 is evenly formed by spin coating a solution containing a solvent and a dye such as an azo dye or a cyanine dye on the surface of the substrate 2. Although any material for optical recording can be used for the optical recording layer 3, light-absorbing organic dyes are preferably used.
The light-reflective layer 4 is a metal film having a high thermal conductivity and a high light reflectivity. For example, the light-reflective layer 4 is formed by vacuuming deposition or sputtering using gold, silver, copper, aluminum, or an alloy thereof.
The protective layer 5 is composed of a resin having a high impact resistance, as in the substrate 2, and superior adhesiveness. For example, the protective layer 5 is formed by applying an ultraviolet-curing resin by spin coating. The resultant substrate is then irradiated with ultraviolet rays to cure the resin.
The dummy substrate 6 is composed of the same material as the substrate 2 to provide the predetermined thickness of about 1.2 mm.
In
The cross-sectional shape and each dimension of the optical information recording medium 1 were measured as follows: A part of the second boundary 12 between the optical recording layer 3 and the light-reflective layer 4 was broken apart by inserting a metal spatula from a center hole of the optical information recording medium 1 to decompose the optical information recording medium 1. Subsequently, the organic dye material (optical recording layer 3) adhered to a side of the light-reflective layer 4 was washed off with ethanol. This sample was used for measuring the shape of the dye layer, except parts damaged during decomposing with the spatula. The organic dye material (optical recording layer 3) adhered to a side of the substrate 2 was washed off with ethanol. This sample was used for measuring the shape of the substrate 2, except parts damaged during decomposing with the spatula. The shapes of each part were measured with an atomic force microscope (AFM) (from ThermoMicroscopes, Autoprobe M5).
The design of thermal control during high speed recording in the present invention will now be described. In recording onto the optical information recording medium 1, the laser power of the laser beam 9 rapidly heats the organic dye material in the pregroove 7. The heat is diffused through the optical recording layer 3 and the light-reflective layer 4. This diffusing heat is transferred to the adjacent tracks or to the pregroove 7. These areas are heated to some degree, forming a preheated state. When the substrate in this preheated state is irradiated with the laser beam 9 for the subsequent recording, an enlarged recording pit is formed due to the effect of the preheating. As a result, the shape of the formed recording pit 10 becomes different from a recording mark that supposed to be recorded.
The stronger the laser power of the laser beam 9, that is, the higher the recording speed, the greater the amount of heat generated. For example, according to a standard DVD-R media, it is expected that the recording power (laser intensity) is about 6 to about 10 mW at 1× speed recording (about 3.5 m/s), about 15 to about 20 mW at 4× speed recording, about 25 to about 30 mW at 8× speed recording, and about 40 mW or more at 16× speed recording. In short, it becomes more important for a media compatible with high speed recording that the heat generated during recording does not affect the adjacent part.
The factors to control the heat generated during recording in the optical information recording medium 1 are roughly divided into control of heat generation and control of heat dissipation. The control of heat generation relates to physical properties of materials such as the calorific value and the decomposition temperature of the material itself of the optical recording layer 3. The control of heat dissipation closely relates to configuration factors such as the shapes of the optical recording layer 3 and the substrate 2, that is, the thickness of the optical recording layer 3, and the shape of the second boundary 12 between the optical recording layer 3 and the light-reflective layer 4. For example, the optical recording layer 3, which is a thin film composed of an organic dye material, is disposed between the light-reflective layer 4 which is a metal thin film, and the substrate 2 composed of polycarbonate. It is obvious that the metal (light-reflective layer 4) has a thermal conductivity higher than that of the polycarbonate, a plastic material (substrate 2). Therefore, the control of heat dissipation closely relates to the configuration factors.
As a result of intensive study to improve the thermal effect, the present inventors have found that it is difficult to achieve a significant advantage by controlling the heat generation, whereas a significant advantage can be achieved by controlling the heat dissipation based on the configuration factors such as the shapes of the optical recording layer 3 and the substrate 2.
As described above, the control of heat dissipation, more specifically, the shapes of the optical recording layer 3 and the light-reflective layer 4 in the pregroove 7, are the most dominant in thermal control during high speed recording. The present invention has been accomplished by paying attention to this point. In particular, the shape of the optical recording layer 3 represented by the following items significantly affects thermal control (control of heat dissipation) during high speed recording. Furthermore, the following Items (1) and (2) particularly affect thermal control.
According to one embodiment of the present invention, in order to be compatible with high speed recording of 8× speed or more, the above Items are preferably in the following range.
In order to be compatible with high speed recording exceeding 8× speed (for example, 16× speed), the above Items are preferably in the following range.
The above Items (1) to (5) in embodiments of the present invention independently affect thermal control during high speed recording. In order to satisfy a high speed recording of 8× speed or more, the shape of the optical information recording medium is advantageous to satisfy at least one of the conditions defined by Items (1) to (5). Among the Items (1) to (5), Item (1) and Item (2) particularly affect thermal control. Therefore, the shape is advantageous to satisfy at least one of the conditions defined by the Items (1) and (2).
The effect of shapes of components such as the substrate 2, the optical recording layer 3, and the light-reflective layer 4 on the characteristics of high speed recording of the media will now be described with reference to the experimental results.
Examples of the present invention will now be described.
A first compound (azo dye) (0.2 g) shown in
High speed recording was performed on the above optical information recording medium 1 with the optical recording layer 3 by a disc checker (DDU-1000, from Pulstec Industrial Co., Ltd.) including a semiconductor laser (NA=0.65) having a wavelength of 660 nm. In this test, an EFM signal was recorded with a linear velocity of 28 m/s at 8× speed. After the recording, the signal was played back with a laser output of 0.7 mW using the disc checker. The reflectance, the modulation amplitude, the error rate, and the jitter were measured. The reflectance (Rtop) was 45.3%, the modulation amplitude (I14/Itop) was 75.3%, the error rate was 1.4, and the jitter was 6.5%. According to the standard values, the reflectance must exceed 45%, the modulation amplitude must exceed 60%, the error rate (PI value) must be less than 280, and the jitter must be less than 8%. Thus, the above optical information recording medium satisfied all these standard values including reflectance, modulation amplitude, error rate (PI value), and jitter.
Another disc, other than the disc used for evaluating the recording property, was prepared. This disc was broken apart at the boundary (second boundary 12) between the light-reflective layer 4 and the optical recording layer 3, and decomposed. The methods of decomposing etc. were the same as described above. The shape of the decomposed disc was measured with an AFM measuring apparatus. The substrate groove angle (β) was 69.1 degrees, and a substrate groove width (full width at half-maximum) was 301 nm. Herein, the substrate groove width (full width at half-maximum) represents a width at the half-way position of the substrate groove depth (Hsg). Numerical values related to, for example, the optical recording layer ratio in the pregroove, i.e., [{(Wst+Wsb)×Hsg/2}−{(Wst−2×Wx+Wdb)×(Hsg−Hsd)/2}/{(Wst+Wsb)×Hsg/2}]×100 shown in
The following items were calculated based on the above values.
A write-once optical information recording medium 1 was prepared as in Example 1, except that the average dye film thickness was about 56 nm, which was thicker than that of Example 1 by about 12%. The recording medium was evaluated and analyzed as in Example 1. The reflectance, the modulation amplitude, the error rate, and the jitter were measured as in Example 1. The reflectance (Rtop) was 46.4%, the modulation amplitude (I14/Itop) was 80.6%, the error rate was 2.1, and the jitter was 7.4%. According to the result of the shape measurement, the substrate groove angle (β) was 69.1 degrees, and the substrate groove width (full width at half-maximum) was 301 nm. Numerical values related to, for example, the optical recording layer ratio in the pregroove shown in
A write-once optical information recording medium 1 was prepared as in Example 1, except that the dye was changed from the first compound (shown in
A write-once optical information recording medium 1 was prepared as in Example 1, except that the average dye film thickness was about 64 nm, which was thicker than that of Example 1 by about 28%. The recording medium was evaluated and analyzed as in Example 1. The reflectance, the modulation amplitude, the error rate, and the jitter were measured as in Example 1. The reflectance (Rtop) was 45%, the modulation amplitude (I14/Itop) was 80.9%, the error rate was 314.0, and the jitter was 14.1%. According to the result of the shape measurement, the substrate groove angle (β) was 69.1 degrees, and the substrate groove width (full width at half-maximum) was 301 nm. Numerical values related to, for example, the optical recording layer ratio in the pregroove shown in
A write-once optical information recording medium 1 was prepared as in Example 1, except that an optical recording layer 3 having an average dye film thickness of about 65 nm on a substrate 2 including a pregroove 7 having a depth of about 165 nm. The recording medium was evaluated and analyzed as in Example 1. The reflectance, the modulation amplitude, the error rate, and the jitter were measured as in Example 1. The reflectance (Rtop) was 53.1%, the modulation amplitude (I14/Itop) was 77.1%, the error rate was 418.8, and the jitter was 21.4%. According to the result of the shape measurement, the substrate groove angle (β) was 69.1 degrees, and the substrate groove width (full width at half-maximum) was 302 nm. Numerical values related to, for example, the optical recording layer ratio in the pregroove shown in
While the above description has pointed out novel features of the invention as applied to various embodiments, the skilled person will understand that various omissions, substitutions, and changes in the form and details of the device or process illustrated may be made without departing from the scope of the invention. Therefore, the scope of the invention is defined by the appended claims rather than by the foregoing description. All variations coming within the meaning and range of equivalency of the claims are embraced within their scope.
Number | Date | Country | Kind |
---|---|---|---|
2003-433005 | Dec 2003 | JP | national |
Number | Name | Date | Kind |
---|---|---|---|
4687728 | Folkard et al. | Aug 1987 | A |
5274623 | Usami et al. | Dec 1993 | A |
5369321 | Koike et al. | Nov 1994 | A |
5696758 | Yanagimachi et al. | Dec 1997 | A |
6028836 | Kosuda et al. | Feb 2000 | A |
6639892 | Usami | Oct 2003 | B2 |
6673411 | Koide et al. | Jan 2004 | B2 |
6984434 | Usami et al. | Jan 2006 | B2 |
20020051941 | Shoda et al. | May 2002 | A1 |
20020106475 | Mihara et al. | Aug 2002 | A1 |
20020150030 | Takagishi et al. | Oct 2002 | A1 |
20020150034 | Takagishi et al. | Oct 2002 | A1 |
20020154595 | Takagishi et al. | Oct 2002 | A1 |
20060114804 | Uchida et al. | Jun 2006 | A1 |
20070054219 | Satake et al. | Mar 2007 | A1 |
Number | Date | Country |
---|---|---|
0467716 | Jan 1992 | EP |
0 881 636 | Dec 1998 | EP |
1039456 | Sep 2000 | EP |
1215671 | Jun 2002 | EP |
1256947 | Nov 2002 | EP |
1333434 | Aug 2003 | EP |
06-282871 | Oct 1994 | JP |
11-213442 | Aug 1999 | JP |
2000-268409 | Sep 2000 | JP |
2000-309722 | Nov 2000 | JP |
2002-222542 | Aug 2002 | JP |
2003-140300 | May 2003 | JP |
2004-272983 | Sep 2004 | JP |
WO 0159778 | Aug 2001 | WO |
WO 0159779 | Aug 2001 | WO |
Number | Date | Country | |
---|---|---|---|
20050169160 A1 | Aug 2005 | US |