Claims
- 1. A method of forming an optically transmissive body comprising a binary sulfide and a ternary sulfide said ternary sulfide having two cation types, a first one selected from the group consisting of metal cations, a second one selected fro the group consisting of the lanthanum series cations comprising the steps of:
- reacting the two cation types with a material which when reacted provides a source of sulfide anions to convert all of said first cation type and a first portion of said second cation type into the ternary sulfide, and reacting a second remaining portion of said second cation type into the binary sulfide, said binary sulfide forming a solid solution with said ternary sulfide with said metal cations and lanthanum series cations selected from those which will form a binary sulfide ternary sulfide solution; and
- forming the binary sulfide and ternary sulfide into the optically transmissive body.
- 2. A method for forming an optically transmissive body comprising a ternary sulfide in solid solution with a binary sulfide comprising the steps of:
- forming a precursor powder having a pair of cation types, a first one selected from the group consisting of calcium and strontium and a second one selected from the group consisting of lanthanum and neodymium in a predetermined nonstoichiometric composition of said ternary sulfide to provide an excess amount of said second cation type;
- reacting the powder with a material which when reacted provides a source of sulfide anions to convert a first portion of said powder into the ternary sulfide, and a remaining portion of said powder into the binary sulfide having the second type cation, said binary sulfide forming a solid solution with said ternary sulfide; and
- processing the binary sulfide and ternary sulfide into the optically transmissive body.
- 3. A method for providing an optically transmissive body comprising calcium lanthanum sulfide in solid solution with lanthanum sulfide comprising the steps of:
- forming a starting powder including calcium cations and lanthanum cations in a ratio of greater than 2 moles of lanthanum cations to 1 mole of calcium cations;
- reacting the starting powder with a material which when reacted provides a source of a sulfide anion to convert a first portion of said powder into the calium lanthanum sulfide, and a remaining portion of such starting powder into lanthanum sulfide, said lanthanum sulfide forming a solid solution with said calcium lanthanum sulfide; and
- processing the solid solution of lanthanum sulfide and calcium lanthanum sulfide into the optically transmissive body.
- 4. A method of forming an optically transmissive body comprising a solid solution of a calcium lanthanum sulfide and lanthanum sulfide comprising the steps of:
- forming a starting powder including calcium and lanthanum cations in the ratio of greater than 2.0 moles of lanthanum to 1.0 moles of calcium;
- reacting at an elevated temperature of at least 900.degree. C. the starting powder with a material which when reacted provides a source of sulfide anions to convert a first portion of the lanthanum cations and all the calcium cations into calcium lanthanum sulfide, and the remaining portion of lanthanum cations into the lanthanum sulfide forming a solid solution with said calcium lanthanum sulfide; and
- processing the solid solution of calcium lanthanum sulfide and lanthanum sulfide into the optically transmissive body.
- 5. The method as recited in claim 4 wherein the step of forming the body further comprises the steps of:
- consolidating the solid solution into the body, providing said solution with a predetermined density;
- sintering the solid solution in an environment of a material which when reacted provides a source of sulfide anions, at an elevated temperature in the range of 900.degree. C. to 1200.degree. C. providing the body with a density in the range of 91 to 95%; and
- compressing the body at an elevated pressure of at least 20,000 psi and at an elevated temperature in the range of 900.degree. C. to 1100.degree. C. providing said solid solution with a density of at least 99%.
- 6. The method as recited in claim 4 wherein the starting powder reacts with the sulfide anions at an elevated temperature of 1000.degree. C.
- 7. The method as recited in claim 3 wherein the reacting step further comprises:
- directing at an elevated temperature in the range of 900.degree. C. to 1100.degree. C. a flow of hydrogen sulfide gas over the starting powder to convert said powder into the calcium lanthanum sulfide and lanthanum sulfide.
- 8. The method as recited in claim 7 wherein the elevated temperature is about 1000.degree. C.
- 9. The method as recited in claim 8 wherein the processing step further comprises the steps of:
- consolidating the solid solution of lanthanum sulfide and calcium lanthanum sulfide into the body having a first density;
- sintering said consolidated body at an elevated temperature in the presence of hydrogen sulfide until said body has a density between 91% and 95% of theoretical density; and
- compressing said solution at an elevated pressure and at an elevated temperature to provide said body having an actual density of at least 99.5% of theoretical density.
- 10. A method as recited in claim 9 wherein during said compressing step, the body is compressed to provide said optically transmissive body, with a sample of said compressed body, having a thickness of 0.048 inches, has an optical transmissivity of at least 50% to energy having a wavelength in the range of 4.0 microns to at least 16.0 microns.
- 11. The method as recited in claim 9 wherein during said compressing step, the body is compressed to provide said optically transmissive body, with a first sample of said body having a first thickness of 0.048 inches has an optical transmissivity of at least 50% and a second sample of said body having a second thickness of about 0.015 inches has an optical transmissivity of at least 50%, eand transmissivity being over the range of at least 0.4 microns to 16.0 microns.
- 12. The method as recited in claim 11 wherein said body has a coefficient of absorption .alpha. of less than 3.0 over said optical wavelength range where .alpha. is given by .alpha.=[1n(T.sub.b /T.sub.a)]/(t.sub.b -t.sub.a) where T.sub.a, T.sub.b are the percent transmissivity of the first and second samples and t.sub.a, t.sub.b are the first and second thickness.
- 13. The method as recited in claim 12 wherein .alpha. is less than 1.0 over the optical range of 4.0 microns to 12.0 microns.
- 14. The method as recited in claim 13 wherein a sample of said body has an optical transmissivity of at least 60% over the wavelength range of 8-12 microns for a thickness of said sample in the range of 0.015 to 0.048 inches.
- 15. The method as recited in claim 6 wherein during said compressing step, the body is compressed to provide said optically transmissive body, with a sample of said body, having a thickness of 0.048 inches, has an optical transmissivity of at least 50% to energy having a wavelength in the range of 4.0 microns to 16.0 microns.
- 16. The method as recited in claim 6 wherein during said compressing step, the body is compressed to provide said optically transmissive body, with a first sample of said body, having a first thickness of 0.048 inches, has an optical transmissivity of at least 50%, and a second sample of said body, having a second thickness of about 0.015 inches, has an optical transmissivity of at least 50%, each transmissivity being over the range of 4.0 microns to 16.0 microns.
- 17. The method as recited in claim 16 wherein said body has a coefficient of absorption .alpha. of less than 3.0 over said optical wavelength range where .alpha. is given by .alpha.=[1n(T.sub.b /T.sub.a)]/(t.sub.b -t.sub.a) where T.sub.a, T.sub.b are the percent transmissivity of the first and second samples and t.sub.a, t.sub.b are the first and second thickness.
- 18. The method as recited in claim 17 wherein .alpha. is less than 1.0 over the optical range of 4.0 microns to 12.0 microns.
- 19. The method as recited in claim 18 wherein a sample of said body has an optical transmissivity of at least 60% over the wavelength range of 8-12 microns, for a thickness of said sample the range of 0.015 to 0.048 inches.
Parent Case Info
This application is a continuation of application Ser. No. 500,703 filed 6-03-83, now abandoned.
US Referenced Citations (3)
Number |
Name |
Date |
Kind |
3545967 |
Reynolds et al. |
Dec 1970 |
|
3873473 |
Susa et al. |
Mar 1975 |
|
4619792 |
Saunders et al. |
Oct 1986 |
|
Continuations (1)
|
Number |
Date |
Country |
Parent |
500703 |
Jun 1983 |
|