Optical Recording Medium, Recording Method Thereof And Evaluation Method Of Optical Recording Medium

Information

  • Patent Application
  • 20090046550
  • Publication Number
    20090046550
  • Date Filed
    September 13, 2005
    19 years ago
  • Date Published
    February 19, 2009
    15 years ago
Abstract
A recording method of an optical recording medium comprises irradiating the medium with a laser having m pulse sets each comprising a heating pulse and a cooling pulse, in which m is a natural number; and scanning the medium with the laser at a scanning speed v to record marks each of a length nT, in which n is a natural number of 3 or more and T is a clock cycle, wherein a length TCPn of a final cooling pulse is determined in accordance with the scanning speed v using the following functions, in v
Description
TECHNICAL FIELD

The present invention relates to a rewritable optical recording medium such as CD-RW, DVD-RW, DVD+RW, DVD-RAM, etc. using a phase-changing material in a recording layer, a recording method of the optical recording medium and an evaluation method of the optical recording medium.


BACKGROUND ART

It has been known to set up parameters for recording speed by linear functions (see Patent Literatures 1 to 3). Particularly, a technique of changing parameters stepwise has been disclosed in the Patent Literatures 2 and 3.


However, it has not been mentioned that the length of at least either of final heating pulses and final cooling pulses (irradiation time) is discontinuously changed.


Rewritable optical disks applied with a phase-changing technique, which are represented by CD-RW, DVD-RW, DVD+RW, etc., have been widely popularized for audio/visual purposes and the information recording purpose of computers. Moreover, improvement of the recording speed onto these optical disks has been anticipated with an increasing capacity of digital information in recent years. Both rewriting performance at a higher scanning speed and rewriting performance in a broader scanning speed range are required for high-speed recording onto optical disks using such a phase-changing technique. The former is the highest recording speed and the latter is equivalent to a recordable speed range. Particularly, the latter corresponds to a CAV (Constant Angular Velocity) recording which is a technique necessary for accelerating random access recording; hence a scale of speed (highest speed/lowest speed) of about 2.4 folds is necessary. Moreover, in the CAV recording, the recording scanning speed v changes corresponding to the recording radius position r, namely, v/r=constant, therefore it must be recordable at any recording speed below the highest recording speed. Furthermore, if the highest speed increases, the scanning speed range also inevitably broadens. For example, in a 4× speed disk of DVD+RW, the scanning speed range of 5.8 to 14.0 m/s is required for the CAV, but in a 8× speed disk, the scanning speed range of 11.6 to 27.9 m/s is required, therefore, the development of such an optical recording medium capable of recording in a very wide range, which can correspond to the 8-hold speed disk, and a recording method of the optical recording medium have been desired.


On the other hand, recording layer material must be changed to material suitable for even higher speed recordings in order to increase the highest recording speed. Usually, a phase-change material is used for the recording layer material of optical disks represented by DVD+RW. For example, in general, the phase change material is made of alloys capable of reversibly changing the phase between an amorphous phase and a crystalline phase. In increasing the recording speed, a phase-change material having a high crystallization rate must be used to accelerate the phase change between the amorphous phase and the crystalline phase.


However, to increase the crystallization rate results in the great difficulty in controlling the crystalline phase at the time of low-speed recording. Therefore, recording methods (strategies) in a speed region close to the highest recording speed and a speed region close to the lowest recording speed must be greatly changed. Hence, there is the problem that it becomes very difficult to record at any recording speed below the highest recording speed if using a recording layer material able to correspond to the high-speed recording.


Patent Literature 1 Japanese Patent Application Laid-Open No. 2000-322740


Patent Literature 2 Japanese Patent Application Laid-Open No. 2001-118245


Patent Literature 3 Japanese Patent Application Laid-Open No. 2001-243626


DISCLOSURE OF INVENTION

An object of the present invention is to provide a recording method capable of a CAV recording for a rewritable optical recording medium applied with a phase-changing technique with the highest recording speed of more than 8× speed of DVD+RW, i.e., a recording method (recording strategy) of the optical medium capable of recording at any recording speed below the highest recording speed of the optical recording medium, an optical recording medium recordable by the recording method and an evaluation method of the optical recording medium.


The present invention provides a recording method of an optical recording medium. In the first aspect of a recording method, there is provided a recording method of an optical recording medium corresponding to different recording speed, which comprises: irradiating the medium with a laser having m pulse sets each comprising a heating pulse of a power Pw and a cooling pulse of a power Pc, in which m is a natural number; and scanning the medium with the laser at a scanning speed v to record marks each of a length nT on the medium, in which n is a natural number of 3 or more, T is a clock cycle, and the relation of m<n is satisfied,


wherein: a length TCPn of a final cooling pulse, which is the m-th cooling pulse, is determined in accordance with the scanning speed v using the following functions (1) and (2),





in a range of v<v0, TCPn/T=f1,n(v)  Function (1)





in a range of v≧v0, TCPn/T=f2,n(v)  Function (2)


where the f1,n(v) and f2,n(v) each represents a continuous function of the scanning speed v to satisfy the relation of f1,n(v0)>f2,n(v0); the f1,n(v) and f2,n(v) each satisfies the condition where an existence ratio of abnormal marks, which is a ratio of the number of abnormal marks to the number of normal marks, is 1.0×10−4 or less, the normal mark satisfying the requirement of L/nT≧n−0.5 and the abnormal mark satisfying the requirement of L/nT<n−0.5 where L is a length of each reproduced mark obtained by reproducing the recorded marks; and v0 is any scanning speed selected to satisfy the existence ratio of the abnormal marks of 1.0×10−4 or less.


According to the recording method of the optical recording medium of the first aspect, the length TCPn of the final cooling pulse is optimized so as not to take a temperature history which induces an abnormal crystal growth inherent for a recording layer material of a high-speed correspondence, thereby suppressing the occurrence of the mark length beyond specifications. Further, the length TCPn is specified by two types of continuous functions, and the optimum value of TCPn is easily determined for any scanning speed v, and thus it is possible to easily carry out the recording with high reproduction reliability.


In the recording method of the optical recording medium of the first aspect, preferably, the length TLPn of the final heating pulse, which is the m-th heating pulse, is properly controlled. Preferably, at least one of the f1,n(v) and f2,n(v) is a linear function of the scanning speed v. Preferably, the function of m=n/2 holds if n is an even number and the function of m=(n−1)/2 holds if n is an odd number. Preferably, the functions of vH/vL≧2.4 and 0.4 vH≦v0≦0.8 vH are satisfied where a highest recording speed of the medium is represented by vH and a lowest recording speed of the medium is represented by vL.


In such methods, the parameter TCPn can be determined by a linear function of the scanning speed, therefore the parameter TCPn can be easily determined with few errors. Moreover, this enables decreasing the number of parameters to be pre-formatted in the optical recording medium as compared with complicated functions, and may correspond to high-speed recording at a scanning speed of 20 m/sec or more by using a 2T strategy. Still further, good characteristics can be obtained in the CAV recording because corresponding speed width and the scanning speed v0 are optimized.


In the second aspect of a recording method, there is provided a recording method of an optical recording medium corresponding to different recording speed, which comprises: irradiating the medium with a laser having m pulse sets each comprising a heating pulse of a power Pw and a cooling pulse of a power Pc, in which m is a natural number; and scanning the medium with the laser at a scanning speed v to record marks each of a length nT on the medium, in which n is a natural number of 3 or more, T is a clock cycle, and the relation of m<n is satisfied,


wherein: a length TLPn of a final heating pulse, which is the m-th heating pulse, is determined in accordance with the scanning speed v using the following functions (3) and (4),





in a range of v<v0, TLPn/T=g1,n(v)  Function (3)





in a range of v≧v0, TLPn/T=g2,n(v)  Function (4)


where the g1,n(v) and g2,n(v) each represents a continuous function of the scanning speed v to satisfy the relation of g1,n(v0)>g2,n(v0); the g1,n(v) and g2,n(v) each satisfies the condition where an existence ratio of abnormal marks, which is a ratio of the number of abnormal marks to the number of normal marks, is 1.0×10−4 or less, the normal mark satisfying the requirement of L/nT≧n−0.5 and the abnormal mark satisfying the requirement of L/nT<n−0.5 where L is a length of each reproduced mark obtained by reproducing the recorded marks; and v0 is any scanning speed selected to satisfy the existent ratio of the abnormal marks of 1.0×10−4 or less.


According to the recording method of the optical recording medium of the second aspect, the length TLPn of the final heating pulse is optimized so as not to take a temperature history which induces an abnormal crystal growth inherent for a recording layer material of a high-speed correspondence, thereby suppressing the occurrence of the mark length beyond specifications. Further, the length TLPn is specified by two types of continuous functions, and the optimum value of TLPn is easily determined for any scanning speed v, and thus it is possible to easily carry out the recording with high reproduction reliability.


In the recording method of the optical recording medium of the second aspect, preferably, the length TCPn of the final cooling pulse, which is the m-th cooling pulse, is properly controlled. Preferably, at least one of the g1,n(v) and g2,n(v) is a linear function of scanning speed v.


Preferably, the function of m=n/2 holds if n is an even number and the function of m=(n−1)/2 holds if n is an odd number. Preferably, the functions of vH/vL≧2.4 and 0.4 vH≦v0≦0.8 vH are satisfied where a highest recording-scanning speed of the medium is represented by vH and a lowest recording-scanning speed of the medium is represented by vL.


In such methods, the parameter TLPn can be determined by the linear functions of the scanning speed, therefore the parameter can be easily determined with few errors. Moreover, this enables decreasing the number of parameters to be pre-formatted in the optical recording medium as compared with complicated functions, and may correspond to high-speed recording at a scanning speed of 20 m/sec or more by using a 2T strategy. Still further, good characteristics can be obtained in the CAV recording because corresponding speed width and the scanning speed v0 are optimized.


In the third aspect of a recording method, there is provided a recording method of an optical recording medium corresponding to different recording speed, which comprises: irradiating the medium with a laser having m pulse sets each comprising a heating pulse of a power Pw and a cooling pulse of a power Pc, in which m is a natural number; and scanning the medium with the laser at a scanning speed v to record marks each of a length nT on the medium, in which n is a natural number of 3 or more, T is a clock cycle, and the relation of m<n is satisfied,


wherein: both of a length TCPn of a final cooling pulse and a length TLPn of a final heating pulse, which are the m-th cooling pulse and the m-th heating pulse, respectively, are determined in accordance with the scanning speed v using the following functions (1) and (4),





in a range of v<v0, TCPn/T=f1,n(v)  Function (1)





in a range of v≧v0, TCPn/T=f2,n(v)  Function (2)





in a range of v<v0, TLPn/T=g1,n(v)  Function (3)





in a range of v≧v0, TLPn/T=g2,n(v)  Function (4)


where the f1,n(v), f2,n(v), g1,n(v) and g2,n(v) each represents a continuous function of the scanning speed v to satisfy the relations of f1,n(v0)>f2,n(v0) and g1,n(v0)>g2,n(v0); the f1,n(v), f2,n(v), g1,n(v) and g2,n(v) each satisfies the condition where an existence ratio of abnormal marks, which is a ratio of the number of abnormal marks to the number of normal marks, is 1.0×10−4 or less, the number of normal mark satisfying the requirement of L/nT≧n−0.5 and the abnormal mark satisfying the requirement of L/nT<n−0.5 where L is a length of each reproduced mark obtained by reproducing the recorded marks; and v0 is any scanning speed selected to satisfy the existence ratio of the abnormal marks of 1.0×10−4 or less.


According to the recording method of the optical recording medium of the third aspect, the length TCPn of the final cooling pulse and the length TLPn of the final heating pulse are optimized so as not to take a temperature history which induces an abnormal crystal growth inherent for a recording layer material of a high-speed correspondence, thereby suppressing the occurrence of the mark length beyond specifications. Further, the length TCPn and the length TLPn are specified respectively by two types of continuous functions, and the optimum values of TCPn and TLPn are easily determined for any scanning speed v, and thus it is possible to easily carry out the recording with high reproduction reliability.


In the recording method of the optical recording medium of the third aspect, preferably, at least one of the f1,n(v) and f2,n(v) and at least one of the g1,n(v) and g2,n(v) are linear functions of the scanning speed v. Preferably, the function of m=n/2 holds if n is an even number and the function of m=(n−1)/2 holds if n is an odd number. Preferably, the functions of vH/vL≧2.4 and 0.4 vH≦v0≦0.8 vH are satisfied where a highest recording-scanning speed of the medium is represented by vH and a lowest recording-scanning speed of the medium is represented by vL.


In the recording method of the optical recording medium according to the present invention, the parameters TCPn and TLPn can be determined by the linear functions of the scanning speed v, therefore the parameters can be easily set up with few errors. Moreover, this enables decreasing the number of parameters to be pre-formatted in the optical recording medium as compared with complicated functions, and may correspond to high-speed recording at a scanning speed of 20 m/sec or more by using a 2T strategy. Still further, good characteristics can be obtained in the CAV recording because corresponding speed width and the scanning speed v0 are optimized.


Further, the present invention provides an optical recording medium. In the first aspect of an optical recording medium, there is provided an optical recording medium which is capable of being recorded using the recording method of the first aspect, wherein information able to univocally decide the v0, f1,n(v) and f2,n(v) is pre-formatted.


In the second aspect of an optical recording medium, there is provided an optical recording medium, which is capable of being recorded using the recording method of the second aspect, wherein information able to univocally decide the v0, g1,n(v) and g2,n(v) is pre-formatted.


In the third aspect of an optical recording medium, there is provided an optical recording medium, which is capable of being recorded using the recording method of the third aspect, wherein information able to univocally decide the v0, f1,n(v), f2,n(v), g1,n(v) and g2,n(v) is pre-formatted.


According to the optical recording medium of any one of the first to third aspects, the appropriate parameters can easily calculated by a recording device because the optimum parameters are pre-formatted in the optical recording media.


Further, the present invention provides an evaluation method of an optical recording medium. In the first aspect of an evaluation method, there is provided an evaluation method of an optical recording medium corresponding to different recording speeds, which comprises:


where marks are recorded on the optical recording medium by: irradiating the medium with a laser having m pulse sets each comprising a heating pulse of a power Pw and a cooling pulse of a power Pc, in which m is a natural number; and scanning the medium with the laser at a scanning speed v to record the marks each of a length nT on the medium, in which n is a natural number of 3 or more, T is a clock cycle, and the relation of m<n is satisfied, performing test recordings by variously changing a length TCPn of a final cooling pulse, which is the m-th cooling pulse; reproducing the test recorded marks; measuring respective lengths L of the reproduced marks; counting normal marks satisfying the requirement of L/nT≧n−0.5 and abnormal marks satisfying the requirement of L/nT<n−0.5; and obtaining an existence ratio of the abnormal marks, which is ratio of the number of the abnormal marks to the number of the normal marks, to evaluate the quality of the optical recording medium.


In the second aspect of an evaluation method, there is provided an evaluation method of an optical recording medium corresponding to different recording speeds, which comprises:


where the optical recording medium is a direct overwrite medium on which marks are recorded by: irradiating the medium the medium with a laser having m pulse sets each comprising a heating pulse of a power Pw and a cooling pulse of a power Pc, in which m is a natural number; and scanning the medium with the laser at a scanning speed v to record the marks each of a length nT on the medium, in which n is a natural number of 3 or more, T is a clock cycle, and the relation of m<n is satisfied, and the recorded marks are erased by: irradiating non-recorded regions of the medium, which are spaces between the marks, with the laser having an erasing pulse of a power Pe, in which the relation of Pw>Pe>Pc is satisfied,


performing test recordings by variously changing the power Pe; reproducing the test recorded marks; measuring respective lengths L of the reproduced marks; counting normal marks satisfying the requirement of L/nT≧n−0.5 and abnormal marks satisfying the requirement of L/nT<n−0.5; and obtaining an existence ratio of the abnormal marks, which is a ratio of the number of the abnormal marks to the number of the normal marks, to evaluate the quality of the optical recording medium.


In the evaluation method of the optical recording medium of the first and second aspects, preferably, the test recordings are carried out using a pattern having alternate 3T marks and 3T spaces between the marks in case of n=3. Preferably, the scanning speed is made to be an average value of the highest recording speed and the lowest recording speed of the medium. Preferably, the test recordings are carried out at the lowest recording speed of the medium using a pattern having alternate 4T marks and 4T spaces in case of n=4.





BRIEF DESCRIPTION OF THE DRAWINGS


FIG. 1A is a diagram showing NRZI data in 2T strategy.



FIG. 1B is a diagram showing a case of n=3 and m=1 in 2T strategy.



FIG. 1C is a diagram showing a case of n=8 and m=4 in 2T strategy.



FIG. 2A is a schematic diagram showing the shape of recording marks in an example of abnormal crystal growth.



FIG. 2B is a diagram showing a reproduction signal in case abnormal crystal growth exists.



FIG. 2C is a diagram showing a binaryzed signal in an example of abnormal crystal growth.



FIG. 3 is a graph showing a result from measuring a binaryzed signal of FIG. 2C by TIA.



FIG. 4 is a graph showing the dependence of the existence ratio of abnormal marks on TCP3 and v.



FIG. 5 is a graph showing the dependence of the existence ratio of abnormal marks on TLP3 and v.



FIG. 6 is a graph showing ranges of v and TCP3 when abnormal marks are more than 1.0×10−4.



FIG. 7 is a graph illustrating parameter setting methods according to the present invention and conventional art.



FIG. 8 is a graph showing the dependence of pulse length on scanning speed in Example 1.



FIG. 9 is a graph showing the dependence of the ratio of the number of abnormal marks to the number of normal marks on scanning speed in Example 1.



FIG. 10 is a graph showing the dependence of pulse length on scanning speed in Comparison Example 1.



FIG. 11 is a graph showing the dependence of the ratio of the number of abnormal marks to the number of normal marks on scanning speed in Comparison Example 1.



FIG. 12 is a graph showing the dependence of pulse length on scanning speed in Example 2.



FIG. 13 is a graph showing the dependence of the ratio of the number of abnormal marks to the number of normal marks on scanning speed in Example 2.



FIG. 14 is a graph showing the dependence of pulse length on scanning speed in Example 3.



FIG. 15 is a graph showing the dependence of the ratio of the number of abnormal marks to the number of normal marks on scanning speed in Example 3.



FIG. 16, is a graph showing the dependence of pulse length on scanning speed in Example 4.



FIG. 17 is a graph schematically showing the dependence of the existence ratio of abnormal marks on TCPn.



FIG. 18 is a graph showing the dependence of the ratio of the number of abnormal marks to the number of normal marks on TCP3 in Example 5.



FIG. 19 is a graph showing a result from obtaining the dependence of the ratio of the number of abnormal marks to the number of normal marks on Pe in Example 6.



FIG. 20 is a graph schematically showing the dependence of the ratio of the number of abnormal marks to the number of normal marks on TCPn.





BEST MODE FOR CARRYING OUT THE INVENTION
<Optical Recording Medium and Recording Method of Optical Recording Medium>

In the first embodiment of a recording method of an optical recording medium according to the present invention, a recording method of an optical recording medium corresponding to different recording speeds, comprises:


irradiating the medium with a laser having m pulse sets each comprising a heating pulse of a power Pw and a cooling pulse of a power Pc, in which m is a natural number; and


scanning the medium with the laser at a scanning speed v to record marks each of a length nT on the medium, in which n is a natural number of 3 or more, T is a clock cycle, and the relation of m<n is satisfied,


wherein:


a length TCPn of a final cooling pulse, which is the m-th cooling pulse, is determined in accordance with the scanning speed v using the following functions (1) and (2),





in a range of v<v0, TCPn/T=f1,n(v)  Function (1)





in a range of v≧v0, TCPn/T=f2,n(v)  Function (2)


where the f1,n(v) and f2,n(v) each represents a continuous function of the scanning speed v to satisfy the relation of f1,n(v0)>f2,n(v0);


the f1,n(v) and f2,n(v) each satisfies the condition where an existence ratio of abnormal marks, which is a ratio of the number of abnormal marks to the number of normal marks, is 1.0×10−4 or less, the normal mark satisfying the requirement of L/nT≧n−0.5 and the abnormal mark satisfying the requirement of L/nT<n−0.5 where L is a length of each reproduced mark obtained by reproducing the recorded marks; and


v0 is any scanning speed selected to satisfy the existence ratio of the abnormal marks of 1.0×10−4 or less.


In the second embodiment of a recording method of an optical recording medium according to the present invention, a recording method of an optical recording medium corresponding to different recording speeds, comprises:


irradiating the medium with a laser having m pulse sets each comprising a heating pulse of a power Pw and a cooling pulse of a power Pc, in which m is a natural number; and


scanning the medium with the laser at a scanning speed v to record marks each of a length nT on the medium, in which n is a natural number of 3 or more, T is a clock cycle, and the relation of m<n is satisfied,


wherein:


a length TLPn of a final heating pulse, which is the m-th heating pulse, is determined in accordance with the scanning speed v using the following functions (3) and (4),





in a range of v<v0, TLPn/T=g1,n(v)  Function (3)





in a range of v≧v0, TLPn/T=g2,n(v)  Function (4)


where the g1,n(v) and g2,n(v) each represents a continuous function of the scanning speed v to satisfy the relation of g1,n(v0)>g2,n(v0);


the g1,n(v) and g2,n(v) each satisfies the condition where an existence ratio of abnormal marks, which is a ratio of the number of abnormal marks to the number of normal marks, is 1.0×10−4 or less, the normal mark satisfying the requirement of L/nT≧n−0.5 and the abnormal mark satisfying the requirement of L/nT<n−0.5 where L is a length of each reproduced mark obtained by reproducing the recorded marks; and


v0 is any scanning speed selected to satisfy the existence ratio of the abnormal marks of 1.0×10−4 or less.


In the third embodiment of a recording method of an optical recording medium according to the present invention, a recording method of an optical recording medium corresponding to different recording speeds, comprises:


irradiating the medium with a laser having m pulse sets each comprising a heating pulse of a power Pw and a cooling pulse of a power Pc, in which m is a natural number; and


scanning the medium with the laser at a scanning speed v to record marks each of a length nT on the medium, in which n is a natural number of 3 or more, T is a clock cycle, and the relation of m<n is satisfied,


wherein:


both of a length TCPn of a final cooling pulse and a length TLPn of a final heating pulse, which are the m-th cooling pulse and the m-th heating pulse, respectively, are determined in accordance with the scanning speed v using the following functions (1) and (4),





in a range of v<v0, TCPn/T=f1,n(v)  Function (1)





in a range of v≧v0, TCPn/T=f2,n(v)  Function (2)





in a range of v<v0, TLPn/T=g1,n(v)  Function (3)





in a range of v≧v0, TLPn/T=g2,n(v)  Function (4)


where the f1,n(v), f2,n(v), g1,n(v) and g2,n(v) each represents a continuous function of the scanning speed v to satisfy the relations of f1,n(v0)>f2,n(v0) and g1,n(v0)>g2,n(v0);


the f1,n(v), f2,n(v), g1,n(v) and g2,n(v) each satisfies the condition where an existence ratio of abnormal marks, which is a ratio of the number of abnormal marks to the number of normal marks, is 1.0×10−4 or less, the normal mark satisfying the requirement of L/nT≧n−0.5 and the abnormal mark satisfying the requirement of L/nT<n−0.5 where L is a length of each reproduced mark obtained by reproducing the recorded marks; and


v0 is any scanning speed selected to satisfy the existence ratio of the abnormal marks of 1.0×10−4 or less.


In the first embodiment of an optical recording medium according to the present invention, an optical recording medium is capable of being recorded using the recording method according to the first embodiment, wherein information able to univocally decide the v0, f1,n(v) and f2,n(v) is pre-formatted.


In the second embodiment of an optical recording medium according to the present invention, an optical recording medium is capable of being recorded using the recording method according to the second embodiment, wherein information able to univocally decide the v0, g1,n(v) and g2,n(v) is pre-formatted.


In the third embodiment of an optical recording medium according to the present invention, an optical recording medium is capable of being recorded using the recording method according to the third embodiment, wherein information able to univocally decide the v0, f1,n(v), f2,n(v), g1,n(v) and g2,n(v) is pre-formatted.


The optical recording method according to the present invention will be described in detail in the following. Details of the optical recording medium according to present invention will be also clarified through the description of the recording method of optical recording medium.


An optical recording medium applied with the recording method of present invention is an optical recording medium having a constant line density of information and must be recordable and rewritable at different recording speed. For recording modes, pulse-width modulation mode in which marks and spaces between the marks having a length nT (wherein n is a natural number and T is a clock cycle) are recorded as information is preferable, and an RLL (Run Length Limited) mode has been generally used in the optical disks. EFM of CD-RW, DVD+RW and EFM+ of DVD-RW are given as their examples. In this case, the recording speed v and the clock cycle T must be taken as v×T=constant to keep the information line density constant. Moreover, v must satisfy the condition of v/r=constant to the disk radius position r in order to correspond to the CAV recording. Accordingly, the recording must be carried out at any speed below the highest recording speed vH and above the lowest recording speed vL of the medium to record at any radius position of medium by CAV. It is preferable that vH/vL≧2.4 in case of a 120 mm-diameter optical disk represented by CD, DVD.


In the optical recording medium applied with the recording method of the present invention, information is recorded by irradiating and scanning an intensity-modulated light in the vicinity of a recording layer to generate a phase change between a crystal phase and an amorphous phase in the recording layer material and form amorphous marks. Moreover, it is preferable that an optical disk using a recording layer material with a high crystallization rate is preferable and the highest recording speed vH is 20 m/s or above.


—Recording Strategies—

The information recording into these optical recording medium corresponding to high-speed recording is carried out by irradiating and scanning intensity-modulated light as described above. These recording methods are generally referred to as “recording strategies”. When forming a recording mark having a length nT, the medium is irradiated with a laser having m pulse sets each comprising a heating pulse of power Pw and a cooling pulse of power Pb. At this time, the relation of Pw>>Pb is satisfied. Moreover, it is possible that the power Pw is arbitrarily changed in conformity to the scanning speed in the recording, but the power Pw is set at a power enough to melt the recording layer. The power Pw is preferably in a range of 20 to 40 mW to correspond to 8× speed of DVD+RW. The power Pb must be very low enough to rapidly cool the recording layer melted by the heating pulses, and it is preferably in a range of 0 to 1 mW.


The pulse number m can be arbitrarily set up, and the mark length can be easily controlled by satisfying the relation of m<n. Moreover, the mark length and the pulse number can take a proportional relation by satisfying the relation of m=n−k (k is a natural number of 1 or more), and the control of mark length is further facilitated. For example, the relation of m=n−1 is satisfied in DVD+RW. However, if the recording speed becomes equivalent to the 8× speed of DVD+RW, the clock cycle T becomes 4.8 ns or less. By contrast, the response time of 10 to 90% of existent LDs is as long as 1.5 ns or more and needs 3 ns or more by coming and going. Accordingly, loss is big relative to a light emission cycle of 4.8 ns, thus sufficient heating effect and cooling effect cannot be obtained. Therefore, it is preferable to decrease m to correspond to high-speed recording with a short clock cycle T.


The 2T strategy adopted by Orange Book Part III, volume 3, version 1.1, which is a US Standard Specification of CD-RW, is given as an example of decreasing m.


An example of the 2T strategy is shown in FIG. 1A to FIG. 1C. FIG. 1A shows NRZ1 (No Return to Zero Inverted) data. FIG. 1B shows a case of n=3, m=1, and FIG. 1C shows a case of n=8, m=4. Namely, in the 2T strategy, the cycle of heating pulses becomes about 2T by taking m=n/2 when n is an even number and m=(n−1)/2 when n is an odd number. As compared with the case of m=n−1, it is possible to melt and rapidly cool the recording layer even in high-speed recording with a short clock cycle T. Moreover, it is preferable to make m≦n/2 to correspond to a high-speed recording of 8× speed or above of DVD.


The length of heating pulse and the length of cooling pulse, i.e. each irradiation time, can be arbitrarily set up, respectively, but it is preferable that appropriate values are set up in accordance with changes of the scanning speed v and the clock cycle T in the recording.


A recording strategy of CD-RW corresponding to the recording and rewriting of 4× speed and to 10× speed is specified in the Orange Book Part III, volume 2, version 1.1 which is a US Standard Specification of CD-RW. At the 4× speed (v=4.8 m/s, T=57.9 ns), the heating pulse=0.2 T, the cooling pulse=0.8 T; at the 8× speed (v=9.6 m/s, T=28.9 ns), the heating pulse=0.4 T, the cooling pulse=0.6 T; at the 10× speed (v=12.0 m/s, T=23.1 ns), the heating pulse=0.5 T, the cooling pulse=0.5 T. Namely, the higher the speed, the longer the length of heating pulse to the clock cycle and the shorter the length of cooling pulse to the clock cycle. The dependence to the v becomes a proportional relation.


The heating pulse width relative to 1× speed to 2.4× speed is specified by a proportional expression of the scanning speed v in DVD+ReWritable 4.7 Gbytes Basic Format Specifications System Description, version 1.2 which is a standard specification of DVD+RW.


Moreover, the respective lengths of heating pulse and cooling pulse can be described with optimum recording parameters at arbitrary recording velocities by describing the lengths with continuous functions of scanning speed v in Japanese Laid-Open Patent Application (JP-A) 2000-322740, JP-A 2001-118245 and JP-A 2001-243626.


If v is decided in a recording speed region, i.e., a speed region of vL≦v≦vH, the lengths of heating pulse and cooling pulse can be uniquely decided in all these techniques.


However, these techniques are not applicable in the optical recording medium using the above-mentioned recording layer material able to correspond to the vH≧20 m/s. Although the crystallization rate of the recording layer material must be increased to correspond to the high-speed recording, the time for irradiating a light on an optical recording medium is inevitably shortened (inversely proportioned to the scanning speed) by accelerating the scanning speed in the recording. As a result, the crystallization or the amorphous phase formation must be carried out in a shorter time. Because the amorphous phase formation is carried out by rapidly cooling the recording layer, it is not inconvenient from the fact that the higher the scanning speed, the easier the layer is quenched, but the crystallization must be slowly cooled, therefore it becomes difficult if the irradiation time is shortened. For this reason, it is preferable that the crystallization be made in a shorter irradiation time by increasing the crystallization rate of a recording layer material.


However, abnormal crystal growth occurs easily due to a little difference of recording conditions in the recording layer material having such a high crystallization rate. An example of abnormal crystal growth is schematically shown in FIG. 2A. FIG. 2A shows the recorded marks in the case where the recording is carried out by a recording strategy shown in FIG. 1B using a pattern having alternate 3T marks and 3T spaces. (It is possible that the mark shape is observed by a transmission electron scope.) As shown in FIG. 2A, marks A and marks C are normal recording marks, and abnormal crystal growth occurs at the end of marks B. A reproduction signal in case of such abnormal crystal growth distorts to the normal case (dotted line) as shown in FIG. 2B. As a result, a signal after binarization is as shown in like FIG. 2C, and only the marks B with abnormal crystal growth is reproduced in shorter than 3T.


If the signal after binarization of FIG. 2C is measured by TIA (Time Interval Analysis) to analyze the rate of occurrence of marks B, a result such as that shown in FIG. 3 can be obtained. Namely, it is divided into a component making a normal distribution with 3T as central value and a component distributing in a shorter side. This component distributing in the shorter side is caused by abnormal crystal growth. If a ratio of the number of marks having abnormal crystal growth (abnormal marks) to the number of marks having normal distribution (normal marks) is taken, it has been found that the ratio greatly depends upon the recording speed v, the length TLP3 of final heating pulse and the length TCP3 of final cooling pulse.


The dependence of the existence ratio of abnormal marks, i.e., the ratio of the number of abnormal marks to the number of normal marks, on TCP3, and v is shown in FIG. 4. The dependence of the existence ratio of abnormal marks on TLP3 and v is shown in FIG. 5. An optical recording medium used for the measurement is a sample recordable until 8× speed of DVD+RW (i.e., vH=27.9 m/s). The existence ratio of abnormal marks becomes very high in some range of T at all recording velocities. The abnormal marks become a signal beyond the specification in reproduction as described above, therefore they become a reason for reading errors. If the existence ratio is more than 1.0×10−4, a possibility of becoming uncorrectable errors is high, thus the reliability of reproduction signal greatly reduces.


A method for measuring the TCPn dependence of an existence ratio of abnormal marks is explained below.


The existence ratio is measured by carrying out the recording of a pattern in which nT marks and nT spaces are alternately arrayed. At this time, the TLPn can be arbitrarily set up in accordance with v, but it is preferable that characteristics such as degree of modulation, asymmetry, jitter, etc. are optimized to better values, and it is preferable that the TLPn is set to an irradiation time substantially the same as other pulses of a pulse train, i.e., the first pulse to (m−1)th pulse. At this time, the TLPn may be set using a continuous function or using two functions in accordance with the scanning speed v.


Optimum recording powers are set for the irradiation power and the erasure power of heating pulses. The optimum recording powers may use the pre-formatted information on the optical recording medium or may be set up by OPC (Optimum Power Control).


The scanning speed is set at the scanning speed v0 at which a function used for setting the TCPn is changed from the function (1) to the function (2) described hereinafter. At this time, the clock cycle T must also be properly set up in conformity to the scanning speed.


The test recordings are carried out by the above settings at a variety of TCPn. The range of varying TCPn is arbitrarily settable, but a range of OT to 3T is preferable. If the setting is too long, a possibility of deviating tracking and focusing increases because the cooling pulse lengthens and the irradiation time with a low power prolongs.


When the recorded region is reproduced to count the number of abnormal marks, an appropriate binarization unit and a time interval analyzer are used as described above. Analysis result of time interval analyzer is as shown in FIG. 3 (example of n=3). Here, mark with a length less than (n−0.5)T is counted as abnormal mark. In contrast, mark with a length in a range of (n±0.5)T is counted as normal mark.


The abnormal mark ratio is calculated by taking the ratio of the number of abnormal marks to the number of normal marks.


The dependence of the existence ratio of abnormal marks thus measured is schematically shown in FIG. 17.


A range where the existence ratio is 1.0×10−4 or less can be found in the following two cases (1) and (2).






T
CPn
≦T
CPn(1)  (1)






T
CPn
≧T
CPn(2)  (2)


Appropriate values of TCPn are set up within respective ranges of the (1) and (2), the continuous functions f1,n and f2,n are set up so that the requirement of TCPn/T=f1,n(v0) in the case (1) and the requirement of TCPn/T=f2,n(v0) in the case (2) are satisfied. The respective continuous functions must be set up so that good characteristics at the lowest recording speed and the highest recording speed can be obtained.


The TLPn and the functions g1,n, g2,n can be set up in the same manner.



FIG. 6 shows the ranges of the TCP3 and v when the existence ratio of abnormal marks is more than 1.0×10−4. In a grey region in FIG. 6, the existence ratio of abnormal marks is high, therefore the TCP3 can not be determined. Here, if attention is paid to a point of 3.3× speed (v=11.5 m/s), a settable range of TCP3 is limited to TCP3>1.5T. On the other hand, two kinds of solutions of TCP3>1.5T and TCP3<0.6T are permitted at the 8× speed (v=27.9 m/s), but TCP3>1.5T results in the impossibility of a normal recording and a high asymmetry because the mark length becomes too long. Accordingly, TCP3<0.6T must be taken.


Here, in order to correspond to the CAV recording, it is necessary that any recording speeds in a range of 3.3× to 8× velocities (11.5-27.9 m/s) can be set. An interpolation method wherein a continuous function is simply interpolated between the set values of TCPn at 3.3× and 8× speeds is generally used in the conventional art. An example thereof is shown in FIG. 7.


The parameter TCP3 setting method in conventional art is shown by a broken line of FIG. 7. A case of the simplest linear function is shown as an example. In this case, at a middle speed, the parameter TCP3 must be set within the range of high existence ratio of abnormal marks, resulting in the significant deterioration of the reproduction reliability of recorded signal.


Contrarily, in the recording method of the optical recording medium according to the present invention, the parameter TCPn is set at a value out of the region of the high existence ratio of abnormal marks. Namely, a function used for setting the parameter is changed from the following function (1) to the following function (2) at a certain middle speed v0 (vL≦v0≦vH), thereby the parameter can be set at a value out of the region of the high existence ratio of abnormal marks.


Namely, in the present invention, the length TCPn of the final cooling pulse is determined using the following functions,





in a range of v<v0, TCPn/T=f1,n(v)  Function (1)





in a range of v≧v0, TCPn/T=f2,n(v)  Function (2)


where both the f1,n(v) and f2,n(v) are continuous functions of v to satisfy the relation of f1,n(v0)>f2,n(v0), resulting in the avoidance of a high-error region.



FIG. 7 shows an example in the case of n=3, i.e., TCP3. The parameter setting method of the present invention is shown by a solid line in FIG. 7, where vH=27.9 m/s, vL=11.5 m/s, and v0=20.9 m/s.


The region of the high existence ratio of abnormal marks can be avoided by changing the setting values TCP3 greatly and discontinuously at v=v0.


Although the speed v0 at which a function used for setting the TCP3 is changed from the function (1) to the function (2) can be arbitrarily set, the speed should be so selected that good characteristics, such as jitter characteristic, degree of modulation can be obtained, wherein the TCPn is set at a value out of the region of the high existence ratio of abnormal marks. Accordingly, the speed is preferably in a range of 0.4 vH≦v0≦0.8 vH.


For the continuous functions f1,n(v) and f2,n(v), aforesaid relation must hold at v=v0, but an arbitrary function system can be set up. It is more preferable to take the functions as linear functions, respectively, to facilitate the setting of the parameter.


With respect to the length TLPn of final heating pulse, the same method is also applicable.


Namely, when the TLPn is set using the following functions (3) and (4),





in a range of v<v0, TLPn/T=g1,n(v)  Function (3)





in a range of v≧v0, TLPn/T=g2,n(v)  Function (4)


where both the g1,n(v) and g2,n(v) are continuous functions of v to satisfy the relation of g1(v0)<g2(v0), it enables greatly decreasing the number of abnormal marks at a middle recording speed.


Any function system may be used for g1,n(v) and g2,n(v), but the setting of the parameter can be easily carried out by taking the system as linear functions. Although the speed v0 at which the function used for setting the TCP3 is changed from the function (3) to the function (4) can be arbitrarily set, the speed should be so selected that good characteristics, such as jitter characteristic, degree of modulation can be obtained, wherein the TLPn is set at a value out of the region of the high existence ratio of abnormal marks. Accordingly, the speed is preferably in a range of 0.4 vH≦v0≦0.8 vH.


It is possible to decrease the number of abnormal marks by setting either one of the TCPn and the TLPn using one continuous function for the scanning speed v and setting the other using two functions or by setting both of the TCPn and the TLPn using two functions. Which parameters are set using two functions are decided by seeing whether the number of abnormal marks and basic recording signal characteristics (jitter, asymmetry, etc.) are in the desired ranges or not.


<Optical Recording Medium>

As described above, the occurrence of abnormal marks greatly depends upon material properties such as the crystallization rate, etc. of a recording layer material. Accordingly, information capable of specifying v0, f1,n(v), f2,n(v), g1,n(v) and g2,n(v) may be pre-formatted on an optical recording medium in advance. For example, when the following functions are satisfied;






f
1,n(v)=a1×v+b1






f
2,n(v)=a2×v+b2,


wherein a1, b1, a2, b2 are inherent constants of optical recording medium, the information showing a1, b1, a2, b2 and v0 is pre-formatted on the optical recording medium in advance.


As a pre-formatting method used in the present technique, for example, ATIP Extra Information of CD-RW and Physical Information of DVD+RW, etc. are given. If the above information are pre-formatted on each optical recording medium, a recording device can acquire optimum recording parameters from the pre-formatted information.


<Evaluation Method of Optical Recording Medium>

In the first embodiment of an evaluation method of an optical recording medium according to the present invention, where marks are recorded on the optical recording medium by: irradiating the medium with a laser having m pulse sets each comprising a heating pulse of a power Pw and a cooling pulse of a power Pc, in which m is a natural number; and scanning the medium with the laser at a scanning speed v to record the marks each of a length nT on the medium, in which n is a natural number of 3 or more, T is a clock cycle, and the relation of m<n is satisfied, an evaluation method of an optical recording medium corresponding to different recording speeds, comprises: performing test recordings by variously changing a length TCPn of a final cooling pulse, which is the m-th cooling pulse; reproducing the test recorded marks; measuring respective lengths L of the reproduced marks; counting normal marks satisfying the requirement of L/nT≧n−0.5 and abnormal marks satisfying the requirement of L/nT<n−0.5; and obtaining an existence ratio of the abnormal marks, which is a ratio of the number of the abnormal marks to the number of the normal marks, to evaluate the quality of the optical recording medium.


In the second embodiment of an evaluation method of an optical recording medium according to the present invention, where the optical recording medium is a direct overwrite medium on which marks are recorded by: irradiating the medium the medium with a laser having m pulse sets each comprising a heating pulse of a power Pw and a cooling pulse of a power Pc, in which m is a natural number; and scanning the medium with the laser at a scanning speed v to record the marks each of a length nT on the medium, in which n is a natural number of 3 or more, T is a clock cycle, and the relation of m<n is satisfied, and the recorded marks are erased by: irradiating non-recorded regions of the medium, which are spaces between the marks, with the laser having an erasing pulse of a power Pe, in which the relation of Pw>Pe>Pc is satisfied, an evaluation method of an optical recording medium corresponding to different recording speeds, comprises: performing test recordings by variously changing the power Pe; reproducing the test recorded marks; measuring respective lengths L of the reproduced marks; counting normal marks satisfying the requirement of L/nT≧n−0.5 and abnormal marks satisfying the requirement of L/nT<n−0.5; and; obtaining an existence ratio of the abnormal marks, which is a ratio of the number of the abnormal marks to the number of the normal marks, to evaluate the quality of the optical recording medium.


As described above, the abnormal crystal growth greatly depends upon the material properties of a recording layer material, such as a crystallization rate and thermal properties, and recording methods, i.e., the setting method of the TLPn and the TCPn. When a phase-changing material, for example, an alloy, is used for the recording layer material, the number of abnormal marks can be decreased if the purity and compositional ratio of constituent elements are properly controlled. However, in general, a disk is a multilayer structure of thin films, so the number of abnormal marks also fluctuates with the film-formed state of respective layers. Namely, the thermal capacity and thermal conductivity of respective layers fluctuate with varying the thickness and film quality of layers, leading to variations of the thermal medium designs. The variations of thermal medium design sometimes has an affect similar to changing recording methods, therefore the variations of the thermal medium design affects a rise in the number of abnormal marks, etc. Accordingly, an adequate evaluation method becomes necessary for realizing a stabilized production of medium.


A specific evaluation method will be described below.


When an optical recording medium is inspected, the sensitivity is bad and an adequate inspection is extremely difficult in the case of using the optimum recording condition, i.e., a recording condition with few abnormal marks. Namely, even if a deviation from an objective thermal design occurs, the increase in number of abnormal marks is only a little and therefore does not exceed measuring errors in many cases.


Therefore, an evaluation method with an even better sensitivity is needed.


The dependence of the abnormal mark ratio on the setting value of the TCPn is shown in FIG. 17. The dependence in case disk characteristics fluctuate is shown in FIG. 20. The abnormal mark ratio for a normal disk is expressed by a solid line. The abnormal mark ratio in case disk characteristics deviate is shown by a broken line.


As described above, the condition with a very low number of abnormal marks (condition A) is the optimum condition for the recording parameter TCPn. However, when disk fluctuates in the optimum condition, a fluctuation of the number of abnormal marks is small. Therefore, an inspection reference setting range in case of inspecting the fluctuation of disk in the optimum condition becomes a very narrow region. Thus, if the TCPn in the small fluctuation region of the number of abnormal marks is used as inspection parameters, it causes a significant deterioration of inspection accuracy when measuring errors occur.


In contrast, the case of the TCPn in a high number of abnormal marks (condition B) enables adopting a broad setting range of inspection reference because of the large fluctuation of the number of abnormal marks. Moreover, the inspection accuracy does not significantly deteriorate even if measuring errors occur.


Considering the above points, accomplishing inspection in a state in which the recording conditions are intentionally deviated from the optimum conditions enables setting up an inspection condition able to accurately judge the fluctuation of medium.


Any parameters can be given as parameters to be deviated intentionally for the inspection, but a parameter exerting a large effect on the number of abnormal marks is preferably chosen, for example, the TCPn or Pe/Pw which is the ratio of erasure power Pe and recording power Pw is given.


Moreover, any data can be used as recording data in the inspection. In order to improve the inspection accuracy, it is more preferable to record a pattern having alternate marks and spaces each having the same length than a random data pattern having alternate marks and spaces having random lengths, enabling reducing the effect of interference between symbols (a phenomenon in which the length of adjacent mark or space affect a reproduction signal), thus the case is more preferable.


Furthermore, in the case of using the pattern with marks and spaces each having the same length, the length can be arbitrary set, but it is preferable to set up the most efficient length for recording speed. More preferably, the recording is carried out using a pattern with marks and spaces each having a length as short as possible, resulting in the increase of the number of samples for the evaluation even in the same reproducing length. Thereby, the accuracy is further improved. As examples of the pattern, a pattern having alternate 3T marks and spaces, a pattern having alternate 4T marks and spaces are given.


According to the present invention, the recording can be easily carried out with high reliability while suppressing the occurrence of mark lengths beyond the specification because the length of the final heating pulse and/or the length of the final cooling pulse are specified by two kinds of continuous functions, and the optimum values of the length of the final heating pulse and/or the length of the final cooling pulse can be easily determined for an arbitrary scanning speed.


The present invention will be explained more concretely by examples and comparative examples, but the present invention is not limited to the examples.


EXAMPLE 1

Since there was no DVD medium corresponding to a high-speed recording of 20 m/sec or above in the market, a sample disk was prepared.


A 60 nm-thick lower protective layer made of a mixture of ZnS and SiO2, a 15 nm-thick recording layer made of a GaSbSnGe alloy, a 10 nm-thick upper protective layer made of a mixture of ZnS and SiO2 and a 200 nm-thick reflective layer made of Ag were successively laminated on a 0.6 mm-thick and 120 mm-diameter polycarbonate DVD+RW substrate having a spiral continuous group of 0.74 μm track pitch by sputtering process. Further, another substrate was pasted on the reflective layer with a commercial UV resin adhesive for optical disk to make it into a 1.2 mm-thick disk. The shape fully satisfied the specification of DVD+RW.


Subsequently, the recording layer was crystallized over the entire surface by an initiation apparatus for a phase-changing type optical disk. The prepared disk was good and satisfied various specifications of DVD+RW in an unrecorded state.


A recording evaluation on the prepared sample disk was carried out by a recording and reproduction evaluation apparatus for DVD+RW (made by Pulstec Industry Inc., DDU1000). The optical pick-up used for recording and reproduction is as follows.

    • Wavelength: 659 nm
    • Objective lens NA: 0.65
    • Irradiation power at reproduction: 0.7 mW
    • Irradiation power in recording: 1.0 to 40.0 mW


      The scanning speed can be set up in a range of 3.49 m/s-30.0 m/s.


A data generator DTG5027 made by Tectronics Co. was used for preparation of a recording strategy. The recording strategy was adopted as the 2T strategy, namely a recording strategy satisfying the condition of n=2 m where n is an even number and the condition of n=2 m+1 where n is an odd number. Here, a pattern having alternate 3T marks and 3T spaces was recorded. Strategy parameters of 3T marks were two, i.e., the heating pulse length TLP3 and the cooling pulse length TCP3. The recordings were carried out at various recording speeds in the conditions of Table 1.













TABLE 1






Scanning
Clock




Speed
speed v (m/s)
cycle T (ns)
TLP3/T
TCP3/T



















3.3X
11.52
11.6
0.313
2.125


4.0X
13.96
9.6
0.375
2.125


5.0X
17.45
7.6
0.438
2.125


6.0X
20.94
6.4
0.500
2.125


6.0X
20.94
6.4
0.500
0.500


7.0X
24.43
5.5
0.563
0.625


8.0X
27.92
4.8
0.625
0.750









Moreover, the dependence of the parameters TLP3 and TCP3 on scanning speed is shown in FIG. 8.


In case of v0=20.94 m/s, TCP3/T can be described by the following functions,






v<v
0
, T
CP3
/T=f
1,3(v)=2.125






v≧v
0
, T
CP3
/T=f
2,3(v)=0.036v−0.25


where the relation of f1,3(v0)>f2,3(v0) was satisfied.


In the recording by this method, the dependence of the ratio of the number of abnormal marks to number of normal marks on scanning speed was obtained. The result is shown in FIG. 9. The existence ratio of abnormal marks was 1.0×10−4 or less in a speed range of 11.52 m/s to 27.92 m/s, thus good reproduction reliability was obtained.


COMPARISON EXAMPLE 1

For a sample disk same as Example 1, the recording was carried out using the same manner as Example 1, except for using the parameters of Table 2, instead of Table 1. As shown Table 2, the parameters TLP3 and TCP3 were determined using a single continuous function as before.













TABLE 2






Scanning
Clock




Speed
speed v (m/s)
cycle T (ns)
TLP3/T
TCP3/T



















3.3X
11.52
11.6
0.313
2.125


4.0X
13.96
9.6
0.375
1.850


5.0X
17.45
7.6
0.438
1.575


6.0X
20.94
6.4
0.500
1.300


7.0X
24.43
5.5
0.563
1.025


8.0X
27.92
4.8
0.625
0.750









The dependence of the parameters TCP3 and TLP3 on scanning speed is shown in FIG. 10. Each of two parameters was determined using a continuous linear function. The dependence of the ratio of the number of abnormal marks to number of normal marks on scanning speed is shown in FIG. 11. From the result of FIG. 11, it has been found that except for scanning speeds of 11.52 m/s, 27.92 m/s, the reproduction reliability of recorded information significantly deteriorates because the existence ratio of abnormal marks is more than 1.0×10−4.


EXAMPLE 2

For a sample disk same as Example 1, the recording was carried out by the same manner as Example 1, except for using the parameters of Table 3, instead of Table 1.













TABLE 3






Scanning
Clock




Speed
speed v (m/s)
cycle T (ns)
TLP3/T
TCP3/T



















3.3X
11.52
11.6
0.313
2.125


4.0X
13.96
9.6
0.328
1.850


5.0X
17.45
7.6
0.344
1.575


6.0X
20.94
6.4
0.359
1.300


6.0X
20.94
6.4
0.625
1.300


7.0X
24.43
5.5
0.656
1.025


8.0X
27.92
4.8
0.688
0.750









The dependence of the parameters TLP3 and TCP3 on scanning speed is shown in FIG. 12. TCP3 was determined using a continuous function, but TLP3 was determined using two functions. Namely, in a range of v<v0, TLP3/T=g1,3(v)=0.00489 v+0.258; in a range of v≧v0, TLP3/T=g2,3 (v)=0.009 v+0.438. Moreover, the relation of g1,3 (v0)<g2,3 (v0) was satisfied.


The recording was carried out by this recording method, and a result from measuring the number of abnormal marks and number of normal marks is shown in FIG. 13.


The number of abnormal marks increased compared with Example 1, but the existence ratio of abnormal marks was in a range of 1.0×10−4 or less. The number of abnormal marks was greatly decreased even if compared with Comparison Example 1.


EXAMPLE 3

For a sample disk same as Example 1, the recording was carried out using the same manner as Example 1, except that a pattern having alternate 10T marks and 10T spaces was recorded by a 2T strategy of n=10 and m=5 and the parameters of Table 4 were used. Here, the length of heating pulses was taken to be the same as the length of final heating pulse, and the same values as those of Example 1 were set.













TABLE 4






Scanning
Clock




Speed
speed v (m/s)
cycle T (ns)
TLP3/T
TCP3/T



















3.3X
11.52
11.6
0.313
1.875


4.0X
13.96
9.6
0.375
1.750


5.0X
17.45
7.6
0.438
1.625


6.0X
20.94
6.4
0.500
1.500


6.0X
20.94
6.4
0.500
0.500


7.0X
24.43
5.5
0.563
0.250


8.0X
27.92
4.8
0.625
0.000









The dependence of the parameters TLP10 and TCP10 on scanning speed is shown in FIG. 14. Namely, TCP10/T can be described by the following functions in case of v0=20.94 m/s,






v<v
0
, T
CP10
/T=f
1,10(v)=−0.0391v+2.312






v≧v
0
, T
CP10
/T=f
2,10(v)=−0.072v+2.00


where the relation of f1,10 (v0)<f2,10 (v0) was satisfied.


Similarly, the results of measuring the ratio of the number of abnormal marks to number of normal marks are shown in FIG. 15. It has been confirmed that the number of abnormal marks is small and the reproduction reliability of recording signal is high in all measured regions. Further, it has been confirmed that it is effective for the recording of longer marks (large n) as well as the marks in case of n=3 and m=1.


EXAMPLE 4

For a sample disk same as Example 1, the recording was carried out using the same manner as Example 1, except for using the parameters of Table 5.













TABLE 5






Scanning
Clock




Speed
speed v (m/s)
cycle T (ns)
TLP3/T
TCP3/T



















3.3X
11.52
11.6
0.313
2.125


6.0X
20.94
6.4
0.500
2.125


6.0X
20.94
6.4
0.613
0.432


8.0X
27.92
4.8
0.688
0.750









The dependence of the parameters TCP3 and TLP3 on scanning speed is shown in FIG. 16. Both TCP3 and TLP3 were determined using two functions. When the same evaluation was carried out as Example 1, the existence ratio of abnormal marks was 1.0×10−4 or less at each scanning speed.


EXAMPLE 5

Two kinds of sample disks were newly prepared similar to the sample disk of Example 1 (disk 1) except for changing the recording layer thickness and the upper protective layer thickness. Namely, one sample disk, which is referred to as a disk 2, was prepared having a 19 nm-thick recording layer and a 12 nm-thick upper protective layer, and the other, which is referred to as a disk 3, was prepared having a 12 nm-thick recording layer and a 6 nm-thick upper protective layer.


A pattern having alternate 3T marks and 3T spaces was recorded on the prepared disks 1 to 3, and the ratio of the number of abnormal marks to the number of normal marks was similarly measured as Example 1. At this time, the scanning speed was taken as 20.9 m/s equivalent to 6× speed of DVD, and the recordings were carried out by variously changing TCP3 in a range of 0.75T to 2.25T.


The TCP3 dependence of the ratio of the number of abnormal marks to the number of normal marks is shown in FIG. 18. It has been found that the ratio of the number of abnormal marks to the number of normal marks greatly varies in disks of different constitutions.


Accordingly, it is possible to inspect the fluctuation of the constitution of optical recording medium by the above method.


EXAMPLE 6

The recording and evaluation of disks 1 to 3 same as Example 5 were similarly carried out as Example 1, except that the scanning speed was taken as 20.9 m/s equivalent to 6× speed of DVD, and TCP3 was fixed at 0.75T.


A pattern having alternate 3T marks and 3T spaces was recorded and the ratio of the number of abnormal marks to the number of normal marks was measured in a manner similar to that of Example 5. At this time, the recordings were carried out by variously changing the erasure power Pe of recording condition. The dependence of the ratio of the number of abnormal marks to the number of normal marks on Pe is shown in FIG. 19. In FIG. 19, the horizontal axis is a value specified by Pw in the case where Pw was fixed at 34 mW.


From FIG. 19, it has been found that the number of abnormal marks changes with changing the erasure power Pe. Particularly, in a range of low Pe/Pw, the number of abnormal marks greatly varied in the disks 1 to 3.


Accordingly, it is possible to inspect the fluctuation of the constitution of the disk by changing the erasure power Pe when the constitution of the disk fluctuates as with disks 1 to 3.

Claims
  • 1. A recording method of an optical recording medium corresponding to different recording speeds, comprising: irradiating the medium with a laser having m pulse sets each comprising a heating pulse of a power Pw and a cooling pulse of a power Pc, in which m is a natural number; andscanning the medium with the laser at a scanning speed v to record marks each of a length nT on the medium, in which n is a natural number of 3 or more, T is a clock cycle, and the relation of m<n is satisfied,wherein:a length TCPn of a final cooling pulse, which is the m-th cooling pulse, is determined in accordance with the scanning speed v using the following functions (1) and (2), in a range of v<v0, TCPn/T=f1,n(v)  Function (1)in a range of v≧v0, TCPn/T=f2,n(v)  Function (2),
  • 2. The recording method of an optical recording medium according to claim 1, further comprising properly controlling a length TLPn of the final heating pulse, which is m-th heating pulse, in accordance with the scanning speed v.
  • 3. The recording method according to claim 1, wherein at least one of the f1,n(v) and f2,n(v) is a linear function of the scanning speed v.
  • 4. A recording method of an optical recording medium corresponding to different recording speeds, comprising: irradiating the medium with a laser having m pulse sets each comprising a heating pulse of a power Pw and a cooling pulse of a power Pc, in which m is a natural number; andscanning the medium with the laser at a scanning speed v to record marks each of a length nT on the medium, in which n is a natural number of 3 or more, T is a clock cycle, and the relation of m<n is satisfied,wherein:a length TLPn of a final heating pulse, which is the m-th heating pulse, is determined in accordance with the scanning speed v using the following functions (3) and (4), in a range of v<v0, TLPn/T=g1,n(v)  Function (3)in a range of v≧v0, TLPn/T=g2,n(v)  Function (4)
  • 5. The recording method of optical recording medium according to claim 4, further comprising properly controlling a length TCPn of the final cooling pulse, which is the m-th cooling pulse, in accordance with the scanning speed v.
  • 6. The recording method according to claim 4, wherein at least one of the g1,n(v) and g2,n(v) is a linear function of the scanning speed v.
  • 7. A recording method of an optical recording medium corresponding to different recording speeds, comprising: irradiating the medium with a laser having m pulse sets each comprising a heating pulse of a power Pw and a cooling pulse of a power Pc, in which m is a natural number; andscanning the medium with the laser at a scanning speed v to record marks each of a length nT on the medium, in which n is a natural number of 3 or more, T is a clock cycle, and the relation of m<n is satisfied,wherein:both of a length TCPn of a final cooling pulse and a length TLPn of a final heating pulse, which are the m-th cooling pulse and the m-th heating pulse, respectively, are determined in accordance with the scanning speed v using the following functions (1) and (4), in a range of v<v0, TCPn/T=f1,n(v)  Function (1)in a range of v≧v0, TCPn/T=f2,n(v)  Function (2)in a range of v<v0, TLPn/T=g1,n(v)  Function (3)in a range of v≧v0, TLPn/T=g2,n(v)  Function (4)
  • 8. The recording method according to claim 4, wherein the functions of vH/vL≧2.4 and 0.4 vH/vL≦v0≦0.8 vH are satisfied where a highest recording speed of the medium is represented by vH and a lowest recording speed of the medium is represented by vL.
  • 9. The recording method according to claim 1, wherein if n is an even number, the function of m=n/2 holds, and if n is an odd number, the function of m=(n−1)/2 holds.
  • 10. The recording method according to claim 1, wherein the functions of vH/vL≧2.4 and 0.4 vH/vL≦v0≦0.8 vH are satisfied where a highest recording speed of the medium is represented by vH and a lowest recording speed of the medium is represented by vL.
  • 11. The recording method according to claim 4, wherein if n is an even number, the function of m=n/2 holds, and if n is an odd number, the function of m=(n−1)/2 holds.
  • 12. The recording method according to claim 7, wherein at least one of the f1,n(v) and f2,n(v) and at least one of the g1,n(v) and g2,n(v) are linear functions of the scanning speed v.
  • 13. The recording method according to claim 7, wherein if n is an even number, the function of m=n/2 holds, and if n is an odd number, the function of m=(n−1)/2 holds.
  • 14. An evaluation method of an optical recording medium corresponding to different recording speeds, where marks are recorded on the optical recording medium by:irradiating the medium with a laser having m pulse sets each comprising a heating pulse of a power Pw and a cooling pulse of a power Pc, in which m is a natural number; andscanning the medium with the laser at a scanning speed v to record the marks each of a length nT on the medium, in which n is a natural number of 3 or more, T is a clock cycle, and the relation of m<n is satisfied,the evaluation method comprising:performing test recordings by variously changing a length TCPn of a final cooling pulse, which is the m-th cooling pulse;reproducing the test recorded marks;measuring respective lengths L of the reproduced marks;counting normal marks satisfying the requirement of L/nT≧n−0.5 and abnormal marks satisfying the requirement of L/nT<n−0.5; andobtaining an existence ratio of the abnormal marks, which is a ratio of the number of the abnormal marks to the number of the normal marks, to evaluate the quality of the optical recording medium.
  • 15. An evaluation method of an optical recording medium corresponding to different recording speeds, where the optical recording medium is a direct overwrite medium on which marks are recorded by:irradiating the medium the medium with a laser having m pulse sets each comprising a heating pulse of a power Pw and a cooling pulse of a power Pc, in which m is a natural number; andscanning the medium with the laser at a scanning speed v to record the marks each of a length nT on the medium, in which n is a natural number of 3 or more, T is a clock cycle, and the relation of m<n is satisfied,and the recorded marks are erased by:irradiating non-recorded regions of the medium, which are spaces between the marks, with the laser having an erasing pulse of a power Pe, in which the relation of Pw>Pe>Pc is satisfied,the evaluation method comprising:performing test recordings by variously changing the power Pe;reproducing the test recorded marks;measuring respective lengths L of the reproduced marks;counting normal marks satisfying the requirement of L/nT≧n−0.5 and abnormal marks satisfying the requirement of L/nT<n−0.5; and; obtaining an existence ratio of the abnormal marks, which is a ratio of the number of the abnormal marks to the number of the normal marks, to evaluate the quality of the optical recording medium.
  • 16. The evaluation method according to claim 15, wherein the test recordings are carried out using a pattern having alternate 3T marks and 3T spaces between the marks in case of n=3.
  • 17. The evaluation method according to claim 15, wherein the scanning speed is made to be an average value of the highest recording speed and the lowest recording speed of the medium.
  • 18. The evaluation method according to claim 15, wherein the test recordings are carried out at the lowest recording speed of the medium using a pattern having alternate 4T marks and 4T spaces in case of n=4.
  • 19. The evaluation method according to claim 14, wherein the test recordings are carried out using a pattern having alternate 3T marks and 3T spaces between the marks in case of n=3.
  • 20. The evaluation method according to claim 14, wherein the scanning speed is made to be an average value of the highest recording speed and the lowest recording speed of the medium.
  • 21. The evaluation method according to claim 14, wherein the test recordings are carried out at the lowest recording speed of the medium using a pattern having alternate 4T marks and 4T spaces in case of n=4.
  • 22. The recording method according to claim 7, wherein the functions of vH/vL≧2.4 and 0.4 vH/vL≦v0≦0.8 vH are satisfied where a highest recording speed of the medium is represented by vH and a lowest recording speed of the medium is represented by vL.
  • 23. An optical recording medium, which is capable of being recorded using the recording method according to claim 1, wherein information able to univocally decide the v0, f1,n(v) and f2,n(v) is pre-formatted.
  • 24. An optical recording medium, which is capable of being recorded using the recording method according to claims 4, wherein information able to univocally decide the v0, g1,n(v) and g2,n(v) is pre-formatted.
  • 25. An optical recording medium, which is capable of being recorded using the recording method according to claim 7, wherein information able to univocally decide the v0, f1,n(v), f2,n(v), g1,n(v) and g2,n(v) is pre-formatted.
Priority Claims (2)
Number Date Country Kind
2004-265953 Sep 2004 JP national
2005-134906 May 2005 JP national
PCT Information
Filing Document Filing Date Country Kind 371c Date
PCT/JP2005/017224 9/13/2005 WO 00 10/9/2007