Patent Application
20100118681
The present invention relates to a write-once optical recording medium, which in addition to the write-once properties also has rewritable properties.
Conventional recordable optical recording media can be divided into write-once optical recording media (WO-media) and rewritable optical recording media (RW-media). A plurality of recording materials for both types of media are known. For example, WO-media are typically realized using organic dyes, metal oxides and nitrides, or bilayers such as a Cu/Si bilayer. RW-media are generally realized using phase-change materials such as Ge2Sb2Te5 or Ag3In5Sb71Te21. Usually a single phase-change layer is used.
Though phase-change layers are typically used for RW-media, they may likewise be used for WO-media. For example, U.S. Pat. No. 6,841,218 discloses the usage of two adjacent recording sublayers of a phase-change material for a write-once optical recording medium. The first recording sublayer comprises a first composition which can be changed into another composition more stable in an amorphous state by combining with a component included in the second recording sublayer.
A further optical recording medium having two recording sublayers is disclosed in U.S. Pat. No. 5,796,708. Information marks are recorded on the medium by alloying material of the two recording sublayers using a light beam.
Still a further optical recording medium having two recording sublayers is disclosed in JP 02-156435. The medium has two layers. A first layer is a stable phase-change layer and serves as a write-once layer. Using an increased beam energy the first layer and the second layer are alloyed to form a rewritable phase-change layer. In order to enable rewritable recording in a rewritable area, an initialization step is necessary to alloy the two layers. As a result, some parts of the optical recording medium serve as a write-once area, whereas other parts of the optical recording medium serve as a rewritable area.
For some applications it would be desirable to have an optical recording medium which has write-once properties as well as rewritable properties in the same area.
It is thus an object of the invention to propose write-once optical recording medium which offers at least a partial additional rewritability.
According to the invention, this object is achieved by an optical recording medium with a recording layer having at least a first recording sublayer and a second recording sublayer for recording information marks by alloying material of the at least first and second recording layers, wherein the materials of the at least first and second recording sublayers are chosen such that the alloyed material is a phase-change material adapted for recording additional data as phase changes of the alloyed material.
The optical recording medium according to the invention has write-once properties as well as rewritable properties. Though the rewritability is limited, it can be used for special applications. For example, the proposed structure of the optical recording medium allows to add additional optional functionality for content protection and tracking of media that have been recorded in manufacturing on demand (MOD) conditions. A more detailed explanation will be given below with reference to specific media structures.
The recording layer consists of at least a first and a second recording sublayer. The materials of the first and the second recording sublayer are chosen such that they can be burned to form an alloy which has phase-change properties. At the same time the optical contrast due to alloying of the materials needs to be high enough to gain sufficient modulation for a write-once optical recording medium.
First the optical recording medium is used like a conventional write-once medium showing high reflectivity and modulation. Then, due to the phase-change properties, the reflectivity and the modulation can be reduced in certain areas of the medium in a second recording step. Two possibilities can be distinguished in this respect.
The first possibility is a reduction of modulation. The reflectivity is slightly changed without disturbing the normal data read-out. In this case the frequency of the reflectivity change preferably is much lower than the frequency of the HF-data stored in the form of alloyed marks. In this case only special drives are able to detect the reflectivity change and thus the data recorded using this reflectivity change. Low pass filtering allows to suppress the HF-data signal and to detect the slight reflectivity change.
One application of this mechanism is a kind of physical content protection. A decryption key or is stored in this slight reflectivity change. If the optical recording medium is copied using a state of the art optical recording medium and drive, this decryption key is lost and the recorded optical recording medium cannot be played. In addition to new optical recording media and new firmware for the recording devices, this application requires players with an adapted firmware and a slightly modified hardware to read the decryption key.
The second possibility is a total suppression of modulation. The reflectivity is changed such that the modulation vanishes completely in certain areas. This effect can be used in different ways. One application is to temporary hide information. Later the information can be recovered by a special recording procedure, because even though the contrast is zero the information is still stored in the marks of the recording layer. Temporary hiding of the marks and recovering is done by changing the state of the phase-change marks from amorphous to crystalline and vice versa.
Of course, other new applications might evolve in the future, which make use of the special properties of the proposed optical recording medium.
Advantageously, the materials of the at least first and second recording sublayers are chosen such that a recording power P1 necessary for changing the state of the alloyed material from amorphous to crystalline and a recording power P2 necessary for changing the state of the alloyed material from crystalline to amorphous are smaller than a recording power P3 necessary for alloying the materials. In other words, for both possibilities the structure of the optical recording medium needs to be optimized in such way that the recording power for the first recording process, i.e. alloying of the different recording sublayers, is substantially higher than the power needed to rewrite the marks having phase-change properties. This ensures that no data are destroyed by an additional alloying during a phase change recording process.
Favorably, the recording power P1 necessary for changing the state of the alloyed material from amorphous to crystalline is smaller than the recording power P2 necessary for changing the state of the alloyed material from crystalline to amorphous. This is a typical constraint for phase change recording media.
Advantageously, the recording process is a ‘High-to-Low’ process. In this case the reflectivity of the recorded marks is lower and, therefore, the absorption is higher. For the modulation reduction described above it is then easily ensured that during the rewriting process of the marks more heat is absorbed by the marks than by the land area, which has a high reflectivity and a low absorption. Then, independent of the state of the phase-change areas, the information which has been recorded in the first step remains unchanged during the rewriting process. The situation is different for the modulation suppression, because once the reflectivity has been changed such that the modulation vanishes completely, the absorption is nearly the same for the marks and the land area. Even then it is, however, possible to design the layer stack in such a way that the power needed for changing the phase-change state is much lower than for alloying the materials.
An appropriate write strategy, for example with a high recording speed and/or short write pulses, ensures that the state of the phase-change marks is amorphous directly after alloying. An additional recording step then allows to change the state of the phase-change marks from amorphous to crystalline.
Favorably, the recording layer includes a first, a second and a third recording sublayer consisting of three materials M1, M2 and M3, respectively. An advantageous composition of materials is M1=Ag, M2=AgInTe2, and M3=Sb70Te30. In this case the thicknesses of each sublayer can be adjusted such that the burned alloy is close to Ag12In4Sb55Te29. In particular the amount of AgInTe2 preferably is essentially 1.7 times the amount of Ag and the amount of Sb70Te30 preferably is essentially 9.2 times the amount of Ag. The corresponding thickness of each layer can be calculated with the average atom diameter of the elements Ag, In, Sb and Te.
With this material composition high reflectivity and modulation values are achieved. For example at a wavelength of 650 nm a reflectivity of 0.5 and a maximum modulation of 0.7 has been calculated. In praxis the modulation is slightly smaller due to the trade-off between modulation and jitter increase caused by cross-writing. Further, the reflectivity measured with focused beam is slightly smaller than the parallel beam reflectivity, which is assumed in the calculation that are discussed below with reference to the figures. However, the reflectivity-modulation product is sufficient to fulfill the specifications applicable to DVD (Digital Versatile Disc).
According to a further aspect of the invention, a method for reading data from an optical recording medium according to the invention has the steps of:
The method allows to retrieve both the data recorded using alloyed marks as well as the data recorded using phase changes of the alloyed material.
The above method is favorably implemented in an apparatus for reading data from an optical recording medium according to the invention.
Specifically, the apparatus has a light source for illuminating the optical recording medium with a light beam, a detector for detecting data from a light beam reflected by the optical recording medium, and a low pass filter for separating the data signal recorded using phase changes of the alloyed material from the data signal recorded using alloyed marks.
Advantageously, a decryption key is retrieved from the data signal recorded using phase changes of the alloyed material. In this way a physical content protection of the recorded data can easily be implemented, as already discussed above.
Similarly, a method for recording data on an optical recording medium according to the invention has the steps of:
The above method is favorably implemented in an apparatus for recording data on an optical recording medium according to the invention.
According to still a further aspect of the invention, a method for activating an optical recording medium according to the invention has the step of increasing the reflectivity and/or the modulation of the alloyed material by changing the state of the recorded marks from amorphous to crystalline by laser radiation or heat treatment. In this way use is made of rewritable properties of the optical recording medium to implement an additional security feature. Without activation it is not possible to retrieve the data recorded on the optical recording medium in a normal playback apparatus.
For a better understanding the invention shall now be explained in more detail in the following description with reference to the figures. It is understood that the invention is not limited to this exemplary embodiment and that specified features can also expediently be combined and/or modified without departing from the scope of the present invention as defined in the appended claims. In the figures:
Two examples of the structure of the optical recording medium 1 will be discussed in more detail in the following. The examples are adapted to a wavelength of 650 nm. Of course, the invention can also be realized for other wavelengths suitable for CD (Compact Disc), DVD (Digital Versatile Disc), HD-DVD (High Density Digital Versatile Disc) or BD (Blu-ray Disc) and so on, e.g. for 405 nm. The following materials are used for the calculation of reflectivity and modulation:
In this case the thickness of AgInTe2 needs to be 1.51 times the thickness of Ag, and the thickness of Sb70Te30 needs to be 8.2 times the thickness of Ag in order to reach the right composition of the recorded marks (approximately Ag12In4Sb55Te29). Values for the real part n and the imaginary part k of the refractive index at a wavelength between 633 nm and 650 nm were derived from measurements or retrieved from the literature ([1]M. M. El-Nahass et al.: “Structural and optical properties of flash evaporated AgInTe thin films”, Eur. Phys. J. Appl. Phys. (2006), pp. 75-83; [2] Y. C. Her et al.: “Effects of Ag and In addition on the optical properties and crystallization kinetics of eutectic Sb70Te30 phase-change recording film”, J. Appl. Phys. 93 (2003), pp. 10097-10103) and are summarized in the below Table 1. Further, it can reasonably be assumed that all materials are very close to the amorphous state after sputtering.
The first exemplary structure of the optical recording medium 1 according to the invention is summarized below in Table 2. The aim of this structure is a reduction of modulation.
Calculations based on algorithms for parallel beam reflection indicate that for the proposed layer structure and materials the reflectivity change due to alloying of the two materials is sufficient for applications in recordable optical recording media.
As shown in
In a next step the reflectivity and the modulation are calculated for the same thicknesses, but with a crystalline state for the recorded marks. The result is shown in
In other words, if the thickness of the SbTe sublayer is 40 nm, the modulation directly after the first recording is about 0.61. After changing from amorphous to crystalline, the modulation is reduced to 0.37. Depending on the thickness of the SbTe sublayer a stronger change in the modulation can be achieved or, if the thickness is reduced below 34 nm, the modulation change can be inverted. In that case the modulation after recording is low (corresponding to the amorphous state) and can be increased by a second step (crystallization process). For example, if the thickness of the SbTe sublayer is 30 nm, the modulation directly after the first recording is about 0.25. After changing from amorphous to crystalline, the modulation is increased to 0.4. This demonstrates that the thickness can be adjusted in such way that the required reflectivity and modulation values are achieved.
The below Table 3 shows reflectivity and modulation values for different thicknesses of the SbTe sublayer and for different states of the recorded marks (amorphous, crystalline). The maximum value for R×M reaches about 0.37 with a SbTe sublayer thickness of 46 nm (0.48×0.78=0.37).
Directly after recording the marks, which are formed of AgInSbTe, are in an amorphous state due to the recording process using short pulses with a high peak power P3. The reflectivity and modulation values are shown in
The condition for the recording powers is as follows:
P1<P2<P3
The first condition P1<P2 is the same as for known rewritable media. The second condition P2<P3 is needed to avoid additional alloying of the recording sublayers R1, R2, R3, which would destroy (i.e. delete) the recorded data. In the present example this can easily be achieved, as the reflectivity of the crystalline recorded marks is still lower than the reflectivity of the unrecorded area. Consequently, the absorption of the crystalline recorded marks is higher than the absorption of the unrecorded area. That means that for this switching between the amorphous state and the crystalline state and vice versa the laser pulses can be applied without knowledge of the channel data even with a laser power P2 close to P3.
The second exemplary structure of the optical recording medium 1 according to the invention is summarized below in Table 4. The aim of this structure is a reversible total suppression of the modulation.
The thicknesses of the sublayers are adjusted in such way that the modulation for the crystalline state of the recorded marks vanishes at one or more thicknesses of the SbTe sublayer. As shown in
As in the first example, directly after recording the marks, which are formed of AgInSbTe, are in an amorphous state due to the recording process using short pulses with a high peak power P3. The reflectivity and modulation values are shown in
The condition for the recording powers is as follows:
P1<P2<P3
As already discussed above for the first exemplary structure the first condition P1<P2 is the same as for known rewritable media. The second condition P2<P3 is needed to avoid additional alloying of the recording sublayers R1, R2, R3. In comparison to the first exemplary structure the power P2 needs to be higher, because the reflectivity of the crystalline recorded marks is higher and the absorption is thus lower. That means that for this switching between the amorphous state and the crystalline state and vice versa the laser pulses can be applied without knowledge of the channel data, but maintaining the condition P2<P3 more rigorously than in the previous example.
For both examples discussed above it may happen that the state of the material in the SbTe sublayer is changed from amorphous (as deposited) to partial crystalline in the unrecorded areas between the marks. This would, however, influence the resulting reflectivity and modulation values only in a very limited way.
An apparatus 20 for reading data from and/or recording data on an optical recording medium 1 according to the invention is schematically illustrated in