Patent Application
20080279080
This application is based on and claims the benefit of priority from the prior Japanese Patent Application No. 2007-124430 filed on May 9, 2007 and No. 2007-312208 filed on Dec. 3, 2007, the entire contents of which is incorporated herein by reference.
The present invention relates to an optical storage medium for which a light beam, such as a laser beam, is used in data recording or reproduction and a method of producing such an optical storage medium. This invention, particularly, relates to a write-once type optical storage medium having a recording layer provided in the vicinity of the surface of either side of the medium and a method of producing such an optical storage medium.
DVD has been the mainstream of optical storage media for data recording or reproduction with a laser beam. Another type of optical storage medium becoming popular is Blu-ray Disc (referred to as BD hereinafter) having a larger storage capacity than DVD.
DVD and BD have the same disc shape with 12 cm in diameter and 1.2 mm in thickness. The differences between DVD and BD are as follows: DVD has a recording layer located at almost the middle of the thickness, or 0.6 mm away from both disc surfaces. Recording/reproduction is performed to the DVD recording layer with a laser beam at a red wavelength of 650 nm. BD has a recording layer located at 0.1 mm from either of the disc surfaces. Recording/reproduction is performed to the BD recording layer with a laser beam at a blue-violet wavelength of 405 nm.
Higher recording density is achieved for BD with a shorter wavelength for a laser beam and a larger number of numerical aperture (NA) for an objective lens than DVD.
A typical BD has at least a reflective film, a first dielectric film, a recording film, a second dielectric film, and a cover layer formed in order on a resin substrate of 1.1 mm in thickness. The total thickness is 0.1 mm except for the substrate.
The inventors of the present invention have found that BDs now on the market suffer deterioration of reproduced signals when left in a hot and humid environment for certain hours.
The test in which optical storage media are left in a hot and humid environment is one of the measures to evaluate the long-term reliability of the optical storage media in a short time. In this test, optical storage media are usually left in an 80° C. and 85% RH environment for 96 hours, which corresponds to a normal environment of 25° C. and 30% RH for several ten to several hundred years. The long-term reliability can be evaluated with measurements of average SER (Symbol Error Rate); the higher the average SER, the more the reproduced signals being deteriorated.
It is presupposed that the cause of deterioration of reproduced signals is the moisture in the air that reaches either or both of the recording and reflective films and generates a chemical reaction to the films or between the films and neighboring films. Deterioration of the recording and/or reflective films gives adverse effects to data recording to the recording film.
One solution to solve the problem caused by the moisture in the air that penetrates into an optical storage medium is disclosed, for example, in Japanese Un-examined Patent Publication No. 2006-294169 (referred to as document 1, hereinafter). The solution is to provide an intermediate layer for adjusting moisture permeability between a recording film made of an organic material and a cover layer. The intermediate layer contains an oxide or a nitride including at least one of the three elements: Nb (niobium), Al (aluminum) and Si (silicon), or a sulfide including Zn (zinc).
The experiments done by the inventors of the present invention for the evaluation of the long-term reliability to sample optical storage media having an inorganic recording film with an intermediate layer made of Nb2O5 showed a higher average SER after the sample media were left in a hot and humid environment.
Evaluated in the document 1 are jitters in reproduction before and after the optical storage media were left in a hot and humid environment. Suppression of jitters only is not enough to meet the demand for longer-term reliability for optical storage media, particularly, those having a recording film made of an inorganic material.
A purpose of the present invention is to provide an optical storage medium excellent in long-term reliability, protected from moisture in the air to reach recording and/or reflective films and a method of producing such an optical storage medium.
The present invention provides an optical storage medium comprising: a substrate; a cover layer that allows light to pass therethrough in recording or reproduction; at least a reflective film, a first dielectric film, a recording film, and a second dielectric film formed in this order from the substrate side and between the substrate and the cover layer; and a damp-proof film provided between the second dielectric film and the cover layer, the damp-proof film being at least partially an amorphous film and containing at least an indium oxide.
Moreover, the present invention provides a method of producing an optical storage medium comprising the steps of: forming at least a reflective film, a first dielectric film, a recording film, and a second dielectric film in this order on a substrate by sputtering; and forming a damp-proof film on the second dielectric film by sputtering with a target of an indium oxide added with at least one compound selected from the group consisting of a tin oxide, a tungsten oxide, and a cerium oxide; and providing a cover layer over the damp-proof film.
[Structure of Optical Storage Medium]
An optical storage medium 100 shown in
The substrate 1 needs to not allow the laser beam L to pass therethrough, different from DVD. Thus, the material for the substrate 1 can be selected under consideration of physical strength and production cost, etc. Such materials are, for example, glass, polycarbonate, polymethylmethacrylate, polyolefin resin, epoxy resin, or polyimide resin. The most suitable material for the substrate 1 is polycarbonate for low hygroscopicity and easiness to process.
Preferable materials for the reflective film 2 are: a reflective metal, such as Al, Au (gold) or Ag (silver); an alloy of any of these metals as a major component with at least one type of metal or semiconductor; and a mixture of a metal, such as Al, Au or Ag, and a metal nitride, a metal oxide or a metal chalcogen of Al, Si, etc. A typical alloy preferable for the reflective film 2 is made of Al and at least one of the following elements: Si, Mg (magnesium), Cu (copper), Pd (palladium), Ti (titanium), Cr (chrome), Hf (hafnium), Ta (tantalum), Nb, Mn (manganese), Zr (zirconium), etc. Another typical alloy preferable for the reflective film 2 is made of Au or Ag and at least one of the following elements: Cr, Ag, Cu, Pd, Pt (platinum), Ni (nickel), Nd (neodymium), In (indium), etc. Most preferable among them are Ag and an alloy of Ag as a major component for higher reflectivity to blue-violet wavelength and higher thermal conductivity for higher signal levels.
The thickness of the reflective film 2 is, preferably, in the range from 50 nm to 300 nm, which depends on the thermal conductivity of a material used for this film. The reflective film 2 of 50 nm or more in thickness is optically stable in, particularly, reflectivity. Nevertheless, a thicker reflective film 2 affects a cooling rate. Thickness over 300 nm requires a longer production time. It is desirable to use a specific material exhibiting a high thermal conductivity that allows the reflective film 2 to have a thickness in an optimum range such as mentioned above.
The interface film 3 is preferably provided between the reflective film 2 and the first dielectric film 4 as shown in
The first and second dielectric films 4 and 6 are provided to protect the substrate 1, the protective film 8 or the other films from deformation due to heat generated in data recording to the recording film 5, so as not to lower the recording characteristics, and to enhance signal contrast with optical interference. The first and second dielectric films 4 and 6 allow a laser beam L to pass therethrough in recording, reproduction or erasure and exhibits a refractive index “n”, preferably, in the range of 1.9<n<2.5. A suitable material for the first and second dielectric films 4 and 6 is a material that exhibits high thermal tolerance, for example, an oxide such as SiO2, SiO, ZnO, TiO2, Ta2O5, Nb2O5, ZrO2 or MgO, a sulfide such as ZnS, In2S3 or TaS4, or a carbide such as SiC, TaC, WC (tungsten carbide) or TiC, or a mixture of these materials. Among them, a mixture of ZnS and SiO2 is the best for higher recording sensitivity, C/N and film-forming rate, and also higher productivity. The first and second dielectric films 4 and 6 may or may not be made of the same material or composition. Their thicknesses are roughly in the range from 10 nm to 200 nm.
The recording film 5 provided between the first and second dielectric films 4 and 6 is made of an inorganic material. The recording film 5 has a dual-layer structure of two elements of a metal and a semiconductor or a single-layer structure of a metal oxide or nitride. The recording film 5 of the dual-layer structure undergoes data recording with fusion of the dual-layer elements due to heat generated when irradiated with the laser beam L. The recording film 5 of the single-layer structure undergoes data recording with liberation of oxygen or nitrogen from the metal oxide or nitride due to heat generated when irradiated with the laser beam L. The metal nitride is the most feasible among the materials for the recording film 5, for excellent jitter and recording-power margin characteristics.
When formed with a metal nitride, the recording film 5 requires to liberate nitrogen at about 600° C. (the recording temperature) or lower for data recording. Thus, the recording film 5 is, preferably, formed with a material that includes, at least, a material of low melting point for which phase separation occurs at about 600° C. or lower. Such materials of low melting point are, for example, BiN (bismuth nitride), Fe2N (iron nitride), Cu3N (copper nitride), etc.
In addition to the material of low melting point, the recording film 5 is, preferably, formed with a material of high melting point for which phase separation does not occur at about 600° C. or lower. Such materials of high melting point are, for example, nitrides and oxides that exhibit a high melting point, which are, for example, GeN, TiN, NbN, ZrN, WO, ZrO2, TiO2, Nb2O5, Ta2O5, etc. When BiN and GeN are selected as the materials of low and high melting points, respectively, GeN and BiN are adjusted to exhibit a molar ratio in the range from 2:8 to 8:2.
When the recording film 5 of such a composition of BiN and GeN is irradiated with a laser beam L in recording, the temperature of the laser-irradiated section rises to allow nitrogen to liberate from BiN, leaving the metal of bismuth only, which results in change in optical characteristics of the recording film 5 to accept data recording or retrieving (reproduction). The liberation of nitrogen from BiN is an irreversible change so that the once-liberated nitrogen cannot combine with bismuth. Therefore, the optical storage medium 100 shown in
As shown in
The amorphous ITO film, or SnO2-rich ITO film, lowers moisture permeability for the damp-proof film 7. If crystalline, the damp-proof film 7 inevitably has the grain boundary which allows moisture to pass therethrough. However, the amorphous damp-proof film 7 does not have the grain boundary so that moisture is prevented or restricted from moving, compared to the crystalline film. The most feasible state for the damp-proof film 7 is that it is completely amorphous. It is, however, preferable that the film 7 is at least partially amorphous. Moreover, it is preferable that the film 7 is amorphous for its 50% or higher in volume. The damp-proof film 7 has a thickness in the range from 5 nm to 100 nm. The thickness thinner than 5 nm cannot restrict moisture from moving whereas thicker than 60 nm lowers productivity. A preferable range for the thickness of the damp-proof film 7 is in the range from 5 nm to 60 nm.
Provided on the damp-proof film 7 is the protective film 8 made of a UV (UltraViolet)-curable resin with a thickness of about several μm. The protective film 8 is covered with the cover layer 9. The cover layer 9 is, for example, a polycarbonate sheet (PC sheet) applied with an adhesive material on its surface at the protective film 8 side and a coating agent on the other surface at the medium 100 surface side. The thickness of the cover layer 9 is about 0.1 mm for the very thin films 2 to 8.
[Optical Storage Medium Production Method]
Lamination of the reflective film 2, the interface film 3, the first dielectric film 4, the recording film 5, the second dielectric film 6, and the damp-proof film 7 on the substrate 1, shown in
A film-forming system feasible for forming the films 2 to 7 on the substrate 1 is a batch system in which a plural number of substrates are simultaneously subjected to a film forming process in a vacuum chamber or a single-wafer system in which substrates are processed one by one. The thickness of each film can be adjusted with control of power to be supplied and its duration in sputtering or monitoring conditions of deposited films with a crystal oscillator.
The films 2 to 7 can be formed while each substrate is being stationary, transferred or rotating. Rotation of the substrate (and further with orbital motion) is most feasible for higher uniformity. An optional cooling process decreases warpage of the substrate.
After formation of these films on the substrate 1, a UV-curable resin is applied on the damp-proof film 7 and cured to become the protective film 8. Then, the cover layer 9 made of a PC sheet and applied with an adhesive material is provided on the protective film 8, to obtain the optical storage medium 100 shown in
Instead of providing the protective film 8 on the damp-proof film 7, a highly-viscous UV-curable resin can be applied on the film 7 at about 0.1 mm in thickness, to be the cover layer 9. For higher productivity, forming the cover layer 9 of the highly-viscous UV-curable resin without the protective film 8 is better than the cover layer 9 of the PC sheet on the protective film 8. On the contrary, forming the cover layer 9 of the PC sheet on the protective film 8 is preferable for higher in-plane thickness uniformity.
Another option is that after a UV-curable resin is applied on the damp-proof film 7 as the protective film 8, a PC sheet is placed on the un-cured protective film 8 as the cover layer 9, and the un-cured protective film 8 is exposed to UV rays via the cover layer 9, to be cured so that the cover layer 9 is fixed on the protective film 8. A further option is that a thermally-curable hardcoat layer is provided on the PC sheet or a highly-viscous UV-curable resin. One requirement for the further option is that the total thickness of the films be 0.1 mm, except for the substrate 1.
Although not shown in
Forming the cover layer 9 on the damp-proof film 7 with the convexes and concaves allows air to remain in the concaves, which impairs the long-term reliability of the optical storage medium 100. The convexes and concaves of the damp-proof film 7 can be erased by forming the protective layer 8 on the damp-proof film 7 with spin coating. The spin-coating technique removes the air from the concaves to solve one of the problems on the long-term reliability. It is thus preferable to form the protective layer 8 on the damp-proof film 7 with spin coating. Spin coating is also preferable when the cover layer 9 is formed by applying a highly-viscous UV-curable resin on the damp-proof film 7, at a thickness of about 0.1 mm.
[Study of Material for Damp-Proof Film]
The inventors of the present invention presupposed that the damp-proof film 7 made of an amorphous film including an indium oxide and provided between the second dielectric film 6 and the protective film 8 could give high long-term reliability to the optical storage medium 100, and found out that the presumption is correct according to the following measurements for embodiment samples E-1 to E-3 and comparative samples C-1 to C-6.
In the following embodiment and comparative media samples, the average SER was measured after each sample was left in an 80° C.-85% RH environment for 96 hours, with an optical-disc drive tester (ODU-1000) equipped with a 405-nm-wavelength laser diode and an optical lens (NA=0.85) made by Pulstec Industrial Co. Ltd.
Several films which will be disclosed later, were formed on a substrate 1 made of a polycarbonate resin with 120 mm in diameter and 1.1 mm in thickness. Grooves were formed on the substrate 1 at 0.32 μm in track pitch, with 25 nm in groove depth and about 50:50 in width ratio of groove to land.
After a vacuum chamber was exhausted up to 3×10−4 Pa, an 80-nm-thick reflective film 2 was formed on the substrate 1 by magnetron sputtering with a target of an alloy of Ag—Pd—Cu at 2×10−1 Pa in an Ar-gas atmosphere.
Formed on the reflective film 2, in order, were: a 2-nm-thick GeCrN interface film 3 with a target of an alloy of GeCr in an Ar—N2 gas-mixture atmosphere; a 20-nm-thick first dielectric film 4 with a target of ZnS added with 20-mol % SiO2; a 25-nm-thick GeBiN recording film 5 with a target of an alloy of GeBi (with an elemental ratio of 50:50) in an Ar—N2 gas-mixture atmosphere; a 50-nm-thick second dielectric film 6 of the same material as the first dielectric film 4; and a 20-nm-thick damp-proof film 7 with a target of In2O3 added with 40-mol % SnO2.
The substrate 1 having the films 2 to 7 formed as described above was then taken out from the vacuum chamber.
The damp-proof film 7 was spin-coated with an acrylic UV-curable resin (SK5110 made by Sonny Chemicals & Information Device Corporation), to have a protective film 8 which was then applied with a PC sheet as a cover layer 9 via an adhesive material, thus the embodiment sample E-1 of the optical storage medium 100 (
Concerning the damp-proof film 7, a sample 100-nm-thick In2O3 film was formed on a silicon wafer, by sputtering, with a target of In2O3 added with 40-mol % SnO2. An X-ray diffraction technique confirmed that this sample In2O3 film was an amorphous film. This proves that the damp-proof film 7 of the optical storage medium 100 is an amorphous film.
Data were recorded on the embodiment sample E-1 of the optical storage medium 100, with the optical-disc drive tester made by Pulstec Industrial Co. Ltd., described above. The embodiment sample E-1 was then left in an 80° C.-85% RH environment for 96 hours, for measurements of the average SER on the data-recorded tracks.
The measured result for the embodiment sample E-1 is shown in TABLE 1 of
As shown in TABLE 1, the embodiment sample E-1 exhibited 5.0×10−5 in the average SER. In the evaluation of the measurements, the maximum acceptable level is set at 2.0×10−4 that is an average SER known as indicating high data reliability. The average SER of 5.0 ×10−5 is lower than the maximum acceptable level. Thus, the embodiment sample E-1 is excellent in the average SER.
The embodiment sample E-2 of the optical storage medium 100 was identical to the embodiment sample E-1, except for the damp-proof film 7 formed, by sputtering, with a target of In2O3 with W2O5 added at 20 mol %. Like the sample E-1, it was also confirmed that the In2O3-sputtering film with W2O5 added at 20 mol % was an amorphous film.
As shown in TABLE 1, the embodiment sample E-2 exhibited 9.1×10−5 in the average SER, lower than the maximum acceptable level of 2.0×10−4, which is excellent. In TABLE 1, IWO is the abbreviation for indium-tungsten oxide.
The embodiment sample E-3 of the optical storage medium 100 was identical to the embodiment sample E-1, except for the damp-proof film 7 formed, by sputtering, with a target of In2O3 with CeO2 (cerium oxide) added at 20 mol %. Like the sample E-1, it was also confirmed that the In2O3-sputtering film with CeO2 added at 20 mol % was an amorphous film.
As shown in TABLE 1, the embodiment sample E-3 exhibited 6.8×10−5 in the average SER, lower than the maximum acceptable level of 2.0×10−4, which is excellent. In TABLE 1, ICO is the abbreviation for indium-cerium oxide.
In the embodiment samples E-1, E-2 and E-3, the damp-proof films 7 were formed, by sputtering, with the targets of In2O3 with a tin oxide, a tungsten oxide, and a cerium oxide, respectively, as described above. However, the damp-proof film 7 of each sample can be formed with the target of In2O3 with a mixture of any of two or three of the following compounds: a tin oxide, a tungsten oxide, and a cerium oxide.
(Comparative Sample C-1)
The comparative sample C-1 of the optical storage medium 100 was identical to the embodiment sample E-1, except that the damp-proof film 7 was not formed.
As shown in TABLE 1, the comparative sample C-1 exhibited 3.2×10−3 in the average SER, higher than the maximum acceptable level of 2.0×10−4, which is not acceptable.
(Comparative Sample C-2)
The comparative sample C-2 of the optical storage medium 100 was identical to the embodiment sample E-1, except for the damp-proof film 7 formed with a target of In2O3 with no other compound added. It was confirmed that the In2O3-sputtering film with no other compound added was a crystalline film.
As shown in TABLE 1, the comparative sample C-2 exhibited 2.1×10−3 in the average SER, higher than the maximum acceptable level of 2.0×10−4, which is not acceptable.
(Comparative Sample C-3)
The comparative sample C-3 of the optical storage medium 100 was identical to the embodiment sample E-1, except for the damp-proof film 7 formed with a target of Si3N4 with no other compound added. It was confirmed that the Si3N4-sputtering film with no other compound added was an amorphous film.
The measurements of the average SER failed due to creation of many defects after the comparative sample C-3 was left in an 80° C.-85% RH environment for 96 hours.
(Comparative Sample C-4)
The comparative sample C-4 of the optical storage medium 100 was identical to the embodiment sample E-1, except for the damp-proof film 7 formed with a target of Si3N4 with SiO2 added at 50 mol %. It was confirmed that the Si3N4-sputtering film with SiO2 added at 50 mol % was an amorphous film.
As shown in TABLE 1, the comparative sample C-4 exhibited 1.8×10−2 in the average SER, higher than the maximum acceptable level of 2.0×10−4, which is not acceptable.
(Comparative Sample C-5)
The comparative sample C-5 of the optical storage medium 100 was identical to the embodiment sample E-1, except for the damp-proof film 7 formed with a target of Al2O3 with no other compound added. It was confirmed that the Al2O3-sputtering film with no other compound added was an amorphous film.
The measurements of the average SER failed for the comparative sample C-5 due to creation of many defects, like the comparative sample C-3.
(Comparative Sample C-6)
The comparative sample C-6 of the optical storage medium 100 was identical to the embodiment sample E-1, except for the damp-proof film 7 formed with a target of SiC with no other compound added. It was confirmed that the SiC-sputtering film with no other compound added was an amorphous film.
As shown in TABLE 1, the comparative sample C-6 exhibited 1.6×10−3 in the average SER, higher than the maximum acceptable level of 2.0×10−4, which is not acceptable.
It is taught from the results shown in TABLE 1 that the recording film 5 or the neighboring films suffers corrosion when moisture penetrates into the optical storage medium 100 via the cover layer 9 when no damp-proof film is provided, like the comparative sample C-1. The result of measurements was very bad for the comparative sample C-1, which was 3.2×10−3 in the average SER.
The results teach that the damp-proof film 7 is an essential component of the optical storage medium 100 for the long-term reliability.
There are particular materials for the damp-proof film 7 to maintain an acceptable average SER, according to TABLE 1 of
The results shown in TABLE 1 of
[Study of Molar Ratio of SnO2 in ITO]
The inventors of the present invention examined the molar ratio of SnO2 in ITO necessary for the damp-proof film 7 to become an amorphous film, according to the embodiments sample E-1, the comparative sample C-2, and the following embodiments sample E-4 to E-7 and comparative samples C-7 to C-9.
The embodiment sample E-4 of the optical storage medium 100 was identical to the embodiment sample E-1, except for the damp-proof film 7 formed, by sputtering, with a target of In2O3 with SnO2 added at 20 mol %. It was confirmed that the In2O3-sputtering film with SnO2 added at 20 mol % was an amorphous film.
As shown in TABLE 2 of
Also shown TABLE 2 are the measured results for the embodiment samples E-1 and E-5 to E-7 and the comparative samples C-2 and C-7 to C-9.
The embodiment sample E-5 of the optical storage medium 100 was identical to the embodiment sample E-1, except for the damp-proof film 7 formed, by sputtering, with a target of In2O3 with SnO2 added at 30 mol %. It was confirmed that the In2O3-sputtering film with SnO2 added at 30 mol % was an amorphous film.
As shown in TABLE 2, the embodiment sample E-5 exhibited 6.9×10−5 in the average SER, lower than the maximum acceptable level of 2.0×10−4, which is excellent.
The embodiment sample E-6 of the optical storage medium 100 was identical to the embodiment sample E-1, except for the damp-proof film 7 formed, by sputtering, with a target of In2O3 with SnO2 added at 60 mol %. It was confirmed that the In2O3-sputtering film with SnO2 added at 60 mol % was an amorphous film.
As shown in TABLE 2, the embodiment sample E-6 exhibited 5.3×10−5 in the average SER, lower than the maximum acceptable level of 2.0×10−4, which is excellent.
The embodiment sample E-7 of the optical storage medium 100 was identical to the embodiment sample E-1, except for the damp-proof film 7 formed, by sputtering, with a target of In2O3 with SnO2 added at 70 mol %. It was confirmed that the In2O3 film with SnO2 added at 70 mol % was an amorphous film.
As shown in TABLE 2, the embodiment sample E-7 exhibited 1.8×10−4 in the average SER, lower than the maximum acceptable level of 2.0×10−4, which is excellent.
(Comparative Sample C-7)
The comparative sample C-7 of the optical storage medium 100 was identical to the embodiment sample E-1, except for the damp-proof film 7 formed with a target of In2O3 with SnO2 added at 5 mol %. It was confirmed that the In2O3-sputtering film with SnO2 added at 5 mol % was not an amorphous film but a crystalline film.
As shown in TABLE 2, the comparative sample C-7 exhibited 1.1×10−3 in the average SER, higher than the maximum acceptable level of 2.0×10−4, which is not acceptable.
(Comparative Sample C-8)
The comparative sample C-8 of the optical storage medium 100 was identical to the embodiment sample E-1, except for the damp-proof film 7 formed with a target of In2O3 with SnO2 added at 10 mol %. It was confirmed that the In2O3-sputtering film with SnO2 added at 10 mol % was not an amorphous film but a crystalline film.
As shown in TABLE 2, the comparative sample C-8 exhibited 7.8×10−4 in the average SER, higher than the maximum acceptable level of 2.0×10−4, which is not acceptable.
(Comparative Sample C-9)
The comparative sample C-9 of the optical storage medium 100 was identical to the embodiment sample E-1, except for the damp-proof film 7 formed with a target of In2O3 with SnO2 added at 80 mol %. It was confirmed that the In2O3-sputtering film with SnO2 added at 80 mol % was an amorphous film.
As shown in TABLE 2, the comparative sample C-9 exhibited 9.5×10−4 in the average SER, higher than the maximum acceptable level of 2.0×10−4, which is not acceptable.
[Study of Film Arrangements]
The inventors of the present invention further examined the location of the damp-proof film 7 on the substrate 1. In
Comparison was then made between the embodiment sample E-1 and the following comparative samples C-10 to C-12 of the optical storage medium 100 that were formed with a different order of films from the sample E-1.
(Comparative Sample C-10)
The comparative sample C-10 of the optical storage medium 100 was identical to the embodiment sample E-1, except that the damp-proof film 7 was provided between the recording film 5 and the second dielectric film 6, not between the second dielectric film 6 and the protective film 8 (
As shown in TABLE 3 of
Also shown TABLE 3 are the measured results for the embodiment sample E-1 and the comparative samples C-11 and C-12.
(Comparative Sample C-11)
The comparative sample C-11 of the optical storage medium 100 was identical to the embodiment sample E-1, except that the damp-proof film 7 was provided between the interface film 3 and the first dielectric film 4.
As shown in TABLE 3, the comparative sample C-11 exhibited 2.3×10−3 in the average SER, higher than the maximum acceptable level of 2.0×10−4, which is not acceptable. A possible reason for the unacceptable average SER is the effects of penetrated moisture to the recording film 5 due to no protection of the recording film 5 by the damp-proof film 7.
(Comparative Sample C-12)
The comparative sample C-11 of the optical storage medium 100 was identical to the embodiment sample E-1, except that the damp-proof film 7 was provided between the reflective film 2 and the interface film 3.
As shown in TABLE 3, the comparative sample C-12 exhibited 2.5×10−3 in the average SER, higher than the maximum acceptable level of 2.0×10−4, which is not acceptable. A possible reason for the unacceptable average SER is the effects of penetrated moisture to the recording film 5 due to no protection of the recording film 5 by the damp-proof film 7, like the comparative sample C-11.
The measured results shown in TABLE 3 confirmed that the optical storage medium 100 requires the damp-proof film 7 to be provided between the second dielectric film 6 and the cover layer 9, for excellent long-term reliability. In particular, it requires that the damp-proof film 7 be provided between the second dielectric film 6 and the protective film 8, for the optical storage medium 100 having the cover layer 9 on the protective film 8, as shown in
The present invention employs BD as the embodiment in which the recording film is provided in the vicinity of either of two medium surfaces. Not only BD, however, the invention can be applied to any types of optical storage media in which the recording film is provided in the vicinity of either of two medium surfaces, with a thin cover layer (or any equivalent surface layer).
As disclosed above in detail, the present invention provides the optical storage medium and the method therefor, with excellent long-term reliability by preventing or restricting moisture in the air from reaching the recording film, the reflective film, etc.
| Number | Date | Country | Kind |
|---|---|---|---|
| JP 2007-124430 | May 2007 | JP | national |
| JP 2007-312208 | Dec 2007 | JP | national |