Optical waveguide element and method for preparation thereof

Information

  • Patent Grant
  • 6818577
  • Patent Number
    6,818,577
  • Date Filed
    Wednesday, November 20, 2002
    21 years ago
  • Date Issued
    Tuesday, November 16, 2004
    19 years ago
Abstract
An optical waveguide element that can stably and inexpensively form an optical waveguide of low loss and low stress in a glass material by ion exchange of Ag ions, and to provide a process for producing the same are provided. The optical waveguide element is made of a multicomponent glass material, which is Na2O—B2O3—Al2O3—SiO2 glass containing from 5 to 13% by mole of Na2O, in which an optical waveguide is formed by doping with Ag ions by ion exchange. The composition is preferably SiO2: 60 to 75% by mole, B2O3: 10 to 20% by mole, Al2O3: 2 to 10% by mole, Na2O: 5 to 13% by mole, Li2O: 0 to 1% by mole, As2O3: 0 to 0.5% by mole, and Sb2O3: 0 to 0.5% by mole (provided that As2O3+Sb2O3: 0.01 to 1% mole).
Description




BACKGROUND OF THE INVENTION




1. Field of the Invention




The present invention relates to an optical waveguide element having an optical waveguide formed by doping a glass material with Ag ions by an ion exchange method, and a process for producing the same.




2. Background Art




A technique for forming an optical waveguide in a glass substrate by an ion exchange method has been known as an optical waveguide element and a process for producing the same. A technique for ion-exchanging Na ions in a glass material by using Ag ions has also been reported.




The Ag-Na ion exchange not only provides a large change in refractive index to form an optical waveguide having a low birefringence, but also provides such an advantage that the exchange rate is large to obtain high productivity. However, such problems have been pointed out that a birefringence occurs by ion exchange of alkali metal ions other than Na ions, and coloring and absorption occur due to formation of an Ag colloid.




In order to form an optical waveguide of low loss and low stress by ion exchange of Ag ions, it has been proposed to use, as a glass material, F-substituted (fluorine-substituted) glass or glass having a small amount of non-bridging oxygen (see JP-A-4-219341).




The F-substituted glass has an advantage that the glass is melted at a lower temperature, and the refractive index is lowered, but is conspicuous in nonuniformity due to fluorine exhibiting high volatility, and thus such problems occur that the productivity of the glass is poor, and a diameter of a substrate (wafer) cannot be increased.




The glass having a small amount of non-bridging oxygen thus proposed not only contains a large amount of an alkali component (about 20% by mole or more) while the amount of a volatile component is not so large, whereby the weather resistance is poor, but also has a high refractive index, and thus mode field matching with an optical fiber is difficult. Furthermore, it also brings about increase of a reflective light amount at a jointed part of the optical waveguide and the optical fiber. Moreover, the use of an additive is noted in the foregoing patent publication in order to avoid coloration, and accordingly, the increase in refractive index thereby cannot be avoided.




Upon practical production of an optical waveguide by ion exchange, such material design is necessary that the ion exchange rate and the embedding controllability are considered. However, there is no sufficient description about it in the patent publications and literatures that are currently known, the relationship among the coloration, the productivity and the composition has not yet been elucidated.




SUMMARY OF THE INVENTION




An object of the invention is to provide an optical waveguide element that can stably and inexpensively form an optical waveguide of low loss and low stress in a glass material by ion exchange of Ag ions, and to provide a process for producing the same.




The invention provides an optical waveguide element comprising a multicomponent glass material, which is Na


2


O—B


2


O


3


—Al


2


O


3


—SiO


2


glass containing from 5 to 13% by mole of Na


2


O, in which an optical waveguide is formed by doping with Ag ions by ion exchange.




The multicomponent glass preferably is that having a composition containing:




SiO


2


: 60 to 75% by mole,




B


2


O


3


: 10 to 20% by mole,




Al


2


O


3


: 2 to 10% by mole,




Na


2


O: 5 to 13% by mole,




Li


2


O: 0 to 1% by mole,




As


2


O


3


: 0 to 0.5% by mole, and




Sb


2


O


3


: 0 to 0.5% by mole




(provided that As


2


O


3


+Sb


2


O


3


: 0.01 to 1% mole).




The composition of the multicomponent glass material is more preferably composed of:




SiO


2


: 63 to 72% by mole,




B


2


O


3


: 10 to 18% by mole,




Al


2


O


3


: 2 to 8% by mole,




Na


2


O: 7 to 13% by mole,




Li


2


O: 0 to 1% by mole,




As


2


O


3


: 0 to 0.5% by mole, and




Sb


2


O


3


: 0 to 0.5% by mole




(provided that As


2


O


3


+Sb


2


O


3


: 0.01 to 1% mole).




It is desired that the glass material has a refractive index of 1.50 or less with respect to a near infrared ray having a wavelength of from 1,200 to 1,650 nm under consideration that the purpose thereof is optical communication. It is also desired that the glass material used in the present invention is in a substrate form having a thickness of 5 mm or less, at least one surface of which is in a state of a mirror surface having a surface roughness Ra of from 0.001 to 0.1 μm.




The optical waveguide formed in the glass material may be formed on the surface of the glass material, but such a structure is preferred that the Ag ion doping region is embedded within the glass material.




Upon producing the optical waveguide element, the ion exchange of Ag ions is carried out, for example, at 200 to 350° C. with a processing bath containing Ag ions.




In order to form an optical waveguide in the glass material, what are important are




a. change in refractive index that is sufficient for single mode waveguide,




b. low birefringence,




c. low absorption characteristics,




d. excellent weather resistance,




e. high productivity (the yield of the glass wafer and the conditions for forming the optical waveguide), and




f. low-loss joint to an optical fiber(matching with the optical fiber).




The high productivity of the item (5) relates to the ion exchange rate, and the low-loss joint property of the item (6) relates to the matching in refractive index. Therefore, such a compositional design is necessary that the characteristics of the glass components considered.




The glass used in the invention is glass of Na


2


O—B


2


O


3


—Al


2


O


3


—SiO


2


system. The functions exerted by the respective components are as follows, and according thereto, it is preferred that the compositional proportions are determined as follows.




SiO


2


is a main component forming a glass network, and the glass is chemically unstable with poor water-resistance and acid-resistance when it is of a low concentration, but the melting temperature thereof is increased when it is of a high concentration. Therefore, it is preferably from 60 to 75% by mole, and more preferably from 63 to 72% by mole.




B


2


O


3


forms the glass network and lowers the melting temperature and the forming temperature of the glass, and therefore, it is necessarily contained. The effect of lowering the melting temperature becomes poor when it is of a low concentration, and when it is of a high concentration, it is liable to be vaporized upon forming, whereby such defects as cord and devitrification occur due to compositional fluctuation. Therefore, it is preferably from 10 to 20% by mole, and more preferably from 10 to 18% by mole.




Al


2


O


3


chemically stabilizes the glass and accelerates the ion exchange. When it is of a low concentration, the effect of accelerating the ion exchange is poor, and when it is of a high concentration, the melting temperature of the glass is increased, and the glass is liable to devitrify. Therefore, it is preferably from 2 to 10% by mole, and more preferably from 2 to 8% by mole.




Na


2


O is necessarily contained in a certain amount or more in order to cause change of the refractive index of the glass by exchange with Ag ions. However, because the durability of the glass is decreased (it is difficult to be vitrified) and the refractive index is increased when it is of a high concentration, it is made as small as possible. Therefore, it is preferably from 5 to 13% by mole, and more preferably from 7 to 13% by mole. Li


2


O is expensive while it improves the melting property (moldability) of the glass. Even when it is of a high concentration, no further improvement in melting property is obtained, and exchange with Ag ions occurs. Therefore, it preferably is 1% by mole or less, and it may not be contained.




In addition to the foregoing basic components, a clarificant and the like may be added in such a range that does not impair the gist of the invention. For example,




As


2


O


3


: 0 to 0.5% by mole, and




Sb


2


O


3


: 0 to 0.5% by mole,




provided that As


2


O


3


+Sb


2


O


3


: 0.01 to 1% mole, are added. These exert such a function that bubbles are liable to be removed (defoaming function).




As described in the foregoing, the low birefringence is necessarily realized in an optical waveguide element, and on that account, it is important to suppress alkali metal ions other than Na ions since they causes stress by exchange with Ag ions. In the invention, K ions is not contained as a glass component.











DETAILED DESCRIPTION OF PREFERRED EMBODIMENTS BEST MODE FOR CARRYING OUT THE INVENTION




Substrates were experimentally prepared with the glass materials of various kinds compositions shown in Table 1, and after subjected to an ion exchange treatment, necessary measurements were carried out.















TABLE 1













Invention




Comparative Example





















Sample No.




1




2




3




4




5




6




7




8




9




10
























Composition (% by mole)
















SiO


2






67.4




69.4




71.4




68.4




71.9




62.4




67




67.4




61.4




75






B


2


O


3






15




15




15




14




11




15




0




15




15




16.4






Al


2


O


3






7




5




3




4.5




5




12




17.4




7




8




5






Na


2


O




10




10




10




12.5




11.5




10




15




7




15




3






Li


2


O




0.5




0.5




0.5




0.5




0.5




0.5




0.5




0.5




0.5




0.5






K


2


O




0




0




0




0




0




0




0




3




0




0






Sb


2


O


3






0.1




0.1




0.1




0.1




0.1




0.1




0.1




0.1




0.1




0.1






Ion exchange temperature




280




280




280




280




280




280




280




280




280




280






(° C.)






Ion exchange concentration




3




3




3




3




3




3




3




3




3




3






(% by mole)






Ion exchange rate (μ m


2


/min)




0.15




0.09




0.08




0.13




0.18




0.14




4.58




0.13




0.25




0.05






Refractive index




1.4797




1.4880




1.4815




1.4947




1.4893




1.4796




1.4914




1.4785




1.5035




1.4750






(λ = 1,550 nm)






Change in refractive index




0.013




0.014




0.014




0.04




0.022




0.010




0.081




0.015




0.045




0.006






Coloration




None




none




none




none




none




None




present




none




none




none






Birefringence




Low




low




low




low




low




Low




low




high




low




low






Melting temperature (° C.)




1,500




1,500




1,470




1,450




1,450




1,600




1,600




1,500




1,450




1,500














Glass raw materials were blended to make the compositions shown in Table 1, and they were melted in a platinum crucible, and after molding, were slowly cooled to produce samples. After worked into a wafer substrate form, the sample glass substrate was immersed in a 3% by mole silver nitrate (AgNO


3


) molten salt (temperature: 280° C.) for 5 hours to exert ion exchange, and then the ion exchange rate, the change in refractive index, coloration characteristics (absorption characteristics) and birefringence were evaluated. The refractive index of the substrate glass and the melting temperature required for homogenization of the glass were also measured.




The sample Nos. 1 to 5 were glass compositions within the scope of the invention, and the sample Nos. 6 to 10 were glass compositions outside the scope of the invention (comparative examples). All species of the glass of sample Nos. 1 to 5 had change amounts of refractive index that were sufficient for single mode design, and they were transparent and had low birefringence. They had low refractive indexes of the glass substrates, and the melting temperatures thereof were relatively low as 1,500° C. or less to form homogeneous glass. On the other hand, the species of glass of sample Nos. 6 and 7 required high temperature melting due to the large amounts of Al


2


O


3


, and it was difficult to prepare homogeneous glass. The glass of sample No. 7, which was only one kind of glass that did not contain B


2


O


3


, caused coloration. Sample No. 8 exhibited birefringence because K


2


O was contained as an oxide of an alkali metal. The glass of sample No. 9 had a high refractive index owing to the excess amount of alkali, and thus matching with an optical fiber was difficult. The glass of sample No. 10 had a small change amount in refractive index owing to a too small amount of alkali, and had such a disadvantage that single mode design was infeasible.




While not particularly exemplified, the invention can be applied to optical waveguide elements of various structures that have optical waveguides in glass substrates, and thus can be applied not only to various kinds of passive optical planar circuits, but also to part of optical integrated circuits having an active part, and it goes without saying that all the cases are encompassed by the invention.




According to the invention, an optical waveguide of low loss an low stress can be formed by ion exchange of Ag ions in glass capable of producing substrates of a large diameter. That is, such change in refractive index is caused that is sufficient for single mode waveguide, low birefringence and low absorption characteristics are obtained, excellent weather resistance is exhibited, high productivity is obtained, and low loss joint with an optical fiber is realized.



Claims
  • 1. An optical waveguide element comprising a multicomponent glass material formed of Na2O—B2O3—Al2O3—SiO2 glass, comprising:SiO2: 60 to 75% by mole, B2O3: 10 to 20% by mole, Al2O3: 2 to 10% by mole, Na2O: 5 to 13% by mole, As2O3: 0 to 0.5% by mole, and Sb2O3: 0 to 0.5% by mole provided that Li2O is greater than 0% and less than 1% by mole, and As2O3+Sb2O3: 0.01 to 1% mole, wherein the multicomponent glass material is doped with Ag ions by ion exchange to form an optical waveguide.
  • 2. An optical waveguide element comprising a multicomponent glass material formed of Na2O—B2O3—Al2O3—SiO2 glass, comprising:SiO2: 63 to 72% by mole, B2O3: 10 to 18% by mole, Al2O3: 2 to 8% by mole, Na2O: 7 to 13% by mole, As2O3: 0 to 0.5% by mole, and Sb2O3: 0 to 0.5% by mole provided that Li2O is greater than 0% and less than 1% by mole, and As2O3+Sb2O3: 0.01 to 1% mole, wherein the multicomponent glass material is doped with Ag ions by ion exchange to form an optical waveguide.
  • 3. An optical waveguide element as described in claim 1, wherein the glass material has a refractive index of 1.50 or less with respect to a near infrared ray having a wavelength of from 1,200 to 1,650 nm.
  • 4. An optical waveguide element as described in claim 1, wherein the glass material is in a substrate form having a thickness of 5 mm or less, at least one surface of which is in a state of a mirror surface having a surface roughness Ra of from 0.001 to 0.1 μm.
  • 5. An optical waveguide element as described in claim 1, wherein an Ag ion doping region is embedded within the glass material.
  • 6. A process for producing an optical waveguide element as described in claim 1, comprising carrying out ion exchange of Ag ions at 200 to 350° C.
  • 7. A process for producing an optical waveguide element as described in claim 6, wherein the ion exchange is carried out with a processing bath containing Ag ions.
PCT Information
Filing Document Filing Date Country Kind
PCT/JP02/00322 WO 00
Publishing Document Publishing Date Country Kind
WO02/06147 8/8/2002 WO A
US Referenced Citations (12)
Number Name Date Kind
3649311 Araujo Mar 1972 A
4160654 Bartholomew et al. Jul 1979 A
4562161 Mennemann et al. Dec 1985 A
4792535 Fine Dec 1988 A
4894303 Wu Jan 1990 A
4902426 Macedo et al. Feb 1990 A
5004707 Ross et al. Apr 1991 A
5007948 Araujo Apr 1991 A
5114453 Ross et al. May 1992 A
5114813 Smoot et al. May 1992 A
5145757 Smoot et al. Sep 1992 A
5790729 Pologe et al. Aug 1998 A
Foreign Referenced Citations (4)
Number Date Country
2170797 Jan 1986 GB
8-86927 Apr 1996 JP
2001-133649 May 2001 JP
550349 Apr 1977 SU
Non-Patent Literature Citations (10)
Entry
Machine Translation of JP 08-086927.*
Machine Translation of JP 2001-133649.*
Derwent Abstract 1977-86114Y of SU 550349.*
G.A.C.M. Splerings et. al., Journal of Non-Crystalline Solids, vol. 113 No. 1 (Nov. 2, 1989) pp. 37-40.
D. Bougaud et. al., Ionics, Vo1.25 (1999) pp. 415-420.
B. Messersycnidt et. al., Optical Materials, vol. 7 No. 4 (May 1997) pp. 165-171.
S. A. Poling et. al., Journal of Non-Crystalline Solids, vol. 272 No. 1 (Jul. 2, 2000) pp. 39-45.
T. Prosner et. al., Glastechnische Berichte, vol. 64 No. 7 (Jul. 1991) pp. 186-190.
Ludwig Roβ, “Integrated optical components in substrate glasses”, Review Paper, pp. 285-297, Glastech, Ber. 62 (1989) Nr. 8.
T. Findakly, “Glass waveguides by ion exchange: a review” Optical Engineering, 1985, vol. 24 No. 2, pp. 244-250.