Claims
- 1. Polyisocyanate based organic aerogel having pore sizes of less than or equal to 100 nm, wherein said aerogel is selected from the group consisting of polyurethane aerogels, polyurea aerogels, polyisocyanurate aerogels, polyisocyanurate/polyurethane aerogels, polyallophanate aerogels, polybidentate aerogels and polybiuret aerogels.
- 2. Aerogel according to claim 1 having pore sizes in the range 5 to 50 nm.
- 3. Aerogel according to claim 1 having densities in the range 1 to 1000 kg/m.sup.3.
- 4. Aerogel according to claim 3 having densities in the range 20 to 400 kg/m.sup.3.
- 5. Aerogel according to claim 1 having surface areas in the range 10 to 1500 m.sup.2 /g.
- 6. Aerogel according to claim 5 having surface areas in the range 200 to 1000 m.sup.2 /g.
- 7. Method for preparing an aerogel as defined in claim 1 comprising the steps of
- a) mixing an organic polyisocyanate and an isocyanate trimerisation catalyst in a suitable solvent,
- b) maintaining said mixture in a quiescent state for a sufficiently long period of time to form a polymeric gel, and
- c) supercritically drying the obtained gel.
- 8. Method according to claim 7 wherein the organic polyisocyanate is diphenylmethane diisocyanate or polymethylene polyphenylene polyisocyanate or an isocyanate-ended prepolymer.
- 9. Method according to claim 7 wherein the organic polyisocyanate is used in amounts ranging from 0.5 to 30% by weight based on the total reaction mixture.
- 10. Method according to claim 7 wherein a higher functionality isocyanate-reactive compound and a urethane catalyst are mixed together with the other ingredients in step a).
- 11. Method according to any one of claim 10 wherein the higher functionality isocyanate-reactive compound is the reaction product of alkylene oxides with initiators containing 2 to 8 active hydrogen atoms per molecule.
- 12. Method according to claim 11 wherein the initiator is ethylene diamine.
- 13. Method according to claim 10 wherein the higher functionality isocyanate-reactive compound is used in amounts varying between 1 and 60% by weight based on the polyisocyanate.
- 14. Method according to claim 7 wherein the isocyanate trimerisation catalyst is a triazine derivative.
- 15. Method according to claim 10 wherein the urethane catalyst is a tertiary amine and wherein the polyisocyanate/catalyst weight ratio is between 5 and 1000.
- 16. Method according to claim 7 wherein the solvent is dichloromethane.
- 17. Method according to claim 7 wherein the solvent is exchanged prior to supercritically drying the gel.
- 18. Method according to claim 17 wherein the solvent is exchanged into liquid carbondioxide.
Priority Claims (2)
Number |
Date |
Country |
Kind |
9315198 |
Jul 1993 |
GBX |
|
9319451 |
Sep 1993 |
GBX |
|
CROSS-REFERENCE TO RELATED APPLICATIONS
The present application is a continuation-in-part of U.S. patent application Ser. No. 08/129,297, filed Sep. 29, 1993 entitled "Organic Aerogels" now abandoned.
US Referenced Citations (11)
Foreign Referenced Citations (1)
Number |
Date |
Country |
1172255 |
Nov 1969 |
GBX |
Continuation in Parts (1)
|
Number |
Date |
Country |
Parent |
129297 |
Sep 1993 |
|