Organic electroluminescence element and method of manufacturing the same

Information

  • Patent Grant
  • 6297588
  • Patent Number
    6,297,588
  • Date Filed
    Thursday, September 2, 1999
    25 years ago
  • Date Issued
    Tuesday, October 2, 2001
    23 years ago
Abstract
An organic electroluminescence element includes a substrate carrying a transparent electrode; a plurality of organic functional layers including an organic light-emitting layer deposited on the transparent electrode; and a metal electrode over the organic functional layers. A part of the organic functional layers covering any foreign body is melted, regardless of whether or not the foreign body has been on the transparent electrode so that the melted part of the organic functional layer on the foreign body is merged into the organic functional layer stacked on the transparent electrode around the foreign body, so as to enclose the solid foreign body in the organic functional layer.
Description




BACKGROUND OF THE INVENTION




1. Field of the Invention




The present invention relates to an organic electroluminescence element (also referred to as “organic EL element” hereinafter) utilizing an organic compound material which exhibits an electroluminescence phenomenon, i.e., emission of light resulting from injection of an electric current into a the organic material and to a method of manufacturing the same.




The present invention also relates to an organic electroluminescence display device (also referred to as “organic EL display device” hereinafter) comprising a plurality of organic EL elements.




2. Description of the Related Art




In recent years, much attention has been focused on the organic EL display device with a flat display panel on which many organic EL elements each comprising an organic light-emitting layer made of an organic material are arranged. In general, as shown in

FIG. 1

, each organic EL element


1


has such a structure that a transparent electrode


3


(anode) made of indium tin oxide (so called ITO), a plurality of organic functional layers


4


made of respective organic materials and including the organic light-emitting layer, and a metal electrode


5


(cathode) are sequentially laminated on a glass substrate


2


serving as a display surface, by vapor deposition or the like. The organic functional layers


4


may include a hole injection layer, a hole transport layer, an electron transport layer and the like if necessary in addition to the organic llght-emitting layer. The hole injection layer is made of an organic material capable of injecting positive holes into the hole transport layer. The hole transport layer is made of an organic material capable of transporting positive holes into the organic light-emitting layer. The electron transport layer is made of an organic material capable of transporting electrons into the organic light-emitting layer. For example, there is an EL display device of the X-Y matrix type in which EL elements are manufactured in such a manner that the hole transport layer and the organic light-emitting layer are deposited in that order on ITO stripes of transparent electrodes (anode lines) previously formed on a transparent glass substrate and then a plurality of metal electrodes (cathode lines) are formed on the organic light-emitting layer so as to cross the ITO stripes on two levels. The respective EL elements at intersections between the anodes and cathodes form a matrix of light-emitting points corresponding to pixels. In addition to the EL element with a two-layered structure composed of the hole transport layer and the organic light-emitting layer above mentioned, there are other EL element types such as a three-layered structure having an organic electron transport layer additionally provided between the organic light-emitting layer and the metal electrodes, and a multiple-layered EL element type formed of still more layers.




Since the vapor depositions of the individual layers on the glass substrate are preformed for making the organic EL element, for example as shown in

FIG. 2

, if dust or a solid foreign body


6


lies on the anode


3


at the time of depositing those layers, the foreign body makes it hard for the following vapor particles to be vapor-deposited around the underlying contact on the anode. It is therefore probable that an organic functional layer


4


tends to be thinner at the peripheral portion of the area underlying the foreign body than at the other areas. As a result, the anode


3


and a cathode


5


to be stacked later come closer to each other in the vicinity of the foreign body


6


, thereby causing concentration of an electric field which will change the luminance of the emitted light. In some case, the anode


3


may come into contact with the cathode


5


thereby causing short-circuiting, which may produce non-luminous areas called “dark spots” or may damage the EL element per se.




One countermeasure that has been taken against this problem is to clean the substrate upon deposition of each layer. However, this method alone is hardly possible to completely remove a foreign body once it is stuck on any layer.




SUMMARY OF THE INVENTION




The present invention has been made in view of the above circumstances, and an object thereof is to provide a reliable EL element in which the possibility of a short circuit or leak current between the transparent electrode anode and the metal electrode cathode is reduced.




To attain the above object, the present invention provides an organic EL element comprises:




a substrate carrying a transparent electrode;




a plurality of organic functional layers including an organic light-emitting layer deposited on the transparent electrode, wherein a part of at least one of the organic functional layers which is heaped on a solid foreign body is melted, regardless of whether or not the solid foreign body has been on the transparent electrode, so that the melted part of the organic functional layer on the solid foreign body is merged into the organic functional layer stacked on the transparent electrode around the solid foreign body, thereby burying the solid foreign body in the organic functional layer; and




a metal electrode over the organic functional layers.




In the organic EL element according to the invention, the melting of the part of the organic functional layer covering the solid foreign body is performed in a way that the whole substrate is heated to a temperature equal to or higher than a glass transition point of the organic functional layer and equal to or lower than a melting point thereof.




To attain the above object, the present invention also provides a method of manufacturing an organic EL element having a plurality of organic functional layers including an organic light-emitting layer sandwiched between a pair of electrodes, which method comprises the steps of:




depositing a first organic functional layer over a transparent electrode previously formed on a light permeable substrate;




melting a part of the first organic functional layer which is heaped on a solid foreign body, regardless of whether or not the solid foreign body has been on the transparent electrode prior to the first organic functional layer forming step, so that the melted part of the first organic functional layer on the solid foreign body is merged into the first organic functional layer stacked on the transparent electrode around the solid foreign body, thereby burying the solid foreign body in the first organic functional layer;




depositing a second organic functional layer on the first organic functional layer; and




forming a metal electrode over the second organic functional layer.




In the method of manufacturing an organic EL element according to the invention, the step of melting the part of the organic functional layer covering the solid foreign body is performed in a way that the whole substrate Is heated to a temperature equal to or higher than a glass transition point of the organic functional layer and equal to or lower than a melting point thereof.




In the method of manufacturing an organic EL element according to the invention, the organic functional layers and the metal electrode are formed through a vapor deposition method.




According to the EL display device having the above construction, even if dust or a solid foreign body is inadvertently introduced during the manufacturing process of the organic EL element, the foreign body is always enclosed by organic material i.e., an organic functional layer, so that the transparent electrode and metal electrode of the organic EL element are always set apart at a predetermined distance from each other, thus preventing the transparent electrode and the metal electrode from coming close to or contacting each other. Even if a foreign body is adhered to the transparent electrode, it is possible to prevent generation of a leak current between the transparent electrode and the metal electrode thereby preventing reduction in the luminance of light emitted from each organic EL element and preventing the organic EL elements from being damaged.











BRIEF DESCRIPTION OF THE DRAWINGS





FIG. 1

is an enlarged sectional view schematically showing an organic EL element;





FIG. 2

is an enlarged sectional view schematically illustrating a substrate in a step of manufacturing a conventional organic EL element; and





FIGS. 3

to


7


are enlarged sectional views schematically each showing a substrate in a step of manufacturing an organic EL element according to an embodiment of the present invention.











DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS




An organic EL element and a method of manufacturing the same according to an embodiment of the present invention will be described in more detail with reference to the accompanying drawings.




Referring first to

FIG. 3

, there is shown a substrate


10


on which an EL element is formed. First, ITO is patterned on the transparent substrate


10


, made of glass or the like, as transparent electrodes


11


in parallel to one another at predetermined intervals, by a vapor deposition method or the like.




Next, as shown in

FIG. 4

, an organic functional layer of Copper phthalocyanine or Cu-Pc is vapor-deposited on the ITO transparent electrodes


11


as a hole injection layer


13


.




Then, as shown in

FIG. 5

, a triphenyldiamine-based compound e.g., N,N′-diphenyl-N-N′-bis(3-methylphenyl)-1,1′-biphenyl-4,4′-diamine (hereinafter referred as “TPD”) is vapor-deposited on the hole injection layer


13


as a hole transport layer


14


. The hole transport layer


14


may be formed of 4,4′, 4″-tris[N-(3-methylphenyl)-N-phenylamino] triphenylamine (so called “MTDATA”) instead of TPD. Alternatively, the organic EL element may be structured in such a way that a hole transport layer


14


is formed on the ITO anode


11


without forming hole injection layer.




Subsequently, as shown in

FIG. 6

, the whole substrate


10


is heated to a temperature equal to or higher than the glass transition point of the hole transport layer of TPD


14


and equal to or lower than the melting point thereof. The heating step is preformed for melting a part of the hole transport layer


14




a


deposited on a solid foreign body


6


, even if lies the foreign body on any transparent electrode


11


or the hole injection layer


13


, and causes the now melted organic material fluid


14




a


to merge, due to gravity and surface tension, with the hole transport layer


14


formed on the transparent electrode. This process encapsulates the foreign body


6


in the hole transport layer


14


. As a result, the hole transport layer


14


is contiguously formed without a break or gap due to the foreign body


6


. With the material of the hole transport layer


14


having a glass transition point of 95° C., for example, the melting temperature is about 150° C. and the heating time is approximately 5 minutes. It is to be noted that a halide lamp may serve as a heater for heating the whole substrate under reduced pressure or in a vacuum chamber.




Next, as shown in

FIG. 7

, for example, tris(8-hydroxyquinoline) aluminum complex or Alq3 is vapor-deposited as an organic light-emitting layer


16


on the hole transport layer


14


. Then, Li


2


O is vapor-deposited as an electron-injecting layer


15


on the organic light-emitting layer


16


. Subsequently, aluminum Al is vapor deposited as a metal electrode


21


on the electron-injecting layer


15


In such a manner that the metal electrode


21


perpendicularly intersects the transparent electrode


11


via the organic functional layers on the substrate. In this way, a display panel comprising organic EL elements Is prepared.




It is also possible to form an electron transport layer between the organic light-emitting layer and the electron-injecting layer, as an additional organic functional layer.




According to the invention, by heating the whole substrate to a temperature equal to or higher than the glass transition point of at least of the organic functional layers on the ITO electrode and equal to or lower than the melting point of the at least of the organic functional layers, even if the foreign body


6


is introduced during the vapor-deposition for layers, the foreign body is covered with an organic material of the hole transport layer and/or electron transport layer, so that the transparent electrode


11


and metal electrode


21


of an organic EL element are set apart at a given distance from each other, thus preventing the transparent electrode layer and the metal electrode layer from coming close to or contacting each other. When a foreign body is adhered to the transparent electrode, it is possible to prevent generation of a leak current between the transparent electrode


11


and the metal electrode


21


to be formed later, thereby preventing reduction in the luminance of light emitted from each organic EL element and preventing the individual organic EL elements of a display panel from being damaged.



Claims
  • 1. An organic electroluminescence element comprising:a substrate carrying a transparent electrode; a plurality of organic functional layers including an organic light-emitting layer deposited on the transparent electrode, wherein at least one of the organic functional layers is melted so as to enclose a foreign body so that a part of said at least one of the organic functional layers on the solid foreign body is merged into another part of said at least one of the organic functional layers around the foreign body, thereby enclosing the foreign body in said at least one organic functional layer; and a metal electrode over the organic functional layers.
  • 2. An organic electroluminescence element according to claim 1, wherein when said at least one of the organic functional layers is melted on the foreign body, the substrate is heated to a temperature equal to or higher than a glass transition point of said at least one organic functional layer and equal to or lower than a melting point thereof.
Priority Claims (1)
Number Date Country Kind
10-256725 Sep 1998 JP
US Referenced Citations (3)
Number Name Date Kind
5231329 Nishikitani et al. Jul 1993
5643829 Kang Jul 1997
6104137 Abiko et al. Aug 2000
Foreign Referenced Citations (1)
Number Date Country
2176340 Dec 1986 GB