This application claims the benefit of Korean Patent Application No. 10-2004-0117962, filed on Dec. 31, 2004, in the Korean Intellectual Property Office, the disclosure of which is incorporated herein in its entirety by reference.
1. Field of the Invention
The present invention relates to an organic electroluminescent device comprising a polymer layer containing a polyimide (PI) having a triphenylamine derivative (TPD) unit.
2. Description of the Related Art
An organic electroluminescent (EL) device is an active drive type emission display device that operates under the principle that when current is applied to fluorescent or phosphorescent organic compound layers (referred to as “organic layers” hereinafter), electrons and holes are combined in the organic layers to then emit light. Organic EL devices have various advantages including being lightweight, simple components, having a simplified fabrication process, and offering a wide viewing angle. Also, organic EL devices can enable moving picture display perfectly with high color purity, and the devices have electrical properties suitable for portable electronic devices at low power consumption and low driving voltage.
A general organic EL device is constructed such that an anode is formed on a substrate, a hole transport layer, an emissive layer, an electron transport layer, and a cathode are sequentially formed on the anode. Here, the hole transport layer, the emissive layer, and the electron transport layer are organic layers made of organic compounds. The electroluminescence mechanism of a general organic EL device will now be described. When a voltage is applied between an anode and a cathode, holes are moved from an anode to an emissive layer via a hole transport layer, and electrons are moved from a cathode to the emissive layer via an electron transport layer. The electrons and holes meet in the emissive layer for recombination, forming excitons. The excitons are subjected to radiative decay, producing light having a wavelength corresponding to a band gap of an emissive layer forming material.
To date, there have been made various attempts to enhance emission efficiency and lifetime characteristics of the organic EL device, including the followings: 1) facilitating injection of electrons and/or holes; 2) increasing electron and/or hole mobility; 3) facilitating recombination of electrons and holes; and 4) increasing photo conversion efficiency.
To achieve the above stated goals, the following techniques are provided: 1) minimizing an energy barrier between an electrode and a transport layer; 2) increasing electron and/or hole mobility through cascade transport; 3) inducing a balanced current using a hetero-junction structure or a low mobility emitter; and 4) using a phosphorescent material and fluorescent/phosphorescent hybrid materials as light-emitting layers.
Another method of enhancing emission efficiency and lifetime characteristics of the organic EL device which has an organic layer structure comprised of a hole transport layer, a light-emitting layer, and an electron transport layer is to control injection, movement and recombination of electrons and holes by providing an polymer interlayer between the hole transport layer and the light-emitting layer.
In other words, the polymer interlayer serves as a buffer layer that prevents migration of sulfur from the hole transport layer, usually a stacked layer of PEDOT/PSS(poly(3,4-ethylenedioxythiophen)/polystyrene sulfonate), and prevents a PEDOT/PSS layer, which is a strongly acidic layer, from directly contacting with the light-emitting layer. In addition, the polymer interlayer prevents electrons and exitons from being induced into the PEDOT/PSS layer, thereby enhancing life characteristics of the organic EL device.
Cho, et al. proposed a polymeric EL device having a hole blocking layer into which PMDA-ODA type polyimide (PI) is injected to various thicknesses in various packing densities, as described in Thin Solid Films 417(2002) 175-179, “The role of PI interlayer deposited by ionized cluster beam on the electroluminescence efficiency” between an ITO electrode and a light-emitting layer made of BEH-PPV polymer using ionized cluster beam (ICB). Here, the PMDA-ODA type polyimide serves as a hole injection barrier that prevents impurities of the ITO electrode from being diffused into the inside of the polyimide layer, causing balanced recombination of holes and electrons. The above-referenced document discloses a PI layer serving to reduce a hole tunneling probability, rather than serving as an electron blocking layer, in order to provide an organic EL device with enhanced efficiency using balanced charge carriers.
Kim, et al. proposed a polymeric EL device (PLED) having a thin polymer interlayer between an PEDOT/PSS and a light-emitting layer, as described in Applied Physic Letter 87(2005), 023506, “Spin-cast thin semiconducting polymer interlayer for improving device efficiency of polymer light-emitting diodes”. The thin interlayer blocks the radiative exitons from direct quenching by PEDOT-PSS and thus removes a nonradiative decay channel introduced by PEDOT-PSS. This exciton blocking property of conjugated polymer interlayer significantly improves the efficiency and lifetime of PLEDs. As a thin conjugated polymer interlayer, triphenylamine-based conjugated polymers, such as poly(9,9-dioctylfluorene-co-bis-N,N′-(4-butylphenyl)-bis-N,N′-phenyl-1,4-phenylenediamine) (PFB) and poly(9,9′-dioctylfluorene-co-N-(4-butylphenyl)diphenylamine) (TFB) can be used, since such polymers are semiconductors having a wide band gap, low ionization potential, and high hole mobility due to their triphenylamine groups in the polymer backbone. However, these conjugated polymers are readily soluble in the common organic solvents, such as toluene and xylene, which are also used for light emitting polymer process. Therefore, when the light-emitting polymer was spin-coated, the underlying spin-cast polymer interlayer was partially dissolved and then washed out by the solution of light emitting polymer, or intermixed with light emitting polymer. The thickness control of a thin conjugated polymer interlayer is, thus, fundamentally difficult, which is a serious problem for the practical use.
The present invention provides an organic EL device comprising a polymer layer polymer containing a polyimide having a TPD unit which is not soluble in a solvent used in coating of a light-emitting material and has electron and exciton blocking capability.
The present invention also provides a polyimide having a TPD unit used for a polymer layer in an organic EL device.
The present invention also provides a method of preparing a polyimide having a TPD unit.
According to an aspect of the present invention, there is provided an organic electroluminescent (EL) device comprising a polymer layer containing a polyimide having the triphenylamine derivative (TPD) unit.
According to another aspect of the present invention, there is provided an organic electroluminescent (EL) device comprising a polymer layer containing a polyimide represented by Formula 1 between an anode and a light emitting layer:
where X is a tetravalent aromatic hydrocarbon group, n is an integer of 1 to 10,000, and Y is
where R1 and R2 are each independently a hydrogen or a monovalent C1-C15 organic group, W is a bond or
where Ar is an aryl group, A is a bond or an aryl group, and Z is a bond or an arylenyl group.
According to another aspect of the present invention, there is provided a polyimide having a triphenylamine derivative (TPD) unit represented by Formula 2:
where X is a tetravalent aromatic hydrocarbon group, n is an integer of 1 to 10,000, and each R1 and each R2 are each independently a hydrogen or a monovalent C1-C15 organic group.
According to still another aspect of the present invention, there is provided a method of preparing a polyimide containing a triphenylamine derivative (TPD) unit represented by Formula 2, the method comprising reacting a tetracarboxylic dianhydride represented by Formula 3 with a triphenylamine derivative represented by Formula 4:
where X is a tetravalent aromatic hydrocarbon group, n is an integer from 1 to 10,000, and each R1 and each R2 are each independently a hydrogen or a monovalent C1-C15 organic group.
The polymer layer comprising the polyimide (PI) having a triphenylamine derivative (TPD) unit according to the present invention has excellent mechanical strength and thermal stability, thus demonstrating various advantages, including good film forming performance, high planarity and excellent solvent selectivity, enabling the organic EL device containing the same to exhibit a good lifetime characteristic.
A more complete appreciation of the present invention, and many of the above and other features and advantages of the present invention, will be readily apparent as the same becomes better understood by reference to the following detailed description when considered in conjunction with the accompanying drawings in which like reference symbols indicate the same or similar components, wherein:
Hereinafter, the embodiments of the present invention will be described in detail with reference to the accompanying drawings.
The present invention provides an organic electroluminescent (EL) device comprising a polymer layer containing a polyimide having the triphenylamine derivative (TPD) unit.
Since the polyimide may serve as a buffer layer preventing a hole transfer layer or a hole injection layer from directly contacting with the light-emitting layer, and the polyimide may prevent electrons from being injected into the hole transport layer, thereby effectively preventing electrons from migrating from the light-emitting layer to the hole transport layer.
Accordingly, the polymer layer may be formed between an anode (or a hole transport layer or hole injection layer) and a light emitting layer:
where X is a tetravalent aromatic hydrocarbon group, n is an integer of 1 to 10,000, and Y is
where R1 and R2 are each independently a hydrogen or a monovalent C1-C15 organic group, W is a bond or
where Ar is an aryl group, A is a bond or an aryl group, Z is a bond or an arylenyl group.
In Formula 1, Y may be any one selected from the followings:
where each R1 and each R2 are each independently a hydrogen or a monovalent C1-C15 organic group.
Preferred examples of X, which is a tetravalent aromatic hydrocarbon group, include:
Preferred polyimide having the triphenylamine derivative (TPD) unit is represented by Formula 2:
where X is a tetravalent aromatic hydrocarbon group, n is an integer of 1 to 10,000, each R1 and each R2 are each independently a hydrogen or a monovalent C1-C15 organic group.
In the polyimide containing the triphenylamine derivative (TPD) unit, since the TPD unit has excellent hole transporting capability, the polyimide serves as a buffer layer which prevents the PEDOT/PSS layer which is a hole transfer layer or a hole injection layer from directly contacting with the light-emitting layer. In addition, the polyimide prevents electrons from being injected into the hole transport layer, thereby effectively preventing electrons from migrating from the light-emitting layer to the hole transport layer.
Also, since the polyimide containing triphenylamine derivative (TPD) unit is generally insoluble in a solvent such as toluene used in coating a light-emitting layer, any solvent can be selected in coating the light-emitting layer without limitation.
In Formula 1, n is an integer from 1 to 10,000, preferably from 1 to 1,000.
In Formula 1, R1 and R2 may be a hydrogen or a monovalent C1-C15 organic group. Examples of the monovalent C1-C15 organic group may include, but are not limited to, a substituted or unsubstituted alkyl, aryl, alkenyl, aralkyl, heteroalkyl, heteroaryl.
The polyimide containing the triphenylamine derivative (TPD) unit represented by Formula 2 can be prepared by reacting aromatic tetracarboxylic dianhydride of Formula 3 with a triphenylamine derivative represented by Formula 4:
where X is a tetravalent aromatic hydrocarbon group, n is an integer from 1 to 10,000, and R1 and R2 are each independently a hydrogen or a monovalent C1-C15 organic group.
The above preparation method can be expressed by the following reaction scheme 1:
where X, n, R1 and R2 are defined as described in Formula 1.
In detail, aromatic tetracarboxylic dianhydride and the triphenylamine derivative mixed in a molar ratio of 1:1, concretely 5 to 30 wt %, preferably 10 to 20 wt %, are added to an organic solvent such as N,N-dimethylacetamide (DMAc), N-methyl-2-pyrrolidone (NMP), or dimethylacetamide (DMAc), and allowed to react with each other under a nitrogen atmosphere at a temperature ranging from 0 to 10° C. for about 4 to 20 hours, preferably for about 10 to about 15 hours, yielding a polyamic acid having such a repeating unit as shown in the above reaction scheme. Toluene was reacted in a solution of the polyamic acid under a nitrogen atmosphere at a temperature ranging from 150 to 180° C. for about 2 to 4 hours, thereby preparing a soluble polyimide having the TPD.
The triphenylamine derivative of Formula 4 used in the present invention can be prepared by a general method. In detail, N,N′-diphenyl-N,N′-bis(4-aminophenyl)-1,1-biphenyl-4,4′-diamine can be prepared by the reaction scheme 2:
Specifically, 4,4′-dibromobiphenyl and 4-nitrodiphenylamine are reacted in a 1:2 molar ratio to obtain N′-diphenyl-N,N′-bis(4-nitrophenyl)-1,1-biphenyl-4,4′-diamine, which is then subjected to a reduction reaction, yielding N,N′-diphenyl-N,N′-bis(4-aminophenyl)-1,1-biphenyl-4,4′-diamine.
The polymer layer of the present invention is formed on a hole transport layer. After forming the hole transport layer on an anode, the obtained polyimide having a TPD unit represented by Formula 1 is dissolved in a solvent such as NMP, DMF, etc., for coating, thereby forming the electron blocking layer.
The polymer layer preferably has a thickness of 10 to 50 nm. If the thickness of the polymer layer is less than 10 nm, a desired electron end exciton blocking effect cannot be achieved. If the thickness of the polymer layer is greater than 30 nm, hole transporting efficiency undesirably deteriorates.
As described above, after forming the polymer layer, a light-emitting layer is subjected to solution-coating thereon. Since the polyimide having a TPD unit represented by Formula 1 is insoluble in a solvent such as toluene, any solvent can be selected, without limitation, in coating the light-emitting layer. In addition, since the polymer layer is not dissolved in the solvent while in use, thinning of the polymer layer does not occur. Thus, a change in the luminance of the organic EL device slowly proceeds over time.
Examples of usable materials from which the hole transport layer can be made include, without limitation, widely used hole transport layer materials, preferably PEDOT/PSS, polytriphenylamine, and so on.
Examples of usable materials from which the electron transport layer can be made include, without limitation, widely used electron transport layer materials, preferably polyoxadiazole.
The organic EL device according to the present invention may also include a hole blocking layer. Examples of usable materials from which the hole blocking layer can be made include, without limitation, widely used hole blocking layer materials, preferably LiF, BaF2, MgF2 and so on.
To manufacture the organic EL device according to the present invention, any particular apparatus or method is not needed. Rather, the organic EL device according to the present invention can be manufactured by a method for manufacturing an organic EL device using a general light-emitting material.
The present invention will be explained in more detail with reference to Examples that follow, but the following examples are for illustrative purposes only, and are not intended to limit the scope of the invention.
In a 100 mL three-necked flask were dissolved 1.56 g of 4,4′-dibromobiphenyl, 2.30 g of 4-nitrodiphenylamine, 1.44 g of sodium tert-butoxide and 0.51 g of tris(dibenzylideneacetone) dipalladium in 50 mL of p-xylene, followed by adding 0.3 mL of tri-t-butylphosphine to the resultant mixture, causing a reaction to take place under a nitrogen atmosphere at about 150° C. for about 16 hours. After the reaction was completed, a resultant solution was filtered to remove solid matter, and dissolved in excess chloroform. The salt was filtered using distilled water and the resultant solution was then concentrated. Then, purification was performed through column chromatography and recrystallization, acquiring 1.2 g of N,N′-diphenyl-N,N′-bis(4-nitrophenyl)-1,1-biphenyl-4,4′-diamine in the form of powder. The acquired powder was dissolved in 50 mL ethanol, 1.5 mL hydrazine monohydrate was added thereto with a catalytic amount of 10% Pd/C, followed by refluxing for 24 hours, yielding 0.9 g of N,N′-diphenyl-N,N′-bis(4-aminophenyl)-1,1-biphenyl-4,4′-diamine.
Synthesis of Soluble Polyimide
In a three-necked flask were dissolved 1:1 molar ratio of 2,2-bis-(3,4-dicarboxyphenyl)hexafluoropropane dianhydride (6FDA) and N,N′-diphenyl-N,N′-bis(4-aminophenyl)-1,1-biphenyl-4,4′-diamine in NMP in a concentration of 10 wt %, causing a reaction to take place under a nitrogen atmosphere at a temperature in a range of 0-5° C. for about 16 hours for polymerization into polyamic acid. The polyamic acid was imidized at about 170° C. for about 4 hours, acquiring the subject compound. The acquired compound has a number average molecular weight of 12,520, a weight average molecular weight of 29,362, and polydispersity of 2.34.
Also,
Fabrication of Organic EL Device
First, the indium tin oxide (ITO) glass (obtained from Samsung Corning Co.) with a sheet resistance of 10 Ω/sq was patterned in a desirable form using a photoresist and etchant, and then cleaned by successive ultrasonic treatment in a detergent, acetone and isopropyl alcohol. Then, a PEDOT-PSS solution (H. C. Starck Batron P Al4083) was spin coated on the ITO layer to form a hole transport layer with a thickness of 50 nm and dried at 200° C. for 5 min in the globe box. The PEDOT-PSS is composed of PEDOT and PSS at the 1:6 weight ratio and the measured conductivity was 6.06×10−4 S/cm. Next, 0.08 g of the compound (A), i.e., polyimide having a TPD unit represented by Formula 1, was dissolved in 9.92 g of DMF and coated on the resultant structure to a thickness of about 15 nm using a spin coater. Next, 0.8 wt % poly [2′,3′,6′,7′-tetrakisoctyloxy spirofluorene-co-10-(4-octyloxy-phenyl)-10H-phenoxazine] was dissolved in 99.2 wt % m-xylene to prepare a composition for a light-emitting layer. The composition was spin coated on the buffer layer and baked in a vacuum oven to remove a solvent from the resultant material, thereby forming a polymer film. Prior to spin coating, the polymer solution was filtered using a 0.2 mm filter. A thickness of the polymer film was adjusted to be about 70 nm by adjusting a concentration of the polymer solution and a spin coating speed.
Subsequently, 4 nm BaF2, 2.7 nm Ca, and 150 nm Al was sequentially deposited on the emissive layer using a vacuum depositor while maintaining a degree of vacuum at 4×10−6 torr or less. During deposition, a thickness and a growing speed of a film were adjusted using a crystal sensor.
An organic EL device was fabricated in the same manner as in Example 1, except for the polyimide layer not being formed.
For the organic EL devices fabricated in Example and Comparative Example, changes in the luminance over time were measured using a luminance meter manufactured by Mcscience-JEIO Tech., and the measurement results are shown in
Use of the polyimide containing the triphenylamine derivative (TPD) unit represented by Formula 1 as an polymer layer makes the polymer layer insoluble in a solvent used when coating the light-emitting layer, thereby adjusting a film thickness of the polymer layer. In addition, any solvent can be selected in coating the light-emitting layer without limitation. Further, since electron and exciton injection from the light-emitting layer to the hole transport layer is prevented, the organic EL device exhibits good luminance efficiency even after a prolonged period use, ultimately leading to enhanced life characteristics.
While the present invention has been particularly shown and described with reference to exemplary embodiments thereof, it will be understood by those of ordinary skill in the art that various changes in form and details may be made therein without departing from the spirit and scope of the present invention as defined by the following claims.
Number | Date | Country | Kind |
---|---|---|---|
10-2004-0117962 | Dec 2004 | KR | national |
Number | Name | Date | Kind |
---|---|---|---|
20030098646 | Suh et al. | May 2003 | A1 |
Number | Date | Country |
---|---|---|
09-298089 | Nov 1997 | JP |
Number | Date | Country | |
---|---|---|---|
20060147736 A1 | Jul 2006 | US |