Patent Grant
9203052
This application claims priority to and the benefit of Korean Patent Application No. 10-2009-0111630 filed in the Korean Intellectual Property Office on Nov. 18, 2009, the entire contents of which are incorporated herein by reference.
1. Field
This disclosure relates to an organic light emitting diode (OLED) device and a method of manufacturing the same.
2. Description of the Related Technology
An organic light emitting diode (OLED) device emits light when electrons injected from one electrode are combined with holes injected from another electrode in an emission layer between the electrodes and generates an exciton, which releases energy. Since the OLED device is self-emissive, it has very low power consumption.
One aspect is an organic light emitting diode (OLED) device capable of improving luminous efficiency. Another aspect is a method of manufacturing an OLED device that increases luminous efficiency and simultaneously is applied to a large size OLED device.
Another aspect is an OLED device that includes a substrate; a first thin film formed on the substrate and having protrusions and depressions at the surface; a second thin film formed on the first thin film and planarizing the protrusions and depressions; a first electrode formed on the second thin film; a light emitting member formed on the first electrode; and a second electrode formed on the first electrode.
The first thin film and the second thin film may include materials having refractive index different from each other. The first thin film and the second thin film may have refractive index of about 1.1 to 3, respectively. The refractive index difference between the first thin film and the second thin film may be at least 0.2.
The refractive index of the first thin film may range from about 1.6 to 2.2; and the refractive index of the second thin film may range from about 1.3 to 1.6. According to one embodiment, the refractive index of the first thin film may range from about 1.3 to 1.6; and the refractive index of the second thin film may range from about 1.6 to 2.2.
The first thin film may include silicon oxide, silicon nitride, polyacryl, polyimide, or a combination thereof; the second thin film may include silicon nitride, aluminum oxide, or a combination thereof. The protrusions and depressions may be irregularly distributed.
Another aspect is a method of manufacturing an OLED device that includes providing a first thin film having protrusions and depressions on a substrate; providing a second thin film planarizing the protrusions and depressions on the first thin film; providing a first electrode on the second thin film; providing a light emitting member on the first electrode; and providing a second electrode on the light emitting member.
The providing a first thin film having protrusions and depressions may include forming a first thin film; coating a dispersing solution including an organic particulate having a first size on the first thin film; drying the dispersing solution; etching the organic particulate to provide an organic particulate having a second size smaller than the first size; and etching the first thin film using the organic particulate having the second size as a mask.
The organic particulate may have a sphere shape. The organic particulate may include polystyrene. The etching an organic particulate may use plasma. The etching a first thin film may be performed by reactive ion etching.
The providing a first thin film having protrusions and depressions may include forming a first thin film including an organic material and treating the surface of first thin film with plasma. The manufacturing method may further include applying a metal cluster on the first thin film after forming the first thin film; and the treating the surface of first thin film with plasma may be performed by using the metal cluster as a mask.
Another aspect is an organic light emitting diode (OLED) device comprising: a substrate; a first thin film formed on the substrate, wherein the first thin film comprises first and second surfaces opposing each other, wherein the first surface contacts the substrate, and wherein a plurality of protrusions and depressions are alternately formed on the second surface of the first thin film; a second thin film formed on the protrusions and depressions of the first thin film; a first electrode formed on the second thin film; a light emitting member formed on the first electrode; and a second electrode formed on the organic light emitting member.
In the above OLED device, the first thin film and the second thin film have different refractive indexes. In the above OLED device, each of the first thin film and the second thin film has a refractive index of about 1.1 to about 3. In the above OLED device, the refractive indexes of the first thin film and second thin film differ by at least about 0.2. In the above OLED device, the first thin film has a refractive index of about 1.6 to about 2.2, and wherein the second thin film has a refractive index of about 1.3 to about 1.6. In the above OLED device, the first thin film has a refractive index of about 1.3 to about 1.6, and wherein the second thin film has a refractive index of about 1.6 to about 2.2. In the above OLED device, the first thin film is formed of silicon oxide, silicon nitride, polyacryl, polyimide, or a combination thereof, and wherein the second thin film is formed of silicon nitride, aluminum oxide, or a combination thereof. In the above OLED device, the protrusions and depressions are irregularly distributed.
Another aspect is a method of manufacturing an organic light emitting diode (OLED) device comprising: providing a first thin film on a substrate, wherein the first thin film comprises first and second surfaces opposing each other, wherein the first surface contacts the substrate, and wherein the second surface of the first thin film has a plurality of protrusions and depressions which are alternately formed with respect to each other; providing a second thin film on the second surface of the first thin film so as to planarize the protrusions and depressions; providing a first electrode on the second thin film; providing a light emitting member on the first electrode; and providing a second electrode on the light emitting member.
In the above method, the providing of the first thin film comprises: forming the first thin film; coating a dispersing solution on the first thin film, wherein the dispersing solution contains a plurality of first organic particles at least one of which has a first size; drying the dispersing solution; etching the first organic particles into a plurality of second organic particles at least one of which has a second size smaller than the first size; and etching the first thin film with the use of the second organic particles as a mask.
In the above method, the first and second organic particles have a sphere shape. In the above method, the first and second organic particles contain polystyrene. In the above method, the etching of the first organic particles is performed by plasma. In the above method, the etching of the first thin film is performed by reactive ion etching. In the above method, the providing of the first thin film comprises: forming a first thin film containing an organic material; and treating the surface of the first thin film with plasma. The above method further comprises applying a metal cluster on the first thin film after laminating the first thin film; and wherein the plasma treating of the surface of the first thin film is performed with the use of the metal cluster as a mask.
Another aspect is an organic light emitting diode (OLED) device comprising: a substrate; a first layer formed on the substrate, wherein the first layer comprises first and second surfaces opposing each other, wherein the first surface contacts the substrate, and wherein the second surface of the first layer has a plurality of convex and concave portions which are alternately formed with respect to each other; a second layer formed on the convex and concave portions of the first layer; and an organic light emitting diode formed on the second layer.
In the above OLED device, the first and second layers have different refractive indexes. In the above OLED device, at least two of the convex and concave portions are not uniformly formed with respect to the remaining convex and concave portions. In the above OLED device, the first layer is formed of silicon oxide, silicon nitride, polyacryl, polyimide, or a combination thereof, and wherein the second layer is formed of silicon nitride, aluminum oxide, or a combination thereof.
In order to further reduce the power consumption, it is important to increase the luminous efficiency of an organic light emitting diode (OLED) device. The luminous efficiency may be determined by the internal quantum efficiency which is a ratio of the charge number injected from electrode to the quantum number generated from emission layer and the external quantum efficiency which is a ratio of quantum number generated from emission layer to quantum number emitted to the outside.
This disclosure will be described more fully hereinafter with reference to the accompanying drawings, in which exemplary embodiments of this disclosure are shown. As those skilled in the art would realize, the described embodiments may be modified in various different ways, all without departing from the spirit or scope of this disclosure.
In the drawings, the thickness of layers, films, panels, regions, etc., are exaggerated for clarity. Like reference numerals designate like elements throughout the specification. It will be understood that when an element such as a layer, film, region, or substrate is referred to as being “on” another element, it can be directly on the other element or intervening elements may also be present. In contrast, when an element is referred to as being “directly on” another element, there are no intervening elements present.
The first thin film 112 may be made of inorganic material or organic material having a refractive index of about 1.1 to about 3.0. The inorganic material may include, for example, silicon oxide (SiO2), silicon nitride (SiNx), or a combination thereof; the organic material may include, for example, polyacryl, polyimide, or a combination thereof. When the refractive index of the first thin film 112 is similar to the refractive index of the insulation substrate 110, it is possible to decrease the internal total reflection generated at the interface between the insulation substrate 110 and the first thin film 112.
A second thin film (or a second layer) 114 may be formed on the first thin film 112 to planarize the protrusions and depressions 112a of the first thin film 112. The second thin film 114 planarizes the protrusions and depressions 112a of the first thin film 112 to provide a plane emission layer. Therefore, it is possible to prevent that the emission layer is formed on the inclined surface of protrusions and depressions 112a in a less thickness. It is also possible to prevent that the current is concentrated in the inclined part in the case that the emission layer is formed along with the shape of protrusions and depressions 112a. As a result, the degeneration of the device is prevented and to the reliability is improved.
In one embodiment, the second thin film 114 has a refractive index of about 1.1 to about 3.0. In addition, when the refractive index of second thin film 114 is similar to the refractive index of first electrode 191, it is possible to decrease the total internal reflection generated at the interface between the second thin film 114 and the first electrode 191.
The second thin film 114 may be made of inorganic material or organic material having a refractive index different from that of the first thin film 112. The inorganic material may include, for example, silicon nitride (SiNx), aluminum oxide (Al2O3), or a combination thereof; the organic material may include, for example, polyacryl, polyimide, or a combination thereof.
The refractive index difference between the first thin film 112 and the second thin film 114 may be at least about 0.2. For example, the first thin film 112 may have a refractive index of about 1.6 to about 2.2 and the second thin film 114 may have a refractive index of about 1.3 to about 1.6. Further, the first thin film 112 may have a refractive index of about 1.3 to about 1.6 and the second thin film 114 may have a refractive index of about 1.6 to about 2.2.
As in above, the total internal reflection is decreased and the extracted amount to the front surface is increased by providing protrusions and depressions at the interface between the first thin film 112 and the second thin film 114 having different refractive index. Accordingly, the light extracting efficiency may be increased.
A first electrode 191 is formed on the second thin film 114. The first electrode 191 may be either anode or cathode and may be made of a transparent conductive material such as ITO or IZO.
An organic light emitting member 370 is formed on the first electrode 191. The organic light emitting member 370 may have a multi-layer structure including an emission layer (not shown) and an auxiliary layer (not shown) for improving the luminous efficiency of emission layer.
The emission layer may be made of and organic material or a mixture of organic material and inorganic material inherently expressing one color light among primary colors of red, green, and blue. It may include aluminum tris(8-hydroxyquinoline), [Alq3], anthracene, distryl compound or a combination thereof. The organic light emitting diode (OLED) device expresses the desirable image by mixing of primary color lights generated from the emission layer.
The auxiliary layer may include one or at least two layers selected from the group consisting of an electron transport layer (ETL) (not shown) and hole transport layer (HTL) (not shown) for balancing electrons and holes; an electron injection layer (EIL) (not shown) and hole injection layer (HIL) (not shown) for enforcing the injection of electrons and holes.
A second electrode 270 is formed on the organic light emitting member 370. When the first electrode 191 is made of a transparent conductive material, the second electrode 270 may be made of opaque conductive material such as aluminum (Al), calcium (Ca) barium (Ba), or a combination thereof.
The first electrode 191 may be an anode, and the second electrode 270 may be a cathode; on the other hand, the first electrode 191 may be a cathode, and the second electrode 270 may be an anode.
As described above, the OLED device according to one embodiment limits the light passage to increase the light extracting effect to the vertical direction of substrate and to increase the light amount emitted to the outside among light generated from the emission layer. Thereby, it is possible to increase the luminous efficiency and the life-span of device, and simultaneously to decrease the driving voltage of the OLED device.
Hereinafter, the method of manufacturing the OLED device shown in
First, as shown in
Then a dispersing solution (not shown) including a plurality of organic particulate 50 are coated on the lower layer 111. The dispersing solution may be, for example, a suspension that the organic particles 50 are mixed into a dispersing solvent such as water. The coating may be performed by, for example, spin coating.
In one embodiment, the organic particles 50 have a sphere shape made of organic material, for example, polystyrene. Each or at least one of the organic particles (or the first organic particles) 50 may have a size of about 0.03 μm to about 3.2 μm. In one embodiment, the dispersing solution is dried to remove the solvent and to provide an organic particles 50.
As shown in
Referring to
Then the etched organic particles 50a are removed, and a second thin film 114 is formed on the first thin film 112. The second thin film 114 may be formed of, for example, silicon nitride, aluminum oxide in accordance with plasma enhanced chemical vapor deposition (PECVD).
Referring back to
According to one embodiment, the protrusions and depressions 112a may be easily provided by coating and etching process. Accordingly, it may be easily applied for a large size OLED device, so it is possible to overcome the limits that it cannot apply for the large area when using laser.
Hereinafter, the method of manufacturing an OLED device according to another embodiment is described. As in the aforementioned embodiment, the lower layer 111 is formed on the substrate 110. The lower layer 111 may be made of an organic material. The lower layer 111 made of organic material may be cured by heating in an oven or on a heating plate after spin coating.
In one embodiment, the surface of the lower layer 111 made of organic material is treated with plasma to provide a rough surface. The plasma may use, for example, argon (Ar) plasma. By treating the surface of the lower layer 111 made of organic material with plasma, it is possible to relatively easily provide the protrusions and depressions 112a. Therefore, the luminous efficiency is increased due to the protrusions and depressions 112a.
Hereinafter, the method of manufacturing an OLED device according to further another embodiment is described. As in the aforementioned embodiment, the lower layer 111 is formed and treated with plasma to provide the protrusions and depressions 112a. However, differing from the aforementioned embodiment, a metal cluster is applied on the lower layer 111. Then the lower layer 111 is treated with plasma using the metal cluster as a mask to provide the first thin film 112 having the protrusions and depressions 112a at the surface.
The following examples illustrate this disclosure in more detail. These examples, however, are not in any sense be interpreted as limiting the scope of this disclosure.
10 g of sphere polystyrene particles having an average diameter of 0.6 μm was dispersed in 100 ml of water to provide a suspension.
A silicon oxide (SiO2) was deposited on a glass substrate in 0.5 μm in accordance with a chemical vapor deposition (CVD) method. Then the suspension was spin-coated on the silicon oxide layer in 800 rpm. The suspension was dried at a temperature of 25° C. to remove the solvent. The substrate was introduced in a plasma chamber and supplied with oxygen gas (O2) and argon gas (Ar) to plasma-etch the polystyrene particles. Oxygen gas (O2) and argon gas (Ar) were supplied in a flowing amount of 2 sccm and 5 sccm, respectively, and RF (radio frequency) was 200 W. By the plasma etch, the size of polystyrene particles was decreased into about 0.3 μm. The silicon oxide layer was dry-etched with using the etched polystyrene particles as a mask. The dry etching was performed using CHF3 in aninductive coupled plasma (ICP) etching device. The CHF3 was supplied in a flowing amount of 20 sccm; the chamber pressure was 50 mT; the ICP output was 500 W; and it was repeated for three times for each 2 minutes. Then the remaining polystyrene particles were removed by supplying oxygen gas (O2) and argon gas (Ar) in a room pressure plasma chamber.
Polyacryl was spin-coated on a glass substrate in 2.0 μm and dried. Then a substrate was introduced into a plasma chamber and supplied with argon gas (Ar) and nitrogen gas (N2) to perform a plasma etching. The plasma etching was performed under the condition of flowing amount of argon gas (Ar) in 40 sccm and nitrogen gas (N2) in 3 sccm; a chamber pressure of 200 mT; ICP output of 400 W; and an etching time of 5 minutes. The roughness of the surface of organic layer after the etching was measured by an atomic force microscopy (AFM).
Silicon oxide (SiO2) was laminated on a glass substrate in 0.5 μm in accordance with a chemical vapor deposition (CVD) method. Then a Ni layer was deposited on the silicon oxide layer in a thickness of 5 nm using an electron beam depositor. A substrate was introduced in a rapid thermal annealing (RTA) device and treated at 850° C. for one minute to provide a nano-sized Ni cluster. A silicon oxide layer was etched by a reactive ion etching (RIE) using the Ni cluster as a mask. Then the Ni cluster was removed using a nitric acid solution. Then similarly to Example 1, a silicon nitride layer, ITO, an emission layer, and silver were sequentially laminated to provide an organic light emitting element.
According to at least one embodiment, since the protrusions and depressions are formed where light generated from the emission layer passes, the light extracting efficiency in the vertical dimension of the substrate increases. Furthermore, the amount of light emitted to the environment increases. Thereby, the luminous efficiency is improved, and the life-span of the device is lengthened. Simultaneously, the driving voltage of an organic light emitting diode (OLED) device may be decreased. In addition, since the protrusions and depressions may be formed by a wet process such as spin-coating or a dry process such as plasma etching, it is possible to be applied for a large size display device.
While this disclosure has been described in connection with what is presently considered to be practical exemplary embodiments, it is to be understood that this disclosure is not limited to the disclosed embodiments, but, on the contrary, is intended to cover various modifications and equivalent arrangements included within the spirit and scope of the appended claims.
| Number | Date | Country | Kind |
|---|---|---|---|
| 10-2009-0111630 | Nov 2009 | KR | national |
| Number | Name | Date | Kind |
|---|---|---|---|
| 5100478 | Kawabata | Mar 1992 | A |
| 6091195 | Forrest et al. | Jul 2000 | A |
| 6638601 | Follensbee | Oct 2003 | B1 |
| 6833667 | Hamano et al. | Dec 2004 | B2 |
| 6900457 | Toguchi et al. | May 2005 | B2 |
| 7342246 | Sugiura et al. | Mar 2008 | B2 |
| 7473932 | Cho et al. | Jan 2009 | B2 |
| 7501665 | Yasuda et al. | Mar 2009 | B2 |
| 7916254 | Matsumori et al. | Mar 2011 | B2 |
| 20020197875 | Lin et al. | Dec 2002 | A1 |
| 20030117067 | Roitman et al. | Jun 2003 | A1 |
| 20040241924 | Chen et al. | Dec 2004 | A1 |
| 20050000564 | Sato et al. | Jan 2005 | A1 |
| 20050007000 | Chou et al. | Jan 2005 | A1 |
| 20050082562 | Ou et al. | Apr 2005 | A1 |
| 20050161693 | Sugiura et al. | Jul 2005 | A1 |
| 20060054907 | Lai | Mar 2006 | A1 |
| 20060071233 | Cho et al. | Apr 2006 | A1 |
| 20060175961 | Choong | Aug 2006 | A1 |
| 20070210676 | Matsuda et al. | Sep 2007 | A1 |
| 20070257608 | Tyan et al. | Nov 2007 | A1 |
| 20070290607 | Okada et al. | Dec 2007 | A1 |
| 20080012005 | Yang et al. | Jan 2008 | A1 |
| 20080067929 | Kuo | Mar 2008 | A1 |
| 20080218076 | Kabay et al. | Sep 2008 | A1 |
| 20090015142 | Potts et al. | Jan 2009 | A1 |
| 20090211783 | Tsutsumi et al. | Aug 2009 | A1 |
| 20090236962 | Fujimoto et al. | Sep 2009 | A1 |
| 20100019235 | Iizumi et al. | Jan 2010 | A1 |
| 20100059365 | Valentin et al. | Mar 2010 | A1 |
| 20110006337 | Kim et al. | Jan 2011 | A1 |
| 20110042695 | Oyamada | Feb 2011 | A1 |
| 20110076456 | Wang | Mar 2011 | A1 |
| 20110114921 | Yang et al. | May 2011 | A1 |
| 20110316036 | Furukawa | Dec 2011 | A1 |
| Number | Date | Country |
|---|---|---|
| 101034879 | Sep 2007 | CN |
| 1 603 367 | Dec 2005 | EP |
| 2003-218383 | Jul 2003 | JP |
| 2003-340289 | Dec 2003 | JP |
| 2005-183905 | Jul 2005 | JP |
| 2009-037810 | Feb 2009 | JP |
| 10-2004-0061798 | Jul 2004 | KR |
| 10-2007-0076738 | Jul 2007 | KR |
| 10-2007-0102947 | Oct 2007 | KR |
| I278250 (B) | Apr 2007 | TW |
| 200902466 (A) | Jan 2009 | TW |
| 200913767 (A) | Mar 2009 | TW |
| WO 2009063954 | May 2009 | WO |
| Entry |
|---|
| Korean Office Action dated Apr. 27, 2011 for Korean Patent Application No. KR 10-2009-0111630 which corresponds to the captioned U.S. Appl. No. 12/946,771. |
| Chiu et al., Efficiency enhancement of UV/blue light emitting diodes via nanoscaled epitaxial lateral overgrowth of GaN on a Si02 nanorod-array patterned sapphire substrate, Journal of Crystal Growth, 310, (2008) 5170-5174. |
| Saxena et al., A review on the light extraction techniques in organic electroluminescent devices, Optical Materials, 32, (2009) 221-233. |
| Wang et al., A nano-patterned organic light-emitting diode with high extraction efficiency, Journal of Crystal Growth, 288, (2006) 119-122. |
| Extended European Search Report dated Jan. 20, 2011 for European Patent Application No. EP 10 19 1279.8 related to the captioned application. |
| Nakanishi, Tsutomu et al., “Improvement of the light extraction efficiency of top-emitting organic light-emitting diodes by a two-dimensional diffraction layer fabricated using self-assembled nanoparticles,” Applied Optics, vol. 48, No. 31, Nov. 1, 2009, pp. 5889-5896. |
| Wang, Jinsong et al., “Nanostructure Fabrication using Nanosphere Lithography for Photonics Devices,” Technical Digest CD-ROM/Conference on Lasers and Electro-Optics, Quantum Electronics and Laser Science Conference, Conference on Photonic Applications, Systems and Technologies: Long Beach Convention Center, Long, Beach, CA, USA: CLEO/QELS, May 21, 2006, pp. 1-2. |
| European Examination Report dated Mar. 14, 2013 for European Patent Application No. EP 10 191 279.8 which shares priority of Korean Patent Application No. KR 10-2009-0111630 with captioned U.S. Appl. No. 12/946,771. |
| Number | Date | Country | |
|---|---|---|---|
| 20110114931 A1 | May 2011 | US |