Patent Application
20120085994
The present invention is concerned with organic light-emitting materials and organic light-emitting devices containing such materials.
A typical organic light-emitting device (OLED) comprises a substrate, on which is supported an anode, a cathode and a light-emitting layer situated in between the anode and cathode and comprising at least one organic electroluminescent material. In operation, holes are injected into the device through the anode and electrons are injected into the device through the cathode. The holes and electrons combine in the light-emitting layer to form an exciton which then undergoes radioactive decay to emit light.
Other layers may be present in the OLED, for example a layer of hole injection material, such as poly(ethylene dioxythiophene)/polystyrene sulphonate (PEDOT/PSS), may be provided between the anode and the light-emitting layer to assist injection of holes from the anode to the light-emitting layer. Further, a hole transport layer may be provided between the anode and the light-emitting layer to assist transport of holes to the light-emitting layer.
Electroluminescent polymers such as conjugated polymers are an important class of materials that will be used in organic light emitting devices for the next generation of information technology based consumer products. The principle interest in the use of polymers, as opposed to inorganic semiconducting and organic dye materials, lies in the scope for low-cost device manufacturing, using solution-processing of film-forming materials. A further advantage of electroluminescent polymers is that they may be readily formed by Suzuki or Yamamoto polymerisation. This enables a high degree of control over the regioregulatory of the resultant polymer.
Since the last decade much effort has been devoted to the improvement of the emission efficiency of organic light-emitting devices either by developing highly efficient materials or efficient device structures. In addition, much effort has been devoted to the improvement in lifetime of organic light-emitting devices, again by developing new materials or device structures. A particular problem has been the low lifetime of blue organic light-emissive materials. Some examples of light-emissive materials known in the art are discussed below.
“Synthesis of a segmented conjugated polymer chain giving a blue-shifted electroluminescence and improved efficiency” by P. L. Burn, A. B. Holmes, A. Kraft, D. D. C. Bradley, A. R. Brown and R. H. Friend, J. Chem. Soc., Chem. Commun., 1992, 32 described the preparation of a light-emitting polymer that had conjugated and non-conjugated sequences in the main chain and exhibited blue-green electroluminescence with an emission maximum at 508 nm. Blue light-emission was observed in two conjugated polymers. Poly(p-phenylene) sandwiched between indium-tin oxide and aluminium contacts has been published by G. Grem, G. Leditzky, B. Ullrich and G. Leising in Adv. Mater. 1992, 4, 36. Similarly, Y. Ohmori, M. Uchida, K. Muro and K. Yoshino reported on “Blue electroluminescent diodes utilizing poly(alkylfluorene)” in Jpn. J. Appl. Phys., 1991, 30, L1941.
Applied Physics Letters, Vol. 75, No. 26, 27 Dec. 1999, 4055-4057 “Reduction of molecular aggregation and its application to the high-performance blue perylene-doped organic electroluminescent device” discloses electroluminescent devices made using perylene as a dopant in bis(2-methyl-8-quinolinolato)(para-phenylphenolato) aluminium (III).
J. Am. Chem. Soc., 2003, 125, 437-443 “Attaching Perylene Dyes to Polyfluorene: Three Simple, Efficient Methods for Facile Color Tuning of Light-Emitting Polymers” discloses attachment of perylene dyes to polyfluorene chains either as (i) comonomers in the main chain, (ii) as endcapping groups at the chain termini, or (iii) as pendant side groups.
Polymer (Korea), 2004, 28(5), 367-373 “Electroluminescence characteristics of blue light emitting copolymer containing perylene and triazine moieties in the side chain” discloses blue light emitting copolymers containing perylene and triazine moieties as light emitting and electron transporting units in the polymer side chain.
Chem. Commun., 2005, 2172-2174 “Selective Ir-catalysed borylation of polycyclic aromatic hydrocarbons: structures of naphthalene-2,6-bis(boronate), pyrene-2,7-bis(boronate) and perylene-2,5,8,11-tetra(boronate) esters” discloses the production of pyrene-bis(boronate) and perylene-tetra(boronate) esters to produce conjugated systems and optical materials.
WO 2005/043640 discloses that blending a perylene derivative with an organic light-emissive material in an organic light-emissive device can give a small increase in the lifetime of the device. However, while higher concentrations of perylene derivative give greater improvements in lifetime this results in a significant red-shift in the emission spectrum.
In light of the above, it is apparent that it is known to incorporate polycyclic aromatic hydrocarbons such as perylene derivatives into a light-emissive polymer in order to act as light-emissive units. It is also apparent that it is known to blend perylene derivatives with organic light-emissive material in an organic light-emissive device in order to increase the lifetime of the device but that only small increases in lifetime are observed and at the expense of a significant red-shift in the emission spectrum.
It is an aim of embodiments of the present invention to provide materials which result in a much larger improvement in the lifetime of organic light-emissive devices while not significantly changing their emission spectrum.
The present applicant has surprising found that incorporating large polycyclic aromatic hydrocarbon units, i.e. those with greater than 12 aromatic sp2 hybridized carbon atoms, as non-emissive units in a light-emissive polymer significantly increases the lifetime of the light-emissive polymer without leading to a large change in the emission spectrum of the light-emissive polymer when compared with merely blending such units with a light-emissive polymer.
In light of this finding, and in accordance with a first aspect of the present invention, there is provided an electroluminescent polymer comprising light-emissive repeat units and a non-emissive polycyclic aromatic hydrocarbon unit with greater than 12 aromatic sp2 hybridized carbon atoms. Preferably, the non-emissive polycyclic aromatic hydrocarbon unit has at least 16 aromatic sp2 hybridized carbon atoms, more preferably at least 18 aromatic sp2 hybridized carbon atoms, and most preferably at least 20 aromatic sp2 hybridized carbon atoms. According to certain preferred embodiments, the non-emissive polycyclic aromatic hydrocarbon unit comprises a perylene unit.
There are several possible explanations as to why the incorporation of a large non-emissive polycyclic aromatic hydrocarbon unit into an electroluminescent polymer increases the lifetime of the electroluminescent polymer without significantly changing its emission spectrum. Without being bound by theory, one possible explanation is that the large polycyclic aromatic hydrocarbon unit provides a rigid conjugated system having a large surface area which allows for improved charge transfer along the polymer. This may explain why incorporating the units as non-emissive charge transporting units within an emissive polymer rather them merely mixing the units as a blend with an emissive material provides such an improvement. By incorporating the units into the polymer the large plate-like units can align in a face-to-face orientation to provide good charge transport along the length of the polymer as opposed to being randomly orientated in a blend. Alternatively, or additionally, by incorporating the large non-emissive polycyclic aromatic hydrocarbon unit into an electroluminescent polymer they are more closely associated with the emissive units and thus function more efficiently at transferring charge to the emissive units.
Furthermore, the large polycyclic aromatic hydrocarbon units appear to have a relatively localized band gap such that they have little effect on the conjugation of the rest of the emissive polymer and thus there is negligible change in the colour of emission. There is substantially no emission from the large polycyclic aromatic hydrocarbon units. This can be ensured, for example, by selecting the large polycyclic aromatic hydrocarbon units and the emissive units such that the band gap of the large polycyclic aromatic hydrocarbon units is larger than the band gap of the emissive units.
It has also been verified by the present applicant that the advantageous effects of the present invention are not achieved by incorporating smaller charge transporting units having a similar band gap to that of the large polycyclic aromatic hydrocarbon units of the present invention. This would appear to support the previously described hypothesis that it is the size of the large plate-like units which is responsible for the observed advantageous effects.
The large polycyclic aromatic hydrocarbon units can be incorporated into the main chain of the electroluminescent polymer as a repeat unit and/or into one or more side chains pendant to the polymer main chain and/or as end capping groups of the polymer main chain. It has been surprising found that even if only a small number of large polycyclic aromatic hydrocarbon units are incorporated into the electroluminescent polymer a significant increase in lifetime is observed. Thus the concentration of the large polycyclic aromatic hydrocarbon units in the electroluminescent polymer may be less than 10 mol % of the total moles of repeat units in the polymer, more preferably less than 2 mol %, more preferably still 1 mol % or less and even less than 0.5 mol %. Thus, very small loadings of the large polycyclic aromatic hydrocarbon units (such as in the range 0.001 to 1 mol %) can be used to give significant increases in lifetime without significantly changing the colour of emission.
The emissive units may preferably be selected from any emissive units which have a smaller band gap than the large polycyclic aromatic hydrocarbon units.
Preferably, the electroluminescent polymer further comprises charge transporting repeat units and the band gap of the non-emissive polycyclic aromatic hydrocarbon unit is intermediate in energy between the charge transporting repeat units and the light-emissive repeat units. In this arrangement, the non-emissive polycyclic aromatic hydrocarbon unit can function to transfer charge from the charge transporting repeat units to the light-emissive repeat units. The charge transporting repeat units may comprise hole transporting and/or electron transporting repeat units. The charge transporting repeat units may comprise a fluorene based repeat unit and/or a triaryl amine based repeat unit.
In one embodiment, the electroluminescent polymer is blue-light emitting. As previously mentioned in the background section, the low lifetime of blue light-emitting polymers is a particular problem to which certain embodiments of the present invention are directed.
For the purposes of the present invention, the term “blue-light emitting” means that the photoluminescent light emission has a peak wavelength in the range of from 400 to 500 nm, preferably 430 to 500 nm.
The non-emissive polycyclic aromatic hydrocarbon unit preferably comprises one or more substituents. Examples of substituents include solubilising groups such as C1-20 alkyl or alkoxy; electron withdrawing groups such as fluorine, nitro or cyano; substituents for increasing glass transition temperature (Tg) of the polymer; and aryl groups such as optionally substituted phenyl, unsubstituted phenyl or phenyl substituted with one or more alkyl or alkoxy groups. A preferred substituent is t-butyl.
When suitably positioned, substituents can act to protect the fused aromatic rings of the non-emissive polycyclic aromatic hydrocarbon unit, for example by blocking reactive sites of the non-emissive polycyclic aromatic hydrocarbon unit. They may also serve to prevent aggregation of the material.
Optionally, substituents present on the non-emissive polycyclic aromatic hydrocarbon unit may be linked together, either by a direct bond or by a linking group or linking atom.
The present invention will now be described by way of example only with reference to the following drawings:
A preferred non-emissive polycyclic aromatic hydrocarbon unit has the following formula A:
wherein R1′-R4′ are optional substituents independently selected from the group consisting of alkyl, optionally substituted aryl, alkoxy, thioether and amine. Preferred substituents are alkyl, more preferably branched alkyl; and phenyl, more preferably alkyl-substituted phenyl. The substituents R1′-R4′ may be present in the 2, 5, 8 and 11 positions. At least one of the R-groups must comprise a linkage to the electroluminescent polymer.
When the non-emissive polycyclic aromatic hydrocarbon is covalently bound as a side chain to the backbone of the electroluminescent polymer, it may comprise a structural unit have formula I:
The structural unit shown by formula I may be substituted, for example at any one or more of the positions C2, C5, and C8, as shown below in formula II:
where R1′, R2′, and R3′ each independently represent an optional substituent, as defined above. In one preferred embodiment, all of substituents R1′, R2′, and R3′ are present. R1′, R2′, and R3′ can act to protect the fused rings of the non-emissive polycyclic aromatic hydrocarbon. Preferably, each of R1′, R2′, and R3′ represents t-butyl.
The non-emissive polycyclic aromatic hydrocarbon (PAH) may be connected to the backbone of the electroluminescent polymer via a spacer group, as shown by the repeat unit in formula III:
A spacer group may be conjugated or non-conjugated.
Conjugated spacer groups include phenyl, for example. Non-conjugated spacer groups include alkyl, for example.
The non-emissive polycyclic aromatic hydrocarbon may also be directly linked to the polymer backbone.
The backbone of the electroluminescent polymer may comprise one or more different repeat units.
In one embodiment, it is preferred that the repeat unit in the backbone of the polymer, to which the non-emissive polycyclic aromatic hydrocarbon is bound, comprises a fluorene, more preferably a 9,9 disubstituted fluorene. The fluorene unit provides stability to the repeat unit as a whole.
When the non-emissive polycyclic aromatic hydrocarbon is bound to the electroluminescent polymer, the electroluminescent polymer may comprise a repeat unit having formula IV:
Preferred repeat units having formula IV are shown in formulae V to VIII:
where R1, R1′, R2′, and R3′ are as defined above; R5′ is a spacer group, preferably alkylene, arylene (in particular phenylene), oxygen, nitrogen, sulphur or combinations thereof, in particular arylalkyl; and n is from 1-10. Preferably, R1 represents an optionally substituted C4-C20 alkyl or aryl group.
Referring to the embodiment where the non-emissive polycyclic aromatic hydrocarbon unit is provided as a repeat unit in the backbone of the conjugated polymer, the non-emissive polycyclic aromatic hydrocarbon unit may be directly bound to adjacent repeat units or it may be bound via spacer groups. The non-emissive polycyclic aromatic hydrocarbon unit may be bound through any position, and substituted at any position. Preferred repeat units according to this embodiment include formulae IX and X:
wherein R1′, R2′ and R5′ are as defined above.
Formulae IX and X illustrate linkage of the non-emissive polycyclic aromatic hydrocarbon unit through its 8 and 11 positions, however it will be appreciated that analogous repeat units may be provided wherein the unit is linked through any combination of two of the 2, 5, 8 and 11 positions.
Referring to the embodiment where the non-emissive polycyclic aromatic hydrocarbon unit is covalently bound as end group of the electroluminescent polymer, preferred end groups have formulae XI and XII:
wherein R1′, R2′, R3′ and R5′ are as defined above.
The polymer is preferably a linear polymer, and the non-emissive polycyclic aromatic hydrocarbon end group is present at one or both ends of the polymer chain.
The polymer preferably contains up to 5 mol % of a repeat unit having one of formulae III to X above, more preferably 0.1 to 2 mol %, still more preferably about 0.2-0.5 mol %.
Some examples of suitable polycyclic aromatic hydrocarbon monomers for manufacturing the electroluminescent polymers of the present invention are given below:
Preferred electron transporting repeat units comprise fluorene. The term “fluorene” used herein includes spirofluorene and indenofluorene within its meaning. In order to optimise electron transport, fluorene units are preferably connected in chains of three or more along the polymer backbone, as is known in the art.
A preferred electron transporting repeat unit comprises an optionally substituted 2,7-linked fluorene, most preferably having formula I:
wherein R1 and R2 are independently selected from hydrogen or optionally substituted alkyl, alkoxy, aryl, arylalkyl, heteroaryl and heteroarylalkyl. More preferably, at least one of R1 and R2 comprises an optionally substituted C4-C20 alkyl or aryl group.
Preferred hole transporting repeat units comprise amine, in particular, a triarylamine, preferably having formula 2:
wherein Ar1 and Ar2 are optionally substituted aryl or heteroaryl groups, n is greater than or equal to 1, preferably 1 or 2, and R is H or a substituent, preferably a substituent. R is preferably alkyl or aryl or heteroaryl, most preferably aryl or heteroaryl. Any of the aryl or heteroaryl groups in the unit of formula 2 may be substituted. Preferred substituents include alkyl and alkoxy groups. Any of the aryl or heteroaryl groups in the repeat unit of Formula 2 may be linked by a direct bond or a divalent linking atom or group. Preferred divalent linking atoms and groups include O, S; substituted N; and substituted C.
Particularly preferred units satisfying formula 2 include units of formulae 3 to 5:
wherein Ar1 and Ar2 are as defined above; and Ar3 is optionally substituted aryl or heteroaryl. Where present, preferred substituents for Ar3 include alkyl and alkoxy groups.
A second aspect of the present invention provides a method for making a material as defined in relation to the first aspect of the present invention.
Preferred methods for preparation of the conjugated polymer are Suzuki polymerisation as described in, for example, WO 00/53656 and Yamamoto polymerisation as described in, for example, T. Yamamoto, “Electrically Conducting And Thermally Stable Π-Conjugated Poly(arylene)s Prepared by Organometallic Processes”, Progress in Polymer Science 1993, 17, 1153-1205. These polymerisation techniques both operate via a “metal insertion” wherein the metal atom of a metal complex catalyst is inserted between an aryl group and a leaving group of a monomer. In the case of Yamamoto polymerisation, a nickel complex catalyst is used; in the case of Suzuki polymerisation, a palladium complex catalyst is used.
For example, in the synthesis of a linear polymer by Yamamoto polymerisation, a monomer having two reactive halogen groups is used. Similarly, according to the method of Suzuki polymerisation, at least one reactive group is a boron derivative group such as a boronic acid or boronic ester and the other reactive group is a halogen. Preferred halogens are chlorine, bromine and iodine, most preferably bromine.
It will therefore be appreciated that repeat units and end groups comprising aryl groups as illustrated throughout this application may be derived from a monomer carrying a suitable leaving groups.
Suzuki polymerisation may be used to prepare regioregular, block and random copolymers. In particular, homopolymers or random copolymers may be prepared when one reactive group is a halogen and the other reactive group is a boron derivative group. Alternatively, block or regioregular, in particular AB, copolymers may be prepared when both reactive groups of a first monomer are boron and both reactive groups of a second monomer are halogen.
As alternatives to halides, other leaving groups capable of participating in metal insertion include groups include tosylate, mesylate and triflate.
The second aspect thus provides a method for making a material as defined in relation to the first aspect of the present invention using Suzuki polymerisation or Yamamoto polymerisation whereby monomers are polymerised, each monomer having at least two reactive groups. Preferably, the reactive groups are selected from boron derivative groups such as a boronic acid or boronic ester, halogen, tosylate, mesylate and triflate.
A third aspect of the present invention provides an organic light-emitting device (OLED) containing a material as defined in relation to the first aspect of the present invention. Typically, said material will be comprised in a layer of the device either alone of in combination with one or more other materials. The device may, for example, consist of one or more diodes.
With reference to
In a practical device, at least one of the electrodes is semi-transparent in order that light may be absorbed (in the case of a photoresponsive device) or emitted (in the case of an OLED). Where the anode is transparent, it typically comprises indium tin oxide.
Further layers may be located between anode 2 and cathode 3, such as charge transporting, charge injecting or charge blocking layers.
In particular, it is desirable to provide a conductive hole injection layer, which may be formed from a conductive organic or inorganic material provided between the anode 2 and the electroluminescent layer 3 to assist hole injection from the anode into the layer or layers of semiconducting polymer. Examples of doped organic hole injection materials include doped poly(ethylene dioxythiophene) (PEDT), in particular PEDT doped with a charge-balancing polyacid such as polystyrene sulfonate (PSS) as disclosed in EP 0901176 and EP 0947123, polyacrylic acid or a fluorinated sulfonic acid, for example Nafion®; polyaniline as disclosed in U.S. Pat. No. 5,723,873 and U.S. Pat. No. 5,798,170; and poly(thienothiophene). Examples of conductive inorganic materials include transition metal oxides such as VOx MoOx and RuOx as disclosed in Journal of Physics D: Applied Physics (1996), 29(11), 2750-2753.
If present, a hole transporting layer located between anode 2 and electroluminescent layer 3 preferably has a HOMO level of less than or equal to 5.5 eV, more preferably around 4.8-5.5 eV. HOMO levels may be measured by cyclic voltammetry, for example.
If present, an electron transporting layer located between electroluminescent layer 3 and cathode 4 preferably has a LUMO level of around 3-3.5 eV.
Electroluminescent layer 3 may consist of the light-emitting material alone or may comprise the light-emitting material in combination with one or more further materials. In particular, the light-emitting material may be blended with hole and/or electron transporting materials as disclosed in, for example, WO 99/48160, or may comprise a luminescent dopant in a semiconducting host matrix. Alternatively, the light-emitting material may be covalently bound to a charge transporting material and/or host material.
Cathode 4 is selected from materials that have a workfunction allowing injection of electrons into the electroluminescent layer. Other factors influence the selection of the cathode such as the possibility of adverse interactions between the cathode and the electroluminescent material. The cathode may consist of a single material such as a layer of aluminium. Alternatively, it may comprise a plurality of metals, for example a bilayer of a low workfunction material and a high workfunction material such as calcium and aluminium as disclosed in WO 98/10621; elemental barium as disclosed in WO 98/57381, Appl. Phys. Lett. 2002, 81(4), 634 and WO 02/84759; or a thin layer of metal compound, in particular an oxide or fluoride of an alkali or alkali earth metal, to assist electron injection, for example lithium fluoride as disclosed in WO 00/48258; barium fluoride as disclosed in Appl. Phys. Lett. 2001, 79(5), 2001; and barium oxide. In order to provide efficient injection of electrons into the device, the cathode preferably has a workfunction of less than 3.5 eV, more preferably less than 3.2 eV, most preferably less than 3 eV. Work functions of metals can be found in, for example, Michaelson, J. Appl. Phys. 48(11), 4729, 1977.
The cathode may be opaque or transparent. Transparent cathodes are particularly advantageous for active matrix devices because emission through a transparent anode in such devices is at least partially blocked by drive circuitry located underneath the emissive pixels. A transparent cathode will comprises a layer of an electron injecting material that is sufficiently thin to be transparent. Typically, the lateral conductivity of this layer will be low as a result of its thinness. In this case, the layer of electron injecting material is used in combination with a thicker layer of transparent conducting material such as indium tin oxide.
It will be appreciated that a transparent cathode device need not have a transparent anode (unless, of course, a fully transparent device is desired), and so the transparent anode used for bottom-emitting devices may be replaced or supplemented with a layer of reflective material such as a layer of aluminium. Examples of transparent cathode devices are disclosed in, for example, GB 2348316.
Optical devices tend to be sensitive to moisture and oxygen. Accordingly, the substrate preferably has good barrier properties for prevention of ingress of moisture and oxygen into the device. The substrate is commonly glass, however alternative substrates may be used, in particular where flexibility of the device is desirable. For example, the substrate may comprise a plastic as in U.S. Pat. No. 6,268,695 which discloses a substrate of alternating plastic and barrier layers or a laminate of thin glass and plastic as disclosed in EP 0949850.
The device is preferably encapsulated with an encapsulant (not shown) to prevent ingress of moisture and oxygen. Suitable encapsulants include a sheet of glass, films having suitable barrier properties such as alternating stacks of polymer and dielectric as disclosed in, for example, WO 01/81649 or an airtight container as disclosed in, for example, WO 01/19142. A getter material for absorption of any atmospheric moisture and/or oxygen that may permeate through the substrate or encapsulant may be disposed between the substrate and the encapsulant.
The embodiment of
A fourth aspect of the present invention provides a method of making an OLED as defined in relation to the third aspect. Preferably, the light-emitting material as defined in relation to the first aspect is deposited (optionally in combination with one or more further materials) from solution by solution processing to form a layer of the OLED.
Suitable solvents for polyarylenes, in particular polyfluorenes, include mono- or poly-alkylbenzenes such as toluene and xylene. Particularly preferred solution deposition techniques are spin-coating and inkjet printing.
Spin-coating is particularly suitable for devices wherein patterning of the electroluminescent material is unnecessary—for example for lighting applications or simple monochrome segmented displays.
Inkjet printing is particularly suitable for high information content displays, in particular full colour displays. Inkjet printing of OLEDs is described in, for example, EP 0880303.
Other solution deposition techniques include dip-coating, roll printing and screen printing.
If multiple layers of the OLED are formed by solution processing then the skilled person will be aware of techniques to prevent intermixing of adjacent layers, for example by crosslinking of one layer before deposition of a subsequent layer or selection of materials for adjacent layers such that the material from which the first of these layers is formed is not soluble in the solvent used to deposit the second layer.
A fifth aspect of the present invention provides a light source such as a full colour display comprising a device as defined in relation to the third aspect of the invention.
According to the fifth aspect, electroluminescent layer 3 may be patterned or unpatterned. A device comprising an unpatterned layer may be used an illumination source, for example. A white light emitting device is particularly suitable for this purpose. A device comprising a patterned layer may be, for example, an active matrix display or a passive matrix display. In the case of an active matrix display, a patterned electroluminescent layer is typically used in combination with a patterned anode layer and an unpatterned cathode. In the case of a passive matrix display, the anode layer is formed of parallel stripes of anode material, and parallel stripes of electroluminescent material and cathode material arranged perpendicular to the anode material wherein the stripes of electroluminescent material and cathode material are typically separated by stripes of insulating material (“cathode separators”) formed by photolithography.
Referring to the device according to the third aspect, the following general comments may be made regarding conjugated polymers.
Electroluminescent and/or charge transporting polymers include poly(arylene vinylenes) such as poly(p-phenylene vinylenes) and polyarylenes.
Polymers preferably comprise a first repeat unit selected from arylene repeat units as disclosed in, for example, Adv. Mater. 2000 12(23) 1737-1750 and references therein. Exemplary first repeat units include: 1,4-phenylene repeat units as disclosed in J. Appl. Phys. 1996, 79, 934; fluorene repeat units as disclosed in EP 0842208; indenofluorene repeat units as disclosed in, for example, Macromolecules 2000, 33(6), 2016-2020; and spirofluorene repeat units as disclosed in, for example EP 0707020. Each of these repeat units is optionally substituted. Examples of substituents include solubilising groups such as C1-20 alkyl or alkoxy; electron withdrawing groups such as fluorine, nitro or cyano; and substituents for increasing glass transition temperature (Tg) of the polymer.
Particularly preferred polymers comprise optionally substituted, 2,7-linked fluorenes, most preferably repeat units of formula 6:
wherein R1 and R2 are independently selected from hydrogen or optionally substituted alkyl, alkoxy, aryl, arylalkyl, heteroaryl and heteroarylalkyl. More preferably, at least one of R1 and R2 comprises an optionally substituted C4-C20 alkyl or aryl group.
Polymers may provide one or more of the functions of hole transport, electron transport and emission depending on which layer of the device it is used in and the nature of co-repeat units.
In particular:
wherein Ar1 and Ar2 are optionally substituted aryl or heteroaryl groups, n is greater than or equal to 1, preferably 1 or 2, and R is H or a substituent, preferably a substituent. R is preferably alkyl or aryl or heteroaryl, most preferably aryl or heteroaryl. Any of the aryl or heteroaryl groups in the unit of formula 1 may be substituted. Preferred substituents include alkyl and alkoxy groups. Any of the aryl or heteroaryl groups in the repeat unit of Formula 1 may be linked by a direct bond or a divalent linking atom or group. Preferred divalent linking atoms and groups include O, S; substituted N; and substituted C.
Particularly preferred units satisfying Formula 1 include units of Formulae 8-10:
wherein Ar1 and Ar2 are as defined above; and Ar3 is optionally substituted aryl or heteroaryl. Where present, preferred substituents for Ar3 include alkyl and alkoxy groups.
Particularly preferred hole transporting polymers of this type are copolymers of the first repeat unit and a triarylamine repeat unit.
Electroluminescent copolymers may comprise an electroluminescent region and at least one of a hole transporting region and an electron transporting region as disclosed in, for example, WO 00/55927 and U.S. Pat. No. 6,353,083. If only one of a hole transporting region and electron transporting region is provided then the electroluminescent region may also provide the other of hole transport and electron transport functionality. Alternatively, an electroluminescent polymer may be blended with a hole transporting material and/or an electron transporting material. Polymers comprising one or more of a hole transporting repeat unit, electron transporting repeat unit and emissive repeat unit may provide said units in a polymer main-chain or polymer side-chain.
The different regions within such a polymer may be provided along the polymer backbone, as per U.S. Pat. No. 6,353,083, or as groups pendant from the polymer backbone as per WO 01/62869.
The non-emissive polycyclic aromatic hydrocarbon containing polymers of the invention may be used as host materials for phosphorescent emitters, in which case the emission of the polymer/phosphorescent emitter composition will be shifted to the colour of emission of the phosphorescent material.
Preferred phosphorescent emitters include metal complexes comprising optionally substituted complexes of formula (26):
ML1qL2rL3s 26
wherein M is a metal; each of L1, L2 and L3 is a coordinating group; q is an integer; r and s are each independently 0 or an integer; and the sum of (a. q)+(b. r)+(c.s) is equal to the number of coordination sites available on M, wherein a is the number of coordination sites on L1, b is the number of coordination sites on L2 and c is the number of coordination sites on L3.
Heavy elements M induce strong spin-orbit coupling to allow rapid intersystem crossing and emission from triplet or higher states (phosphorescence). Suitable heavy metals M include:
lanthanide metals such as cerium, samarium, europium, terbium, dysprosium, thulium, erbium and neodymium; and
d-block metals, in particular those in rows 2 and 3 i.e. elements 39 to 48 and 72 to 80, in particular ruthenium, rhodium, palladium, rhenium, osmium, iridium, platinum and gold.
Suitable coordinating groups for the f-block metals include oxygen or nitrogen donor systems such as carboxylic acids, 1,3-diketonates, hydroxy carboxylic acids, Schiff bases including acyl phenols and iminoacyl groups. As is known, luminescent lanthanide metal complexes require sensitizing group(s) which have the triplet excited energy level higher than the first excited state of the metal ion. Emission is from an f-f transition of the metal and so the emission colour is determined by the choice of the metal. The sharp emission is generally narrow, resulting in a pure colour emission useful for display applications.
The d-block metals are particularly suitable for emission from triplet excited states. These metals form organometallic complexes with carbon or nitrogen donors such as porphyrin or bidentate ligands of formula 27:
wherein Ar4 and Ar5 may be the same or different and are independently selected from optionally substituted aryl or heteroaryl; X1 and Y1 may be the same or different and are independently selected from carbon or nitrogen; and Ar4 and Ar5 may be fused together. Ligands wherein X1 is carbon and Y1 is nitrogen are particularly preferred.
Examples of bidentate ligands are illustrated below:
Each of Ar4 and Ar5 may carry one or more substituents. Two or more of these substituents may be linked to form a ring, for example an aromatic ring. Particularly preferred substituents include fluorine or trifluoromethyl which may be used to blue-shift the emission of the complex as disclosed in WO 02/45466, WO 02/44189, US 2002-117662 and US 2002-182441; alkyl or alkoxy groups as disclosed in JP 2002-324679; carbazole which may be used to assist hole transport to the complex when used as an emissive material as disclosed in WO 02/81448; bromine, chlorine or iodine which can serve to functionalise the ligand for attachment of further groups as disclosed in WO 02/68435 and EP 1245659; and dendrons which may be used to obtain or enhance solution processability of the metal complex as disclosed in WO 02/66552.
A light-emitting dendrimer typically comprises a light-emitting core bound to one or more dendrons, wherein each dendron comprises a branching point and two or more dendritic branches. Preferably, the dendron is at least partially conjugated, and at least one of the core and dendritic branches comprises an aryl or heteroaryl group. In one preferred embodiment, the branch group comprises
Other ligands suitable for use with d-block elements include diketonates, in particular acetylacetonate (acac); triarylphosphines and pyridine, each of which may be substituted.
Main group metal complexes show ligand based, or charge transfer emission. For these complexes, the emission colour is determined by the choice of ligand as well as the metal.
The host material and metal complex may be combined in the form of a physical blend. Alternatively, the metal complex may be chemically bound to the host material. In the case of a polymeric host, the metal complex may be chemically bound as a substituent attached to the polymer backbone, incorporated as a repeat unit in the polymer backbone or provided as an end-group of the polymer as disclosed in, for example, EP 1245659, WO 02/31896, WO 03/18653 and WO 03/22908.
A wide range of fluorescent low molecular weight metal complexes are known also and have been demonstrated in organic light emitting devices [see, e.g., Macromol. Sym. 125 (1997) 1-48, U.S. Pat. No. 5,150,006, U.S. Pat. No. 6,083,634 and U.S. Pat. No. 5,432,014]. Again, a polymer comprising non-emissive polycyclic aromatic hydrocarbon units or end group(s) may be used as a host material for such emitters. Suitable ligands for di or trivalent metals include: oxinoids, e.g. with oxygen-nitrogen or oxygen-oxygen donating atoms, generally a ring nitrogen atom with a substituent oxygen atom, or a substituent nitrogen atom or oxygen atom with a substituent oxygen atom such as 8-hydroxyquinolate and hydroxyquinoxalinol-10-hydroxybenzo (h) quinolinato (II), benzazoles (III), schiff bases, azoindoles, chromone derivatives, 3-hydroxyflavone, and carboxylic acids such as salicylato amino carboxylates and ester carboxylates. Optional substituents include halogen, alkyl, alkoxy, haloalkyl, cyano, amino, amido, sulfonyl, carbonyl, aryl or heteroaryl on the (hetero) aromatic rings which may modify the emission colour.
A monomer for forming a main chain perylene repeat unit was prepared according to the scheme below:
An end-capping reactive material for forming an end-capping group of a polymer was prepared according to the scheme below:
A monomer comprising a pendent perylene group was prepared according to the method set out below:
8 eq. HexPh, 2 eq. CF3SO3H, room temp. 45° C., 3 hr
0.2 eq. Sodium 3-mercaptopropan sulfinic acid, 45° C., 6 hr. HexPh removed by distillation. Product precipitated into methanol and recrystallised twice from IPA/toluene.
1.2 eq. 4-F—C6H4NO2, 1.5 eq. K2CO3, DMF, 6 h. Precipitated into water and dried.
3.75 eq. SnCl2, EtOH, reflux, 12 hr. ⅔ EtOH removed and pH raised to 10 with aq. NaOH. Aqueous work up with toluene, precipitated from toluene with 5 vol. eq. hexane.
Dissolved in 6M HCl/MeCN, cool to 0° C. Added 1.05 eq. NaNO2 (aq) dropwise. Stir for 1 hr at 0° C. Added slowly to solution of 2 eq. K2CO3, 2 eq. NEt2H at 0° C. Stirred for 2 hr at 0° C. Warmed to room temp, extracted into CHCl3. Purified by column chromatography.
Excess MeI, 2 eq I2 80° C. 8 hr. Remove MeI under reduced pressure, extract with CHCl3, wash with Na2S2O4. Purify by column chromatography followed by repeated crystallisation from toluene/methanol.
0.2 eq. Pd(PPh3)4, 2.5 eq. Cs2CO3, anhyd. DMF, room temp, 16 h. Purified by column chromatography and repeated recrystallisation from nBuOAc/MeOH.
A polymer comprising emissive units, fluorene units of formula 6, amine repeat units of formula 7, and a main chain polycyclic aromatic hydrocarbon derived from the monomer of Monomer Example 1 was prepared by Suzuki polymerisation as described in WO 00/53656.
A polymer comprising emissive units; fluorene units of formula 6, amine repeat units of formula 7, and a side chain polycyclic aromatic hydrocarbon derived from the monomer of Monomer Example 2 was prepared by Suzuki polymerisation as described in WO 00/53656.
A polymer comprising emissive units, fluorene units of formula 6, amine repeat units of formula 7, and an end capping group derived from the material of Monomer Example 3 was prepared by Suzuki polymerisation as described in WO 00/53656.
For the purpose of comparison, a polymer corresponding to Polymer Example 1 was prepared, except that the large polycyclic aromatic hydrocarbon was replaced by an amine of formula 7.
| Number | Date | Country | Kind |
|---|---|---|---|
| 0906588.9 | Apr 2009 | GB | national |
| Filing Document | Filing Date | Country | Kind | 371c Date |
|---|---|---|---|---|
| PCT/GB2010/000802 | 4/15/2010 | WO | 00 | 12/7/2011 |