Information
-
Patent Application
-
20030008174
-
Publication Number
20030008174
-
Date Filed
April 23, 200222 years ago
-
Date Published
January 09, 200321 years ago
-
CPC
-
US Classifications
-
International Classifications
- B32B009/00
- B32B019/00
- C09K011/06
Abstract
An organic luminescence device is constituted by a pair of an anode and a cathode, and at least one organic layer disposed between the anode and the cathode. The above-mentioned at least one organic layer includes a layer of a fused polynuclear compound represented by the following formula (I):
1
Description
FIELD OF THE INVENTION AND RELATED ART
[0001] The present invention relates to an organic luminescence device using a specific fused polynuclear (or polycyclic) compound, particularly an organic luminescence device wherein an electric field is applied to a film of an organic compound comprising the fused polynuclear compound to cause luminescence.
[0002] An organic luminescence device is a device such that a thin film containing a fluorescent organic compound is sandwiched between an anode and a cathode, and holes and electrons are injected from the anode and the cathode, respectively, into the fluorescent organic compound layer to generate excitons which emit light at the time of being returned to a ground state.
[0003] For example, according to Eastman Kodak's study (“Appl. Phys. Lett.”, 51,913 (1987)), when a voltage of ca. 10 volts is applied to a function separation-type organic luminescence device including two layers of an aluminum quinolinol complex (as electron transport and luminescence material) and a triphenylamine derivative (as hole transport material) disposed between an anode of ITO (indium tin oxide) and a cathode of a magnesium-silver alloy, an emission luminance of ca. 1000 cd/m2 is obtained. Related patents thereof are, e.g., U.S. Pat. Nos. 4,539,507; 4,720,432; and 4,885,211.
[0004] Further, it is possible to effect luminescence ranging from ultraviolet region to infrared region by appropriately changing the species of a fluorescent organic compound used. In recent years, studies on various fluorescent organic compounds have been made extensively as, e.g., described in U.S. Pat. Nos. 5,151,629; 5,409,783; and 5,382,477; and Japanese Laid-Open Patent Application (JP-A) Nos. 2-247278 (corr. to U.S. Pat. Nos. 5,130,603 and 6,093,864); 3-255190 (corr. to U.S. Pat. No. 5,227,252); 5-202356: 9-202878; and9-227576.
[0005] In addition to the above-mentioned organic luminescence devices using low-molecular weight materials, an organic luminescence device using a conjugated system polymer has been reported by a research group of Cambridge University (“Nature”, 347,539 (1990)). According to this report, by forming a single layer of PPV (polyphenylenevinylene) by means of wet coating, luminescence from the layer has been confirmed.
[0006] Related patents as to organic luminescence devices using conjugated system polymers may include: U.S. Pat. Nos. 5,247,190; 5,514,878; and 5,672,678; JP-A 4-145192 (corr. to U.S. Pat. Nos. 5,317,169 and 5,726,457) and JP-A 5-247460.
[0007] As described above, recent progress of the organic luminescence devices is noticeable. More specifically, it is possible to realize a thin and light-weight luminescence device allowing high luminance at low applied voltage, variety of emission wavelength and high-speed responsiveness, thus suggesting possibilities of application to various uses.
[0008] However, the organic luminescence devices are required to exhibit further improved performances such as light output at high luminance and high conversion efficiency. Further, the organic luminescence devices have been accompanied with problems in terms of durability such as a change in luminance with time due to continuous use for a long time, and a deterioration (e.g., an occurrence of dark spots due to leakage of current) by ambient gas containing oxygen or by humidity.
[0009] As fluorescent organic compounds for use in an electron injection layer and/or an electron transport layer, a large number of heterocyclic compounds have been proposed as described in, e.g., JP-A 6-184125, 9-286980 and 9-291274. However, resultant emission luminances and durabilities and luminescence efficiencies have been still insufficient.
SUMMARY OF THE INVENTION
[0010] A principal object of the present invention is to provide an organic luminescence device having solved the above-mentioned problems.
[0011] A specific object of the present invention is to provide an organic luminescence device capable of effecting output of light with very high efficiency and luminance by using a specific fused polynuclear aromatic compound.
[0012] Another object of the present invention is to provide an organic luminescence device having a high durability.
[0013] A further object of the present invention is to provide an organic luminescence device which can be prepared readily and relatively inexpensively.
[0014] According to the present invention, there is provided an organic luminescence device, comprising:
[0015] a pair of an anode and a cathode, and
[0016] at least one organic layer disposed between the anode and the cathode, wherein
[0017] at least one organic layer described above comprises a layer comprising at least one species of a fused polynuclear compound represented by the following formula (I):
2
[0018] wherein R1 to R12 independently denote a hydrogen atom, an alkyl group, a substituted or unsubstituted aralkyl group, a substituted or unsubstituted aryl group, a substituted or unsubstituted heterocyclic group, a substituted amino group, a cyano group or a halogen atom; R1 to R4, R5 to R8 and R9 to R12 being independently capable of including adjacent two groups forming a substituted or unsubstituted aliphatic cyclic structure, a substituted or un-substituted aromatic ring structure, or a substituted or unsubstituted heterocyclic structure, and X1, X2 and X3 independently denote an oxygen atom, a sulfur atom, C(CN)2, C(CF3)2, C(Ar1)Ar2 or N—Ar3, wherein Ar1, Ar2 and Ar3 independently denote a substituted or unsubstituted aryl group or a substituted or unsubstituted heterocyclic group; Ar1 and Ar2 being capable of forming a ring structure.
[0019] In the above formula (I), at least one of X1, X2 and X3 may preferably be C(CN)2. Particularly, X1, X2 and X3 may desirably be C(CN)2 at the same time as shown by the following formula (II):
3
[0020] In another preferred embodiment, X1, X2 and X3 may desirably be O (oxygen atom) at the same time as shown by the following formula (III):
4
[0021] Further, in the present invention, the above-mentioned layer of fused polynuclear compound of the formula (I), preferably formula (II) or (III), may desirably be any one of an electron injection layer, an electron transport layer and a hole blocking layer.
[0022] These and other objects, features and advantages of the present invention will become more apparent upon a consideration of the following description of the preferred embodiments of the present invention taken in conjunction with the accompanying drawings.
BRIEF DESCRIPTION OF THE DRAWINGS
[0023] FIGS. 1 to 6 are respectively a schematic sectional view showing an embodiment of the organic luminescence device according to the present invention.
DESCRIPTION OF THE PREFERRED EMBODIMENTS
[0024] Hereinbelow, the present invention will be described more specifically.
[0025] The organic luminescence device according to the present invention comprises a pair of electrodes composed of an anode and a cathode and at least one organic layer disposed between the pair of electrodes. Examples of such an organic layer may include a luminescence layer, a hole transport layer, an electron transport layer, an electron injection layer and a hole blocking layer.
[0026] In the present invention, the above-mentioned at least one organic layer may preferably have one to six layer structures specifically described hereinafter with reference to FIGS. 1-6.
[0027] In the present invention, at least one organic layer described above may preferably include at least one layer comprising a fused polynuclear compound represented by any one of the above-mentioned formulas (I) to (III).
[0028] Specific examples of R1 to R12 and Ar1 to Ar3 in the formulas (I) to (III) for the fused polynuclear compound used in the present invention will be shown below.
[0029] Examples of alkyl group may include methyl, ethyl, n-propyl, iso-propyl, n-butyl, tert-butyl and octyl.
[0030] Examples of aralkyl group may include benzyl and phenethyl.
[0031] Examples of aryl group may include phenyl, biphenyl, terphenyl, naphthyl, anthryl, phenanthryl, pyrenyl, tetracenyl, pentacenyl and fluorenyl.
[0032] Examples of heterocyclic group may include thienyl, pyrrolyl, pyridyl, quinolyl, carbazolyl, oxazolyl, oxadiazolyl, thiazolyl, thiadiazolyl, terthienyl and terpyrrolyl.
[0033] Examples of substituted amino group may include dimethylamino, diethylamino, dibenzylamino, diphenylamino, ditolylamino and dianisolylamino.
[0034] Examples of aliphatic cyclic structure may include cyclopropane ring and cyclohexane ring.
[0035] Examples of aromatic ring structure and heterocycle structure may include rings comprising those for aryl group and heterocyclic group, respectively.
[0036] Examples of substituents for the above-mentioned groups (or structures) for R1 to R12 and Ar1 to Ar3 may include: alkyl groups such as methyl, ethyl and propyl; aralkyl groups such as benzyl and phenethyl; aryl groups such as phenyl, naphthyl, anthryl, phenanthryl, pyrenyl, tetracenyl, pentacenyl, and fluorenyl; heterocyclic groups such as thienyl, pyrrolyl and pyridyl; amino groups such as dimethylamino, diethylamino, dibenzylamino, diphenylamino, ditolylamino and dianisolylamino; alkoxy groups such as methoxy, ethoxy, propoxy and phenoxy; cyano group; and nitro group.
[0037] Hereinafter, the fused polynuclear compounds of the formulas (I) to (III) used in the present invention will be shown below specifically by their structural formulas (Example Compound Nos. 1 to 35) for the respective formulas (I) to (III) but are not restricted to the following specific compounds.
5
[0038] As apparent from the above fused polynuclear compounds of formulas (I), (II) and (III) (Ex. Comp. Nos. 1 to 35), the fused polynuclear compound used in the present invention may include truxenone (tribenzo[a,f,k]triindenone) (Ex. Comp. No. 1) and its derivatives.
[0039] More specifically, such derivatives of truxenone may include: a compound (Ex. Comp. No. 2) having three carbonyl portions (>C=0) and substituted aryl groups; a compound (Ex. Comp. No. 9) having a substituted one carbonyl portion where oxygen atom is replaced by dicyan methyl group (C(CN)2) (dicyan methylation); a compound (Ex. Comp. No. 11) having substituted three carbonyl portions where each oxygen atom is replaced by sulfur atom; a compound (Ex. Comp. No. 18) having substituted three carbonyl portions where each oxygen atom is replaced by C(CF3)2; a compound (Ex. Comp. No. 19) having substituted three carbonyl portions where each oxygen atom is substituted by C(Ar1)Ar2 (Ar1═Ar2═
6
[0040] and a compound (Ex. Comp. No. 22) having one dicyan methyl group and substituted two carbonyl portions where each oxygen atom is replaced by N—Ar3 (Ar3═
7
[0041] Truxenone (Ex. Comp. No. 1) is a compound having a central benzene ring (six-membered ring) connected to three five-membered rings at three different positions and further connected to three benzene rings via each five-membered ring.
[0042] The fused polynuclear compound used in the present invention may preferably have a chemical structure comprising a central benzene ring, three five-membered rings connected to the central benzene ring, and three six-membered rings each different from benzene ring and connected to the three five-membered rings, respectively, as shown by Ex. Comp. Nos. 1 to 35.
[0043] Further, three five-membered rings each having the carbonyl portion (>C=0) or carbonyl-corresponding portion (>C=) may include one or two rings different from the remaining ring(s) in the carbonyl(-corresponding) portion as in Ex. Comp. Nos. 9 and 22.
[0044] The fused polynuclear compound of formulas (I) to (III) used in the present invention may be synthesized through known processes including those as described in, e.g., “Angew. Chem. Int. Ed. Engl.”, 31, 1101 (1992), “Tetrahedron Lett.”, 38, 1081 (1997) and “Tetrahedron Lett.”, 40, 8625 (1999).
[0045] The first and second articles describe processes of synthesizing toluxenone and the third article describes a process for effecting dicyan methylation of carbonyl portions (>C=0).
[0046] The fused polynuclear compound of the formulas (I) to (III) used in the present invention is an excellent organic luminescence function material in terms of at least one of electron injection performance, electron transfer performance, hole blocking performance and durability, compared with conventional compounds, thus being a material suitable for an organic layer, particularly an electron injection layer, an electron transport layer and/or a hole blocking layer. Further when such an organic layer is formed by vacuum (vapor) deposition or wet coating using an appropriate solvent, the resultant organic layer is less liable to cause crystallization, thus being excellent in stability with time.
[0047] In the present invention, as described above, the organic layer disposed between the pair of electrodes (anode and cathode) may be formed in one or a plurality of organic compound layers including at least one layer thereof comprising the above-mentioned fused polynuclear compound of the formulas (I) to (III). Further, such at least one layer may preferably function as an electron injection layer, an electron transport layer or a hole blocking layer.
[0048] Each of the organic (compound) layers may preferably be formed in a thickness of at most 10 μm, more preferably at most 0.5 μm, most preferably 0.01-0.5 μm.
[0049] Hereinbelow, layer structures of the organic luminescence device according to the present invention will be described specifically with reference to FIGS. 1 to 6 each illustrating a preferred embodiment thereof.
[0050] Referring to FIGS. 1-6 the respective organic luminescence devices basically include a substrate 1, an anode 2 disposed on the substrate 1, one or more organic layer disposed on the anode 2, and a cathode 4 disposed on the one or more organic layer.
[0051] In an embodiment shown in FIG. 1, the organic layer is composed of a single layer exhibiting multifunctional performances in terms of a hole transport ability, an electron transportability and a luminescence performance. These performances may be given by using a single multifunctional compound or by mixing the respective functional materials in a single layer.
[0052] In another embodiment shown in FIG. 2, the organic layer is composed of a hole transport layer 5 disposed on the anode 2 and an electron transport layer 6 disposed on the hole transport layer 5. In this embodiment, a luminescent material also exhibits either one or both of a hole transport performance and an electron transport performance and is used in combination with a hole transport material free from a luminescence performance or an electron transport material free from a luminescence performance. In this embodiment, either one of the hole transport layer 5 and the electron transport layer 6 also functions as in the luminescence layer.
[0053] In another embodiment shown in FIG. 3, the organic layer is composed of three layers consisting of a hole transport layer 5, a luminescence layer 3 and an electron transport layer 6 disposed in this order on the anode 2. In this embodiment, carrier (hole/electron) transport performances and luminescence performance are functionally separated into the three layers which may appropriately be formed by using functional materials exhibiting a hole transport performance, an electron transport performance and a luminescence performance, respectively. As a result, it is possible to allow not only an increased latitude in selection of materials but also use of various compounds different in emission wavelength, thus resulting in a variety of emission hues. Further, it also becomes possible to effectively confining respective carriers or excitons in the luminescence layer 3, thus improving a luminescence efficiency.
[0054]
FIG. 4 shows another embodiment of the organic luminescence device of the present invention. Referring to FIG. 4, the organic luminescence device has four layers as the organic layers including three functional layers similar to those (hole transport layer 5, luminescence layer 3 and electron transport layer 6) shown in FIG. 3 and further an electron injection layer 7 disposed between the cathode 4 and the electron transport layer 6. The use of the electron injection layer 7 is effective in improving adhesive properties between the cathode 4 and the electron transport layer 6 or electron injection performance, thus resulting in luminescence at a low applied voltage.
[0055]
FIGS. 5 and 6 show other embodiments similar to those shown in FIGS. 3 and 4, respectively, except that a hole (or exciton) blocking layer 8 for blocking passing of holes or excitons to the cathode side is disposed between the electron transport layer 6 and the luminescence layer 3. In these embodiments, by using a compound exhibiting a very high ionization potential in the hole blocking layer 8, a resultant luminescence efficiency is effectively improved.
[0056] In the above-mentioned layer structures of organic luminescence device of the present invention, between the cathode 4 and the luminescence layer 3, the electron transport layer 6 or the electron injection layer 7 may generally be disposed in contact with the cathode 4, and the electron transport layer 6 or the hole blocking layer 8 may generally be disposed in contact with the luminescence layer 3. Further, the electron injection layer 7 and the hole blocking layer 8 may generally have a thickness smaller than the electron transport layer 6.
[0057] The layer structure of organic luminescence device of the present invention using the above-mentioned fused polynuclear compound is not restricted to those described above with reference to FIGS. 1-6 illustrating basic device structures of the organic luminescence device of the present invention.
[0058] The fused polynuclear compound used in the present invention (represented by any one of the formulas (I) to (III)) may preferably be used as a material suitable for the electron injection layer, the electron transport layer and/or the luminescence layer but may appropriately be used, as desired, in combination with conventionally known materials, such as hole transport compounds, luminescent compounds and/or electron transport compounds shown below.
[0059] Hole Transport Material
[0060] Hole Transport Material
8
[0061] Electron Transport Luminescence Material
9
[0062] Luminescence Material
10
[0063] Luminescence Layer Matrix (Host) Material and Electron Transport Material
11
[0064] Polymer-Type Hole Transport Material
12
[0065] Polymer-Type Luminescence Material and Charge Transport Material
13
[0066] In the organic luminescence device according to the present invention, a layer of the fused polynuclear compound represented by the formulas (I) to (III) and other layers comprising organic compounds may generally be formed in a thin film by vacuum deposition or wet coating using an appropriate solvent for dissolving such organic compounds (including the fused polynuclear compound). Particularly, in the case of using the wet coating, it is also possible to form a film in combination with an appropriate binder resin.
[0067] The binder resin may appropriately be selected from various known resins. Examples of the binder resin may include: polyvinyl carbazole, polycarbonate resin, polyester resin, polyarylate resin, polystyrene resin, acrylic resin, methacrylic resin, butyral resin, polyvinyl acetal resin, diallyl phthalate resin, phenolic resin, epoxy resin, silicone resin, polysulfone resin and urea resin. These resins may be used singly (as a homopolymer) or in combination of two or more species (as a copolymer).
[0068] The binder resin may preferably be used in an amount of 0.01-20 wt. parts, more preferably 0.1-10 wt. parts, per 1 wt. part of the fused polynuclear compound.
[0069] The anode (electrode) constituting the organic luminescence device of the present invention may desirably be formed of a material having a work function as large as possible. Examples of such a material may include: metals such as gold, platinum, nickel, palladium, cobalt, selenium and vanadium; alloys of those metals; and metal oxides such as tin oxide, zinc oxide, indium tin oxide (ITO) and indium zinc oxide. Further, it is also possible to use electroconductive polymers such as polyaniline, polypyrrole, polythiophene, and polyphenylene sulfide. These materials may be used singly or in mixture.
[0070] On the other hand, the cathode (electrode) may desirably be formed of a material having a work function as small as possible. Examples of such a material may include: metals such as lithium, sodium, potassium, calcium, magnesium, aluminum, indium, silver, lead, tin and chromium; and alloys of these metals. It is also possible to use metal oxides such as ITO. The cathode may be formed in a single layer or plural layers.
[0071] The substrate for the organic luminescence device of the present invention is not particularly limited. Examples of the substrate may include an opaque substrate such as a metal substrate or ceramic substrate, and a transparent substrate such as glass substrate, quartz substrate or plastic sheet. Further, it is also possible to control emitted light by using a color filter film, a fluorescent color conversion film or a dielectric reflection film, in combination with the substrate.
[0072] The organic luminescence device of the present invention may further comprise a protective layer or a sealing layer in order to prevent contact of the organic luminescence device with ambient oxygen or moisture.
[0073] Examples of the protective layer may include: a diamond film, a film of inorganic material such as metal oxide or metal nitride, a film of polymer such as fluorine-containing resin, polyparaxylene, polyethylene, silicone resin or polystyrene, and a film of a photo-curable resin. Further, it is possible to effect packaging of the organic luminescence device per se by covering, e.g., glass substrate, gas-impermeable film or metal film with an appropriate sealing resin.
[0074] Hereinbelow, the present invention will be described more specifically based on Examples but is not restricted to the Examples.
EXAMPLE 1
[0075] An organic luminescence device shown in FIG. 4 was prepared in the following manner.
[0076] On a 0.7 mm-thick glass substrate 1, a 120 nm-thick ITO (indium tin oxide) film (anode 2) was formed by sputtering to prepare a transparent electroconductive support, which was then successively subjected to ultrasonic cleaning with acetone and that with isopropyl alcohol (IPA). The resultant transparent electroconductive support was then subjected to boiling cleaning with IPA and was dried, followed by UV/ozone cleaning.
14
[0077] On the thus-treated transparent electroconductive support, a solution of a hole transport material shown below in chloroform was applied by spin coating to form a 20 nm-thick hole transport layer 5.
[0078] On the hole transport layer 5, a 20 nm-thick luminescence layer 3 of rubrene shown below and Alq3 (aluminum tris-quinolinol) shown below (1:20 by weight) was formed by co-vacuum deposition.
15
[0079] On the luminescence layer 3, a 40 nm-thick electron transport layer 6 of Alq3 was formed by vacuum deposition.
[0080] On the electron transport layer 6, a 10 nm-thick electron injection layer 7 of a fused polynuclear compound (Ex. Comp. No. 1) was formed by vacuum deposition under conditions including a vacuum degree (pressure) of 1.0×10−4 Pa and a deposition rate of 0.2-0.3 nm/sec.
[0081] Then, on the electron injection layer 7, a 150 nm-thick metal electrode (cathode 4) of an aluminum-lithium alloy (Li content: 1 atomic %) was formed by vacuum deposition (1.0×10−4 Pa; 1.0-1.2 nm/sec).
[0082] To the thus-prepared organic luminescence device as shown in FIG. 4, a DC voltage of 4 volts was applied between the ITO electrode (anode 2, positive pole) and the Al-Li electrode (cathode 4, negative pole), whereby a current was passed through the organic luminescence device at a current density of 4.5 mA/cm2 and yellow luminescence was observed at a luminance of 880 cd/m2.
[0083] Then, when the organic luminescence device was supplied with a voltage for 100 hours while keeping a current density of 4.0 mA/cm2 in a nitrogen atmosphere, a luminance of 810 cd/m2 (as initial luminance) was merely decreased to 790 cd/m2 even after 100 hours of the voltage application, thus exhibiting a good durability (less deterioration in luminance). The results are also shown in Table 1 appearing hereinafter.
EXAMPLES 2-15
[0084] Organic luminescence devices were prepared and evaluated in the same manner as in Example 1 except that the fused polynuclear compound (Ex. Comp. No. 1) was changed to those (Ex. Comp. Nos. 4, 8, 10, 13, 16, 18, 20, 23, 24, 26, 28, 32, 34 and 35), respectively.
[0085] The results are shown in Table 1.
COMPARATIVE EXAMPLE 1
[0086] An organic luminescence device was prepared and evaluated in the same manner as in Example 1 except that the electron injection layer 7 was not formed.
[0087] The results are shown in Table 2.
COMPARATIVE EXAMPLES 2-4
[0088] Organic luminescence devices were prepared and evaluated in the same manner as in Example 1 except that the fused polynuclear compound (Ex. Comp. No. 1) was changed to the following comparative compounds Nos. 1-3, respectively.
[0089] The results are shown in Table 2.
[0090] Comparative Compound No. 1
16
[0091] Comparative Compound No. 2
17
[0092] Comparative Compound No. 3
181TABLE 1
|
|
InitialLuminance
Ex.Applied(at 4.0 mA/cm2)
Ex.Comp.voltageLuminanceInitialAfter 100 hr
No.No.(V)(cd/m2)(cd/m2)(cd/m2)
|
114880810790
244840780750
384870800740
4104920870860
51341050990960
61641000980940
7184810760750
8204790730690
9234850820800
10244860800750
11264770730690
12284810770730
13324990950940
143441020950930
15354960920890
|
[0093]
2
TABLE 2
|
|
|
Comp.
Initial
Luminance
|
Comp.
Ex.
Applied
(at 4.0 mA/cm2)
|
Ex.
Comp.
voltage
Luminance
Initial
After 100 hr
|
No.
No.
(V)
(cd/m2)
(cd/m2)
(cd/m2)
|
|
1
None
4
630
590
410
|
2
Comp.1
4
260
240
No
|
luminescence
|
3
Comp.2
4
490
480
40
|
4
Comp.3
4
190
180
No
|
luminescence
|
|
EXAMPLE 16
[0094] An organic luminescence device shown in FIG. 3 was prepared in the following manner.
[0095] In a similar manner as in Example 1, a transparent electroconductive support was prepared.
[0096] On the transparent electroconductive support, a 40 nm-thick hole transport layer 5 of a compound shown below was formed by vacuum deposition.
19
[0097] On the hole transport layer 5, a 20 nm-thick luminescence layer 3 of a compound shown below was formed by vacuum deposition.
20
[0098] On the luminescence layer 3, a 40 nm-thick electron transport layer 6 of a fused polynuclear compound (Ex. Comp. No. 2) was formed by vacuum deposition (1.0×10−4 Pa;0.2-0.3 nm/sec).
[0099] Then, on the electron transport layer 6, a 150 nm-thick metal electrode (cathode 4) of an aluminum-lithium alloy (Li content: 1 atomic %) was formed by vacuum deposition (1.0×10−4 Pa;1.0-1.2 nm/sec).
[0100] To the thus-prepared organic luminescence device as shown in FIG. 3, a DC voltage of 8 volts was applied between the ITO electrode (anode 2, positive pole) and the Al-Li electrode (cathode 4, negative pole), whereby a current was passed through the organic luminescence device at a current density of 7.6 mA/cm2 and blue luminescence was observed at a luminance of 3800 cd/m2.
[0101] Then, when the organic luminescence device was supplied with a voltage for 100 hours while keeping a current density of 7.0 mA/cm2 in a nitrogen atmosphere, a luminance of 3650 cd/m2 (as initial luminance) was merely decreased to 3500 cd/m2 even after 100 hours of the voltage application, thus exhibiting a good durability. The results are shown in Table 3 appearing hereinafter.
EXAMPLES 17-30
[0102] Organic luminescence devices were prepared and evaluated in the same manner as in Example 16 except that the fused polynuclear compound (Ex. Comp. No. 2) was changed to those (Ex. Comp. Nos. 6, 9, 12, 15, 17, 19, 21, 22, 25, 27, 29, 30, 31 and 33), respectively.
[0103] The results are shown in Table 3.
COMPARATIVE EXAMPLES 5-7
[0104] Organic luminescence devices were prepared and evaluated in the same manner as in Example 16 except that the fused polynuclear compound (Ex. Comp. No. 2) was changed to the above-mentioned comparative compounds Nos. 1-3, respectively.
[0105] The results are shown in Table 4.
3TABLE 2
|
|
InitialLuminance
Ex.Applied(at 7.0 mA/cm2)
Ex.Comp.voltageLuminanceInitialAfter 100 hr
No.No.(V)(cd/m2)(cd/m2)(cd/m2)
|
1628380036503500
1768315031002950
1898320031002900
19128460043004150
20158485044504100
21178445044004100
22198290027002450
23218335032003000
24228280025002300
25258305028002550
26278385035003350
27298370035003350
28308430040003850
29318400038003600
30338355034003300
|
[0106]
4
TABLE 4
|
|
|
Comp.
Initial
Luminance
|
Comp.
Ex.
Applied
(at 7.0 mA/cm2)
|
Ex.
Comp.
voltage
Luminance
Initial
After 100 hr
|
No.
No.
(V)
(cd/m2)
(cd/m2)
(cd/m2)
|
|
5
Comp.1
8
350
310
No
|
luminescence
|
6
Comp.2
8
730
670
90
|
7
Comp.3
8
230
220
No
|
luminescence
|
|
Example 31
[0107] An organic luminescence device shown in FIG. 5 was prepared in the following manner.
[0108] On a transparent electroconductive support prepared in the same manner as in Example 1, a 20 nm-thick hole transport layer 5 and a 20 nm-thick luminescence layer 3 were formed in the same manner as in Example 1.
[0109] On the luminescence layer 3, a 10 nm-thick hole blocking layer 8 of a fused polynuclear compound (Ex. Comp. No. 3) was formed by vacuum deposition.
[0110] On the hole blocking layer 8, a 40 nm-thick electron transport layer 6 of Alq3 was formed by vacuum deposition (1.0×10−4 Pa;0.2-0.3 nm/sec).
[0111] Then, on the electron transport layer 6, a 150 nm-thick metal electrode (cathode 4) of an aluminum-lithium alloy (Li content: 1 atomic %) was formed by vacuum deposition (1.0×10−4 Pa;1.0-1.2 nm/sec).
[0112] To the thus-prepared organic luminescence device as shown in FIG. 5, a DC voltage of 8 volts was applied between the ITO electrode (anode 2, positive pole) and the Al-Li electrode (cathode 4, negative pole), whereby a current was passed through the organic luminescence device at a current density 2 of 7.1 mA/cm and yellow luminescence was observed at a luminance of 7500 cd/m2.
[0113] Then, when the organic luminescence device was supplied with a voltage for 100 hours while keeping a current density of 7.0 mA/cm in a nitrogen atmosphere, a luminance of 7300 cd/m2 (as initial luminance) was merely decreased to 6950 cd/m2 even after 100 hours of the voltage application, thus exhibiting a good durability. The results are shown in Table 5 appearing hereinafter.
EXAMPLES 32-35
[0114] Organic luminescence devices were prepared and evaluated in the same manner as in Example 31 except that the fused polynuclear compound (Ex. Comp. No. 3) was changed to compounds (Ex. Comp. Nos. 5, 7, 11 and 14), respectively.
[0115] The results are shown in Table 5.
COMPARATIVE EXAMPLES 8-10
[0116] Organic luminescence devices were prepared and evaluated in the same manner as in Example 31 except that the fused polynuclear compound (Ex. Comp. No. 3) was changed to the above-mentioned comparative compounds Nos. 1-3, respectively.
[0117] The results are shown in Table 5.
5TABLE 5
|
|
InitialLuminance
Ex.Applied(at 7.0 mA/cm2)
Ex.Comp.voltageLuminanceInitialAfter 100 hr
No.No.(V)(cd/m2)(cd/m2)(cd/m2)
|
3138750073006950
3258935090008600
3378810079507300
34118680066006200
35148705069006450
CompComp813501300190
Ex.8No.1
CompComp826002450600
Ex.9No.2
CompComp895090050
Ex.10No.3
|
[0118] As described hereinabove, according to the present invention, by using a fused polynuclear compound of the formula (I) (preferably the formula (II) or (III)) as a material for organic luminescence function layer, particularly for an electron injection layer, an electron transport layer, or a hole blocking layer, disposed in contact with a cathode or a luminescence layer in an organic luminescence device, the resultant organic luminescence device allows a high-luminance luminescence at a lower applied voltage and is also excellent in durability.
[0119] The organic luminescence device of the present invention can be readily prepared by vacuum deposition or wet coating, thus being produced in a large-area device relatively inexpensively.
Claims
- 1. An organic luminescence device, comprising:
a pair of an anode and a cathode, and at least one organic layer disposed between the anode and the cathode, wherein
said at least one organic layer comprises a layer of a fused polynuclear compound represented by the following formula (I): 21wherein R1 to R12 independently denote a hydrogen atom, an alkyl group, a substituted or unsubstituted aralkyl group, a substituted or unsubstituted aryl group, a substituted or unsubstituted heterocyclic group, a substituted amino group, a cyano group or a halogen atom; R1 to R4, R5 to R8 and R9 to R12 being independently capable of including adjacent two groups forming a substituted or unsubstituted aliphatic cyclic structure, a substituted or unsubstituted aromatic ring structure, or a substituted or unsubstituted heterocyclic structure, and X1, X2 and X3 independently denote an oxygen atom, a sulfur atom, C(CN)2, C(CF3)2, C(Ar1)Ar2 or N—Ar3, wherein Ar1, Ar2 and Ar3 independently denote a substituted or unsubstituted aryl group or a substituted or unsubstituted heterocyclic group; Ar1 and Ar2 being capable of forming a ring structure.
- 2. A device according to claim 2, wherein at least one of X1, X2 and X3 in the formula (I) is C(CN)2.
- 3. A device according to claim 1, wherein said fused polynuclear compound of the formula (I) is represented by the following formula (II):
- 4. A device according to claim 1, wherein said fused polynuclear compound of the formula (I) is represented by the following formula (III):
- 5. A device according to claim 1, wherein said at least one organic layer comprises a layer comprising at least one species of said fused polynuclear compound of the formula (I) disposed in contact with the cathode.
- 6. A device according to claim 3, wherein said at least one organic layer comprises a layer comprising at least one species of said fused polynuclear compound of the formula (II) disposed in contact with the cathode.
- 7. A device according to claim 4, wherein said at least one organic layer comprises a layer comprising at least one species of said fused polynuclear compound of the formula (III) disposed in contact with the cathode.
- 8. A device according to claim 1, wherein said at least one organic layer comprises a lulminescence layer and a layer comprising at least one species of said fused polynuclear compound of the formula (I) disposed in contact with the luminescence layer.
- 9. A device according to claim 3, wherein said at least one organic layer comprises a luminescence layer and a layer comprising at least one species of said fused polynuclear compound of the formula (II) disposed in contact with the luminescence layer.
- 10. A device according to claim 4, wherein said at least one organic layer comprises a luminescence layer and a layer comprising at least one species of said fused polynuclear compound of the formula (III) disposed in contact with the luminescence layer
Priority Claims (1)
Number |
Date |
Country |
Kind |
131361/2001(PAT.) |
Apr 2001 |
JP |
|