ORGANIC PROTON-TYPE IONIC LIQUID, TWO-DIMENSIONAL PEROVSKITE PURE-PHASE QUANTUM WELL FILM, PREPARATION METHOD AND USE THEREOF

Abstract

Disclosed are an organic proton-type ionic liquid, a film with a two-dimensional perovskite pure-phase quantum well structure, a preparation method and use thereof. The chemical formula of the organic proton-type alkylamine acetate ionic liquid is RNH3+—RCOO−, where R represents an alkyl group of C4-8 or a phenyl group, preferably, the chemical formula of the organic proton-type alkylamine acetate ionic liquid is CH3(CH2)3NH3+—CH2COO−. The organic proton-type alkylamino acetate ionic liquid disclosed in the present disclosure can be used to prepare perovskite material, the prepared perovskite film thereby can form a pure-phase single quantum well, and the crystal grain size of the film can reach the level of micrometers or even millimeters.

Description

TECHNICAL FIELD

The present disclosure relates to the field of organic and inorganic photoelectronic devices, in particular to an organic proton-type butylamine acetate ionic liquid, a film with a two-dimensional perovskite pure-phase quantum well structure, a preparation method and use thereof.

BACKGROUND

The existing low-dimensional perovskite materials are prepared by using the hydriodate and the hydrobromate of amine compounds as organic amine salts. The low-dimensional perovskite prepared by the existing materials and methods has a multi-phase mixed multi-quantum well structure, and a single pure-phase perovskite quantum well has not been obtained, especially a perovskite film with a higher quantum well width distribution.

SUMMARY

The objective of the present disclosure is to provide an organic proton-type alkylamine acetate ionic liquid, which can be used to prepare perovskite material.

Furthermore, the present disclosure also provides a method for preparing the above organic proton-type alkylamine acetate ionic liquid.

Furthermore, the present disclosure also provides a method for preparing a film with a two-dimensional perovskite pure-phase quantum well structure based on the organic proton-type alkylamine acetate ionic liquid.

Furthermore, the present disclosure also provides a use of the above organic proton-type alkylamine acetate ionic liquid.

The organic proton-type alkylamine acetate ionic liquid can be used as a new solvent for dissolving the perovskite precursor.

The organic proton-type butylamine acetate ionic liquid can be used as a potential electrolyte for lithium ion batteries.

The present disclosure provides an organic proton-type alkylamine acetate ionic liquid, wherein a chemical formula of the organic proton-type alkylamine acetate ionic liquid is RNH₃⁺—RCOO⁻, and R represents an alkyl group of C4-8 or a phenyl group.

In some embodiments, the organic proton-type alkylamine acetate ionic liquid is a butylamine acetate ionic liquid, and the chemical formula of the butylamine acetate ionic liquid is CH₃(CH₂)₃NH₃⁺—CH₂COO⁻.

The present disclosure provides a method for preparing the organic proton-type alkylamine acetate ionic liquid described above, comprising:

• • 1) mixing a carboxyl group-containing organic acid and an amine group-containing organic amine in a molar ratio of the amine group and the carboxyl group of 1:1, then adding the same volume of a diluent as the amine group-containing organic amine, cooling to 0° C. and stirring to react for 2-2.5 h to obtain a mixture; and
  • 2) removing the diluent and other organic impurities from the mixture by reduced pressure distillation at 80° C., then lowering the temperature to −4° C. for recrystallization, standing for 1 h to obtain a solidified mixture, washing the solidified mixture with 1000 mL of a volatile anti-solvent for 3 times, then dissolving the solidified mixture in 100 mL of a diluent, stirring for 30 min, and then removing the diluent by reduced pressure distillation at 80° C. to obtain the organic proton-type alkylamine acetate ionic liquid.

In some embodiments, the carboxyl group-containing organic acid includes one or more of formic acid, acetic acid, propionic acid, butyric acid, pentanoic acid and hexanoic acid;

• • the amino group-containing organic amine is one or more selected from aminomethane, (di)aminoethane, (di)aminopropane, (di)aminobutane, (di)aminopentane and (di)aminohexane;
  • the diluent is one or more selected from water, ethanol, methanol, propanol and isopropanol; and
  • the volatile anti-solvent is an ethers reagent.

In some embodiments, the ethers reagent is diethyl ether.

The present disclosure provides a use of the organic proton-type alkylamine acetate ionic liquid described above in the fields of organic and inorganic photoelectric materials and semiconductor devices.

The present disclosure provides a use of the organic proton-type alkylamine acetate ionic liquid described above in the fields of new solvents for dissolving perovskite precursors and electrolytes for lithium-ion batteries.

The present disclosure provides a two-dimensional perovskite pure-phase quantum well material prepared based on an organic proton-type alkylamine acetate ionic liquid, wherein the chemical formula of the two-dimensional perovskite pure-phase quantum well material is A_aB_bM_mX_x, where A is a long carbon chain organic cation, and a-value ranges from 0 to 2.5;

• • B is an amine group-containing monovalent cation, b-value satisfies 0≤(m−1)<b<(m+1), and m is any natural number; M is a divalent metal cation; and
  • X is one or more of halogen ion, carboxylate ion and thiocyanate ion, and x-value satisfies (3m−1)<x<(3m+1).
  • In some embodiments, the long carbon chain organic cation is one or more of CH₃CH₂NH₃⁺, CH₃CH₂CH₂NH₃⁺, CH₃CH₃CH₂CH₂NH₃⁺, CH₃CH₂CH₂CH₂CH₂NH₃⁺ and CH₃CH₂CH₂CH₂CH₂CH₂NH₃⁺;
  • the amine group-containing monovalent cation is one or more of methylamine ion, formamidine ion, guanidine ion, and cesium ion; the divalent metal cation is one or more of lead ion, tin ion, copper ion, zinc ion, manganese ion and bismuth ion; and
  • the halogen is one or more of F, Cl, Br, and I.

In some embodiments, the chemical formula of the two-dimensional perovskite pure-phase quantum well material is A₂B₂M₃X₁₀.

In some embodiments, the chemical formula of the two-dimensional perovskite pure-phase quantum well material is [CH₃(CH₂)₃NH₃]₂(CH₃NH₃)Pb₂I₇, [CH₃(CH₂)₃NH₃]₂(CH₃NH₃)₂Pb₃I₁₀, [CH₃(CH₂)₃NH₃]₂(CH₃NH₃)₃Pb₄I₁₃ or [CH₃(CH₂)₃NH₃]₂(CH₃NH₃)₄M₅I₁₆.

The present disclosure provides a method for preparing a film with a two-dimensional perovskite pure-phase quantum well structure, comprising:

• • 1) preparing materials in a molar ratio of the organic proton-type alkylamine acetate ionic liquid, BX and MX of 2:(m+1):m;
  • 2) adding BX to a DMSO solution to prepare a DMSO mixture with a BX mass fraction of 1-35%;
  • 3) adding the organic proton-type alkylamine acetate ionic liquid to the DMSO mixture prepared in step 2), mixing evenly, stirring at 25° C. for 2 h, and then adding MX;
  • 4) then adding 1600 μL of DMF reagent, heating to 65° C. and stirring until fully dissolved, and cooling to room temperature to obtain a mixed solution;
  • 5) subjecting the mixed solution prepared in step 4) to spin-coating with heating on the surface of a glass substrate in the air with a humidity of 20%-80%, and maintaining the temperature at 25° C.-250° C. to obtain the two-dimensional perovskite pure-phase quantum well film;
  • where, X is one or more of halogen ion, carboxylate ion and thiocyanate ion;
  • BX is a compound salt of a monovalent cation; and
  • MX is a compound formed by a divalent metal cation and an X ion.

In some embodiments, a compound salt of the monovalent cation is one or more selected from a compound salt of methylamine ion, a compound salt of formamidine ion, a compound salt of guanidine ion and a compound salt of cesium ion.

In some embodiments, an addition amount of the DMF reagent in the step 3) is 5-50 times an addition amount of the organic proton-type alkylamine acetate ionic liquid in volume.

In some embodiments, the spin-coating with heating comprises:

• • heating the glass substrate to 80° C.-100° C., setting a spin-coating speed to 500-1000 rpm/min and performing spin-coating for 5-10 s, then setting a spin-coating speed to 2000-6000 rpm/min and performing spin-coating for 5-10 s, continuously heating the substrate between the two spin-coating steps, covering a film obtained after spin-coating with a petri dish with a diameter of 100 mm, and then subjecting to heat-treatment at 80° C.-120° C. for 5-10 min.

In some embodiments, the method for preparing a film with a two-dimensional perovskite pure-phase quantum well structure comprises:

• • 1) preparing materials in a molar ratio of butylamine acetate ionic liquid, methyl ammonium iodide and lead iodide of 2:4:3;
  • 2) adding methyl ammonium iodide to the DMSO solution to prepare a DMSO mixture with a mass fraction of methyl ammonium iodide of 1-35 wt %;
  • 3) adding butylamine acetic acid ionic liquid to the DMSO mixture prepared in step 2), mixing evenly, stirring at 25° C. for 2 h, and then adding lead iodide powder; then adding a DMF reagent, heating to 65° C., stirring until fully dissolved, and cooling to room temperature to obtain a mixed solution; and
  • 4) subjecting the mixed solution prepared in step 3) to spin-coating with heating on the surface of the glass substrate in the air with a humidity of 20%-80%, and maintaining the temperature at 25° C.-250° C.

Compared with the above background art, the present disclosure has the following advantages:

• • 1) New organic butylamine acetate ionic liquid (BAAc, CH₃(CH₂)₃NH₃+—CH₂COO⁻) is used, which is cheaper and more readily available than traditional halogen chemicals.
  • 2) The prepared perovskite film can form a pure-phase single quantum well, and the crystal grain size of the film can reach a level of micrometers or even millimeters.
  • 3) The carboxyl group-containing organic amine salts can further increase the size and width of the single quantum well.

The low-dimensional perovskite materials prepared in the present disclosure is an ionic liquid molten salt formed based on the carboxylate of an organic amine compound. It is a new type of liquid, stable, inexpensive, and easily available organic amine salt, which can be used as a solvent to directly prepare perovskite materials.

The low-dimensional perovskite prepared by the existing materials and methods has a multi-phase mixed multi-quantum well structure, and the present disclosure provides a pure-phase quantum well structure, which is a major breakthrough in this field. Compared with the low-dimensional perovskite materials prepared by the existing methods and materials, the material in the present disclosure has the advantages of similar or superior photoelectric conversion efficiency, improved stability of the device, low cost, simpler operation, and more suitable for large-area preparation.

The low-dimensional perovskite material prepared by organic amine ionic liquid is more stable and efficient because of the extra hydrogen bonding and van der Waals force, which makes the inorganic layer and organic layer combine more strongly.

The prior art has not yet obtained a single pure-phase perovskite quantum well, especially a perovskite film with a higher quantum well width distribution. The two-dimensional perovskite pure-phase quantum well film prepared by the present disclosure has a purity of the special width quantum well more than 98%.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 shows the appearance of the organic proton-type butylamine acetate ionic liquid.

FIG. 2 is an ultrafast spectroscopic analysis spectrum of the two-dimensional perovskite pure-phase quantum well film prepared in Example 1.

FIG. 3 is an ultrafast spectroscopic analysis spectrum of the two-dimensional perovskite pure-phase quantum well film prepared in Example 2.

FIG. 4 is an ultrafast spectroscopic analysis spectrum of the two-dimensional perovskite pure-phase quantum well film prepared in Example 3.

FIG. 5 is an ultrafast spectroscopic analysis spectrum of the two-dimensional perovskite pure-phase quantum well film prepared in Example 4.

FIG. 6 is an ultrafast spectroscopic analysis spectrum of the two-dimensional perovskite pure-phase quantum well film prepared in Comparative Example 1.

FIG. 7 is an ultrafast spectroscopic analysis spectrum of the two-dimensional perovskite pure-phase quantum well film prepared in Comparative Example 2.

FIG. 8 is an ultrafast spectroscopic analysis spectrum of the two-dimensional perovskite pure-phase quantum well film prepared in Comparative Example 3.

FIG. 9 is a scanning electron micrograph of the two-dimensional perovskite pure-phase quantum well film prepared in Example 1.

FIG. 10 is a scanning electron micrograph of the two-dimensional perovskite pure-phase quantum well film prepared in Comparative Example 1.

FIG. 11 is a nuclear magnetic resonance hydrogen spectrum of the proton-type butylamine acetate ionic liquid.

DETAILED DESCRIPTION

In order to enable those skilled in the art to better understand the technical solutions of the present disclosure, the present disclosure will be further described in detail below with reference to the accompanying drawings and specific embodiments.

Source of Raw Materials.

Except for the organic amine salt ionic liquid, the materials used in the embodiments of the present disclosure are all commercially available, and the purity is higher than 98-99%.

The instruments and equipment used in the present disclosure are as follows:

• • magnetic heating stirrer (1 set), freezing thermostat (1 set), rotary evaporator (1 set), mechanical pump (1 set), heating spin-coater (1 set), spin-coater (2 sets), and glove box (1 set).

Preparation of Organic Proton-Type Butylamine Acetate Ionic Liquid:

• • 1) the acetic acid and 1-aminobutane were mixed in a molar ratio of 1:1, then the same volume of ethanol as 1-aminobutane was added, the temperature was cooled to 0° C. and stirred for 2 h to obtain a mixture; and
  • 2) the ethanol and water were removed from the mixture by reduced pressure distillation at 80° C., then the temperature was lowered to −4° C. for recrystallization, a solidified mixture was obtained after standing for 1 h, the mixture was washed with 1000 mL of diethyl ether for 3 times, then the mixture was dissolved in 100 mL of ethanol, stirred for 30 min, and then the ethanol was removed by reduced pressure distillation at 80° C. to obtain an organic proton-type butylamine acetate ionic liquid (CH₃(CH₂)₃NH₃⁺—CH₂COO⁻).

As shown in the subgraph on the right side of FIG. 1, the organic proton-type butylamine acetate ionic liquid prepared by the present disclosure is a colorless and transparent liquid with good fluidity and special aromatic odor, which is a new type of environmentally friendly and pollution-free organic amine salt for low-dimensional perovskite. The subgraph on the left side of FIG. 1 is a common organic halogen organic amine salt, which is white powder or massive crystal in appearance.

FIG. 11 is a nuclear magnetic resonance hydrogen spectrum of the organic proton-type butylamine acetate ionic liquid, indicating that the product is an ionic product composed of butylamine and acetate.

Example 1

Preparation of Two-Dimensional Perovskite Pure-Phase Quantum Well Film (m-Value is 2, a Narrow Quantum Well Structure with a Broad Band-Gap):

82.94 mg of butylamine acetate ionic liquid CH₃(CH₂)₃NH₃·CH₂COO⁻ was drawn, 148.72 mg of methyl ammonium iodide CH₃NH₃I was weighed, then the two were preferentially mixed in 400 μL of DMSO solution, stirred fully at 25° C. for about 2 h. When the solution was uniform, 287.48 mg of PbI₂ powder was weighed, and then 1600 μL of DMF reagent was drawn to be added in the solution to obtain a mixture, the mixture was continued to heat and stir at 65° C. until it was completely dissolved, and finally cooled to room temperature for use. The mixture was subjected to heating coating in the air with a humidity of 20%-80%, the glass substrate was maintained smooth and tidy during the entire coating process, and the temperature was maintained at 25° C.-250° C. First, the glass substrate was heated to 80-100° C., the spin-coating speed was set to 500-1000 rpm/min, and the spin-coating time was 5-10 s, secondly, the spin-coating speed was set to 2000-6000 rpm/min, the spin-coating time was 5-10 s, the substrate was heated continuously between the two spin-coating steps. The film obtained after spin-coating was covered with a petri dish with a diameter of 100 mm, and then subjected to a heat treatment at 80-120° C. Finally, a flat and smooth two-dimensional perovskite pure-phase quantum well film with micron-level grains was obtained, as shown in FIG. 9, of which the chemical formula is [CH₃(CH₂)₃NH₃]₂(CH₃NH₃)Pb₂I₇. FIG. 10 is a two-dimensional perovskite multiphase quantum well film prepared by butylamine iodine.

Example 2

Preparation of Two-Dimensional Perovskite Pure-Phase Quantum Well Film:

56.78 mg of butylamine acetate ionic liquid CH₃(CH₂)₃NH₃⁺—CH₂COO⁻ was drawn, 135.89 mg of methyl ammonium iodide CH₃NH₃I was weighed, then the two were preferentially mixed in 400 μL of DMSO solution, stirred fully at 25° C. for about 2 h. When the solution was uniform, 295.51 mg of PbI₂ powder was weighed, and then 1600 μL of DMF reagent was drawn to be added in the solution to obtain a mixture, the mixture was continued to heat and stir at 65° C. until it was completely dissolved, and finally cooled to room temperature for use. The mixture was subjected to heating coating in the air with a humidity of 20%-80%, the glass substrate was maintained smooth and tidy during the entire coating process, and the temperature was maintained at 25° C.-250° C. First, the glass substrate was heated to 80-100° C., the spin-coating speed was set to 500-1000 rpm/min, and the spin-coating time was 5-10 s, secondly, the spin-coating speed was set to 2000-6000 rpm/min, the spin-coating time was 5-10 s, the substrate was heated continuously between the two spin-coating steps. The film obtained after spin-coating was covered with a petri dish with a diameter of 100 mm, and then subjected to a heat treatment at 80-120° C. Finally, a flat and smooth two-dimensional perovskite pure-phase quantum well film with micron-level grains was obtained with a chemical formula of [CH₃(CH₂)₃NH₃]₂(CH₃NH₃)₂Pb₃I₁₀.

Example 3

Preparation of Two-Dimensional Perovskite Pure-Phase Quantum Well Film (m-Value is 4, a Broad Quantum Well Structure with a Narrow Band-Gap):

43.18 mg of butylamine acetate ionic liquid CH₃(CH₂)₃NH₃⁺—CH₂COO⁻ was drawn, 129.06 mg of methyl ammonium iodide CH₃NH₃I was weighed, then the two were preferentially mixed in 400 μL of DMSO solution, stirred fully at 25° C. for about 2 h. When the solution was uniform, 299.36 mg of PbI₂ powder was weighed, and then 1600 μL of DMF reagent was drawn to be added in the solution to obtain a mixture, the mixture was continued to heat and stir at 65° C. until it was completely dissolved, and finally cooled to room temperature for use. The mixture was subjected to heating coating in the air with a humidity of 20%-80%, the glass substrate was maintained smooth and tidy during the entire coating process, and the temperature was maintained at 25° C.-250° C. First, the glass substrate was heated to 80-100° C., the spin-coating speed was set to 500-1000 rpm/min, and the spin-coating time was 5-10 s, secondly, the spin-coating speed was set to 2000-6000 rpm/min, the spin-coating time was 5-10 s, the substrate was heated continuously between the two spin-coating steps. The film obtained after spin-coating was covered with a petri dish with a diameter of 100 mm, and then subjected to a heat treatment at 80-120° C. Finally, a flat and smooth two-dimensional perovskite pure-phase quantum well film with micron-level grains was obtained, of which the chemical formula is [CH₃(CH₂)₃NH₃]₂(CH₃NH₃)₃Pb₄I₁₃.

Example 4

Preparation of Two-Dimensional Perovskite Pure-Phase Quantum Well Film (m-Value is 5, a Broad Quantum Well Structure with a Narrow Band-Gap):

34.84 mg of butylamine acetate ionic liquid CH₃(CH₂)₃NH₃⁺—CH₂COO⁻ was drawn, 124.92 mg of methyl ammonium iodide CH₃NH₃I was weighed, then the two were preferentially mixed in 400 μL of DMSO solution, stirred fully at 25° C. for about 2 h. When the solution was uniform, 295.51 mg of PbI₂ powder was weighed, and then 1600 μL of DMF reagent was drawn to be added in the solution to obtain a mixture, the mixture was continued to heat and stir at 65° C. until it was completely dissolved, and finally cooled to room temperature for use. The mixture was subjected to heating coating in the air with a humidity of 20%-80%, the glass substrate was maintained smooth and tidy during the entire coating process, and the temperature was maintained at 25° C.-250° C. First, the glass substrate was heated to 80-100° C., the spin-coating speed was set to 500-1000 rpm/min, and the spin-coating time was 5-10 s, secondly, the spin-coating speed was set to 2000-6000 rpm/min, the spin-coating time was 5-10 s, and the substrate was heated continuously between the two spin-coating steps. The film obtained after spin-coating was covered with a petri dish with a diameter of 100 mm, and then subjected to a heat treatment at 80-120° C. Finally, a flat and smooth two-dimensional perovskite pure-phase quantum well film with micron-level grains was obtained, of which the chemical formula is [CH₃(CH₂)₃NH₃]₂(CH₃NH₃)₄Pb₅I₁₆.

Comparative Example 1

a. The n-butylamine iodide CH₃(CH₂)₃NH₃I, methylamine chloride CH₃NH₃Cl, and lead iodide PbI₂ were dissolved in methylamine acetate in a molar ratio of 2:3:4, and stirred at 60° C. for 1 h-24 h to obtain a precursor solution with a concentration of 200 mg·mL⁻¹; b. The precursor solution was preheated to 50° C.-100° C., and then spin-coated for 10 s-60 s on a heating spin-coater at 60° C.-130° C., and the heating was continued during the whole spin-coating process, and then gradient annealing was performed at 60° C.-100° C. for 3 min-10 min to obtain a mixed multi-quantum well perovskite film with no fixed chemical formula. Its main components include [CH₃(CH₂)₃NH₃]₂(CH₃NH₃)Pb₂I₇, [CH₃(CH₂)₃NH₃]₂(CH₃NH₃)₂Pb₃I₁₀, [CH₃(CH₂)₃NH₃]₂(CH₃NH₃)₃Pb₄I₁₃, [CH₃(CH₂)₃NH₃]₂(CH₃NH₃)₄Pb₅I₁₆ and CH₃NH₃PbI₃.

Comparative Example 2

a. The n-butylamine iodide CH₃(CH₂)₃NH₃I, methylamine chloride CH₃NH₃C1, and lead iodide PbI₂ were dissolved in DMF at the molar ratio of 2:3:4, and stirred at 60° C. for 1 h-24 h to prepare a precursor solution with a concentration of 200 mg·mL⁻¹; b. The precursor solution was preheated to 50° C.-100° C., and then spin-coated for 10 s-60 s on a room-temperature spin-coater at 60° C.-130° C., and then gradient annealing was performed at 60° C.-100° C. for 3 min-10 min to obtain a mixed multi-quantum well perovskite film with no fixed chemical formula. Its main components include [CH₃(CH₂)₃NH₃]₂(CH₃NH₃)Pb₂I₇, [CH₃(CH₂)₃NH₃]₂(CH₃NH₃)₂Pb₃I₁₀, [CH₃(CH₂)₃NH₃]₂(CH₃NH₃)₃Pb₄I₁₃, [CH₃(CH₂)₃NH₃]₂(CH₃NH₃)₄Pb₅I₁₆ and CH₃NH₃PbI₃.

Comparative Example 3

a. The butylamine acetate ionic liquid CH₃(CH₂)₃NH₃⁺·CH₃COO⁻, methylamine chloride CH₃NH₃C1, and lead iodide PbI₂ were dissolved in DMF at the molar ratio of 2:3:4, and stirred at 60° C. for 1 h-24 h to prepare a precursor solution with a concentration of 200 mg·mL⁻¹; b. The precursor solution was preheated to 50° C.-100° C., and then spin-coated for 10 s-60 s on a room-temperature spin-coater at 60° C.-130° C., and then gradient annealing was performed at 60° C.-100° C. for 3 min-10 min to obtain a mixed multi-quantum well perovskite film with no fixed chemical formula. The main components include [CH₃(CH₂)₃NH₃]₂(CH₃NH₃)Pb₂I₇, [CH₃(CH₂)₃NH₃]₂(CH₃NH₃)₂Pb₃I₁₀, [CH₃(CH₂)₃NH₃]₂(CH₃NH₃)₃Pb₄I₁₃, [CH₃(CH₂)₃NH₃]₂(CH₃NH₃)₄Pb₅I₁₆ and CH₃NH₃PbI₃.

The two-dimensional perovskite pure-phase quantum well films prepared in Examples 1, 2, 3, 4 and Comparative Examples 1, 2, and 3 were subjected to ultrafast spectroscopy analysis. The equipment name and test conditions are as follows: ultrafast system HELIOS-TA spectrometer, the laser source is a Coherent Legend regenerative amplifier (150 fs, 1 KHz, 800 nm) injected by a Coherent Vitesse oscillator (100 fs, 80 MHz). Broadband probe pulse (420-780 nm) is generated by focusing a small part (about 10 mj) of a basic 800 nm laser pulse onto a 2 mm sapphire plate to obtain FIG. 2, FIG. 3, FIG. 4, FIG. 5, FIG. 6, FIG. 7 and FIG. 8, respectively.

It can be seen from the figures that the two-dimensional perovskite pure-phase quantum well film prepared in Example 1 has a single perovskite pure-phase quantum well with an n-value of 2, i.e. the distribution width of the quantum well is two lead-iodine octahedrons on average, it is well distributed with no quantum wells with other n values, and the purity is close to 100%. According to the scanning electron micrographs, it can be seen that the grain size of the perovskite film has reached the micron level with a high crystallinity, the film is dense and has no holes, and the surface is smooth and flat.

The two-dimensional perovskite pure-phase quantum well film prepared in Example 2 has a single perovskite pure-phase quantum well with an n value of 3, i.e. the distribution width of the quantum well is three lead-iodine octahedrons on average, it is well distributed with no quantum wells with other n values, and the purity is close to 100%.

The two-dimensional perovskite pure-phase quantum well film prepared in Example 3 has a single perovskite pure-phase quantum well with an n value of 4, i.e. the distribution width of the quantum well is four lead-iodine octahedrons on average, it is well distributed with no quantum wells with other n values, and the purity is more than 98%.

The two-dimensional perovskite pure-phase quantum well film prepared in Example 4 has a single perovskite pure-phase quantum well with an n value of 5, i.e. the distribution width of the quantum well is five lead-iodine octahedrons on average, it is well distributed with no quantum wells with other n values, and the purity is more than 98%.

The two-dimensional perovskite multiphase quantum well film prepared in Comparative Example 1 has a target quantum well width of 4, but a complex multiphase quantum well film is actually obtained, which contains phases with various widths of 2, 3, 4 and infinite three-dimensional perovskite parts, and even impurity phases such as lead iodide. It can be seen from the scanning electron micrographs that the perovskite film has a smaller grain size in the nanometer range, and the crystallinity of the grain is average, the film has a small number of holes and a high surface roughness.

The two-dimensional perovskite multiphase quantum well film prepared in Comparative Example 2 has a target quantum well width of 4, but a complex multiphase quantum well film is actually obtained, which contains phases with various widths of 2, 3, 4 and infinite three-dimensional perovskite parts, even the content of infinity phase is more, and there are still impurity phases such as lead iodide.

The two-dimensional perovskite multiphase quantum well film prepared in Comparative Example 3 has a target quantum well width of 4, but a complex multiphase quantum well film is actually obtained, which contains phases with various widths of 2, 3, 4 and infinite three-dimensional perovskite parts, even the content of infinity phase is more, and there is still a small amount of impurity phases such as lead iodide.

It can be seen that the films prepared in Examples 1-3 are significantly better than the films prepared in Comparative Examples 1 and 2 in terms of crystallinity, grain size, especially the width distribution and purity of quantum wells.

The foregoing description of the disclosed embodiments enables those skilled in the art to implement or use the present disclosure. Various modifications to these embodiments will be obvious to those skilled in the art, and the general principles defined herein can be implemented in other embodiments without departing from the spirit or scope of the present disclosure. Therefore, the present disclosure will not be limited to the embodiments shown in this document, but should conform to the widest scope consistent with the principles and novel features disclosed in this document.

Claims

1. An organic proton-type alkylamine acetate ionic liquid, wherein a chemical formula of the organic proton-type alkylamine acetate ionic liquid is RNH3+—RCOO−, where R represents an alkyl group of C4-8 or a phenyl group.

2. A method for preparing the organic proton-type alkylamine acetate ionic liquid, and the organic proton-type alkylamine acetate ionic liquid is a butylamine acetate ionic liquid, having a chemical formula of H3(CH2)3NH3+—CH2COO−, comprising: 1. mixing a carboxyl group-containing organic acid and an amine group-containing organic amine in a molar ratio of the amine group and the carboxyl group of 1:1, then adding a same volume of a first diluent as the amine group-containing organic amine, cooling to 0° C. and stirring to react for 2-2.5 h to obtain a mixture; and2. removing the first diluent and other organic impurities from the mixture by reduced pressure distillation at 80° C., then lowering the temperature to −4° C. for recrystallization, standing for 1 hour to obtain a solidified mixture, washing the solidified mixture with 1000 mL of a volatile anti-solvent for 3 times, then dissolving the solidified mixture in 100 mL of a second diluent, stirring for 30 min, and then removing the second diluent by reduced pressure distillation at 80° C. to obtain the organic proton-type alkylamine acetate ionic liquid.

3. (canceled)

4. The method according to claim 2, wherein the carboxyl group-containing organic acid comprises one or more of formic acid, acetic acid, propionic acid, butyric acid, pentanoic acid and hexanoic acid; the amine group-containing organic amine is one or more selected from aminomethane, (di)aminoethane, (di)aminopropane, (di)aminobutane, (di)aminopentane and (di)aminohexane;the first diluent is one or more selected from water, ethanol, methanol, propanol and isopropanol; andthe volatile anti-solvent is an ethers reagent.

5. The method according to claim 4, wherein the ethers reagent is diethyl ether.

6. (canceled)

7. (canceled)

8. A two-dimensional perovskite pure-phase quantum well material prepared based on an organic proton-type alkylamine acetate ionic liquid, wherein a chemical formula of the two-dimensional perovskite pure-phase quantum well material is AaBbMmXx, where: A is a long carbon chain organic cation, and a-value ranges from 0 to 2.5;B is an amine group-containing monovalent cation, b-value satisfies 0≤(m−1)<b<(m+1), and m is any natural number;M is a divalent metal cation; andX is one or more of halogen ion, carboxylate ion and thiocyanate ion, and x-value satisfies (3m−1)<x<(3m+1).

9. The two-dimensional perovskite pure-phase quantum well material according to claim 8, wherein: the long carbon chain organic cation is one or more of CH3CH2NH3+, CH3CH2CH2NH3+, CH3CH3CH2CH2NH3+, CH3CH2CH2CH2CH2NH3+ and CH3CH2CH2CH2CH2CH2NH3+;the amine group-containing monovalent cation is one or more of methylamine ion, formamidine ion, guanidine ion, and cesium ion;the divalent metal cation is one or more of lead ion, tin ion, copper ion, zinc ion, manganese ion and bismuth ion; andthe halogen is one or more of F, Cl, Br, and I.

10. The two-dimensional perovskite pure-phase quantum well material according to claim 8, wherein a chemical formula of the two-dimensional perovskite pure-phase quantum well material is A2B2M3X10.

11. The two-dimensional perovskite pure-phase quantum well material according to claim 8, wherein a chemical formula of the two-dimensional perovskite pure-phase quantum well material is [CH3(CH2)3NH3]2(CH3NH3)Pb2I7, [CH3(CH2)3NH3]2(CH3NH3)2Pb3I10, [CH3(CH2)3NH3]2(CH3NH3)3Pb4I13 or [CH3(CH2)3NH3]2(CH3NH3)4Pb5I16.

12. A method for preparing a film with a two-dimensional perovskite pure-phase quantum well structure, comprising: 1. preparing materials in a molar ratio of the organic proton-type alkylamine acetate ionic liquid according to claim 1, BX and MX of 2:(m+1):m;2. adding BX to a DMSO solution to prepare a DMSO mixture with a BX mass fraction of 1-35%;3. adding the organic proton-type alkylamine acetate ionic liquid to the DMSO mixture prepared in step 2), mixing evenly, stirring at 25° C. for 2 h, and then adding MX;4. then adding 1600 μL of a DMF reagent, heating to 65° C. and stirring until fully dissolved, and cooling to room temperature to obtain a mixed solution; and5. subjecting the mixed solution prepared in step 4) to spin-coating with heating on the surface of a glass substrate in the air with a humidity of 20%-80%, and maintaining the temperature at 25° C.-250° C. to obtain the two-dimensional perovskite pure-phase quantum well film;wherein, X is one or more of halogen ion, carboxylate ion and thiocyanate ion;BX is a compound salt of a monovalent cation; andMX is a compound formed by a divalent metal cation and an X ion.

13. The method according to claim 12, wherein the compound salt of the monovalent cation is one or more selected from a compound salt of methylamine ion, a compound salt of formamidine ion, a compound salt of guanidine ion and a compound salt of cesium ion.

14. The method according to claim 12, wherein an addition amount of the DMF reagent in step 3) is 5-50 times an addition amount of the organic proton-type alkylamine acetate ionic liquid in volume.

15. The method according to claim 12, wherein the spin-coating with heating comprises: heating the glass substrate to 80° C.-100° C., setting a spin-coating speed to 500-1000 rpm/min and performing spin-coating for 5-10 s, then setting a spin-coating speed to 2000-6000 rpm/min and performing spin-coating for 5-10 s, continuously heating the substrate between the two spin-coating steps, covering a film obtained after spin-coating with a petri dish with a diameter of 100 mm, and then subjecting to heat-treatment at 80° C.-120° C. for 5-10 min.

16. The method according to claim 12, comprising: 1. preparing materials in a molar ratio of a butylamine acetate ionic liquid, methyl ammonium iodide and lead iodide of 2:4:3;2. adding methyl ammonium iodide to a DMSO solution to prepare a DMSO mixture with a mass fraction of methyl ammonium iodide of 1-35 wt %;3. adding the butylamine acetate ionic liquid to the DMSO mixture prepared in step 2), mixing evenly, stirring at 25° C. for 2 h, and then adding lead iodide powder; then adding a DMF reagent, heating to 65° C., stirring until fully dissolved, and cooling to room temperature to obtain a mixed solution; and4. subjecting the mixed solution prepared in step 3) to spin-coating with heating on the surface of a glass substrate in the air with a humidity of 20%-80%, and maintaining the temperature at 25° C.-250° C.

17. The two-dimensional perovskite pure-phase quantum well material according to claim 11, wherein: the long carbon chain organic cation is one or more of CH3CH2NH3+, CH3CH2CH2NH3+, CH3CH3CH2CH2NH3+, CH3CH2CH2CH2CH2NH3+ and CH3CH2CH2CH2CH2CH2NH3+;the amine group-containing monovalent cation is one or more of methylamine ion, formamidine ion, guanidine ion, and cesium ion;the divalent metal cation is one or more of lead ion, tin ion, copper ion, zinc ion, manganese ion and bismuth ion; andthe halogen is one or more of F, Cl, Br, and I.

18. The method according to claim 12, wherein the ionic liquid is a butylamine acetate ionic liquid, and a chemical formula of the butylamine acetate ionic liquid is CH3(CH2)3NH3+—CH2COO−.