Organic Red Electro-Luminescent Device and Dopant

Description

Summary of Invention

[0019] It was the task of the invention, to make an organic electroluminescent device with improved quantum efficiency and improved long-time stability available and thus to develop new luminescent compounds for the luminescent layer and new doping agents for familiar luminescent compounds, especially for AlQ3. Another objective was to make available new compounds.

[0020] According to the invention, the electroluminescent device consists of at least one hole transport layer and one luminescent layer between two conductive electrodes, wherein at least one electrode is transparent, and it is characterized by the fact that the luminescent layer contains at least one compound of the general formula I as the luminescent compound or as doping agent for a luminescent compound,

wherein B represents an unsaturated carbo-cyclic or hetero-cyclic 4-8-link ring with O, N or S as hetero-atom, wherein in the case of a 6-8-link ring two C-atoms in this ring can be bridged, i.e. they can form a bridge; the D and E - rings are five- or six-link rings, each of which can contain an additional hetero-atom, selected from N, O and S; the radicals R are one or more substituents, which can be the same or different and are hydrogen or straight-chain or branched C1-C6-alkyl; X and Y are carbon or nitrogen; R1, R2 and R9 are the same or different and are hydrogen or straight-chain or branched C1-C6-alkyl or halogen, in particular hydrogen or methyl or fluorine; R3 and R8 are the same or different and are hydrogen, straight-chain or branched C1-C6-alkyl, hydroxy, -OR16, -COOR16, N,N-dialkylamino, acetylamino or halogen, wherein R16 is hydrogen, or straight-chain or branched C1-C6-alkyl, R1 and R2 or R2 and R3 and/or R8 and R9 together can form an alicyclic, heterocyclic or aromatic ring, and A1 and A2, which can be the same or different, are cyan, nitro or -COO R16, wherein R16 takes on the above-mentioned designation.

[0021] A particular embodiment of the invention relates to electroluminescent devices, which contain a compound of the general formula II as doping agent, either alone or in a mixture with other doping agents,

wherein R1, R2, R4 to R7 and R9 are the same or different and are hydrogen, or straight-chain or branched C1-C6-alkyl, R3 and R8 are the same or different and are hydrogen, straight-chain or branched C1-C6-alkyl, hydroxy, -OR16, -COOR16, N,N-dialkylamino, acetylamino or halogen, wherein R16 is hydrogen or straight-chain or branched C1-C6-alkyl, R1 and R2 or R2 and R3 and/or R8 and R9 together can form an alicyclic, heterocyclic or aromatic ring, and B is a five- or six-link unsaturated ring, where in the case of a 6-link ring, two ring atoms in the 1,3-position can form an alicyclic bridge with each other, and the radicals R are one or more substituents, which can be the same or different and are hydrogen or straight-chain or branched C1-C6-alkyl; A1 and A2, which can be the same or different, are cyan, nitro or -COOR16, wherein R16 is hydrogen or straight-chain or branched C1-C6-alkyl.

[0022] Preferred radicals R through R9 in their meaning as low alkyl radicals (C1-C6) are such that represent methyl, isopropyl or tert-butyl, respectively.

[0023] Another preferred design type relates to a device in which a compound of the general formula III or the general formula IV is contained as doping agent,

wherein R10 through R15 are hydrogen, straight-chain or branched C1-C6-alkyl, preferably methyl, and the other radicals which have the above-mentioned significance. R10 and R15 can form an alicyclic bridge, such as e.g. in the dye 2 or 4, as necessary, see Table I further below.

[0024] The organic electroluminescent device, in its simplest case, is made of a multi-layer composite in accordance with Fig. 1, consisting of a metal electrode 1 (cathode), of a luminescent layer 2, which apart from an organic luminescent compound, in particular AlQ3, contains at least one organic doping agent, of a hole transport layer 3, which contains an organic hole transport compound, of a transparent conductive anode 4 as well as of a carrier 5 made of glass or a similar transparent material. In a different set-up of the electroluminescent device, such as e.g. in accordance with Fig. 2, with an additional electron transport layer 6 and, in accordance with Fig. 3, with two hole transport layers 3a and 3b, the properties of this device can be optimized. Another layer is possible, e.g. a thin CuPC layer between the conductive transparent layer 4 and the hole transport layer 3.

[0025] The compound of formula I or of formula II also exists advantageously as adoping agent in a mixture with other doping agents, which can be selected from the group consisting of 2-alkyl-6-N,N-dialkylaminostyryl- or julolidine-substituted 4-dicyanomethylene-4-H-pyrans, corresponding to pyrans substituted with tert-butyl on the pyran ring and 3-(dicyanomethylene)-5,5-dimethyl-1-(4-N,N-dimethylamino-styryl)cyclohexane, in particular with a 1,2- or 1-3-substituted dihydroxycyclobutene-dione dye. The joint usage of several doping agents can occur e.g. through co-vaporization.

[0026] The organic luminescent compound is preferably selected from tris-(8-hydroxyquinolino)-aluminum (AlQ3), derivatives of the 1,3,4-oxadiazol and distyryl-aryl derivatives, wherein (AlQ3) is particularly preferred.

[0027] It has been determined that novel and familiar compounds used recently in electroluminescent devices in a concentration range of >1 percent by weight to 8 percent by weight, preferably >1 to 5 percent by weight, in particular 1.5-3 percent by weight, with respect to the weight of the organic luminescent compound AlQ3, create a very efficient pure red light alone or together with AlQ3 with luminance in the range of 570 to 2100 cd/m2 at 10 to 14V, in particular 580 to 2050 cd/m2 at 10.2 to 13.8V. This occurs without secondary emission of AlQ3 in the range around 530 nm.

[0028] The increased concentration range with doping agents, compared to familiar electroluminescent devices, leads to light of considerably higher quality where the inherent luminescence of the luminescent compound, e.g. AlQ3, does not distort the red color tone.

[0029] Furthermore, the surprising finding was made that the organic electroluminescent device in the case of "under-doping" of a luminescent device, in particular with under-doping of AlQ3, emits white light with the doping agents to be used pursuant to the invention. Under-doping exists when the doping agent is used alone or in a mixture with different doping agents in a concentration between 0.1 percent by weight and 0.8 percent by weight, particularly between 0.1 percent by weight and 0.5 percent by weight, referred to the weight of AlQ3, e.g. by co-vaporizing both.

[0030] Without intermediate ventilation, the metal cathode 1 is finally applied through a vapor deposition process by vaporizing LiF or Li-benzoate and Al, generally at a ratio of 10:1 (0.7 nm Li-benzoate + 100 nm Al). However, other metals, such as silver, magnesium, calcium or indium, or alloys thereof, or different ratios of the metals or alloys, can also be used.

[0031] The object of the invention consists also of new compounds of the general formula I

wherein B is a 4-, 5-, 7- or 8-link unsaturated carbocyclic ring, which is substituted by hydrogen and/or C1-C6-alkyl and, in the case of a 5-link ring carries at least one C1-C6-alkyl radical; or B is possibly a 6-link unsaturated carbocyclic ring, substituted by one or more straight-chain or branched C1-C6-alkyl groups, where two ring atoms in the 1,3-position can form an alicyclic bridge with each other; or B is a 6-link unsaturated carbocyclic ring, which is substituted by one or more C1-C6-alkyl groups; or B is an unsaturated heterocyclic 4- to 8-link ring with O, N or S as hetero-atom, which is substituted by hydrogen and/or one or more C1-C6-alkyl groups; and the rings D and E are five- or six-link rings, each of which can contain one more hetero-atom, selected from N, O and S with the specification that at least one of the two rings contains another hetero-atom; and the radicals R are one or more substituents, which can be the same or different and are hydrogen or straight-chain or branched C1-C6-alkyl; X and Y can be carbon or nitrogen; R1, R2 and R9 are the same or different and are hydrogen or straight-chain or branched C1-C6-alkyl; R3 and R8 are the same or different and are hydrogen, straight-chain or branched C1-C6-alkyl, hydroxy, -OR16, -COOR16, N,N-dialkylamino, acetylamino or halogen, wherein R16 is hydrogen, or straight-chain or branched C1-C6-alkyl, R1 and R2 or R2 and R3 and/or R8 and R9 together can form an alicyclic, heterocyclic or aromatic ring, and A1 and A2, which can be the same or different, are cyan, nitro or -COOR16, wherein R16 is hydrogen, or straight-chain or branched C1-C6-alkyl.

[0032] A specific design of the invention is represented by the compounds of the general formula I, wherein B is a 5-link unsaturated carbocyclic ring and the rings D and E are six-link carbocyclic rings, which are substituted by C1-C6-alkyl groups; or wherein B is a six-link unsaturated carbocyclic ring, which may be substituted by one or more straight-chain or branched C1-C6-alkyl groups, where two ring atoms in the 1,3-position can form an alicyclic bridge with each other with the structure

and the rings D and E are six-link carbocyclic rings, which are substituted by hydrogen and/or C1-C6-alkyl groups, and wherein X and Y represent carbon.

[0033] Preferred radicals R through R9 in the designation of C1-C6-alkyl are methyl, isopropyl or tert-butyl.

[0034] Production of the electroluminescent device generally occurs in such a way that initially the dye to be used as luminescent compound, however the doping agent in particular, is produced by preparing it, for example, from isophoron, verbenon or another cyclic 1-methyl-vinylketone with malonitril and corresponding 9-formyl julolidine while employing a Knoevenagel catalyst in an aprotically dipolar solvent, such as DMF, possibly without separation of intermediate products that form, isolating it, pre-cleaning it through recrystallization and, finally, obtaining it in its purest form through sublimation in a high vacuum. Then, for example, this dye is applied as a luminescent compound or as doping agent of a luminescent compound, possibly in a mixture with additional different doping agents, onto a conductive transparent (ITO) carrier that has been vaporized with one or more hole transport layers or it is applied together with a luminescent substance, preferably with AlQ3, in a high vacuum, e.g. through co-vaporization, onto a conductive transparent (ITO) carrier that has been coated with one or more hole transport layers aromatic ring, and through spin coating.

[0035] The multi-layer composite obtained this way can be equipped with additional layers, if necessary, such as an electron transport layer. Subsequently the metal cathode is applied through vaporization of particularly Li-benzoate and Al.

Brief Description of Drawings

[0036] The drawings depict:

[0037] Fig. 1:simple multi-layer composite of an electroluminescent device

[0038] Fig. 2:multi-layer composite with additional electron transport layer

[0039] Fig. 3:multi-layer composite with additional hole transport layer

[0040] Fig. 4: multi-layer composite with additional hole injection layer.

Detailed Description

[0041] In the drawing, U represents the tension that is applied between the corresponding electrodes.

[0042] Individually, the production proceeds in such a way that in the device that is to be used in accordance with the invention, first the anode is applied onto a stable glass carrier as a transparent conductive layer of indium tin oxide (ITO) at a layer thickness of 10 nm to 200 nm. Just before application of the organic layers, this ITO layer, particularly after an extended storage time, is to be treated in an ultrasound bath first with pure acetone and then with methanol. After blowing off insoluble particles with a jet of vaporizable CO2 ice crystals, the layer is subsequently also treated with oxygen plasma, wherein organic contaminations are burnt and removed.

[0043] Also according to the state of the art, the hole transport layer 3 (HTL) can be prepared with the spin coating technique. The hole transport layer 3 consists e.g. of a molecular dispersion of N,N'-diphenyl-N,N'-bis-(3-methylphenyl)-1,1'-biphenyl-4,4'-diamine (TPD) in poly-(N-vinylcarbazol) (PVK) or a suitable polycarbonate at a weight ratio of 1:1, wherein the ratio of hole transport material to hole-transporting binding agents or also to an insulating binding agent, such as polycarbonate, can vary within a broad range. Initially a clear solution of PVK/TPD is prepared in an organic solvent or solvent mixture, such as e.g. methylene chloride, according to conventional method, while stirring in a solvent container, as well as inert gas at room temperature and, subsequently, the electrically conductive transparent substrate is coated with a spin coating device in such a way that the hole transport layer 3 upon drying at 250C to 400C with inert gas, for example, in a vacuum drying chamber with a dry layer thickness of 50 to 80 nm. It should be mentioned that the hole transport layer 3, according to the state of the art of technology, consisting preferably of N,N'-diphenyl-N,N'-bis-(3-methylphenyl)-1,1'-biphenyl-4,4'-diamine (TPD) or N,N'-biphenyl-N,N'-bis-(1-naphthyl)-benzidine (1-NPB), can also be applied onto the conductive carrier through vacuum metallizing.

[0044] Subsequently, in a high vacuum, a dye pursuant to the invention is applied onto this layer as a luminescent compound either alone or as doping agent, individually or in the form of a mixture with different doping agents, using the co-vaporization technique along with the luminescent compound, e.g. together with AlQ3. The concentration of the doping agent or also of a doping agent mixture, referred to the weight of the luminescent compound AlQ3, can be in the concentration range of 1 percent by weight to 8 percent by weight, preferably 1.5 percent by weight to 3 percent by weight.

[0045] Depending on the application purpose of the electroluminescent device, the concentration of the different doping agent, when using a mixture of doping agents can vary within a broad range, for example, between 0.1 percent by weight and 50 percent by weight, with respect to the overall weight of all doping agents.

[0046] And finally, without intermediate ventilation, the metal cathode 1 is applied through co-vaporization of Mg/Ag, generally at the ratio of 10:1, preferably, however, through vaporization of Li-benzoate and Al (0.7 nm Li-benzoate plus 100 nm Al). However other metals, such as silver, magnesium, calcium or indium, alloys thereof or other ratios of the metals or alloys can also be used.

[0047] Very efficient red electroluminescent devices can also be obtained when, in the luminescent layer 2, the compounds 1 through 6 listed in Table I are used preferably as new doping agents, which have not been known for these purposes until now, either individually or also in a mixture for the doping of AlQ3 (the quantity ratio of equivalent doping agents can be selected freely).

[0048] Very efficient red electroluminescent devices are also obtained when the new doping agents, or also mixtures thereof are co-vaporized with a different doping agent (for example dyes pursuant to US-A-4,769,292), such as with a 1,2- or 1,3-substituted dihydroxycyclobutene-dione dye, are used in the production of the luminescent layer.

[0049] The synthesis procedure for the preparation of the dyes made according to the invention, which have been used in particular as doping agents for luminescent combinations, have been known as such for a long time and was referenced extensively by Lemke (Lemke, R.: Chem. Ber. 103, 1970, 1894-1899; Lemke, R.: DE-A-2,345,189; Lemke, R.: Synthesis 1974, 359-361).

[0050] The starting substances required for the new dyes or doping agents with the structure I or II, such as e.g. the 1-oxajulolidine, in the case of synthesis of the dyes 7, 8, 11, 19, 20 pursuant to Table 1 are produced from 8-hydroxyquinoline, monochlor acetic acid under reduction conditions in THF through sodium boron hydride according to H. Katayama, M. Ohkoshi: Synthesis 1982, 692-693. The synthesis of the corresponding 9-formyl-1-oxajulolidines occurs subsequently according to familiar formylation procedures (Organikum, Organic-Chemical Basic Practicum, 13th Edition, VEB Deutscher Verlag der Wissenschaften Publishing House, Berlin 1974).

[0051] The method for preparing 9-formyl-1,7-dithiojulolidine is also known and has been published in US-A-3,511,831.

[0052] Hetero-bridged 1-methyl-vinyl ketones, such as 5-methyl-2H-pyran-3(6H)-one, are produced according to K. Skinnemoen, K. Undheim: Acta Chemica Scandinavica B 34, 1980, 295-297 in a two-stage process from di-(2-propynyl)-ether through the diacetonyl ether reaction stage and subsequently through intra-molecular ring closure.

[0053] The corresponding 5-methyl-2H-l-thiopyran-3(6H)-one is gained similarly through diacetonyl thioether through intra-molecular ring closure.

[0054] Preferred dyes of the present invention are the compounds listed in the following Table 1. Some of them are dyes, e.g. dye 1, that are already known for non-linear optical applications (NLO) and published in DE 68919989 T2. The generation of very high electric field strengths through the de-localization of electrons in atomic dimensions, for example, as are generally used with lasers, affect non-linear polarization vectors and susceptibility sensors in the hyper-polarized compound, which are taken advantage of in laser radiation of the optical device for the purpose of generating new (higher) frequencies in absorption and reflection (frequency doubling, sum and difference frequencies) and in various effects and applications (Pockels effect, coherent anti-Stokes Raman scattering, two-photon absorption and emission spectroscopy; optical Kerr effect for optical switches and the like).

[0055] However since these NLO applications are primarily about absorption properties and the fluorescent properties are not affected, the usage of these familiar compounds for emission applications such as in organic light-emitting device is not evident.

1TABLE IDye 1

Dye 2

Dye 3

Dye 4

Dye 5

Dye 6

[0056]

2

Dye 7

Dye 8

Dye 9

Dye 10

Dye 11

Dye 12

[0057]

3

Dye 13

Dye 14

Dye 15

Dye 16

Dye 17

Dye 18

[0058]

4

Dye 19

Dye 20

Dye 21

Dye 22

[0059] The following examples serve the purpose of explaining the invention in more detail, however, the invention is not limited to these examples.

[0060]

Example 1
(general synthesis example): For the preparation of the dyes that are to be used pursuant to this invention, 11 mmol of a cyclic 1-methyl-vinyl ketone (isophoron, verbenon, 5-methyl-2H-pyran-3(6h)-one, 5-methyl-2H-thiopyran-3(6H)-one and the like), 0.66 g (10 mmol) malonitril and 0.15 g piperidine in 10 ml dimethylformamide are placed in a 50 ml three-necked flask, equipped with a thermometer and magnetic stirrer, and warmed initially for 1 hour at 250C while stirring. Afterwards, the mixture is heated for another hour at a temperature of 800C. The reaction mixture takes on an increasingly brown color. Now, 10 mmol of the corresponding 9-formyljulolidine e.g. 9-formyl-8-fluor-1,1,7,7-tetramethyljulolidine, 9-formyl-1,7-dithiojulolidine or 9-formyl-1-oxajulolidine, as solid matter or also in solution, are added in several portions to the hot reaction mixture while stirring and it is heated again for 1 hour at 800C. The color of the reaction mixture changes to a deep red violet. The reaction process is observed through thin-layer chromatography (silica gel 60, running agent mixture: 1-butanol/ethanol/acetic acid/water 60/10/5/20). After the respective dye has been formed in the desired quantity, the reaction is stopped. The mixture is allowed to cool down and sit overnight, whereupon the crystallisate is vacuumed off, rinsed several times with methanol, to remove any non-reacted portions of the starting substance, and dried at 600C in a vacuum drying chamber for 8 hours. Dyes that do not crystallize right away are brought to crystallization by adding to the reaction solution a precipitating agent, such as e.g. methanol.

[0061] Cleaning of the dyes generally occurs through re-crystallization, for example from methanol, and subsequent sublimation in a high vacuum.

[0062]

Example 2
On a glass carrier 5 coated with ITO (indium tin oxide) 4 pursuant to Fig. 1 a hole transport layer (HTL) 3 was applied through the spin coating of a solution of N,N'-diphenyl-N,N'-bis-(3-methylphenyl)-benzidine mixed with poly-(N-vinylcarbazol) 1:1 (parts by weight) in dichlormethane. Upon drying the layer under inert gas at a temperature between 250C and 400C, the layer thickness is 50 nm. Then, in a high vacuum (10-5 hPa), the electroluminescence layer 2 is applied through co-vaporization of AlQ3 on the hole transport layer 3 obtained this way and the cleaned dye 1 in a concentration of 1.5 percent by weight, with respect to AlQ3. Subsequently, the metal cathode 1 is applied through the vaporization of LiF and Al (0.7 nm Li-fluoride + 100 nm Al). The procedure for the metal cathode can also occur in a fashion corresponding to example 3.

[0063] For the purpose of measuring the electroluminescence, a controlled tension of between 1 and 20V is applied between the ITO and metal electrodes. The device obtained this way produces a luminance of up to 580 cd/m2 at 12.6V. The emitted light is free from secondary emissions of the AlQ3 in the range around 530 nm and visually exhibits a very pure red color tone.

[0064]

Example 3
On a glass carrier 5 coated with ITO (indium tin oxide) 4, pursuant to Fig. 1 a hole transport layer (HTL) 3 made of N,N'-diphenyl-N,N'-bis-(3-methylphenyl)-benzidine at a layer thickness of 50 nm is applied through vapor deposition in a high vacuum (10-5 hPa). On the hole transport layer 3 obtained this way, the electroluminescence layer 2 is then applied through co-vaporization of AlQ3 and the cleaned dye 1 at a concentration of 2 percent by weight, with respect to AlQ3. The thickness of the applied electroluminescence layer 2 is 60 nm. Subsequently the metal cathode 1 is applied through the vaporization of Li-benzoate and Al (0.7 nm Li-benzoate + 100 nm Al).

[0065] For the purpose of measuring the electroluminescence, a controlled tension between 1 and 20V has been applied between the ITO and metal electrodes. The device obtained this way produces a luminance of up to 600 cd/m2 at 12.8V. The emitted light is free from secondary emissions of the AlQ3 in the range around 530 nm and visually exhibits a very pure red color tone.

[0066]

Example 4
On a glass carrier 5 coated with ITO (indium tin oxide) 4, pursuant to Fig. 2 a hole transport layer (HTL) 3 made of 4,4',4"-tris-(N-(1-naphthyl)-N-phenyl-amino)-triphenylamine at a layer thickness of 55 nm was applied through vapor deposition in a high vacuum (10-5 hPa). On the hole transport layer 3 obtained this way then the luminescent layer 2 is applied through co-vaporization of AlQ3 and the cleaned dye 1 at a concentration of 1.5 percent by weight, referred to AlQ3. The thickness of the applied luminescent layer 2 is 30 nm. Onto this layer, now 10 nm AlQ3 are applied through vapor deposition as the electron transport layer 6. Subsequently the metal cathode 1 is applied through the vaporization of LiF and Al (0.7 nm LiF + 100 nm AL). The procedure for the metal cathode can also occur in a fashion corresponding to example 3.

[0067] For the purpose of measuring the electroluminescence, a controlled tension between 1 and 15V has been applied between the ITO and metal electrodes. The device obtained this way produces a luminance of up to 900 cd/m2 at 14V. The emitted light is free from secondary emissions of the AlQ3 in the range around 530 nm and visually exhibits a very pure red color tone.

[0068]

Example 5
On a glass carrier 5 coated with ITO (indium tin oxide) 4, a 5 nm thick hole injection layer made of CuPC, a hole transport layer (HTL) 3b made of 4,4',4"-tris-(N-(1-naphthyl)-N-phenyl-amino)-triphenylamine at a layer thickness of 55 nm and one additional hole transport layer 3a made of N,N'-biphenyl-N,N'-bis-(1-naphthyl)-benzidine (1-NPB) at a layer thickness of 5 nm are applied through vapor deposition in a high vacuum (10-5 hPa). On the hole transport layers 3a, 3b obtained this way then the luminescent layer 2 is applied through co-vaporization of AlQ3 and the cleaned dye 1 at a concentration of 2 percent by weight, referred to AlQ3. The thickness of the applied luminescent layer 2 is 40 nm. Onto this layer, now 5 nm AlQ3 are applied through vapor deposition as the electron transport layer 6. Subsequently the metal cathode 1 is applied through the vaporization of Li-benzoate and Al (0.7 nm Li-benzoate + 100 nm Al).

[0069] For the purpose of measuring the electroluminescence, a controlled tension between 1 and 15V has been applied between the ITO and metal electrodes. The device obtained this way produces a luminance of up to 2,050 cd/m2 at 14.0V. The emitted light is free from secondary emissions of the AlQ3 in the range around 530 nm and visually exhibits a very pure red color tone.

[0070]

Example 6
Analogous to the layer structure in example 5, the luminescent layer 2 is applied onto the hole transport layers 3a, 3b through co-vaporization of AlQ3 and dye 1, wherein it is used at a concentration of only 0.7 percent by weight (under-doping) referred to AlQ3, then an electroluminescent device is obtained, which emits alternatively white light at a tension of 17V that is applied between the ITO and metal electrodes.

[0071]

Example 7
On a glass carrier 5 coated with ITO (indium-tin-oxide) 4, a 5 nm thick hole injection layer made of CuPC, a hole transport layer (HTL) 3b made of 4,4',4"-tris-(N-(1-naphthyl)-N-phenyl-amino)-triphenylamine at a layer thickness of 55 nm and another hole transport layer 3a made of N,N'-biphenyl-N,N'-bis-(1-naphthyl)-benzidine (1-NPB) at a layer thickness of 5 nm are applied successively through vapor deposition in a high vacuum (10-5 hPa). On the hole transport layers 3a, 3b obtained this way then the luminescent layer 2 is applied through co-vaporization of AlQ3 and the cleaned dye 14 at a concentration of 2.5 percent by weight, with respect to AlQ3. The thickness of the applied luminescent layer 2 is 40 nm. Onto this layer, now 5 nm AlQ3 are applied through vapor deposition as the electron transport layer 6. Subsequently the metal cathode 1 is applied through the vaporization of Li-benzoate and Al (0.7 nm Li-benzoate + 100 nm AL).

[0072] For the purpose of measuring the electroluminescence, a controlled tension between 1 and 15V has been applied between the ITO and metal electrodes. The device obtained this way produces a luminance of up to 2,000 cd/m2 at 13.8V. The emitted light is free from secondary emissions of the AlQ3 in the range around 530 nm and visually exhibits a very pure red color tone.

[0073]

Example 8
If analogue to the layer structure of example 7 the luminescent layer 2 is applied onto the hole transport layers 3a, 3b through co-vaporization of AlQ3 and dye 14, wherein it is used at a concentration of only 0.6 percent by weight (under-doping) referred to AlQ3, then an electroluminescent device is obtained, which emits alternatively white light at a tension of 17V that is applied between the ITO and metal electrodes.

Claims

1. Electroluminescent device, consisting of a hole transport layer and a luminescent layer between two conductive electrodes, wherein at least one electrode is transparent, is characterized by the fact that the luminescent layer contains at least one compound of the general formula I as the luminescent compound or a doping agent for a luminescent compound 30
2. Electroluminescent device pursuant to claim 1, is characterized by the fact that it contains a compound of the general formula II as doping agent for electroluminescent compounds, 31
3. Electroluminescent device pursuant to claim 1, characterized by the fact that the radicals R through R9 in their meaning as C1-C6-alkyl represent methyl, isopropyl or tert-butyl.
4. Electroluminescent device pursuant to claim 1, is characterized by the fact that the compound of formula I exists as doping agent in a mixture with other doping agents, which can be selected from the group consisting of 2-alkyl-6-N,N-dialkylaminostyryl- or julolidine-substituted 4-dicyanomethylene-4-H-pyrans, corresponding to pyrans substituted with tert-butyl on the pyran ring and 3-(dixyanomethylene)-5,5-dimethyl-1-(4-N,N-dimethylamino-styryl)cyclohexane, in particular with a 1,2- or 1-3-substituted dihydroxycyclobutene-dione dye.
5. Electroluminescent device pursuant to claim 1, is characterized by the fact that the organic luminescent compound is selected from tris-(8-hydroxyquinolino)-aluminum (AlQ3), derivatives of the 1,3,4-oxadiazol and distyryl-aryl derivatives.
6. Electroluminescent device pursuant to claim 1, is characterized by the fact that the concentration of the doping agent of formula I is in the range of >1 percent by weight to 8 percent by weight, preferably in the range of 1.5 to 3 percent by weight, with respect to the weight of the luminescent compound AlQ3.
7. Electroluminescent device pursuant to claim 6, is characterized by the fact that together with AlQ3 it creates pure red light emission.
8. Electroluminescent device pursuant to claim 7, is characterized by the fact that it has a luminance in the range of 580-2,050 cd/m2 at 10-12V and emits red light without secondary emission of AlQ3 at 530 nm.
9. Electroluminescent device pursuant to claim 1, is characterized by the fact that the concentration of the doping agents is in the range of 0.1 to 1 percent by weight,
10. Compounds of the general formula I 32
11. Compounds of the general formula I pursuant to claim 10, wherein B is a six-link unsaturated carbocyclic ring, possibly substituted by one or more straight-chain or branched C1-C6-alkyl groups, where two ring atoms in the 1,3-position can form an alicyclic bridge with each other 33
12. Compound pursuant to claim 10, characterized by the fact that the radicals R through R9 in their meaning as C1-C6-alkyl represent methyl, isopropyl or tert-butyl.
13. Compounds pursuant to the general formula V, 34 wherein R1, R2 and R9 are the same or different and are hydrogen or halogen or straight-chain or branched C1-C6-alkyl;
14. Compounds pursuant to claim 13 of the general formula VI 35 wherein R3 and R8 can be the same or different and are hydrogen or halogen; and
15. Compounds of the general formula VII 36 wherein B is an unsaturated carbocyclic or heterocyclic 4-8-link ring with O, N or S as hetero-atom, wherein in the case of a 6-8-link ring two C-atoms can form a bridge with each other;
16. Compounds pursuant to claim 15, wherein R1, R2 and R9 can be the same or different and are hydrogen or methyl;
17. Compounds pursuant to claim 15 of the general formula VIII 37 R1, R2 and R9 are the same or different and are hydrogen or methyl;
18. Compounds pursuant to claim 16, wherein R1, R2 and R9 are hydrogen;
19. Compounds pursuant to claim 17 of the general formula IX 38 wherein R4, R5, R6 and R7 are the same and are hydrogen or methyl; and
20. Compound of the general formula X 39

Organic Red Electro-Luminescent Device and Dopant

Information

Publication Number

Date Filed

Date Published

Inventors

Original Assignees

CPC

US Classifications

International Classifications

Abstract

Description

Claims