Patent Application
20070003463
1. Field of the Invention
The present invention relates to organically modified fine particles having hydrocarbon strongly bound to the surface of fine particles, particularly, organically modified metal oxide fine particles, a process for producing the same, and further a recovery or collection method of fine particles such as nanoparticles, and applied techniques thereof.
2. Description of the Related Art
Fine particles, particularly, particles of nanometer size (nanoparticles) are expected to realize a technology satisfying requests of a higher precision, a smaller size and a lighter weight than in the current condition for all materials and products because of a variety of unique excellent properties, characteristics and functions thereof. Therefore, nanoparticles are attracting attentions as a material enabling the higher function, higher performance, higher density, and higher preciseness of industrial materials, pharmaceutical and cosmetic materials and the like such as ceramic nano-structure modified material, optical functional coating material, electromagnetic shielding material, secondary battery material, fluorescent material, electronic part material, magnetic recording material, and abrasive material, and also as a 21st century material. There is a lot of attention from the industrial world being given thereto, because a series of discoveries such as onset of extra-high functionalities or new physical properties by the quantum size effect of the nanoparticles, and syntheses of new materials have been made in the recent basic researches for the nanoparticles. However, practical application of the nanoparticles requires addition of unique functions to the respective fine particles, and to that end, establishment of a technique for modifying the surface of particles is desired for enabling the addition of the functions. Organic modification is convenient for adding stably usable and applicable functions to fine particles, particularly nanoparticles, and a modification through strong bond is particularly demanded.
Many reports for organic/inorganic composite materials and syntheses thereof have been disclosed up to now, and researches for organic modification of inorganic particles have been also made, each of which intended to carry out a reaction in an organic solvent for the organic modification. A technique for reacting an organic material with fine particles in a reaction field or water while synthesizing the particles in water or an aqueous solution is not known. For the surface modification of particles, many techniques for modifying the surface of inorganic particles in an organic solvent are known. However, particles of nano-size are easy to coagulate, and a pretreatment such as use of a surface active agent is particularly needed for dispersing the particles synthesized in water to an organic solvent. As mentioned above, no report has been made for the technique for modifying the surface of particles while synthesizing the particles in water.
As a method for in-situ surface modification, reversed micelle method, hot soap method, and the like have been reported. In the reversed micelle method, water is suspended to an oil phase by use of a surface active agent to generate a reversed micelle, and a reactive substrate is added thereto to reactively crystallize it. The metal oxide particles generated in the suspended water phase are stabilized by the surface active agent to stably disperse nanoparticles, in which the surface active agent is in a state adsorbed by the particle surface without a linkage by reaction. In the hot soap method, the above method is performed at high temperature by use of only the surface active agent without oil phase. This method is a technique using the effect that an aqueous solution of metal salt to be reacted is rapidly supplied with stirring and reactively crystallized, while the circumferential surface active agent is adsorbed thereto. The cases reported up to now for the organic modification involve adsorption of alkanethiol, but not reactive modification.
There are frequently reported that high-temperature, high-pressure water forms a homogeneous phase also with an organic material, and water functions as an acid or basic catalyst in a high-temperature, high-pressure field to progress an organic synthetic reaction even under no catalyst. However, no method for a reaction between an inorganic material and an organic material is reported.
It is known that highly crystalline particles of nano-size can be synthesized by adapting supercritical water as a reaction field for hydrothermal synthesis. However, there is no report for modification of the surface of the produced nanoparticles in this reaction field, or synthesis of organically modified particles by a reaction with an organic material.
A technique for performing an in-situ surface modification simultaneously with CVD in a supercritical fluid is also known, in which alkanethiol or alcohol is made coexist in a reaction field for synthesizing metal nanoparticles by CVD in the supercritical fluid, taking reference to the above-mentioned hot soap method or the like. It is reported that the growth of particles can be inhibited to generate particles of nanometer according to this technique. For the CVD technique, it is reported that the reduction reaction and surface modification by alkanethiol simultaneously occur, and the resulting product is metal Cu having an alkanethiol-coordinated structure. It is also reported to produce nanoparticles by performing the synthesis in the presence of alkanethiol similarly to the above by use of a reducing agent in supercritical water, thereby coordinating the thiol group with metal nanoparticles to inhibit the growth of particles. In case of the alcohol, it is shown in a part of the result that not only orientation but also linkage was caused to perform in-situ surface modification in the reaction filed. However, this is caused not by the reactive crystallization in supercritical “water”, but by only a technique belonging to reactive in-situ surface reforming method in an organic solvent.
A surface treatment of glass or silica gel in water is well known, but this method is based on CNBr activation or epoxy activation. Since each of the CNBr method and the epoxy activation method is carried out in an alkaline solution, particles of about nanometer (nm) are entirely dissolved. Therefore, these known reactions cannot be used for the surface modification of oxide nanoparticles in water.
Conventional organic modification methods will be collectively described.
1) Synthesis of Organic-Inorganic Composite Material
Silane coupling is given as a general method for modifying a metal oxide surface. (Polymer Frontier 21 Series 15 “Inorganic/Polymer Nano Interface Control”, edited by Society of Polymer Science, pp. 3-23, NTS, 2003). There are researches for syntheses of organic/inorganic composite materials [“Formation of Ordered Monolayer of Anionic Silica Particles on a Cationic Molecular Layer”, T. Yonezawa, S. Onoue, and T. Kunitake, Chem. Lett., No. 7, 689-690 (1998); Molecular Imprinting of Azobenzene Carboxylic Acid on a TiO2 Ultrathin Film by the Surface Sol-Gel Process”, S.-W. Lee, I. Ichinose, T. Kunitake, Langmuir, Vol. 14, 2857-2863 (1998); “Alternate Molecular Layers of Metal Oxides and Hydroxyl Polymers Prepared by the Surface Sol-Gel Process”, I. Ichinose, T. Kawakami, T. Kunitake, Adv. Mater., Vol. 10, 535-539 (1998); and “Molecular Imprinting of Protected Amino Acids in Ultrathin Multilayers of TiO2 Gel”, S. W. Lee, I. Ichinose, T. Kunitake, Chem. Lett., No. 12, 1993-1994 (1998)]. Surface modifications of oxides in water are also known. Techniques for surface-modifying glass or silica gel in water include CNBr activation or epoxy activation, in which CNBr or epoxy is reacted with OH on the surface to give the functional group of the CN or epoxy, and an intended functional group is introduced through it. However, such a reaction requires setting of pH and addition of a catalyst, and involves generation of an acid as a product. Since these activations are carried out in an alkaline solution, all particles of about nm are dissolved, and it is therefore impossible to perform the surface modification of oxide nanoparticles in water by use of these known reactions (Rolf Axen, Jerker Porath, Sverker Embvack, “Chemica Coupling of Peptides and Proteins to Polysaccharides by Means of Cyanogen Halides”, Nature, Vol. 214, 1967, pp. 1302-1304). In every method described above, the organic modification depends on a reaction in an organic solvent. Particles of nano-size are easy to coagulate because of high surface energy. A solution method such as sol-gel process or hydrothermal process is effective, as shown in
2) Technique for Performing In-Situ Surface Modification
Reversed Micelle Method
Water is suspended in an oil phase by use of a surface active agent to form a reversed micelle, and a reactive substrate is added thereto to reactively crystallize it. For example, CdS nanoparticles and NaNO3 can be generated by mixing an aqueous solution of Cd(NO3)2 with micelle of Na2S. The CdS nanoparticles can be stabilized by supplying a stabilizing agent such as alkanethiol. The surface active agent is in a state adsorbed to the surface without a linkage by reaction (A) New Technology for Production, Evaluation, Application and Equipment of Nanoparticles”, pp. 16-19, 2002, published by CMC). Recently, a method using supercritical carbon dioxide as solvent has been also reported (Ye, X. R., Lin, Y. Wang, C., Wai, C. M., Adv. Materials, 2003, 15, 316; and Ye, X. R., Lin, Y Wang, C., Wai, C. M., Chem. Comm., 2003, 642).
Hot Soap Method
The above-mentioned method is carried out at high temperature by use of only a surface active agent without oil phase. An aqueous solution of metal salt to be reacted is rapidly supplied with stirring and reactively crystallized, while the circumferential surface active agent is adsorbed thereto (A) “New Technology for Production, Evaluation, Application and Equipment of Nanoparticles”, pp. 19-21, 2002, published by CMC). Most of the cases reported up to now are based on adsorption of alkanethiol, and no reactive modification has been practiced.
In-Situ Surface Modification in Supercritical Fluid by Reactive Crystallization
A method for performing an organic modification simultaneously with thermal decomposition CVD (chemical vapor deposition) in a supercritical fluid is also proposed. Particularly, an article for a surface modification performed in coexistence of alkanethiol in a supercritical hydrothermal synthesis (Technoarch's Patent) field is disclosed. When the coexistence of hexane thiol with an aqueous solution of Cu(NO3)2 laid in a supercritical state results in synthesis of Cu particles by reduction and stabilization thereof by hexane thiol in situ. In this case, the thiol acts as a reducing agent to coordinate the hexane thiol with the surface of the generated Cu nanoparticles. This is a well-known coordination with metal (Kirk J. Ziegler, R. Christopher Doty, Keith P. Johnston, and Brian A. Korgel, “Synthesis of Organic Monolayer-Stabilized Copper Nanocrystals in Supercritical Water”, J. Am. Chem. Soc., 2001, 123, 7797-7803). Surface modification of SiO2 with alcohol with synthesis thereof is also known (the same reference as above Kirk J. Ziegler, R. Christopher Doty, Keith P. Jonston, and Brian A. Korgel, “Synthesis of Organic Monolayer-Stabilized Copper Nanocrystals in Supercritical Water”, J. Am. Chem. Soc., 2001, 123, 7797-7803).
The present inventors have proposed a nanoparticle synthesis in supercritical water for synthesizing highly crystalline particles of nano-size by adapting supercritical water as a reaction field for hydrothermal synthesis, but not referred to a process for modification of the surface of the produced particles or synthesis of organically modified particles by a reaction with an organic matter. There are frequently reported that high-temperature, high-pressure water forms a homogenous phase also with an organic material and that water functions as an acid or basic catalyst to progress an organic synthetic reaction even in no catalyst in a high-temperature, high-pressure field. However, the process for reaction between an inorganic material and an organic material has not been reported yet.
With respect to fine particles, particularly, nanoparticles, the usability of which is expected because of various useful properties and functions, a number of synthetic methods have been proposed and developed, including the supercritical synthetic method. However, a method for recovering the thus-synthesized fine particles or nanoparticles, and a method for dispersing and stabilizing the fine particles as they are without coagulation after recovery are needed. At the time of use, they must be satisfactorily dispersed in a resin, plastic or solvent. Particularly, nanoparticles synthesized in water are not easily recovered from water since they frequently have hydrophilic surfaces. The nanoparticles or the like have the problem of unfamiliarity with organic solvents, resins or the like.
In order to satisfy these needs, it might be necessary to modify the surface of nanoparticles with organic materials according to the respective purposes. For example, modification with the same polymer as the resin, or donation of the same functional group as the solvent is desirable. If the nanoparticles can be surface-modified in water, the separate recovery of the nanoparticles from water is facilitated. However, although it is desirable for the surface modification of nanoparticles synthesized in water with an organic material that the organic material forms a homogeneous phase with water, the modifying agent usable therefor is limited to an amphipathic surface active agent, a lower alcohol soluble even to water, and the like. Further, even if the nanoparticles are recovered by any method, the recovered nanoparticles are extremely easy to coagulate, and it is difficult to redisperse the nanoparticles coagulated once even by use of a dispersant. The surface modification of such nanoparticles is entirely difficult.
It is well-known that water and an organic material form a homogenous phase in a high-temperature, high-pressure field and, for example, alcohol and sugar, carboxylic acid and alcohol, or carboxylic acid and amine non-catalytically cause a dehydration reaction in high-temperature, high-pressure water. However, it is not known that a reaction is caused between hydroxyl group on the particle surface and the organic material in this condition.
Thus, it is needed to develop the method for introducing a required desirable functional group to nanoparticles at the time of synthesis thereof in water. As a result of the earnest studies, the present inventors found that synthesis of metal oxide particles in a high-temperature, high-pressure hydrothermal synthetic field in the coexistence of an organic material results in surface-modified fine particles having the organic material strongly bonded with the particle surface by the occurrence of a homogenous phase reaction between the particle surface and the organic material. It is also found that the resulting nanoparticles can be phase-separated from water with the remaining organic material, and easily recovered after cooling because they are organically modified. The present invention has been accomplished based on such knowledge.
The present invention provides the followings in typical aspects.
[1] Organically modified fine particles, including hydrocarbon strongly bonded with the surface of fine particles.
[2] The fine particles according to [1], wherein the hydrocarbon is strongly bonded with the surface of metal oxide fine particles, and the organically modified fine particles are organically modified metal oxide fine particles.
[3] The fine particles according to [1], wherein the average diameter of the fine particles is 100 nm or less.
[4] The fine particles according to [1], wherein the average diameter of the fine particles is 50 nm or less.
[5] The fine particles according to [1], wherein the average diameter of the fine particles is 20 nm or less.
[6] The fine particles according to [1], wherein the average diameter of the fine particles is 10 nm or less.
[7] The fine particles according to [1], wherein the average diameter of the fine particles is 5 nm or less.
[8] The fine particles according to any one of [1] to [7], wherein the hydrocarbon is a long-chain hydrocarbon having a chain having 1, 2, 3 or more carbon atoms.
[9] The fine particles according to any one of [1] to [8], wherein the strong bond is selected from the group consisting of ether bond, ester bond, bond through N atom, bond through S atom, metal-C— bond, metal-C═ bond, and metal-(C═O)— bond.
[10] The fine particles according to any one of [1] to [9], wherein the covering ratio of the particle surface for the organic modification is adjusted.
[11] The fine particles according to any one of [1] to [10], wherein the hydrocarbon is strongly bonded with the surface of the fine particles with high-temperature, high-pressure water as a reaction field.
[12] The fine particles according to any one of [1] to [11], wherein the hydrocarbon is strongly bonded with the surface of the fine particles with water of a supercritical or subcritical condition as a reaction field.
[13] A process for producing organically modified metal oxide fine particles, comprising strongly bonding an organic material with the surface of metal oxide fine particles with high-temperature, high-pressure water as a reaction field, thereby synthesizing organically modified metal oxide fine particles.
[14] The process according to [13], wherein water of pressure and/or temperature conditions corresponding to or exceeding a critical point is adapted as the reaction field.
[15] The process according to [13] or [14], wherein the organically modified metal oxide fine particles are synthesized in a reaction field where water of conditions of temperature 250-500° C. and pressure 10-30 MPa is present.
[16] The process according to any one of [13] to [15], wherein the hydrocarbon is a long-chain hydrocarbon having a chain having 1, 2, 3 or more carbon atoms.
[17] The process according to any one of [13] to [16], wherein the strong bond is selected from the group consisting of ether bond, ester bond, bond through N atom, bond through S atom, metal-C— bond, metal-C═ bond, and metal-(C═O)— bond.
[18] The process according to any one of [13] to [17], wherein an organic modifying agent is selected from the group consisting of alcohol, aldehyde, carboxylic acid, amine, thiol, amide, ketone, oxime, phosgene, enamine, amino acid, peptide, and sugar.
[19] The process according to any one of [13] to [18], wherein a solvent for promoting the phase homogenization of the organic modifying agent with water is used as a coexistent material.
[20] The process according to [19], wherein the solvent is selected from the group consisting of methanol, ethanol, propanol, i-propanol, butanol, i-butanol, t-butanol and ethylene glycol.
[21] The process according to any one of [13] to [18], wherein the reaction is carried out in the coexistence of an assistant for promoting the reaction.
[22] The process according to [21], wherein the reaction promoting assistant is an acid.
[23] The process according to [22], wherein the acid is selected from the group consisting of nitric acid, sulfuric acid, hydrochloric acid, bromic acid, formic acid, acetic acid, propionic acid and toluene sulfonic acid.
[24] The process according to any one of [13] to [23], wherein the reaction ratio of the organic modification is controlled by controlling a factor selected from the group consisting of the temperature, the acid concentration and the reaction time.
[25] A method for recovering or collecting fine particles, comprising organically modifying the surface of fine particles, thereby:
(1) precipitating and recovering metal oxide fine particles dispersed in an aqueous solution;
(2) transferring metal oxide fine particles dispersed in an aqueous solution to an organic solvent followed by recovering; or
(3) collecting metal oxide fine particles in an oil phase-water phase interface.
[26] A process for producing fine particles, comprising producing metal oxide fine particles satisfactorily dispersed in an aqueous solution by organic surface modification including hydrophilic groups.
[27] A process for producing organically modified metal oxide fine particles, comprising producing metal oxide fine particles in the coexistence of an organic modifying agent in a reaction field for supercritical hydrothermal synthesis.
[28] The process according to [27], wherein the particle size of the generated particles is adjusted to a further small particle size.
[29] A process for producing organically modified metal oxide fine particles, comprising subjecting a metal compound to a hydrothermal reaction with high-temperature, high-pressure water as a reaction field to form metal oxide fine particles, and strongly bonding an organic matter to the surface of the formed metal oxide fine particles, thereby synthesizing organically modified metal oxide fine particles.
Fine particles with hydrophilic surface (particularly, nanoparticles) are surface-modified with the hydrophobic group of an organic matter such as hydrocarbon, whereby the particles which are difficult to be recovered from an aqueous medium can be easily and surely transferred to an organic medium and separated/recovered without impairing useful characteristics of the fine particles (particularly, nanoparticles). On the other hand, hydrophobic fine particles (particularly, nanoparticles) can be transferred to and separated/recovered from an aqueous medium side such as an aqueous solution by modifying the surface thereof with a hydrocarbon having hydrophilic group.
Since metal oxide fine particles (particularly, nanoparticles) present in an aqueous medium hardly form a homogeneous reaction system with a modifying agent having organic group such as hydrophobic hydrocarbon, the fine particles (particularly, nanoparticles) could not be organically modified without impairing the useful characteristics of the particles. However, this can be made possible by applying the modification of the present invention. Further, since the degree of modification can be controlled, various unique characteristics can be imparted, respectively, by the modification.
Other objects, features and superiority of the present invention and aspects thereof will be obvious for those skilled in the art from the following description. However, it should be understood that the accompanying specification including the following description and concrete examples describes preferred embodiments of the present invention and is disclosed only for illustration. It will be easily understood by those skilled in the art from the following description and the knowledge derived from other parts of the specification that various changes and/or alternations (or modifications) can be made without departing from the intention and scope of the present invention. All patent literatures and reference literatures cited herein are described for illustration, and the content thereof should be included herein as a part of the specification.
The present invention provides a technique for bonding an organic matter with the surface of metal oxide fine particles with high-temperature, high-pressure water as a reaction field to synthesize organically modified metal oxide fine particles, particularly, organically modified metal oxide nanoparticles, which are attracting attentions in recent years because of their peculiar characteristics, the resulting organically modified metal oxide fine particles, and usage and applied technologies thereof. The present invention involves an organic modification method paying attention to the point that water and an organic material form a homogeneous phase in a reaction field showing a certain phase behavior. The features of this method are conceptually and schematically shown in
As the reaction field of the modification reaction of the present invention, suitably, pressure and/or temperature conditions corresponding to or exceeding the subcritical or critical point of water are given.
At the time of using nanoparticles, by introducing a functional group having high affinity with a solvent or resin to be used for to the particles, the particles can be dispersed to the solvent or resin at high concentration.
In the present invention, the particle size can be also controlled by performing the in-situ surface modification in a reaction field for hydrothermal synthesis including a supercritical region.
The term “fine particles” referred to herein may indicate those with an average particle size of 1 μm (1,000 nm) or less and, preferably, nanoparticles. The nanoparticles may generally include those of an average particle size of 200 nm or less and, preferably, those of 200 nm or less. The nanoparticles can have an average particle size of 100 nm or less in a certain case, and an average particle size of 50 nm or less in another case. The nanoparticles further can have an average particle size of 20 nm or less in a suitable case, and an average particle size of 10 nm or less, or 5 nm or less in other cases. Although the particle size of nanoparticles is preferably uniformed, those different in particle size can be suitably mixed in a fixed ratio.
The particle size can be measured by a method known in the relevant field, for example, by TEM, adsorption method, light scattering method, SAXS or the like. In the TEM, at the time of electron microscopic observation, it must be carefully confirmed that particles within the field of view are representative for all the particles when the particle size distribution is wide. In the adsorption method, a BET surface area is evaluated by N2 adsorption or the like.
Fine particles generated by means of hydrolysis reaction are generally composed of a hydroxide such as Fe(OH)3, and the equilibrium is shifted to FeO(OH) and Fe2O3 as the temperature is raised. The molecular arrangement state is shifted from a random amorphous state to a neatly arranged crystal state as the temperature is raised. Highly crystalline nanoparticles which are organically modified can be obtained by using the technique of the present invention.
The high crystallinity can be confirmed by electron diffraction method, analysis of electron microgram, X-ray diffraction, thermogravimetry or the like. In the electron diffraction, as a diffraction interference image, dots are obtained in case of monocrystal, rings in polycrystal, and halos in amorphous. In the electron microgram, a crystal plane is clearly observed in case of monocrystal, and polycrystal has a shape such that crystals further appear from above particles. When primary particles of polycrystal are small, and many particles are coagulated to form a secondary particle, a spherical shape is observed. The amorphous necessarily shows a spherical shape. In the X-ray diffraction, a sharp peak can be observed in case of monocrystal. The crystallite size can be evaluated from the width of ½ height of the X-ray peak by use of Sherre's expression. When the crystallite size obtained by this evaluation is equal to the particle size evaluated from the electron microscopic image, monocrystal is evaluated. In the thermogravimetry, when heating is performed in a dry inactive gas by a thermobalance, a reduction in weight by evaporation of adsorbed moisture is observed at about 100° C., and a reduction in weight by dehydration from the particles is observed up to about 250° C. If an organic material is contained, a further large reduction in weight is observed at 250-400° C. In case of the particles obtained by the technique of the present invention, even if the temperature is raised to 400° C., the reduction in weight by dehydration from the crystals is 10% or less at a maximum, greatly different from the case of metal oxide fine particles synthesized at low temperature. Accordingly, the fine particles of organically modified metal oxide fine particles obtained according to the present invention have high crystallinity as features; for example, they have sharp peaks in X-ray diffraction, dots or rings are observed in electron diffraction, dehydration of crystal water is 10% or less per dry particle in thermogravimetry, and/or the primary particle has a crystal plane in electron microgram.
When a separating or dispersing operation of fine particles is performed in relative to particle size by opposing the surface energy with an external energy such as gravity or electric field or by means of centrifugal force, gravity settling, electrophoresis, or the like, particles with a particle size of several 100 nm or less can be dispersed only when a large external field force is given thereto. With a particle size of 50 nm or less, the influence of the surface energy is further increased, and the dispersion is extremely difficult only with the external field energy, unless the surface property, the physical property of the solvent, or the like is controlled. The technique of the present invention can solve this problem.
Particularly, when the particle size is 10 nm or less, the overlapping in a quantum state is eliminated, and the electron state on the surface seriously affects the bulk physical properties. Therefore, physical properties completely different from those of bulk particles can be obtained, or a quantum size effect (Kubo's effect) is exhibited. Although the particles of a size of about 10 nm or less can be regarded particularly as completely different materials, such fine nanoparticles can be suitably organically modified according to the technique of the present invention.
Typical fine particles in the present invention include those essentially composed of a metal oxide, and these will be hereinafter referred to as “metal oxide fine particles”.
As the “metal” in a metal oxide contained in the metal oxide fine particles, typically, any metal capable of producing nanoparticles can be selected and used, without particular limitation, from metals known by those skilled in the art. Examples of typical metals include, with the line connecting boron (B) of the group IIIB, silicon (Si) of the group IVB, arsenic (As) of the group VB, and tellurium (Te) of the group VIB in the long-period periodic table as a border, elements located on this line and elements situated on the left side or the lower side of the border in the long-period periodic table, including Fe, Co, Ni, Ru, Rh, Pd, Os, Ir, Pt, etc. as elements of the VIII group; Cu, Ag, Au, etc. as elements of the group IB; Zn, Cd, Hg, etc. as elements of the group IIB; B, Al, Ga, In, Ti, etc. as elements of the group IIIB; Si, Ge, Sn, Pb, etc. as elements of the group IVB; As, Sb, Bi, etc. as elements of the group VB; Te, Po, etc. as elements of the group VIB; and elements of the groups IA-VIIA. Examples of the metal oxide include oxides of Fe, Co, Ni, Cu, Ag, Au, Zn, Cd, Hg, Al, Ga, In, Ti, Si, Ge, Sn, Pb, Ti, Zr, Mn, Eu, Y, Nb, Ce, Ba, etc., and concrete examples thereof include SiO2, TiO2, ZnO2, SnO2, Al2O3, MnO2, NiO, Eu2O3, Y2O3, Nb2O3, InO, ZnO, Fe2O3, Fe3O4, CO3O4, ZrO2, CeO2, BaO.6Fe2O3, Al5(Y+Tb)3O12, BaTiO3, LiCoO2, LiMn2O4, K2O.6TiO2, AlOOH, and the like.
In the organic modification of the surface of fine particles, particularly, nanoparticles, any device capable of attaining a high-temperature, high-pressure condition can be selected and used, without particular limitation, from devices well-known by those skilled in the art in the relevant field. For example, both a batch device and a distribution type device are applicable. A typical reactor is shown in
As the organic modifying agent, those capable of strongly bonding hydrocarbon with the surface of fine particles can be selected, without particular limitation, from organic materials well-known in the fields where the application of nanoparticles is expected, including the fields of organic chemistry, inorganic material, and polymer chemistry. As the organic modifying agent, for example, those permitting formation of a strong bond such as ether bond, ester bond, bond through N atom, bond through S atom, metal-C— bond, metal-C═ bond, metal-(C═O)— bond or the like are given. As the hydrocarbon, those having 1 or 2 carbon atoms can be used without particularly limiting the carbon number. From the point of effectively using the features of the present invention, a long-chain hydrocarbon having a chain having 3 or more carbon atoms is preferably used, and examples thereof include straight-chain, branched-chain or cyclic hydrocarbons having 3-20 carbon atoms. The hydrocarbons may be substituted or non-substituted. The substituent may be selected from functional groups well-known in the fields of organic chemistry, inorganic material, polymer chemistry and the like, and one or more substituents can exist in the hydrocarbon, wherein the substituents may be the same or different.
Examples of the organic modifying agent include alcohols, aldehydes, ketones, carboxylic acids, esters, amines, thiols, amides, oximes, phosgenes, enamines, amino acids, peptides, sugars and the like.
Typical modifying agents include pentanol, pentanal, pentanoic acid, pentane amide, pentathiol, hexanol, hexanal, hexanoic acid, hexane amide, hexane thiol, heptanol, heptanal, heptanoic acid, heptane amide, heptane thiol, octanol, octanal, octanoic acid, octane amide, octane thiol, decanol, decanal, decanic acid, decane amide, decane thiol, and the like.
Examples of the hydrocarbon group include a straight-chain or branched-chain alkyl group which may be substituted, a cyclic alkyl group which may be substituted, an aryl group which may be substituted, an aralkyl group which may be substituted, a saturated or unsaturated heterocyclic group which may be substituted, and the like. Examples of the substituent include carboxyl group, cyano group, nitro group, halogen, ester group, amide group, ketone group, formyl group, ether group, hydroxyl group, amino group, sulfonyl group, —O—, —NH—, —S— and the like.
Reaction Mechanism
A hydroxyl group is generally present on the surface of a metal oxide in water. This is resulted from the following equilibrium in reaction.
MO+H2O=M(OH) (1)
This reaction is generally endothermic, and the equilibrium is shifted to the left at a high temperature side. The reaction by the surface modifying agent used is as follows, and it is caused by dehydration reaction.
The left-pointing reaction (reverse reaction) is a reaction well-known as hydrolysis of alkoxide or the like, which is easily caused by addition of water even at about room temperature. This reverse reaction is generally inhibited at high temperature side because it is an endothermic reaction, and the right-pointing reaction becomes more advantageous. This is the same as the temperature dependency of the dehydration reaction of metal hydroxide of equation (1).
The product in water is stabilized more advantageously as the polarity of the solvent is lower, since the polarity of the product is low in the right-pointing reaction (dehydration), compared with in the reaction original system. The higher the temperature is, the lower the dielectric constant of water is. The dielectric constant is reduced to 15 or less at 350° C. or less and suddenly reduced to about 1-10, particularly, in the vicinity of the critical point. Therefore, the dehydration reaction is accelerated beyond a general temperature effect.
M(OH)+ROH=M(OR)+H2O=M.R+2H2O
M(OH)+RCOOH=M(OCOR)+H2O=MR+H2O+CO2
M(OH)+RCHO=M(OH)CR+H2O=MC═R+2H2O, MCR+2H2O,
MR+H2+CO2
M(OH)+RSH=MSR+H2O (reduction)
(these equations are referred to as (2))
Although it is known that the attack on hydroxyl group by amine progresses in the coexistence of a strong acid or through a substitution by Cl at room temperature, its replacement with OH occurs in high-temperature, high-pressure water. It is confirmed, with respect to organic materials, that amination of hexanol progresses with carboxylic acid as a catalyst between hexane amide and hexanol, and it can be presumed that a similar reaction is proceeding. A part of the reaction mechanism of this technique is schematically shown in
In case of thiol, the probability of reduction in the reaction field is reported and it can be presumed that the thiol was partially reduced on the metal oxide surface, causing a thiol additive reaction thereby.
Setting Method of Conditions
1) Equilibrium in Reaction
The reaction condition causing the organic modification can be summarized as followed although it is varied depending on the kind of metals and the modifying agent.
When the equilibrium of equation (1) is on the right and the equilibrium of equation (2) is on the right, the reaction progresses. Since the respective equilibriums are varied depending on the kind of metals and modifying agent, the optimum reaction condition therefor is also varied. When the temperature is raised, the equilibrium of equation (2) is shifted to the right and suddenly shifted to the progress side, particularly, at 350° C. or higher, while the equilibrium of equation (1) is shifted to the left. For the reaction conditions, DB of equations (1) and (2) are referred to.
Since the functional group on the surface of the metal oxide can be made to OH by coexistence of a base or acid, the dehydration reaction with the modifying agent can be progressed in this condition. In that case, since the dehydration reaction is apt to occur in the presence of the acid, the reaction can be progressed by slight coexistence of the acid at high temperature.
2) Phase Equilibrium
Since alcohols, aldehydes, carboxylic acids and amines which are relatively short-chain hydrocarbons are soluble to water, for example, surface modification of the metal oxide with methanol is possible. However, in case of long-chain hydrocarbons, since phase separation from water phase is caused, the metal oxide actually located in water phase may not react with the organic modifying agent even if the equilibrium in reaction gets closer to the progress side. Namely, introduction of lipophilic group is relatively easy, but the phase behavior must be taken into consideration when a long-chain hydrocarbon having three or more carbon atoms is intended.
The phase behavior of hydrocarbon and water is already reported, and this can be referred to. In general, since they form a homogeneous phase in an optional ratio with a vapor-liquid critical locus or more, such temperature/pressure conditions are set, whereby a satisfactory reaction condition can be set.
When a further lower optimum reaction temperature is desired, a third component can be made to coexist to form a homogeneous phase of water and the organic matter. For example, it is known that the coexistent region of hexanol and water can be formed at a further low temperature by the coexistence of ethanol or ethylene glycol which forms a homogeneous phase with water even at low temperature. This can be applied to the reaction of a metal oxide and an organic material. In this case, it is important to select the third component so as not to cause a surface modification reaction by the third component.
The long-chain organic modification in water can be performed only by the above-mentioned technique.
In-Situ Surface Modification in Hydrothermal Synthesis
As described above, the generation of hydroxyl group on the metal oxide surface of equation (1) and the temperature dependency of organic modification reaction of equation (2) are reversed. Therefore, when the reaction of equation (1) is on the left or on the dehydration side, in order to cause a surface modification reaction, the setting of the reaction condition such as coexistence of an acid becomes extremely important, but might be difficult.
The in-situ surface modification in hydrothermal synthesis enables this.
The hydrothermal synthesis progresses by the following reaction route.
Al(NO3)3+3H2O═Al(OH)3+3HNO3
nAl(OH)3=nAlO(OH)+nH2O
nAlO(OH)=n/2Al2O3+n/2H2O
In use of other metal spices and sulfates, hydrochlorides or the like, the synthesis progresses also by such a route. When the hydrothermal synthesis is carried out, for example, by use of a device as shown in
As shown herein, even if the hydroxyl group is finally desorbed from the surface by the dehydration reaction, many hydroxyl groups are generated in a product or on the surface thereof as a reaction precursor. If the organic modifying agent is coexistent in this reaction field, the reaction can be carried out in a condition where the hydroxyl groups are present. Since the acid also as a catalyst for proceeding the dehydration reaction is coexistent in the reaction field, the modification reaction is accelerated. Accordingly, the surface modification which could not be performed to oxides can be carried out.
According to the technique of the present invention, the surface of fine particles can be organically modified without being based on that the equilibration to an oxide by attainment of a high-temperature field, such that a precursor is once synthesized and then subjected to hydrolysis or the like to synthesize a metal oxide or metal hydroxide, or without using a surface radical polymerizing substrate, for example, an oxidizing material sensitive to temperature or light. Accordingly, metal particles or particles with different oxidation-reduction states can be organically surface-modified.
In the present invention, synthesis of an inorganic-organic composite material is attempted by use of a phase state such that water and an organic material forms a homogeneous phase, in which the surface of highly crystalline metal or metal oxide nanoparticles of a size of several nm to 50 nm or less is modified with an organic molecule while synthesizing them. By using the high-temperature, high-pressure water hydrothermal synthetic method therein, the conventional problems of 1) organically modifying the surface of highly crystalline nanoparticles while synthesizing it and 2) forming a polymer film of single layer can be solved. Further, the conventional industrial problems of 1) recovery of nanoparticles from a reaction solvent; 2) stable dispersion and retention thereof over a long period at high concentration in the solvent; 3) homogenous dispersion thereof with a polymer in high concentration; and 4) two-dimensional arrangement of nanoparticles can be solved thereby.
Various nanoparticle synthetic methods such as CVD, PVD, atomization thermal decomposition, sol-gel process, reversed micelle method, hot soap method, and supercritical hydrothermal synthesis have been developed. However, because nanoparticles are easily coagulated with extremely high surface energy, natural physical properties thereof cannot be often exhibited. A method for recovering the nanoparticles is needed. Further, the nanoparticles must be dispersed and stabilized after recovery. The nanoparticles must be satisfactorily dispersed to a resin, plastic or solvent at the time of use. To satisfy these needs, it is necessary to modify the surface of the nanoparticles with organic materials according to the respective purposes. It is desirable to modify the same polymer as the resin and the same functional group as the solvent. These can be solved by the present invention.
Some techniques for surface-modifying the nanoparticles are proposed. However, with a conventional weak linkage such as coordination of thiol with a metal surface or adsorption of a surface active agent to a metal oxide, semiconductor characteristic, fluorescent characteristic, light emitting characteristic, dielectric characteristic and the like, which are developed by making particles to a nano-size, might be lost. If a metal or metal oxide can be covalent-bonded with an organic molecule, nonconventional characteristics of nanoparticles can be derived. In BaTiO3, for example, although a dielectric loss appears in an adsorption layer, it can be significantly reduced in a covalent-bond molecule.
The technique for performing the organic modification by forming the covalent bond includes use of a silane coupling agent. In this case, formation of a Si atom layer on the nanoparticle surface might cause a loss of semiconductor characteristic, fluorescent characteristic, light emitting characteristic, dielectric characteristic and the like of the nanoparticles similarly to the above. Introduction of a functional group by use of a chloro-compound is also included. This might cause dissolution of nanoparticles in the modification reaction condition (in a high pH or a low pH). These problems can be solved by the present invention. According to the present invention, a high-temperature, high-pressure hydrothermal synthetic method can be adapted, and highly crystal nanoparticles can be organically modified with synthesis thereof. When an organic material is made coexist in a high-temperature, high-pressure hydrothermal synthetic field, a strong surface modification having the organic material bonded with the surface of metal oxide particles is formed by the homogeneous phase reaction of the organic material with the particle surface, while synthesizing the particles. Even particles of a particle size of 50 nm or less can be sufficiently provided while keeping extremely high crystallinity. The high-temperature, high-pressure water forms a homogenous phase even with the organic material. An organic-inorganic combination is formed on the generated particle surface. Since other reactions such as polymerization reaction are never caused, modification of only one layer can be performed. The surface modification inhibits the crystal growth to enable synthesis of nanoparticles. At the time of synthesis, an in-situ high-temperature thermal treatment effect can be obtained to enhance the crystallinity.
In the present invention, use of an organic/inorganic composite body as a precursor is not requested as a means for synthesizing nanoparticles, and the applicable range thereof is remarkably excellent.
Consequently, the following effects can be expected.
1) Recovery of Nanoparticles from Water Phase.
The nanoparticles synthesized in supercritical water are generally suspended in water. However, they can be transferred to oil phase by the surface modification of the present invention, and perfectly separated from water.
The recovery of the nanoparticles was extremely difficult. Although addition of a coagulating agent or use of a surface active agent or adsorbent is empirically adapted, a technique for further recovering the nanoparticles therefrom is needed, and a new dispersing technique is also requested to disperse them. According to the technique of the present invention, the particles can be recovered as they are without requiring such an operation.
2) Satisfactory Dispersion of Nanoparticles in an Organic Solvent, Super-High Concentration Dispersion Possible in Principle
Hydrophilic titania particles were suspended in water, but transferred from water to chloroform phase by the surface modification of the present invention.
The surface modification can be performed while performing crystal precipitation without surface modifying operation, a surface reforming operation with a surface active agent or the like as in the past. Although the conventional methods had a limitation for introduction of a modifying group, an optional modifying group can be introduced. Accordingly, a solvent most suitable to a resin or solvent can be selected. The same molecule as the resin or solvent is used, whereby ultimately high-concentration dispersion and even dispersion without using the solvent or resin can be performed.
3) Interface Arrangement by Surface Modification with Controlled Covering Ratio
It was observed that, when the covering ratio is reduced by controlling the reaction, particles are arranged in the interface of water and oil. Accordingly, in addition to the recovery of particles, a nanoparticle arrangement can be performed by using the technique of the present invention.
4) Continuous Control of Dispersibility
The nanoparticles dispersed in water can be easily precipitated by use of a proper solvent system such as a solution of water:ethanol=50:50 by surface-modifying them according to the technique of the present invention. The concentration at which the precipitation starts can be continuously changed by controlling the degree of surface modification. Concretely, for example, a phenomenon as shown in
5) Presentation of Selective Recognition Ability
Nanoparticles modified with a functional group forming no chemical bond therewith or nanoparticles modified with a functional group forming a chemical bond therewith can be produced. The mutually bonding ability can be given by such a surface modification, and a high-order structure of nanoparticles can be formed by use of the technique of the present invention.
The nanoparticles are applied to various uses; for example, SiO2 for a pigment, a catalyst carrier, a high-temperature material, a honeycomb, an anticorrosive material, etc.; Fe2O3 for a pigment, a magnetic material, etc.; CeO2 for an abrasive material, a catalyst carrier, an ion conductor, a solid electrolyte, etc.; TiO2 for a photocatalyst, a cosmetic, etc.; Y2O3 for a pigment, a catalyst carrier, etc.; InO for a transparent conductor, etc.; ZnO for a phosphor material, a conductive material, a pigment, a electronic material, etc.; SiO2 for a catalyst carrier, a zeolite, a filler, a bead, etc.; SnO2 for a conductive material, a conductor, a sensor, a honeycomb, etc.; Nb2O3 for a magnetic material, etc.; Cu, Ag or Al for an electrode, a catalyst material, etc.; Ni for an electrode, a magnetic material, a catalyst material, etc.; Co or Fe for a magnetic material, a catalyst material, etc.; Ag/Cu for an electrode, a catalyst material, etc.; and B4C, AIN, TiB2 and the like for a high-temperature material, a high-strength material, etc.
The nanoparticles or a thin film having a specified arrangement of the nanoparticles are recognized to show unique excellent characteristics, respectively. For example, it is known that nanoparticles arranged in a single layer, or magnetic nanoparticles show excellent functions as a near-field storage medium, in which the nanoparticles can be compactly filled. They effectively exhibit excellent characteristics in application to a magnetic tape or the like. Since a quantum size effect can be obtained in nanoparticles arranged in a dispersion system pattern, for example, a nanophosphor, a product such as quantum effect phosphor, quantum effect light emitter, or LSI high-density mounting base can be provided. A multilayer simultaneous arrangement of nanoparticles such as titania shows excellent functions such as low light scattering and photocatalyst effect, and is made into a wet photoelectric conversion element, a high-function photocatalyst coating or the like. A particle-dispersed film shows excellent functions such as a reinforcing effect or an inflammable effect, and is made into a semiconductor sealant or the like. Typical nanoparticles and fine particles and the preparation methods and particle sizes thereof will be understood in reference to
Fine particles (including nanoparticles) organically surface-modified according to the present invention function as particles suitable to users' needs. For example, the particles are useful as a high-concentration barium titanate-dispersed resin for semiconductor packaging, nanoparticle-dispersed ink for ink jet, a battery material, a catalyst material, a lubricant or the like, and such a material can be prepared as follows.
An electronic part such as a semiconductor is needed to be packaged with a high-dielectric constant resin in order to eliminate electric disturbance out of the package. A barium titanate particle-dispersed thermosetting resin is used therefor. A high-concentration barium titanate-dispersed resin for packaging a semiconductor requires high concentration dispersion of barium titanate particles. Although the barium titanate can be dispersed in a resin using a surface active agent, it has the problem of causing a dielectric loss in the interface. By using the technique for producing organic modified fine particles of the present invention, surface-modified particles with strong linkage can be synthesized, and by introducing the same monomer as the resin, a material in which the resin is integrated with the organic material can be ultimately synthesized.
The nanoparticles are used for ink for high-tech equipment, for example, nanoparticle-dispersed ink for ink jet because of excellent physical properties such as hue, satisfactory coloring and durability. An ink jet printer by the ink dispersed with nanoparticles is expected to be used for formation of wiring and circuit diagrams by ink jet. However, to that end, it is necessary to synthesize nanoparticles suitable thereto and disperse them to a solvent in a high concentration. According to the technique for producing organically modified fine particles of the present invention, particles having the same polymer as an ink solvent can be synthesized.
A battery material, for example, an electrode material such as an Li ion battery or a capacitor material, is mixed with a carbonaceous material and made to a material for product. The battery material is needed to be sufficiently dispersed to carbon and a solvent. In general, a treatment using a dispersant is needed. According to the technique for producing organically modified fine particles of the present invention, a material homogenously dispersible with the solvent can be synthesized without using the dispersant.
A carrier metal catalyst is activated by a charge transfer caused by the interaction of the orbital function of the metal with an oxide catalyst. By using the technique for producing organically modified fine particles of the present invention, capable of mixing dissimilar materials in a nanometer order, a catalyst having activating points where the metal makes contact with the oxide in a high density can be prepared to produce an excellent catalyst material.
A lubricant, which is used to reduce the friction acting between solid bodies, can be expected to work as a nano-bearing by including the nanoparticles therein. Concretely, shearing force is converted to the rotating motion energy of the bearing, whereby the transmission to the other side of the shearing force is prevented. Conventionally, an organic polymer has been used as the lubricant, and oxide nanoparticles having a strong structure can be dispersed thereto by the technique for producing organically modified fine particles of the present invention.
The present invention will be further concretely described with working examples. The examples are provided simply to be illustrative of the present invention and informative for concrete embodiments thereof. These examples describe specified concrete embodiments of the present invention, but never limit the scope of the invention disclosed in the present application or indicate a limitation thereof. It should be understood that various embodiments can be made based on the idea herein.
All the examples were executed or can be executed by use of standard techniques, except those described in detail, and they are well-known and regular for those skilled in the art.
(Organic Modification of Metal Oxide Fine Particles in High-Temperature, High-Pressure Water)
An experiment was carried out using a 5 α-tubular autoclave (tube bomb reactor). TiO2 nanoparticles 0.1 g was charged in a reactor tube with pure water 2.5 cc and hexanal 0.1 cc. The reactor tube was put in a heating furnace preliminarily set to 400° C., and heated. The pressure is 390 bar on the assumption of pure water. It took 1.5 min to raise the temperature. The reaction was carried out for 10 min. The reaction was stopped by putting the reactor tube to cold water. The product was recovered by repeating washing with water and washing with chloroform twice. The recovered product is shown on the right of
Accordingly, surface modification of a metal oxide can be performed by using high-temperature, high-pressure water as a reaction solvent.
(Organic Modification of Metal Oxide Fine Particles in High-Temperature, High-Pressure Water)
An experiment was carried out using a 5-cc tubular autoclave (tube bomb reactor) similarly to Example 1. SiO2 nanoparticles 0.1 g was charged in a reactor tube with pure water 2.5 cc and hexylamine 0.1 cc. The reactor tube was put in a heating furnace preliminarily set to 400° C., and heated. The pressure is 390 bar on the assumption of pure water. It took 1.5 min to raise the temperature. The reaction was carried out for 10 min. The reaction was stopped by putting the reactor tube to cold water. The product was recovered by repeating washing with water and washing with chloroform twice. In case of using no hexylamine, the recovered product is in a state suspended in water similarly to Example 1. This is caused by generation of hydrophilic groups. In contrast, when the modification was performed, the particles were collected to the interface between chloroform and water. It was found therefrom that the modification is too imperfect to provide a sufficient wetting angle to water and chloroform, the particles are not transferred to the chloroform phase but collected to the interface. A controlled organic modification in high-temperature, high-pressure water shows the probability of collection of a metal oxide to the interface. In this case, also, such a remarkable difference cannot be observed only by mixing a modifying agent without reaction, showing that this is not resulted from physical adsorption of a modifying group. According to the IR spectral measurement of the resulting particles, peaks of CH2 and CH3 were observed on the surface (
(Amino Acid Modification of Metal Oxide Fine Particles in High-Temperature, High-Pressure Water)
An experimental reaction was carried out using a 5 α-tubular autoclave (tube bomb reactor).
SiO2 nanoparticles 0.1 g was charged in a reactor tube with pure water 2.5 cc and cysteine 100 mg. The reactor tube was put in a heating furnace preliminarily set to 400° C., and heated. The pressure is 390 bar on the assumption of pure water. It took 1.5 min to raise the temperature. The reaction was carried out for 10 min. The reaction was stopped by putting the reactor tube to cold water. The recovered particles are perfectly dispersed in water more satisfactorily than in the suspended state before reaction. This shows that coagulation of SiO2 is prevented by donation of hydrophilic groups to enhance the dispersibility.
Similarly to Examples 1 and 2, such a remarkable difference cannot be observed only by mixing a modifying agent without reaction, showing that this is not resulted from physical adsorption of a modifying group. According to the IR spectral measurement of the resulting particles, COOH and NH2 groups are reduced, while linkages of Si—N—R and SIO—(CO)R are observed on the surface. Accordingly, the formation of covalent bond by the reaction could be confirmed.
(Organic Modification of Metal Oxide Fine Particles in High-Temperature, High-Pressure Water in Coexistence of Acid)
An experimental reaction was carried out using a 5-cc tubular autoclave (tube bomb reactor).
Al2O3 nanoparticles 0.1 g was charged in a reactor tube with 0.1M aqueous solution of H2SO4 2.5 cc and hexanal 0.1 cc. The reactor tube was put in a heating furnace preliminarily set to 400° C., and heated. The pressure is 390 bar on the assumption of pure water. It took 1.5 min to raise the temperature. The reaction was carried out for 10 min. The reaction was stopped by putting the reactor tube to cold water. The product was recovered by repeating washing with water and washing with chloroform twice. An experiment for recovering the product not with chloroform but with hexanol was also carried out in the same manner.
In case of using pure water without addition of the acid, the recovered product is in a state precipitated in the bottom of the chloroform phase (the lower phase). This is the same as the result of the experiment without surface treatment. In contrast, when the surface modification is performed in the coexistence of the acid, the product is laid in a state partially suspended in the chloroform phase. When recovered with hexanol, the product is partially suspended in the hexanol and partially collected to the interface between hexanol (the upper phase) and water. This shows that the surface treatment reaction progresses by the coexistence of the acid. Even in such a reaction system where the organic modification is difficult to progress, the reaction can be progressed by the coexistence of the acid. The same experiment was carried out for ZnO which was difficult to modify, and it was confirmed that the coexistence of the acid enables the modification thereof.
(Long-Chain Organic Modification of Metal Oxide Fine Particles in High-Temperature, High-Pressure Water)
An experimental reaction was carried out using a 5 cc-tubular autoclave (tube bomb reactor).
SiO2 nanoparticles 0.1 g was charged in a reactor tube with pure water 1.5 cc and dodecanal 1 cc. The reactor tube was put in a heating furnace preliminarily set to 400° C., and heated. The pressure is 390 bar on the assumption of pure water. It took 1.5 min to raise the temperature. The reaction was carried out for 10 min. The reaction was stopped by putting the reactor tube to cold water. The product was recovered by repeating washing with water and washing with chloroform twice. The same experiment was carried out by use of hexanal.
In case of using no decanal, the recovered product was in a state suspended in water. In contrast, when the modification was performed, the particles were collected to the interface between chloroform and water at 400° C., showing that the modification was attained. In case of using hexanal, the reaction was satisfactorily progressed at 300° C. and 400° C., and a slight progress of the reaction was confirmed further at 200° C. However, in case of using dodecanal, satisfactory surface modification could be performed at 400° C., but the reaction was not progressed at all at 200° C. Even at 300° C., the degree of progress of the reaction was low, compared with the case of hexanal.
Sufficient examples for the phase behavior of alkane-water phase were reported, and formation of a heterogeneous phase was probably caused at low temperature, drawing up the phase behavior of the dodecane-water system.
(Organic Modification of Metal Oxide Fine Particles in High-Temperature, High-Pressure Water)
An experimental reaction was carried out using a 5-cc tubular autoclave (tube bomb reactor). TiO2 nanoparticles 0.1 g was charged in a reactor tube with pure water 2.5 cc and hexanoic acid 0.1 cc. The reactor tube was put in a heating furnace preliminarily set to 400° C., and heated. The pressure is 390 bar on the assumption of pure water. It took 1.5 min to raise the temperature. The reaction was carried out for 10 min. The reaction was stopped by putting the reactor tube to cold water. The product was recovered by repeating washing with water and washing with chloroform twice. The recovered product is shown in
In case of using no hexanoic acid or performing no surface modification, the recovered product is in a state suspended in water (the upper phase) as shown in the left of
By using high-temperature, high-pressure water as a reaction solvent, surface modification of a metal oxide can be performed. The same result is also obtained in the use of hexanamide.
(Organic Modification of Meal Oxide Fine Particles in High-Temperature, High-Pressure Water with Amino Acid)
An experimental reaction was carried out using a 5-cc tubular autoclave (tube bomb reactor). TiO2 nanoparticles 0.1 g was charged in a reactor tube with pure water 2.5 cc and asparaginic acid 100 mg. The reactor tube was put in a heating furnace preliminarily set to 400° C., and heated. The pressure is 390 bar on the assumption of pure water. It took 1.5 min to raise the temperature. The reaction was carried out for 10 min. The reaction was stopped by putting the reactor tube to cold water. The recovered particles were perfectly dispersed in water more satisfactorily (the right of
Similarly to Examples 2 and 6, such a remarkable difference cannot be observed only by mixing a modifying agent without reaction, showing that this is not caused by physical adsorption of a modifying group. According to the IR spectral measurement of the resulting particles, COOH and NH2 groups were reduced, while linkages of Ti—N—R, TiO—(CO)R and Ti—R were observed on the surface. According to this, the formation of covalent bond by the reaction could be confirmed.
(Organic Modification of Metal Oxide Fine Particles in High-Temperature, High-Pressure Water with Long-Chain Hydrocarbon)
An experimental reaction was carried out using a 5-cc tubular autoclave (tube bomb reactor). SiO2 nanoparticles 0.1 g was charged in a reactor tube with pure water 1.5 cc and decanoic acid 1 cc. The reactor tube was put in a heating furnace preliminarily set to 400° C., and heated. The pressure is 390 bar on the assumption of pure water. It took 1.5 min to raise the temperature. The reaction was carried out for 10 min. The reaction was stopped by putting the reactor tube to cold water. The product was recovered by repeating washing with water and washing with hexadecane twice. The recovered product is shown in the right of
The same experiment was carried out for decanal and decane amine, and the same result was obtained. The state of organically modified nanoparticles with decane amine is shown on the left of
(In-Situ Organic Modification in High-Temperature, High-Pressure Hydrothermal Synthesis (1))
An experimental reaction was carried out using a 5-cc tubular autoclave (tube bomb reactor). Hydrogen peroxide was added to 0.01 Mol/l of Mn(NO3)2 aqueous solution to have an amount of 0.05 Mol/l, the resulting mixture 2.5 g was charged in a reactor tube, and hexanol 0.1 cc was further charged therein. The reactor tube was put in a heating furnace preliminarily set to 400° C., and heated. The pressure is 390 bar on the assumption of pure water. It took 1.5 min to raise the temperature. The reaction was carried out for 10 min, and the product was recovered. The recovered product is shown in
In general, although it is technically difficult to recover nanoparticles generated in an aqueous solution from water phase, the particles can be easily separated and recovered from the aqueous solution according to the technique of the present invention. Although it is not easy to modify a preliminarily generated metal oxide with hexanol, the organic modification of the oxide nanoparticle surface can be performed by the in-situ surface modification.
(In-Situ Organic Modification in High-Temperature, High-Pressure Hydrothermal Synthesis (2))
An experimental reaction was carried out using a 5-cc tubular autoclave (tube bomb reactor). Hydrogen peroxide was added to 0.01 Mol/l of Zn(NO3)2 aqueous solution to have an amount of 0.05 Mol/l, the resulting mixture 2.5 g was charged in a reactor tube, and hexanol 0.1 cc was further charged therein. The reactor tube was put in a heating furnace preliminarily set to 400° C., and heated. The pressure is 390 bar on the assumption of pure water. It took 1.5 min to raise the temperature. The reaction was carried out for 10 min, and the product was recovered. In case of using no hexanol, the recovered product is in a state suspended in water, and this is caused by generation of hydrophilic groups. In contrast, when the modification was performed, the product was laid in a state perfectly separated from water phase. The same experiment was carried out using Zn(COOH)2 in addition to Zn(NO3)2.
In every case, as shown in Example 4, it was difficult for ZnO to perform satisfactory modification without the coexistence of an acid. According to the present technique, the in-situ surface modification can be performed. Particularly, in case of a formate, the generated acid is HCOOH, the decomposition of which to H2+CO2 in a high temperature field is known, and it does not function as the acid. The reason that satisfactory surface modification can be attained despite of it is attributable to that the dehydration reaction of hydroxyl group OH with an organic modifying agent in the initial stage of crystal growth satisfactorily progresses.
TEM images of the particles obtained according to the present technique are shown in
(In-Situ Organic Modification in High-Temperature, High-Pressure Hydrothermal Synthesis (3))
An experimental reaction was carried out using a 5-cc tubular autoclave (tube bomb reactor). Hydrogen peroxide was added to 0.01 Mol/l of Mn(NO3)2 aqueous solution to have an amount of 0.1 Mol/l, the resulting mixture 2.5 g was charged in a reactor tube, and hexanol 0.1 cc was further charged therein. The reactor tube was put in a heating furnace preliminarily set to 400° C., and heated. The pressure is 390 bar on the assumption of pure water. It took 1.5 min to raise the temperature. The reaction was carried out for 10 min, and the product was recovered. The recovered product is shown in
[In-Situ Organic Modification in High-Temperature, High-Pressure Hydrothermal Synthesis (4)]
An experimental reaction was carried out using a 5-cc tubular autoclave (tube bomb reactor). Hydrogen peroxide was added to 0.01 Mol/l of Ce(NO3)2 aqueous solution to have an amount of 0.01 Mol/l, the resulting mixture 2.5 g was charged in a reactor tube, and hexanoic acid 0.1 cc was further charged therein. The reactor tube was put in a heating furnace preliminarily set to 400° C., and heated. The pressure is 390 bar on the assumption of pure water. It took 1.5 min to raise the temperature. The reaction was carried out for 10 min, and the product was recovered. The recovered product is shown in
In the modification by use of the hexanoic acid insoluble to water, the treatment does not progress at a low temperature of 200° C. since a homogenous layer cannot formed with water, but progresses at 300° C. or 400° C., where the dielectric constant of water is reduced to enable the formation of the homogeneous phase with a modifying agent. This shows also the presence of a case essentially requiring a treatment in a high-temperature range where the reaction can sufficiently progress.
[In-Situ Organic Modification in High-Temperature, High-Pressure Hydrothermal Synthesis (5)]
With respect to Fe2O3, NiO, ZnO and CO203, reactions were carried out in coexistence of hexanol, hexanoic acid, hexylamine, hexanal, and hexane thiol in the same manner as Examples 9-12. The results are collectively shown in Tables 1-4.
The respective notations in the tables mean as follows:
None: No modifying agent, W: Water phase, Int.: Interface phase between water phase and organic phase, O: Organic phase, a little: Existing a little, little: Existing only a little, w: Transferred from interface to water phase by slight vibration, o: Transferred from interface to oil phase by slight vibration, more: Existing more, NP: nanoparticles, L: Thickness of boundary phase with a subscript showing the treatment temperature, S: Solubility of NP in organic phase with a subscript showing the treatment temperature.
The comparison result as the whole is shown in Table 5.
With respect to ZnO, the surface modification treatment can be performed in the same manner. The effect of the surface modification can be sufficiently obtained. However, in case of using hexanol, it could not be said that sufficient surface modification can be obtained in every case.
Therefore, the in-situ organic modification was carried out. The experimental method was the same as in Examples 8 and 9. Namely, the experimental reaction was carried out using a 5-cc tubular autoclave (tube bomb reactor). Hydrogen peroxide was added to 0.01 Mol/l of Zn(NO3)2 aqueous solution to have an amount of 0.1 Mol/l, the resulting mixture 2.5 g was charged in a reactor tube, and hexanol 0.1 cc was further charged therein. The reactor tube was put in a heating furnace preliminarily set to 200° C., 300° C. and 400° C., and heated. The pressure is 390 bar on the assumption of pure water. It took 1.5 min to raise the temperature. The reaction was carried out for 10 min, and the product was recovered. In case of using no hexanol, the recovered product was in a state suspended in water and oil phase, but the particles were transferred to the oil phase by the surface modification using hexanol. Thus, a sufficient surface modification effect is obtained.
Even if the surface modification cannot be sufficiently performed on the particles generated once, sufficient surface modification can be performed by the in-situ surface modification.
The results of the same surface modification treatment of nanoparticles of ZnO, CeO2, Al2O3, SnO2, and SiO2 are collectively shown in Tables 6 and 7. Table 6 comparatively shows the result of surface modification of the fine particles of each metal oxide, and Table 7 shows the result of the in-situ modification thereof. In the tables, o shows that transfer of particles to organic phase was recognized, and x shows that transfer of particles to organic phase was not clearly recognized. A shows that the organic modification progressed although it was insufficient.
As is apparent from the comparison of Tables 1-7, the same in-situ surface modification effect is obtained in ZnO, CeO2, TiO2 and the like.
[In-Situ Organic Modification in High-Temperature, High-Pressure Hydrothermal Synthesis (6)]
According to the same manner as in Examples 8 and 9, syntheses of Fe2O3, CO2O3, NiO, ZnO, and TiO2 were carried out in the coexistence of hexanol, hexanoic acid, hexylamine, hexanal, and hexane thiol. The results are collectively shown in Table 7. Based on the case of using no surface modifying agent, the magnitude of the surface modification effect is expressed by indexes of 1-10.
It was found from the table that the degree of progress of the surface modification reaction is varied depending on not only the temperature but also the reactant. This reason is that even if no surface modification is performed, some reactants can be dispersed in water while sufficiently retaining hydrophilic groups as ZnO and NiO, while some reactants can be dispersed in oil phase with minimized hydrophobic groups as TiO2, and the stability or reactivity of the functional group on the particle surface is thus varied even if the in-situ surface modification is performed in a particle generating field. In case of modification with aldehyde or modification with amine, surface modification can be obtained more satisfactorily at 300° C. than at 400° C. This is resulted from that a hydrolysis reaction is caused in a high-temperature field. Namely, the optimum condition is 300-400° C., and an excessively high temperature conceivably causes the influence of the reverse reaction.
The present invention provides organically modified fine particles (particularly, nanoparticles) having hydrocarbon strongly bonded with the surface of fine particles, particularly, organically modified metal oxide fine particles, a process for producing the same, and further a method for recovering or collecting fine particles such as nanoparticles, with an intention to promote the use of nanoparticles showing various unique excellent properties, characteristics and functions as industrial materials and pharmaceutical and cosmetic materials such as ceramic nano-structure modified material, optical functional coating material, electromagnetic shielding material, secondary battery material, fluorescent material, electronic part material, magnetic recording material, and abrasive material.
It will be obvious that the present invention can be executed beyond the above-mentioned description and examples. In view of the above-mentioned teaching, a lot of alterations and modifications of the present invention can be made, and such alterations and modifications are therefore intended to be embraced by the appended claims.