ORGANOSILICA MATERIALS AND USES THEREOF

FIELD OF THE INVENTION

The present invention relates to organosilica materials, methods of making and uses thereof.

BACKGROUND OF THE INVENTION

Porous inorganic solids have found great utility as catalysts and separation media for industrial application. In particular, mesoporous materials, such as silicas and aluminas, having a periodic arrangement of mesopores are attractive materials for use in adsorption, separation and catalysis processes due to their uniform and tunable pores, high surface areas and large pore volumes. The pore structure of such mesoporous materials is large enough to absorb large molecules and the pore wall structure can be as thin as about 1 nm. Further, such mesoporous materials are known to have large specific surface areas (e.g., 1000 m²/g) and large pore volumes (e.g., 1 cm³/g). For these reasons, such mesoporous materials enable reactive catalysts, adsorbents composed of a functional organic compound, and other molecules to rapidly diffuse into the pores and therefore, can be advantageous over zeolites, which have smaller pore sizes. Consequently, such mesoporous materials can be useful not only for catalysis of high-speed catalytic reactions, but also as large capacity adsorbents.

It was further discovered that the inclusion of some organic groups in the mesoporous framework can provide adjustable reactive surfaces and also contributes to uniformity in pore size, higher mechanical strength, and hydrothermal stability of the material. Thus, mesoporous organosilica materials can exhibit unique properties compared to mesoporous silica such as enhanced hydrothermal stability, chemical stability, and mechanical properties. Organic groups can be incorporated using bridged silsesquioxane precursors of the form Si—R—Si to form mesoporous organosilicas.

Mesoporous organosilicas are conventionally formed by the self-assembly of the silsequioxane precursor in the presence of a structure directing agent, a porogen and/or a framework element. The precursor is hydrolysable and condenses around the structure directing agent. These materials have been referred to as Periodic Mesoporous Organosilicates (PMOs), due to the presence of periodic arrays of parallel aligned mesoscale channels. For example, Landskron, K., et al. [Science, 302:266-269 (2003)] report the self-assembly of 1,3,5-tris[diethoxysila]cylcohexane [(EtO)₂SiCH₂]₃in the presence of a base and the structure directing agent, cetyltrimethylammonium bromide to form PMOs that are bridged organosilicas with a periodic mesoporous framework, which consist of SiO₃R or SiO₂R₂building blocks, where R is a bridging organic group. In PMOs, the organic groups can be homogenously distributed in the pore walls. U.S. Pat. Pub. No. 2012/0059181 reports the preparation of a crystalline hybrid organic-inorganic silicate formed from 1,1,3,3,5,5 hexaethoxy-1,3,5 trisilyl cyclohexane in the presence of NaAlO₂and base. U.S. Patent Application Publication No. 2007/003492 reports preparation of a composition formed from 1,1,3,3,5,5 hexaethoxy-1,3,5 trisilyl cyclohexane in the presence of propylene glycol monomethyl ether.

However, the use of a structure directing agent, such as a surfactant, in the preparation of an organosilica material, such as a PMO, requires a complicated, energy intensive process to eliminate the structure directing agent at the end of the preparation process. This limits the ability to scale-up the process for industrial applications. Therefore, there is a need to provide additional organosilica materials with a desirable pore diameter, pore volume and surface area. Further, there is a need to provide such organosilica materials that can be prepared by a method that can be practiced in the absence of a structure directing agent, a porogen or surfactant.

SUMMARY OF THE INVENTION

It has been found that an organosilica material with desirable pore diameter, pore volume, and surface area can be achieved. Further, such organosilica material can be successfully prepared without the need for a structure directing agent, a porogen or surfactant.

Thus, in one aspect, embodiments of the invention provide an organosilica material, which is a polymer of at least one independent monomer of Formula [Z¹OZ²OSiCH₂]₃(I), wherein Z¹and Z²each independently represent a hydrogen atom, a C₁-C₄alkyl group or a bond to a silicon atom of another monomer and at least one other monomer selected from the group consisting of: (i) an independent unit of Formula Z³OZ⁴Z⁵Z⁶(II), wherein each Z³represents a hydrogen atom, a C₁-C₄alkyl group or a bond to a silicon atom of another monomer; and Z⁴, Z⁵and Z⁶are each independently selected from the group consisting of a hydroxyl group, a C₁-C₄alkyl group, a C₁-C₄alkoxy group, a nitrogen-containing C₁-C₁₀alkyl group, a nitrogen-containing heteroaralkyl group, a nitrogen-containing optionally substituted heterocycloalkyl group, and an oxygen atom bonded to a silicon atom of another monomer; (ii) an independent unit of Formula Z⁷Z⁸Z⁹Si—R¹—SiZ⁷Z⁸Z⁹(III), wherein each Z⁷independently represents a hydroxyl group, a C₁-C₄alkoxy group or an oxygen bonded to a silicon atom of another comonomer; each Z⁸and Z⁹independently represent a hydroxyl group, a C₁-C₄alkoxy group, a C₁-C₄alkyl group or an oxygen bonded to a silicon atom of another monomer; and R¹represents a nitrogen-containing C₂-C₁₀alkylene group; and (iii) a combination thereof.

In still another aspect, embodiments of the invention provide a gas separation process comprising contacting a gas mixture containing at least one contaminant with the organosilica material described herein.

In still another aspect, embodiments of the invention provide a process for selectively separating a contaminant from a feed gas mixture, the process comprising: a) contacting the feed gas mixture under sorption conditions with the organosilica material as described herein; b) adsorbing the contaminant into/onto the organosilica material; c) subjecting the organosilica material as described herein to desorption conditions by which at least a portion of the sorbed contaminant is desorbed; and d) retrieving a contaminant-rich product stream that has a higher mol % of contaminant than the feed gas mixture.

Other embodiments, including particular aspects of the embodiments summarized above, will be evident from the detailed description that follows.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 illustrates an X-Ray Diffraction (XRD) spectrum for Sample 1A and Comparative Sample 2.

FIG. 2a illustrates thermal gravimetric analysis (TGA) data for Sample 1A in N₂.

FIG. 2b illustrates TGA data for Sample 1A in air.

FIG. 3 illustrates BET N₂adsorption for Sample 1A, Comparative Sample 2 and Sample 5.

FIG. 4 illustrates a BET pore diameter distribution for Sample 1A, Comparative Sample 2 and Sample 5.

FIG. 5 illustrates comparison of BET surface area and microporous surface area for Sample 1A, Sample 3, Sample 5A and Sample 6.

FIG. 6 illustrates comparison of pore volume and pore diameter for Sample 1A, Sample 3, Sample 5A and Sample 6.

FIG. 7a illustrates a ²⁹Si MAS NMR spectrum for Sample 1A.

FIG. 7b illustrates a ²⁹Si MAS NMR spectrum for Comparative Sample 2.

FIG. 8a illustrates TGA data for Comparative Sample 2 in N₂.

FIG. 8b illustrates TGA data for Comparative Sample 2 in air.

FIG. 9 illustrates an XRD spectrum for Sample 1A and Sample 3.

FIG. 10 illustrates a ²⁹Si MAS NMR spectrum for Sample 4A, Sample 4B, Sample 4C and Sample 4D.

FIG. 11 illustrates an XRD spectrum for Sample 5 and Sample 6.

FIG. 12 illustrates TGA data for Sample 5 in air and N₂.

FIG. 13 illustrates a ²⁹Si MAS NMR spectrum for Sample 1A and Sample 5.

FIG. 14 illustrates a ²⁹Si MAS NMR spectrum for Sample 7A and Sample 7B.

FIG. 15 illustrates an XRD spectrum for Sample 9, Sample 10, Sample 11A, and Sample 12.

FIG. 16 illustrates an XRD spectrum for Sample 13 and Sample 21.

FIG. 17 illustrates N₂adsorption isotherms for Sample 13, Sample 14 and Sample 15.

FIG. 18 illustrates pore diameter distribution for Sample 13, Sample 14 and Sample 15.

FIG. 19 illustrates CO₂adsorption isotherms at 40° C. for Sample 13A.

FIG. 20 illustrates CO₂adsorption isotherms at 30° C. for Sample 17.

DETAILED DESCRIPTION OF THE INVENTION

In various aspects of the invention, organosilica materials, methods for preparing organosilica materials and gas and liquid separation processes using the organosilica materials are provided.

I. DEFINITIONS

For purposes of this invention and the claims hereto, the numbering scheme for the Periodic Table Groups is according to the IUPAC Periodic Table of Elements.

The term “and/or” as used in a phrase such as “A and/or B” herein is intended to include “A and B”, “A or B”, “A”, and “B”.

The terms “substituent”, “radical”, “group”, and “moiety” may be used interchangeably.

As used herein, and unless otherwise specified, the term “C_n” means hydrocarbon(s) having n carbon atom(s) per molecule, wherein n is a positive integer.

As used herein, and unless otherwise specified, the term “hydrocarbon” means a class of compounds containing hydrogen bound to carbon, and encompasses (i) saturated hydrocarbon compounds, (ii) unsaturated hydrocarbon compounds, and (iii) mixtures of hydrocarbon compounds (saturated and/or unsaturated), including mixtures of hydrocarbon compounds having different values of n.

As used herein, and unless otherwise specified, the term “alkyl” refers to a saturated hydrocarbon radical having from 1 to 12 carbon atoms (i.e. C₁-C₁₂alkyl), particularly from 1 to 8 carbon atoms (i.e. C₁-C₈alkyl), particularly from 1 to 6 carbon atoms (i.e. C₁-C₆alkyl), and particularly from 1 to 4 carbon atoms (i.e. C₁-C₄alkyl). Examples of alkyl groups include, but are not limited to, methyl, ethyl, propyl, butyl, pentyl, hexyl, heptyl, octyl, decyl, and so forth. The alkyl group may be linear, branched or cyclic. “Alkyl” is intended to embrace all structural isomeric forms of an alkyl group. For example, as used herein, propyl encompasses both n-propyl and isopropyl; butyl encompasses n-butyl, sec-butyl, isobutyl and tert-butyl and so forth. As used herein, “C₁alkyl” refers to methyl (—CH₃), “C₂alkyl” refers to ethyl (—CH₂CH₃), “C₃alkyl” refers to propyl (—CH₂CH₂CH₃) and “C₄alkyl” refers to butyl (e.g. —CH₂CH₂CH₂CH₃, —(CH₃)CHCH₂CH₃, —CH₂CH(CH₃)₂, etc.). Further, as used herein, “Me” refers to methyl, and “Et” refers to ethyl, “i-Pr” refers to isopropyl, “t-Bu” refers to tert-butyl, and “Np” refers to neopentyl.

As used herein, and unless otherwise specified, the term “alkylene” refers to a divalent alkyl moiety containing 1 to 12 carbon atoms (i.e. C₁-C₁₂alkylene) in length and meaning the alkylene moiety is attached to the rest of the molecule at both ends of the alkyl unit. For example, alkylenes include, but are not limited to, —CH₂—, —CH₂CH₂—, —CH(CH₃)CH₂—, —CH₂CH₂CH₂—, etc. The alkylene group may be linear or branched.

As used herein, and unless otherwise specified, the term “nitrogen-containing alkyl” refers to an alkyl group as defined herein wherein one or more carbon atoms in the alkyl group is substituted with a nitrogen atom or a nitrogen-containing cyclic hydrocarbon having from 2 to 10 carbon atoms (i.e., a nitrogen-containing cyclic C₂-C₁₀hydrocarbon), particularly having from 2 to 5 carbon atoms (i.e., a nitrogen-containing cyclic C₂-C₅hydrocarbon), and particularly having from 2 to 5 carbon atoms (i.e., a nitrogen-containing cyclic C₂-C₅hydrocarbon). The nitrogen-containing cyclic hydrocarbon may have one or more nitrogen atoms. The nitrogen atom(s) may optionally be substituted with one or two C₁-C₆alkyl groups. The nitrogen-containing alkyl can have from 1 to 12 carbon atoms (i.e. C₁-C₁₂nitrogen-containing alkyl), particularly from 1 to 10 carbon atoms (i.e. C₁-C₁₀nitrogen-containing alkyl), particularly from 2 to 10 carbon atoms (i.e. C₂-C₁₀nitrogen-containing alkyl), particularly from 3 to 10 carbon atoms (i.e. C₃-C₁₀nitrogen-containing alkyl), and particularly from 3 to 8 carbon atoms (i.e. C₁-C₁₀nitrogen-containing alkyl). Examples of nitrogen-containing alkyls include, but are not limited to,

embedded image

As used herein, and unless otherwise specified, the term “nitrogen-containing alkylene” refers to an alkylene group as defined herein wherein one or more carbon atoms in the alkyl group is substituted with a nitrogen atom. The nitrogen atom(s) may optionally be substituted with one or two C₁-C₆alkyl groups. The nitrogen-containing alkylene can have from 1 to 12 carbon atoms (i.e. C₁-C₁₂nitrogen-containing alkylene), particularly from 2 to 10 carbon atoms (i.e. C₂-C₁₀nitrogen-containing alkylene), particularly from 3 to 10 carbon atoms (i.e. C₃-C₁₀nitrogen-containing alkylene), particularly from 4 to carbon atoms (i.e. C₄-C₁₀nitrogen-containing alkylene), and particularly from 3 to 8 carbon atoms (i.e. C₃-C₈nitrogen-containing alkyl). Examples of nitrogen-containing alkylenes include, but are not limited to,

embedded image

As used herein, and unless otherwise specified, the term “alkenyl” refers to an unsaturated hydrocarbon radical having from 2 to 12 carbon atoms (i.e., C₂-C₁₂alkenyl), particularly from 2 to 8 carbon atoms (i.e., C₂-C₈alkenyl), particularly from 2 to 6 carbon atoms (i.e., C₂-C₆alkenyl), and having one or more (e.g., 2, 3, etc.) carbon-carbon double bonds. The alkenyl group may be linear, branched or cyclic. Examples of alkenyls include, but are not limited to ethenyl (vinyl), 2-propenyl, 3-propenyl, 1,4-pentadienyl, 1,4-butadienyl, 1-butenyl, 2-butenyl and 3-butenyl. “Alkenyl” is intended to embrace all structural isomeric forms of an alkenyl. For example, butenyl encompasses 1,4-butadienyl, 1-butenyl, 2-butenyl and 3-butenyl, etc.

As used herein, and unless otherwise specified, the term “alkenylene” refers to a divalent alkenyl moiety containing 2 to about 12 carbon atoms (i.e. C₂-C₁₂alkenylene) in length and meaning that the alkylene moiety is attached to the rest of the molecule at both ends of the alkyl unit. For example, alkenylenes include, but are not limited to, —CH═CH—, —CH═CHCH₂—, —CH═CH═CH—, —CH₂CH₂CH═CHCH₂—, etc. —CH₂CH₂—, —CH(CH₃)CH₂—, —CH₂CH₂CH₂—, etc. The alkenylene group may be linear or branched.

As used herein, and unless otherwise specified, the term “alkynyl” refers to an unsaturated hydrocarbon radical having from 2 to 12 carbon atoms (i.e., C₂-C₁₂alkynyl), particularly from 2 to 8 carbon atoms (i.e., C₂-C₈alkynyl), particularly from 2 to 6 carbon atoms (i.e., C₂-C₆alkynyl), and having one or more (e.g., 2, 3, etc.) carbon-carbon triple bonds. The alkynyl group may be linear, branched or cyclic. Examples of alkynyls include, but are not limited to ethynyl, 1-propynyl, 2-butynyl, and 1,3-butadiynyl. “Alkynyl” is intended to embrace all structural isomeric forms of an alkynyl. For example, butynyl encompassses 2-butynyl, and 1,3-butadiynyl and propynyl encompasses 1-propynyl and 2-propynyl (propargyl).

As used herein, and unless otherwise specified, the term “alkynylene” refers to a divalent alkynyl moiety containing 2 to about 12 carbon atoms (i.e. C₂-C₁₂alkenylene) in length and meaning that the alkylene moiety is attached to the rest of the molecule at both ends of the alkyl unit. For example, alkenylenes include, but are not limited to, —C≡C—, —C≡CCH₂—, —C≡CCH₂C≡C—, —CH₂CH₂C≡CCH₂—, etc. —CH₂CH₂—, —CH(CH₃)CH₂—, —CH₂CH₂CH₂—, etc. The alkynlene group may be linear or branched.

As used herein, and unless otherwise specified, the term “alkoxy” refers to —O-alkyl containing from 1 to about 10 carbon atoms. The alkoxy may be straight-chain or branched-chain. Non-limiting examples include methoxy, ethoxy, propoxy, butoxy, isobutoxy, tert-butoxy, pentoxy, and hexoxy. “C₁alkoxy” refers to methoxy, “C₂alkoxy” refers to ethoxy, “C₃alkoxy” refers to propoxy and “C₄alkoxy” refers to butoxy. Further, as used herein, “OMe” refers to methoxy and “OEt” refers to ethoxy.

As used herein, and unless otherwise specified, the term “aromatic” refers to unsaturated cyclic hydrocarbons having a delocalized conjugated π system and having from 5 to 20 carbon atoms (aromatic C₅-C₂₀hydrocarbon), particularly from 5 to 12 carbon atoms (aromatic C₅-C₁₂hydrocarbon), and particularly from 5 to 10 carbon atoms (aromatic C₅-C₁₂hydrocarbon). Exemplary aromatics include, but are not limited to benzene, toluene, xylenes, mesitylene, ethylbenzenes, cumene, naphthalene, methylnaphthalene, dimethylnaphthalenes, ethylnaphthalenes, acenaphthalene, anthracene, phenanthrene, tetraphene, naphthacene, benzanthracenes, fluoranthrene, pyrene, chrysene, triphenylene, and the like, and combinations thereof. Additionally, the aromatic may comprise one or more heteroatoms. Examples of heteroatoms include, but are not limited to, nitrogen, oxygen, and/or sulfur. Aromatics with one or more heteroatom include, but are not limited to furan, benzofuran, thiophene, benzothiophene, oxazole, thiazole and the like, and combinations thereof. The aromatic may comprise monocyclic, bicyclic, tricyclic, and/or polycyclic rings (in some embodiments, at least monocyclic rings, only monocyclic and bicyclic rings, or only monocyclic rings) and may be fused rings.

As used herein, and unless otherwise specified, the term “aryl” refers to any monocyclic or polycyclic cyclized carbon radical containing 6 to 14 carbon ring atoms, wherein at least one ring is an aromatic hydrocarbon. Examples of aryls include, but are not limited to phenyl, naphthyl, pyridinyl, and indolyl.

As used herein, and unless otherwise specified, the term “aralkyl” refers to an alkyl group substituted with an aryl group. The alkyl group may be a C₁-C₁₀alkyl group, particularly a C₁-C₆, particularly a C₁-C₄alkyl group, and particularly a C₁-C₃alkyl group. Examples of aralkyl groups include, but are not limited to phenymethyl, phenylethyl, and naphthylmethyl. The aralkyl may comprise one or more heteroatoms and be referred to as a “heteroaralkyl.” Examples of heteroatoms include, but are not limited to, nitrogen (i.e., nitrogen-containing heteroaralkyl), oxygen (i.e., oxygen-containing heteroaralkyl), and/or sulfur (i.e., sulfur-containing heteroaralkyl). Examples of heteroaralkyl groups include, but are not limited to, pyridinylethyl, indolylmethyl, furylethyl, and quinolinylpropyl.

As used herein, and unless otherwise specified, the term “heterocyclo” refers to fully saturated, partially saturated or unsaturated or polycyclic cyclized carbon radical containing from 4 to 20 carbon ring atoms and containing one or more heteroatoms atoms. Examples of heteroatoms include, but are not limited to, nitrogen (i.e., nitrogen-containing heterocyclo), oxygen (i.e., oxygen-containing heterocyclo), and/or sulfur (i.e., sulfur-containing heterocyclo). Examples of heterocyclo groups include, but are not limited to, thienyl, furyl, pyrrolyl, piperazinyl, pyridyl, benzoxazolyl, quinolinyl, imidazolyl, pyrrolidinyl, and piperidinyl.

As used herein, and unless otherwise specified, the term “heterocycloalkyl” refers to an alkyl group substituted with heterocyclo group. The alkyl group may be a C₁-C₁₀alkyl group, particularly a C₁-C₆, particularly a C₁-C₄alkyl group, and particularly a C₁-C₃alkyl group. Examples of heterocycloalkyl groups include, but are not limited to thienylmethyl, furylethyl, pyrrolylmethyl, piperazinylethyl, pyridylmethyl, benzoxazolylethyl, quinolinylpropyl, and imidazolylpropyl.

As used herein, the term “hydroxyl” refers to an —OH group.

As used herein, the term “mesoporous” refers to solid materials having pores that have a diameter within the range of from about 2 nm to about 50 nm.

As used herein, the term “organosilica” refers to an organosiloxane compound that comprises one or more organic groups bound to two or more Si atoms.

As used herein, the term “silanol” refers to a Si—OH group.

As used herein, the term “silanol content” refers to the percent of the Si—OH groups in a compound and can be calculated by standard methods, such as NMR.

As used herein, the terms “structure directing agent,” “SDA,” and/or “porogen” refer to one or more compounds added to the synthesis media to aid in and/or guide the polymerization and/or polycondensing and/or organization of the building blocks that form the organosilica material framework. Further, a “porogen” is understood to be a compound capable of forming voids or pores in the resultant organosilica material framework. As used herein, the term “structure directing agent” encompasses and is synonymous and interchangeable with the terms “templating agent” and “template.”

As used herein, and unless otherwise specified, the term “adsorption” includes physisorption, chemisorption, and condensation onto a solid material and combinations thereof.

II. ORGANOSILICA MATERIALS

The invention relates to organosilica materials. In a first embodiment, the organosilica material may be a polymer of at least one independent monomer of Formula [Z¹OZ²OSiCH₂]₃(I), wherein Z¹and Z²each independently can be a hydrogen atom, a C₁-C₄alkyl group or a bond to a silicon atom of another siloxane and at least one other monomer selected from the group consisting of:

- (i) an independent unit of Formula Z³OZ⁴Z⁵Z⁶(II), wherein each Z³represents a hydrogen atom, a C₁-C₄alkyl group or a bond to a silicon atom of another monomer; and Z⁴, Z⁵and Z⁶are each independently selected from the group consisting of a hydroxyl group, a C₁-C₄alkyl group, a C₁-C₄alkoxy group, a nitrogen-containing C₁-C₁₀alkyl group, a nitrogen-containing heteroaralkyl group, a nitrogen-containing optionally substituted heterocycloalkyl group, and an oxygen atom bonded to a silicon atom of another monomer;
- (ii) a unit of Formula Z⁷Z⁸Z⁹Si—R¹—SiZ⁷Z⁸Z⁹(III), wherein each Z⁷independently represents a hydroxyl group, a C₁-C₄alkoxy group or an oxygen bonded to a silicon atom of another comonomer; Each Z8 and Z9 independently represent a hydroxyl group, a C₁-C₄alkoxy group, a C₁-C₄alkyl group or an oxygen bonded to a silicon atom of another monomer; and each R¹represents a nitrogen-containing C₂-C₁₀alkylene group; and
- (iii) a combination thereof.

As used herein, and unless otherwise specified, “a bond to a silicon atom of another monomer” means the bond can advantageously displace a moiety (particularly an oxygen-containing moiety such as a hydroxyl, an alkoxy or the like), if present, on a silicon atom of the another monomer so there may be a bond directly to the silicon atom of the another monomer thereby connecting the two monomers, e.g., via a Si—O—Si linkage. As used herein, and unless otherwise specified, “an oxygen atom bonded to a silicon atom of another monomer” means that the oxygen atom can advantageously displace a moiety (particularly an oxygen-containing moiety such as a hydroxyl, an alkoxy or the like), if present, on a silicon atom of the another monomer so the oxygen atom may be bonded directly to the silicon atom of the another monomer thereby connecting the two monomers, e.g., via a Si—O—Si linkage. For clarity, in the aforementioned bonding scenarios, the “another monomer” can be a monomer of the same type or a monomer of a different type.

II.A. Monomers of Formula (I)

In various embodiments, Z¹and/or Z²each can be a hydrogen atom.

Additionally or alternatively, Z¹and/or Z²each can be a C₁-C₄alkyl group, a C₁-C₃alkyl group, a C₁-C₂alkyl group or methyl.

Additionally or alternatively, Z¹and/or Z²each can be a bond to a silicon atom of another siloxane monomer.

Additionally or alternatively, Z¹and Z²each independently can be a hydrogen atom, a C₁-C₂alkyl group or a bond to a silicon atom of another monomer.

Additionally or alternatively, Z¹and Z²each independently can be a hydrogen atom, ethyl or a bond to a silicon atom of another monomer.

Additionally or alternatively, Z¹and Z²each independently can be a hydrogen atom or a bond to a silicon atom of another monomer.

II.B. Monomers of Formula (II)

In various embodiments, the organosilica material may further comprise another monomer in combination with independent units of Formula (I), such as another monomer having at least one independent unit of Formula Z³OZ⁴Z⁵Z⁶Si (II), wherein each Z³can be a hydrogen atom, a C₁-C₄alkyl group or a bond to a silicon atom of another monomer; and Z⁴, Z⁵and Z⁶each independently can be selected from the group consisting of a hydroxyl group, a C₁-C₄alkyl group, a C₁-C₄alkoxy group, a nitrogen-containing C₁-C₁₀alkyl group, a nitrogen-containing heteroaralkyl group, and a nitrogen-containing optionally substituted heterocycloalkyl group, and an oxygen atom bonded to a silicon atom of another monomer.

In various aspects, each Z³can be a hydrogen atom.

Additionally or alternatively, each Z³can be a C₁-C₄alkyl group, a C₁-C₃alkyl group, a C₁-C₂alkyl group or methyl.

Additionally or alternatively, each Z³can be a hydrogen atom or a C₁-C₂alkyl group.

Additionally or alternatively, each Z³can be a bond to a silicon atom of another monomer.

Additionally or alternatively, each Z³can be a hydrogen atom, a C₁-C₂alkyl group or a bond to a silicon atom of another monomer.

Additionally or alternatively, each Z³can be a hydrogen atom, ethyl, methyl or a bond to a silicon atom of another monomer.

Additionally or alternatively, Z⁴, Z⁵and Z⁶each independently can be a hydroxyl group.

Additionally or alternatively, each Z³can be a hydrogen atom, a C₁-C₂alkyl group or a bond to a silicon atom of another monomer; and Z⁴, Z⁵and Z⁶each independently can be a hydroxyl group.

Additionally or alternatively, Z⁴, Z⁵and Z⁶each independently can be a C₁-C₄alkyl group, a C₁-C₃alkyl group, a C₁-C₂alkyl group or methyl.

Additionally or alternatively, Z⁴, Z⁵and Z⁶each independently can be a hydroxyl group or a C₁-C₂alkyl group.

Additionally or alternatively, each Z³can be a hydrogen atom, a C₁-C₂alkyl group or a bond to a silicon atom of another monomer; and Z⁴, Z⁵and Z⁶each independently can be a hydroxyl group or a C₁-C₂alkyl group.

Additionally or alternatively, Z⁴, Z⁵and Z⁶each independently can be a C₁-C₄alkoxy group, a C₁-C₃alkoxy group, a C₁-C₂alkoxy group or methoxy.

Additionally or alternatively, Z⁴, Z⁵and Z⁶each independently can be selected from the group consisting of a hydroxyl group, a C₁-C₂alkyl group and a C₁-C₂alkoxy group.

Additionally or alternatively, each Z³can be a hydrogen atom, a C₁-C₂alkyl group or a bond to a silicon atom of another monomer; and Z⁴, Z⁵and Z⁶each can be selected from the group consisting of a hydroxyl group, a C₁-C₂alkyl group and a C₁-C₂alkoxy group.

Additionally or alternatively, Z⁴, Z⁵and Z⁶each independently can be a nitrogen-containing C₁-C₁₀alkyl group, a nitrogen-containing C₁-C₉alkyl group, a nitrogen-containing C₁-C₈alkyl group, a nitrogen-containing C₁-C₇alkyl group, a nitrogen-containing C₁-C₆alkyl group, a nitrogen-containing C₁-C₅alkyl group, a nitrogen-containing C₁-C₄alkyl group, a nitrogen-containing C₁-C₃alkyl group, a nitrogen-containing C₁-C₂alkyl group, or a methylamine. In particular, Z⁴, Z⁵and Z⁶each independently can be a nitrogen-containing C₂-C₁₀alkyl group, a nitrogen-containing C₃-C₁₀alkyl group, a nitrogen-containing C₃-C₉alkyl group, or a nitrogen-containing C₃-C₈alkyl group. The aforementioned nitrogen-containing alkyl groups may have one or more nitrogen atoms (e.g., 2, 3, etc.). Examples of nitrogen-containing C₁-C₁₀alkyl groups include, but are not limited to,

embedded image

Additionally or alternatively, Z⁴, Z⁵and Z⁶each independently can be selected from the group consisting of a hydroxyl group, a C₁-C₂alkyl group, a C₁-C₂alkoxy group and a nitrogen-containing C₃-C₁₀alkyl group.

Additionally or alternatively, Z⁴, Z⁵and Z⁶each independently can be a nitrogen-containing heteroaralkyl group. The nitrogen-containing heteroaralkyl group can be a nitrogen-containing C₄-C₁₂heteroaralkyl group, a nitrogen-containing C₄-C₁₀heteroaralkyl group, or a nitrogen-containing C₄-C₈heteroaralkyl group. Examples of nitrogen-containing heteroaralkyl groups include but are not limited to pyridinylethyl, pyridinylpropyl, pyridinylmethyl, indolylmethyl, pyrazinylethyl, and pyrazinylpropyl. The aforementioned nitrogen-containing heteroaralkyl groups may have one or more nitrogen atoms (e.g., 2, 3, etc.).

Additionally or alternatively, Z⁴, Z⁵and Z⁶each independently can be selected from the group consisting of a hydroxyl group, a C₁-C₂alkyl group, a C₁-C₂alkoxy group, nitrogen-containing C₃-C₁₀alkyl group and a nitrogen-containing heteroaralkyl group.

Additionally or alternatively, each Z³can be a hydrogen atom, a C₁-C₂alkyl group or a bond to a silicon atom of another monomer; and Z⁴, Z⁵and Z⁶each independently can be selected from the group consisting of a hydroxyl group, a C₁-C₂alkyl group, a C₁-C₂alkoxy group, a nitrogen-containing C₃-C₁₀alkyl group and a nitrogen-containing heteroaralkyl group.

Additionally or alternatively, Z⁴, Z⁵and Z⁶each independently can be a nitrogen-containing heterocycloalkyl group, wherein the heterocycloalkyl group may be optionally substituted with a C₁-C₆alkyl group, particularly a C₁-C₄alkyl group. The nitrogen-containing heterocycloalkyl group can be a nitrogen-containing C₄-C₁₂heterocycloalkyl group, a nitrogen-containing C₄-C₁₀heterocycloalkyl group, or a nitrogen-containing C₄-C₈heterocycloalkyl group. Examples of nitrogen-containing heterocycloalkyl groups include but are not limited to piperazinylethyl, piperazinylpropyl, piperidinylethyl, piperidinylpropyl. The aforementioned nitrogen-containing heterocycloalkyl groups may have one or more nitrogen atoms (e.g., 2, 3, etc.).

Additionally or alternatively, Z⁴, Z⁵and Z⁶each independently can be an oxygen atom bonded to a silicon atom of another monomer.

Additionally or alternatively, each Z³can be a hydrogen atom, a C₁-C₂alkyl group or a bond to a silicon atom of another monomer; and Z⁴, Z⁵and Z⁶each independently can be selected from the group consisting of a hydroxyl group, a C₁-C₂alkyl group, a C₁-C₂alkoxy group, a nitrogen-containing C₃-C₈alkyl group, C₄-C₁₀heteroaralkyl group, a nitrogen-containing optionally substituted C₄-C₁₀heterocycloalkyl group, and an oxygen atom bonded to a silicon atom of another monomer.

Additionally or alternatively, each Z³can be a hydrogen atom or a bond to a silicon atom of another monomer; and Z⁴, Z⁵and Z⁶each independently can be selected from the group consisting of a hydroxyl group, a C₁-C₂alkyl group, a nitrogen-containing C₃-C₈alkyl group, C₄-C₁₀heteroaralkyl group, a nitrogen-containing optionally substituted C₄-C₁₀heterocycloalkyl group, and an oxygen atom bonded to a silicon atom of another monomer.

In another particular embodiment, each Z³can be a hydrogen atom, methyl or a bond to a silicon atom of another comonomer; Z⁴and Z⁵each independently can be selected from the group consisting of a hydroxyl group, methoxy, and an oxygen atom bonded to a silicon atom of another monomer; and each Z⁶can be

embedded image

In another particular embodiment, each Z³can be a hydrogen atom, ethyl or a bond to a silicon atom of another comonomer; Z⁴and Z⁵each independently can be selected from the group consisting of a hydroxyl group, ethoxy, and an oxygen atom bonded to a silicon atom of another monomer; and each Z⁶can be

embedded image

II.C. Monomers of Formula (III)

In various embodiments, the organosilica material may further comprise another monomer in combination with independent units of Formula (I) and optionally independent units Formula (II), such as another monomer having at least one independent unit of Formula Z⁷Z⁸Z⁹Si—R—SiZ⁷Z⁸Z⁹(III), wherein each Z⁷independently can be a hydroxyl group, a C₁-C₄alkoxy group or an oxygen atom bonded to a silicon atom of another comonomer; Each Z8 and Z9 independently can a hydroxyl group, a C₁-C₄alkoxy group, a C₁-C₄alkyl group or an oxygen atom bonded to a silicon atom of another monomer; and each R¹can be a nitrogen-containing C₂-C₁₀alkylene group.

In various aspects, each Z⁷can be a hydroxyl group.

Additionally or alternatively, each Z⁷can be a C₁-C₄alkoxy group, a C₁-C₃alkoxy group, a C₁-C₂alkoxy group or methoxy.

Additionally or alternatively, each Z⁷can be a hydroxyl group or a C₁-C₂alkoxy group.

Additionally or alternatively, each Z⁷can be an oxygen atom bonded to a silicon atom of another comonomer.

Additionally or alternatively, each Z⁷can be a hydroxyl group, a C₁-C₂alkoxy group or an oxygen atom bonded to a silicon atom of another comonomer.

Additionally or alternatively, each Z⁷can be a hydroxyl group or an oxygen atom bonded to a silicon atom of another comonomer.

Additionally or alternatively, each Z8 and Z9 independently can be a hydroxyl group.

Additionally or alternatively, each Z8 and Z9 independently can be a C₁-C₄alkoxy group, a C₁-C₃alkoxy group, a C₁-C₂alkoxy group or methoxy.

Additionally or alternatively, each Z8 and Z9 independently can be a hydroxyl group or a C₁-C₂alkoxy group.

Additionally or alternatively, each Z⁸and Z⁹independently can be a C₁-C₄alkyl group, a C₁-C₃alkyl group, a C₁-C₂alkyl group or methyl.

Additionally or alternatively, each Z8 and Z9 independently can be a hydroxyl group, a C₁-C₂alkoxy group, or a C₁-C₂alkyl group.

Additionally or alternatively, each Z8 and Z9 independently can be an oxygen atom bonded to a silicon atom of another comonomer.

Additionally or alternatively, each Z8 and Z9 independently can be a hydroxyl group, a C₁-C₂alkoxy group, a C₁-C₂alkyl group, or an oxygen atom bonded to a silicon atom of another comonomer.

Additionally or alternatively, each Z8 and Z9 independently can be a hydroxyl group, a C₁-C₂alkyl group, or an oxygen atom bonded to a silicon atom of another comonomer.

Additionally or alternatively, each Z⁷can be a hydroxyl group, a C₁-C₂alkoxy group or an oxygen atom bonded to a silicon atom of another comonomer; and each Z8 and Z9 independently can be a hydroxyl group, a C₁-C₂alkoxy group, a C₁-C₂alkyl group, or an oxygen atom bonded to a silicon atom of another comonomer.

Additionally or alternatively, each Z⁷can be a hydroxyl group, ethoxy, methoxy or an oxygen atom bonded to a silicon atom of another comonomer; and each Z8 and Z9 independently can be a hydroxyl group, ethoxy, methyl, or an oxygen atom bonded to a silicon atom of another comonomer.

Additionally or alternatively, each Z⁷can be a hydroxyl group or an oxygen atom bonded to a silicon atom of another comonomer; and each Z8 and Z9 independently can be a hydroxyl group, methyl, or an oxygen atom bonded to a silicon atom of another comonomer.

Additionally or alternatively, each Z⁷can be a hydroxyl group or an oxygen atom bonded to a silicon atom of another comonomer; and each Z8 and Z9 independently can be a hydroxyl group or an oxygen atom bonded to a silicon atom of another comonomer.

Additionally or alternatively, each R¹can be a nitrogen-containing C₂-C₁₀alkylene group, a nitrogen-containing C₃-C₁₀alkylene group, a nitrogen-containing C₄-C₁₀alkylene group, a nitrogen-containing C₄-C₉alkylene group, a nitrogen-containing C₄-C₈alkylene group, or nitrogen containing C₃-C₈alkylene group. The aforementioned nitrogen-containing alkylene groups may have one or more nitrogen atoms (e.g., 2, 3, etc.). Examples of nitrogen-containing alkylene groups include, but are not limited to,

embedded image

Additionally or alternatively, each Z⁷can be a hydroxyl group, a C₁-C₂alkoxy group or an oxygen atom bonded to a silicon atom of another comonomer; each Z8 and Z9 independently can be a hydroxyl group, a C₁-C₂alkoxy group, a C₁-C₂alkyl group, or an oxygen atom bonded to a silicon atom of another comonomer; and R¹can be a nitrogen-containing C₄-C₁₀alkylene group.

Additionally or alternatively, each Z⁷can be a hydroxyl group, ethoxy, methoxy or an oxygen atom bonded to a silicon atom of another comonomer; each Z8 and Z9 independently can be a hydroxyl group, ethoxy, methoxy, methyl, or an oxygen atom bonded to a silicon atom of another comonomer; and R can be selected from the group consisting of

embedded image

Additionally or alternatively, each Z⁷can be a hydroxyl group or an oxygen atom bonded to a silicon atom of another comonomer; each Z8 and Z9 independently can be a hydroxyl group, methyl, or an oxygen atom bonded to a silicon atom of another comonomer; and R can be selected from the group consisting of

embedded image

Additionally or alternatively, each Z⁷can be a hydroxyl group or an oxygen atom bonded to a silicon atom of another comonomer; each Z⁸and Z⁹independently can be a hydroxyl group, or an oxygen atom bonded to a silicon atom of another comonomer; and R can be selected from the group consisting of

embedded image

In another particular embodiment, each Z⁷can be a hydroxyl group, methoxy or an oxygen atom bonded to a silicon atom of another comonomer; each Z⁸and Z⁹independently can be selected from the group consisting of a hydroxyl group, methoxy, and an oxygen atom bonded to a silicon atom of another monomer; and R can be

embedded image

In another particular embodiment, each Z⁷can be a hydroxyl group, ethoxy or an oxygen atom bonded to a silicon atom of another comonomer; Z⁸can be a hydroxyl group, ethoxy, and an oxygen atom bonded to a silicon atom of another monomer; Z¹⁹can be methyl; and R can be

embedded image

In another particular embodiment, each Z⁷can be a hydroxyl group, methoxy or an oxygen atom bonded to a silicon atom of another comonomer; Z⁸can be a hydroxyl group, methoxy, and an oxygen atom bonded to a silicon atom of another monomer; Z⁹can be methyl; and R can be

embedded image

II.D. Monomers of Formula (IV)

In various embodiments, each Z¹⁰can be a hydrogen atom.

Additionally or alternatively, each Z¹⁰can be a C₁-C₄alkyl group, a C₁-C₃alkyl group, a C₁-C₂alkyl group or methyl.

Additionally or alternatively, each Z¹⁰can be a hydrogen atom or a C₁-C₂alkyl group.

Additionally or alternatively, each Z¹⁰can be a bond to a silicon atom of another monomer.

Additionally or alternatively, each Z¹⁰can be a hydrogen atom, a C₁-C₂alkyl group or a bond to a silicon atom of another monomer.

Additionally or alternatively, each Z¹⁰can be a hydrogen atom, ethyl or a bond to a silicon atom of another monomer.

Additionally or alternatively, each Z¹¹can be a hydroxyl group.

Additionally or alternatively, each Z¹¹can be a C₁-C₆alkyl group, a C₁-C₅alkyl group, a C₁-C₄alkyl group, a C₁-C₃alkyl group, a C₁-C₂alkyl group or methyl.

Additionally or alternatively, each Z¹¹can be a hydroxyl group or a C₁-C₄alkyl group.

Additionally or alternatively, each Z¹¹can be an oxygen atom bonded to a silicon atom of another monomer.

Additionally or alternatively, each Z¹¹can be a hydroxyl group, a C₁-C₄alkyl group or an oxygen atom bonded to a silicon atom of another monomer.

Additionally or alternatively, each Z¹¹can be a hydroxyl group, methyl or an oxygen atom bonded to a silicon atom of another monomer.

Additionally or alternatively, each Z¹⁰can be a hydrogen atom, a C₁-C₂alkyl group or a bond to a silicon atom of another monomer and Z¹¹can be a hydroxyl group, a C₁-C₄alkyl group or an oxygen atom bonded to a silicon atom of another monomer.

Additionally or alternatively, each Z¹⁰can be a hydrogen atom, ethyl or a bond to a silicon atom of another monomer and Z¹¹can be a hydroxyl group, methyl or an oxygen atom bonded to a silicon atom of another monomer.

Additionally or alternatively, each Z¹⁰can be a hydrogen atom or a bond to a silicon atom of another monomer and each Z¹¹can be a hydroxyl group, methyl or an oxygen atom bonded to a silicon atom of another monomer.

II.E. Monomers of Formula (V)

In various embodiments, the organosilica material may further comprise another monomer in combination with independent units of Formula (I) and optionally independent units Formulas(II), (III) and/or (IV), such as another monomer having at least one independent unit of Formula Z¹²OZ¹³Z¹⁴Z¹⁵Si (V), wherein each Z¹²can be a hydrogen atom or a C₁-C₄alkyl group or a bond to a silicon atom of another monomer; and Z¹³, Z¹⁴and Z¹⁵each independently can be selected from the group consisting of a hydroxyl group, a C₁-C₄alkyl group, a C₁-C₄alkoxy group and an oxygen atom bonded to a silicon atom of another monomer.

In various aspects, each Z¹²can be a hydrogen atom.

Additionally or alternatively, each Z¹²can be a C₁-C₄alkyl group, a C₁-C₃alkyl group, a C₁-C₂alkyl group or methyl.

Additionally or alternatively, each Z¹²can be a hydrogen atom or a C₁-C₂alkyl group.

Additionally or alternatively, each Z¹²can be a bond to a silicon atom of another monomer.

Additionally or alternatively, each Z¹²can be a hydrogen atom, a C₁-C₂alkyl group or a bond to a silicon atom of another monomer.

Additionally or alternatively, each Z¹²can be a hydrogen atom, ethyl, methyl or a bond to a silicon atom of another monomer.

Additionally or alternatively, Z¹³, Z¹⁴and Z¹⁵each independently can be a hydroxyl group.

Additionally or alternatively, each Z¹²can be a hydrogen atom, a C₁-C₂alkyl group or a bond to a silicon atom of another monomer; and Z¹³, Z¹⁴and Z¹⁵each independently can be a hydroxyl group.

Additionally or alternatively, Z¹³, Z¹⁴and Z¹⁵each independently can be a C₁-C₄alkyl group, a C₁-C₃alkyl group, a C₁-C₂alkyl group or methyl.

Additionally or alternatively, Z¹³, Z¹⁴and Z¹⁵each independently can be a hydroxyl group or a C₁-C₂alkyl group.

Additionally or alternatively, Z¹³, Z¹⁴and Z¹⁵each independently can be a C₁-C₄alkoxy group, a C₁-C₃alkoxy group, a C₁-C₂alkoxy group or methoxy.

Additionally or alternatively, Z¹³, Z¹⁴and Z¹⁵each independently can be selected from the group consisting of a hydroxyl group, a C₁-C₂alkyl group and a C₁-C₂alkoxy group.

Additionally or alternatively, each Z¹²can be a hydrogen atom, a C₁-C₂alkyl group or a bond to a silicon atom of another monomer; and Z¹³, Z¹⁴and Z¹⁵each can be selected from the group consisting of a hydroxyl group, a C₁-C₂alkyl group and a C₁-C₂alkoxy group.

Additionally or alternatively, Z¹³, Z¹⁴and Z¹⁵each independently can be an oxygen atom bonded to a silicon atom of another monomer.

Additionally or alternatively, each Z¹²can be a hydrogen atom, a C₁-C₂alkyl group or a bond to a silicon atom of another monomer; and Z¹³, Z¹⁴and Z¹⁵each independently can be selected from the group consisting of a hydroxyl group, a C₁-C₂alkyl group, a C₁-C₂alkoxy group, and an oxygen atom bonded to a silicon atom of another monomer.

Additionally or alternatively, each Z²can be a hydrogen atom, a C₁-C₂alkyl group or a bond to a silicon atom of another monomer; and Z¹³, Z¹⁴and Z¹⁵each independently can be selected from the group consisting of a hydroxyl group, a C₁-C₂alkyl group, a C₁-C₂alkoxy group and an oxygen atom bonded to a silicon atom of another monomer.

Additionally or alternatively, each Z¹²can be a hydrogen atom or a bond to a silicon atom of another monomer; and Z¹³, Z¹⁴and Z¹⁵each independently can be selected from the group consisting of a hydroxyl group, a C₁-C₂alkyl group and an oxygen atom bonded to a silicon atom of another monomer.

In a particular embodiment, each Z¹²can be a hydrogen atom, ethyl or a bond to a silicon atom of another monomer; and Z¹³, Z¹⁴and Z¹⁵each independently can be selected from the group consisting of a hydroxyl group, ethoxy, and an oxygen atom bonded to a silicon atom of another monomer.

In another particular embodiment, each Z¹²can be a hydrogen atom, ethyl or a bond to a silicon atom of another comonomer; Z¹³and Z¹⁴each independently can be selected from the group consisting of a hydroxyl group, ethoxy, and an oxygen atom bonded to a silicon atom of another monomer; and Z¹⁵can be methyl.

II.E. Monomers of Formula (VI)

In various embodiments, the organosilica material may further comprise another monomer in combination with independent units of Formula (I) and optionally independent units Formulas(II), (III) (IV) and/or (V), such as another monomer having at least one independent unit of Formula Z¹⁶Z¹⁷Z¹⁸Si—R²—SiZ¹⁶Z¹⁷Z¹⁸(VI), wherein each Z¹⁶independently represents a hydroxyl group, a C₁-C₄alkoxy group or an oxygen atom bonded to a silicon atom of another comonomer; each Z¹⁷and Z¹⁸independently represent a hydroxyl group, a C₁-C₄alkoxy group, a C₁-C₄alkyl group or an oxygen atom bonded to a silicon atom of another monomer; and each R²is selected from the group consisting a C₁-C₈alkylene group, a C₂-C₈alkenylene group, a C₂-C₈alkynylene group, an optionally substituted C₆-C₂₀aralkyl and an optionally substituted C₄-C₂₀heterocycloalkyl group.

In various aspects, each Z¹⁶can be a hydroxyl group.

Additionally or alternatively, each Z¹⁶can be a C₁-C₄alkoxy group, a C₁-C₃alkoxy group, a C₁-C₂alkoxy group or methoxy.

Additionally or alternatively, each Z¹⁶can be a hydroxyl group or a C₁-C₂alkoxy group.

Additionally or alternatively, each Z¹⁶can be an oxygen atom bonded to a silicon atom of another comonomer.

Additionally or alternatively, each Z¹⁶can be a hydroxyl group, a C₁-C₂alkoxy group or an oxygen atom bonded to a silicon atom of another comonomer.

Additionally or alternatively, each Z¹⁶can be a hydroxyl group or an oxygen atom bonded to a silicon atom of another comonomer.

Additionally or alternatively, each Z¹⁷and Z¹⁸independently can be a hydroxyl group.

Additionally or alternatively each Z¹⁷and Z¹⁸independently can be a C₁-C₄alkoxy group, a C₁-C₃alkoxy group, a C₁-C₂alkoxy group or methoxy.

Additionally or alternatively, each Z¹⁷and Z¹⁸independently can be a hydroxyl group or a C₁-C₂alkoxy group.

Additionally or alternatively, each Z¹⁷and Z¹⁸independently can be a C₁-C₄alkyl group, a C₁-C₃alkyl group, a C₁-C₂alkyl group or methyl.

Additionally or alternatively each Z¹⁷and Z¹⁸independently can be a hydroxyl group, a C₁-C₂alkoxy group, or a C₁-C₂alkyl group.

Additionally or alternatively, each Z¹⁷and Z¹⁸independently can be an oxygen atom bonded to a silicon atom of another comonomer.

Additionally or alternatively, each Z¹⁷and Z¹⁸independently can be a hydroxyl group, a C₁-C₂alkoxy group, a C₁-C₂alkyl group, or an oxygen atom bonded to a silicon atom of another comonomer.

Additionally or alternatively, each Z¹⁷and Z¹⁸independently can be a hydroxyl group, a C₁-C₂alkyl group, or an oxygen atom bonded to a silicon atom of another comonomer.

Additionally or alternatively, each Z¹⁶can be a hydroxyl group, a C₁-C₂alkoxy group or an oxygen atom bonded to a silicon atom of another comonomer; and each Z¹⁷and Z¹⁸independently can be a hydroxyl group, a C₁-C₂alkoxy group, a C₁-C₂alkyl group, or an oxygen atom bonded to a silicon atom of another comonomer.

Additionally or alternatively, each Z¹⁶can be a hydroxyl group, ethoxy, methoxy or an oxygen atom bonded to a silicon atom of another comonomer; and each Z¹⁷and Z¹⁸independently can be a hydroxyl group, ethoxy, methyl, or an oxygen atom bonded to a silicon atom of another comonomer.

Additionally or alternatively, each Z¹⁶can be a hydroxyl group or an oxygen atom bonded to a silicon atom of another comonomer; and each Z¹⁷and Z¹⁸independently can be a hydroxyl group, methyl, or an oxygen atom bonded to a silicon atom of another comonomer.

Additionally or alternatively, each R²can be a C₁-C₈alkylene group, a C₁-C₇alkylene group, a C₁-C₆alkylene group, a C₁-C₅alkylene group, a C₁-C₄alkylene group, a C₁-C₃alkylene group, a C₁-C₂alkylene group or —CH₂—.

Additionally or alternatively, each R²can be a C₂-C₈alkenylene group, a C₂-C₇alkenylene group, a C₂-C₆alkenylene group, a C₂-C₅alkenylene group, a C₂-C₄alkenylene group, a C₂-C₃alkenylene group, or —HC═CH—.

Additionally or alternatively, each Z¹⁶can be a hydroxyl group, a C₁-C₂alkoxy group or an oxygen atom bonded to a silicon atom of another comonomer; each Z¹⁷and Z¹⁸independently can be a hydroxyl group, a C₁-C₂alkoxy group, a C₁-C₂alkyl group, or an oxygen atom bonded to a silicon atom of another comonomer; and R²can be selected from the group consisting of a C₁-C₄alkylene group and a C₂-C₄alkenylene group.

Additionally or alternatively, each R²can be a C₂-C₈alkynylene group, a C₂-C₇alkynylene group, a C₂-C₆alkynylene group, a C₂-C₅alkynylene group, a C₂-C₄alkynylene group, a C₂-C₃alkynylene group, or —C≡C—.

Additionally or alternatively, each R²can be an optionally substituted C₆-C₂₀aralkyl, an optionally substituted C₆-C₁₄aralkyl, or an optionally substituted C₆-C₁₀aralkyl. Examples of C₆-C₂₀aralkyls include, but are not limited to, phenymethyl, phenylethyl, and naphthylmethyl. The aralkyl may be optionally substituted with a C₁-C₆alkyl group, particularly a C₁-C₄alkyl group.

Additionally or alternatively, each R²can be an optionally substituted C₄-C₂₀heterocycloalkyl group, an optionally substituted C₄-C₁₆heterocycloalkyl group, an optionally substituted C₄-C₁₂heterocycloalkyl group, or an optionally substituted C₄-C₁₀heterocycloalkyl group. Examples of C₄-C₂₀heterocycloalkyl groups include, but are not limited to, thienylmethyl, furylethyl, pyrrolylmethyl, piperazinylethyl, pyridylmethyl, benzoxazolylethyl, quinolinylpropyl, and imidazolylpropyl. The heterocycloalkyl may be optionally substituted with a C₁-C₆alkyl group, particularly a C₁-C₄alkyl group.

Additionally or alternatively, each Z¹⁶can be a hydroxyl group, ethoxy, methoxy or an oxygen atom bonded to a silicon atom of another comonomer; each Z¹⁷and Z¹⁸independently can be a hydroxyl group, ethoxy, methoxy, methyl, or an oxygen atom bonded to a silicon atom of another comonomer; and R²can be selected from the group consisting of —CH₂—, —CH₂CH₂—, and —HC═CH—.

Additionally or alternatively, each Z¹⁶can be a hydroxyl group or an oxygen atom bonded to a silicon atom of another comonomer; each Z¹⁷and Z¹⁸independently can be a hydroxyl group, methyl, or an oxygen atom bonded to a silicon atom of another comonomer; and R²can be selected from the group consisting of —CH₂—, —CH₂CH₂—, and —HC═CH—.

In a particular embodiment, each Z¹⁶can be a hydroxyl group, ethoxy or an oxygen atom bonded to a silicon atom of another comonomer; each Z¹⁷can be a hydroxyl group, ethoxy, and an oxygen atom bonded to a silicon atom of another monomer; each Z¹⁸can be methyl; and R²can be —CH₂CH₂—.

In another particular embodiment, each Z¹⁶can be a hydroxyl group, ethoxy or an oxygen atom bonded to a silicon atom of another comonomer; each Z¹⁷and Z¹⁸independently can be selected from the group consisting of a hydroxyl group, ethoxy, and an oxygen atom bonded to a silicon atom of another monomer; and R²can be —CH₂—.

The organosilica materials made by the methods described herein can be characterized as described in the following sections.

II.A. X-Ray Diffraction Peaks

The organosilica materials described herein can exhibit powder X-ray diffraction patterns with one broad peak between about 1 and about 4 degrees 2θ, particularly one peak between about 1 and about 3 degrees 2θ. In the 0.5 to 12 degrees 2θ range, the organosilica materials can exhibit substantially no peaks. The organosilica materials can exhibit substantially no peaks in the range of about 3 to about 12 degrees 2θ, about 4 to about 12 degrees 2θ, in the range of about 5 to about 12 degrees 2θ, in the range of about 6 to about 12 degrees 2θ, in the range of about 7 to about 12 degrees 2θ, in the range of about 8 to about 12 degrees 2θ, in the range of about 9 to about 12 degrees 2θ, in the range of about 10 to about 12 degrees 2θ, or in the range of about 11 to about 12 degrees 2θ.

II.B. Silanol Content

The organosilica materials obtainable by the method of the invention can have a silanol content that varies within wide limits, depending on the composition of the synthesis solution. The silanol content can conveniently be determined by solid state silicon NMR.

In various aspects, the organosilica material can have a silanol content of greater than about 5%, greater than about 10%, greater than about 15%, greater than about 20%, greater than about 25%, greater than about 30%, greater than about 33%, greater than 35%, greater than about 40%, greater than about 41%, greater than about 44%, greater than about 45%, greater than about 50%, greater than about 55%, greater than about 60%, greater than about 65%, greater than about 70%, greater than about 75%, or about 80%. In certain embodiments, the silanol content can be greater than about 30% or greater than about 41%.

Additionally or alternatively, the organosilica material may have a silanol content of about 5% to about 80%, about 5% to about 75%, about 5% to about 70%, about 5% to about 65%, about 5% to about 60%, about 5% to about 55%, about 5% to about 50%, about 5% to about 45%, about 5% to about 44%, about 5% to about 41%, about 5% to about 40%, about 5% to about 35%, about 5% to about 33%, about 5% to about 30%, about 5% to about 25%, about 5% to about 20%, about 5% to about 15%, about 5% to about 10%, about 10% to about 80%, about 10% to about 75%, about 10% to about 70%, about 10% to about 65%, about 10% to about 60%, about 10% to about 55%, about 10% to about 50%, about 10% to about 45%, about 10% to about 44%, about 10% to about 41%, about 10% to about 40%, about 10% to about 35%, about 10% to about 33%, about 10% to about 30%, about 10% to about 25%, about 10% to about 20%, about 20% to about 80%, about 20% to about 75%, about 20% to about 70%, about 20% to about 65%, about 20% to about 60%, about 20% to about 55%, about 20% to about 50%, about 20% to about 45%, about 20% to about 44%, about 20% to about 41%, about 20% to about 40%, about 20% to about 35%, about 20% to about 33%, about 20% to about 30%, about 20% to about 25%, about 30% to about 80%, about 30% to about 75%, about 30% to about 70%, about 30% to about 65%, about 30% to about 60%, about 30% to about 55%, about 30% to about 50%, about 30% to about 45%, about 30% to about 44%, about 30% to about 41%, about 30% to about 40%, about 30% to about 35%, about 30% to about 33%, about 40% to about 80%, about 40% to about 75%, about 40% to about 70%, about 40% to about 65%, about 40% to about 60%, about 40% to about 55%, about 40% to about 50%, about 40% to about 45%, about 40% to about 44%, or about 40% to about 41%.

II.C. Pore Size

The organosilica material described herein are advantageously in a mesoporous form. As indicated previously, the term mesoporous refers to solid materials having pores with a diameter within the range of from about 2 nm to about 50 nm. The average pore diameter of the organosilica material can be determined, for example, using nitrogen adsorption-desorption isotherm techniques within the expertise of one of skill in the art, such as the BET (Brunauer Emmet Teller) method.

The organosilica material can have an average pore diameter of about 0.2 nm, about 0.4 nm, about 0.5 nm, about 0.6 nm, about 0.8 nm, about 1.0 nm, about 1.5 nm, about 1.8 nm or less than about 2.0 nm.

Additionally or alternatively, the organosilica material can advantageously have an average pore diameter within the mesopore range of about 2.0 nm, about 2.5 nm, about 3.0 nm, about 3.1 nm, about 3.2 nm, about 3.3 nm, about 3.4 nm, about 3.5 nm, about 3.6 nm, about 3.7 nm, about 3.8 nm, about 3.9 nm about 4.0 nm, about 4.1 nm, about 4.5 nm, about 5.0 nm, about 6.0 nm, about 7.0 nm, about 7.3 nm, about 8 nm, about 8.4 nm, about 9 nm, about 10 nm, about 11 nm, about 13 nm, about 15 nm, about 18 nm, about 20 nm, about 23 nm, about 25 nm, about 30 nm, about 40 nm, about 45 nm, or about 50 nm.

Additionally or alternatively, the organosilica material can have an average pore diameter of 0.2 nm to about 50 nm, about 0.2 nm to about 40 nm, about 0.2 nm to about 30 nm, about 0.2 nm to about 25 nm, about 0.2 nm to about 23 nm, about 0.2 nm to about 20 nm, about 0.2 nm to about 18 nm, about 0.2 nm to about 15 nm, about 0.2 nm to about 13 nm, about 0.2 nm to about 11 nm, about 0.2 nm to about 10 nm, about 0.2 nm to about 9 nm, about 0.2 nm to about 8.4 nm, about 0.2 nm to about 8 nm, about 0.2 nm to about 7.3 nm, about 0.2 nm to about 7.0 nm, about 0.2 nm to about 6.0 nm, about 0.2 nm to about 5.0 nm, about 0.2 nm to about 4.5 nm, about 0.2 nm to about 4.1 nm, about 0.2 nm to about 4.0 nm, about 0.2 nm to about 3.9 nm, about 0.2 nm to about 3.8 nm, about 0.2 nm to about 3.7 nm, about 0.2 nm to about 3.6 nm, about 0.2 nm to about 3.5 nm, about 0.2 nm to about 3.4 nm, about 0.2 nm to about 3.3 nm, about 0.2 nm to about 3.2 nm, about 0.2 nm to about 3.1 nm, about 0.2 nm to about 3.0 nm, about 0.2 nm to about 2.5 nm, about 0.2 nm to about 2.0 nm, about 0.2 nm to about 1.0 nm, about 1.0 nm to about 50 nm, about 1.0 nm to about 40 nm, about 1.0 nm to about 30 nm, about 1.0 nm to about 25 nm, about 1.0 nm to about 23 nm, about 1.0 nm to about 20 nm, about 1.0 nm to about 18 nm, about 1.0 nm to about 15 nm, about 1.0 nm to about 13 nm, about 1.0 nm to about 11 nm, about 1.0 nm to about 10 nm, about 1.0 nm to about 9 nm, about 1.0 nm to about 8.4 nm, about 1.0 nm to about 8 nm, about 1.0 nm to about 7.3 nm, about 1.0 nm to about 7.0 nm, about 1.0 nm to about 6.0 nm, about 1.0 nm to about 5.0 nm, about 1.0 nm to about 4.5 nm, about 1.0 nm to about 4.1 nm, about 1.0 nm to about 4.0 nm, about 1.0 nm to about 3.9 nm, about 1.0 nm to about 3.8 nm, about 1.0 nm to about 3.7 nm, about 1.0 nm to about 3.6 nm, about 1.0 nm to about 3.5 nm, about 1.0 nm to about 3.4 nm, about 1.0 nm to about 3.3 nm, about 1.0 nm to about 3.2 nm, about 1.0 nm to about 3.1 nm, about 1.0 nm to about 3.0 nm or about 1.0 nm to about 2.5 nm.

In particular, the organosilica material can advantageously have an average pore diameter in the mesopore range of about 2.0 nm to about 50 nm, about 2.0 nm to about 40 nm, about 2.0 nm to about 30 nm, about 2.0 nm to about 25 nm, about 2.0 nm to about 23 nm, about 2.0 nm to about 20 nm, about 2.0 nm to about 18 nm, about 2.0 nm to about 15 nm, about 2.0 nm to about 13 nm, about 2.0 nm to about 11 nm, about 2.0 nm to about 10 nm, about 2.0 nm to about 9 nm, about 2.0 nm to about 8.4 nm, about 2.0 nm to about 8 nm, about 2.0 nm to about 7.3 nm, about 2.0 nm to about 7.0 nm, about 2.0 nm to about 6.0 nm, about 2.0 nm to about 5.0 nm, about 2.0 nm to about 4.5 nm, about 2.0 nm to about 4.1 nm, about 2.0 nm to about 4.0 nm, about 2.0 nm to about 3.9 nm, about 2.0 nm to about 3.8 nm, about 2.0 nm to about 3.7 nm, about 2.0 nm to about 3.6 nm, about 2.0 nm to about 3.5 nm, about 2.0 nm to about 3.4 nm, about 2.0 nm to about 3.3 nm, about 2.0 nm to about 3.2 nm, about 2.0 nm to about 3.1 nm, about 2.0 nm to about 3.0 nm, about 2.0 nm to about 2.5 nm, about 2.5 nm to about 50 nm, about 2.5 nm to about 40 nm, about 2.5 nm to about 30 nm, about 2.5 nm to about 25 nm, about 2.5 nm to about 23 nm, about 2.5 nm to about 20 nm, about 2.5 nm to about 18 nm, about 2.5 nm to about 15 nm, about 2.5 nm to about 13 nm, about 2.5 nm to about 11 nm, about 2.5 nm to about 10 nm, about 2.5 nm to about 9 nm, about 2.5 nm to about 8.4 nm, about 2.5 nm to about 8 nm, about 2.5 nm to about 7.3 nm, about 2.5 nm to about 7.0 nm, about 2.5 nm to about 6.0 nm, about 2.5 nm to about 5.0 nm, about 2.5 nm to about 4.5 nm, about 2.5 nm to about 4.1 nm, about 2.5 nm to about 4.0 nm, about 2.5 nm to about 3.9 nm, about 2.5 nm to about 3.8 nm, about 2.5 nm to about 3.7 nm, about 2.5 nm to about 3.6 nm, about 2.5 nm to about 3.5 nm, about 2.5 nm to about 3.4 nm, about 2.5 nm to about 3.3 nm, about 2.5 nm to about 3.2 nm, about 2.5 nm to about 3.1 nm, about 2.5 nm to about 3.0 nm, about 3.0 nm to about 50 nm, about 3.0 nm to about 40 nm, about 3.0 nm to about 30 nm, about 3.0 nm to about 25 nm, about 3.0 nm to about 23 nm, about 3.0 nm to about 20 nm, about 3.0 nm to about 18 nm, about 3.0 nm to about 15 nm, about 3.0 nm to about 13 nm, about 3.0 nm to about 11 nm, about 3.0 nm to about 10 nm, about 3.0 nm to about 9 nm, about 3.0 nm to about 8.4 nm, about 3.0 nm to about 8 nm, about 3.0 nm to about 7.3 nm, about 3.0 nm to about 7.0 nm, about 3.0 nm to about 6.0 nm, about 3.0 nm to about 5.0 nm, about 3.0 nm to about 4.5 nm, about 3.0 nm to about 4.1 nm, or about 3.0 nm to about 4.0 nm.

In one particular embodiment, the organosilica material described herein can have an average pore diameter of about 1.0 nm to about 30.0 nm, particularly about 1.0 nm to about 25.0 nm, particularly about 2.0 nm to about 25.0 nm, particularly about 2.0 nm to about 20.0 nm, particularly about 2.0 nm to about 15.0 nm, particularly about 2.0 nm to about 10.0 nm, or particularly about 3.0 nm to about 10.0 nm.

Using surfactant as a template to synthesize mesoporous materials can create highly ordered structure, e.g. well-defined cylindrical-like pore channels. In some circumstances, there may be no hysteresis loop observed from N₂adsorption isotherm. In other circumstances, for instance where mesoporous materials can have less ordered pore structures, a hysteresis loop may be observed from N2 adsorption isotherm experiments. In such circumstances, without being bound by theory, the hysteresis can result from the lack of regularity in the pore shapes/sizes and/or from bottleneck constrictions in such irregular pores.

II.D. Surface Area

The surface area of the organosilica material can be determined, for example, using nitrogen adsorption-desorption isotherm techniques within the expertise of one of skill in the art, such as the BET (Brunauer Emmet Teller) method. This method may determine a total surface area, an external surface area, and a microporous surface area. As used herein, and unless otherwise specified, “total surface area” refers to the total surface area as determined by the BET method. As used herein, and unless otherwise specified, “microporous surface area” refers to microporous surface are as determined by the BET method.

In various embodiments, the organosilica material can have a total surface area greater than or equal to about 100 m²/g, greater than or equal to about 200 m²/g, greater than or equal to about 300 m²/g, greater than or equal to about 400 m²/g, greater than or equal to about 450 m²/g, greater than or equal to about 500 m²/g, greater than or equal to about 550 m²/g, greater than or equal to about 600 m²/g, greater than or equal to about 700 m²/g, greater than or equal to about 800 m²/g, greater than or equal to about 850 m²/g, greater than or equal to about 900 m²/g, greater than or equal to about 1,000 m²/g, greater than or equal to about 1,050 m²/g, greater than or equal to about 1,100 m²/g, greater than or equal to about 1,150 m²/g, greater than or equal to about 1,200 m²/g, greater than or equal to about 1,250 m²/g, greater than or equal to about 1,300 m²/g, greater than or equal to about 1,400 m²/g, greater than or equal to about 1,450 m²/g, greater than or equal to about 1,500 m²/g, greater than or equal to about 1,550 m²/g, greater than or equal to about 1,600 m²/g, greater than or equal to about 1,700 m²/g, greater than or equal to about 1,800 m²/g, greater than or equal to about 1,900 m²/g, greater than or equal to about 2,000 m²/g, greater than or equal to greater than or equal to about 2,100 m²/g, greater than or equal to about 2,200 m²/g, greater than or equal to about 2,300 m²/g or about 2,500 m²/g.

Additionally or alternatively, the organosilica material may have a total surface area of about 50 m²/g to about 2,500 m²/g, about 50 m²/g to about 2,000 m²/g, about 50 m²/g to about 1,500 m²/g, about 50 m²/g to about 1,000 m²/g, about 100 m²/g to about 2,500 m²/g, about 100 m²/g to about 2,300 m²/g, about 100 m²/g to about 2,200 m²/g, about 100 m²/g to about 2,100 m²/g, about 100 m²/g to about 2,000 m²/g, about 100 m²/g to about 1,900 m²/g, about 100 m²/g to about 1,800 m²/g, about 100 m²/g to about 1,700 m²/g, about 100 m²/g to about 1,600 m²/g, about 100 m²/g to about 1,550 m²/g, about 100 m²/g to about 1,500 m²/g, about 100 m²/g to about 1,450 m²/g, about 100 m²/g to about 1,400 m²/g, about 100 m²/g to about 1,300 m²/g, about 100 m²/g to about 1,250 m²/g, about 100 m²/g to about 1,200 m²/g, about 100 m²/g to about 1,150 m²/g, about 100 m²/g to about 1,100 m²/g, about 100 m²/g to about 1,050 m²/g, about 100 m²/g to about 1,000 m²/g, about 100 m²/g to about 900 m²/g, about 100 m²/g to about 850 m²/g, about 100 m²/g to about 800 m²/g, about 100 m²/g to about 700 m²/g, about 100 m²/g to about 600 m²/g, about 100 m²/g to about 550 m²/g, about 100 m²/g to about 500 m²/g, about 100 m²/g to about 450 m²/g, about 100 m²/g to about 400 m²/g, about 100 m²/g to about 300 m²/g, about 100 m²/g to about 200 m²/g, about 200 m²/g to about 2,500 m²/g, about 200 m²/g to about 2,300 m²/g, about 200 m²/g to about 2,200 m²/g, about 200 m²/g to about 2,100 m²/g, about 200 m²/g to about 2,000 m²/g, about 200 m²/g to about 1,900 m²/g, about 200 m²/g to about 1,800 m²/g, about 200 m²/g to about 1,700 m²/g, about 200 m²/g to about 1,600 m²/g, about 200 m²/g to about 1,550 m²/g, about 200 m²/g to about 1,500 m²/g, about 200 m²/g to about 1,450 m²/g, about 200 m²/g to about 1,400 m²/g, about 200 m²/g to about 1,300 m²/g, about 200 m²/g to about 1,250 m²/g, about 200 m²/g to about 1,200 m²/g, about 200 m²/g to about 1,150 m²/g, about 200 m²/g to about 1,100 m²/g, about 200 m²/g to about 1,050 m²/g, about 200 m²/g to about 1,000 m²/g, about 200 m²/g to about 900 m²/g, about 200 m²/g to about 850 m²/g, about 200 m²/g to about 800 m²/g, about 200 m²/g to about 700 m²/g, about 200 m²/g to about 600 m²/g, about 200 m²/g to about 550 m²/g, about 200 m²/g to about 500 m²/g, about 200 m²/g to about 450 m²/g, about 200 m²/g to about 400 m²/g, about 200 m²/g to about 300 m²/g, about 500 m²/g to about 2,500 m²/g, about 500 m²/g to about 2,300 m²/g, about 500 m²/g to about 2,200 m²/g, about 500 m²/g to about 2,100 m²/g, about 500 m²/g to about 2,000 m²/g, about 500 m²/g to about 1,900 m²/g, about 500 m²/g to about 1,800 m²/g, about 500 m²/g to about 1,700 m²/g, about 500 m²/g to about 1,600 m²/g, about 500 m²/g to about 1,550 m²/g, about 500 m²/g to about 1,500 m²/g, about 500 m²/g to about 1,450 m²/g, about 500 m²/g to about 1,400 m²/g, about 500 m²/g to about, 300 m²/g, about 500 m²/g to about 1,250 m²/g, about 500 m²/g to about 1,200 m²/g, about 500 m²/g to about 1,150 m²/g, about 500 m²/g to about 1,100 m²/g, about 500 m²/g to about 1,050 m²/g, about 500 m²/g to about 1,000 m²/g, about 500 m²/g to about 900 m²/g, about 500 m²/g to about 850 m²/g, about 500 m²/g to about 800 m²/g, about 500 m²/g to about 700 m²/g, about 500 m²/g to about 600 m²/g, about 500 m²/g to about 550 m²/g, about 1,000 m²/g to about 2,500 m²/g, about 1,000 m²/g to about 2,300 m²/g, about 1,000 m²/g to about 2,200 m²/g, about 1,000 m²/g to about 2,100 m²/g, about 1,000 m²/g to about 2,000 m²/g, about 1,000 m²/g to about 1,900 m²/g, about 1,000 m²/g to about 1,800 m²/g, about 1,000 m²/g to about 1,700 m²/g, about 1,000 m²/g to about 1,600 m²/g, about 1,000 m²/g to about 1,550 m²/g, about 1,000 m²/g to about 1,500 m²/g, about 1,000 m²/g to about 1,450 m²/g, about 1,000 m²/g to about 1,400 m²/g, about 1,000 m²/g to about 1,300 m²/g, about 1,000 m²/g to about 1,250 m²/g, about 1,000 m²/g to about 1,200 m²/g, about 1,000 m²/g to about 1,150 m²/g, about 1,000 m²/g to about 1,100 m²/g, or about 1,000 m²/g to about 1,050 m²/g.

In one particular embodiment, the organosilica material described herein may have a total surface area of about 200 m²/g to about 2,500 m²g, particularly about 400 m²/g to about 2,500 m²g, particularly about 400 m²/g to about 2,000 m²/g, particularly about 500 m²/g to about 2,000 m²/g, or particularly about 400 m²/g to about 1,500 m²/g.

III.E. Pore Volume

The pore volume of the organosilica material made by the methods described herein can be determined, for example, using nitrogen adsorption-desorption isotherm techniques within the expertise of one of skill in the art, such as the BET (Brunauer Emmet Teller) method.

In various embodiments, the organosilica material can have a pore volume greater than or equal to about 0.1 cm³/g, greater than or equal to about 0.2 cm³/g, greater than or equal to about 0.3 cm³/g, greater than or equal to about 0.4 cm³/g, greater than or equal to about 0.5 cm³/g, greater than or equal to about 0.6 cm³/g, greater than or equal to about 0.7 cm³/g, greater than or equal to about 0.8 cm³/g, greater than or equal to about 0.9 cm³/g, greater than or equal to about 1.0 cm³/g, greater than or equal to about 1.1 cm³/g, greater than or equal to about 1.2 cm³/g, greater than or equal to about 1.3 cm³/g, greater than or equal to about 1.4 cm³/g, greater than or equal to about 1.5 cm³/g, greater than or equal to about 1.6 cm³/g, greater than or equal to about 1.7 cm³/g, greater than or equal to about 1.8 cm³/g, greater than or equal to about 1.9 cm³/g, greater than or equal to about 2.0 cm³/g, greater than or equal to about 2.5 cm³/g, greater than or equal to about 3.0 cm³/g, greater than or equal to about 3.5 cm³/g, greater than or equal to about 4.0 cm³/g, greater than or equal to about 5.0 cm³/g, greater than or equal to about 6.0 cm³/g, greater than or equal to about 7.0 cm³/g, or about 10.0 cm³/g.

Additionally or alternatively, the organosilica material can have a pore volume of about 0.1 cm³/g to about 10.0 cm³/g, about 0.1 cm³/g to about 7.0 cm³/g, about 0.1 cm³/g to about 6.0 cm³/g, about 0.1 cm³/g to about 5.0 cm³/g, about 0.1 cm³/g to about 4.0 cm³/g, about 0.1 cm³/g to about 3.5 cm³/g, about 0.1 cm³/g to about 3.0 cm³/g, about 0.1 cm³/g to about 2.5 cm³/g, about 0.1 cm³/g to about 2.0 cm³/g, about 0.1 cm³/g to about 1.9 cm³/g, about 0.1 cm³/g to about 1.8 cm³/g, about 0.1 cm³/g to about 1.7 cm³/g, about 0.1 cm³/g to about 1.6 cm³/g, about 0.1 cm³/g to about 1.5 cm³/g, about 0.1 cm³/g to about 1.4 cm³/g, about 0.1 cm³/g to about 1.3 cm³/g, about 0.1 cm³/g to about 1.2 cm³/g, about 0.1 cm³/g to about 1.1, about 0.1 cm³/g to about 1.0 cm³/g, about 0.1 cm³/g to about 0.9 cm³/g, about 0.1 cm³/g to about 0.8 cm³/g, about 0.1 cm³/g to about 0.7 cm³/g, about 0.1 cm³/g to about 0.6 cm³/g, about 0.1 cm³/g to about 0.5 cm³/g, about 0.1 cm³/g to about 0.4 cm³/g, about 0.1 cm³/g to about 0.3 cm³/g, about 0.1 cm³/g to about 0.2 cm³/g, 0.2 cm³/g to about 10.0 cm³/g, about 0.2 cm³/g to about 7.0 cm³/g, about 0.2 cm³/g to about 6.0 cm³/g, about 0.2 cm³/g to about 5.0 cm³/g, about 0.2 cm³/g to about 4.0 cm³/g, about 0.2 cm³/g to about 3.5 cm³/g, about 0.2 cm³/g to about 3.0 cm³/g, about 0.2 cm³/g to about 2.5 cm³/g, about 0.2 cm³/g to about 2.0 cm³/g, about 0.2 cm³/g to about 1.9 cm³/g, about 0.2 cm³/g to about 1.8 cm³/g, about 0.2 cm³/g to about 1.7 cm³/g, about 0.2 cm³/g to about 1.6 cm³/g, about 0.2 cm³/g to about 1.5 cm³/g, about 0.2 cm³/g to about 1.4 cm³/g, about 0.2 cm³/g to about 1.3 cm³/g, about 0.2 cm³/g to about 1.2 cm³/g, about 0.2 cm³/g to about 1.1, about 0.5 cm³/g to about 1.0 cm³/g, about 0.5 cm³/g to about 0.9 cm³/g, about 0.5 cm³/g to about 0.8 cm³/g, about 0.5 cm³/g to about 0.7 cm³/g, about 0.5 cm³/g to about 0.6 cm³/g, about 0.5 cm³/g to about 0.5 cm³/g, about 0.5 cm³/g to about 0.4 cm³/g, about 0.5 cm³/g to about 0.3 cm³/g, 0.5 cm³/g to about 10.0 cm³/g, about 0.5 cm³/g to about 7.0 cm³/g, about 0.5 cm³/g to about 6.0 cm³/g, about 0.5 cm³/g to about 5.0 cm³/g, about 0.5 cm³/g to about 4.0 cm³/g, about 0.5 cm³/g to about 3.5 cm³/g, about 0.5 cm³/g to about 3.0 cm³/g, about 0.5 cm³/g to about 2.5 cm³/g, about 0.5 cm³/g to about 2.0 cm³/g, about 0.5 cm³/g to about 1.9 cm³/g, about 0.5 cm³/g to about 1.8 cm³/g, about 0.5 cm³/g to about 1.7 cm³/g, about 0.5 cm³/g to about 1.6 cm³/g, about 0.5 cm³/g to about 1.5 cm³/g, about 0.5 cm³/g to about 1.4 cm³/g, about 0.5 cm³/g to about 1.3 cm³/g, about 0.5 cm³/g to about 1.2 cm³/g, about 0.5 cm³/g to about 1.1, about 0.5 cm³/g to about 1.0 cm³/g, about 0.5 cm³/g to about 0.9 cm³/g, about 0.5 cm³/g to about 0.8 cm³/g, about 0.5 cm³/g to about 0.7 cm³/g, or about 0.5 cm³/g to about 0.6 cm³/g.

In a particular embodiment, the organosilica material can have a pore volume of about 0.1 cm³/g to about 5.0 cm³/g, particularly about 0.1 cm³/g to about 3.0 cm³/g, particularly about 0.2 cm³/g to about 3.0 cm³/g, particularly about 0.2 cm³/g to about 2.5 cm³/g, or particularly about 0.2 cm³/g to about 1.5 cm³/g.

III.F. Additional Metals

In some embodiments, the organosilica material can further comprise at least one catalyst metal incorporated within the pores of the organosilica material. Exemplary catalyst metals can include, but are not limited to, a Group 6 element, a Group 8 element, a Group 9 element, a Group 10 element or a combination thereof. Exemplary Group 6 elements can include, but are not limited to, chromium, molybdenum, and/or tungsten, particularly including molybdenum and/or tungsten. Exemplary Group 8 elements can include, but are not limited to, iron, ruthenium, and/or osmium. Exemplary Group 9 elements can include, but are not limited to, cobalt, rhodium, and/or iridium, particularly including cobalt. Exemplary Group 10 elements can include, but are not limited to, nickel, palladium and/or platinum.

The catalyst metal can be incorporated into the organosilica material by any convenient method, such as by impregnation, by ion exchange, or by complexation to surface sites. The catalyst metal so incorporated may be employed to promote any one of a number of catalytic tranformations commonly conducted in petroleum refining or petrochemicals production. Examples of such catalytic processes can include, but are not limited to, hydrogenation, dehydrogenation, aromatization, aromatic saturation, hydrodesulfurization, olefin oligomerization, polymerization, hydrodenitrogenation, hydrocracking, naphtha reforming, paraffin isomerization, aromatic transalkylation, saturation of double/triple bonds, and the like, as well as combinations thereof.

Thus, in another embodiment, a catalyst material comprising the organosilica material described herein is provided. The catalyst material may optionally comprise a binder or be self-bound. Suitable binders, include but are not limited to active and inactive materials, synthetic or naturally occurring zeolites, as well as inorganic materials such as clays and/or oxides such as silica, alumina, zirconia, titania, silica-alumina, cerium oxide, magnesium oxide, or combinations thereof. In particular, the binder may be silica-alumina, alumina and/or a zeolite, particularly alumina. Silica-alumina may be either naturally occurring or in the form of gelatinous precipitates or gels including mixtures of silica and metal oxides. It should be noted it is recognized herein that the use of a material in conjunction with a zeolite binder material, i.e., combined therewith or present during its synthesis, which itself is catalytically active may change the conversion and/or selectivity of the finished catalyst. It is also recognized herein that inactive materials can suitably serve as diluents to control the amount of conversion if the present invention is employed in alkylation processes so that alkylation products can be obtained economically and orderly without employing other means for controlling the rate of reaction. These inactive materials may be incorporated into naturally occurring clays, e.g., bentonite and kaolin, to improve the crush strength of the catalyst under commercial operating conditions and function as binders or matrices for the catalyst. The catalysts described herein typically can comprise, in a composited form, a ratio of support material to binder material of about 100 parts support material to about zero parts binder material; about 99 parts support material to about 1 parts binder material; about 95 parts support material to about 5 parts binder material. Additionally or alternatively, the catalysts described herein typically can comprise, in a composited form, a ratio of support material to binder material ranging from about 90 parts support material to about 10 parts binder material to about 10 parts support material to about 90 parts binder material; about 85 parts support material to about 15 parts binder material to about 15 parts support material to about 85 parts binder material; about 80 parts support material to 20 parts binder material to 20 parts support material to 80 parts binder material, all ratios being by weight, typically from 80:20 to 50:50 support material:binder material, preferably from 65:35 to 35:65. Compositing may be done by conventional means including mulling the materials together followed by extrusion of pelletizing into the desired finished catalyst particles.

In some embodiments, the organosilica material can further comprise cationic metal sites incorporated into the network structure. Such cationic metal sites may be incorporated by any convenient method, such as impregnation or complexation to the surface, through an organic precursor, or by some other method. This organometallic material may be employed in a number of hydrocarbon separations conducted in petroleum refining or petrochemicals production. Examples of such compounds to be desirably separated from petrochemicals/fuels can include olefins, paraffins, aromatics, and the like.

Additionally or alternatively, the organosilica material can further comprise a surface metal incorporated within the pores of the organosilica material. The surface metal can be selected from a Group 1 element, a Group 2 element, a Group 13 element, and a combination thereof. When a Group 1 element is present, it can preferably comprise or be sodium and/or potassium. When a Group 2 element is present, it can include, but may not be limited to, magnesium and/or calcium. When a Group 13 element is present, it can include, but may not be limited to, boron and/or aluminum.

One or more of the Group 1, 2, 6, 8-10 and/or 13 elements may be present on an exterior and/or interior surface of the organosilica material. For example, one or more of the Group 1, 2 and/or 13 elements may be present in a first layer on the organosilica material and one or more of the Group 6, 8, 9 and/or 10 elements may be present in a second layer, e.g., at least partially atop the Group 1, 2 and/or 13 elements. Additionally or alternatively, only one or more Group 6, 8, 9 and/or 10 elements may present on an exterior and/or interior surface of the organosilica material. The surface metal(s) can be incorporated into/onto the organosilica material by any convenient method, such as by impregnation, deposition, grafting, co-condensation, by ion exchange, and/or the like.

III. METHODS OF MAKING ORGANOSILICA MATERIALS

In another embodiment, methods of producing the organosilica material described herein are provided. The method comprises:

(a) providing an aqueous mixture that contains essentially no structure directing agent and/or porogen;

(b) adding at least one compound of Formula [R¹R²SiCH₂]₃(Ia) into the aqueous mixture to form a solution, wherein each R¹represents a C₁-C₄alkoxy group and R²represents a C₁-C₄alkoxy group or a C₁-C₄alkyl group;

- (i) a compound of Formula R³OR⁴R⁵R⁶Si (IIa) wherein each R³can be a C₁-C₆alkyl group, and R⁴, R⁵and R⁶each independently can be selected from the group consisting of a C₁-C₆alkyl group, a C₁-C₆alkoxy group, a nitrogen-containing C₁-C₁₀alkyl group, a nitrogen-containing heteroaralkyl group, and a nitrogen-containing optionally substituted heterocycloalkyl group;
- (ii) a compound of Formula Z¹⁹Z²⁰Z²¹Si—R⁷—Si Z¹⁹Z²⁰Z²¹(IIIa), wherein each Z¹⁹independently can be a C₁-C₄alkoxy group; Z²⁰and Z²¹each independently can be a C₁-C₄alkoxy group or a C₁-C₄alkyl group; and R⁷can be selected from the group consisting a C₁-C₈alkylene group, a C₂-C₈alkenylene group, a C₂-C₈alkynylene group, a nitrogen-containing C₂-C₁₀alkylene group, an optionally substituted C₆-C₂₀aralkyl group, and an optionally substituted C₄-C₂₀heterocycloalkyl group; or
- (iii) a combination thereof;

(d) aging the solution to produce a pre-product; and

(e) drying the pre-product to obtain an organosilica material which is a polymer comprising at least one independent monomer of Formula (I) as described herein and at least one independent unit of Formulas (II), (III), (IV), (V) and/or (VI) as described herein.

III.A. Aqueous Mixture

The organosilica materials described herein may be made using essentially no structure directing agent or porogen. Thus, the aqueous mixture contains essentially no added structure directing agent and/or no added porogen.

As used herein, “no added structure directing agent,” and “no added porogen” means either (i) there is no component present in the synthesis of the organosilica material that aids in and/or guides the polymerization and/or polycondensing and/or organization of the building blocks that form the framework of the organosilica material; or (ii) such component is present in the synthesis of the organosilica material in a minor, or a non-substantial, or a negligible amount such that the component cannot be said to aid in and/or guide the polymerization and/or polycondensing and/or organization of the building blocks that form the framework of the organosilica material. Further, “no added structure directing agent” is synonymous with “no added template” and “no added templating agent.”

1. Structure Directing Agent

Examples of a structure directing agent can include, but are not limited to, non-ionic surfactants, ionic surfactants, cationic surfactants, silicon surfactants, amphoteric surfactants, polyalkylene oxide surfactants, fluorosurfactants, colloidal crystals, polymers, hyper branched molecules, star-shaped molecules, macromolecules, dendrimers, and combinations thereof. Additionally or alternatively, the surface directing agent can comprise or be a poloxamer, a triblock polymer, a tetraalkylammonium salt, a nonionic polyoxyethylene alkyl, a Gemini surfactant, or a mixture thereof. Examples of a tetraalkylammonium salt can include, but are not limited to, cetyltrimethylammonium halides, such as cetyltrimethylammonium chloride (CTAC), cetyltrimethylammonium bromide (CTAB), and octadecyltrimethylammonium chloride. Other exemplary surface directing agents can additionally or alternatively include hexadecyltrimethylammonium chloride and/or cetylpyridinium bromide.

Poloxamers are block copolymers of ethylene oxide and propylene oxide, more particularly nonionic triblock copolymers composed of a central hydrophobic chain of polyoxypropylene (poly(propylene oxide)) flanked by two hydrophilic chains of polyoxyethylene (poly(ethylene oxide)). Specifically, the term “poloxamer” refers to a polymer having the formula HO(C₂H₄))a(C₃H₆O)_b(C₂H₄O)_aH in which “a” and “b” denote the number of polyoxyethylene and polyoxypropylene units, respectively. Poloxamers are also known by the trade name Pluronic®, for example Pluronic® 123 and Pluronic®F127. An additional triblock polymer is B50-6600.

Nonionic polyoxyethylene alkyl ethers are known by the trade name Brij®, for example Brij® 56, Brij® 58, Brij® 76, Brij® 78. Gemini surfactants are compounds having at least two hydrophobic groups and at least one or optionally two hydrophilic groups per molecule have been introduced.

2. Porogen

A porogen material is capable of forming domains, discrete regions, voids and/or pores in the organosilica material. An example of a porogen is a block copolymer (e.g., a di-block polymer). As used herein, porogen does not include water. Examples of polymer porogens can include, but are not limited to, polyvinyl aromatics, such as polystyrenes, polyvinylpyridines, hydrogenated polyvinyl aromatics, polyacrylonitriles, polyalkylene oxides, such as polyethylene oxides and polypropylene oxides, polyethylenes, polylactic acids, polysiloxanes, polycaprolactones, polycaprolactams, polyurethanes, polymethacrylates, such as polymethylmethacrylate or polymethacrylic acid, polyacrylates, such as polymethylacrylate and polyacrylic acid, polydienes such as polybutadienes and polyisoprenes, polyvinyl chlorides, polyacetals, and amine-capped alkylene oxides, as well as combinations thereof.

Additionally or alternatively, porogens can be thermoplastic homopolymers and random (as opposed to block) copolymers. As used herein, “homopolymer” means compounds comprising repeating units from a single monomer. Suitable thermoplastic materials can include, but are not limited to, homopolymers or copolymers of polystyrenes, polyacrylates, polymethacrylates, polybutadienes, polyisoprenes, polyphenylene oxides, polypropylene oxides, polyethylene oxides, poly(dimethylsiloxanes), polytetrahydrofurans, polyethylenes, polycyclohexylethylenes, polyethyloxazolines, polyvinylpyridines, polycaprolactones, polylactic acids, copolymers of these materials and mixtures of these materials. Examples of polystyrene include, but are not limited to anionic polymerized polystyrene, syndiotactic polystyrene, unsubstituted and substituted polystyrenes (for example, poly(α-methyl styrene)). The thermoplastic materials may be linear, branched, hyperbranched, dendritic, or star like in nature.

Additionally or alternatively, the porogen can be a solvent. Examples of solvents can include, but are not limited to, ketones (e.g., cyclohexanone, cyclopentanone, 2-heptanone, cycloheptanone, cyclooctanone, cyclohexylpyrrolidinone, methyl isobutyl ketone, methyl ethyl ketone, acetone), carbonate compounds (e.g., ethylene carbonate, propylene carbonate), heterocyclic compounds (e.g., 3-methyl-2-oxazolidinone, dimethylimidazolidinone, N-methylpyrrolidone, pyridine), cyclic ethers (e.g., dioxane, tetrahydrofuran), chain ethers (e.g., diethyl ether, ethylene glycol dimethyl ether, propylene glycol dimethyl ether, tetraethylene glycol dimethyl ether, polyethylene glycol dimethyl ether, ethylene glycol monomethyl ether, ethylene glycol monoethyl ether, propylene glycol monomethyl ether (PGME), triethylene glycol monobutyl ether, propylene glycol monopropyl ether, triethylene glycol monomethyl ether, diethylene glycol ethyl ether, diethylene glycol methyl ether, dipropylene glycol methyl ether, dipropylene glycol dimethyl ether, propylene glycol phenyl ether, tripropylene glycol methyl ether), alcohols (e.g., methanol, ethanol), polyhydric alcohols (e.g., ethylene glycol, propylene glycol, polyethylene glycol, polypropylene glycol, glycerin, dipropylene glycol), nitrile compounds (e.g., acetonitrile, glutarodinitrile, methoxyacetonitrile, propionitrile, benzonitrile), esters (e.g., ethyl acetate, butyl acetate, methyl lactate, ethyl lactate, methyl methoxypropionate, ethyl ethoxypropionate, methyl pyruvate, ethyl pyruvate, propyl pyruvate, 2-methoxyethyl acetate, ethylene glycol monoethyl ether acetate, propylene glycol monomethyl ether acetate (PGMEA), butyrolactone, phosphoric acid ester, phosphonic acid ester), aprotic polar substances (e.g., dimethyl sulfoxide, sulfolane, dimethylformamide, dimethylacetamide), nonpolar solvents (e.g., toluene, xylene, mesitylene), chlorine-based solvents (e.g., methylene dichloride, ethylene dichloride), benzene, dichlorobenzene, naphthalene, diphenyl ether, diisopropylbenzene, triethylamine, methyl benzoate, ethyl benzoate, butyl benzoate, monomethyl ether acetate hydroxy ethers such as dibenzylethers, diglyme, triglyme, and mixtures thereof.

3. Base/Acid

In various embodiments, the aqueous mixture used in methods provided herein can comprise a base and/or an acid.

In certain embodiments where the aqueous mixture comprises a base, the aqueous mixture can have a pH from about 8 to about 15, from about 8 to about 14.5, from about 8 to about 14, from about 8 to about 13.5, from about 8 to about 13, from about 8 to about 12.5, from about 8 to about 12, from about 8 to about 11.5, from about 8 to about 11, from about 8 to about 10.5, from about 8 to about 10, from about 8 to about 9.5, from about 8 to about 9, from about 8 to about 8.5, from about 8.5 to about 15, from about 8.5 to about 14.5, from about 8.5 to about 14, from about 8.5 to about 13.5, from about 8.5 to about 13, from about 8.5 to about 12.5, from about 8.5 to about 12, from about 8.5 to about 11.5, from about 8.5 to about 11, from about 8.5 to about 10.5, from about 8.5 to about 10, from about 8.5 to about 9.5, from about 8.5 to about 9, from about 9 to about 15, from about 9 to about 14.5, from about 9 to about 14, from about 9 to about 13.5, from about 9 to about 13, from about 9 to about 12.5, from about 9 to about 12, from about 9 to about 11.5, from about 9 to about 11, from about 9 to about 10.5, from about 9 to about 10, from about 9 to about 9.5, from about 9.5 to about 15, from about 9.5 to about 14.5, from about 9.5 to about 14, from about 9.5 to about 13.5, from about 9.5 to about 13, from about 9.5 to about 12.5, from about 9.5 to about 12, from about 9.5 to about 11.5, from about 9.5 to about 11, from about 9.5 to about 10.5, from about 9.5 to about 10, from about 10 to about 15, from about 10 to about 14.5, from about 10 to about 14, from about 10 to about 13.5, from about 10 to about 13, from about 10 to about 12.5, from about 10 to about 12, from about 10 to about 11.5, from about 10 to about 11, from about 10 to about 10.5, from about 10.5 to about 15, from about 10.5 to about 14.5, from about 10.5 to about 14, from about 10.5 to about 13.5, from about 10.5 to about 13, from about 10.5 to about 12.5, from about 10.5 to about 12, from about 10.5 to about 11.5, from about 10.5 to about 11, from about 11 to about 15, from about 11 to about 14.5, from about 11 to about 14, from about 11 to about 13.5, from about 11 to about 13, from about 11 to about 12.5, from about 11 to about 12, from about 11 to about 11.5, from about 11.5 to about 15, from about 11.5 to about 14.5, from about 11.5 to about 14, from about 11.5 to about 13.5, from about 11.5 to about 13, from about 11.5 to about 12.5, from about 11.5 to about 12, from about 12 to about 15, from about 12 to about 14.5, from about 12 to about 14, from about 12 to about 13.5, from about 12 to about 13, from about 12 to about 12.5, from about 12.5 to about 15, from about 12.5 to about 14.5, from about 12.5 to about 14, from about 12.5 to about 13.5, from about 12.5 to about 13, from about 12.5 to about 15, from about 12.5 to about 14.5, from about 12.5 to about 14, from about 12.5 to about 13.5, from about 12.5 to about 13, from about 13 to about 15, from about 13 to about 14.5, from about 13 to about 14, from about 13 to about 13.5, from about 13.5 to about 15, from about 13.5 to about 14.5, from about 13.5 to about 14, from about 14 to about 15, from about 14 to about 14.5, and from about 14.5 to about 15.

In a particular embodiment comprising a base, the pH can be from about 9 to about 15, from about 9 to about 14 or from about 8 to about 14.

Exemplary bases can include, but are not limited to, sodium hydroxide, potassium hydroxide, lithium hydroxide, pyridine, pyrrole, piperazine, pyrrolidine, piperidine, picoline, monoethanolamine, diethanolamine, dimethylmonoethanolamine, monomethyldiethanolamine, triethanolamine, diazabicyclooctane, diazabicyclononane, diazabicycloundecene, tetramethylammonium hydroxide, tetraethylammonium hydroxide, tetrapropylammonium hydroxide, tetrabutylammonium hydroxide, ammonia, ammonium hydroxide, methylamine, ethylamine, propylamine, butylamine, pentylamine, hexylamine, octylamine, nonylamine, decylamine, N,N-dimethylamine, N,N-diethylamine, N,N-dipropylamine, N,N-dibutylamine, trimethylamine, triethylamine, tripropylamine, tributylamine, cyclohexylamine, trimethylimidine, 1-amino-3-methylbutane, dimethylglycine, 3-amino-3-methylamine, and the like. These bases may be used either singly or in combination. In a particular embodiment, the base can comprise or be sodium hydroxide and/or ammonium hydroxide.

In certain embodiments where the aqueous mixture comprises an acid, the aqueous mixture can have a pH from about 0.01 to about 6.0, from about 0.01 to about 5, from about 0.01 to about 4, from about 0.01 to about 3, from about 0.01 to about 2, from about 0.01 to about 1, about 0.1 to about 6.0, about 0.1 to about 5.5, about 0.1 to about 5.0, from about 0.1 to about 4.8, from about 0.1 to about 4.5, from about 0.1 to about 4.2, from about 0.1 to about 4.0, from about 0.1 to about 3.8, from about 0.1 to about 3.5, from about 0.1 to about 3.2, from about 0.1 to about 3.0, from about 0.1 to about 2.8, from about 0.1 to about 2.5, from about 0.1 to about 2.2, from about 0.1 to about 2.0, from about 0.1 to about 1.8, from about 0.1 to about 1.5, from about 0.1 to about 1.2, from about 0.1 to about 1.0, from about 0.1 to about 0.8, from about 0.1 to about 0.5, from about 0.1 to about 0.2, about 0.2 to about 6.0, about 0.2 to about 5.5, from about 0.2 to about 5, from about 0.2 to about 4.8, from about 0.2 to about 4.5, from about 0.2 to about 4.2, from about 0.2 to about 4.0, from about 0.2 to about 3.8, from about 0.2 to about 3.5, from about 0.2 to about 3.2, from about 0.2 to about 3.0, from about 0.2 to about 2.8, from about 0.2 to about 2.5, from about 0.2 to about 2.2, from about 0.2 to about 2.0, from about 0.2 to about 1.8, from about 0.2 to about 1.5, from about 0.2 to about 1.2, from about 0.2 to about 1.0, from about 0.2 to about 0.8, from about 0.2 to about 0.5, about 0.5 to about 6.0, about 0.5 to about 5.5, from about 0.5 to about 5, from about 0.5 to about 4.8, from about 0.5 to about 4.5, from about 0.5 to about 4.2, from about 0.5 to about 4.0, from about 0.5 to about 3.8, from about 0.5 to about 3.5, from about 0.5 to about 3.2, from about 0.5 to about 3.0, from about 0.5 to about 2.8, from about 0.5 to about 2.5, from about 0.5 to about 2.2, from about 0.5 to about 2.0, from about 0.5 to about 1.8, from about 0.5 to about 1.5, from about 0.5 to about 1.2, from about 0.5 to about 1.0, from about 0.5 to about 0.8, about 0.8 to about 6.0, about 0.8 to about 5.5, from about 0.8 to about 5, from about 0.8 to about 4.8, from about 0.8 to about 4.5, from about 0.8 to about 4.2, from about 0.8 to about 4.0, from about 0.8 to about 3.8, from about 0.8 to about 3.5, from about 0.8 to about 3.2, from about 0.8 to about 3.0, from about 0.8 to about 2.8, from about 0.8 to about 2.5, from about 0.8 to about 2.2, from about 0.8 to about 2.0, from about 0.8 to about 1.8, from about 0.8 to about 1.5, from about 0.8 to about 1.2, from about 0.8 to about 1.0, about 1.0 to about 6.0, about 1.0 to about 5.5, from about 1.0 to about 5.0, from about 1.0 to about 4.8, from about 1.0 to about 4.5, from about 1.0 to about 4.2, from about 1.0 to about 4.0, from about 1.0 to about 3.8, from about 1.0 to about 3.5, from about 1.0 to about 3.2, from about 1.0 to about 3.0, from about 1.0 to about 2.8, from about 1.0 to about 2.5, from about 1.0 to about 2.2, from about 1.0 to about 2.0, from about 1.0 to about 1.8, from about 1.0 to about 1.5, from about 1.0 to about 1.2, about 1.2 to about 6.0, about 1.2 to about 5.5, from about 1.2 to about 5.0, from about 1.2 to about 4.8, from about 1.2 to about 4.5, from about 1.2 to about 4.2, from about 1.2 to about 4.0, from about 1.2 to about 3.8, from about 1.2 to about 3.5, from about 1.2 to about 3.2, from about 1.2 to about 3.0, from about 1.2 to about 2.8, from about 1.2 to about 2.5, from about 1.2 to about 2.2, from about 1.2 to about 2.0, from about 1.2 to about 1.8, from about 1.2 to about 1.5, about 1.5 to about 6.0, about 1.5 to about 5.5, from about 1.5 to about 5.0, from about 1.5 to about 4.8, from about 1.5 to about 4.5, from about 1.5 to about 4.2, from about 1.5 to about 4.0, from about 1.5 to about 3.8, from about 1.5 to about 3.5, from about 1.5 to about 3.2, from about 1.5 to about 3.0, from about 1.5 to about 2.8, from about 1.5 to about 2.5, from about 1.5 to about 2.2, from about 1.5 to about 2.0, from about 1.5 to about 1.8, about 1.8 to about 6.0, about 1.8 to about 5.5, from about 1.8 to about 5.0, from about 1.8 to about 4.8, from about 1.8 to about 4.5, from about 1.8 to about 4.2, from about 1.8 to about 4.0, from about 1.8 to about 3.8, from about 1.8 to about 3.5, from about 1.8 to about 3.2, from about 1.8 to about 3.0, from about 1.8 to about 2.8, from about 1.8 to about 2.5, from about 1.8 to about 2.2, from about 1.8 to about 2.0, about 2.0 to about 6.0, about 2.0 to about 5.5, from about 2.0 to about 5.0, from about 2.0 to about 4.8, from about 2.0 to about 4.5, from about 2.0 to about 4.2, from about 2.0 to about 4.0, from about 2.0 to about 3.8, from about 2.0 to about 3.5, from about 2.0 to about 3.2, from about 2.0 to about 3.0, from about 2.0 to about 2.8, from about 2.0 to about 2.5, from about 2.0 to about 2.2, about 2.2 to about 6.0, about 2.2 to about 5.5, from about 2.2 to about 5.0, from about 2.2 to about 4.8, from about 2.2 to about 4.5, from about 2.2 to about 4.2, from about 2.2 to about 4.0, from about 2.2 to about 3.8, from about 2.2 to about 3.5, from about 2.2 to about 3.2, from about 2.2 to about 3.0, from about 2.2 to about 2.8, from about 2.2 to about 2.5, about 2.5 to about 6.0, about 2.5 to about 5.5, from about 2.5 to about 5.0, from about 2.5 to about 4.8, from about 2.5 to about 4.5, from about 2.5 to about 4.2, from about 2.5 to about 4.0, from about 2.5 to about 3.8, from about 2.5 to about 3.5, from about 2.5 to about 3.2, from about 2.5 to about 3.0, from about 2.5 to about 2.8, from about 2.8 to about 6.0, about 2.8 to about 5.5, from about 2.8 to about 5.0, from about 2.8 to about 4.8, from about 2.8 to about 4.5, from about 2.8 to about 4.2, from about 2.8 to about 4.0, from about 2.8 to about 3.8, from about 2.8 to about 3.5, from about 2.8 to about 3.2, from about 2.8 to about 3.0, from about 3.0 to about 6.0, from about 3.5 to about 5.5, from about 3.0 to about 5.0, from about 3.0 to about 4.8, from about 3.0 to about 4.5, from about 3.0 to about 4.2, from about 3.0 to about 4.0, from about 3.0 to about 3.8, from about 3.0 to about 3.5, from about 3.0 to about 3.2, from about 3.2 to about 6.0, from about 3.2 to about 5.5, from about 3.2 to about 5, from about 3.2 to about 4.8, from about 3.2 to about 4.5, from about 3.2 to about 4.2, from about 3.2 to about 4.0, from about 3.2 to about 3.8, from about 3.2 to about 3.5, from about 3.5 to about 6.0, from about 3.5 to about 5.5, from about 3.5 to about 5, from about 3.5 to about 4.8, from about 3.5 to about 4.5, from about 3.5 to about 4.2, from about 3.5 to about 4.0, from about 3.5 to about 3.8, from about 3.8 to about 5, from about 3.8 to about 4.8, from about 3.8 to about 4.5, from about 3.8 to about 4.2, from about 3.8 to about 4.0, from about 4.0 to about 6.0, from about 4.0 to about 5.5, from about 4.0 to about 5, from about 4.0 to about 4.8, from about 4.0 to about 4.5, from about 4.0 to about 4.2, from about 4.2 to about 5, from about 4.2 to about 4.8, from about 4.2 to about 4.5, from about 4.5 to about 5, from about 4.5 to about 4.8, or from about 4.8 to about 5.

In a particular embodiment comprising an acid, the pH can be from about 0.01 to about 6.0, about 0.2 to about 6.0, about 0.2 to about 5.0 or about 0.2 to about 4.5.

Exemplary acids can include, but are not limited to, inorganic acids such as hydrochloric acid, nitric acid, sulfuric acid, hydrofluoric acid, phosphoric acid, boric acid and oxalic acid; and organic acids such as acetic acid, propionic acid, butanoic acid, pentanoic acid, hexanoic acid, heptanoic acid, octanoic acid, nonanoic acid, decanoic acid, oxalic acid, maleic acid, methylmalonic acid, adipic acid, sebacic acid, gallic acid, butyric acid, mellitic acid, arachidonic acid, shikimic acid, 2-ethylhexanoic acid, oleic acid, stearic acid, linoleic acid, linolenic acid, salicylic acid, benzoic acid, p-amino-benzoic acid, p-toluenesulfonic acid, benzenesulfonic acid, monochloroacetic acid, dichloroacetic acid, trichloroacetic acid, trifluoroacetic acid, formic acid, malonic acid, sulfonic acid, phthalic acid, fumaric acid, citric acid, tartaric acid, succinic acid, itaconic acid, mesaconic acid, citraconic acid, malic acid, a hydrolysate of glutaric acid, a hydrolysate of maleic anhydride, a hydrolysate of phthalic anhydride, and the like. These acids may be used either singly or in combination. In a particular embodiment, the acid can comprise or be hydrochloric acid.

III.B. Compounds of Formula (Ia)

The methods provided herein comprise the step of adding at least one compound of Formula [R¹R²SiCH₂]₃(Ia) into the aqueous mixture to form a solution, wherein each R¹represents a C₁-C₄alkoxy group and each R²represents a C₁-C₄alkoxy group or a C₁-C₄alkyl group.

In one embodiment, each R¹can be a C₁-C₃alkoxy or methoxy or ethoxy.

Additionally or alternatively, each R²can be a C₁-C₄alkoxy, a C₁-C₃alkoxy or methoxy or ethoxy. Additionally or alternatively, each R²can comprise methyl, ethyl or propyl, such as a methyl or ethyl.

Additionally or alternatively, each R¹can be a C₁-C₂alkoxy group and R²can be a C₁-C₂alkoxy group or a C₁-C₂alkyl group.

Additionally or alternatively, each R¹can be methoxy or ethoxy and each R²can be methyl or ethyl.

In a particular embodiment, R¹and R²can be ethoxy, such that the compound corresponding to Formula (Ia) can be 1,1,3,3,5,5-hexaethoxy-1,3,5-trisilacyclohexane, ([(EtO)₂SiCH₂]₃).

In a particular embodiment, R¹can be ethoxy and R²can be methyl, such that compound corresponding to Formula (Ia) can be 1,3,5-trimethyl-1,3,5-triethoxy-1,3,5-trisilacyclohexane, ([EtOCH₃SiCH₂]₃).

In various aspects, more than one compound of Formula (Ia) (e.g., same or different compound) may be added to the aqueous mixture to form a solution. For example, [(EtO)₂SiCH₂]₃and [EtOCH₃SiCH₂]₃may both be added to the aqueous mixture to form a solution.

When more than one compound of Formula (Ia) is used, the respective compounds may be used in a wide variety of molar ratios. For example, if two compounds of Formula (Ia) are used, the molar ratio of each compound may vary from 1:99 to 99:1, such as from 10:90 to 90:10. The use of different compounds of Formula (Ia) allows to tailor the properties of the organosilica materials made by the process of the invention, as will be further explained in the examples and in the section of this specification describing the properties of the organosilicas made by the present processes.

III.D. Compounds of Formula (IIa)

In additional embodiments, the methods provided herein can further comprise adding to the aqueous solution a compound of Formula R³OR⁴R⁵R⁶Si (IIa) to obtain an organosilica material which is a copolymer comprising at least one independent unit of Formula (I) as described herein and at least one independent unit of Formulas (II), (IV), and/or (V) as described herein, wherein each R³can be a C₁-C₆alkyl group, and R⁴, R⁵and R⁶each independently can be selected from the group consisting of a C₁-C₆alkyl group, a C₁-C₆alkoxy group, a nitrogen-containing C₁-C₁₀alkyl group, a nitrogen-containing heteroaralkyl group, and a nitrogen-containing optionally substituted heterocycloalkyl group.

In one embodiment, each R³can be a C₁-C₆alkyl group, and R⁴, R⁵and R⁶each independently can be selected from the group consisting of a C₁-C₆alkyl group and a C₁-C₆alkoxy group.

In various embodiments, each R³can be a C₁-C₅alkyl group, a C₁-C₄alkyl group, a C₁-C₃alkyl group, a C₁-C₂alkyl group, or methyl. In particular, each R³can be methyl or ethyl.

Additionally or alternatively, R⁴, R⁵and R⁶can be each independently a C₁-C₅alkyl group, a C₁-C₄alkyl group, a C₁-C₃alkyl group, a C₁-C₂alkyl group, or methyl.

Additionally or alternatively, each R³can be a C₁-C₂alkyl group and R⁴, R⁵and R⁶can be each independently a C₁-C₂alkyl group.

Additionally or alternatively, R⁴, R⁵and R⁶can be each independently a C₁-C₅alkoxy group, a C₁-C₄alkoxy group, a C₁-C₃alkoxy group, a C₁-C₂alkoxy group, or methoxy.

Additionally or alternatively, each R³can be a C₁-C₂alkyl group and R⁴, R⁵and R⁶can be each independently a C₁-C₂alkoxy group.

Additionally or alternatively, each R³can be a C₁-C₂alkyl group and R⁴, R⁵and R⁶can be each independently a C₁-C₂alkyl group or a C₁-C₂alkoxy group.

Additionally or alternatively, R⁴, R⁵and R⁶can be each independently a nitrogen-containing C₁-C₉alkyl group, a nitrogen-containing C₁-C₈alkyl group, a nitrogen-containing C₁-C₇alkyl group, a nitrogen-containing C₁-C₆alkyl group, a nitrogen-containing C₁-C₅alkyl group, a nitrogen-containing C₁-C₄alkyl group, a nitrogen-containing C₁-C₃alkyl group, a nitrogen-containing C₁-C₂alkyl group, or a methylamine. In particular, R⁴, R⁵and R⁶can be each independently a nitrogen-containing C₂-C₁₀alkyl group, a nitrogen-containing C₃-C₁₀alkyl group, a nitrogen-containing C₃-C₉alkyl group, or a nitrogen-containing C₃-C₈alkyl group. The aforementioned nitrogen-containing alkyl groups may have one or more nitrogen atoms (e.g., 2, 3, etc.). Examples of nitrogen-containing C₁-C₁₀alkyl groups include, but are not limited to,

embedded image

Additionally or alternatively, each R³can be a C₁-C₂alkyl group and R⁴, R⁵and R⁶can be each independently a nitrogen-containing C₃-C₈alkyl group.

Additionally or alternatively, each R³can be a C₁-C₂alkyl group and R⁴, R⁵and R⁶can be each independently a C₁-C₂alkyl group, a C₁-C₂alkoxy group or a nitrogen-containing C₃-C₈alkyl group.

Additionally or alternatively, R⁴, R⁵and R⁶can be each independently a nitrogen-containing heteroaralkyl group. The nitrogen-containing heteroaralkyl group can be a nitrogen-containing C₄-C₁₂heteroaralkyl group, a nitrogen-containing C₄-C₁₀heteroaralkyl group, or a nitrogen-containing C₄-C₈heteroaralkyl group. Examples of nitrogen-containing heteroaralkyl groups include but are not limited to pyridinylethyl, pyridinylpropyl, pyridinylmethyl, indolylmethyl, pyrazinylethyl, and pyrazinylpropyl. The aforementioned nitrogen-containing heteroaralkyl groups may have one or more nitrogen atoms (e.g., 2, 3, etc.).

Additionally or alternatively, each R³can be a C₁-C₂alkyl group and R⁴, R⁵and R⁶can be each independently a nitrogen-containing heteroaralkyl group.

Additionally or alternatively, each R³can be a C₁-C₂alkyl group and R⁴, R⁵and R⁶can be each independently a C₁-C₂alkyl group, a C₁-C₂alkoxy group, a nitrogen-containing C₃-C₈alkyl group or a nitrogen-containing heteroaralkyl group.

Additionally or alternatively, R⁴, R⁵and R⁶can be each independently a nitrogen-containing heterocycloalkyl group, wherein the heterocycloalkyl group may be optionally substituted with a C₁-C₆alkyl group, particularly a C₁-C₄alkyl group. The nitrogen-containing heterocycloalkyl group can be a nitrogen-containing C₄-C₁₂heterocycloalkyl group, a nitrogen-containing C₄-C₁₀heterocycloalkyl group, or a nitrogen-containing C₄-C₈heterocycloalkyl group. Examples of nitrogen-containing heterocycloalkyl groups include but are not limited to piperazinylethyl, piperazinylpropyl, piperidinylethyl, piperidinylpropyl. The aforementioned nitrogen-containing heterocycloalkyl groups may have one or more nitrogen atoms (e.g., 2, 3, etc.).

Additionally or alternatively, each R³can be a C₁-C₂alkyl group and R⁴, R⁵and R⁶can be each independently a nitrogen-containing optionally substituted heterocycloalkyl group.

Additionally or alternatively, each R³can be a C₁-C₂alkyl group and R⁴, R⁵and R⁶can be each independently a C₁-C₂alkyl group, C₁-C₂alkoxy group, a nitrogen-containing C₃-C₁₀alkyl group, a nitrogen-containing C₄-C₁₀heteroaralkyl group, or a nitrogen-containing optionally substituted C₄-C₁₀heterocycloalkyl group.

In a particular embodiment, each R³can be ethyl and R⁴, R⁵and R⁶can be ethoxy, such that the compound corresponding to Formula (IIa) can be tetraethyl orthosilicate (TEOS) ((EtO)₄Si).

In another particular embodiment, a compound of Formula (Ia) can be 1,1,3,3,5,5-hexaethoxy-1,3,5-trisilacyclohexane ([(EtO)₂SiCH₂]₃), a compound of Formula (IIa) can be tetraethyl orthosilicate (TEOS) ((EtO)₄Si).

In another particular embodiment, each R³can be ethyl, R⁴can be methyl and R⁵and R⁶can be ethoxy, such that the compound corresponding to Formula (IIa) can be methyltriethoxysilane (MTES) ((EtO)₃CH₃Si).

In another particular embodiment, a compound of Formula (Ia) can be 1,1,3,3,5,5-hexaethoxy-1,3,5-trisilacyclohexane ([(EtO)₂SiCH₂]₃and a compound of Formula (IIa) can be methyltriethoxysilane (MTES) ((EtO)₃CH_3-Si).

In another particular embodiment, a compound of Formula (Ia) can be 1,3,5-trimethyl-1,3,5-triethoxy-1,3,5-trisilacyclohexane ([EtOCH₃SiCH₂]₃and a compound of Formula (IIa) can be tetraethyl orthosilicate (TEOS) ((EtO)₄Si).

In another particular embodiment, R³can be ethyl, R⁴and R⁵can be ethoxy and R⁶can be

embedded image

such that the compound corresponding to Formula (IIa) can be (3-aminopropyl)triethoxysilane (H₂N(CH₂)₃(EtO)₃Si).

In another particular embodiment, a compound of Formula (Ia) can be 1,1,3,3,5,5-hexaethoxy-1,3,5-trisilacyclohexane ([(EtO)₂SiCH₂]₃) and a compound of Formula (IIa) can be (3-aminopropyl)triethoxysilane (H₂N(CH₂)₃(EtO)₃Si).

In another particular embodiment, R³can be methyl, R⁴and R⁵can be methoxy and R⁴can be

embedded image

such that the compound corresponding to Formula (IIa) can be (N,N-dimethylaminopropyl)trimethoxysilane (((CH₃)₂N(CH₂)₃)(MeO)₃Si).

In another particular embodiment, a compound of Formula (Ia) can be 1,1,3,3,5,5-hexaethoxy-1,3,5-trisilacyclohexane ([(EtO)₂SiCH₂]₃) and a compound of Formula (IIa) can be (N,N-dimethylaminopropyl)trimethoxysilane (((CH₃)₂N(CH₂)₃)(MeO)₃Si).

In another particular embodiment, R³can be ethyl, R⁴and R⁵can be ethoxy and R⁶can be

embedded image

such that the compound corresponding to Formula (IIa) can be (N-(2-aminoethyl)-3-aminopropyltriethoxysilane ((H₂N(CH₂)₂NH (CH₂)₃)(EtO)₂Si).

In another particular embodiment, a compound of Formula (Ia) can be 1,1,3,3,5,5-hexaethoxy-1,3,5-trisilacyclohexane ([(EtO)₂SiCH₂]₃) and a compound of Formula (IIa) can be (N-(2-aminoethyl)-3-aminopropyltriethoxysilane ((H₂N(CH₂)₂NH (CH₂)₃)(EtO)₂Si).

In another particular embodiment, R³can be ethyl, R⁴and R⁵can be ethoxy and R⁶can be

embedded image

such that the compound corresponding to Formula (IIa) can be 4-methyl-1-(3-triethoxysilylpropyl)-piperazine.

In another particular embodiment, R³can be ethyl, R⁴and R⁵can be ethoxy and R⁶can be

embedded image

such that the compound corresponding to Formula (IIa) can be 4-(2-(triethoxysily)ethyl)pyridine.

In another particular embodiment, R³can be ethyl, R⁴and R⁵can be ethoxy and R⁵can be

embedded image

such that the compound corresponding to Formula (IIa) can be 1-(3-(triethoxysilyl)propyl)-4,5-dihydro-1H-imidazole.

In another particular embodiment, a compound of Formula (Ia) can be 1,1,3,3,5,5-hexaethoxy-1,3,5-trisilacyclohexane ([(EtO)₂SiCH₂]₃) and a compound of Formula (IIa) can be 1-(3-(triethoxysilyl)propyl)-4,5-dihydro-1H-imidazole.

The molar ratio of compound of Formula (Ia) to compound of Formula (IIa) may vary within wide limits, such as from about 99:1 to about 1:99, from about 1:5 to about 5:1, from about 4:1 to about 1:4 or from about 3:2 to about 2:3. For example, a molar ratio of compound of Formula (Ia) to compound of Formula (IIa) can be from about 4:1 to 1:4 or from about 2.5:1 to about 1:2.5, about 2:1 to about 1:2, such as about 1.5:1 to about 1.5:1.

III.D. Compounds of Formula (IIIa)

In additional embodiments, the methods provided herein can further comprise adding to the aqueous solution a compound of Formula Z¹⁹Z²⁰Z²¹Si—R⁷—Si Z¹⁹Z²⁰Z²¹(IIIa) to obtain an organosilica material which is a copolymer comprising at at least one independent unit Formula (I) as described herein and at least one independent unit of Formulas (III), (IV) and/or (VI) as described herein, wherein each Z¹⁹independently can be a C₁-C₄alkoxy group; Z²⁰and Z²¹each independently can be a C₁-C₄alkoxy group or a C₁-C₄alkyl group; and each R⁷can be selected from the group consisting a C₁-C₈alkylene group, a C₂-C₈alkenylene group, a C₂-C₈alkynylene group, a nitrogen-containing C₂-C₁₀alkylene group, an optionally substituted C₆-C₂₀aralkyl group, and an optionally substituted C₄-C₂₀heterocycloalkyl group.

In one embodiment, each Z¹⁹can be a C₁-C₄alkoxy group; Z²⁰and Z²¹each independently can be a C₁-C₄alkoxy group or a C₁-C₄alkyl group; and R⁷can be selected from the group consisting a C₁-C₈alkylene group, a C₂-C₈alkenylene group, a C₂-C₈alkynylene group, an optionally substituted C₆-C₂₀aralkyl group, and an optionally substituted C₄-C₂₀heterocycloalkyl group.

In another embodiment, each Z¹⁹can be a C₁-C₄alkoxy group; Z²⁰and Z²¹each independently can be a C₁-C₄alkoxy group or a C₁-C₄alkyl group; and each R⁷can be a nitrogen-containing C₂-C₁₀alkylene group.

In various embodiments, each Z¹⁹can be a C₁-C₃alkoxy group, a C₁-C₂alkoxy group, or methoxy.

Additionally or alternatively, Z²⁰and Z²¹each independently can be a C₁-C₃alkoxy group, a C₁-C₂alkoxy group, or methoxy.

Additionally or alternatively, each Z¹⁹can be a C₁-C₂alkoxy group and Z²⁰and Z²¹each independently can be a C₁-C₂alkoxy group.

Additionally or alternatively, Z²⁰and Z²¹each independently can be a C₁-C₃alkyl group, a C₁-C₂alkyl group, or methyl.

Additionally or alternatively, each Z¹⁹can be a C₁-C₂alkoxy group and Z²⁰and Z²¹each independently can be a C₁-C₂alkyl group.

Additionally or alternatively, Z¹⁹can be a C₁-C₂alkoxy group and Z²⁰and Z²¹each independently can be a C₁-C₂alkoxy group or a C₁-C₂alkyl group.

Additionally or alternatively, each R⁷can be a C₁-C₇alkylene group, a C₁-C₆alkylene group, a C₁-C₅alkylene group, a C₁-C₄alkylene group, a C₁-C₃alkylene group, a C₁-C₂alkylene group, or —CH₂—.

Additionally or alternatively, each Z¹⁹can be a C₁-C₂alkoxy group; Z²⁰and Z²¹each independently can be a C₁-C₂alkoxy group or a C₁-C₂alkyl group; and each R⁷can be a C₁-C₂alkylene group.

Additionally or alternatively, each R⁷can be a C₂-C₇alkenylene group, a C₁-C₆alkenylene group, a C₂-C₅alkenylene group, a C₂-C₄a alkenylene group, a C₂-C₃alkenylene group, or —CH═CH—.

Additionally or alternatively, each Z¹⁹can be a C₁-C₂alkoxy group; Z²⁰and Z²¹each independently can be a C₁-C₂alkoxy group or a C₁-C₂alkyl group; and each R⁷can be a C₁-C₂alkenylene group.

Additionally or alternatively, each R⁷can be a C₂-C₇alkynylene group, a C₁-C₆alkynylene group, a C₂-C₅alkynylene group, a C₂-C₄a alkynylene group, a C₂-C₃alkynylene group, or —C≡C—.

Additionally or alternatively, each Z¹⁹can be a C₁-C₂alkoxy group; Z²⁰and Z²¹each independently can be a C₁-C₂alkoxy group or a C₁-C₂alkyl group; and R⁷can be a C₂-C₄alkynylene group.

Additionally or alternatively, each Z¹⁹can be a C₁-C₂alkoxy group; Z²⁰and Z²¹each independently can be a C₁-C₂alkoxy group or a C₁-C₂alkyl group; and each R⁷can be a C₂-C₄alkylene group, a C₂-C₄alkenylene group or a C₂-C₄alkynylene group.

Additionally or alternatively, each R⁷can be a nitrogen-containing C₂-C₁₀alkylene group, a nitrogen-containing C₃-C₁₀alkylene group, a nitrogen-containing C₄-C₁₀alkylene group, a nitrogen-containing C₄-C₉alkylene group, a nitrogen-containing C₄-C₈alkylene group, or nitrogen containing C₃-C₈alkylene group. The aforementioned nitrogen-containing alkylene groups may have one or more nitrogen atoms (e.g., 2, 3, etc.). Examples of nitrogen-containing alkylene groups include, but are not limited to,

embedded image

Additionally or alternatively, each Z¹⁹can be a C₁-C₂alkoxy group; Z²⁰and Z²¹each independently can be a C₁-C₂alkoxy group or a C₁-C₂alkyl group; and each R⁷can be a nitrogen-containing C₄-C₁₀alkylene group.

Additionally or alternatively, each R⁷can be an optionally substituted C₆-C₂₀aralkyl, an optionally substituted C₆-C₁₄aralkyl, or an optionally substituted C₆-C₁₀aralkyl. Examples of C₆-C₂₀aralkyls include, but are not limited to, phenymethyl, phenylethyl, and naphthylmethyl. The aralkyl may be optionally substituted with a C₁-C₆alkyl group, particularly a C₁-C₄alkyl group.

Additionally or alternatively, each Z¹⁹can be a C₁-C₂alkoxy group; Z²⁰and Z²¹each independently can be a C₁-C₂alkoxy group or a C₁-C₂alkyl group; and each R⁷can be an optionally substituted C₆-C₁₀aralkyl.

Additionally or alternatively, R⁷can be an optionally substituted C₄-C₂₀heterocycloalkyl group, an optionally substituted C₄-C₁₆heterocycloalkyl group, an optionally substituted C₄-C₁₂heterocycloalkyl group, or an optionally substituted C₄-C₁₀heterocycloalkyl group. Examples of C₄-C₂₀heterocycloalkyl groups include, but are not limited to, thienylmethyl, furylethyl, pyrrolylmethyl, piperazinylethyl, pyridylmethyl, benzoxazolylethyl, quinolinylpropyl, and imidazolylpropyl. The heterocycloalkyl may be optionally substituted with a C₁-C₆alkyl group, particularly a C₁-C₄alkyl group.

Additionally or alternatively, each Z¹⁹can be a C₁-C₂alkoxy group; Z²⁰and Z²¹each independently can be a C₁-C₂alkoxy group or a C₁-C₂alkyl group; and R⁷can be an optionally substituted C₄-C₁₂heterocycloalkyl group.

In a particular embodiment, Z¹⁹and Z²⁰can be ethoxy, Z²¹can be methyl and R⁷can be —CH₂CH₂—, such that compound corresponding to Formula (IIIa) can be 1,2-bis(methyldiethoxysilyl)ethane (CH₃(EtO)₂Si—CH₂CH₂—Si(EtO)₂CH₃).

In another particular embodiment, a compound of Formula (Ia) can be 1,1,3,3,5,5-hexaethoxy-1,3,5-trisilacyclohexane ([(EtO)₂SiCH₂]₃), and a compound of Formula (IIIa) can be 1,2-bis(methyldiethoxysilyl)ethane (CH₃(EtO)₂Si—CH₂CH₂—Si(EtO)₂CH₃).

In another particular embodiment, Z¹⁹, Z²⁰and Z²¹can be ethoxy and R⁷can be —CH₂—, such that compound corresponding to Formula (IIIa) can be bis(triethoxysilyl)methane ((EtO)₃Si—CH₂—Si(EtO)₃).

In another particular embodiment, a compound of Formula (Ia) can be 1,1,3,3,5,5-hexaethoxy-1,3,5-trisilacyclohexane ([(EtO)₂SiCH₂]₃) and a compound of Formula (IIIa) can be bis(triethoxysilyl)methane ((EtO)₃Si—CH₂—Si(EtO)₃).

In another particular embodiment, Z¹⁹, Z²⁰and Z²¹can be ethoxy and R⁷can be —HC═CH—, such that compound corresponding to Formula (IIIa) can be 1,2-bis(triethoxysilyl)ethylene ((EtO)₃Si—HC═CH—Si(EtO)₃).

In another particular embodiment, a compound of Formula (Ia) can be 1,1,3,3,5,5-hexaethoxy-1,3,5-trisilacyclohexane ([(EtO)₂SiCH₂]₃)) and a compound of Formula (IIIa) can be 1,2-bis(triethoxysilyl)ethylene ((EtO)₃Si—HC═CH—Si(EtO)₃).

In another particular embodiment, a compound of Formula (IIIa) can be bis(triethoxysilyl)methane ((EtO)₃Si—CH₂—Si(EtO)₃) and a compound of Formula (IIa) can be tetraethyl orthosilicate (TEOS) ((EtO)₄Si).

In a particular embodiment, Z¹⁹, Z²⁰and Z²¹can be methoxy and R⁷can be

embedded image

such that compound corresponding to Formula (IIIa) can be N,N′-bis[(3-trimethoxysilyl)propyl]ethylenediamine.

In another particular embodiment, a compound of Formula (Ia) can be 1,1,3,3,5,5-hexaethoxy-1,3,5-trisilacyclohexane ([(EtO)₂SiCH₂]₃) and a compound of Formula (IIIa) can be N,N′-bis[(3-trimethoxysilyl)propyl]ethylenediamine.

In another particular embodiment, Z¹⁹and Z²⁰can be ethoxy, Z²¹can be methyl and R⁷can be

embedded image

such that compound corresponding to Formula (IIIa) can be bis[(methyldiethoxysilyl)propyl]amine.

In another particular embodiment, a compound of a compound of Formula (Ia) can be 1,1,3,3,5,5-hexaethoxy-1,3,5-trisilacyclohexane ([(EtO)₂SiCH₂]₃) and a compound of Formula (IIIa) can be bis[(methyldiethoxysilyl)propyl]amine.

In another particular embodiment, Z¹⁹and Z²⁰can be methoxy, Z²¹can be methyl and R⁷can be

embedded image

such that compound corresponding to Formula (IIIa) can be bis[(methyldimethoxysilyl)propyl]-N-methylamine.

The molar ratio of compound of Formula (Ia) to compound of Formula (IIIa) may vary within wide limits, such as from about 99:1 to about 1:99, from about 1:5 to about 5:1, from about 4:1 to about 1:4 or from about 3:2 to about 2:3. For example, a molar ratio of compound of Formula (Ia) to compound of Formula (IIIa) can be from about 4:1 to 1:4 or from about 2.5:1 to 1:2.5, about 2:1 to about 1:2, such as about 1.5:1 to about 1.5:1.

III.C. Metal Chelate Sources

In additional embodiments, the methods provided herein can further comprise adding to the aqueous solution a source of metal chelate compounds.

Examples of metal chelate compounds, when present, can include titanium chelate compounds such as triethoxy.mono(acetylacetonato) titanium, tri-n-propoxy.mono(acetylacetonato)titanium, tri-i-propoxy. mono(acetylacetonato)titanium, tri-n-butoxy.mono(acetylacetonato)titanium, tri-sec-butoxy.mono(acetylacetonato)titanium, tri-t-butoxy.mono(acetylacetonato)titanium, diethoxy.bis(acetylacetonato)titanium, di-n-propoxy.bis(acetylacetonato)titanium, di-i-propoxy.bis(acetylacetonato)titanium, di-n-butoxy.bis(acetylacetonato)titanium, di-sec-butoxy.bis(acetylacetonato)titanium, di-t-butoxy.bis(acetylacetonato)titanium, monoethoxy.tris(acetylacetonato)titanium, mono-n-propoxy.tris(acetylacetonato) titanium, mono-i-propoxy.tris(acetylacetonato)titanium, mono-n-butoxy. tris(acetylacetonato)titanium, mono-sec-butoxy.tris(acetylacetonato)titanium, mono-t-butoxy-tris(acetylacetonato)titanium, tetrakis(acetylacetonato)titanium, triethoxy. mono(ethylacetoacetaato)titanium, tri-n-propoxy.mono(ethylacetoacetato)titanium, tri-i-propoxy.mono(ethylacetoacetato) titanium, tri-n-butoxy.mono(ethylacetoacetato) titanium, tri-sec-butoxy.mono(ethylacetoacetato) titanium, tri-t-butoxy-mono(ethylacetoacetato)titanium, diethoxy.bis(ethylacetoacetato)titanium, di-n-propoxy.bis(ethylacetoacetato)titanium, di-i-propoxy.bis(ethylacetoacetato)titanium, di-n-butoxy.bis(ethylacetoacetato)titanium, di-sec-butoxy.bis(ethylacetoacetato)titanium, di-t-butoxy.bis(ethylacetoacetato)titanium, monoethoxy.tris(ethylacetoacetato)titanium, mono-n-propoxy.tris(ethylacetoaetato)titanium, mono-i-propoxy.tris(ethylacetoacetato) titanium, mono-n-butoxy.tris(ethylacetoacetato)titanium, mono-sec-butoxy. tris(ethylacetoacetato)titanium, mono-t-butoxy.tris(ethylacetoacetato)titanium, tetrakis(ethylacetoacetato)titanium, mono(acetylacetonato)tris(ethylacetoacetato) titanium, bis(acetylacetonato)bis(ethylacetoacetato)titanium, and tris(acetylacetonato)mono(ethylacetoacetato)titanium; zirconium chelate compounds such as triethoxy.mono(acetylacetonato)zirconium, tri-n-propoxy.mono(acetylacetonato) zirconium, tri-i-propoxy.mono(acetylacetonato)zirconium, tri-n-butoxy. mono(acetylacetonato)zirconium, tri-sec-butoxy.mono(acetylacetonato)zirconium, tri-t-butoxy.mono(acetylacetonato)zirconium, diethoxy.bis(acetylacetonato)zirconium, di-n-propoxy.bis(acetylacetonato)zirconium, di-i-propoxy.bis(acetylacetonato)zirconium, di-n-butoxy.bis(acetylacetonato)zirconium, di-sec-butoxy.bis(acetylacetonato)zirconium, di-t-butoxy.bis(acetylacetonato)zirconium, monoethoxy.tris(acetylacetonato)zirconium, mono-n-propoxy.tris(acetylacetonato)zirconium, mono-i-propoxy.tris(acetylacetonato) zirconium, mono-n-butoxy.tris(acetylacetonato)zirconium, mono-sec-butoxy. tris(acetylacetonato)zirconium, mono-t-butoxy.tris(acetylacetonato)zirconium, tetrakis(acetylacetonato)zirconium, triethoxy.mono(ethylacetoacetato)zirconium, tri-n-propoxy.mono(ethylacetoacetato)zirconium, tri-i-propoxy.mono(ethylacetoacetato) zirconium, tri-n-butoxy.mono(ethylacetoacetato)zirconium, tri-sec-butoxy. mono(ethylacetoacetato)zirconium, tri-t-butoxy.mono(ethylacetoacetato)zirconium, diethoxy.bis(ethylacetoacetato)zirconium, di-n-propoxy.bis(ethylacetoacetato)zirconium, di-i-propoxy.bis(ethylacetoacetato)zirconium, di-n-butoxy.bis(ethylacetoacetato) zirconium, di-sec-butoxy.bis(ethylacetoacetato)zirconium, di-t-butoxy. bis(ethylacetoacetato)zirconium, monoethoxy.tris(ethylacetoacetato)zirconium, mono-n-propoxy.tris(ethylacetoacetato)zirconium, mono-i-propoxy.tris(ethylacetoacetato) zirconium, mono-n-butoxy.tris(ethylacetoacetato)zirconium, mono-sec-butoxy. tris(ethylacetoacetato)zirconium, mono-t-butoxy.tris(ethylacetoacetato)zirconium, tetrakis(ethylacetoacetato)zirconium, mono(acetylacetonato)tris(ethylacetoacetato) zirconium, bis(acetylacetonato)bis(ethylacetoacetato)zirconium, and tris(acetylacetonato)mono(ethylacetoacetato)zirconium; and aluminum chelate compounds such as tris(acetylacetonato)aluminum and tris(ethylacetoacetato)aluminum. Of these, the chelate compounds of titanium or aluminum can be of note, of which the chelate compounds of titanium can be particularly of note. These metal chelate compounds may be used either singly or in combination.

III.D. Molar Ratio

In the methods described herein, a molar ratio of Formula (Ia):Formula (IIa), Formula (Ia):Formula (IIIa) of about 99:1 to about 1:99, about 75:1 to about 1:99, about 50:1 to about 1:99, about 25:1 to about 1:99, about 15:1 to about 1:99, about 50:1 to about 1:50, about 25:1 to about 1:25 or about 15:1 to about 1:15 may be used. For example, molar ratios of about 3:2, about 4:1, about 4:3, about 5:1, about 2:3, about 1:1 about 5:2 and about 15:1 may be used. For example a molar ratio of Formula (Ia):Formula (IIa), Formula (Ia):Formula (IIIa) of about 3:2, about 4:1, about 4:3, about 2:3, about 1:1 and about 5:2 may be used. For example, a molar ratio of Formula (Ia):Formula (IIa) can be about 2:3, about 4:3, about 4:1 or about 3:2. A molar ratio of Formula (Ia):Formula (IIIa) can be about 2:3, and about 4:1. A molar ratio of Formula (III):Formula (II) can be about 5:2, about 1:1, about 1:2 or about 2:3.

For the sake of the following discussion, the compounds of Formula (Ia), (IIa) and (IIIa) shall be referred to collectively as starting siloxane. Depending on the choice of starting materials, the solution may have a variety of compositions. For example, if base is used, the solution may have molar ratios of starting siloxane to OH⁻ of from about 1:5 to about 1:20, such as from about 1:5 to about 1:15 or from about 1:5 to 1:10, or from about 1:6 to 1:20. If acid is used, the solution may have molar ratios of starting siloxane:H⁺ of from about 50:1 to about 5:1, such as from about 45:1 to about 10:1. In both cases when acid or base is used, the molar ratios of starting siloxane to H₂O may vary from about 1:50 to about 1:1000, such as from about 1:100 to about 1:500.

III.E. Aging the Solution

The solution formed in the methods described herein can be aged for at least about 4 hours, at least about 6 hours, at least about 12 hours, at least about 18 hours, at least about 24 hours (1 day), at least about 30 hours, at least about 36 hours, at least about 42 hours, at least about 48 hours (2 days), at least about 54 hours, at least about 60 hours, at least about 66 hours, at least about 72 hours (3 days), at least about 96 hours (4 days), at least about 120 hours (5 days) or at least about 144 hours (6 days).

Additionally or alternatively, the solution formed in the methods described herein can be aged for about 4 hours to about 144 hours (6 days), about 4 hours to about 120 hours (5 days), about 4 hours to about 96 hours (4 days), about 4 hours to about 72 hours (3 days), about 4 hours to about 66 hours, about 4 hours to about 60 hours, about 4 hours to about 54 hours, about 4 hours to about 48 hours (2 days), about 4 hours to about 42 hours, about 4 hours to about 36 hours, about 4 hours to about 30 hours, about 4 hours to about 24 hours (1 day), about 4 hours to about 18 hours, about 4 hours to about 12 hours, about 4 hours to about 6 hours, about 6 hours to about 144 hours (6 days), about 6 hours to about 120 hours (5 days), about 6 hours to about 96 hours (4 days), about 6 hours to about 72 hours (3 days), about 6 hours to about 66 hours, about 6 hours to about 60 hours, about 6 hours to about 54 hours, about 6 hours to about 48 hours (2 days), about 6 hours to about 42 hours, about 6 hours to about 36 hours, about 6 hours to about 30 hours, about 6 hours to about 24 hours (1 day), about 6 hours to about 18 hours, about 6 hours to about 12 hours, about 12 hours to about 144 hours (6 days), about 12 hours to about 120 hours (5 days), about 12 hours to about 96 hours (4 days), about 12 hours to about 72 hours (3 days), about 12 hours to about 66 hours, about 12 hours to about 60 hours, about 12 hours to about 54 hours, about 12 hours to about 48 hours (2 days), about 12 hours to about 42 hours, about 12 hours to about 36 hours, about 12 hours to about 30 hours, about 12 hours to about 24 hours (1 day), about 12 hours to about 18 hours, about 18 hours to about 144 hours (6 days), about 18 hours to about 120 hours (5 days), about 18 hours to about 96 hours (4 days), about 18 hours to about 72 hours (3 days), about 18 hours to about 66 hours, about 18 hours to about 60 hours, about 18 hours to about 54 hours, about 18 hours to about 48 hours (2 days), about 18 hours to about 42 hours, about 18 hours to about 36 hours, about 18 hours to about 30 hours, about 18 hours to about 24 hours (1 day), about 24 hours (1 day) to about 144 hours (6 days), about 24 (1 day) hours (1 day) to about 120 hours (5 days), about 24 hours (1 day) to about 96 hours (4 days), about 24 hours (1 day) to about 72 hours (3 days), about 24 hours (1 day) to about 66 hours, about 24 hours (1 day) to about 60 hours, about 24 hours (1 day) to about 54 hours, about 24 hours (1 day) to about 48 hours (2 days), about 24 hours (1 day) to about 42 hours, about 24 hours (1 day) to about 36 hours, about 24 hours (1 day) to about 30 hours, about 30 hours to about 144 hours (6 days), about 30 hours to about 120 hours (5 days), about 30 hours to about 96 hours (4 days), about 30 hours to about 72 hours (3 days), about 30 hours to about 66 hours, about 30 hours to about 60 hours, about 30 hours to about 54 hours, about 30 hours to about 48 hours (2 days), about 30 hours to about 42 hours, about 30 hours to about 36 hours, about 36 hours to about 144 hours (6 days), about 36 hours to about 120 hours (5 days), about 36 hours to about 96 hours (4 days), about 36 hours to about 72 hours (3 days), about 36 hours to about 66 hours, about 36 hours to about 60 hours, about 36 hours to about 54 hours, about 36 hours to about 48 hours (2 days), about 36 hours to about 42 hours, about 42 hours to about 144 hours (6 days), about 42 hours to about 120 hours (5 days), about 42 hours to about 96 hours (4 days), about 42 hours to about 72 hours (3 days), about 42 hours to about 66 hours, about 42 hours to about 60 hours, about 42 hours to about 54 hours, about 42 hours to about 48 hours (2 days), about 48 hours (2 days) to about 144 hours (6 days), about 48 hours (2 days) to about 120 hours (5 days), about 48 hours (2 days) to about 96 hours (4 days), about 48 hours (2 days) to about 72 hours (3 days), about 48 hours (2 days) to about 66 hours, about 48 hours (2 days) to about 60 hours, about 48 hours (2 days) to about 54 hours, about 54 hours to about 144 hours (6 days), about 54 hours to about 120 hours (5 days), about 54 hours to about 96 hours (4 days), about 54 hours to about 72 hours (3 days), about 54 hours to about 66 hours, about 54 hours to about 60 hours, about 60 hours to about 144 hours (6 days), about 60 hours to about 120 hours (5 days), about 60 hours to about 96 hours (4 days), about 60 hours to about 72 hours (3 days), about 60 hours to about 66 hours, about 66 hours to about 144 hours (6 days), about 66 hours to about 120 hours (5 days), about 66 hours to about 96 hours (4 days), about 66 hours to about 72 hours (3 days), about 72 hours (3 days) to about 144 hours (6 days), about 72 hours (3 days) to about 120 hours (5 days), about 72 hours (3 days) to about 96 hours (4 days), about 96 hours (4 days) to about 144 hours (6 days), about 96 hours (4 days) to about 120 hours (5 days), or about 120 hours (5 days) to about 144 hours (6 days).

Additionally or alternatively, the solution formed in the method can be aged at temperature of at least about 10° C., at least about 20° C., at least about 30° C., at least about 40° C., at least about 50° C., at least about 60° C., at least about 70° C., at least about 80° C., at least about 90° C., at least about 100° C., at least about 110° C., at least about 120° C. at least about 130° C., at least about 140° C., at least about 150° C., at least about 175° C., at least about 200° C., at least about 250° C., or about 300° C.

Additionally or alternatively, the solution formed in the method can be aged at temperature of about 10° C. to about 300° C., about 10° C. to about 250° C., about 10° C. to about 200° C., about 10° C. to about 175° C., about 10° C. to about 150° C., about 10° C. to about 140° C., about 10° C. to about 130° C., about 10° C. to about 120° C., about 10° C. to about 110° C., about 10° C. to about 100° C., about 10° C. to about 90° C., about 10° C. to about 80° C., about 10° C. to about 70° C., about 10° C. to about 60° C., about 10° C. to about 50° C., about 20° C. to about 300° C., about 20° C. to about 250° C., about 20° C. to about 200° C., about 20° C. to about 175° C., about 20° C. to about 150° C., about 20° C. to about 140° C., about 20° C. to about 130° C., about 20° C. to about 120° C., about 20° C. to about 110° C., about 20° C. to about 100° C., about 20° C. to about 90° C., about 20° C. to about 80° C., about 20° C. to about 70° C., about 20° C. to about 60° C., about 20° C. to about 50° C., about 30° C. to about 300° C., about 30° C. to about 250° C., about 30° C. to about 200° C., about 30° C. to about 175° C., about 30° C. to about 150° C., about 30° C. to about 140° C., about 30° C. to about 130° C., about 30° C. to about 120° C., about 30° C. to about 110° C., about 30° C. to about 100° C., about 30° C. to about 90° C., about 30° C. to about 80° C., about 30° C. to about 70° C., about 30° C. to about 60° C., about 30° C. to about 50° C., about 50° C. to about 300° C., about 50° C. to about 250° C., about 50° C. to about 200° C., about 50° C. to about 175° C., about 50° C. to about 150° C., about 50° C. to about 140° C., about 50° C. to about 130° C., about 50° C. to about 120° C., about 50° C. to about 110° C., about 50° C. to about 100° C., about 50° C. to about 90° C., about 50° C. to about 80° C., about 50° C. to about 70° C., about 50° C. to about 60° C., about 70° C. to about 300° C., about 70° C. to about 250° C., about 70° C. to about 200° C., about 70° C. to about 175° C., about 70° C. to about 150° C., about 70° C. to about 140° C., about 70° C. to about 130° C., about 70° C. to about 120° C., about 70° C. to about 110° C., about 70° C. to about 100° C., about 70° C. to about 90° C., about 70° C. to about 80° C., about 80° C. to about 300° C., about 80° C. to about 250° C., about 80° C. to about 200° C., about 80° C. to about 175° C., about 80° C. to about 150° C., about 80° C. to about 140° C., about 80° C. to about 130° C., about 80° C. to about 120° C., about 80° C. to about 110° C., about 80° C. to about 100° C., about 80° C. to about 90° C., about 90° C. to about 300° C., about 90° C. to about 250° C., about 90° C. to about 200° C., about 90° C. to about 175° C., about 90° C. to about 150° C., about 90° C. to about 140° C., about 90° C. to about 130° C., about 90° C. to about 120° C., about 90° C. to about 110° C., about 90° C. to about 100° C., about 100° C. to about 300° C., about 100° C. to about 250° C., about 100° C. to about 200° C., about 100° C. to about 175° C., about 100° C. to about 150° C., about 100° C. to about 140° C., about 100° C. to about 130° C., about 100° C. to about 120° C., about 100° C. to about 110° C., about 110° C. to about 300° C., about 110° C. to about 250° C., about 110° C. to about 200° C., about 110° C. to about 175° C., about 110° C. to about 150° C., about 110° C. to about 140° C., about 110° C. to about 130° C., about 110° C. to about 120° C., about 120° C. to about 300° C., about 120° C. to about 250° C., about 120° C. to about 200° C., about 120° C. to about 175° C., about 120° C. to about 150° C., about 120° C. to about 140° C., about 120° C. to about 130° C., about 130° C. to about 300° C., about 130° C. to about 250° C., about 130° C. to about 200° C., about 130° C. to about 175° C., about 130° C. to about 150° C., or about 130° C. to about 140° C.

III.I. Drying the Pre-Product

The methods described herein comprise drying the pre-product (e.g., a gel) to produce an organosilica material.

In some embodiments, the pre-product (e.g., a gel) formed in the method can be dried at a temperature of greater than or equal to about 50° C., greater than or equal to about 70° C., greater than or equal to about 80° C., greater than or equal to about 100° C., greater than or equal to about 110° C., greater than or equal to about 120° C., greater than or equal to about 150° C., greater than or equal to about 200° C., greater than or equal to about 250° C., greater than or equal to about 300° C., greater than or equal to about 350° C., greater than or equal to about 400° C., greater than or equal to about 450° C., greater than or equal to about 500° C., greater than or equal to about 550° C., or greater than or equal to about 600° C.

Additionally or alternatively, the pre-product (e.g., a gel) formed in the method can be dried at temperature of about 50° C. to about 600° C., about 50° C. to about 550° C., about 50° C. to about 500° C., about 50° C. to about 450° C., about 50° C. to about 400° C., about 50° C. to about 350° C., about 50° C. to about 300° C., about 50° C. to about 250° C., about 50° C. to about 200° C., about 50° C. to about 150° C., about 50° C. to about 120° C., about 50° C. to about 110° C., about 50° C. to about 100° C., about 50° C. to about 80° C., about 50° C. to about 70° C., about 70° C. to about 600° C., about 70° C. to about 550° C., about 70° C. to about 500° C., about 70° C. to about 450° C., about 70° C. to about 400° C., about 70° C. to about 350° C., about 70° C. to about 300° C., about 70° C. to about 250° C., about 70° C. to about 200° C., about 70° C. to about 150° C., about 70° C. to about 120° C., about 70° C. to about 110° C., about 70° C. to about 100° C., about 70° C. to about 80° C., about 80° C. to about 600° C., about 70° C. to about 550° C., about 80° C. to about 500° C., about 80° C. to about 450° C., about 80° C. to about 400° C., about 80° C. to about 350° C., about 80° C. to about 300° C., about 80° C. to about 250° C., about 80° C. to about 200° C., about 80° C. to about 150° C., about 80° C. to about 120° C., about 80° C. to about 110° C., or about 80° C. to about 100° C.

In a particular embodiment, the pre-product (e.g., a gel) formed in the method can be dried at temperature from about 70° C. to about 200° C.

Additionally or alternatively, the pre-product (e.g., a gel) formed in the method can be dried in a N₂and/or air atmosphere.

III.K. Optional Further Steps

In some embodiments, the method can further comprise calcining the organosilica material to obtain a silica material. The calcining can be performed in air or an inert gas, such as nitrogen or air enriched in nitrogen. Calcining can take place at a temperature of at least about 300° C., at least about 350° C., at least about 400° C., at least about 450° C., at least about 500° C., at least about 550° C., at least about 600° C., or at least about 650° C., for example at least about 400° C. Additionally or alternatively, calcining can be performed at a temperature of about 300° C. to about 650° C., about 300° C. to about 600° C., about 300° C. to about 550° C., about 300° C. to about 400° C., about 300° C. to about 450° C., about 300° C. to about 400° C., about 300° C. to about 350° C., about 350° C. to about 650° C., about 350° C. to about 600° C., about 350° C. to about 550° C., about 350° C. to about 400° C., about 350° C. to about 450° C., about 350° C. to about 400° C., about 400° C. to about 650° C., about 400° C. to about 600° C., about 400° C. to about 550° C., about 400° C. to about 500° C., about 400° C. to about 450° C., about 450° C. to about 650° C., about 450° C. to about 600° C., about 450° C. to about 550° C., about 450° C. to about 500° C., about 500° C. to about 650° C., about 500° C. to about 600° C., about 500° C. to about 550° C., about 550° C. to about 650° C., about 550° C. to about 600° C. or about 600° C. to about 650° C.

IV. ORGANOSILICA MATERIAL PRODUCT-BY-PROCESS

Organosilica materials can be made from the methods described herein. In another particular embodiment, organosilica materials made from an aqueous mixture as described herein that contains essentially no structure directing agent or porogen as described herein, wherein the organosilica material may be:

(i) a copolymer of:

- (a) at least one independent unit of Formula (I) as described herein:
- (b) at least one independent unit of Formula (II) as described herein and/or at least one independent unit of Formula (III) as described herein; and
- (c) optionally, at least one independent unit of Formula (IV) as described herein, Formula (V) as described herein, and/or at least one unit of Formula (VI) as described herein.

The organosilica materials made from the methods described herein may exhibit an XRD pattern as described herein, particularly with only one peak between about 0.5 and about 3 degrees 2θ. Additionally or alternatively, the organosilica materials made from the methods described herein can exhibit substantially no peaks in the range of about 0.5 to about 10 degrees 2θ, about 0.5 to about 12 degrees 2θ range, about 0.5 to about 15 degrees 2θ, about 0.5 to about 20 degrees 2θ, about 0.5 to about 30 degrees 2θ, about 0.5 to about 40 degrees 2θ, about 0.5 to about 50 degrees 2θ, about 0.5 to about 60 degrees 2θ, about 0.5 to about 70 degrees 2θ, about 2 to about 10 degrees 2θ, about 2 to about 12 degrees 2θ range, about 2 to about 15 degrees 2θ, about 2 to about 20 degrees 2θ, about 2 to about 30 degrees 2θ, about 2 to about 40 degrees 2θ, about 2 to about 50 degrees 2θ, about 2 to about 60 degrees 2θ, about 2 to about 70 degrees 2θ, about 3 to about 10 degrees 2θ, about 3 to about 12 degrees 2θ range, about 3 to about 15 degrees 2θ, about 3 to about 20 degrees 2θ, about 3 to about 30 degrees 2θ, about 3 to about 40 degrees 2θ, about 3 to about 50 degrees 2θ, about 3 to about 60 degrees 2θ, or about 3 to about 70 degrees 2θ.

Additionally or alternatively, the organosilica materials may have an average pore diameter as described herein, particularly, between about 2.0 nm and about 25.0 nm.

V. USES OF THE ORGANOSILICA MATERIALS

The organosilica materials described herein find uses in several areas.

In certain embodiments, the organosilica material described herein can be used as adsorbents or support matrices for separation and/or catalysis processes.

V.A. Gas Separation Processes

In some cases, the organosilica materials can be used in a gas separation process as provided herein. In various aspects, a gas separation process is provided herein. The gas separation process can comprise contacting a gas mixture containing at least one contaminant with the organosilica material described herein as prepared according to the methods described herein.

In various embodiments, the gas separation process can be achieved by swing adsorption processes, such as pressure swing adsorption (PSA) and temperature swing adsorption (TSA). All swing adsorption processes typically have an adsorption step in which a feed mixture (typically in the gas phase) is flowed over an adsorbent to preferentially adsorb a more readily adsorbed component relative to a less readily adsorbed component. A component may be more readily adsorbed because of kinetic or equilibrium properties of the adsorbent. The adsorbent (e.g., the organosilica material described herein) can typically be contained in a contactor that is part of the swing adsorption unit. The contactor can typically contain an engineered structured adsorbent bed or a particulate adsorbent bed. The bed can contain the adsorbent (e.g., the organosilica material described herein) and other materials such as other adsorbents, mesopore filling materials, and/or inert materials used to mitigated temperature excursions from the heat of adsorption and desorption. Other components in the swing adsorption unit can include, but are not necessarily limited to, valves, piping, tanks, and other contactors. Swing adsorption processes are described in detail in U.S. Pat. Nos. 8,784,533; 8,784,534; 8,858,683; and 8,784,535, each of which are incorporated herein by reference. Examples of processes that can be used herein either separately or in combination are PSA, TSA, pressure temperature swing adsorption (PTSA), partial purge displacement swing adsorption (PPSA), PPTSA, rapid cycle PSA (RCPSA), RCTSA, RCPPSA and RCPTSA.

PSA processes rely on the fact that gases under pressure tend to be adsorbed within the pore structure of the adsorbent materials (e.g., the organosilica material described herein). Typically, the higher the pressure, the greater the amount of targeted gas component that will be adsorbed. When the pressure is reduced, the adsorbed targeted component is typically released, or desorbed. PSA processes can be used to separate gases of a gas mixture, because different gases tend to fill the pores or free volume of the adsorbent to different extents due to either the equilibrium or kinetic properties of the adsorbent. In many important applications, to be described as “equilibrium-controlled” processes, the adsorptive selectivity is primarily based upon differential equilibrium uptake of the first and second components. In another important class of applications, to be described as “kinetic-controlled” processes, the adsorptive selectivity is primarily based upon the differential rates of uptake of the first and second components.

If a gas mixture, such as natural gas, is passed under pressure through a vessel containing a polymeric or microporous adsorbent that is more selective towards carbon dioxide than it is for methane, at least a portion of the carbon dioxide can be selectively adsorbed by the adsorbent, and the gas exiting the vessel can be enriched in methane. When the adsorbent (e.g., the organosilica material described herein) reaches the end of its capacity to adsorb carbon dioxide, it can be regenerated by reducing the pressure, thereby releasing the adsorbed carbon dioxide. The adsorbent can then typically purged and repressurized and ready for another adsorption cycle.

TSA processes also rely on the fact that gases under pressure tend to be adsorbed within the pore structure of the adsorbent materials. When the temperature of the adsorbent (e.g., the organosilica material described herein) is increased, the adsorbed gas is typically released, or desorbed. By cyclically swinging the temperature of adsorbent beds, TSA processes can be used to separate gases in a mixture when used with an adsorbent selective for one or more of the components in a gas mixture. Partial pressure purge displacement (PPSA) swing adsorption processes regenerate the adsorbent with a purge. Rapid cycle (RC) swing adsorption processes complete the adsorption step of a swing adsorption process in a short amount of time. For kinetically selective adsorbents, it can be preferable to use a rapid cycle swing adsorption process. If the cycle time becomes too long, the kinetic selectivity can be lost. These swing adsorption protocols can be performed separately or in combinations. Examples of processes that can be used herein either separately or in combination are PSA, TSA, pressure temperature swing adsorption (PTSA), partial purge displacement swing adsorption (PPSA), PPTSA, rapid cycle PSA (RCPSA), RCTSA, vacuum pressure swing adsorption (VPSA), RCPPSA and RCPTSA.

In PSA processes, a feed gas mixture containing the first and second gas components is separated by cyclic variations of pressure coordinated with cyclic reversals of flow direction in a flow path contacting a fixed bed of the adsorbent material in an adsorber vessel. In the case of TSA or PPSA processes, cyclic variations of temperature and/or partial pressure of the gas components may be coordinated with gas flow through a flow path to perform a separation. The process in any specific PSA application operates at a cyclic frequency characterized by its period, and over a pressure envelope between a first relatively higher pressure and a second relatively lower pressure. Separation in PSA is achieved by coordinating the pressure variations with the flow pattern within the flow path, so that the gas mixture in the flow path is enriched in the second component (owing to preferential adsorptive uptake of the first component in the adsorbent material) when flowing in a first direction in the flow path, while the gas mixture is enriched in the first component (which has been desorbed by the adsorbent material) when flowing in the opposite direction in the flow path. In order to achieve separation performance objectives (i.e. product gas purity, recovery and productivity), process parameters and operating conditions should be designed to achieve a sufficiently high adsorptive selectivity of the first and second components over the adsorbent material, at the cyclic frequency and within the pressure envelope.

Swing adsorption processes can be applied to remove a variety of target gases, also referred to as “contaminant gas” from a wide variety of gas mixtures. Typically, in binary separation systems, the “light component” as utilized herein is taken to be the species or molecular component(s) not preferentially taken up by the adsorbent in the adsorption step of the process. Conversely in such binary systems, the “heavy component” as utilized herein is typically taken to be the species or molecular component(s) preferentially taken up by the adsorbent in the adsorption step of the process. However, in binary separation systems where the component(s) that is(are) preferentially adsorbed has(have) a lower molecular weight than the component(s) that is(are) not preferentially adsorbed, those descriptions may not necessarily correlate as disclosed above.

An example of gas mixture that can be separated in the methods described herein is a gas mixture comprising CH₄, such as a natural gas stream. A gas mixture comprising CH₄can contain significant levels of contaminants such as H₂O, H₂S, CO₂, N₂, mercaptans, and/or heavy hydrocarbons. Additionally or alternatively, the gas mixture can comprise NO_xand/or SO_xspecies as contaminants, such as a waste gas stream, a flue gas stream and a wet gas stream. As used herein, the terms “NO_x,” and “NO_x” species refers to the various oxides of nitrogen that may be present in waste gas, such as waste gas from combustion processes. The terms refer to all of the various oxides of nitrogen including, but not limited to, nitric oxide (NO), nitrogen dioxide (NO₂), nitrogen peroxide (N₂O), nitrogen pentoxide (N₂O₅), and mixtures thereof. As used herein, the terms “SO_x,” and “SO_xspecies,” refers to the various oxides of sulfur that may be present in waste gas, such as waste gas from combustion processes. The terms refer to all of the various oxides of sulfur including, but not limited to, SO, SO₂, SO₃, SO₄, S₇O₂and S₆O₂. Thus, examples of contaminants include, but are not limited to H₂O, H₂S, CO₂, N₂, mercaptans, heavy hydrocarbons, NO_xand/or SO_xspecies. In particular, the gas mixture may comprise CH₄and the at least one contaminant is CO₂and/or H₂S.

In various aspects, a process for selectively separating a contaminant from a feed gas mixture is provided herein. The process may comprise: a) contacting the feed gas mixture under sorption conditions with organosilica material described herein; b) adsorbing the contaminant into/onto the organosilica material described herein; c) subjecting the organosilica material described herein to desorption conditions by which at least a portion of the sorbed contaminant is desorbed; and d) retrieving a contaminant-rich product stream that has a higher mol % of contaminant than the feed gas mixture. The feed gas mixture may be any of the gas mixtures described above. Particularly, the feed gas mixture may comprise CH₄. The contaminant may be any of the contaminants described above, e.g., CO₂, H₂S, etc.

It may be desirable to operate with a multiplicity of structure adsorbent beds, with several coupled in a heating/cooling operation and others involved in adsorption (and/or desorption). In such an operation, the adsorbent bed can be substantially cooled by a circulating heat transfer medium before it is switched into service for adsorption. One advantage of such an operation can be that the thermal energy used to swing the bed is retained in the heat transfer medium. If adsorption were to proceed simultaneously with cooling, then a substantial part of the heat in the bed could be lost to the adsorbate-free feed, and a higher heat load could be needed to restore the high temperature of the heat transfer medium.

Adsorptive kinetic separation (AKS) processes, as described above, are useful for development and production of hydrocarbons, such as gas and oil processing. Particularly, as described in U.S. Patent Application Publication No. 2013/032716, which is herein incorporated by reference in its entirety, the AKS processes described herein can use one or more kinetic swing adsorption process, such as pressure swing adsorption (PSA), thermal swing adsorption (TSA), calcination, and partial pressure swing or displacement purge adsorption (PPSA), including combinations of these processes; each swing adsorption process may be utilized with rapid cycles, such as using one or more rapid cycle pressure swing adsorption (RC-PSA) units, with one or more rapid cycle temperature swing adsorption (RC-TSA) units or with one or more rapid cycle partial pressure swing adsorption (RC-PPSA) units; exemplary kinetic swing adsorption processes are described in U.S. Pat. Nos. 7,959,720; 8,545,602; 8,529,663; 8,444,750; and 8,529,662 and U.S. Provisional Application Nos. 61/448,121; 61/447,848; 61/447,869; and 61/447,877, which are each herein incorporated by reference in its entirety. The provided processes, can be useful for rapid, large scale, efficient separation of a variety of target gases from gas mixtures.

The provided processes and apparatuses may be used to prepare natural gas products by removing contaminants. The provided processes and apparatuses can be useful for preparing gaseous feed streams for use in utilities, including separation applications such as dew point control, sweetening/detoxification, corrosion protection/control, dehydration, heating value, conditioning, and purification. Examples of utilities that utilize one or more separation applications can include generation of fuel gas, seal gas, non-potable water, blanket gas, instrument and control gas, refrigerant, inert gas, and hydrocarbon recovery. Exemplary “not to exceed” product (or “target”) acid gas removal specifications can include: (a) 2 vol % CO₂, 4 ppm H₂S; (b) 50 ppm CO₂, 4 ppm H₂S; or (c) 1.5 vol % CO₂, 2 ppm H₂S.

The provided processes and apparatuses may also be used to remove acid gas from hydrocarbon streams. Acid gas removal technology becomes increasingly important as remaining gas reserves exhibit higher concentrations of acid (sour) gas resources. Hydrocarbon feed streams can vary widely in amount of acid gas, such as from several parts per million to 90 vol %. Non-limiting examples of acid gas concentrations from exemplary gas reserves can include concentrations of at least: (a) 1 vol % H₂S, 5 vol % CO₂; (b) 1 vol % H₂S, 15 vol % CO₂; (c) 1 vol % H₂S, 60 vol % CO₂; (d) 15 vol % H₂S, 15 vol % CO₂; or (e) 15 vol % H₂S, 30 vol % CO₂.

One or more of the following may be utilized with the processes and apparatuses provided herein, to prepare a desirable product stream, while maintaining relatively high hydrocarbon recovery:

(a) removing acid gas with RC-TSA using advanced cycles and purges as described in U.S. Provisional Application No. 61/447,854, filed Mar. 1, 2011, as well as the U.S. Pat. No. 8,784,533, which are together incorporated by reference herein in their entirety;

(b) using a mesopore filler to reduce the amount of trapped methane in the adsorbent bed and increase the overall hydrocarbon recovery, as described in U.S. Pat. Nos. 7,959,720; 8,444,750; and 8,529,663, each of which is herein incorporated by reference in its entirety;

(c) depressurizing one or more RC-TSA units in multiple steps to intermediate pressures so that the acid gas exhaust can be captured at a higher average pressure, thereby decreasing the compression required for acid gas injection; pressure levels for the intermediate depressurization steps may be matched to the interstage pressures of the acid gas compressor to optimize the overall compression system;

(d) using exhaust or recycle streams to minimize processing and hydrocarbon losses, such as using exhaust streams from one or more RC-TSA units as fuel gas instead of re-injecting or venting;

(e) using multiple adsorbent particles in a single bed to remove trace amounts of first contaminants, such as H₂S, before removal of a second contaminant, such as CO₂; such segmented beds may provide rigorous acid gas removal down to ppm levels with RC-TSA units with minimal purge flow rates;

(f) using feed compression before one or more RC-TSA units to achieve a desired product purity;

(g) contemporaneous removal of non-acid gas contaminants such as mercaptans, COS, and BTEX; selection processes and materials to accomplish the same;

(h) selecting a cycle time and cycle steps based on adsorbent material kinetics; and

(i) using a process and apparatus that uses, among other equipment, two RC-TSA units in series, wherein the first RC-TSA unit cleans a feed stream down to a desired product purity and the second RC-TSA unit cleans the exhaust from the first unit to capture methane and maintain high hydrocarbon recovery; use of this series design may reduce the need for a mesopore filler.

The processes, apparatuses, and systems provided herein can be useful in large gas treating facilities, such as facilities that process more than five million standard cubic feet per day (MSCFD) of natural gas, for example more than 15 MSCFD, more than 25 MSCFD, more than 50 MSCFD, more than 100 MSCFD, more than 500 MSCFD, more than one billion standard cubic feet per day (BSCFD), or more than two BSCFD.

V.B. Aromatic Hydrogenation Process

The organosilica materials made according to the methods described herein can be used as support materials in hydrogenation catalysts. In particular, the hydrogenation catalyst can comprise the organosilica materials as a support material where the organosilica material has at least one catalyst metal incorporated on the pore surface. The at least one catalyst metal may be a Group 8 metal, a Group 9 metal, a Group 10 metal, e.g., Pt, Pd, Ir, Rh, Ru or a combination thereof. The hydrogenation catalyst can further comprise a binder such as, but not limited to, active and inactive materials, inorganic materials, clays, ceramics, activated carbon, alumina, silica, silica-alumina, titania, zirconia, niobium oxide, tantalum oxide, or a combination thereof, particularly, silica-alumina, alumina, titania, or zirconia. These hydrogenation catalysts can be used for both hydrogenation and aromatic saturation of a feedstream.

In various embodiments, the hydrogenation process can be achieved by contacting a hydrocarbon feedstream comprising aromatics with a hydrogenation catalyst described herein in the presence of a hydrogen-containing treat gas in a first reaction stage operated under effective aromatics hydrogenation conditions to produce a reaction product with reduced aromatics content.

Hydrogen-containing treat gasses suitable for use in a hydrogenation process can be comprised of substantially pure hydrogen or can be mixtures of other components typically found in refinery hydrogen streams. It is preferred that the hydrogen-containing treat gas stream contains little, more preferably no, hydrogen sulfide. The hydrogen-containing treat gas purity should be at least about 50% by volume hydrogen, preferably at least about 75% by volume hydrogen, and more preferably at least about 90% by volume hydrogen for best results. It is most preferred that the hydrogen-containing stream be substantially pure hydrogen.

Feedstreams suitable for hydrogenation by the hydrogenation catalyst described herein include any conventional hydrocarbon feedstreams where hydrogenation or aromatic saturation is desirable. Typically, an input feed for an aromatic saturation process can be generated as a product or side-product from a previous type of hydroprocessing, such as hydrocracking for fuels or lubricant base stock production. A wide range of petroleum and chemical feedstocks can be hydroprocessed. Such feedstreams can include hydrocarbon fluids, diesel, kerosene, lubricating oil feedstreams, heavy coker gasoil (HKGO), de-asphalted oil (DAO), FCC main column bottom (MCB), steam cracker tar. Such feedstreams can also include other distillate feedstreams such as light to heavy distillates including raw virgin distillates, wax-containing feedstreams such as feeds derived from crude oils, shale oils and tar sands. Synthetic feeds such as those derived from the Fischer-Tropsch process can also be aromatically saturated using the hydrogenation catalyst described herein. Typical wax-containing feedstocks for the preparation of lubricating base oils have initial boiling points of about 315° C. or higher, and include feeds such as whole and reduced petroleum crudes, hydrocrackates, raffinates, hydrotreated oils, gas oils (such as atmospheric gas oils, vacuum gas oils, and coker gas oils), atmospheric and vacuum residues, deasphalted oils/residua (e.g., propane deasphalted residua, brightstock, cycle oil), dewaxed oils, slack waxes and Fischer-Tropsch wax, and mixtures of these materials. Such feeds may be derived from distillation towers (atmospheric and vacuum), hydrocrackers, hydrotreaters and solvent extraction units, and may have wax contents of up to 50% or more. Preferred lubricating oil boiling range feedstreams include feedstreams which boil in the range of 650-1100° F. Diesel boiling range feedstreams include feedstreams which boil in the range of 480-660° F. Kerosene boiling range feedstreams include feedstreams which boil in the range of 350-617° F.

Hydrocarbon feedstreams suitable for use herein also contain aromatics and nitrogen- and sulfur-contaminants. Feedstreams containing up to 0.2 wt. % of nitrogen, based on the feedstream, up to 3.0 wt. % of sulfur, and up to 50 wt. % aromatics can be used in the present process In various embodiments, the sulfur content of the feedstreams can be below about 500 wppm, or below about 300 wppm, or below about 200 wppm, or below about 100 wppm, or below about 50 wppm, or below about 15 wppm. The pressure used during an aromatic hydrogenation process can be modified based on the expected sulfur content in a feedstream. Feeds having a high wax content typically have high viscosity indexes of up to 200 or more. Sulfur and nitrogen contents may be measured by standard ASTM methods D2622 (sulfur), and D5453 and/or D4629 (nitrogen), respectively.

Effective hydrogenation conditions may be considered to be those conditions under which at least a portion of the aromatics present in the hydrocarbon feedstream are saturated, preferably at least about 50 wt. % of the aromatics are saturated, more preferably greater than about 75 wt. %. Effective hydrogenation conditions can include temperatures of from 150° C. to 400° C., a hydrogen partial pressure of from 740 to 20786 kPa (100 to 3000 psig), a space velocity of from 0.1 to 10 liquid hourly space velocity (LHSV), and a hydrogen to feed ratio of from 89 to 1780 m³/m³(500 to 10000 scf/B).

Additionally or alternatively, effective hydrogenation conditions may be conditions effective at removing at least a portion of the nitrogen and organically bound sulfur contaminants and hydrogenating at least a portion of said aromatics, thus producing at least a liquid lube boiling range product having a lower concentration of aromatics and nitrogen and organically bound sulfur contaminants than the lube boiling range feedstream.

Additionally or alternatively, effective hydrogenation conditions may be conditions effective at removing at least a portion of the nitrogen and organically bound sulfur contaminants and hydrogenating at least a portion of said aromatics, thus producing at least a liquid diesel boiling range product having a lower concentration of aromatics and nitrogen and organically bound sulfur contaminants than the diesel boiling range feedstream.

As stated above, in some instances, the hydrocarbon feedstream (e.g., lube oil boiling range) may be hydrotreated to reduce the sulfur contaminants to below about 500 wppm, particularly below about 300 wppm, particularly below about 200 wppm or particularly below about 100 wppm. In such an embodiment, the process may comprise at least two reaction stages, the first reaction state containing a hydrotreating catalyst operated under effective hydrotreating conditions, and the second containing a hydrogenation catalyst has described herein operated under effective hydrogenation conditions as described above. Therefore, in such an embodiment, the hydrocarbon feedstream can be first contacted with a hydrotreating catalyst in the presence of a hydrogen-containing treat gas in a first reaction stage operated under effective hydrotreating conditions in order to reduce the sulfur content of the feedstream to within the above-described range. Thus, the term “hydrotreating” as used herein refers to processes wherein a hydrogen-containing treat gas is used in the presence of a suitable catalyst that is active for the removal of heteroatoms, such as sulfur, and nitrogen. Suitable hydrotreating catalysts for use in the present invention are any conventional hydrotreating catalyst and includes those which are comprised of at least one Group 8 metal, preferably Fe, Co and Ni, more preferably Co and/or Ni, and most preferably Ni; and at least one Group 6 metal, preferably Mo and W, more preferably Mo, on a high surface area support material, preferably alumina. Additionally or alternatively, more than one type of hydrotreating catalyst can be used in the same reaction vessel. The Group 8 metal may typically be present in an amount ranging from about 2 to 20 wt. %, preferably from about 4 to 12 wt. %. The Group 6 metal can typically be present in an amount ranging from about 5 to 50 wt. %, preferably from about 10 to 40 wt. %, and more preferably from about 20 to 30 wt. %. All metals weight percents are “on support” as described above.

Effective hydrotreating conditions may be considered to be those conditions that can effectively reduce the sulfur content of the feedstream (e.g., lube oil boiling range) to within the above-described ranges. Typical effective hydrotreating conditions can include temperatures ranging from about 150° C. to about 425° C., preferably about 200° C. to about 370° C., more preferably about 230° C. to about 350° C. Typical weight hourly space velocities (“WHSV”) may range from about 0.1 to about 20 hr⁻¹, preferably from about 0.5 to about 5 hr⁻¹. Any effective pressure can be utilized, and pressures can typically range from about 4 to about 70 atmospheres (405 to 7093 kPa), preferably 10 to 40 atmospheres (1013 to 4053 kPa). In a particular embodiment, said effective hydrotreating conditions may be conditions effective at removing at least a portion of said organically bound sulfur contaminants and hydrogenating at least a portion of said aromatics, thus producing at least a reaction product (e.g., liquid lube oil boiling range product) having a lower concentration of aromatics and organically bound sulfur contaminants than the lube oil boiling range feedstream.

The contacting of the hydrocarbon feedstream with the hydrotreating catalyst may produce a reaction product comprising at least a vapor product and a liquid product. The vapor product may typically comprise gaseous reaction products, such as H₂S, and the liquid reaction product may typically comprise a liquid hydrocarbon having a reduced level of nitrogen and sulfur contaminants. The total reaction product can be passed directly into the second reaction stage, but it may be preferred that the gaseous and liquid reaction products be separated, and the liquid reaction product conducted to the second reaction stage. Thus, in one embodiment, the vapor product and the liquid product may be separated, and the liquid product may be conducted to the second reaction stage. The method of separating the vapor product from the liquid product can be accomplished by any means known to be effective at separating gaseous and liquid reaction products. For example, a stripping tower or reaction zone can be used to separate the vapor product from the liquid product (e.g., liquid lube oil boiling range product). The liquid product thus conducted to the second reaction stage can have a sulfur concentration within the range of about 500 wppm, particularly below about 300 wppm, or particularly below about 200 wppm or particularly below about 100 wppm.

In still other embodiments, the hydrogenation catalysts described herein can be used in integrated hydroprocessing methods. In addition to the hydrofinishing and/or aromatic hydrogenation/saturation processes involving the hydrogenation catalyst described herein, an integrated hydroprocessing method can also include various combinations of hydrotreating, hydrocracking, catalytic dewaxing (such as hydrodewaxing), and/or solvent dewaxing. The scheme of hydrotreating followed by hydrofinishing described above represents one type of integrated process flow. Another integrated processing example is to have a dewaxing step, either catalytic dewaxing or solvent dewaxing, followed by hydroprocessing with the hydrogenation catalysts described herein. Still another example is a process scheme involving hydrotreating, dewaxing (catalytic or solvent), and then hydroprocessing with the hydrogenation catalysts described herein. Yet another example is hydroprocessing with the hydrogenation catalysts described herein followed by dewaxing (catalytic or solvent). Alternatively, multiple hydrofinishing and/or aromatic hydrogenation steps can be employed with hydrotreatment, hydrocracking, or dewaxing steps. An example of such a process flow is hydrofinishing, dewaxing (catalytic or solvent), and then hydrofinishing again, where at least one of the hydrofinishing steps may use a hydrogenation catalysts described herein. For processes involving catalytic dewaxing, effective catalytic dewaxing conditions can include temperatures of from 150° C. to 400° C., preferably 250° C. to 350° C., pressures of from 791 to 20786 kPa (100 to 3000 psig), preferably 1480 to 17338 kPa (200 to 2500 psig), liquid hourly space velocities of from 0.1 to 10 hr⁻¹, preferably 0.1 to 5 hr⁻¹and hydrogen treat gas rates from 45 to 1780 m³/m³(250 to 10000 scf/B), preferably 89 to 890 m³/m³(500 to 5000 scf/B). Any suitable dewaxing catalyst may be used.

In embodiments where the product of an aromatic saturation process will be a lubricant base oil, the input feed should also have suitable lubricant base oil properties. For example, an input feed intended for use as a Group I or Group II base oil can have a viscosity index (VI) of at least about 80, preferably at least about 90 or at least about 95. An input feed intended for use as a Group I+ base oil can have a VI of at least about 100, while an input feed intended for use as a Group II+ base oil can have a VI of at least 110. The viscosity of the input feed can be at least 2 cSt at 100° C., or at least 4 cSt at 100° C., or at least 6 cSt at 100° C.

VI. FURTHER EMBODIMENTS

The invention can additionally or alternately include one or more of the following embodiments.

Embodiment 1

An organosilica material, which is a polymer of at least one independent monomer of Formula [Z¹OZ²OSiCH₂]₃(I), wherein Z¹and Z²each independently represent a hydrogen atom, a C₁-C₄alkyl group or a bond to a silicon atom of another monomer and at least one other monomer selected from the group consisting of:

- (i) an independent unit of Formula Z³OZ⁴Z⁵Z⁶(II), wherein each Z³represents a hydrogen atom, a C₁-C₄alkyl group or a bond to a silicon atom of another monomer; and Z⁴, Z⁵and Z⁶are each independently selected from the group consisting of a hydroxyl group, a C₁-C₄alkyl group, a C₁-C₄alkoxy group, a nitrogen-containing C₁-C₁₀alkyl group, a nitrogen-containing heteroaralkyl group, a nitrogen-containing optionally substituted heterocycloalkyl group, and an oxygen atom bonded to a silicon atom of another monomer;
- (ii) an independent unit of Formula Z⁷Z⁸Z⁹Si—R¹—SiZ⁷Z⁸Z⁹(III), wherein each Z⁷independently represents a hydroxyl group, a C₁-C₄alkoxy group or an oxygen bonded to a silicon atom of another comonomer; each Z8 and Z9 independently represent a hydroxyl group, a C₁-C₄alkoxy group, a C₁-C₄alkyl group or an oxygen bonded to a silicon atom of another monomer; and each R¹represents a nitrogen-containing C₂-C₁₀alkylene group; and
- (iii) a combination thereof.

Embodiment 2

The organosilica material of embodiment 1, wherein Z¹and Z²each independently represent a hydrogen atom, a C₁-C₂alkyl group or a bond to a silicon atom of another monomer.

Embodiment 3

The organosilica material of embodiment 1 or 2, wherein Z¹and Z²each independently represent a hydrogen atom, ethoxy or a bond to a silicon atom of another monomer.

Embodiment 4

The organosilica material of any one of the previous embodiments, wherein at least one independent unit of Formula (II) is present, wherein each Z³represents a hydrogen atom, a C₁-C₂alkyl group or a bond to a silicon atom of another comonomer; and Z⁴, Z⁵and Z⁶are each independently selected from the group consisting of a hydroxyl group, a C₁-C₂alkyl group, C₁-C₂alkoxy group, a nitrogen-containing C₄-C₁₀alkyl group, a nitrogen-containing C₄-C₁₀heteroaralkyl group, or a nitrogen-containing optionally substituted C₄-C₁₀heterocycloalkyl group.

Embodiment 5

The organosilica material of embodiment 4, wherein each Z³represents a hydrogen atom, methyl, ethyl, or a bond to a silicon atom of another comonomer; and Z⁴, Z⁵and Z⁶are each independently selected from the group consisting of a hydroxyl group, methoxy, ethoxy

embedded image

and an oxygen bonded to a silicon atom of another monomer.

Embodiment 6

The organosilica material of any one of the previous embodiments, wherein at least one independent unit of Formula (III) is present, wherein each Z⁷represents a hydroxyl group, a C₁-C₂alkoxy group or an oxygen bonded to a silicon atom of another monomer; each Z8 and Z9 independently represent a hydroxyl group, a C₁-C₂alkoxy group, a C₁-C₂alkyl group or an oxygen bonded to a silicon atom of another monomer; and each R¹represents a nitrogen-containing C₄-C₁₀alkyl group.

Embodiment 7

The organosilica material of embodiment 6, wherein each Z⁷represents a hydroxyl group, methoxy, ethoxy, or an oxygen bonded to a silicon atom of another monomer; each Z⁸and Z⁹independently represent a hydroxyl group, methoxy, ethoxy, methyl or an oxygen bonded to a silicon atom of another monomer; and each R¹is selected from the group consisting of

embedded image

Embodiment 8

The organosilica material of any one of the previous embodiments further comprising a monomer selected from the group consisting of:

- (i) an independent unit of Formula [Z¹⁰OZ¹¹SiCH₂]₃(IV), wherein each Z¹⁰represents a hydrogen atom, a C₁-C₄alkyl group or a bond to a silicon atom of another monomer and each Z¹¹represents a hydroxyl group, a C₁-C₆alkyl group or an oxygen atom bonded to a silicon atom of another monomer;
- (ii) an independent unit of Formula Z¹²OZ¹³Z¹⁴Z¹⁵Si (V), wherein each Z²represents a hydrogen atom or a C₁-C₄alkyl group or a bond to a silicon atom of another monomer; and Z¹³, Z¹⁴and Z¹⁵are each independently selected from the group consisting of a hydroxyl group, a C₁-C₄alkyl group, a C₁-C₄alkoxy group, and an oxygen atom bonded to a silicon atom of another monomer;
- (iii) an independent unit of Formula Z¹⁶Z¹⁷Z¹⁸Si—R²—SiZ¹⁶Z¹⁷Z¹⁸(VI), wherein each Z¹⁶independently represents a hydroxyl group, a C₁-C₄alkoxy group or an oxygen bonded to a silicon atom of another comonomer; each Z¹⁷and Z¹⁸independently represent a hydroxyl group, a C₁-C₄alkoxy group, a C₁-C₄alkyl group or an oxygen bonded to a silicon atom of another monomer; and each R²is selected from the group consisting of a C₁-C₈alkylene group, a C₂-C₈alkenylene group, a C₂-C₈alkynylene group an optionally substituted C₆-C₂₀aralkyl and an optionally substituted C₄-C₂₀heterocycloalkyl group; and
- (iv) a combination thereof.

Embodiment 9

The organosilica material of any one of the previous embodiments, wherein the organosilica has an average pore diameter between about 2.0 nm and about 25.0 nm.

Embodiment 10

The organosilica material of any one of the previous embodiments, wherein the organosilica material has a total surface area of about 500 m²/g to about 2000 m²/g.

Embodiment 11

The organosilica material of any one of the previous embodiments, wherein the organosilica material has a pore volume of about 3.0 cm³/g to about 3.0 cm³/g.

Embodiment 12

The organosilica material of any one of the previous embodiments, further comprising at least one catalytic metal incorporated within the pores of the material.

Embodiment 13

The organosilica material of embodiment 12, wherein the catalytic metal is selected from the group consisting of a Group 6 element, a Group 8 element, a Group 9 element, a Group 10 element and a combination thereof.

Embodiment 14

The organosilica material of any one of the previous embodiments made using essentially no structure directing agent or porogen.

Embodiment 15

A gas separation process comprising contacting a gas mixture containing at least one contaminant with the organosilica material of any one of the previous embodiments.

Embodiment 16

The process of embodiment 15, wherein the gas mixture comprises CH₄and the at least one contaminant is CO₂and/or H₂S.

Embodiment 17

The process of embodiment 15 or 16, wherein the process comprises PSA, TSA, PPSA, PTSA, RCPSA, RCTSA, RC-PPSA or RC-PTSA.

Embodiment 18

A process for selectively separating a contaminant from a feed gas mixture, the process comprising:

- a) contacting the feed gas mixture under sorption conditions with the organosilica material of any one of embodiments 1-14;
- b) adsorbing the contaminant into/onto the organosilica material;
- c) subjecting the organosilica material of any one of embodiments 1-14 to desorption conditions by which at least a portion of the sorbed contaminant is desorbed; and
- d) retrieving a contaminant-rich product stream that has a higher mol % of contaminant than the feed gas mixture.

Embodiment 19

The process of embodiment 18, wherein the feed gas mixture comprises CH₄.

Embodiment 20

The process of embodiment 18 or 19, wherein the contaminant is CO₂and/or H₂S.

EXAMPLES
General Methods
Small Angle X-Ray Diffraction Analysis

X-ray powder diffraction (XRD) patterns were collected on a PANalytical X'pert diffractometer equipped with an accessory for low angle measurements. XRD analyses were recorded using the Cu Ka (=1.5405980 Å) line in the 2θ range from 0.5 to 100 with a step size of 0.0167° and a counting time of 1.2 s.

Solid-State (SS) NMR Measurements

The ²⁹Si MAS NMR spectra were recorded on a Varian InfinityPlus-400 spectrometer (operating at 9.4 T) and Varian InfinityPlus-500 (operating at 11.74 T), corresponding to ²⁹Si Larmor frequencies of 79.4 MHz and 99.2 MHz, respectively, with a 7.5 mm MAS probe heads using 5 kHz spinning, 4.0 μs 90° pulses, and at least 60 s recycle delay, with proton decoupling during data acquisition. The ²⁹Si chemical shifts are referenced with respect to an external tetramethyl silane (δ_si=0.0 ppm). The ¹³C CPMAS NMR spectra were recorded on a Varian InfinityPlus-500 spectrometer corresponding to ¹³C Larmor frequency of 125 MHz, with 1.6 mm MAS probe head using 40 kHz spinning, ¹H-¹³C cross-polarization (CP) contact time of at least 1 ms, a recycle delay of at least 1 s, with proton decoupling during data acquisition. The ¹³C chemical shifts are referenced with respect to an external tetramethyl silane (δ_C=0.0 ppm). The ²⁷Al MAS NMR spectra were recorded on a Varian InfinityPlus-500 corresponding to ²⁷Al Larmor frequency of 130.1 MHz using a 4 mm MAS probe head using 12 kHz spinning, with a π/12 radian pulse length, with proton decoupling during data acquisition, and a recycle delay of 0.3 s. The chemical shifts are referenced with respect to an external solution of Al(H₂O)₆³⁺ (δ_Al=0.0 ppm). All NMR spectra were recorded at room temperature using air for spinning.

Thermal Gravimetric Analysis (TGA)

Thermal stability results were recorded on Q5000 TGA. Ramp rate was 5° C./min, temperature range was from 25° C. to 800° C. All the samples were tested in both air and nitrogen.

CO₂Adsorption

The work was done with a Quantchrom autosorb iQ2. All the samples were pre-treated at 120° C. in vacuum for 3 hours before collecting the CO₂isotherm at different temperatures.

Nitrogen Porosimetry

The nitrogen adsorption/desorption analyses was performed with different instruments, e.g. TriStar 3000, TriStar II 3020 and Autosorb-1. All the samples were pre-treated at 120° C. in vacuum for 4 hours before collecting the N₂isotherm. The analysis program calculated the experimental data and report BET surface area (total surface area), microporous surface area (S), total pore volume, pore volume for micropores, average pore diameter (or radius), etc.

Example 1
Organosilica Material Syntheses Using Formula [R¹R²SiCH₂]₃(Ia) in Basic or Acidic Media

1A. Synthesis Using [(EtO)₂SiCH₂]₃in Basic Aqueous Medium—without Surfactant.

A solution with 18.6 g of 30% NH₄OH and 23.76 g deionized water (DI) water was made. The pH of the solution was 12.55. To the solution, 3.0 g of 1,1,3,3,5,5-hexaethoxy-1,3,5-trisilacyclohexane ([(EtO)₂SiCH₂]₃) was added, producing a mixture having the molar composition:

1.0[(EtO)₂SiCH₂]₃:21OH:270H₂O

and stirred for 1 day at room temperature (20-25° C.). The solution was transferred to an autoclave and aged at 80° C.-90° C. for 1 day to produce a gel. The gel was dried at 80° C. in a vacuum to remove most of the water and then fully dried at 110° C. for three hours. This produced Sample 1A as a clear solid, which was converted to white powder after grinding. No surface directing agent or porogen were used in this preparation.

The procedure was repeated with the following molar composition

4.0[(EtO)₂SiCH₂]₃:21OH:270H₂O

to produce Sample 1B.

XRD Analysis

XRD was performed on Sample 1A. The XRD pattern of Sample 1A is shown in FIG. 1.

TGA Analysis

TGA weight loss studies were performed on Sample 1A in nitrogen and air. FIGS. 2a and 2b display the TGA data for Sample 1A in nitrogen and air, respectively.

Nitrogen Adsorption/Desorption Analysis

Nitrogen adsorption/desorption analysis was performed on Sample 1A, and the results are provided in Table 1 below and FIGS. 3-6.

SS-NMR-Analysis

Sample 1A was characterized with ²⁹Si MAS NMR with the results as shown in FIG. 7a.

1B. Comparative-Synthesis Using [(EtO)₂SiCH₂]₃in Basic Aqueous Medium—with Surfactant.

In this example, an organosilica material was prepared according to Landskron, K., et al., Science 302:266-269 (2003).

Cetyltrimethylammonium bromide (CTMABr, 0.9 mmol, 0.32 g, Aldrich) was dissolved in a mixture of 2.16 g NH₄OH (35 wt %) and 3.96 g de-ionized water at 20° C. to form a solution.

[(EtO)₂SiCH₂]₃(1.26 mmol, 0.5 g) was added to the solution, producing a solution having the molar composition:

1.0[(EtO)₂SiCH₂]₃:17OH:236H₂O:0.7CTMABr

which was stirred for 1 day at 20° C. and a white precipitate formed. Afterwards, the solution was aged for 1 day at 80° C. Then the precipitate was filtered off and washed with water. The sample was then stirred for 48 hours in a solution of 12 g HCl (36 wt %) and 80 g of methanol. The sample was then filtered off again and washed with MeOH, resulting in Comparative Sample 2.

XRD Analysis

XRD was performed Comparative Sample 2. A comparison of the XRD patterns for Sample Al and Comparative Sample 2 is shown in FIG. 1. Compared to the XRD pattern of Sample 1A, the XRD pattern of Comparative Sample 2 exhibits a shoulder at about 3 degrees 2θ.

TGA Analysis

TGA weight loss studies were performed on Comparative Sample 2 in nitrogen and air. FIGS. 8a and 8b display the TGA data for Comparative Sample 2 in nitrogen and air, respectively.

Nitrogen Adsorption/Desorption Analysis

Nitrogen adsorption/desorption analysis was performed on Comparative Sample 2. The surface area, average pore diameter, and pore volume obtained by the nitrogen adsorption/desorption analysis for Sample 1A and Comparative Sample 2 are shown below in Table 1 and FIGS. 3 and 4.

TABLE 1

BET
Pore Diameter
Pore Volume

Material
(m²/g)
(nm)
(cc/g)

Comparative Sample 2
1520
3.02
1.07

Sample 1A
1410
3.18
0.92

SS-NMR-Analysis

Comparative Sample 2 was characterized with ²⁹Si MAS NMR as shown in FIG. 7b. As shown below in Table 2, Sample 1A had a higher silanol content (i.e., 47%) compared to Comparative Sample 2 (i.e., 41%).

TABLE 2

D₁
D₂
T sites
Si(OH)/Si

Sample 1A (%)
96
4
47

45.6
50.4

Comparative Sample 2(%)
89
11
41

34.7
54.3

embedded image

1C. Synthesis Using [(EtO)₂SiCH₂]₃in Acidic Aqueous Medium—without Surfactant.

A 14 g HCl solution with a pH of 2 was made by adding 0.778 mol water and 0.14 mmol HCl. To the solution, 1.0 g (2.52 mmol) of [(EtO)₂SiCH₂]₃was added producing a solution having the molar composition:

18[(EtO)₂SiCH₂]₃:1HCl:5556H₂O

which was stirred for 1 day at room temperature (20-25° C.). The solution was transferred to an autoclave and aged at 94° C. for 1 day to produce a gel. The gel was dried in a vacuum at 120° C. overnight (16-24 hours) to produce Sample 3. No surface directing agent or porogen were used.

XRD Analysis

XRD was performed on Sample 3. A comparison of XRD patterns for Sample 1A and Sample 3 is shown in FIG. 9.

Nitrogen Adsorption/Desorption Analysis

Nitrogen adsorption/desorption analysis was performed on Sample 3. The surface area, microporous surface area, average pore diameter, and pore volume obtained by the nitrogen adsorption/desorption analysis for Sample 3 are shown in FIGS. 5 and 6.

1D. Synthesis Using [(EtO)₂SiCH₂]₃and [CH₃EtOSiCH₂]₃

A solution with 6.21 g of 30% NH₄OH and 7.92 g DI water was made. To the solution, 0.6 g of [(EtO)₂SiCH₂]₃and 0.306 g of 1,3,5-trimethyl-1,3,5-triethoxy-1,3,5-trisilacyclohexane ([CH₃EtOSiCH₂]₃) was added producing a solution having the molar composition:

1.5[(EtO)₂SiCH₂]₃:1.0[CH₃EtOSiCH₂]₃:53OH:682H₂O

which was stirred for 1 day at room temperature (20-25° C.). The solution was transferred to an autoclave and aged at 90° C. for 1 day to produce a gel. The gel was dried in a vacuum at 120° C. overnight (16-24 hours) and Sample 4A was obtained. No structure directing agent or porogen were used.

Nitrogen Adsorption/Desorption Analysis

This above preparation method was repeated, except the relative ratio of [(EtO)₂SiCH₂]₃(Reagent 1) to [CH₃EtOSiCH₂]₃(Reagent 2) was varied. Nitrogen adsorption/desorption analysis was performed on each material and the results for each material is given below in Table 3.

TABLE 3

Reagent
BET
V
Pore Diameter

Material
1:Reagent 2
(m²/g)
(cc/g)
(nm)

Sample 1A
5:0
1410
0.915
3.18

Sample 4A
3:2
819
1.52
7.39

Sample 4B
4:1
1100
1.14
4.17

Sample 4C
2:3
460
1.09
13.9

Sample 4D
0:5
1.81
7.73E−03
68.8

As Reagent 2 increased, the average pore diameter was observed to increase, which without being bound by theory may be due to Reagent 2 containing less reactive —OR groups compared to Reagent 1. The porosity of the material decreased as Reagent 2 was greater than 60% (mol ratio).

SS-NMR-Analysis

The materials in Table 3 were characterized with ²⁹Si MAS NMR, as shown in FIG. 10.

Example 2
Organosilica Material Syntheses Using Formula [R¹R²SiCH₂]₃(Ia) and Formula R³OR⁴R⁵R⁶Si (IIa) in Basic or Acidic Media

2A. Synthesis Using [(EtO)₂SiCH₂]₃and Tetraethylorthosilicate (TEOS) ((EtO)₄Si) in Basic Aqueous Medium

A solution with 6.21 g of 30% NH₄OH (53 mmol NH₄OH) and 7.92 g DI water was made. To the solution, 0.8 g (2 mmol) of [(EtO)₂SiCH₂]₃and 0.625 g (3 mmol) of TEOS was added to produce a solution having the molar composition:

2.0[(EtO)₂SiCH₂]₃:3.0TEOS:53OH:682H₂O

which was stirred for three days at room temperature (20-25° C.). The solution was transferred to an autoclave and aged at 80° C.-90° C. for 2 days to produce a gel. The gel was dried in a vacuum at 110° C. overnight (16-24 hours) and Sample 5 was obtained. No structure directing agent or porogen was used.

A solution with 6.21 g of 30% NH₄OH (53 mmol NH₄OH) and 7.92 g DI water was made. To the solution, 3.2 g (8 mmol) of [(EtO)₂SiCH₂]₃and 2.5 g (12 mmol) of TEOS was added to produce a solution having the molar composition:

8.0[(EtO)₂SiCH₂]₃:12.0TEOS:53OH:682H₂O

which was stirred for three days at room temperature (20-25° C.). The solution was transferred to an autoclave and aged at 80° C.-90° C. for 2 days to produce a gel. The gel was dried in a vacuum at 110° C. overnight (16-24 hours) and Sample 5A was obtained. No structure directing agent or porogen was used.

XRD Analysis

XRD was performed on Sample 5. The XRD pattern of Sample 5 is shown in FIG. 11.

TGA Analysis

TGA weight loss studies were performed on Sample 5 in nitrogen and air. FIG. 12 display the TGA data for Sample 5 in nitrogen and air.

SS-NMR-Analysis

Sample 5 was characterized with ²⁹Si MAS NMR and compared with Sample 1A as shown in FIG. 13. As shown in FIG. 13, Sample 5 had a silanol content of 44%.

Nitrogen Adsorption/Desorption Analysis

Nitrogen adsorption/desorption analysis was performed on Sample 5 and Sample 5A, and the results are provided below in Table 4 and FIGS. 5 and 6.

TABLE 4

BET
Pore Diameter
Pore Volume

Material
(m²/g)
(nm)
(cc/g)

Sample 5
1430
3.42
1.21

Sample 5A
1027
4.84
1.20

2B. Synthesis Using [(EtO)₂SiCH₂]₃and TEOS in Acidic Aqueous Medium

A 14 g HCl solution with a pH of 2 was made by adding 0.778 mol water and 0.14 mmol HCl. To the solution, 0.8 g (2 mmol) of [(EtO)₂SiCH₂]₃and 0.625 g (3 mmol) TEOS was added to produce a solution having the molar composition:

2.0[(EtO)₂SiCH₂]₃:3.0TEOS:0.14H:778H₂O

which was stirred for 1 day at room temperature (20-25° C.). The solution was transferred to an autoclave and aged at 94° C. for 1 day to produce a gel. The gel was dried in a vacuum at 120° C. overnight (16-24 hours) to produce Sample 6. No structure directing agent or porogen were used.

XRD Analysis

XRD was performed on Sample 6. The XRD pattern of Sample 6 is shown in FIG. 11.

Nitrogen Adsorption/Desorption Analysis

Nitrogen adsorption/desorption analysis was performed on Sample 6, and the results are provided in FIGS. 5 and 6.

2C. Synthesis Using [CH₃EtOSiCH₂]₃and TEOS

A solution with 6.21 g of 30% NH₄OH (53 mmol NH₄OH) and 7.92 g DI water was made. To the solution, 0.612 g (2 mmol) of 1,3,5-trimethyl-1,3,5-triethoxy-1,3,5-trisilacyclohexane ([CH₃EtOSiCH₂]₃) and 0.625 g (3 mmoles) of TEOS was added to produce a solution having the molar composition:

2.0[CH₃EtOSiCH₂]₃:3.0TEOS:53OH:682H₂O

which was stirred for 1 day at room temperature (20-25° C.). The solution was transferred to an autoclave and aged at 90° C. for 1 day to produce a gel. The gel was dried in a vacuum at 120° C. overnight (16-24 hours) and Sample 7A was obtained. No structure directing agent or porogen were used.

Nitrogen Adsorption/Desorption Analysis

This above preparation method was repeated, except the relative ratio of TEOS (Reagent 3) to [CH₃EtOSiCH₂]₃(Reagent 2) was varied. Table 5 below is a summary of the N₂adsorption analysis for the materials obtained with varied reagent ratios.

TABLE 5

(Reagent
BET
Pore Volume
Pore Diameter

Material
3:Reagent 2)
(m²/g)
(cc/g)
(nm)

Sample 7A
3:2
471
1.9
18.6

Sample 7B
3:4
493
2.16
23.1

SS-NMR-Analysis

The materials made by this method were characterized with by ²⁹Si MAS NMR, as shown in FIG. 14.

2D. Synthesis Using [(EtO)₂SiCH₂]₃and Methyltriethoxysilane (MTES) ((EtO)₃CH₃Si)

A solution with 6.21 g of 30% NH₄OH (53 mmol NH₄OH) and 7.92 g DI water was made. To the solution, 0.4 g (1 mmol) of [(EtO)₂SiCH₂]₃and 0.267 g (1.5 mmol) of MTES was added to produce a solution having the molar composition:

1.0[(EtO)₂SiCH₂]₃:1.5MTES:53OH:682H₂O

which was stirred for 1 day at room temperature (20-25° C.). The solution was transferred to an autoclave and aged at 90° C. for 1 day to produce a gel. The gel was dried in a vacuum at 120° C. overnight (16-24 hours) and Sample 8A was obtained. No structure directing agent or porogen were used.

Nitrogen Adsorption/Desorption Analysis

This above preparation method was repeated, except the relative ratio of [(EtO)₂SiCH₂]₃(Reagent 1) and of MTES (Reagent 2) was varied. Table 6 below is a summary of the N₂adsorption analysis for the materials obtained with varied reagent ratios.

TABLE 6

Reagent
BET
Pore Volume
Pore Diameter

Material
1:Reagent 2
(m²/g)
(cc/g)
(nm)

Sample 1A
5:0
1410
0.915
3.18

Sample 8A
2:3
821
1.06
4.5

Sample 8B
4:1
1130
1.0
3.59

Sample 8C
3:2
1040
1.05
3.89

Example 3
Organosilica Material Syntheses Using Formula [R¹R²SiCH₂]₃(Ia) Formula R³OR⁴R⁵R⁶Si (IIa), and/or Formula Z¹⁹Z²⁰Z²¹Si—R—SiZ¹⁹Z²⁰Z²¹(IIa)

3A. Synthesis Using [(EtO)₂SiCH₂]₃and CH₃(EtO)₂Si—CH₂CH₂—Si(EtO)₂CH₃.

A solution with 6.21 g of 30% NH₄OH (53 mmol NH₄OH) and 7.9 g DI water was made. To the solution, 0.8 g (2 mmol) of [(EtO)₂SiCH₂]₃and 0.88 g (3 mmol) 1,2-bis(methyldiethyoxysilyl)ethane (CH₃(EtO)₂Si—CH₂CH₂—Si(EtO)₂CH₃) was added to produce a solution having the molar composition:

2.0[(EtO)₂SiCH₂]₃:3.0CH₃(EtO)₂Si—CH₂CH₂—Si(EtO)₂CH₃:53OH:682H₂O

which was stirred for 1 day at room temperature (20-25° C.). The solution was transferred to an autoclave and aged at 80° C.-90° C. for 1 day to produce a gel. The gel was dried in a vacuum at 110° C. overnight (16-24 hours) and Sample 9 was obtained. No structure directing agent or porogen were used.

XRD Analysis

XRD was performed on Sample 9. The XRD pattern of Sample 9 is shown in FIG. 15.

Nitrogen Adsorption/Desorption Analysis

Nitrogen adsorption/desorption analysis was performed on Sample 9, and the results are provided in Table 7.

3B. Synthesis Using [(EtO)₂SiCH₂]₃and (EtO)₃Si—CH₂—Si(EtO)₃

A solution with 6.21 g of 30% NH₄OH (53 mmol NH₄OH) and 7.9 g DI water was made. To the solution, 0.8 g (2 mmol) of [(EtO)₂SiCH₂]₃and 1.02 g (3 mmol) of bis(triethoxysilyl)methane ((EtO)₃Si—CH₂—Si(EtO)₃) was added to produce a solution having the molar composition:

2.0[(EtO)₂SiCH₂]₃:3.0(EtO)₃Si—CH₂—Si(EtO)₃:53OH:682H₂O

which was stirred for 1 day at room temperature (20-25° C.). The solution was transferred to an autoclave and aged at 80° C.-90° C. for 1 day to produce a gel.

The gel was dried in a vacuum at 110° C. overnight (16-24 hours) and Sample 10 was obtained. No structure directing agent or porogen were used.

XRD Analysis

XRD was performed on Sample 10. The XRD pattern of Sample 10 is shown in FIG. 15.

Nitrogen Adsorption/Desorption Analysis

Nitrogen adsorption/desorption analysis was performed on Sample 10, and the results are provided in Table 7.

3C. Synthesis using TEOS and (EtO)₃Si—CH₂—Si(EtO)₃

A solution with 6.21 g of 30% NH₄OH (53 mmoles NH₄OH) and 7.92 g DI water was made. To the solution, 1.7 g (5 mmol) of bis(triethoxysilyl)methane ((EtO)₃Si—CH₂—Si(EtO)₃) and 0.416 g (2 mmol) of TEOS were added to produce a solution having the molar composition:

5.0(EtO)₃Si—CH₂—Si(EtO)₃:2.0TEOS:53OH:682H₂O

which was stirred for 1 day at room temperature (20-25° C.). The solution was transferred to an autoclave and aged at 80° C.-90° C. for 1 day to produce a gel. The gel was dried in a vacuum at 110° C. overnight (8-16 hours) and Sample 11A was obtained. No structure directing agent or porogen were used.

Two more preparations with different ratios of reagents were also made, one with a (EtO)₃Si—CH₂—Si(EtO)₃:TEOS molar ratio of 4:4 to obtain Sample 11B and another with a (EtO)₃Si—CH₂—Si(EtO)₃:TEOS molar ratio of 3:6 to obtain Sample 11C.

XRD Analysis

XRD was performed on Sample 11A. The XRD pattern of Sample 11A is shown in FIG. 15.

Nitrogen Adsorption/Desorption Analysis

Nitrogen adsorption/desorption analysis was performed on Sample 11A, and the results are provided in Table 7.

3D. Synthesis Using [(EtO)₂SiCH₂]₃and (EtO)₃Si—CH═CH—Si(EtO)₃

A solution with 12.42 g of 30% NH₄OH (106 mmol NH₄OH) and 15.8 g DI water was made. To the solution, 1.6 g (4 mmol) of [(EtO)₂SiCH₂]₃and 0.352 g (1 mmol) 1,2-bis(triethoxysilyl)ethylene ((EtO)₃Si—CH═CH—Si(EtO)₃) was added to produce a solution having the molar composition:

4.0[(EtO)₂SiCH₂]₃:1.0(EtO)₃Si—CH═CH—Si(EtO)₃:106OH:1364H₂O

which was stirred for 1 day at room temperature (20-25° C.). The solution was transferred to an autoclave and aged at 80° C.-90° C. for 1 day to produce a gel. The gel was dried in a vacuum at 110° C. overnight (8-16 hours) and Sample 12 was obtained. No structure directing agent or porogen were used.

XRD Analysis

XRD was performed on Sample 12. The XRD pattern of Sample 12 is shown in FIG. 15.

Nitrogen Adsorption/Desorption Analysis

Nitrogen adsorption/desorption analysis was performed on Sample 12, and the results are provided in Table 7.

TABLE 7

BET
S
Pore Diameter
Pore Volume

Material
(m2/g)
(m2/g, micro)
(nm)
(cc/g)

Sample 9
551
233
8.4
0.76

Sample 10
1270
512
3.35
0.96

Sample 11A
870
0
3.83
0.84

Sample 12
1030
0
3.69
1.02

Example 4
Organosilica Material Syntheses Using Formula [R¹R²SiCH₂]₃(Ia) and Nitrogen-Containing Monomers

Synthesis:

1. Made a solution with 6.21 g 30% NH₄OH and 7.9 g DI water (53 mmol NH₄OH; 682 mmol H₂O);
2. Added 0.8 g (2 mmol) of [(EtO)₂SiCH₂]₃(Reagent 1) to Reagent 2 into the above solution, kept stirring for 1 day at room temperature;
3. Transferred the solution to an autoclave, aging at 80-90° C. for 1 day;
4. Dried the gel at 110° C. in vacuum overnight.

The above synthesis was performed with the following reagents in Table 8 to obtain Samples 13, 14, 15 and 21.

The above synthesis was performed with the following reagents in Table 8 to obtain Samples 16, 17, 18 and 19 except 1.6 g of Reagent 1, 12.4 g 30% NH₄OH and 15.8 g DI water were used for the preparation.

The above synthesis was performed with the following reagents in Table 8 to obtain Sample 20 except 3.2 g of Reagent 1, 24.8 g 30% NH₄OH and 31.6 g of DI water were used for the preparation.

TABLE 8

Reagent 2
Reagent

Amount
1:Reagent 2

Material
Reagent 2
(g)
Molar ratio

Sample 13
N,N′-bis[(3-trimethoxy-
0.192
2:0.5

silyl)propyl]ethylenediamine

Sample 13A
N,N′-bis[(3-trimethoxy-

2:3

silyl)propyl]ethylenediamine

Sample 14
bis[(methyldiethoxy-
0.183
2:0.5

silyl)propyl]amine

Sample 15
bis[(methyldimethoxy-
0.162
2:0.5

silyl)propyl]-N-methylamine

Sample 16
(N,N-dimethylamino-
1.24
2:3

propyl)trimethoxysilane

Sample 17
N-(2-aminoethyl)-3-
1.58
2:3

aminopropyltriethoxysilane

Sample 18
4-methyl-1-(3-triethoxy-
1.83
2:3

silylpropyl)-piperazine

Sample 19
4-(2-(triethoxysily)ethyl)pyridine
0.271
2:0.5

Sample 20
1-(3-(triethoxysilyl)propyl)-
0.553
2:0.5

4,5-dihydro-1H-imidazole

Sample 21
(3-aminopropyl)triethoxysilane
0.22
2:0.5

XRD Analysis

XRD was performed on Samples 13 and 21. The XRD patterns of Samples 13 and 21 are shown in FIG. 16.

Nitrogen Adsorption/Desorption Analysis

Nitrogen adsorption/desorption analysis was performed on Samples 13, 14 and 15, and the results are provided in Table 9 and FIGS. 17 and 18.

TABLE 9

BET
Pore Diameter
Pore Volume

Material
(m²/g)
(nm)
(cc/g)

Sample 13
1127
4.11
1.26

Sample 14
691
5
0.96

Sample 15
787
4.56
0.97

Example 5
CO₂Isotherms

CO₂adsorption isotherms were measured at 40° C. for Sample 13A and at 30° C. for Sample 17, as shown in FIGS. 19 and 20, respectively.

	Number	Date	Country
	62091071	Dec 2014	US
	62091077	Dec 2014	US

ORGANOSILICA MATERIALS AND USES THEREOF

Information

Publication Number

Date Filed

Date Published

Inventors

Original Assignees

CPC

International Classifications

Abstract

Description

Claims

CROSS-REFERENCE TO RELATED APPLICATIONS

Provisional Applications (2)