The present invention relates to an exhaust gas oxidation catalyst for a compressed natural gas combustion system, and more particularly to an exhaust gas purification catalyst for a compressed natural gas lean-burn engine, in which a conventional exhaust gas purification catalyst for a compressed natural gas lean-burn engine, loaded with noble metal components containing platinum and palladium, is further impregnated with a specific component serving as a cocatalyst to thus prevent catalyst deactivation.
The use of CNG (Compressed Natural Gas) as fuel in a combustion system including a vehicle engine is environmentally friendly, generates economic benefits, and is characterized by low emission of toxic materials such as HC, CO, and PM (Particulate Matter), thus leading to almost none of the odors and fumes of exhaust gas. In the present invention, a combustion system includes a vehicle engine, and in some cases, a combustion system other than one for a vehicle is also called a static combustion system, which is distinguished from one for a vehicle, that is, a dynamic combustion system.
In the related art with regard to an exhaust gas purification catalyst for a compressed natural gas vehicle and a purification method thereof, Korean Patent No. 670221 by the present applicant discloses, as an exhaust gas oxidation catalyst for a compressed natural gas vehicle, loaded with noble metal components containing palladium and platinum, a catalyst for improving oxidation activity on exhaust gas from a compressed natural gas vehicle, which is configured such that palladium-impregnated first alumina, platinum-impregnated second alumina, CeO2—ZrO2 composite ceria and nickel oxide are loaded on a ceramic support. Also, as disclosed in Korean Patent No. 1524054 by the present applicant, an exhaust gas oxidation catalyst for a compressed natural gas combustion system, particularly a catalyst for improving oxidation activity on exhaust gas from a compressed natural gas vehicle or static combustion system in excess air, is configured such that palladium-impregnated first alumina, platinum-impregnated second alumina, and a ceria component are loaded on a ceramic support and the first alumina is impregnated with a cocatalyst selected from the group consisting of barium, nickel, lanthanum, samarium and yttrium so as to improve oxidation activity on methane, which is an exhaust gas component from a compressed natural gas vehicle or static combustion system, in excess air.
A currently useful catalyst for purifying CNG exhaust gas from a CNG engine operating in a fuel lean-burn atmosphere is problematic in terms of catalyst durability, that is, catalyst deactivation. The causes of deactivation of a platinum/palladium-based catalyst for purifying exhaust gas from a CNG lean-burn engine have not been accurately identified. The present applicant has developed a catalyst for solving the problem of deactivation of a CNG lean-burn engine catalyst in such a manner that, in an exhaust gas oxidation catalyst for a compressed natural gas combustion system, configured such that palladium-impregnated first alumina, platinum-impregnated second alumina, and a ceria component are loaded on a ceramic support, the palladium-impregnated first alumina is further impregnated with a cocatalyst selected from the group consisting of barium, nickel, lanthanum, samarium, and yttrium, but a solution for the catalyst deactivation is still desired.
Therefore, the present invention is intended to provide a catalyst composition for preventing the deactivation of an exhaust gas purification catalyst for a compressed natural gas combustion system, loaded with noble metal components containing platinum and palladium. The present inventors have ascertained that a barium component serving as a cocatalyst is added to a support containing platinum loaded thereon to thus improve catalyst durability, unlike the conventional art. Specifically, in an exhaust gas oxidation catalyst for a compressed natural gas combustion system, configured such that platinum-impregnated first alumina, palladium-impregnated second alumina, and a ceria component are loaded on a ceramic support, the platinum-impregnated first alumina is further impregnated with a barium cocatalyst, by which prevention of the deactivation of the CNG lean-burn engine catalyst has been confirmed. Without limitation thereto, in the present invention, the weight ratio of platinum and palladium impregnated respectively on the first alumina and the second alumina fall in the range of 1:1 to 1:10. According to the present invention, the barium cocatalyst is added in an amount of 1 to 20 wt % based on the amount of platinum, and the weight ratio of the platinum-impregnated alumina and the palladium-impregnated alumina fall in the range of 15:15 to 15:150.
According to the present invention, the deactivation of a CNG lean-burn engine catalyst can be prevented by virtue of the interaction between platinum and a barium cocatalyst.
Hereinafter, a detailed description will be given of the present invention, without limitation to embodiments thereof.
As described above, the catalyst for purifying CNG lean-burn engine exhaust gas is composed mainly of platinum (Pt) and palladium (Pd). The most recently developed catalyst is configured such that a cocatalyst is introduced adjacent to Pd based on the fact that Pd has superior oxidation performance compared to Pt in terms of methane conversion efficiency. Specifically, a support containing Pd loaded thereon is added with a cocatalyst such as barium, nickel, lanthanum, samarium or yttrium, in which the cocatalyst component contributes to catalyst durability by altering the electron state of Pd due to complexation. Unexpectedly, however, the present inventors have ascertained that catalyst durability may be improved as a result of introducing a cocatalyst component, particularly barium, adjacent to a platinum component, rather than palladium.
According to the present invention, the catalyst is prepared by impregnating first alumina with Pt and a cocatalyst precursor, particularly barium acetate, and simultaneously impregnating second alumina with Pd, mixing the first alumina with the second alumina, and adding ceria thereto, followed by uniform milling and firing. Preferably, the weight ratio of platinum and palladium, impregnated respectively on the first alumina and the second alumina, falls in the range of 1:1 to 1:10, and the barium cocatalyst is further added in an amount of 1 to 20 wt % based on the amount of platinum to the support containing platinum loaded thereon, and the weight ratio of the platinum-barium-impregnated alumina and the palladium-impregnated alumina preferably falls in the range of 15:15 to 15:150. If the amount of the cocatalyst according to the present invention is less than 1 wt % based on the amount of platinum, the cocatalyst does not function. On the other hand, if the amount thereof exceeds 20 wt % based on the amount of platinum, durability is significantly worsened. The catalyst according to the present invention is configured such that the barium cocatalyst is impregnated only on the platinum-impregnated support and is not loaded on the support impregnated with the other noble metal, for example, palladium, unlike the recently developed palladium-cocatalyst-based catalyst. The above weight ratio of the platinum-barium-impregnated alumina and the palladium-impregnated alumina is an optimal range obtained through a numerous variety of tests. Although not delineated in any particular theory, the cocatalyst component enhances catalyst durability through the interaction with the platinum component. The catalyst of the invention is not deactivated and the activity thereof is still maintained even after the reaction time, unlike the conventional CNG lean-burn engine exhaust gas catalyst.
A better understanding of the present invention will be given through the following examples, which are not to be construed as limiting the present invention. In particular, the noble metal and the precursor of the metal used for the cocatalyst are not limited by the examples, and nitrate, acetate, chloride, sulfate, and the like are variously used. For the sake of brief description, a lean-burn engine vehicle is exemplified, but the present invention is not limited thereto, and may be applied to all combustion systems using compressed natural gas as fuel.
a. 15.0 g/l of a first alumina powder was impregnated with chloroplatinic acid and 80.0 g/l of a second alumina powder was impregnated with palladium nitrate and barium acetate (in an amount of 10 wt % based on the amount of Pd), thus preparing Pt-impregnated active alumina and Pd—Ba-impregnated active alumina, and a ceria powder (alumina 5 wt %) was dispersed in water to give a slurry. Here, the weight ratio of Pt and Pd was 1:5.
b. The slurry was milled such that about 90% thereof had a particle size of 6 to 8 μm, and the treated slurry was applied on a cordierite honeycomb, dried at 150° C. to 160° C. for about 10 min, and then fired at 530° C. to 550° C. for about 40 to 60 min, thereby completing a comparative catalyst.
The same procedures as in Comparative Example 1 were performed, with the exception that the amount of barium was changed to 1 wt %, 5 wt % and 20 wt % based on the amount of Pd. The results are shown in
The same procedures as in Comparative Example 1 were performed, with the exception that the amount of barium was fixed to 1 wt % based on the amount of Pd and that the weight ratio of Pt and Pd was changed from 1:5 to 1:6, 1:7, 1:8, and 1:9. The results are shown in
The same procedures as in Comparative Example 1 were performed, with the exception that the amount of barium was fixed to 1 wt % based on the amount of Pd and that the weight ratio of Pt and Pd was fixed to 1:7, and the amount of the second alumina powder applied to Pd was changed from 80 g/l to 100 g/l, 120 g/l and 140 g/l. The results are shown in
On the basis of the above Comparative Examples, a platinum-barium catalyst was prepared under conditions in which the amount of barium was set to 1 wt % based on the amount of Pt, the weight ratio of platinum and palladium was 1:7, the amount of the second alumina powder as the palladium support was set to 120 g/L, and the impregnation position of the barium cocatalyst was changed, after which the durability of the catalyst was tested. The results are shown in
| Number | Date | Country | Kind |
|---|---|---|---|
| 10-2015-0184454 | Dec 2015 | KR | national |
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/KR2016/014808 | 12/16/2016 | WO | 00 |