Oxidation of ammonia over a mixed catalyst bed of cobalt and aluminum oxides

Abstract

This invention is a catalyst and method of oxidizing ammonia by contacting the ammonia and air with catalyst of cobalt oxide, wherein the improvement comprises using activated alumina in conjunction with the cobalt oxide catalyst.

Description

BACKGROUND OF THE INVENTION

This invention relates to the catalytic oxidation of ammonia to oxides of nitrogen, particularly oxidation of ammonia over a mixed catalyst bed of cobalt and aluminum oxide.

The process and catalyst of cobalt oxide mixed with other metal oxides for the oxidation ammonia are known in U.S. Pat. No. 1,919,005 hereby incorporated by reference. Also, mixturs of cobalt oxide with other metals as catalyst in the oxidation of ammonia are known in U.S. Pat. No. 3,985,681, hereby incorporated by reference. The above patents set forth clearly the prior art process and catalysts. However, those operating such processes are continually looking for improved catalysts and yields. The process produces NO and NO.sub.2, hereinafter NO.sub.x.

Admixtures of metal oxides within individual pellets or co-catalyst is known art, and is believed to utilize complex chemistry that involves interactive or sequential reactions. However, alumina alone is regarded as an inert material under ammonia oxidation conditions. This can be demonstrated by its use either as a catalyst support bed or as a feed-gas preheater layer on top of the colbalt oxide catalyst bed; neither of which give improved yields of NO.sub.x.

SUMMARY OF THE INVENTION

The catalyst and process of this invention has substantially increased yields of NO.sub.x. The method of the invention is the improvement in oxidizing ammonia by contacting ammonia and air with the catalyst of particles of cobalt oxide, wherein the improvement comprises using particles of activated alumina in conjunction with the cobalt oxide particles. Preferably, about 10 to 50 percent by weight of alumina is used. Both the alumina and the cobalt oxide particles preferably have a particle size of 6 to 14 mesh. Ammonia and air mixtures having an ammonia concentration by volume of 7.5-12 percent are introduced at a space velocity of 15,000 to 100,000 liters of gas per liter of catalyst in a bed of at least 3.75 cm (1.5 inches) deep. The inert gas temperature can be between 25.degree. and 250.degree. C. Upon ignition the bed temperature ranges from 500.degree. C. to 900.degree. C., preferably 600.degree. C. to 850.degree. C. The preferred pressure of the reaction is slightly above atospheric. The catalyst of this invention for oxidizing ammonia by contact with air and ammonia consists essentially of from about 90 to 50 percent by weight of cobalt oxide particles and from about 10 to about 50 percent by weight of alumina particles.

DESCRIPTION OF THE PREFERRED EMBODIMENT

Example

Solid particles of 6-14 mesh of alumina, Al.sub.2 O.sub.3, and particles of cobalt dioxide, Co.sub.3 O.sub.4, of the same particle size or larger were placed in a two-inch tubular insulated reactor. Twenty-five ml of alumina particles and 75 ml of cobalt oxide particles were added. Ammonia and air, with the amount of ammonia shown as percent by volume in Table I, were preheated to 80.degree. C. and passed through the reactor at volumetric velocity (VVH) shown. Oxidation proceeded at the upper and lower bed temperature (s) shown for the time shown. The yield in percent by weight of conversion of ammonia to NO.sub.x was measured in the reacted gases at the outlet. Results are shown in Table I.

CONTROL

A control example was run omitting the alumina, but otherwise operating in the same manner. Results are shown in Table II.

DISCUSSION

The tables show by comparing yields of control runs against the runs of the example of the invention that yields are improved substantially at otherwise comparable operating conditions.

Surprisingly, we have found that a uniform physical mixture of catalyst (Co.sub.3 O.sub.4) and inert (Al.sub.2 O.sub.3) pellets, as separate particles, lowers the operating temperature of the catalyst bed and provides a substantial improvement in NO.sub.x yield. This is especially important at ammonia in air concentrations above 7.5 percent, where the increase in adiabatic catalyst bed exit temperatures normally results in decreasing NO.sub.x yields as an economic trade-off with higher throughput capacity.

It is postulated that the temperature at the actual pore surface of each Co.sub.3 O.sub.4 catalyst particle, where reaction is actually taking place, is much higher than that of the gas stream with which it is in contact. There are then simultaneous transfers occuring through the gas/solid interface film: mass transfer of ammonia and oxygen to the catalyst surface and NO.sub.x back into the gas stream, accompanied by heat transfer of the heat of reaction from the catalyst pellet to the gas stream. Intimate physical contact of the Co.sub.3 O.sub.4 catalyst pellets with inert A1.sub.2 O.sub.3 pellets, allows another path for heat transfer via conduction into the alumina and thence into the gas stream, thus lowering the equilibrium temperature of each catalyst particle, providing improved yield to NO.sub.x. A synergistic benefit is evident, in that higher yields reduce the by-product losses to nitrogen--a very high heat release reaction, which reduces the total quantity of heat generated and further reduces the temperature differential created between the catalyst pore surface and the gas stream. The large difference in bed temperatures between Table II and Table I is due to use of the inert alumina as a heat-sink. Table III shows the temperture differences.

TABLE I______________________________________EXAMPLE (25 ml Activated Alumina - 75 ml Co.sub.3 O.sub.4) * Volume Upper Bed Lower BedRun Velocity % Time, Tempera- Tempera- Yield,No. Per Hour NH.sub.3 Hours ture, .degree.C. ture, .degree.C. %______________________________________1 40,000 11.5 4 831 810 90.1 40,000 11.5 8 828 808 89.9 40,000 11.5 12 832 811 89.32 20,000 11.5 4 717 643 101.1 20,000 11.5 8 714 642 96.4 20,000 11.5 12 708 639 94.03 20,000 7.5 4 550 494 68.1 20,000 7.5 8 550 498 66.0 20,000 7.5 12 550 499 63.54 20,000 9.5 4 634 570 86.2 20,000 9.5 8 637 570 89.3 20,000 9.5 12 645 579 89.55 40,000 9.5 4 719 700 95.4 40,000 9.5 8 717 699 93.4 40,000 9.5 12 730 711 97.46 40,000 7.5 4 620 608 77.5 40,000 7.5 8 620 609 73.1 40,000 7.5 12 629 616 79.0______________________________________ *Volume velocity assuming 75 ml bed volume = ratio of flow rate of gas feed mixture to volume of catalyst in liters. TABLE II______________________________________CONTROL (WITHOUT ALUMINA) Volume Upper Bed Lower BedRun Velocity % Time, Tempera- Tempera- Yield,No. Per Hour NH.sub.3 Hours ture, .degree.C. ture, .degree.C. %______________________________________1 40,000 11.5 4 816 842 79.3 40,000 11.5 8 822 857 75.5 40,000 11.5 12 834 865 74.22 20,000 11.5 4 740 705 79.8 20,000 11.5 8 736 708 74.8 20,000 11.5 12 789 749 79.13 20,000 7.5 4 567 540 44.5 20,000 7.5 8 568 548 43.7 20,000 7.5 12 581 560 48.14 20,000 9.5 4 660 633 70.5 20,000 9.5 8 649 629 64.1 20,000 9.5 12 674 653 66.45 40,000 9.5 4 558 770 78.2 40,000 9.5 8 722 769 74.8 40,000 9.5 12 722 760 73.16 40,000 7.5 4 208 635 64.1 40,000 7.5 8 260 638 65.5 40,000 7.5 12 214 633 62.1______________________________________ TABLE III__________________________________________________________________________Lower Bed Temperatures, .degree. C. Upper Bed Temperatures, .degree.C.Run No. Table II - Table I = .DELTA.T Average .DELTA.T Table II - Table I = .DELTA.T Average__________________________________________________________________________ .DELTA.T1 842 810 32 45 816 831 -15 -6 857 808 49 822 828 -6 865 811 54 834 832 22 705 643 62 79 740 717 23 42 708 642 66 736 714 22 749 639 110 789 708 813 540 494 46 65 567 550 17 22 548 498 59 568 550 18 560 499 74 581 550 314 633 570 63 65 650 634 26 22 629 570 59 649 637 12 653 579 74 674 645 295 770 700 70 63 558 719 -161 -54 769 699 70 722 717 5 760 711 49 722 730 -86 635 608 27 24 208 620 -412 -395 638 609 29 260 620 -360 633 616 17 214 629 -415__________________________________________________________________________ Note the upper bed temperatures at 40,000 (VVH) velocity in Table II, run 1, 5 and 6, appear to have inordinately low temperatures due to movement of the reaction zone into the bed and away from the normal surface location where the thermocouple had been placed.

Claims

1. In a method of oxidizing ammonia by contacting ammonia and air with a catalyst of cobalt oxide, the improvement comprising

using separate particles of activated alumina in conjunction with

the separate particles of cobalt oxide catalyst

and wherein about 10 to about 50 percent by weight alumina is added and

the catalyst particle size is 6 to 14 mesh, the ammonia and air mixture has an ammonia concentration by volume of 7.5 to 12 percent introduced at a space velocity of from between about 15,000 to 100,000 liters of gas per liter of catalyst bed, the inlet gas temperature is from between about 25.degree. C. to 250.degree. C. and upon ignition the bed temperature ranges from 500.degree. C. to 900.degree. C.

2. The method of claim 1 wherein the bed temperature is between 600.degree. C. and 850.degree. C.