Patent Application
20120058396
1. Field of the Invention
This present invention relates to electrode designs for rechargeable oxide-ion battery (ROB) cells. More specifically, the invention describes the application of oxidation-resistance metal including stainless steel as a support and current collector in a ROB metal electrode for reducing materials cost and improving cell performance.
2. Description of Related Art
Electrical energy storage is crucial for the effective proliferation of an electrical economy and for the implementation of many renewable energy technologies. During the past two decades, the demand for the storage of electrical energy has increased significantly in the areas of portable, transportation, load-leveling and central backup applications. The present electrochemical energy storage systems are simply too costly to penetrate major new markets. Higher performance is required, and environmentally acceptable materials are preferred. Transformational changes in electrical energy storage science and technology are in great demand to allow higher and faster energy storage at lower costs and longer lifetimes necessary for major market enlargement. Most of these changes require new materials and/or innovative concepts, with demonstration of larger redox capacities that react more rapidly and reversibly with cations and/or anions.
Batteries are by far the most common form of storing electrical energy, ranging from: standard every day lead—acid cells, exotic iron-silver batteries for submarines taught by Brown in U.S. Pat. No. 4,078,125, nickel-metal hydride (NiMH) batteries taught by Kitayama in U.S. Pat. No. 6,399,247 B1, metal-air cells taught in U.S. Pat. No. 3,977,901 (Buzzelli), to Isenberg in U.S. Pat. No. 4,054,729, and to the lithium-ion battery taught by Ohata in U.S. Pat. No. 7,396,612 B2. These latter metal-air, nickel-metal hydride and lithium-ion battery cells require liquid electrolyte systems.
Batteries range in size from button cells used in watches, to megawatt load leveling applications. They are, in general, efficient storage devices, with output energy typically exceeding 90% of input energy, except at the highest power densities. Rechargeable batteries have evolved over the years from lead-acid through nickel-cadmium and nickel-metal hydride (NiMH) to lithium-ion batteries. NiMH batteries were the initial workhorse for electronic devices such as computers and cell phones, but they have almost been completely displaced from that market by lithium-ion batteries because of the latter's higher energy storage capacity. Today, NiMH technology is the principal battery used in hybrid electric vehicles, but it is likely to be displaced by the higher power energy and now lower cost lithium batteries, if the latter's safety and lifetime can be improved. Of the advanced batteries, lithium-ion is the dominant power source for most rechargeable electronic devices.
What is needed is a dramatically new electrical energy storage device that can easily discharge and charge a high capacity of energy quickly and reversibly, as needed. What is also needed is a device that can operate for years without major maintenance. What is also needed is a device that does not need to operate on natural gas, hydrocarbon fuel or its reformed by-products such as H2. One possibility is a rechargeable oxide-ion battery (ROB), as set out in application Ser. No. 12/695,386, filed on Jan. 28, 2010.
A ROB comprises a metal electrode, an oxide-ion conductive electrolyte, and a cathode. The metal electrode undergoes reduction-oxidation cycles during charge and discharge processes for energy storage. For example, in discharging mode, the metal is oxidized:
yMe+x/2O2=MeyOx
and is reduced in charging mode:
Me
yOx=x/2O2+yMe, where Me=metal.
Because the metal redox reactions are accompanied by large volume variation, for instance, if manganese (Mn) metal is used, the volume change associated with reaction of Mn+1/2O2=MnO is 1.73. In the case of tungsten (W), the volume change is 3.39 when W is totally oxidized to WO3. Without appropriately designed electrode, such drastic volume variation in practice can lead to spallation of metal electrode and possible failure of a ROB cell. The electrode comprises a structural skeleton, active metal component, and pores. The skeleton is made of single and/or multiple components and is capable of conducting electrical current, and it contains active metal component in its pores. The skeleton maintains structural integrity by accommodating the volume change associated with metal redox reactions in its pores.
The metal electrode must meet the following requirements to be effective in practice. It must be compatible with adjacent components including electrolyte and interconnect during battery fabrication and operation in terms of minimal mismatch in coefficient of thermal expansion and negligible chemical reactions with the electrolyte and interconnect. It must possess adequate electrical conductivity to minimize its Ohmic loss. It must possess sufficient catalytic activity to promote metal redox reaction to reduce polarization losses.
The energy storage capacity in terms of watt hour (Wh) of a ROB cell is ultimately determined by the amount of active metal incorporated into the metal electrode, assuming complete utilization of the active metal. Therefore, the more active metal in the electrode, the larger the storage capacity. Consequently, this is capacity advantage by increasing the thickness of a metal electrode. Producing thicker electrode, on the other hand, requires more skeleton materials and the cost of skeleton must be low for profitable purpose. Also the thick electrode can limit the cell power in watts (W) if the skeleton is incapable of sufficiently conducting electrical current, in other words, the Ohmic resistance of the skeleton is high. Thus, highly electrically conductive and low cost skeleton is needed to attain both high capacity and high power on the per capital basis.
It is a main object of this invention to provide cost effective oxidation-resistance metal as a support and current collector as a metal electrode for a ROB cell.
The above need for producing a low-cost, high capacity and high power ROB is supplied and object accomplished by providing oxidation-resistant metal (e.g. stainless steel) as the support in the metal electrode. The oxidation-resistant metal supplies a highly electrically conductive path in the metal electrode so that the Ohmic resistance from the metal electrode will be minimized. Secondly, the oxidation-resistant metal also possesses higher mechanical strength than its ceramic counterparts. As a result, the reliability and cell-production yield can be improved too. More importantly, selected oxidation-resistant metal such as stainless steel is cost effective. The invention broadly comprises a combination of side layers of oxidation-resistant metal, active metal component between the side layers and a bottom layer for producing and consuming oxygen species.
For a better understanding of the invention, reference may be made to the preferred embodiments exemplary of this invention, shown in the accompanying drawings in which:
The working principles of a rechargeable oxide-ion battery cell 10 are schematically shown in
Compared to its ceramic counterpart described above, the stainless steel used in this invention possesses high electrical conductivity, for example ˜9500 S/cm in the same environment. Its higher conductivity makes stainless steel outperform its ceramic counterparts for ROB metal electrode application. For instance,
The surface of the oxidation-resistant metal can be preferably modified with a protective coating 160 possessing electronic but negligible oxide-ion conductivity. The protective coating 160 is compromised of noble metal and electronic conductive ceramic including doped LaCrO3, doped SrTiO3 , and doped LaVO3, and any of their mixture, having a thickness from 10 nanometers to 500 micrometers, preferably from 100 nanometers to 100 micrometers, more preferably 1 micrometer to 50 micrometers. The oxygen redox bottom layer 120 is made of composite materials possessing high catalytic activity toward oxygen redox reaction and can possess mixed electronic and ionic conductivity. Exemplary materials include doped CeO2, stabilized zirconia, doped/updoped LaxSr1-xGayMg1-yO3, doped LaCrO3, doped SrTiO3, and doped LaVO3, and any of their mixture. Its thickness ranges from 10 nanometers to 200 micrometers, preferably from 100 nanometers to 100 micrometers, more preferably 5 micrometer to 50 micrometers. Processing techniques can include vapor deposition, thermal spraying, plating and impregnation.
The oxidation-resistant metal 140 can have a planar or closed end tubular geometry or a hybrid of the two. Electrolyte 220 is sandwiched between the bottom oxygen redox layer 120 and an outer air electrode 240.
While specific embodiments of the invention have been described in detail, it will be appreciated by those skilled in the art that various modifications and alternatives to those details could be developed in light of the overall teachings of the disclosure. Accordingly, the particular embodiments disclosed are meant to be illustrative only and not limiting as to the scope of the invention which is to be given the full breadth of the appended claims and any and all equivalents thereof.