Oxygen absorbent

BACKGROUND OF THE INVENTION
This invention relates to an oxygen absorbent, and particularly relates to an oxygen absorbent comprising a dithionite and a compound having water of crystallization or water of hydration.
In order to preserve foodstuffs, such as vegetables, fishes, shellfishes, meats, processed foodstuffs, such as potato chips, cakes, peanuts, etc., and so on, it is necessary to prevent the foodstuffs' from getting moldy and from putrefying. Prior art methods have used freezer storage, CA cold storage, vacuum packaging and replacing the gas present in the inner part of packaging by an inert gas for preventing foodstuffs from getting moldy and putrefying. Additives, such as antioxidant, have been used for preserving foodstuffs. Recently, governments have started to regulate the use of additives for food, since it is realized that some additives are injurious to humans. The freezer storage method requires large-scale apparatus and complicated operation, so the freezer storage method is costly.
Molds or eumycetes, bacterias and higher organisms such as insects tend to disturb preservation of foodstuffs. These mold eumycetes, bacterias and insects live and grow in the presence of oxygen and cause putrefaction and change in quality of foodstuffs.
Therefore, if oxygen can be selectively removed from the atmosphere in which the foodstuffs is packed, the problem of putrefaction and change in quality of foodstuffs can be overcome, and it will become possible to preserve foodstuffs for a long time.
It was known in the prior art that a dithionite reacts with oxygen in the presence of water to form a sulfate and sulfurous acid gas. By utilizing this property of dithionite a disoxidant or an oxygen absorbent comprising a dithionite, an alkaline material and activated carbon was known in the prior art (Japanese Pat. No. 686,561). The known disoxidant is prepared by mixing each component in a perfectly dry state. A small amount of water is added to the resulting mixture at the time of using the disoxidant. The known disoxidant has the following shortcomings:
(1) It is necessary to use a large amount of activated carbon in the disoxidant in order to prevent the disoxidant from hardening.
(2) Since, in the order of addition, water is the last component to be added to the composition, water is not uniformly distributed throughout the composition.
In general, activated carbon has deodorizing action, so it was said that the use of activated carbon for removing sulfurous acid gas as well as a gas generated from a dithionite is preferred. In this case, the amount of activated carbon present in the oxygen absorbent comprising dithionite, an alkaline material and activated carbon is as high as 50% by weight per 100 parts of the alkaline material. The above amount of activated carbon exceeds the amount of activated carbon required for deodorizing. Too great an amount of an oxygen absorbent containing excess activated carbon is required for exhibiting a desired oxygen-absorbing ability. In addition, since uneven distribution of water in the absorbent results in causing different rates of absorbing oxygen, an oxygen absorbent having a desired rate of absorbing oxygen can not be obtained. When a relatively large amount of water is added to the oxygen absorbent, water is likely to be uniformly distributed. But since the oxygen-absorbing rate of the oxygen absorbent containing a large amount of water becomes large, some of the dithionite reacts with oxygen in air before the use of the absorbent, and therefore, addition of a large amount of water results in a considerable amount of the dithionite. When the oxygen-absorbing rate is large, a rapid rise in temperature occurs through exothermic reaction. Such rise in temperature may be dangerous. In order to uniformly distribute water throughout the absorbent a process for adding water-containing sawdust to the absorbent has been proposed in place of direct addition of water thereto, but the process is not practical.
U.S. Pat. No. 2,825,651 proposes a process for preparing an oxygen absorbent comprising mixing a finely divided sulfite and a finely divided metal salt and compression-pelletizing the mixture in order to increase the rate of the oxidation of sulfite. However it was found that the rate of oxidation of the sulfite in the oxygen absorbent was not sufficient, and the absorbent has a low oxygen-absorbing rate.
SUMMARY OF THE INVENTION
We have carried out a wide range of research to find an oxygen absorbent which has neither the above shortcomings, nor reacts with oxygen in air before the use thereof. As a result, we have found that when a dithionite is mixed with a compound having water of crystallization, an oxygen absorbent not having the above shortcoming can be obtained.
Therefore, an object of this invention is to provide an oxygen absorbent which hardly react with oxygen before use but absorbs oxygen at a suitable rate at the time of using it. In other words, the oxygen absorbent of the present invention keeps a good absorbing ability of oxygen for a long time.
DETAILED DESCRIPTION OF THE INVENTION
This invention relates to an oxygen absorbent comprising a dithionite and at least one compound having water of crystallization or water of hydration, and substantially free from free water.
The term "oxygen absorbent" in the specification and the claim means an agent for absorbing oxygen.
The term "compound having water of crystallization or water of hydration" means compound having a water molecule and another component's molecule bonded to each other in a fixed ratio in its crystal structure. Examples of the compounds having water of crystallization include the following compound having water of crystallization: inorganic compounds, such as metal oxides, metal hydroxides, sulfides, halides, sulfates, sulfites, thiosulfates, nitrates, borates, phosphates, hydrogenphosphates, pyrophosphates, hydrogenpyrophosphates, carbonates, hydrogencarbonates, silicates, metasilicates, chromates, iodites, bromates, trimolybdates, tungstates, and ammonium salts; and organic compounds, such as organic acids, and organic salts.
The compound having water of crystallization or water of hydration has a catalytic action to the reaction of the dithionite with oxygen. An oxygen absorbent which has a desired oxygen-absorbing rate and the absorption reaction of which occurs at a desired temperature can be obtained by selecting the kind of the compound having water of hydration, the proportion thereof and the combination of two or more of said compounds. To the contrary, a compound not having water of hydration does not have such catalytic action.
The term "dithionite" means a compound represented by the formula
M.sub.x S.sub.2 O.sub.4
wherein M is cation, when valence of M is 1, x is 2, and when valence of M is 2, x is 1. The dithionite is generally called hydrosulfite. Examples of the dithionite include sodium dithionite (Na.sub.2 S.sub.2 O.sub.4) and zinc dithionite (ZnS.sub.2 O.sub.4). Sodium dithionite is preferred.
The amount of the compound having water of crystallization (sometimes referred to as catalytic compound) added to the dithionite is not critical. Conveniently, the amount of compound used may be in the range of from about 0.2 parts to about 2000 parts by weight, preferably from about 1 part to 1000 parts by weight, per 100 parts by weight of the dithionite. One of the compounds or two or more of the compounds may be used in the present invention.
The catalytic compounds are of two types: one is a compound exhibiting the catalytic action at room temperature and the other is a compound not exhibiting the catalytic action at room temperature, but exhibiting the catalytic action only when heated at as high as 90.degree. C or more.
The catalytic compounds exhibiting the catalytic action at room temperature include, such as, sodium carbonate decahydrate, sodium carbonate heptahydrate, sodium sulfate decahydrate, sodium sulfate heptahydrate, zinc sulfate heptahydrate, mixture of manganese sulfate tetra-, penta- and hexahydrate, ferrous sulfate heptahydrate, cerium sulfate tetrahydrate, sodium sulfite heptahydrate, calcium chloride hexahydrate, nickel chloride hexahydrate, sodium tetraborate deca-hydrate, sodium metaborate tetrahydrate, sodium pyrophosphate decahydrate, sodium tertiary phosphate dodecahydrate, disodium hydrogenphosphate dodecahydrate, sodium dihydrogenphosphate dihydrate, sodium metasilicate nonahydrate, barium hydroxide octahydrate, lithium hydroxide monohydrate, strontium hydroxide octahydrate, lead acetate trihydrate, oxalic acid dihydrate and mixture thereof. Of these compounds, most preferable compounds are as follows: sodium carbonate decahydrate, sodium carbonate heptahydrate, sodium sulphate decahydrate, sodium sulfate heptahydrate, manganese sulfate tetra-, penta- and hexahydrate, ferrous sulfate heptahydrate, sodium sulfite heptahydrate, calcium chloride hexahydrate, sodium tetraborate decahydrate, sodium metaborate tetrahydrate, sodium tertiary phosphate dodecahydrate, disodium hydrogen phosphate dodecahydrate, and sodium metasilicate nonahydrate.
The catalytic compounds exhibiting the catalytic action only when heated at as high as 90.degree. C or more include, such as, sodium thiosulfate pentahydrate, copper sulfate pentahydrate, nickel sulfate heptahydrate, CaSO.sub.4.1/2 H.sub.2 O, barium chloride dihydrate, calcium chloride dihydrate, molybdic acid monohydrate, sodium carbonate monohydrate, sodium acetate trihydrate and mixture thereof.
The oxygen absorbent of this invention may contain as third component(s) (a) at least one anhydrous alkaline material, such as sodium hydroxide potassium hydroxide, sodium carbonate, sodium bicarbonate, potassium carbonate, potassium bicarbonate, sodium phosphate, sodium tetraborate, magnesium hydroxide, calcium hydroxide and mixture thereof and/or (b) at least one adsorbent, such as activated carbon, zeolite silica gel, alumina, diatomaceous earth, activated clay and mixture thereof. When such alkaline material and or such adsorbent are contained in the oxygen absorbent of this invention, the generation of sulfurous acid gas can further be prevented. When an alkaline material is used as the compound having water of crystallization or water of hydration, the alkaline material can prevent the generation of sulfurous acid gas without addition of the third component.
The amount of the adsorbent incorporated in the oxygen absorbent may be in the range of from about 2 to about 75 parts by weight per 100 parts by weight of the dithionite.
When an alkaline material is used as a compound having water of hydration, the amount of the alkaline material incorporated in the oxygen absorbent as the third component may be in the range of from 0 to about 2400 parts by weight per 100 parts by weight of the dithionite. When alkaline material is not used as the compound having water of crystallization, the amount of the alkaline material incorporated in the oxygen absorbent as the third component may be in the range of from about 150 to about 2400 parts by weight per 100 parts by weight of the dithionite.
The oxygen absorbent of the present invention has relatively slow oxygen-absorbing rate, so handling of the absorbent as well as the preparation of the absorbent are easy. The oxygen-absorbing rate of the present oxygen absorbent depends on the kind of the catalytic compound, the proportion thereof and the combination of two or more catalytic compounds. So an oxygen absorbent having a desired oxygen-absorbing rate according to the object of use can be obtained. When the present oxygen absorbent is preserved while be isolated from oxygen, little dithionite decomposes, and the absorbent is hardly hardened during the preservation and during using it.
The present oxygen absorbent should be preserved while being isolated from oxygen. In addition, the present oxygen absorbent can be used as it is without any addition of water to the absorbent.
For example, the present oxygen absorbent can be stored in a sealed bag made of inpermeable material, such as aluminum foil, polyester, polyvinylidene chloride and the like. When the seal is broken, the absorbent begins to absorb oxygen.
The oxygen absorbent of this invention is usable in a variety of industrial fields, but is particularly useful for preventing change in quality of fresh vegetables, fresh fish and shellfish, and processed foodstuffs, such as potato chips, cakes, peanuts, oil and the like, and for anti-oxidizing metals and organic chemicals.

The present invention is further illustrated by the following Examples and Comparative Examples. However, this invention should not be limited by these examples and comparative examples. The percent and parts in the Examples are based on weight unless otherwise specified.
EXAMPLE 1
Three grams of anhydrous sodium dithionite (85% pure) was thoroughly mixed with each of the particulate compounds having water of crystallization as shown in Table 1 in the amount as shown in Table 1 in a nitrogen atmosphere. Each of the mixtures was placed in a 1l sealed glass bottle equipped with an Hg manometer, which contains dried air. The absorption reaction was carried out at 25.degree. C. The degree of reduced pressure in the glass bottle was periodically determined by Hg manometer at 25.degree. C, thereby calculating the proportion of oxygen removed or absorbed. After the absorption reaction had continued for 72 hours, quantitative analysis for residual oxygen and generated sulfurous acid gas was carried out by using the Hempel method and detector tube for 1 to 80 ppm, respectively. The results are shown in Table 1.
For comparison, absorbing tests on only the dithionite and the mixture of the dithionite and anhydrous compound were carried out. The results are also shown in Table 1.
Table 1______________________________________ Gas analysis after 72 hrsCompound having Time required residual residualwater of crystalliza- for removing oxygen sulfuroustion and amount 50% of oxygen (% by acid gasthereof added in the bottle volume) (ppm)______________________________________Examplesodium carbonate less than less than less thandecahydrate (20 gr) 5 minutes 0.2 1sodium carbonate less than " "heptahydrate (15 gr) 5 minutessodium boratedecahydrate (10 gr) 1 hr " "sodium boratedecahydrate (5 gr) 4 hrs " "sodium metaboratetetrahydrate (7 gr) 2 hrs " "disodium hydrogen-phosphate dodeca- 5 minutes " "hydrate (20 gr)barium hydroxideoctahydrate (11 gr) 30 minutes " "sodium pyrophosphatedecahydrate (13 gr) 18 hrs " "lithium hydroxide less thanmonohydrate (12 gr) 5 minutes " "sodium metasilicatenonahydrate (9 gr) 10 minutes " "strontium hydroxide less thanoctahydrate (9 gr) 5 minutes " "sodium tertiaryphosphate dode- 20 minutes " "cahydrate (9 gr)Controlnone -- 21.0 --anhydrous sodiumcarbonate (20 gr) -- 21.0 --anhydrous sodiumborate (10 gr) -- 21.0 --anhydrous sodiummetaborate (7 gr) -- 21.0 --anhydrous disodiumhydrogenphosphate -- 21.0 --(20 gr)______________________________________
EXAMPLE 2
Three grams of anhydrous sodium dithionite (85% pure), 12 gr of dried calcium hydroxide or magnesium hydroxide was thoroughly mixed with each of the particulate compounds having water of crystallization as shown in Table 2 in the amount as shown in Table 2 in a nitrogen atmosphere. Test procedure and gas analysis were carried out in the same way as in Example 1. For comparison, the tests on the composition containing anhydrous compound in place of the catalytic compound were carried out. The results are shown in Table 2.
Table 2__________________________________________________________________________ Time required Gas analysis after 72 hrs Compound having water of for removing residual residualAlkaline crystallization and amount 50% of oxygen oxygen sulfurousmaterial thereof added in the bottle (% by volume) acid gas (ppm)__________________________________________________________________________ExampleMg(OH).sub.2 sodium carbonate less than less than less than decahydrate (0.5 gr) 5 minutes 0.2 1" sodium carbonate less than " " heptahydrate (1 gr) 5 minutesCa(OH).sub.2 disodium hydrogenphosphate less than " " dodecahydrate (5 gr) 5 minutes" sodium metaborate 2 hrs " " tetrahydrate (11 gr)" sodium dihydrogenphosphate 5 hrs " " dihydrate (20 gr)" calcium chloride 1 hr " " hexahydrate (4 gr)" sodium sulfite 10 minutes " " heptahydrate (2 gr)Ca(OH).sub.2 sodium sulfate less than " " decahydrate (1 gr) 5 minutes" nickel chloride 6 hrs " " hexahydrate (10 gr)Mg(OH).sub.2 zinc sulfate heptahydrate 13 hrs " " (11 gr)Ca(OH).sub.2 mixture of manganese sulfate tetra, penta 4 hrs " " and hexahydrate (14 gr)" ferrous sulfate 4 hrs " " heptahydrate (9.8 gr)" cerium sulfate 40 minutes " " tetrahydrate (5 gr)" lead acetate trihydrate 12 hrs " " (12 gr)" sodium sulfate less than " " heptahydrate (1 gr) 5 minutes" oxalic acid dihydrate (20 gr) 12 hrs " "ControlMg(OH).sub.2 anhydrous sodium carbonate (1 gr) -- 21.0 --Ca(OH).sub.2 anhydrous disodium hydrogenphosphate (5 gr) -- 21.0 --" anhydrous sodium dihydro- genphosphate (20 gr) -- 21.0 --" anhydrous calcium chloride (4 gr) -- 21.0 --" anhydrous sodium sulfite (2 gr) -- 21.0 --__________________________________________________________________________
EXAMPLE 3
Three grams of anhydrous sodium dithionite (85% pure) was mixed with the particulate components as shown in Table 3 in the amount shown in Table 3 in a nitrogen atmosphere. The compounds having water of crystallization were particulate. Test procedure and gas analysis were carried out in the same way as in Example 1. The results are shown in Table 3.
Table 3__________________________________________________________________________ Gas analysis afterCompounds having Amount of 72 hrswater of crystalli- dried Time required residual residualzation and amount of calcium for removing oxygen sulfurousthe compound added hydroxide 50% of oxygen (% by acid gas(gr) added in the bottle volume) (ppm)__________________________________________________________________________sodium carbonateheptahydrate(5 gr) and sodium non- less than less than less thanmetaborate tetra- addition 5 minutes 0.2 1hydrate (5 gr)disodium hydrogen-phosphate dodeca-hydrate (1 gr) and 12 gr less thansodium sulfate 5 min. " "decahydrate (1 gr)sodium borate deca-hydrate (10 gr) and non- 10 minutessodium sulfite addition " "heptahydrate (2 gr)calcium chloridehexahydrate (5 gr)and sodium dihydro- 12 gr 1 hr " "genphosphatedihydrate (5 gr)sodium carbonatedecahydrate (2 gr) 12 gr less thanand sodium borate 5 minutes " "decahydrate (2 gr)__________________________________________________________________________
EXAMPLE 4
Three grams of anhydrous sodium dithionite (85% pure) was mixed with the particulate components shown in Table 4 in the amount shown in Table 4 in a nitrogen atmosphere. The activated carbon employed was dried and particulate. Test procedure and gas analysis were carried out in the same way as in Example 1. For comparison, the above procedure was repeated except that the composition not containing the compound having water of crystallization and the composition containing an anhydrous compound in place of the catalytic compound were used. The results are shown in Table 4.
Table 4__________________________________________________________________________ Amount of Gas analysis after dried Amount of 72 hrsCompound having water calcium activated Time required residual residualof crystallization and hydroxide carbon for removing oxygen sulfurousamount thereof added added added 50% of oxygen (% by acid gas(gr) (gr) (gr) in the bottle volume) (ppm)__________________________________________________________________________Examplesodium borate deca- non- 0.5 1 hr less than less thanhydrate (10 gr) addition 0.2 1sodium carbonate less than " "decahydrate (1 gr) 12 0.5 5 minutessodium dihydrogen-phosphate dihydrate 12 0.5 6 hrs " "(20 gr)Controlnone 12 -- -- 21.0 "none 12 0.5 -- 21.0 "none non- 12 -- 21.0 " additionanhydrous sodium 12 0.5 -- 21.0 "carbonate (1 gr)anhydrous sodium 12 0.5 -- 21.0 "sulfate (10 gr)__________________________________________________________________________
EXAMPLE 5
Nine grams of anhydrous sodium dithionite (85% pure) was mixed with the components as shown in Table 5 in the amount as shown in Table 5 in a nitrogen atmosphere. Each of the mixtures was usually divided into three parts, and the first one-third of each mixture was immediately placed in a 2l triangle glass flask equipped with Hg manometer, which contains dried air. The absorption reaction was carried out at 20.degree. C until oxygen was absorbed no longer. The degree of reduced pressure in the bottle was determined by Hg manometer at 25.degree. C, thereby calculating the amount of oxygen removed or absorbed.
The remaining two-thirds were left standing in a 100 ml sealed glass bottle at 22.degree. C to 25.degree. C for 1 week or one month, respectively. Thereafter, the absorption tests of each mixture aliquot left standing for 1 week or one month were carried out in the same way as above.
The ratio of the oxygen absorption of each mixture aliquot left standing for the above specified periods to that of each mixture aliquot which was not left standing was calculated. The results are shown in Table 5. The data show that the smaller the ratio, the more the quality of mixture was impaired.
For comparison, the above procedure was repeated except that water was used in place of the compound having water of crystallization. The results are shown in Table 5 as control.
Table 5______________________________________ Amount AmountCompound having water of dried of driedof crystallization calcium activated * -and amount thereof hydroxide carbon After Afteradded (gr) or amount added added one oneof water added (gr) (gr) (gr) week month______________________________________Examplesodium carbonatedecahydrate (60 gr) -- -- 91.6 87.3sodium carbonateheptahydrate (45 gr) -- -- 91.9 88.2sodium borate deca-hydrate (30 gr) -- -- 93.2 89.1sodium metaboratetetrahydrate (21 gr) -- -- 92.1 88.5disodium hydrogen-phosphate dodeca- -- -- 90.2 87.0hydrate (60 gr)sodium carbonatedecahydrate (3 gr) 36 1.5 91.1 86.9sodium boratedecahydrate (30 gr) -- 1.5 92.9 89.3calcium chloridehexahydrate (12 gr) 36 -- 89.9 81.1sodium dihydrogen-phosphate dihydrate 36 -- 88.1 82.0(60 gr)sodium sulfatedecahydrate (4.5 gr) 36 -- 87.0 79.1sodium sulfiteheptahydrate (6 gr) 36 -- 87.5 80.1nickel chloridehexahydrate (30 gr) 36 -- 87.7 79.3zinc sulfate hepta-hydrate (33 gr) 36 -- 88.3 79.6cerium sulfate tetra-hydrate (15 gr) 36 -- 87.4 79.5mixture of manganesesulfate tetra, penta- 36 -- 87.9 80.6and heptahydrate(42 gr)ferrous sulfateheptahydrate (29.4 gr) 36 -- 86.9 79.1sodium dihydrogen-phosphate dihydrate 36 1.5 88.7 82.0(60 gr)sodium sulfatedecahydrate (30 gr) 36 1.5 88.1 81.4Controlwater (1.5 gr) 36 -- 85.0 73.8water (6 gr) 36 -- 73.2 46.9water (1.5 gr) 36 1.5 85.7 74.7water (6 gr) 36 1.5 73.9 47.5______________________________________ Note: mark "--" shows non-addition. mark "*" shows the ratio of the oxygen absorption of each mixture aliquot left standing for the following specified periods to that of each mixture aliquot which was not left standing.
EXAMPLE 6
Three grams of anhydrous sodium dithionite (85% pure) was mixed with the components as shown in Table 6 in the amount as shown in Table 6 in a nitrogen atmosphere. Sodium sulfate decahydrate and sodium borate decahydrate employed were particulate. Each of the mixtures was placed in a 1l sealed glass bottle equipped with Hg manometer, which contains dried air. The degree of reduced pressure in the glass bottle was periodically determined by Hg manometer at 25.degree. C and 5.degree. C, thereby calculating the proportion of oxygen removed or absorbed. For comparison, the above procedure was repeated except that water was used in place of the compound having water of crystallization. The results are shown in Table 6.
Table 6______________________________________Compound of Timewater Amount requiredcrystallization of dried for amount calcium Time required removing thereof hydroxide for removing 50% of added added 50% of oxygen oxygen inkinds (gr) (gr) in the bottle the bottle______________________________________25.degree. CExamplesodiumsulfate 0.200 12 15 minutes 35 minutesdecahy-drate" 0.150 12 20 minutes 1 hr" 0.125 12 30 minutes 2 hrs" 0.100 12 1 hr 5 hrs" 0.075 12 2 hrs 20 hrs" 0.050 12 7 hrs 55 hrssodiumborate 10 -- 50 minutes 3 hrsdecahy-drate" 6 -- 1.5 hrs 10 hrs" 4 -- 2.5 hrs 40 hrs" 2 -- 5.5 hrs 75 hrs" 1 -- 18 hrs 125 hrs25.degree. CControlwater 0.20 12 12 minutes 40 minutes" 0.10 12 1 hr 20 hrs Only 80% of oxygen was" 0.075 12 7.5 hrs removed after 10 days passed. Only 32% of oxygen was" 0.05 12 removed even after 10 days passed.5.degree. CExamplesodiumsulfate 3.2 12 4 hrs 25 hrsdecahy-drate" 1.6 12 7 hrs 35 hrs" 0.8 12 9 hrs 50 hrs" 0.4 12 12 hrs 65 hrs" 0.2 12 18 hrs 80 hrs" 0.1 12 40 hrs 200 hrs5.degree. CControlwater 0.8 12 2 minutes 10 minutes" 0.4 12 5 minutes 1 hr Only 75% of oxygen was" 0.2 12 30 minutes removed even after 10 days passed Only 45% of oxygen was" 0.1 12 removed even after 10 days passed. Only 10% of oxygen was" 0.05 12 removed even after 10 days passed______________________________________ Note: The mark "--" shows non-addition.
EXAMPLE 7
The procedure of Example 1 was repeated except that 3 gr of anhydrous sodium dithionite was mixed with 20 gr of dried calcium hydroxide and the particulates components as shown in Table 7, and the absorption reaction was carried out at 90.degree. C. For comparison, absorbing tests on the composition not containing the compound having water of crystallization and the composition containing an anhydrous compound in place of the catalytic compound were carried out.
The results are shown in Table 7.
Table 7______________________________________ Gas analysis after 72 hrsCompound having Time required residual residualwater of crystalliza- for removing oxygen sulfuroustion and amount 50% of oxygen (% by acid gasthereof added in the bottle volume) (ppm)______________________________________ExampleCalcium chloride 30 minutes less than less thandihydrate (5 gr) 0.2 1barium chloridedihydrate (3 gr) 1 hr " "sodium carbonatemonohydrate (5 gr) 1 hr " "CaSO.sub.4 . 1/2 H.sub.2 O(27 gr) 3 hrs " "molybdic acidmonohydrate (20 gr) 2 hrs " "sodium acetatetrihydrate (3 gr) 1 hr " "nickel sulfate hepta-hydrate (5 gr) 2 hrs " "Controlnone -- 21.0 --anhydrous calciumchloride (5 gr) -- 21.0 --anhydrous sodiumcarbonate (5 gr) -- 21.0 --______________________________________
EXAMPLE 8
The procedure of Example 1 was repeated except that 3 gr of anhydrous sodium dithionite was mixed with 12 gr of dried calcium hydroxide and the particulate components as shown in Table 8, and the absorption reaction was carried out at 50.degree. C. For comparison, absorbing tests on the composition not containing, the compound having water of crystallization and the composition containing an anhydrous compound in place of the catalytic compound were carried out.
The results are shown in Table 8.
Table 8______________________________________ Gas analysis after 72 hrsCompound having Time required residual residualwater of crystalliza- for removing oxygen sulfuroustion and amount 50% of oxygen (% by acid gasthereof added in the bottle volume) (ppm)______________________________________Examplesodium thiosulfate 15 minutes less than less thanpentahydrate (4 gr) 0.2 1copper sulfatepentahydrate (5 gr) 2 hrs " "Controlnone -- 21.0 --anhydrous sodiumthiosulfate (4 gr) -- 21.0 --anhydrous coppersulfate (5 gr) -- 21.0 --______________________________________
EXAMPLE 9
The procedure of Example 5 was repeated except that 9 gr of anhydrous sodium dithionite was mixed with the components as shown in Table 9, and absorption reaction was carried out at 90.degree. C.
Table 9______________________________________Compound having water of *crystallizaton and amount After Afterthereof added (gr) one week one month______________________________________Calcium chloride dihydrate(15 gr) 98.2 96.9barium chloride dihydrate(9 gr) 99.2 98.0sodium carbonate mono-hydrate (15 gr) 99.0 97.9CaSO.sub.4 . 1/2 H.sub.2 O (81 gr) 99.1 98.2molybdic acid monohydrate(60 gr) 98.4 97.5sodium acetate trihydrate(15 gr) 98.3 97.1nickel sulfate hepta-hydrate (15 gr) 99.0 98.4______________________________________ * shows the ratio of the oxygen absorption of each mixture aliquot left standing for the following specified periods to that of each mixture aliquot which was not left standing.
EXAMPLE 10
Three grams of anhydrous sodium dithionite (85% pure) was mixed with the particulate components as shown in Table 10 in the amount as shown in Table 10 in a nitrogen atmosphere. Test procedure and gas analysis were carried out in the same way as in Example 1. For comparison, the above procedure was repeated except that anhydrous sodium sulfate was used in place of the sodium dithionite. The results are shown in Table 10. It is apparent from the above results that the mixture of anhydrous sodium sulfite and a compound having water of hydration does not absorb oxygen.
Table 10__________________________________________________________________________ Gas analysis afterCompounds having Amount 72 hourswater of crystalliza- of dried Time required residual residualtion and amount of calcium for removing oxygen sulfurousthe compound added hydroxide 50% of oxygen (% by acid gas(gr) added in the bottle volume (ppm)__________________________________________________________________________ ferrous sulphate heptahydrate 12 gr 23 hrs less than less than (0.45 gr) 0.2 1Exam-ple sodium sulphate decahydrate (0.10 gr) 12 gr 1 hr " " ferrous sulphate heptahydrate (0.45 gr) -- -- 21 "Con-trol sodium sulphate -- -- 21 " decahydrate (0.10 gr)__________________________________________________________________________

Oxygen absorbent

Information

Patent Number

Date Filed

Date Issued

Inventors

Original Assignees

Examiners

Agents

CPC

US Classifications

Field of Search

US

International Classifications

Abstract

Description

Claims

Priority Claims (1)

US Referenced Citations (1)