Patent Application
20150376817
The present invention relates to oxygen and nitrogen co-doped polyacrylonitrile-based carbon fibers and the preparation method thereof, and in particular, to oxygen and nitrogen co-doped polyacrylonitrile-based carbon fibers prepared by electrochemical modification. The present invention belongs in the technical field of electrochemistry of materials.
Carbon fibers are obtained from carbonization or graphitization of organic fibers and have turbostratic graphitic microstructure. They are inorganic high-molecular-weight fibers having a carbon content above 90%, and are called graphite fibers when the carbon content is higher than 99%. Carbon fibers have high axial strength and modulus, no creep, good fatigue resistance and corrosion resistance, specific heat and conductivity between those of non-metal and metal, a small thermal expansion coefficient, low fiber density and good X-ray transmission, while they are poor in impact resistance, prone to damage, and oxidized under the action of strong acids, and may also lead to phenomena like metal carbonization, carburization and electrochemical corrosion when compounded with metals. Therefore, surface treatment of carbon fibers before use is necessary.
Carbon fibers can be prepared from carbonization of each of polyacrylonitrile fibers, pitch fibers, viscose or phenolic fibers, and can be classified into filaments, staple fibers and chopped fibers according to their state, or into general carbon fibers and high-performance carbon fibers according to their mechanical properties. General carbon fibers have strength of 1,000 MPa and a modulus of approximately 100 GPa. High-performance carbon fibers can be further categorized into the high-strength type (strength: 2,000 MPa; modulus: 250 GPa) and the high-modulus type (modulus: 300 GPa or higher), wherein those having strength higher than 4,000 MPa are called the ultrahigh-strength type and those having a modulus higher than 450 GPa are called the ultrahigh-modulus type. With the advances in the aeronautic and astronautic industry, a high-strength-and-high-elongation type of carbon fibers having elongation greater than 2% has also been developed. Polyacrylonitrile (PAN) carbon fibers are most used and have a market share of 90% or more. Preparation of carbon fibers comprises the following four procedures: fiber spinning (production of precursor), thermal stabilization (pre-oxidation), carbonization, and graphitization, during which the accompanying chemical reactions include dehydrogenation, cyclization, pre-oxidation, oxidation, deoxygenation, and the like.
PAN as the precursor of carbon fibers contains cyano groups (—C≡N), which have a high polarity and impart unique characteristics to the structure and performance of PAN. After sufficient carbonization (at 1,000° C. to 1,500° C.) of the PAN precursor, the mass percentages of N, H and O dramatically decrease and the carbon content reaches 93%-98%, while some doped nitrogen still remains with a nitrogen content of 2%-7%. Graphite fibers are obtained from high-temperature graphitization of carbon fibers at 2,200° C. to 3,000° C., which is a continuation of solid-phase carbonization, driving nearly all non-carbon elements (mainly nitrogen) out of the carbon fibers and leaving graphite fibers having almost 100% carbon. Therefore, one important feature of the PAN-based carbon fibers not treated with the high-temperature graphitization is its distinctive nitrogen-doped structure. For pitch-based carbon fibers, the content of doped nitrogen is low, generally less than 1%, while viscose-based carbon fibers do not contain doped nitrogen.
Thanks to their excellent mechanical property, carbon fibers have been used mainly as reinforcing components in composite materials. Recently, because of their superior conductivity, for example the T700PAN-based carbon fibers produced by Toray Industries, Inc., Japan having resistivity of 1.6×10−3 Ω·cm, carbon fibers have started drawing attentions for their application in electrochemistry, and may be used to produce electrode materials for cells utilizing oxygen dissolved in seawater (metal half-fuel cells using seawater as the medium), proton exchange membrane fuel cells, metal-air fuel cells, microbial fuel cells, a supercapacitor, redox flow cells, lead-acid cells, lithium-ion cells, electrochemical treatment of waste water, an electrochemical transducer, and the like.
Carbon fibers may serve as the electrode material for cathodic oxygen reduction. Oxygen reduction reaction (ORR) plays a vital role in electrochemistry. In various fuel cell technologies, electric powder is generated from an electrochemical reaction constituted by the cathodic oxygen reduction and the anodic oxidation of fuels (such as hydrogen, methanol, active metal, microorganisms, etc.). In the waste water treatment technology by the Electro-Fenton method, cathodic oxygen reduction by electrochemical means produces H2O2 as a continuous source of the Fenton reagent, and the H2O2 reacts with Fe2+ in the solution to produce a highly oxidizing .OH free radical, which can nonselectively destroy nearly all organic contaminants to complete mineralization. Hence, development of carbon-fiber electrode material having excellent electrocatalytic activity for cathodic oxygen reduction offers very bright prospects for various applications.
Fuel cells have been well acknowledged as a clean energy-conversion system. However, their commercialization has been thwarted by two major technical limitations, i.e. cost and reliability. Currently, Pt-based catalysts are the major reason for the high cost of fuel cells, and cheap, highly active and highly stable electrocatalysts for oxygen reduction have been the hot spot of research on fuel cells. In recent years, the fact that nitrogen doping has a significant impact on the performance of carbon and its composite electrocatalyst has attracted wide attention. It has been reported that nitrogen-doped carbon and its composite material have significantly improved catalytic performance which in a basic medium surpasses that of commercial Pt catalysts, and look very promising as a non-noble metal catalyst to replace Pt for use in fuel cells (Gong K, et al., Nitrogen-Doped Carbon Nanotube Arrays with High Electrocatalytic Activity for Oxygen Reduction, Science, 2009. 333: 760-764).
Methods for doping nitrogen in carbon material can be basically classified into (1) in situ doping, wherein nitrogen is doped during synthesis of carbon material; and (2) post doping, wherein synthesized carbon material is subjected to post-treatment with a N-containing precursor (Wen Y, et al., Studies on Nitrogen-Doped Nano-Carbons and Their Non-Pt Metal Composites as Electrocatalysts, Progress in Chemistry, 2010, 22: 1550-1555). In in situ doping, chemical vapor deposition (CVD) is performed on a substrate or template with an organic nitride as a precursor, and, similar to hydrocarbons, the nitride may retain some C—N bonds when the substrate decomposes such that a N-doped nanostructure is formed. In post doping, nano-carbon undergoes post-treatment in a nitrogen-containing atmosphere, so as to afford nitrogen-doped nano-carbon material. Both doping methods are for nano-scale carbon material and generally require a preparation temperature not higher than 1,000° C. A preparation temperature over 1,000° C. may lead to severe escaping of doped nitrogen, which affects the nitrogen doping effect, while an excessively low preparation temperature may also create negative impacts on conductivity of the nitrogen-doped carbon material. In addition, the reactions during the preparation require strict conditions and thus are not suitable for large-scale production, and in actual applications an adhesive agent will be required to manufacture an electrode from the prepared nano-scale nitrogen-doped carbon material.
Commercialized PAN-based carbon fibers are fibrous structures in a size of a few microns, excellent in conductivity, and easy to be processed into an electrode. Commercialized SWB1200 seawater cells (Kongsberg Simrad, Norway), which employ a brush electrode made from PAN-based carbon fibers as the positive electrode for the seawater cells utilizing dissolved oxygen. Although obtained through carbonization at a temperature over 1,000° C., such commercialized PAN-based carbon fibers still have a residual doped nitrogen content of 2%-7%. Therefore, the doped nitrogen contained therein has higher thermal and chemical stability than those obtained by the two doping methods describe above. However, the doped nitrogen inherent in unmodified PAN-based carbon fibers has limited catalytic activity for ORR, and thus has not caught a lot of interest and needs certain modification to obtain good ORR activity (Xu H, et al., Seawater Battery with Electrochemical Supercapacitance, Journal of Electrochemistry, 2012, 18: 24-30).
Previous surface modifications of carbon fibers mainly aim to improve the binding strength between carbon fibers and the composite material, and major modification methods include ozone chemical oxidation and electrochemical anodic oxidation. PAN-based carbon fibers have a smooth surface and show chemical inertness, and these characteristics are unfavorable for them to produce good interface binding with a resin substrate. If surface treatment is applied to PAN-based carbon fibers to introduce active groups onto the surface and increase the surface roughness, then the binding of the carbon fibers can be improved and the mechanical performance of resin-based composite material can be enhanced. Among these methods, anodic oxidation is easy to control, can achieve even oxidation of every fiber, has great operational flexibility, is readily applicable to large-scale treatment, and can increase the interlayer shearing strength in carbon-fiber composite material to about 100 MPa by introducing active functional groups such as oxygen- and nitrogen-containing groups to the surface. However, anodic oxidation as a method for improving mechanical performance requires mild oxidation conditions. Furthermore, if anodic oxidation is used alone for treatment, the introduced oxygen-containing functional groups would be mostly located at the carbon basal planes, and the introduced nitrogen-containing functional groups would be an imino (—NH) or amino (—NH2) group, in which case the introduced doped nitrogen comes from the compounds in the anodic oxidation solution and is not a nitrogen-containing functional group formed from the inherent doped nitrogen previously present in the carbon fibers. In addition, these oxygen- and nitrogen-containing functional groups fail to exhibit effective pseudocapacitive characteristics and electrocatalytic activity for cathodic oxygen reduction, and thus cannot meet the requirements on electrode material.
CN101697323A discloses an electrochemically modified graphite electrode, in which a graphite body is subjected to cyclic treatment between electrochemical oxidation and electrochemical reduction in an aqueous solution of an electrolyte, so as to directly obtain a rough, porous activated layer having certain thickness, abundant oxygen-containing active functional groups and a microcrystalline flake-like structure. The reversible redox reactivity of these oxygen-containing active functional groups may be used for an electrochemical capacitor. CN102176380A discloses a redox reaction electrochemical capacitor, and discloses that the electrochemically modified graphite electrode also has electrocatalytic activity for the redox couples frequently used in redox flow cells. Since graphite itself does not contain oxygen, the surface of the graphite electrode obtained after the above electrochemical treatment does not have a nitrogen-containing active functional group, and thus does not have the characteristics of nitrogen-doped material.
Furthermore, the electrochemical capacitor is characterized by high power, and the fuel cell is characterized by high energy density. Since they are individual devices, a combination thereof is needed to satisfy the requirement for both high power and high energy density with respect to power performance. If they are combined in one unit, the volume of the system will be reduced. This sets out a requirement for electrode material having the characteristics of both the electrochemical capacitor and the fuel cell (mainly depending on the ORR performance).
In summary, development of an oxygen and nitrogen co-doped PAN-based carbon fiber prepared by electrochemical modification remains a crucial problem to be eagerly solved in the field of electrochemistry of material.
In order to solve the above technical problems, the present invention aims to provide oxygen and nitrogen co-doped PAN-based carbon fibers which have on their surface oxygen-containing active functional groups and nitrogen-containing active functional groups, and also have pseudocapacitive characteristics for redox reactions and electrocatalytic activity for cathodic oxygen reduction reactions (ORR).
The present invention also aims to provide a method for preparing the oxygen and nitrogen co-doped PAN-based carbon fibers described above.
In order to achieve the above aims, the present invention provides a kind of oxygen and nitrogen co-doped PAN-based carbon fibers, which are prepared by electrochemical modification of raw-material PAN-based carbon fibers such that their surface has an active layer formed by oxygen-containing active functional groups and nitrogen-containing active functional groups, wherein the nitrogen-containing active functional groups are obtained after activation of the doped nitrogen inherent in the raw-material PAN-based carbon fibers by electrochemical modification. In the active layer, the oxygen-containing active functional groups have reversible redox reactivity, and the nitrogen-containing active functional groups have electrocatalytic activity for cathodic oxygen reduction. Therefore, the oxygen and nitrogen co-doped PAN-based carbon fibers according to the present invention have both the pseudocapacitive characteristics, generated on the basis of the reversible redox reactions of the active functional groups, and electrocatalytic activity for cathodic oxygen reduction.
In the oxygen and nitrogen co-doped PAN-based carbon fibers described above, preferably, the nitrogen-containing active functional groups are one or a combination of more of pyridinic nitrogen, pyrrolic nitrogen, graphitic nitrogen and the like located at the edges of carbon basal planes on the surface of the oxygen and nitrogen co-doped PAN-based carbon fibers. One or more of the nitrogen-containing active functional groups have electrocatalytic activity for cathodic oxygen reduction.
In the oxygen and nitrogen co-doped PAN-based carbon fibers described above, preferably, the oxygen-containing active functional groups are one or a combination of more of carboxyl oxygen, ketonic oxygen, hydroxyl oxygen and the like located at the edges of carbon basal planes on the surface of the oxygen and nitrogen co-doped PAN-based carbon fibers. The different oxygen-containing active functional groups have reversible redox reactivity therebetween.
In the oxygen and nitrogen co-doped PAN-based carbon fibers described above, preferably, the raw-material PAN-based carbon fibers have not been treated by graphitization, and have a nitrogen content of 1% or more with respect to the total mass of the raw-material PAN-based carbon fibers.
According to an embodiment of the present invention, preferably, the shape of the oxygen and nitrogen co-doped PAN-based carbon fibers described above may be one or a combination of more of the shapes of a bundle, felt, foam, a brush, paper, cloth, and the like. The oxygen and nitrogen co-doped PAN-based carbon fibers provided in the present invention may be obtained by electrochemical modification after being processed into the above shapes, or may be processed into the above shapes after electrochemical modification. A person skilled in the art can select a size for the PAN-based carbon fibers of different shapes upon needs.
In the oxygen and nitrogen co-doped PAN-based carbon fibers described above, preferably, the electrochemical modification comprises the steps of: placing raw-material PAN-based carbon fibers in an electrolyte solution, and applying cyclic treatment between electrochemical oxidation and electrochemical reduction, to obtain the oxygen and nitrogen co-doped PAN-based carbon fibers.
The present invention also provides a method for preparing the oxygen and nitrogen co-doped PAN-based carbon fibers described above, the method comprising the steps of: placing raw-material PAN-based carbon fibers in an electrolyte solution, and applying cyclic treatment between electrochemical oxidation and electrochemical reduction, to obtain the oxygen and nitrogen co-doped PAN-based carbon fibers. In the preparation method, after the cyclic treatment between electrochemical oxidation and electrochemical reduction, an active layer formed by oxygen-containing active functional groups and nitrogen-containing active functional groups is obtained, wherein the nitrogen-containing active functional groups are obtained after activation of the non-active doped nitrogen inherent in the unmodified raw-material PAN-based carbon fibers by electrochemical modification.
In the preparation method above, preferably, based on the total mass of the oxygen and nitrogen co-doped PAN-based carbon fibers, the total quantity of electricity for electrochemical oxidation is 1,000 to 10,000 C/g, and the total quantity of electricity for electrochemical reduction is 1,000 to 10,000 C/g. During the cyclic treatment between electrochemical oxidation and electrochemical reduction, the electrochemical oxidation and the electrochemical reduction should be alternately performed, but which one of them is performed first or last is not limited. In addition, the number of cycles of electrochemical oxidation and electrochemical reduction is not limited, and when the total quantities of electricity for electrochemical oxidation and reduction meet the above requirements, the reactions can be stopped to obtain the oxygen and nitrogen co-doped PAN-based carbon fibers. If the total quantity of electricity for electrochemical oxidation and/or reduction is less than 1,000 C/g, the active layer will have insufficient active functional groups and low activity. If the total quantity of electricity for electrochemical oxidation and/or reduction is more than 10,000 C/g, the active layer will peel off, be damaged and loss the activity, even resulting in damaged substrate structure.
In the preparation method above, preferably, for the entire cyclic treatment, the total quantity of electricity for electrochemical oxidation is equal to or greater than the total quantity of electricity for electrochemical reduction. The quantity of electricity for electrochemical oxidation in each cycle and the quantity of electricity for electrochemical reduction in each cycle are not limited, and the former may be greater than, equal to, or smaller than the latter. Furthermore, the quantities of electricity for electrochemical oxidation in different cycles may be the same as or different from each other, and the quantities of electricity for electrochemical reduction in different cycles may be the same as or different from each other.
In the preparation method above, preferably, the electrolyte solution is an acidic electrolyte solution, a basic electrolyte solution, a neutral electrolyte solution, or the like.
In the preparation method above, preferably, the acidic electrolyte solution is one or a combination of more of aqueous solutions of oxygen-containing inorganic acids and the like. More preferably, the acidic electrolyte solution is an aqueous solution of sulfuric acid.
In the preparation method above, preferably, the basic electrolyte solution is one or a combination of more of aqueous solutions of an alkali metal hydroxide, an alkali earth metal hydroxide, an oxygen-containing salt of alkali metal, an ammonium salt and the like. More preferably, the basic electrolyte solution is an aqueous solution of ammonium bicarbonate.
In the preparation method above, preferably, the neutral electrolyte solution is one or a combination of more of aqueous solutions of sodium nitrate, potassium nitrate, ammonium nitrate, sodium sulfate, potassium sulfate, ammonium sulfate and the like. More preferably, the neutral electrolyte solution is an aqueous solution of sodium nitrate.
In the preparation method above, as long as the reactions can unimpededly proceed, a person skilled in the art may select and adjust the concentration and use amount of the above electrolyte solution as necessary. In addition, among the acidic electrolyte solution, the basic electrolyte solution and the neutral electrolyte solution described above, most preferred is an aqueous solution of sulfuric acid.
The oxygen and nitrogen co-doped PAN-based carbon fibers provided according to the present invention are prepared by electrochemical modification of raw-material PAN-based carbon fibers and have both oxygen-containing active functional groups and nitrogen-containing active functional groups formed at the edges of carbon basal planes of the fiber surface, such that the fibers have certain pseudocapacitive characteristics and electrocatalytic activity for oxygen reduction reactions and redox couples. Use of the oxygen and nitrogen co-doped PAN-based carbon fibers provided according to the present invention as electrode material can exploit either or both of the pseudocapacitive characteristics and the electrocatalytic activity to improve the activity and performance in use of electrode material, and offers advantages such as good activity, high conductivity, low material cost, stability, and a long lifetime. The method for preparing oxygen and nitrogen co-doped PAN-based carbon fibers by electrochemical modification provided according to the present invention has the advantages such as simple preparation, low production cost, and suitability for industrial production.
The oxygen and nitrogen co-doped PAN-based carbon fibers provided according to the present invention may be used for the manufacture of electrodes for cells utilizing oxygen dissolved in seawater, proton exchange membrane fuel cells, metal-air fuel cells, microbial fuel cells, a supercapacitor, redox flow cells, lead-acid cells, lithium-ion cells, electrochemical treatment of waste water, an electrochemical transducer, as well as for various technical fields of electrochemistry engineering using such electrode material.
a shows the capacitance-electrode potential curve of cyclic voltammetry of electrochemically modified graphite fiber filaments;
b shows the chronoamperometric plot of electrochemically modified graphite fiber filaments;
a shows the cyclic voltammetry curves of the raw-material PAN-based carbon fiber felt according to Example 2;
b shows the cyclic voltammetry curves of the oxygen and nitrogen co-doped PAN-based carbon fiber felt according to Example 2;
a shows the H2O2-production curves of the brush electrode made from the oxygen and nitrogen co-doped PAN-based carbon fiber filaments according to Example 3; and
b shows the current efficiency curves of the brush electrode made from the oxygen and nitrogen co-doped PAN-based carbon fiber filaments according to Example 3.
In order to provide a better understanding of the technical features, objectives and beneficial effects of the present invention, a detailed description of the technical solution of the present invention is provided below, but should not be construed as limiting the scope of embodiments of the present invention.
Further descriptions of the technical solution of the present invention are provided below through examples.
This example provides a kind of oxygen and nitrogen co-doped PAN-based carbon fiber filaments, which were prepared by electrochemical modification of the T700SC 12K PAN-based carbon fiber filaments such that their surface had an active layer formed by oxygen-containing active functional groups and nitrogen-containing active functional groups, wherein the nitrogen-containing active functional groups were obtained after activation of the non-active doped nitrogen inherent in the unmodified raw-material PAN-based carbon fibers by the electrochemical modification.
The method for preparing the oxygen and nitrogen co-doped PAN-based carbon fiber filaments according to this example comprised the steps of:
Following the above preparation method expect for changing the total quantities of electricity supplied for oxidation and reduction, another three kinds of oxygen and nitrogen co-doped PAN-based carbon fiber filaments were correspondingly prepared, wherein the total quantities of electricity supplied for the oxidation/reduction in preparation of the three kinds of oxygen and nitrogen co-doped PAN-based carbon fiber filaments were 3,000 C/3,000 C; 6,000 C/6,000 C; and 10,000 C/0,000 C, respectively.
As a result, in this example totally four kinds of oxygen and nitrogen co-doped PAN-based carbon fiber filaments were prepared.
1 g of the raw-material PAN-based carbon fiber filaments were graphitized at a high temperature of 2,200° C. to 3,000° C. to afford graphite fiber filaments, which were then subjected to electrochemical modification with both the total quantities of electricity supplied for oxidation and reduction being 6,000 C according to the preparation method of this example, to afford electrochemically modified graphite fiber filaments. The electrochemically modified graphite fiber filaments were assayed according to the assay conditions shown in
Table 1 shows the XPS analysis results of the surface elements of the four kinds of oxygen and nitrogen co-doped PAN-based carbon fiber filaments and the raw-material PAN-based carbon fiber filaments provided according to this example. As shown in Table 1, the raw-material PAN-based carbon fiber filaments that were not electrochemically modified had doped nitrogen on the surface, while the oxygen and nitrogen co-doped PAN-based carbon fiber filaments that were electrochemically modified showed a significant increase in surface oxygen content, which was responsible for their pseudocapacitive characteristics, but also showed a little change in nitrogen content. Considering the above electrochemical assay results and the fact that there was no nitrogen-containing compound in the treatment solution, it can be inferred that the non-active doped nitrogen inherent in the raw-material PAN-based carbon fibers were activated by the electrochemical modification and converted into nitrogen-containing active functional groups.
This example provides a kind of oxygen and nitrogen co-doped PAN-based carbon fiber felt, which was prepared by electrochemical modification of PAN-based carbon fiber felt (thickness: 6 mm; mass per geometric area: 0.1 g/cm2) such that its surface had an active layer formed by oxygen-containing active functional groups and nitrogen-containing active functional groups, wherein the nitrogen-containing active functional groups were obtained after activation of the non-active doped nitrogen inherent in the unmodified raw-material PAN-based carbon fibers by the electrochemical modification.
The method for preparing the oxygen and nitrogen co-doped PAN-based carbon fiber felt according to this example comprised the steps of:
a shows the cyclic voltammetry curves of the raw-material PAN-based carbon fiber felt according to this example in an aqueous solution of vanadyl sulfate and sulfuric acid (1 M VOSO4+2 M H2SO4). Curves 1-3 in
This example provides a kind of oxygen and nitrogen co-doped PAN-based carbon fiber filaments, which were prepared by electrochemical modification of the T300 12K PAN-based carbon fiber filaments such that their surface had an active layer formed by oxygen-containing active functional groups and nitrogen-containing active functional groups, wherein the nitrogen-containing active functional groups were obtained after activation of the non-active doped nitrogen inherent in the unmodified raw-material PAN-based carbon fibers by the electrochemical modification. This example further provides a brush electrode made from the oxygen and nitrogen co-doped PAN-based carbon fiber filaments, which can be used for the waste water treatment technology by the Electro-Fenton method.
The method for preparing the oxygen and nitrogen co-doped PAN-based carbon fiber filaments and the brush electrode made thereof according to this example comprised the steps of:
A brush electrode was made from the oxygen and nitrogen co-doped PAN-based carbon fiber filaments and titanium wire having a diameter of 1 mm, wherein the brush body was 180 mm long and had a diameter of 30 mm.
a shows the H2O2-production curves of the brush electrode made from the oxygen and nitrogen co-doped PAN-based carbon fiber filaments according to this example in a 0.4 M solution of Na2SO4 under different currents;
The brush electrode according to this example was used to treat waste water containing 20 mg/L methylene blue by the Electro-Fenton method, in which the initial pH of the waste water was adjusted to 3, the decoloration was 91% upon 5-min electrolysis, and the decoloration was 98% or more after 30 min. This result demonstrates that the electrochemically modified PAN-based carbon fiber filaments and the brush electrode made thereof can serve as the highly efficient cathode material and electrode for the Electro-Fenton method.
This example provides an oxygen and nitrogen co-doped PAN-based carbon-fiber brush, which was prepared by making a brush body from the T300 12K PAN-based carbon fiber filaments and then electrochemically modifying the brush body, such that the surface of carbon fibers in the brush body had an active layer formed by oxygen-containing active functional groups and nitrogen-containing active functional groups, wherein the nitrogen-containing active functional groups were obtained after activation of the non-active doped nitrogen inherent in the unmodified raw-material PAN-based carbon fibers by the electrochemical modification. The oxygen and nitrogen co-doped PAN-based carbon-fiber brush can be used as the positive electrode in seawater cells utilizing the dissolved oxygen.
The method for preparing the oxygen and nitrogen co-doped PAN-based carbon-fiber brush according to this example comprised the steps of:
The effect of the flow rate of natural seawater on the cathodic oxygen reduction reaction was measured with the above oxygen and nitrogen co-doped PAN-based carbon-fiber brush, and the results are shown in Table 2 and Table 3. Table 2 shows the initial reduction potentials of oxygen when using electrochemically unmodified and modified PAN-based carbon-fiber brushes in seawater at different flow rates; and Table 3 shows the cathodic oxygen reduction currents at corresponding polarization potentials when using the electrochemically unmodified and modified PAN-based carbon-fiber brushes in seawater at different flow rates. As shown in Table 2 and Table 3, when compared to the electrochemically unmodified PAN-based carbon-fiber brush, the electrochemically modified PAN-based carbon-fiber brush showed a nearly 300 mV higher initial reduction potential of oxygen, and higher working current under the same cathodic polarization potential. Furthermore, the higher the flow rate, the higher the oxygen reduction current was. These results demonstrate that the oxygen and nitrogen co-doped PAN-based carbon-fiber brush obtained by electrochemical modification showed very high electro-reducing activity for the oxygen dissolved in seawater.
A seawater cell utilizing the oxygen dissolved in seawater can be manufactured by using the oxygen and nitrogen co-doped PAN-based carbon-fiber brush of this example as the positive electrode. This cell was constituted with (i) a central magnesium anode bar as the negative electrode, and (ii) totally 60 oxygen and nitrogen co-doped carbon-fiber brushes arranged in an upper layer and a lower layer around the magnesium bar, as the positive electrode. The positive electrode was fixed to a full-titanium metal frame by welding, the negative electrode was fixed at the center of the frame with a bolt in an insulating jacket, the frame was 360 mm×360 mm×390 mm in size (the volume of the cell was about 50 L), and the initial distance between the positive and negative electrodes was 50 mm. As a result, the cell had a maximal power of 5.4 W, a minimal power of 2 W, and a volumetric specific power of 40 W/m3, demonstrating that the cell had better performance than SWB1200 whose volumetric specific power is 2.7 W/m3. Therefore, since the seawater cell utilizing the oxygen dissolved in seawater employed the oxygen and nitrogen co-doped PAN-based carbon-fiber brush of this example as the positive electrode, the seawater cell had a smaller volume and a higher volumetric specific power than those in the prior art.