Patent Application
20050176588
1. Field of the Invention
The invention is generally related to the field of oxygen sorbent materials.
2. Related Art
Materials having the ability to absorb oxygen are useful in many industries, for example enrichment of oxygen from air or other multicomponent fluid. One useful class of crystalline materials is the so-called mixed ionic-electronic conductors (MIEC). These materials have exhibited enhanced sorption, as well as enhanced ionic and electronic conductivities, particularly their oxide-ion mobility and oxygen-(O2)-storing capacities. High-temperature non-stoichiometric defects (such as oxide-ion vacancies or interstitial oxygen sites) in the crystal-lattice allow the materials to temporarily sorb oxygen at high-temperature for oxygen enrichment of gas streams, as well as for catalytic transformations of other compounds using the oxygen that is temporarily absorbed.
Potential applications of MIEC materials have been documented: production of syngas and H2; partial oxidation of light hydrocarbons; production of pure O2 (with a view toward replacing, possibly, cryogenic distillation); production of O2-enriched gas mixtures; various environment-related solutions; and solid-oxide fuel cells and sensors (cf., for example, P. J. Gellings and H. J. M. Bouwmeester, Solid State Electrochemistry, CRC Press, Boca Raton, 1996; H. Ullmann, Keramische Zeitschrift, 53 (2001) 100-107; S. J. Skinner and J. A. Kilner, materialstoday (March 2003) 30-37. Specifically, Ion-Transport-Membrane (ITM) technologies for O2 separation and syngas production are under quickly progressing development.
Technologies other than ITM, such as cyclic high-temperature sorption-desorption processes based on O2 partial-pressure swings, have gained considerable interest. Cyclic O2-recovery processes that utilize specific ceramic materials, such as K2NiF4 as sorbent/catalyst having high-temperature non-stoichiometric defects are being developed. These processes are referred to as ceramic autothermal recovery processes, or CAR processes, to be discussed further in the Description. They consist of alternately passing air and another medium (or applying vacuum) through pellets or granules of the material in a fixed-bed configuration, with cycle times of the order of minutes or less. Oxygen retained in the solid material during the air contacting step is released by decrease in O2-partial pressure via application of vacuum, steam, carbon dioxide, steam-carbon dioxide mixtures, flue-gas mixtures or other appropriate means, to generate an O2-enriched stream, which is used as feed to other systems, into which CAR could be integrated, e.g., combustion processes.
Key advantages of CAR over ITM processes are ease of material fabrication, plant design and process execution using traditional unit operations. Preliminary estimates indicate significant economic benefits compared to the traditional cryogenic air separation, due to lower energy consumption. On the other hand, cryogenic air separation plants are well understood and, despite their high operating costs, industry momentum is geared toward designing these plants cost-effectively, and this leads to reduced engineering and design costs, and inherent safety built up over time.
One of the key technical issues and risks of the CAR process for O2 enrichment relates to material development. Of the MIEC materials of interest, perovskites and perovskite-like materials have attracted attention in the past. The process-related crystal-structure oxide-ion, O2−, deficiency can be exemplified by perovskite-type oxides, which originally referred to the mineral CaTiO3. Today, “perovskite” denotes a series of oxygen-containing compounds with a unique general crystal structure, ABO3, with high-temperature O2− vacancies, denoted by the symbol δ, which obeys the general formula ABO3-δ. The “A”-site cations can be rare earth, alkaline earth, alkaline and other large cations such as Pb2+, Bi3+, or Ce4+, and the “B”-site cations can be 3d, 4d, or 5d transition-metal cations. Multiple cation-type occupations of those two sites are possible. Framework sites “A” and “B” are dodecahedral and octahedral, respectively, cf., L. G. Tejuca and J. L. Fierro, Properties and Applications of Perovskite-type Oxides, Marcel Dekker, New York, 1993.
A standard cubic high-temperature perovskite phase remains stable and reversible with regard to changes of δ within a certain range: The value δ could be as high as 0.25, but as a rule δ=0.05-0.25 (although higher values have been reported), at elevated temperature and low oxygen partial pressure, i.e., δ is a function of temperature and partial pressure of oxygen. On the other hand, perovskite stability is governed by cation radii of lattice metals in various valence states combined into a parameter “t” called “tolerance factor”, cf., Z. Shao, et al., Sep. Purif. Technol., 25 (2001) 419-42. A perovskite structure can only be formed if t ranges from 0.75-1. These circumstances have set limits to the performance potential of perovskites in O2-recovery and related processes. Tereoka et al. described the material La1-xSrxCo1-yFeyO3-δ as a medium for oxide-ion permeation with excellent performance at high temperature (Y. Tereoka et al., Chemistry Letters, (1985) 1367-1370; 1743-1746). In this case, the O2 permeation is driven by the O2-partial-pressure difference between the two sides of the membrane, and it results from oxygen-ion transport through the vacant sites in the lattice structure. Significant efforts have been directed to the investigation of the fabrication and utilization of these materials as O2-transport membranes for gas separation and reaction. Mazanec, et al., (U.S. Pat. No. 4,933,054) were awarded a patent in this area in 1990. One recent study of SrCo0.4Fe0.6O3-δ reported, however, a decrease in oxygen permeability through samples that were purposely made stronger by addition of up to 9 wt % ZrO2, where the Zr4+ cations replaced some of the B site cations. Yang, et al., Effect of the Size and Amount of ZrO2 Addition on Properties of SrCo0.4Fe0.6O3-δ, AIChE Journal, Vol. 49, Issue 9, pages 2374-2382 (2003).
Desorption of O2 from La1-xSrxCoO3-δ was studied and reported by Nakamura et al. (Chemistry Letters, (1981) 1587-1581) in 1981. Later, Teraoka et al. (Chemistry Letters, (1985) 1367-1370) examined O2 sorption properties of La1-xSrxCo1-yFeyO3-δ. They observed that considerable amount of O2 was desorbed from this class of oxides as temperature was increased from 300° C. to 1100° C., and was absorbed as temperature was decreased. Mizusaki et al. (J. Solid State Chemistry, 80 (1989) 102) measured the oxygen non-stoichiometry of the perovskite-type oxide La1-xSrxCoO3-δ as function of temperature, Sr content (x) and O2-partial pressure. Lankhorst and Bouwmeester (J. Electrochem. Soc., 144 (1997) 1268) measured the oxygen non-stoichiometry of La0.8Sr0.2CoO3-δ. Zeng and Lin (Solid State Ionics, 110 (1998) 209-221) investigated O2-sorption and desorption rates of a La0.2Sr0.8CoO3-δ sample subjected to sudden changes of O2-partial pressure at constant temperatures. They found that this rate could be correlated to a linear-driving force of the deviation of oxygen-vacancy concentration in the bulk phase of the sample from its corresponding thermodynamically equilibrated one.
Few patents have been issued for processes using the O2-sorption properties of perovskite-type oxides for gas separation and purification. Doi et al., KoKai Patent No. Hei 5(1993)-4044, 1993) disclose using a perovskite-type oxide, ABO3-δ, as high-temperature O2 sorbent to remove O2-containing impurities, such as NOx by means of a TSA technique to regenerate the sorbent. A Chinese patent application by Yang, et al., Appl. No. 99 1 13004.9, describes a material, Ba).5Sr0.5Co0.8Fe0.2O3-δ, with very high concentration of oxygen vacancies. The CAR concept, developed by Lin, et al., U.S. Pat. No. 6,059,858, also uses perovskite-type oxides as sorbents to separate O2 from an O2-containing stream, particularly air, by a type of mixed TSA-PSA process. This patent also discloses methods of sorbent regeneration using CO2 or steam as the purge gas.
U.S. Pat. No. 6,143,203 describes CAR technology extended to the area of hydrogen and synthesis-gas production using perovskite-type oxide sorbents. See also U.S. Pat. Nos. 6,379,586 and 6,464,955. A material patent of common assignment hereto has also been applied for: Supported Perovskite-Type Oxides and Methods for Preparation Thereof by Zeng, et al., U.S. Pub. Pat. Appl., U.S. Ser. No. 2002/0179887 A1 (2002).
As mentioned, the ability of perovskite and perovskite-like materials to function as commercial sorbents has limits. There have been recent efforts to improve the O2-sorption performance of these materials, but with limited success. U.S. Pat. No. 6,772,501 discloses composites of metals and ion conductors; U.S. Pat. No. 6,740,441 discloses using perovskites to thin-film coat “current collects” (metal screens or mesh) in solid oxide fuel cells, and other devices, and gas separations are mentioned; U.S. Pat. Nos. 6,641,626 and 6,471,921 disclose MIEC conducting membranes for HC processing, and disclose ceramic membranes which have good ionic and electrical conductivity, plus excellent strength under reactor operating conditions. The compositions comprise a matrix of MIEC (especially brownmillerite) with one or more second crystal phase, non-conductive, which enhances strength; U.S. Pat. No. 6,541,159 discloses O2-separation membranes having an array of interconnecting pores and an OH− ion conductor extending through the pores, and an electrical conductor extending through the pores, discrete from the OH− ion conductor; U.S. Pat. No. 6,440,283 discusses forming pellets, powders, and two layer structures of La/Sr oxides; U.S. Pat. No. 6,146,549 discloses La/Sr ceramic membranes for catalytic membrane reactors with high ionic conduction and low thermal expansion; U.S. Pat. Nos. 5,509,189 and 5,403,461 discuss solid solutions of pyrochlore crystal phase and perovskite crystal structures.
Despite improvements in the art, the need remains for compositions, which take better advantage of the excellent O2-sorption and permeability properties of perovskites and perovskite-like materials, while exhibiting enhanced durability, so that the materials may be used commercially.
In accordance with the present invention, compositions, composites, and methods of use are presented which reduce or overcome many of the problems of previously known materials.
A first aspect of the invention relates to compositions of matter, specifically perovskite-like crystalline ceramic oxide compositions comprising at least one compound within general formulas (1), (2), (3), (4), (5), (6), and (7):
and combinations thereof, wherein:
Compositions of the invention within general formulas (1), (2), and (3) are compositions within the invention, wherein A is a cation of atoms having atomic number ranging from 57-71, inclusive, or cation of yttrium, and B is selected from cations of Ni, Co and Fe atoms.
Compositions within general formula (5) are another set of compositions of the invention, particularly those where Me is a cation of Cu.
Compositions within general formula (6), particularly those wherein A′ is a cation of Na, and B′ is a cation of W are another set of compounds of the invention.
Compositions within general formula (7), particularly those wherein A is Gd, and B is Ti, are another set of compounds of the invention.
Compounds of the invention include compositions within general formula (4), particularly YBa2Cu3O7-δ and doped versions thereof, as discussed more fully in the detailed description.
Compositions of the invention may be formed as structured particles having a particle size ranging from about 0.01 to about 100 microns in largest dimension, or ranging from about 0.1 to about 50 microns.
Compositions of the invention may be supported on, or serve as support for, an “active” matrix selected from porous inorganic materials that are stable at temperatures ranging from about 500 to about 1200° C. In this form the inventive compositions may be referred to as supported crystalline ceramic oxides. “Active”—as that term is used when referring to support or matrix materials—means that even the supporting material acts in the oxygen sorption and transport. Active supports may be compounds within general formulas (1) to (7), inclusive, which form together with binary metal oxides a set of composites of the invention. Compounds within the general formula M′On, referred to as “binary metal oxides”, mean a single metal element that assumes different oxidation states within the oxygen partial pressure range of the CAR process, enabling the metal oxides to release oxygen at different partial pressures of oxygen in CAR processes. In the binary metal oxides, M′On, M′ is a metal of the d block transition metals that changes its oxidation state. Metals may be Cu, Co, Ni, Bi, Pb, V, Mn, and Cr, the oxides of which release oxygen by changing their crystal phase or by their reduction up to the metal. In their pure states, the binary metal oxides do not form stable ceramic shapes because of crystal phase transformations. However, in combination with an active support or matrix oxide (perovskite-like materials within general formulas (1), (2), (3), (4), (5), (6), and (7)), stability of the binary metal oxides can be enhanced, while extending the oxygen sorption/desorption capacities of the perovskite-like compositions. Other suitable active support materials include apatite compositions.
Supported crystalline ceramic oxides of the invention may be shaped, structured articles of manufacture, having shape selected from beads, pellets, saddles, rings, cubes, cylinders, pyramids, extrudates with any cross sectional shapes with or without holes, honey-combs with uniform channels and monoliths with random porosity and foam structure, and the like. The inorganic support may be a porous inorganic support comprising a plurality of pores, as further described herein.
A second aspect of the invention are methods of separating a gas component from a mixture of gases by either of pressure swing adsorption, thermal swing adsorption, or combination thereof, comprising passing a gas mixture through (or past) a composition (or composite) of the invention. Methods of the invention include converting a light hydrocarbon (C5 or less) into hydrogen and carbon monoxide by contacting one or more hydrocarbons with a composition of the invention, including reactions of partial oxidation, steam reforming, auto-thermal reforming, and the like, in either batch, semi-continuous, continuous or cyclic operations. The reactions may be carried out in well-known bed-type reaction vessels, where the bed of particles may be fluidized, semi-fluidized, or non-fluidized.
Thus, the present invention provides for novel materials and methods of use, specifically modified mixed ionic-electronic conductor (MIEC) materials (either alone or as composites with active oxygen exchange support materials) with enhanced performance in sorption, catalytic processes, and the like. The inventive compositions owe their ionic and electronic conductivities, particularly their oxide-ion mobility and O2-storing capacities, to high-temperature non-stoichiometric defects such as oxide-ion vacancies—or interstitial oxygen sites—in the crystal-lattice structure of the solids, and also on changed valency states of a selected series of transition metals, which lead to different oxides of one and the same metal. These materials will have strong potential for high-temperature processes that utilize the O2-storing/releasing properties for purposes of the enrichment of O2 in gas streams but also for multi-fold catalytic transformations of other compounds. The inventive compositions may also be formed into chemically and mechanically robust ceramic composites such as sorbent and membrane materials with high O2 capacities (in the case of absorbents) and high O2 permeation fluxes (in the case of membranes). This enables the design of high-performance structured ceramics of regular or random shapes, allowing for high performance in O2 enrichment and, at the same time, the ability to withstand the expected operating conditions in large scale plants, and be cost-effective in addition. The inventive compositions and composites may be utilized advantageously for high-temperature CAR-type PVSA and TSA processes (and also for other related applications) to produce substantially pure O2, syngas and H2 (at small and large scale), as well as O2 and fuel in integrated process schemes, for example, so-called oxy-fuel processes, power plants, gas turbines, and many other processes.
Further aspects and advantages of the invention will become apparent by reviewing the detailed description of the invention that follows.
Novel materials that reversibly deliver O2 in CAR processes and other methods of use are now described in further detail. Primary attention is paid to new compositions of oxides that act reversibly with high exchange rate and high capacity for O2 over an O2-partial pressure region between 5 and 0.01 atmosphere. Beside these parameters, their chemical and long-time mechanical stability under the conditions of commercial processes, with maintenance of both the desired crystal structure and secondary ceramic shape, specifically by considering chemical reaction with gases and thermal expansion coefficients as important material-specific parameters, are accounted for.
Compositions of the invention may generally be categorized as “perovskite-like” compounds within the general formulas:
where framework sites “A” are dodecahedral and “B” are octahedral. As used herein, the term “perovskite-like” means a composition that is strictly not a perovskite in crystal structure of the ABO3-δ type, but under the temperatures at which the materials are intended to be used, they form a standard cubic high-temperature perovskite phase. As mentioned in the background section, a standard cubic high-temperature (about 500-1200° C.) perovskite phase remains stable and reversible with regard to changes of δ within δ=0.05-0.25 at elevated temperature and low oxygen partial pressure. On the other hand, perovskite stability is governed by cation radii of lattice metals in various valence states combined into a parameter “t” called “tolerance factor”, and a perovskite structure can only be formed if t ranges from 0.75-1. These circumstances have set limits to the performance potential of perovskite-like materials in O2-recovery and related processes. Attempts to extend the limits of useful perovskites have failed, at least as far as oxygen permeability is concerned. For example, when a perovskite material was purposely made stronger by addition of ZrO2, where the Zr4+ cations replaced some of the B site cations, the material was stronger, the oxygen permeability decreased. Yang, et al., Effect of the Size and Amount of ZrO2 Addition on Properties of SrCo0.4Fe0.6O3-δ, AIChE Journal, Vol. 49, Issue 9, pages 2374-2382 (2003).
Perovskite-like Crystalline Ceramic Oxides
The inventors herein have discovered that compositions of the invention overcome some or all the limitations of previous compositions in enhancing oxygen permeability and oxygen trapping ability. Compositions of the invention are perovskite-like crystalline ceramic oxide compositions comprising one or more compounds within the general formulas:
and combinations thereof, wherein:
As may be seen from the above general description of perovskite-like crystalline ceramic oxide compositions of the invention, the key to the effectiveness of the compositions of the invention lies in the ability of the these compositions to form the perovskite cubic phase at high temperatures. Selection of the B site cations, such as cations of d-block transition metals Fe, Co, Ni, Cu, Cr and Mn, which have the ability to be present in more than one oxidation state in the crystal lattice at high temperatures allows the compositions of the invention to be particularly useful in temporarily absorbing oxygen, especially in certain unexpected combinations of cations. It is also theorized that the ionic radii of the selected cations in their various oxidation states, and the fluctuation between these states and radii, perhaps help in the generation of oxide ion vacancies in the crystal lattice. The valency states of the various transition metals deemed useful in the compositions of the invention, and the ionic radii of the most stable ion, are presented in Table 1, in accordance with R. D. Shannon, Acta Cryst., A32 (1976) 751-767. The ionic and electronic conductivities of these compositions, particularly their oxide-ion mobility, and oxygen-(O2)-storing capacities that are based on high-temperature non-stoichiometric defects such as oxide ion vacancies, or interstitial oxygen sites, in the crystal-lattice structures of these solids, makes compositions of the invention particularly useful in oxygen separation.
*Most stable cation
Some specific crystalline ceramic oxides of the invention include those in Table 2.
One group of compounds of the invention include compositions within general formula (4), particularly YBa2Cu3O7-δ and doped versions thereof, such as Y1-xLaxBa2-ySryCu3O7-δ and Y1-xLaxBa2-yCayCu3O7-δ, wherein x ranges from 0 to about 1, and y ranges from about 0.5 to about 1.5. The inventive materials within general formula (4) comprise a selection of 1,2,3-type superconductor compounds. They are specifically Rare Earth (RE)-1,2,3-type superconductors, e.g., (RE)M2Cu3O7-δ, with a molar ratio RE—M—Cu=1:2:3, specifically, YBa2Cu3O7-δ, with Y—Ba—Cu=1:2:3, wherein partial substitution by appropriate dopants may be of their basic metal components RE and barium, Ba, is envisioned, in addition. For the purpose of this invention, they do not need to show any superconductivity properties. One group of dopants for the purposes of the invention include lanthanide metal dopants such as lanthanum, La, praseodymium, Pr, gadolinium, Gd, and holmium, Ho.
The structure of the 1,2,3-type superconductor-type materials contains in particular perovskite-like structural units as mentioned above. Therein are systematic oxygen-atom vacancies in the unit cell compared to a stack of simple perovskite unit cells. These vacancies occur between adjacent copper atoms in the CuO3 chains along the crystallographic c axis. The vacancies are in the RE, specifically yttrium-atom plane. There are also additional vacancies between Cu atoms along the crystallographic a axis in the Cu-and-O planes that lie between the planes of Ba atoms. The stoichiometry seems to be odd, viz., (RE)M2Cu3O7-δ, which results from additional oxygen vacancies (defect structure), at certain sites such that it holds 0.0<δ<0.4. For YBa2Cu3O7-δ, usually δ=0.19, within the temperature region of superconductivity, i.e., (100±20)K. It is well known, however, that δ is a function of temperature. The defect structure gets increasingly pronounced with temperature, and since utilization of the materials of this invention would take place at high temperature, the assessed utilization is based on the reasonable assumption of 0.2<δ<0.4. Additionally, the parameter δ is assumed to depend on O2 partial pressure as well.
For the specific purpose of this invention, the inventive materials within the general formula (RE)M2Cu3O7-δ, have been shown in testing to have O2 “working” sorption capacities larger by factors ranging from about 3 to about 10 times higher for CAR, compared to the currently known materials, at given constant O2 pressure ratios. The following related properties of a (RE)M2Cu3O7-δ, viz., YBa2Cu3O7-δ, have been assessed:
Doping the specific material YBa2Cu3O7-δ with other cations of the types RE and M, for example, those of lanthanum and calcium, strontium, respectively, increases significantly the chemical stability of it but also the mechanical strengths of the resulting specimens. The latter purpose could also be achieved by incorporating titanium cation.
When more than one crystalline ceramic oxide is present in a composition of the invention, the differing crystalline ceramic oxides may be present in a variety of formats, including, but not limited to, solid solutions, layered compositions, randomly mixed compositions, and the like. For example, the two or more crystalline ceramic oxides may be present as intergrown layers, or as discrete layers. As examples of these: La2CoO4-δ in alternating or intergrown layers with Gd2Ti2O7-δ; YBa2Cu3O7-δ in alternating or intergrown layers with NaWO3; YBa2Cu3O7-δ in alternating or intergrown layers with Gd2Ti2O7-δ. Multiple layers are possible, with alternating layers of two or more of the inventive crystalline ceramic oxides. These compositions of the invention may be comprised of alternating layers of crystalline ceramic oxides of the invention. Such arrangements allow for (i) buffering thermal-mechanical properties, (ii) increasing the surface-reaction rate by enhancing the accessible surface and the influence of grain-boundary region effects, and (iii) synergistic effects for increasing the “working capacity” of the materials.
The meaning of the process parameter “working capacity” follows from
Crystalline ceramic oxide compositions of the invention may be formed as particles having a particle size ranging from about 0.01 to about 100 microns in largest diameter, or ranging from about 0.1 to about 50 microns. When a binary metal oxide is present with a perovskite-type compound of the invention, the binary metal oxide may overlay the perovskite-type compound, and the binary metal oxide has a crystallite size ranging from about 0.1 to about 0.5 microns. The particles may be shaped articles of manufacture, having shape selected from beads, pellets, saddles, rings, pyramids, cubes, cylinders, extrudates with any cross sectional shapes with or without holes, honey-combs with uniform channels and monoliths with random porosity and foam structure, and the like.
Crystalline ceramic oxide compositions of the invention may be made and characterized using standard ceramic processing steps and equipment. For example, to make Gd2Ti2O7-δ, one might start with technical grade samples of each rare earth oxide and metal oxide required. Stoichiometric amounts, according to the desired end composition, are well mixed using an agate and pestle. The mixture would then be fired at a high temperature, usually about 1000° C. The as prepared powder is then pressed into the desired shapes under pressure, and then sintered to make the dense material. If a layered structure is desired, such as a binary metal oxide layer overlaying a perovskite matrix, these steps would be repeated with stoichiometric amounts of the desired binary metal oxide being mixed with the crystalline ceramic oxide from the first procedure. The structure of the powder and the final shaped articles may be studied using XRD employing a diffractometer such as that known under the trade designation D/Max-RB, available from Rigaku. Oxygen temperature-programmed desorption equipment is readily available. A heating rate of 10° C./min is typical. Oxygen permeation of membrane materials may be studied using known gas chromatography (GC) techniques. For example, a disk of the sintered material may be sealed in the end of an alumina tube, one side of the disk exposed to air, the other exposed to flowing helium. The outlet gas (He+O2) is connected to the GC, for example a GC available from Hewlett-Packard known under the trade designation HP5890A. The GC is calibrated frequently using standard gases. The O2 permeation flux (JO2) may be calculated from known equations, such as the following:
JO2=S/S°×P°×F/Sm,
where S is the oxygen area of the outlet gas, S° the oxygen area of the standard gas, P° the percentage of O2 in the standard gas, F the outlet gas flow rate and Sm the effective inner surface area of the membrane material.
Composite Compositions
The crystalline ceramic oxides of the invention may be supported on, or function as a support for, an “active” support selected from porous inorganic materials that are stable at temperatures ranging from about 500 to about 1000° C. In this form the inventive compositions may be referred to as supported crystalline ceramic oxides, or simply composite compositions, and these materials are particularly well-suited for high-temperature CAR-type processes for O2 enrichment. Recall that primary compositional changes/doping of basic perovskite-type materials to improve their properties with regard to oxygen exchange have reached their limits. As used herein, the term “composite” means mechanical combinations on a macro scale of two or more solid materials, one of which is a crystalline ceramic oxide of the invention, resulting in compositions with specific goal-oriented macroscopic properties. The phenomenon of building up/using composites allows for significant unexpected (i) additional O2-exchange capacity; (ii) improved thermo-chemical properties; (iii) appropriate changes in surface-reaction rates; and (iv) improved ceramic-material processing.
Examples of composite compositions of the invention include compositions where the “core” O2-exchange material and the matrix (support) material are both active with regard to O2-exchange. For example, composites of this invention include one or more crystalline ceramic oxides of the invention (discussed supra) combined with an oxygen-exchange active matrix, which may be an oxide such as another perovskite that is slightly active, but contributes desirable mechanical and thermal properties to the composite. Composites of the invention optionally include a stabilizing component. It is anticipated that for most composites of the invention an appropriate binder will have to be utilized.
The stabilizing component functions to maintain the ability of the composition to undergo repeated cyclic changes in its crystal structure as temperature, pressure, or both are cycled. Suitable stabilizers are rare earth (lanthanides series) elements and their oxides, such as erbium and erbium oxide.
Binders function to maintain the intended physical shape of the composites of the invention under the constraints of the conditions of use. These constraints include chemical, electrical, and mechanical, and suitable binders are materials that substantially match the chemical, electrical, mechanical, and thermo-mechanical properties of the crystalline ceramic oxides and active support materials. In particular for non-membrane CAR extrudates to be used under pressure-swing conditions, the binder should allow composites of the invention to achieve a crush strength of at least about 3 kg/cm2, or at least about 5 kg/cm2, as tested by specific techniques and criteria the particular features of which depend greatly on both the shape and geometry of the particles investigated. Specifically, “buffering” of the thermal-expansion coefficient at O− deficiency conditions (for crystals) allows for maximum Δδ to be utilized by substantially reducing or eliminating the thermo-mechanical-stress gradient across the CAR-type macroscopic particle. The mechanical strength of composites of the invention under operating conditions may be improved, for example, by choosing appropriate supports, inert fillers, fibers and the like. Suitable binders may or may not be chemically active, and include metal oxides that do not undergo significant change in oxidation state, examples of which include the various aluminas, silicas, titanias and zirconia. These materials are well known in the ceramics art.
Active supports for the binary metal oxides, in particular binary metal oxides of d-block transition metals and mixtures thereof, may be perovskite-like compounds within general formulas (1), (2), (3), (4), (5), (6), and (7). The active support may have a particle size (largest dimension) ranging from about 1 to about 10,000 microns, or ranging from about 10 to about 1,000 microns. Supported crystalline ceramic oxides of the invention may be shaped articles of manufacture, having shape selected from beads, rings, pyramids, extrudates with any cross sectional shapes with or without holes, honey-comb with uniform channels and monolith with random porosity and foam structure, and the like.
As with the embodiments of crystalline ceramic oxides of the invention having two or more crystalline ceramic oxide present, composites of the invention may be comprised of alternating and densely packed thin layers of oxygen-exchange active materials. Such arrangements provide for an opportunity to (i) buffer thermal-mechanical properties, (ii) increase the surface-reaction rate by enhancing the accessible surface, and also the influence of grain-boundary region effects, (iii) provide for synergistic effects for increasing the working capacity of the material. For purposes of enhanced rate processes, the compositions of the invention enhance the macroscopic properties that are dependent on reaction rates that are in turn dependent on macro-kinetic properties.
Intimately arranged physical mixtures of crystallographically incompatible structures also have utility as dual-compounded composite materials of the invention. For example, one or more crystalline ceramic oxides of the invention may be physically dry mixed with an active matrix material of the type mentioned herein with a suitable binder material.
Specific macroscopic size and system properties of compositions of the invention of physical/physico-chemical nature that have an unexpected strong (positive) influence on enhanced O2-exchange capacity, including improved thermo-chemical properties and accelerated surface-reaction rate are as follows:
Two component composites of the invention may vary greatly in terms of ratio of composition of the two components (ratio of mass or volume of core oxygen exchange material to mass or volume of matrix or support material). This ratio may vary from about 1:100 to about 1:20. The particle size for any particular composite of the invention may vary over a large particle size distribution or a narrow particle size distribution, expressed in terms of Gaussian distribution curves.
Composites of the invention may be prepared by means known to those of skill in the ceramics art. They may be prepared by dispersing the crystalline ceramic oxides of the invention onto an active support with or without the aid of a liquid solvent, and treating the mixture of ceramic oxide and support at a temperature ranging from about 600 to about 1,500° C. The active inorganic support may be a porous inorganic material comprising a plurality of pores. The porous structure may be formed from a “green” composition comprising additives useful in forming pores in the porous inorganic material and useful to control pore structure of the pores, such as water, organic solvents, celluloses, polymers, synthetic and naturally formed fibers, starches, metal oxides, and the like, and combinations thereof. Additives may be selected from water, cellulose, about 0.1 to 1 wt % MgO and about 0.1 to 0.5 wt % TiO2. Pore sizes may range from about 0.001 to 10 microns, or ranging from 0.01 to 1 micron, and specific surface area may range from about 1 to 200 m2/g, or ranging from 1 to 50 m2/g.
Methods of Use
A second aspect of the invention are methods of separating a gas component from a mixture of gases by either of pressure swing adsorption, thermal swing adsorption, or combination thereof comprising passing a gas mixture through or past a composition or composite of the invention. Methods of the invention include those wherein the sorbed oxygen may then be used in situ for reacting with another compound while still sorbed, or desorbed and subsequently reacted, or combination of these (for example the oxygen may be desorbed from the compositions of the invention contained in a vessel and subsequently reacted, in the same vessel, with a compound to be oxidized). If used in thin membrane form, the compositions of the invention may serve as mixed ion and electron conductors, where O2 atoms contacting one side of the membrane accept 2 electrons conducted through the membrane to form O2− ions, while a hydrocarbon flows past the other side of the membrane and reacts with O2− ions conducted through the membrane to form CO, H2 and release 2 electrons. Reactions using the oxygen so sorbed or recovered, such as partial hydrocarbon oxidation, hydrocarbon steam reforming, hydrocarbon auto-thermal reforming, and the like, in either batch, semi-continuous, continuous or cyclic operations, are considered within the invention. Aside from the use of the compositions of the invention in these methods, the methods are themselves known to skilled artisans. For example, the method descriptions in U.S. Pat. Nos. 6,143,203; 6,379,586 and 6,464,955, and U.S. Pub. Pat. Appl. No. 2002/0179887 A1 are incorporated herein by reference.
Methods of the invention include converting a light hydrocarbon (C5 or less) into hydrogen and carbon monoxide by contacting one or more hydrocarbons with a particulate composition (or composite) of the invention, carried out in well-known bed-type reaction vessels, where the bed of particles may be fluidized, semi-fluidized, or non-fluidized. Alternatively, membrane configurations may be employed, as discussed above. Partial hydrocarbon oxidation reactions are advantageous in that they are exothermic, and typically carried out at temperatures ranging from about 600 to about 1200° C. In these temperature regimes, the compositions and composites of the invention are well-suited, since the high temperature perovskite cubic structure predominates.
CAR is a Ceramic Auto-thermal Recovery process executed cyclically on conventionally shaped perovskites or related solids in a fixed-bed sorption-type arrangement at high temperature; as a rule at T>700° C. One scheme, illustrated in
Oxygen sorption-desorption characteristics such as exchange-capacity data was measured by means of a home-built technique that utilized a Lambda sensor for oxygen detection and analysis. The Lambda sensor used was of type LSU 4.2 of the Bosch Company (Germany) with a voltage chosen at 0.6 V. At this voltage, the current does not depend on voltage. Calibration took place with mixtures of dry air and argon to arrive at oxygen concentrations between 1 vol. % and 21 vol. % (air). This resulted in a linear dependence between oxygen concentration in the gas and the current that passes the sensor. The gas flow could be switched between air (oxygen sorption uptake) and argon (with about 10 ppm oxygen trace content) (oxygen desorption/release). The temperature was kept at 800° C., in all experiments. Gas flow rates were established/measured at 6 l/hr for both air and argon.
Results of these experiments are shown in
These results offer several options to enhance CAR-process performance efficiency: (1) reducing sorbent mass and absorber sizes by about factor 3 if keeping constant all the other process parameters; (2) maximizing the cycling frequency of CAR processes towards their kinetic limits; (3) maximizing yield and specific product of overall processes, 4) minimizing the process temperatures.
After a start-up period, enrichment leads to nearly constant oxygen levels in the product stream amounting to about 60 to 70% oxygen (with nitrogen and water as residuals), which are almost independent of both the type of secondary particle shape and process temperature.
A combination of results of Examples 2 and 3 enables to predict a significant increase in oxygen content in product streams based on air as feed gas for the CAR process. This holds for process versions with any type of oxygen partial pressure decrease in order to release oxygen from the bed: either by applying vacuum or purge by either steam or carbon dioxide or by their mixtures, or by other inert gases. In each of those cases, it becomes possible to enable an up-to-three-fold increase in oxygen percentage in the product gas stream. This means that resulting oxygen-enriched gas products would essentially be composed of oxygen only, with traces of nitrogen still retained in the bed and of the purge gas used.
Although the foregoing description is intended to be representative of the invention, it is not intended to in any way limit the scope of the appended claims.
This application claims priority from U.S. provisional application No. 60/531,780, filed Dec. 22, 2003, which is incorporated herein by reference in its entirety.
| Number | Date | Country | |
|---|---|---|---|
| 60531780 | Dec 2003 | US |