Patent Application
20200115126
The present invention relates to a packaging bag.
Three-sided seal bags or four-sided seal bags are well known. The three-sided seal bags are formed by folding one laminated rectangular film in half and sealing the overlapped edges with each other to provide a container part. The four-sided seal bags are formed by overlapping a pair of laminated rectangular films with each other and sealing (heat-sealing) the edges to provide a container part.
PTL 1 discloses a rectangular packaging bag (four-sided seal bag) in which score lines (opening lines) where strength is reduced are formed on the front and back laminated films. The score lines are formed such as by half-cutting so as to respectively extend parallel to two adjacent edges among the four edges. This packaging bag can package sheet-shaped contents, such as a medical tape or a patch, for transdermal administration of medication.
The user of this packaging bag firstly breaks the laminated films from a start notch formed at an edge of the packaging bag along a score line until the break reaches the opposite end. Then, the user of the packaging bag breaks the laminated films from a start notch formed at another edge of the packaging bag along another score line until the break reaches the opposite end. As a result, an opening is formed in the packaging bag, being defined by the break lines which are formed along the two score lines. Since a large opening is provided, the user of the packaging bag can easily remove the contents from the opening.
[Citation List] [Patent Literature] PTL 1: WO 2015/105101-A1
Such packaging bags are used for various purposes. However, no sufficient studies have been made for suitably usable shapes of the score lines.
The present invention has been made in light of such an issue and aims to provide a packaging bag which is provided with a score line that can be suitably used.
To solve the issue set forth above, an aspect of the present invention is a packaging bag having a rectangular shape formed by overlapping film sheets and sealing at least three edges thereof to form a container part. In the packaging bag, a score line, in which the strength of the films is reduced, is formed on the container part away from the seal part in plan view.
The present invention can provide a packaging bag that can be suitably used with provision of a score line.
With reference to the accompanying Figures, a description will now be given of representative embodiments according to the present invention. The present invention is not limited to the following representative embodiments, and appropriate modifications can be made without departing from the spirit of the present invention. The representative embodiments described below are merely examples of the present invention, and the design thereof could be appropriately changed by one skilled in the art. Here, the drawings are schematic, and the relationship between thickness and plane size, the ratio of the thickness of each layer, etc., may be different from actual ones. The embodiments described below are merely examples of the configurations for embodying the technical idea of the present invention, and the technical idea of the present invention should not limit the materials, shapes, structures, and the like of the components to those described below. The technical idea of the present invention can be modified in various ways within the technical scope specified by the claims.
The same constituent elements are denoted by the same reference numerals unless there is a reason for the sake of convenience, and redundant description is omitted. In the drawings referred to in the following description, for clarity, characteristic parts are enlarged, and thus the components are not shown to scale. It is, however, clear that one or more embodiments can be implemented without such details. In addition, known structures and devices may be schematically represented for simplicity.
In the following description, the edge in which the first notch 51 is formed is referred to as a first edge 71, the edge which faces the first edge 71 is referred to as a second edge 72, and, of the edges adjacent to the first edge 71, the edge near the first notch 51 is referred to as a third edge 73, and the edge which faces the third edge 73 is referred to as a fourth edge 74.
(Films)
The films 10 each have a rectangular shape. By sealing the edges 71 to 74 of the films 10, a packaging bag 100 having a container part 30 can be provided. As the films 10, multilayer films may be suitably used. To seal the edges 71 to 74 of the films such as by heat sealing, the multilayer films may each include two or more layers including a sealant layer as an innermost layer. For example, materials that can be used for the layer of each film 10 include polyethylene terephthalate (PET), aluminum (AL), cellophane, polyethylene (PE), transparent deposition PET, and low adsorption sealant (PET having heat-sealing properties, cyclic polyolefin, EVOH sealant or the like). In the case of a multilayer film, these materials may be combined as appropriate.
(Notches)
The first and second notches 51 and 52 are formed in the edges 71 to 74 of the packaging bag 100. When opening the container part 30, the user of the packaging bag 100 can break the films 10 using the first and second notches 51 and 52 as start points. As shown in FIG. 1, the packaging bag 100 includes the first notch 51 formed in the first edge 71, and the second notch 52 formed in the fourth edge 74. The first and second notches 51 and 52 are formed by cutting the seal part 20 in a line over a predetermined length toward corresponding ones of the facing edges 71 to 74. As long as the first and second notches 51 and 52 can serve as start points for breaking the films 10, the shape of them is not limited to a linear shape but may be a triangular or pentagonal shape, or other shapes.
(Score Lines)
The first and second score lines 41 and 42 are portions in which the strength of the films 10 is reduced in a line. The first score line 41 can guide the break line starting from the first notch 51 to the vicinity of the seal part 20 where there is the second edge 72 facing the first edge 71. The second score line 42 can guide the break line started from the second notch 52 to the vicinity of the seal part 20 where there is the third edge 73 facing the fourth edge 74.
In the packaging bag 100, the first and second score lines 41 and 42 are formed on both of the two films 10 so that those in one film 10 respectively align with those in the other film 10 in plan view when the films 10 are formed into the packaging bag 100. However, the first and second score lines 41 and 42 may be formed on either one of the two films 10.
As shown in
The first and second score lines 41 and 42 can be obtained by forming intermittent linear cuts (half-cuts) in each film 10. When the film 10 is a laminated film, the first and second score lines 41 and 42 may be formed by forming cuts only through the outermost layer of the laminated film. A known method, such as a method using a Thomson blade or a razor blade, or a method using a carbon dioxide laser, may be used for forming the first and second score lines 41 and 42.
(Modifications)
The first and second score lines 41 and 42 may be curves instead of straight lines.
As long as the first and second score lines 41 and 42 can reduce the strength of the films 10 in a line, the shape of them is not limited to perforations which are structured by intermittent cuts.
The packaging bag 100 is a four-sided seal bag. However, as long as the packaging bag is a rectangular packaging bag having a container part that is formed by sealing at least three edges, the packaging bag is not limited to a four-sided seal bag. For example, the packaging bag may be a three-sided seal bag formed by folding one laminated rectangular film in half and sealing the overlapped edges with each other. Alternatively, the packaging bag may be a four-sided seal bag formed by folding one laminated rectangular film in half to provide four edges.
In the packaging bag 100, one first score line 41 and one second score line 42 are formed. However, either one of them may be formed.
(Score Lines)
The first and second score lines 41 and 42 are portions in which the strength of the films 10 is reduced in a line. The first score line 41 can prevent the break line from reaching the third edge 73 which is an edge near the first notch 51 among the edges adjacent to the first edge 71. The second score line 42 can prevent the break line from reaching the second edge 72 which is an edge near the second notch 52 among the edges adjacent to the fourth edge 74.
In the packaging bag 200, the first and second score lines 41 and 42 are formed on both of the two films 10 so that those in one film 10 respectively align with those in the other film 10 in plan view when the films 10 are formed into the packaging bag 200. However, the first and second score lines 41 and 42 may be formed on either one of the two films 10.
As shown in
The second score line 42 is formed so as to pass through an area sandwiched between a phantom second straight line 62 and the second edge 72. The second phantom straight line 62 extends from the second notch 52 to the third edge 73 in a direction perpendicular to the third edge 73. More specifically, the second score line 42 is structured by a first curve and a second curve. The first curve extends from the vicinity of the fourth edge 74 toward the third edge 73 so as to approach the second edge 72 and intersects the phantom second straight line 62 extending from the second notch 52 to the third edge 73 in a direction perpendicular to the third edge 73. The second curve extends from a third edge 73 end of the first curve toward the third edge 73 so as to be substantially parallel to the second edge 72.
The first and second score lines 41 and 42 can be obtained by forming intermittent linear cuts (half-cuts) in each film 10. When the film 10 is a laminated film, the first and second score lines 41 and 42 may be formed by forming cuts only through the outermost layer of the laminated film. A known method, such as a method using a Thomson blade or a razor blade, or a method using a carbon dioxide laser, may be used for forming the first and second score lines 41 and 42.
(Functions of the Score Lines)
When the first and second score lines 41 and 42 of the packaging bag 200 are formed so as to have portions respectively intersecting the first and second straight lines 61 and 62, the break line that has been started from the first notch 51 or the second notch 52, even when the direction of the break line is not parallel to the first straight line 61 or the second straight line 62, can smoothly reach the first score line 41 or the second score line 42.
The break line that has reached the first score line 41 or the second score line 42 advances along the first score line 41 or the second score line 42. The first score line 41 is formed extending toward the second edge 72. The second score line 42 is formed extending toward the third edge 73. Therefore, the break line that has reached the first score line 41 or the second score line 42 can advance to the vicinity of the second edge 72 or the third edge 73 along the first score line 41 or the second score line 42.
As described above, due to provision of the first score line 41, the packaging bag 200 can prevent the break line started from the first notch 51 from reaching the third edge 73 or the fourth edge 74 and can guide the break line to the vicinity of the second edge 72. Similarly, due to provision of the second score line 42, the packaging bag 200 can prevent the break line started from the second notch 52 from reaching the first edge 71 or the second edge 72 and can guide the break line to the vicinity of the third edge 73. Thus, the packaging bag 200 can minimize possible failure in opening which would otherwise occur due to the break line not reaching the edge which faces the first notch 51 or the second notch 52, while minimizing the occurrence of microcracks in the films 10. Furthermore, due to provision of the first and second score lines 41 and 42 for the first and second notches 51 and 52 respectively, openability in two directions can be improved.
The first and second score lines 41 and 42 of the packaging bag 200 are formed so as to respectively intersect the first and second straight lines 61 and 62. Thus, the first notch 51 and second notch 52 each have an allowable angular range in terms of the direction of forming the break line as viewed from the first notch 51. Accordingly, the ranges of forming the first and second notches 51 and 52 can be imparted with margins in the respective first and fourth edges 71 and 74. Therefore, compared to the conventional art in which notches have been formed so as to abut with the ends of the respective score lines, accuracy in the position of forming the notches can be alleviated.
(Modifications)
The first and second score lines 41 and 42 may be straight lines instead of moderate curves.
As long as the first and second score lines 41 and 42 can reduce the strength of the films 10 in a line, the shape of them is not limited to perforations which are structured by intermittent cuts.
In the packaging bag 200, one first score line 41 and one second score line 42 are formed. However, either one of them may be formed.
(Score Lines)
The first and second score lines 41 and 42 are portions in which the strength of the films 10 is reduced in a line. The first score line 41 can prevent the break line from reaching the third edge 73 which is an edge near the first notch 51 among the edges adjacent to the first edge 71. The second score line 42 can prevent the break line from reaching the second edge 72 which is an edge near the second notch 52 among the edges adjacent to the fourth edge 74.
In the packaging bag 300, the first and second score lines 41 and 42 are formed on both of the two films 10 so that those in one film 10 respectively align with those in the other film 10 in plan view when the films 10 are formed into the packaging bag 300. However, the first and second score lines 41 and 42 may be formed on either one of the two films 10.
As shown in
The second score line 42 is formed so as to pass through an area sandwiched between a phantom second straight line 62 and the second edge 72. The second phantom straight line 62 extends from the second notch 52 to the third edge 73 in a direction perpendicular to the fourth edge 74.
(Auxiliary Score Lines)
Similar to the first and second score lines 41 and 42, the first and second auxiliary score lines 81 and 82 are portions in which the strength of the films 10 is reduced in a line. The first and second auxiliary score lines 81 and 82 can prevent the break line started from the first notch 51 from reaching the fourth edge 74 and can prevent the break line started from the second notch 52 from reaching the first edge 71.
As shown in
The second auxiliary score line 82 is formed along a straight line intersecting the second straight line 62 and extending from a first edge 71 side position relative to the second notch 52 of the fourth edge 74 and connected to the second score line 42.
The first and second score lines 41 and 42, and the first and second auxiliary score lines 81 and 82 can be obtained by forming intermittent linear cuts (half-cuts) in each film 10. When the film 10 is a laminated film, the first and second score lines 41 and 42, and the first and second auxiliary score lines 81 and 82 may be formed by forming cuts only through the outermost layer of the laminated film. A known method, such as a method using a Thomson blade or a razor blade, or a method using a carbon dioxide laser, may be used for forming the first and second score lines 41 and 42, and the first and second auxiliary score lines 81 and 82.
(Functions of the score lines)
Thus, provision of the first and second score lines 41 and 42 to the packaging bag 100 enables the break line that is started from the first notch 51 or the second notch 52 to reach the first score line 41 or the second score line 42 if the break line is directed to the third edge 73 or the second edge 72 instead of being directed to the facing edge. Furthermore, provision of the first and second auxiliary score lines 1 and 2 can prevent the break line started from the first notch 51 from reaching the fourth edge 74, and can prevent the break line started from the second notch 52 from reaching the first edge 71.
The break line that has reached the first score line 41 or the second score line 42 advances along the first score line 41 or the second score line 42. The first score line 41 is formed extending from the vicinity of the first edge 71 toward the second edge 72. The second score line 42 is formed extending from the vicinity of the fourth edge 74 toward the third edge 73. Therefore, the break line that has reached the first score line 41 or the second score line 42 can advance to the second edge 72 or the third edge 73, which faces the edge where the first notch 51 or the second notch 52 is formed, along the first score line 41 or the second score line 42.
As described above, due to provision of the first score line 41, the packaging bag 300 can prevent the break line started from the first notch 51 from reaching the third edge 73 and can guide the break line so as to reach the second edge 72. Similarly, due to provision of the second score line 42, the packaging bag 300 can prevent the break line started from the second notch 52 from reaching the second edge 72 and can guide the break line so as to reach the third edge 73. Thus, the packaging bag 300 can minimize failure in opening which would otherwise occur due to the break line not reaching the edge which faces the first notch 51 or the second notch, while minimizing the occurrence of microcracks in the films 10. Furthermore, due to provision of the first and second score lines 41 and 42 for the first and second notches 51 and 52 respectively, openability in two directions can be improved. In other words, the packaging bag 300 can also achieve advantageous effects similar to those of the packaging bags 100 and 200.
Since the first and second score lines 41 and 42 are formed so as to be respectively away from the first and second straight lines 61 and 62 by 1 mm or more, the break line is prevented from passing across the first score line 41 or the second score line 42 caused by momentum when breaking of the films 10 is started from the first notch 51 or the second notch 52 as a start point.
(Modifications)
The first and second score lines 41 and 42 may be curves instead of straight lines.
As long as the first and second score lines 41 and 42 can reduce the strength of the films 10 in a line, the shape of them is not limited to perforations which are structured by intermittent cuts.
In the packaging bag 300, one first score line 41 and one second score line 42 are formed. However, either one of them may be formed. The first and second auxiliary score lines 81 and 82 are not necessarily required.
The above description has dealt with packaging bags which are capable of preventing or reducing loss of barrier properties due to possible occurrence of microcracks. However, as shown in
Packaging bags for examples and comparative examples were prepared and the occurrence of microcracks in the aluminum layer of each packaging bag was examined. The packaging bags of the examples were each prepared by changing the position (distance La) and the shape of the score lines of the packaging bag 100 shown in
For each of the examples and the comparative examples, packaging bags respectively using the films having the following layer structures from the outermost layer to the innermost layer were prepared.
(1) Polyethylene terephthalate (PET) (12 μm)/aluminum (AL) (7 μm)/PET having heat-sealing properties (20 μm to 50 μm)
(2) Cellophane (#300 to #500)/AL (7 μm)/PET having heat-sealing properties (20 μm to 50 μm)
(3) PET (12 μm)/AL (9 μm)/polyethylene (PE) (20 μm to 50 μm)
(4) PET (12 μm)/PE (10 μm to 30 μm)/AL (7 μm)/PE (10 μm to 40 μm)
(5) Cellophane (#300 to #500)/PE (10 μm to 30 μm)/AL (7 μm)/PE (10 μm to 40 μm)
The above films were each cut into a rectangular shape corresponding to a packaging bag dimension described later and then score lines were formed on the surfaces of the films. After that, two films, in which the score lines were formed, were overlapped with each other so that the innermost layers (sealant layers) would face each other and then contents prepared in advance were placed in the container part, followed by heat-sealing the four edges. The seal width (Ls of
Table 1 shows information on the packaging bags of Examples 1-1 to 1-14 and Comparative Examples 1-1 to 1-11 in terms of the dimension of the packaging bag, the distance La from each end of the first and second score lines to the inner edge of the seal part, the shape of the score lines, and evaluation (presence or absence of cracks in the aluminum layer). It should be noted that when the distance La has a positive value, the score line is away from the seal part in plan view, and when it has a negative value, the score line is formed being extended onto the seal part.
In the packaging bags of Examples 1-1 to 1-14, the first and second score lines were formed away from the inner edge of the seal part by 1 mm or more. Therefore, stress caused by sealing in the aluminum layer near the inner edge of the seal part was reduced. Thus, as shown in Table 1, microcracks occurred in none of the samples. Accordingly, it was confirmed that occurrence of microcracks in the aluminum layer near the inner edge of the seal part was prevented by forming the score lines away from the seal part. From this result, it is considered that the occurrence of microcracks can be more effectively prevented in a packaging bag using a film not including an aluminum layer.
In the packaging bags of Comparative Examples 1-1 to 1-11, the score lines were formed so as to abut with the seal part or formed being extended onto the seal part. Therefore, large stress was caused by sealing in the aluminum layer near the inner edge of the seal part. Thus, as shown in Table 1, microcracks occurred in all of the samples.
Packaging bags of examples and comparative examples were prepared and openability of these packaging bags was evaluated. The packaging bags of the examples were each prepared by changing the position and the shape of the score lines of the packaging bag 200 shown in
For each of the examples and the comparative examples, packaging bags respectively using the films having the following layer structures from the outermost layer to the innermost layer were prepared.
(1) Polyethylene terephthalate (PET) (12 μm)/aluminum (AL) (7/PET having heat-sealing properties (20 μm to 50 μm)
(2) Cellophane (#300 to #500)/AL (7 μm)/PET having heat-sealing properties (20 μm to 50 μm)
(3) PET (12 μm)/AL (9 μm)/polyethylene (PE) (20 μm to 50 μm)
(4) PET (12 μm)/PE (10 μm to 30 μm)/AL (7 μm)/PE (10 μm to 40 μm)
(5) Cellophane (#300 to #500)/PE (10 μm to 30 μm)/AL (7 μm)/PE (10 μm to 40 μm)
(6) PET (12 μm)/PET having heat-sealing properties (10 μm to 50 μm)
(7) Transparent deposition PET (12 μm)/PET having heat-sealing properties (10 μm to 50 μm)
(8) PET (12 μm)/PE (10 μm to 50 μm)
The above films were each cut into a rectangular shape corresponding to a packaging bag dimension described later and then score lines were formed on the surfaces of the films. After that, two films, in which the score lines were formed, were overlapped with each other so that the innermost layers (sealant layers) would face each other, followed by sealing the four edges. The seal width (Ls of
The prepared packaging bags were evaluated in terms of openability when opened from the first and second notches as start points. Table 2 shows information on Examples 2-1 to 2-14 and Comparative Examples 2-1 to 2-11 in terms of the dimension of the packaging bag, the positions La1 and La2 of ends of each score line, the shape of the score lines, and evaluation (openability). It should be noted that when the positions La1 and La2 of the ends have a positive value, the score line is at a position above the first straight line 61 in
In the evaluations, if the break line reached the edge that faced the notch in all the samples, the packaging bag was taken to have sufficient openability and evaluated with a mark “++”. If the break line did not reach the edge that faced the edge in which the notch was formed and failure in opening occurred in all the samples, the packaging bag was taken to have no openability and evaluated with a mark “−”. If some samples were confirmed to have good openability and other samples caused failure in opening, the packaging bag was taken to have insufficient openability and was evaluated with a mark “+”.
In the packaging bags of Examples 2-1 to 2-14, the first and second score lines could each have an allowable angular range relative to the direction of forming the break line. Therefore, even when the direction of forming the break line was not parallel to the straight line extending from the notch to the facing edge, the break line could smoothly reach the first score line or the second score line, i.e., the break line could reach the facing edge from the notch. From this result, as shown in Table 2, it was confirmed that the packaging bags of Examples 2-1 to 2-14 had sufficient openability. It should be noted that regardless of the layer structures and thicknesses of the films, the same results were obtained.
In contrast, in some films of the packaging bags of Comparative Examples 2-1 to 2-11, the break line could not reach the facing edge from the notch, causing failure in opening. Specifically, in the packaging bags of Comparative Examples 2-1, 2-3 to 2-7 and 2-9 to 2-11, the first and second score lines could not each have an allowable angular range relative to the direction of forming the break line. Therefore, if the direction of forming the break line was not parallel to the straight line extending from the notch to the facing edge, the break line could not successfully reach the first score line or the second score line. Accordingly, the break line could not reach the facing edge from the notch, causing failure in opening. It should be noted that regardless of the layer structures and thicknesses of the films, the same results were obtained.
In Comparative Examples 2-2 and 2-8, the first and second score lines each did not have an allowable angular range relative to the direction of forming the break line. However, the break line was prevented from being directed to the edge near the notch, i.e., the edge adjacent to the edge in which the notch was formed. Thus in some samples, the occurrence of failure in opening was prevented.
Although the packaging bags related to the third embodiment are not included in Examples 2-1 to 2-14, similar results are expected to be obtained from these packaging bags.
<Examples According to the Third Embodiment, i.e., the Mode in which the Score Lines are Extended onto the Seal Part>
Packaging bags of examples and comparative examples were prepared and openability of these packaging bags was evaluated. The packaging bags of the examples were prepared by changing the positions (distance La3, see
For each of the examples and the comparative examples, packaging bags respectively using the films having the following layer structures from the outermost layer to the innermost layer were prepared.
(1) Polyethylene terephthalate (PET) (12 μm)/aluminum (AL) (7/PET having heat-sealing properties (20 μm to 50 μm)
(2) Cellophane (#300 to #500)/AL (7 μm)/PET having heat-sealing properties (20 μm to 50 μm)
(3) PET (12 μm)/AL (9 μm)/polyethylene (PE) (20 μm to 50 μm)
(4) PET (12 μm)/PE (10 μm to 30 μm)/AL (7 μm)/PE (10 μm to 40 μm)
(5) Cellophane (#300 to #500)/PE (10 μm to 30 μm)/AL (7 μm)/PE (10 μm to 40 μm)
(6) PET (12 μm)/PET having heat-sealing properties (10 μm to 50 μm)
(7) Transparent deposition PET (12 μm)/PET having heat-sealing properties (10 μm to 50 μm)
(8) PET (12 μm)/PE (10 μm to 50 μm)
The above films were each cut into a rectangular shape corresponding to a packaging bag dimension described later and then score lines were formed on the surfaces of the films. After that, two films, in which the score lines were formed, were overlapped with each other so that the innermost layers (sealant layers) would face each other, followed by sealing the four edges. The seal width (Ls of
The prepared packaging bags were evaluated in terms of openability when opened from the first and second notches as start points. When opening each packaging bag, the films were each broken by applying a load in a direction of forming the break line toward the edge that was adjacent to the edge where the notch was formed, i.e., toward the edge near the notch. Table 3 shows information on the packaging bags of Examples 3-1 to 3-14 and Comparative Examples 3-1 to 3-11 in terms of the dimension of the packaging bag, the minimum value La3 of the distance from the first or second score line to the phantom straight line extending from the notch, the shape of the score lines, presence or absence of the auxiliary lines, and evaluation (openability). It should be noted that when the minimum value La3 of the distance has a positive value, the score line is at a position above the first straight line 61 in
In the evaluations, if the break line reached the edge that faced the notch in all the samples, the packaging bag was taken to have sufficient openability and evaluated with a mark “+”. If the break line did not reach the edge that faced the edge in which the notch was formed and failure in opening occurred in all the samples, the packaging bag was taken to have no openability and evaluated with a mark “−”.
In the packaging bags of Examples 3-1 to 3-14, the break line was formed so as to pass through a portion of the container part sandwiched between the phantom straight line extending from the notch and the edge near the notch among the edges adjacent to the edge in which the notch was formed. Therefore, even when the break line was formed toward the edge near the notch among the edges adjacent to the edge in which the notch was formed, the break line could smoothly reach the score line and could be guided to the edge which faced the notch. Accordingly, as shown in Table 3, it was confirmed that the packaging bags of Examples 3-1 to 3-14 had sufficient openability. It should be noted that regardless of the layer structures and thicknesses of the films, the same results were obtained.
In contrast, in the packaging bags of Comparative Examples 3-1 to 3-11, the break line could not reach the facing edge from the notch, causing failure in opening, in at least either one of the first and second score lines 1 and 2. Specifically, in Comparative Examples 3-2 and 3-8, the break line deviated from the first score line formed on the straight line extending from the notch and caused failure in opening. In Comparative Examples 3-3 and 3-10 as well, the break line deviated from the sixth score line formed on the straight line extending from the notch and caused failure in opening. In other comparative examples, the break lines deviated from both the first and second score lines and caused failure in opening.
As the packaging bags of Examples 3-1 to 3-14, packaging bags, in which only either one of the first and second score lines was formed, were additionally formed to evaluate openability. The packaging bags in which only either one of the first and second score lines was formed also produced the same results as in the packaging bags of Examples 3-1 to 3-14 shown in Table 3.
The present invention can be suitably used for packaging sheet-shaped contents, such as a medical tape or a patch, for transdermal administration of medication, as well as for other applications.
100-103, 200-203, 300-303, 901-905 Packaging bag; 10 Film; 20 Seal part; 21 Inner edge of seal part; 30 Container part; 41 First score line; 42 Second score line; 51 First notch; 52 Second notch; 61 Phantom first straight line; 62 Phantom second straight line; 71 First edge; 72 Second edge; 73 Third edge; 74 Fourth edge; 81 First auxiliary score line; 82 Second auxiliary score line.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2017-118741 | Jun 2017 | JP | national |
| 2017-118742 | Jun 2017 | JP | national |
| 2017-118743 | Jun 2017 | JP | national |
This application is a continuation application filed under 35 U.S.C. § 111(a) claiming the benefit under 35 U.S.C. §§ 120 and 365(c) of International Patent Application No. PCT/JP2018/022437, filed on Jun. 12, 2018, which is based upon and claims the benefit of priority to Japanese Patent Application No. 2017-118741, filed on Jun. 16, 2017; Japanese Patent Application No. 2017-118742, filed on Jun. 16, 2017; and Japanese Patent Application No. 2017-118743, filed on Jun. 16, 2017; the disclosures of which are all incorporated herein by reference in their entireties.
| Number | Date | Country | |
|---|---|---|---|
| Parent | PCT/JP2018/022437 | Jun 2018 | US |
| Child | 16714051 | US |