This invention relates generally to detection of soft errors in electronic systems and, more particularly, to packaging integrated circuits, including logic circuits and array circuits, for accelerated testing of soft error rates due to errors caused by ionizing particle emission.
Accurate estimates of soft error rates (SER's) in computer systems are desirable for the implementation of reliable systems. Soft errors are caused by single-event upsets (SEU's), which are random, isolated events that can be caused by passage of cosmic rays or transient ionizing particles, such as alpha particles. That is, ionizing particles can generate enough free charge to flip a structure or device to its opposite state. In an integrated circuit (IC) chip package, emission of trace amounts of radioactive impurities is one cause of SEU's. For wire-bonded structures, accelerated testing using a radioactive source of alpha particles is straightforward. In particular, a source of alpha particles with a known emission rate, such as, for example, a thorium foil, may be easily positioned adjacent to the wire-bonded chip with little energy loss as viewed from the source to the chip.
Unfortunately, however, for integrated circuits (IC's) that use, for example, solder bumps or balls, such as controlled collapsible chip connections (herein referred to as solder bumps), the chip-to-substrate gap is too small (e.g., on the order of 100 microns or less) to allow access by a hand-held radioactive source. Furthermore, the substrate blocks any access to the semiconductor device by a radioactive source, handheld or otherwise. Moreover, the range of alpha particles is substantially smaller than the thickness of the substrate, such that the alpha particles emitted from an external source cannot reach the semiconductor device. Typically, a low alpha emission underfill is inserted into the gap in order to stabilize the solder bond and act as a shield or block for any alpha particles that may emanate from the substrate or carrier.
Eliminating lead from the solder bumps reduces, but does not eliminate, the alpha radiation to the chip. Other sources of alpha particles may be, for example, trace amounts of thorium in chip materials that have been produced from mined ores. In addition, alpha particles from packaging materials, or solder bumps, add to, or compete with, neutron-induced soft errors caused by the liberation of charged particles when atmospheric neutrons strike silicon or other materials surrounding the chips. Disadvantageously, soft errors occur with greater frequency with advances in CMOS technology, for example; i.e., as dimensions get smaller, densities increase, and bias voltages become lower. Furthermore, while soft errors in caches and other static random access memory (SRAM) arrays can be detected and corrected with the aid of error correction codes (ECC's), for example, this is not the case for soft errors in logic circuits.
A current method for estimating soft error rates (SER's) is to add the soft error contributions from each circuit element. To this end, derating factors need to be estimated, and these are affected by, for example, SEU's in a portion of an IC that is not being used, or a node that is a logical off state. Unfortunately, therefore, these derating factors are difficult to estimate. Furthermore, relying on measurements from systems being tested in the field necessitates delays in acquisition of SER information until after a product is made.
Accordingly, it is desirable to provide a technique for packaging IC's to enable accelerated detection, in situ, of SER's due to transient particle emission.
The shortcomings of the prior art are overcome and additional advantages are provided through packaging integrated circuits (IC's) for accelerated detection of SER's due to transient particle emission. An IC device is packaged for accelerated transient particle emission by doping the underfill thereof with at least one transient-particle-emitting material having a predetermined, substantially constant emission rate. In one aspect, a radioactive adhesive composition is provided for bonding a semiconductor device to a chip carrier, i.e., a structure which holds a chip and which is used to facilitate its placement on a substrate. The radioactive adhesive composition comprises a cured reaction product comprising a resin and filler material(s), and may be reworkable or non-reworkable. Either the resin or the filler, individually or both together as a mix, are doped substantially uniformly with the transient-particle-emitting material, thereby putting the transient-particle-emitting material in close proximity with the IC to be tested. The underfill is formulated to have a stable chemistry, and the doped particles are encapsulated, so as to contain the emissions. Accelerated transient-particle-emission testing may then performed on the IC in situ. Advantageously, therefore, SER's due to soft errors may be detected, and a quantitative measurement of the SER may be determined therefrom.
Further, additional features and advantages are realized through the techniques of the present invention. Other embodiments and aspects of the invention are described in detail herein and are considered a part of the claimed invention.
The subject matter that is regarded as the invention is particularly pointed out and distinctly claimed in the claims at the conclusion of the specification. The foregoing and other objects, features, and advantages of the invention are apparent from the following detailed description taken in conjunction with the accompanying drawings in which:
Presented herein is a technique for packaging IC's for accelerated detection of SER's due to transient-particle emission in integrated circuits (IC's), including, but not limited to, logic circuits. Logic circuits are defined herein as comprising all structures on an IC apart from SRAM arrays, including but not limited to, combinatorial logic, latches in the logic paths, register files, buffers, and input/output circuits.
In accordance with an aspect of the present invention, an IC device is packaged for accelerated transient particle emission by doping the underfill thereof with at least one transient-particle-emitting material having a predetermined, substantially constant emission rate, the doped underfill being referred to herein as a “hot underfill” or “HUF”.
In preferred embodiments, the volume and surface area of radioactive fillets 19 are reduced in order to minimize emission of radioactive particles to the ambient. A vacuuming or wicking process may be employed to reduce the fillet. In a vacuuming process, for example, a standard pressure feed fluid dispense tool is used in a vacuum pick-up mode to pick up the radioactive underfill fillet. Alternatively, in a wicking process, an exemplary wicking fabric, such as a lint-free clean room cloth, is used to contact the radioactive underfill, which is picked up through wicking action.
After radioactive fillet 19 is substantially reduced in size, a soft-cure, or B-stage cure, is completed to solidify the radioactive underfill. Next, a cold, or undoped underfill material (CUF) 20, that is preferably chemically compatible with the hot underfill, is dispensed over the remaining, substantially reduced-in-size HUF fillet in order to encapsulate it and provide a cover barrier to the radioactive underfill. The underfill is then fully cured, resulting in a structure with any exposed HUF being protected from surface abrasion or erosion by CUF fillet 20, resulting in reduced radioactive emissions to the ambient.
An exemplary underfill comprises a silica filler. A filler material may be electrically conductive or non-conductive, or thermally conductive. An exemplary doped underfill in accordance with an aspect of the present invention comprises radioactive lead or polonium, or a mixture of both, contributing an accelerated alpha-particle emission rate compared to standard IC packaging materials. By way of example, an HUF formulation having an alpha particle emission rate of approximately 1E6 alpha particles/cm2/khr was used for demonstration. For this example, if the alpha particle flux from packaging materials, such as solder, were 20 alpha particles/cm2/khr, the introduction of HUF would provide an acceleration factor of over 50,000.
Those skilled in the art will recognize that the energy distribution and flux of the HUF could be measured with a silicon surface barrier type detector (not shown). Furthermore, a plurality of silicon surface barrier type detectors could be employed for measuring the uniformity of alpha particle activity across the integrated circuit.
The gap 18 between the substrate 12 and the semiconductor 11 is typically on the order of, for example, 100 microns, as indicated hereinabove. The range of alpha particles from 210 Po (5.3 MeV) in most fillers is on the order of approximately 35 microns. Therefore, when an underfill is doped with an alpha particle emitting isotope, the source appears to be “thick”, and the alpha particles advantageously emerge from the filler at the semiconductor side with a broad distribution of energies. This is opposed to a mono-energetic distribution, which would otherwise occur if the doped region were substantially thinner than the alpha-particle range, or if all the radioactive material were segregated on the chip surface.
In accordance with an aspect of the present invention, the emission rate of the hot underfill is substantially constant over a predetermined period of time. To this end, the HUF is doped with an appropriate alpha- particle-emitting material or other radioactive source that provides a substantially constant particle emission rate. In particular, the emission rate does not substantially increase or decrease, and thus does not approach an exponential rate. An exemplary substantially constant alpha particle emission rate may have, for example, a 10% or less variation in flux per month.
By way of example, alpha particles from 210Po emitted from solder bumps can be a major source of SER for IC's. In accordance with one aspect of the present invention, an underfill comprising 210Po is provided in order to duplicate the alpha-particle range distribution of the solder bumps. The half-life of 210Po (138 days) is too short for the duration of most experiments so a mixture with 210Pb is provided to generate a nearly constant emission rate.
In another aspect of the present invention, one or more components of the underfill may be doped to be radioactive either separately or as a combination.
HUF is applied to an IC. The fillet 19 (
The method of doping the underfill of an IC for accelerated SER detection in accordance with an aspect of the present invention may be extended to other radioactive isotopes, such as, for example, thorium or uranium, to mirror the flux and alpha-particle energy distribution from real packaging materials because there might be impurities in materials such as mined silica.
In another aspect of the present invention, the transient particle emission rate may be tunable by adjusting the ratios of the radioactive isotopes, e.g., 210Po and 210Pb that are mixed together in the underfill.
Those skilled in the art will recognize that permutations of the process using a reworkable underfill are possible. For example, underfills exhibiting different activities or energy distributions could be used to test the same chip. Alternatively, the same underfill formulation could be used with different chips for testing.
Advantageously, the packaging technique described hereinabove allows for accelerated transient-particle emission testing in situ on IC 10, i.e., without necessitating delays due to field testing. In particular, the hot underfill (HUF) allows for accelerated testing for transient-particle-induced (e.g., alpha-particle-induced) SER events at the system level, board level, chip level, or any combination thereof. The test type may be of any suitable form comprising, for example, actual application programs and data; programs and data that simulate applications or test cases; test programs that are intended to stress certain desired cases, functions, or parts of a system; a built-in self-test; static tests that read in 1's and 0's, then wait, and then read out the results and detect the SER's. For each test type, the result can be tested for upsets by either detecting a system crash; detecting an error through detection circuitry, such as a parity checker; comparing the resulting data stream to the expected data stream; comparing duplicate structures; residue checking; or any other suitable method. When the results are read out, they are counted to form a SER per circuit, or per bit, as desired.
The present invention can be included in an article of manufacture (e.g., one or more computer program products) having, for instance, computer usable media. The media has embodied therein, for instance, computer readable program code means for providing and facilitating the capabilities of the present invention. The article of manufacture can be included as a part of a computer system or sold separately.
Additionally, at least one program storage device readable by a machine embodying at least one program of instructions executable by the machine to perform the capabilities of the present invention can be provided.
The diagrams depicted herein are just examples. There may be many variations to these diagrams or the steps (or operations) described therein without departing from the spirit of the invention. For instance, the steps may be performed in a differing order, or steps may be added, deleted or modified. All of these variations are considered a part of the claimed invention.
Although preferred embodiments have been depicted and described in detail herein, it will be apparent to those skilled in the relevant art that various modifications, additions, substitutions and the like can be made without departing from the spirit of the invention and these are therefore considered to be within the scope of the invention as defined in the following claims.
This application is related to U.S. patent application No.______ (POU9-2004-0174), assigned to the instant assignee, filed concurrently herewith and incorporated by reference herein.