Patent Grant
9988746
Synthetic composite materials possess desirably high strength-to-weight ratios; however, synthetic composites typically have lacked dynamic functionality that occurs in natural composite materials. Natural composite materials can utilize vascular networks to accomplish a variety of biological functions, in both soft and hard tissue. For example, composite structures such as bone tissue or wood are lightweight and have high strength, yet contain extensive vasculature capable of transporting mass and energy.
Another feature of natural composite materials is their ability to have different levels of communication between distinct vascular networks, depending on the specific role of the material within an organism. In one example, the phloem and xylem channels of plant vascular bundles may be independent and separated by lignin layers, such that the contents of the channels do not interact. In another example, physical contact between the artery and vein channels of a human or animal circulatory system may provide for heat transfer between the channels; however, the chemical compositions of the fluids in these channels remain separate. In yet another example, gas exchange of oxygen and carbon dioxide occurs between the blood vessel channels and the alveoli channels within the lungs.
An ongoing challenge in materials science is the development of microvascular networks in synthetic materials using conventional manufacturing processes. Specialized fabrication methods such as laser-micromachining, soft lithography, templating with degradable sugar fibers, and incorporating hollow glass or polymeric fibers can produce some microvascular structures in synthetic materials. These specialized methods, however, are not currently suitable for rapid, large-scale production of materials having complex vasculatures.
In one approach to microfluidic materials, relatively short microfluidic channels are provided in a matrix in the form of hollow glass fibers (WO 2007/005657 to Dry). The glass fibers are present as repair conduits containing a fluid that can heal a crack in the composite matrix. A significant limitation of this approach is the brittle nature of the hollow glass fibers, which limits the shapes and lengths of microfluidic channels that can be present in the material. In addition, the glass fibers cannot readily be used to form a microfluidic network.
In another approach to microfluidic materials, microfluidic channels are formed in a polymeric matrix by arranging hollow polymeric fibers and then forming the matrix around the hollow polymeric fibers (U.S. Publication No. 2008/0003433 to Mikami). Hollow polymeric fibers may offer a wider variety of microfluidic channel shapes than those available from hollow glass fibers. This approach, however, also has a number of limitations, including an inability to form a network from the individual hollow fibers, the relatively small number of materials available as hollow fibers, and the possibility of incompatibility between the hollow fiber and the matrix.
Microfluidic networks can be formed in a polymeric matrix using a three-dimensional (3-D) direct-write assembly technique (U.S. Publication No. 2008/0305343 to Toohey et al.). While this fabrication method provides excellent spatial control, the resulting networks typically will not survive the mechanical and/or thermal stresses encountered in the conventional processes of forming reinforced composites.
It is desirable to provide multiple microvascular networks in synthetic materials, where the type and level of communication between the distinct microvascular networks can be varied between different materials. It is desirable for such complex microvascular networks to be formed using conventional manufacturing processes. It also is desirable for the microfluidic channels of the different networks within a material to be available in a variety of shapes and dimensions, and for a variety of polymers to be available as the polymeric matrix of such composites.
In one aspect, there is provided a partially degradable polymeric fiber that includes a thermally degradable polymeric core and a coating surrounding at least a portion of the core. The thermally degradable polymeric core includes a polymeric matrix including a poly(hydroxyalkanoate), and a metal selected from the group consisting of an alkali earth metal and a transition metal, in the core polymeric matrix. The concentration of the metal in the polymeric matrix is at least 0.1 wt %.
In another aspect, there is provided a method of making a partially degradable polymeric fiber that includes combining a fiber containing a poly(hydroxyalkanoate) and having an exterior surface, and a composition containing a fluorinated fluid and a metal selected from the group consisting of an alkali earth metal and a transition metal. The method further includes maintaining the fiber and the composition together at a temperature and for a time sufficient to provide a concentration of the metal in the fiber of at least 0.1 wt %, separating the fiber and the fluorinated fluid, and depositing a layer of a material on at least a portion of the exterior surface of the fiber.
In another aspect, there is provided a partially degradable fiber system that includes a thermally degradable polymeric core and a coating surrounding at least a portion of the core. The thermally degradable polymeric core has a degradation temperature of at most 250° C. At least a portion of the coating does not thermally degrade at temperatures below 275° C.
In another aspect, there is provided a microvascular system that includes a solid polymeric matrix including a first material, and a woven structure in the matrix. The woven structure includes a plurality of microfluidic channels having a channel wall including a second material, where the second material is different from the first material.
In another aspect, there is provided a method of making a microvascular system that includes forming a composite including a solid polymeric matrix, and a plurality of partially degradable polymeric fibers in the matrix. The partially degradable polymeric fibers include a thermally degradable polymeric core having a degradation temperature of at most 250° C., and a coating surrounding at least a portion of the thermally degradable polymeric core, where at least a portion of the coating does not thermally degrade at temperatures below 275° C. The method further includes heating the composite to a temperature of from 100 to 250° C., maintaining the composite at a temperature of from 100 to 250° C. for a time sufficient to form degradants from the polymeric core, and removing the degradants from the composite to provide a network of microfluidic channels. The degradants have an average molecular weight less than 500 Daltons.
In a further aspect, there is provided a method of making a microporous film that includes providing a coating precursor including a thermally degradable polyhydroxyalkanoate having a degradation temperature of at most 250° C., and a thermally stable material that does not thermally degrade at temperatures below 275° C. The method further includes casting a film of the coating precursor, solidifying the coating precursor, and heating the film to a temperature of from 100° C. to 250° C. for a time sufficient to form degradants from the thermally degradable polyhydroxyalkanoate. The method also includes removing the degradants from the film to provide a microporous film. The microporous film may serve as separator in energy storage devices such as lithium-ion batteries.
The subject matter of the present application can be better understood with reference to the following drawings and description. The components in the figures are not necessarily to scale and are not intended to accurately represent molecules or their interactions, emphasis instead being placed upon illustrating the principles of the subject matter of the present application. Moreover, in the figures, like referenced numerals designate corresponding parts throughout the different views.
In one aspect, a partially degradable polymeric fiber includes a thermally degradable polymeric core and a coating surrounding at least a portion of the core. The partially degradable polymeric fiber may be used to form a microvascular system having a solid polymeric matrix and a woven structure in the matrix, where the woven structure includes a plurality of microfluidic channels having a channel wall, which may have any of a variety of permeability properties.
Such microvascular systems can provide unprecedented applications, and can be designed to contain a variety of microvascular network types and sizes—from simple, straight conduits to complex, computer-controlled 3D woven architectures. The microvascular systems may be formed from commercially available materials, and may be integrated seamlessly with conventional fiber-reinforced composite manufacturing methods.
A microvascular system may be formed from composite materials containing partially degradable polymeric fibers and optionally containing reinforcing fibers. Partially degradable polymeric fibers may be used to form biomimetic material systems in a reliable manner, and may be used to model, reproduce and/or extend transport functions performed by microvascular systems in nature. Composite materials containing both partially degradable polymeric fibers and reinforcing fibers can be used to provide microvascular systems, such as those described above.
A partially degradable polymeric fiber may include a thermally degradable polymeric core that degrades at temperatures above those typically used for forming composite materials, but below the typical degradation temperatures of composite materials. The thermally degradable polymeric core may be at least partially surrounded by a coating, where at least a portion of the coating does not thermally degrade at the same temperatures as the core. The thermally degradable polymeric core may include a polymeric fiber matrix and a catalyst in the fiber matrix that lowers the degradation temperature of the matrix polymer to within an appropriate temperature window.
Partially Degradable Polymeric Fibers
Partially degradable polymeric fibers, such as fiber 100, preferably have a combination of desirable properties. These desirable properties include sufficient strength for configuration as a preform and/or for combination with a composite matrix precursor using standard composite formation methods, and mechanical integrity at temperatures typically used to form composites. The desirable properties also include degradation and volatilization temperatures within a range between the highest composite matrix solidification temperatures and the lowest thermal degradation temperatures of the composite matrix. Preferably the partially degradable polymeric fiber has all of these desirable properties.
The thermally degradable polymeric core 110 preferably has a degradation temperature below 280° C., and preferably has a degradation temperature of at most 250° C. Preferably the thermally degradable polymeric core 110 has a degradation temperature between 100 and 250° C. Preferably the thermally degradable polymeric core 110 has a degradation temperature of at most 220° C., of at most 180° C., of at most 150° C., or of at most 100° C.
The thermally degradable polymeric core 110 may include a poly(hydroxyalkanoate). A poly(hydroxyalkanoate) is an aliphatic polyester having the general structure:O—C(R1R2)—(CR3R4)x—C(═O)
n
where n is an integer of at least 10, x is an integer from 0 to 4, and R1-R4 independently are —H or an alkyl group. Examples of poly(hydroxyalkanoate)s include poly(3-hydroxybutyrate) (P3HB), poly(4-hydroxybutyrate) (P4HB), poly(3-hydroxy-valerate) (PHV), polycaprolactone, poly(lactic acid) (PLA), poly(glycolic acid) (PGA), and copolymers of the monomeric units of these polymers.
It has now been discovered that thermally degradable poly(hydroxyalkanoate) fibers can be at least partially surrounded with a coating to produce partially degradable fibers, which can be used successfully as coated sacrificial fibers in polymeric matrices such as epoxies. These coated sacrificial fibers preferably include a thermally degradable fiber core having a polymeric fiber matrix including a poly(hydroxyalkanoate) and including a metal in the fiber matrix, where the metal includes an alkali earth metal and/or a transition metal. Preferably the concentration of the metal in the fiber matrix is at least 0.1 percent by weight (wt %).
Poly(hydroxyalkanoate)s may degrade at elevated temperatures through a depolymerization process, forming small molecule degradants that may be gases. For example, poly(lactic acid) (PLA) is a thermoplastic poly(hydroxyalkanoate) that depolymerizes at temperatures above 280° C., forming lactide as a gaseous degradant. The depolymerization temperature of poly(hydroxyalkanoate)s such as PLA may be reduced by blending the poly(hydroxyalkanoate) with an alkaline earth metal and/or a transition metal. A reduced depolymerization temperature may help prevent damage to materials in contact with the thermally degradable polymeric core 110, such as the coating 120 or a polymeric matrix in which the partially degradable polymeric fiber 100 is contained. Preferably the thermally degradable polymeric core 110 depolymerizes within an appropriate temperature range, but without deterioration of the desirable mechanical properties of the fiber 100 below the degradation temperature. Preferably the poly(hydroxyalkanoate) has a degradation temperature below 280° C., and preferably has a degradation temperature of at most 250° C.
Preferably the concentration of the metal in the poly(hydroxyalkanoate) fiber matrix is at least 0.2 wt %, at least 0.5 wt %, at least 1 wt %, at least 2 wt %, at least 2.5 wt %, at least 3 wt %, at least 5 wt %, at least 7 wt %, or at least 10 wt %. The concentration of the metal in the poly(hydroxyalkanoate) fiber matrix may be from 0.1 to 10 wt %, from 0.2 to 7 wt %, from 0.5 to 5 wt %, or from 1 to 3 wt %. Preferably the metal is present in the fiber as MgO, CaO, BaO, SrO, tin(II) acetate, tin(II) oxalate, tin(II) octoate, or scandium triflate (Sc(OTf)3). More preferably the metal is present in the fiber as strontium oxide, tin(II) oxalate or tin(II) octoate.
The coating 120 that surrounds at least a portion of the core includes a polymeric material having a degradation temperature higher than the degradation temperature of the thermally degradable polymeric core 110. When the fiber 100 is heated to the degradation temperature of the thermally degradable polymeric core 110, the core will degrade and can be removed, providing a hollow fiber having a wall containing the polymeric material of the coating 120. Preferably, the coating 120 does not thermally degrade at temperatures below 250° C. Preferably, the coating 120 does not thermally degrade at temperatures below 275° C., at temperatures below 280° C., at temperatures below 300° C., at temperatures below 325° C., or at temperatures below 350° C.
The coating 120 may include a polyamide such as nylon; a polyester such as poly(ethylene terephthalate) and polycaprolactone; a polycarbonate; a polyether; an epoxy polymer; an epoxy vinyl ester polymer; a polyimide such as polypyromellitimide (for example KAPTON® (DuPont, Wilmington, Del.); a phenol-formaldehyde polymer such as bakelite (polyoxybenzylmethylenglycolanhydride; an amine-formaldehyde polymer such as a melamine polymer; a polysulfone; a polyacrylonitrile-butadiene-styrene) (ABS); a polyurethane; a polyolefin such as polyethylene, polystyrene, polyacrylonitrile, a polyvinyl, polyvinyl chloride and poly(DCPD); a polyacrylate such as poly(ethyl acrylate); a poly(alkylacrylate) such as poly(methyl methacrylate); a polysilane such as poly(carborane-silane); and/or a polyphosphazene.
The coating 120 may include an elastomer, such as an elastomeric polymer, an elastomeric copolymer, an elastomeric block copolymer, and/or an elastomeric polymer blend. Examples of elastomer polymers include polyolefins, polysiloxanes such as poly(dimethylsiloxane) (PDMS), polychloroprene, and polysulfides; examples of copolymer elastomers may include polyolefin copolymers and fluorocarbon elastomers; examples of block copolymer elastomers may include acrylonitrile block copolymers, polystyrene block copolymers, polyolefin block copolymers, polyester block copolymers, polyamide block copolymers, and polyurethane block copolymers; and examples of polymer blend elastomers include mixtures of an elastomer with another polymer.
The coating 120 may include a mixture of these polymers, including copolymers that include repeating units of two or more of the polymers, and/or including blends of two or more of the polymers. In one example, the coating 120 includes a blend of at least a first polymer and a second polymer, where the first polymer has a degradation temperature below 280° C., and the second polymer does not thermally degrade at temperatures below 280° C. In this example, one portion of the coating 120 may degrade at a temperature similar to the temperature at which the thermally degradable polymeric core 110 degrades, while another portion of the coating 120 may not degrade at this temperature. When such a coated fiber is heated to the degradation temperature of the first polymer of the coating, the thermally degradable polymeric core 110 and the portion of the coating containing the first polymer can degrade and can be removed, providing a hollow fiber having a wall containing the second polymer of the coating 120.
The coating 120 may include other ingredients in addition to the polymeric material. For example, the coating may contain one or more particulate fillers, stabilizers, antioxidants, flame retardants, plasticizers, colorants and dyes, fragrances, or adhesion promoters. An adhesion promoter is a substance that increases the adhesion between two substances, such as the adhesion between two polymers. One type of adhesion promoter that may be present includes substances that promote adhesion between the coating 120 and the thermally degradable polymeric core 110, and substances that promote adhesion between the coating 120 and a polymeric matrix in which the partially degradable polymeric fiber 100 is contained.
Methods of Making Partially Degradable Polymeric Fibers
An alkali earth metal or a transition metal may be incorporated into a poly(hydroxyalkanoate) fiber through an infusion process, as outlined by the combining 210, maintaining 220 and separating 230 of method 200. In one example, PLA fibers may be infused with a tin(II) oxalate (SnOx) catalyst present in an aqueous trifluoroethanol (TFE) mixture. Exposing the PLA fibers to a solution of TFE:H2O using a ratio of 60:40 parts by volume (pbv) with 2% SnOx parts by weight (pbw), for a minimum of 24 h yielded partially degradable polymeric fibers suitable for use in the composite formation method of Vaporization of Sacrificial Components (VaSC). The catalyst-containing fibers converted to gas at a lower temperature and in less time than did pure PLA fibers, as measured by isothermal gravimetric analysis (iTGA), indicating a lower depolymerization onset temperature.
An alkali earth metal or a transition metal may be incorporated into a poly(hydroxyalkanoate) fiber through a liquid spinning process, as outlined by the forming 310, passing 320, drying 330 and optionally cold-drawing 340 of method 300. In one example, a solution of PLA in dichloromethane containing 10% SnOx pbw was spun through a 0.5 millimeter (mm) spinneret to provide a continuous strand of PLA containing the SnOx catalyst. The catalyst-containing fibers formed by liquid spinning converted to gas at a lower temperature and in less time than did comparable fibers formed by an infusion process, as measured by thermogravimetric analysis (TGA), indicating a lower depolymerization onset temperature. Cold-drawing the fibers formed from liquid spinning could increase the fiber strength, ensuring that the fibers can be woven using conventional techniques.
Thermally degradable fibers formed by a liquid spinning process, such as that outlined in
A liquid spinning process may be more efficient in its use of catalyst than an infusion process. For example, a spun fiber formed by a liquid spinning process may include a higher concentration of catalyst than an infused fiber formed by an infusion process, even though the spinning liquid and the infusion liquid include the same initial concentration of catalyst. Thus, to achieve a given loading of catalyst in a thermally degradable fiber, a liquid spinning process may require less total catalyst than a comparable infusion process.
Thermally degradable fibers formed by a liquid spinning process may include a wider variety of depolymerization catalysts than can be included using an infusion process. In one example, infusion of PLA fibers with tin(II) octoate (SnOc) provided fibers with a greasy surface, whereas liquid spinning provided PLA fibers containing SnOc, but with a more desirable non-greasy surface. As the depolymerization temperature of PLA fibers containing SnOc is lower than that of PLA fibers containing SnOx, the liquid spinning method can provide PLA fibers that are readily incorporated into a composite and that depolymerize at a relatively low temperature.
A method of making a thermally degradable fiber may include other known methods of incorporating an additive into a polymer fiber, such as melt spinning. In the example of melt spinning, the temperature of the material should be maintained below 180° C., the temperature at which PLA can depolymerize in the presence of a catalyst containing an alkali earth metal or a transition metal. One potential advantage of melt spinning PLA fibers containing a depolymerization catalyst is that the fibers may be stronger than comparable fibers formed by infusion or by liquid spinning.
The depositing (240, 350) a layer of a material on at least a portion of the exterior surface of a fiber may include any of a variety of methods for depositing a coating material on a fiber. The depositing may include contacting the exterior surface of the thermally degradable fiber with a coating precursor, and then solidifying the coating precursor to form a solid coating on at least a portion of the exterior surface of the fiber. A coating precursor may be any substance that can form a solid polymeric material when solidified. The coating precursor may be substantially homogeneous, or it may include other substances, such as fillers and/or viscosity modifiers.
In one example, a coating precursor includes a monomer and/or prepolymer that can polymerize to form a polymer, such as a polymer as described above with regard to coating 120. The coating precursor may then be solidified by polymerizing the monomer and/or prepolymer of the precursor to form the solid polymeric coating. Examples of monomers and/or prepolymers that can polymerize to form a polymer include cyclic olefins; unsaturated monomers such as acrylates, alkylacrylates (including methacrylates and ethacrylates), styrenes, isoprene and butadiene; lactones (such as caprolactone); lactams; epoxy-functionalized monomers, prepolymers or polymers; functionalized siloxanes; and two-part precursors for polymers such as polyethers, polyesters, polycarbonates, polyanhydrides, polyamides, formaldehyde polymers (including phenol-formaldehyde, urea-formaldehyde and melamine-formaldehyde), and polyurethanes. Polymerization of a coating precursor may include crosslinking of monomers and/or prepolymers to form an insoluble polymer network. Crosslinking may be performed by a variety of methods, including the addition of chemical curing agents and/or exposure to radiation such as infrared radiation (IR; i.e. heat), visible light, or ultraviolet radiation (UV).
In another example, the coating precursor includes a polymer in a solvent. The polymer may be dissolved or dispersed in the solvent to form the coating precursor. The coating precursor may be solidified by removing at least a portion of the solvent from the composition to form the solid polymeric coating.
The depositing (240, 350) a layer of a material on at least a portion of the exterior surface of the fiber may further include applying a surface treatment to the solid polymeric coating. Examples of surface treatments include functionalization of the coating by contacting the coating with an oxidizing or reducing atmosphere or by contacting the coating with a liquid containing a functionalizing reagent. Examples of surface treatments include applying an adhesion promoter to the coating.
In one example, the coating precursor in the bath 420 includes a mixture of a polyimide in a solvent. When the solvent is removed, the resulting coated fiber 406 includes the thermally degradable fiber 402 and a polyimide coating surrounding at least a portion of the thermally degradable fiber. In another example, the coating precursor in the bath 420 includes a mixture of a polyimide and a thermally degradable poly(hydroxyalkanoate) such as PLA in a solvent. When the solvent is removed, the resulting coated fiber 406 includes the thermally degradable fiber 402 and a coating containing both a polyimide and the poly(hydroxyalkanoate), surrounding at least a portion of the thermally degradable fiber.
In one example, the coating precursor in the bath 470 includes a mixture of a polysiloxane precursor and an ultraviolet (UV) initiator in a solvent. When the polysiloxane is cured, the resulting coated fiber 456 includes the thermally degradable fiber 452 and a polysiloxane coating surrounding at least a portion of the thermally degradable fiber.
Composite Materials Including Partially Degradable Polymeric Fibers
The solid polymer matrix 510 may include a polyamide such as nylon; a polyester such as poly(ethylene terephthalate) and polycaprolactone; a polycarbonate; a polyether; an epoxy polymer; an epoxy vinyl ester polymer; a polyimide such as polypyromellitimide (for example KAPTON®); a phenol-formaldehyde polymer such as bakelite; an amine-formaldehyde polymer such as a melamine polymer; a polysulfone; a poly(acrylonitrile-butadiene-styrene) (ABS); a polyurethane; a polyolefin such as polyethylene, polystyrene, polyacrylonitrile, a polyvinyl, polyvinyl chloride and poly(DCPD); a polyacrylate such as poly(ethyl acrylate); a poly(alkylacrylate) such as poly(methyl methacrylate); a polysilane such as poly(carborane-silane); and/or a polyphosphazene.
The solid polymer matrix 510 may include an elastomer, such as an elastomeric polymer, an elastomeric copolymer, an elastomeric block copolymer, and/or an elastomeric polymer blend. Examples of elastomer polymers include polyolefins, polysiloxanes such as poly(dimethylsiloxane) (PDMS), polychloroprene, and polysulfides; examples of copolymer elastomers may include polyolefin copolymers and fluorocarbon elastomers; examples of block copolymer elastomers may include acrylonitrile block copolymers, polystyrene block copolymers, polyolefin block copolymers, polyester block copolymers, polyamide block copolymers, and polyurethane block copolymers; and examples of polymer blend elastomers include mixtures of an elastomer with another polymer. Composite materials that include an elastomer as the solid polymer matrix are disclosed, for example, in U.S. Pat. No. 7,569,625 to Keller et al., and in U.S. Application Publication 2009/0191402 to Beiermann et al., which are incorporated by reference. The solid polymer matrix 510 may include a mixture of these polymers, including copolymers that include repeating units of two or more of these polymers, and/or including blends of two or more of these polymers.
The solid polymer matrix 510 may include other ingredients in addition to the polymeric material. For example, the matrix may contain one or more particulate fillers, stabilizers, antioxidants, flame retardants, plasticizers, colorants and dyes, fragrances, or adhesion promoters. An adhesion promoter is a substance that increases the adhesion between two substances, such as the adhesion between two polymers. One type of adhesion promoter that may be present includes substances that promote adhesion between the solid polymer matrix 510 and the coating 524.
The partially degradable fiber 520, including the thermally degradable polymeric core 522 and the coating 524 surrounding at least a portion of the core, may be as described above for the partially degradable fiber 100. The partially degradable fiber 520 may be configured in a variety of shapes, including a woven shape. In one example, composite 500 includes a woven structure in the solid polymer matrix 510, where the woven structure includes a plurality of partially degradable fibers 520 that are interwoven. In another example, composite 500 includes a woven structure in the solid polymer matrix 510, where the woven structure includes a first plurality of partially degradable fibers, and a second plurality of partially degradable fibers. In this example, each plurality of partially degradable fibers may be as described above for the partially degradable fiber 520. In yet another example, composite 500 includes a woven structure in the solid polymer matrix 510, where the woven structure includes a plurality of partially degradable fibers 520, and a plurality of reinforcing fibers.
When the composite 500 is heated to and maintained at a temperature of from 100 to 250° C., the thermally degradable polymeric core 522 can form degradants that can be removed from the composite 500. Complete degradation of the core 522 and removal of the resulting degradants yields a microvascular system containing the solid polymeric matrix 510 and a microfluidic channel, where the walls of the microfluidic channel are provided by the coating 524.
Microvascular Systems Formed from Partially Degradable Polymeric Fibers
The woven structure 620 includes at least one ply containing at least one plurality of microfluidic channels 630, and may include more than one ply containing microfluidic channels. For a microvascular system that includes the optional second plurality of microfluidic channels (i.e. 640), the woven structure 620 also may include at least one ply containing only the first plurality of microfluidic channels 630 and/or may include at least one ply containing only the second plurality of microfluidic channels 640. Each plurality of microfluidic channels has channel walls including materials that are different from the material of the solid polymeric matrix 610.
The microfluidic channels 630 may include a fluid, such as a gas or a liquid, or they may include a vacuum. The microvascular system 600 may be referred to as an “apomatrix” when the microfluidic channels 630 include a fluid. Without fluid, or with air, microvascular system 600 may be referred to as a “holomatrix”.
A variety of fluids may be present in the microfluidic channels of a microvascular system such as system 600, including aqueous solutions, organic solvents, liquid metals, reactive gases and inert gases. A fluid in the microfluidic channels 630 can flow through one channel and into another channel by way of an interconnect between the channels. An interconnect is present wherever two or more channels are in contact without a channel wall separating the channels. In this manner, interconnects establish fluid communication between the channels. Microfluidic channels 630 that are interconnected thus form a microfluidic network. If the polymeric matrix includes an inlet port, a fluid delivered through the inlet port can flow through interconnected microfluidic channels 630 within the polymeric matrix. If the interconnected microfluidic channels form a network, the introduced fluid may at least partially fill the network.
For a microvascular system that includes the optional second plurality of microfluidic channels (i.e. 640), the first plurality of microfluidic channels 630 and the second plurality of microfluidic channels 640 may be independent, or they may be in fluid communication. Fluid communication between the first and second pluralities of microfluidic channels may be provided by interconnects between channels. Fluid communication between the first and second pluralities of microfluidic channels also may be provided by channels that are in contact, even if the channels are separated by one or more channel walls. The latter type of fluid communication is provided by permeation of a fluid through the channel wall(s).
The nature and/or level of any fluid communication between the first and second plurality of microfluidic channels is affected by the relative configurations of the microfluidic channels. For a first and second plurality of channels that are in fluid communication, it is preferred that at least one channel of each of the pluralities are in physical contact with each other. If the channels are not in physical contact, fluid communication would require permeation of a fluid through the solid polymer matrix, in addition to permeation through the channel wall(s).
The nature and/or level of any fluid permeation between the first and second plurality of microfluidic channels is affected by the properties of their channel walls. In one example, the channel walls of the microfluidic channels 630 are impermeable to a fluid within the channels. An impermeable channel wall may allow substantially no transport of a liquid through the channel wall. For example, the channel wall may include a liquid barrier polymer such as polyethylene, polypropylene, polystyrene, polyamide, polyester, polycarbonate (PC), poly(methyl methacrylate) (PMMA), or poly(vinyl chloride) (PVC). An impermeable channel wall may allow substantially no transport of a gas through the channel wall. For example, the channel wall may include a gas barrier polymer such as isobutylene-isoprene rubber, bromobutyl rubber, chlorobutyl rubber, or poly(tetrafluoroethylene) (PTFE) or other fluoroelastomers.
In another example, the channel walls of the microfluidic channels 630 are permeable to a fluid within the channels. A permeable channel wall may allow a liquid and/or a gas to be transported through the channel wall. For example, the channel wall may include a porous polymeric material conventionally used for ultrafiltration membranes, microfiltration membranes, nanofiltration membranes, or reverse osmosis membranes. Such porous materials may be formed from polymers such as cellulose acetate, polyethylene, polypropylene, PVC, polysulfone, polyamide, polyimide, polysulfone, polyether sulfone, poly(vinylidene fluoride) (PVDF), polyacrylonitrile (PAN), and ion-exchange membrane such as a sulfonated PTFE (for example NAFION® (DuPont)).
The permeability properties of a channel wall material may depend on the chemical nature of the fluid. A channel wall is semi-permeable when it is permeable to some fluids, but impermeable to other fluids. For example, a hydrophobic polymer may be impermeable with regard to aqueous liquids, but may have some permeability with regard to lipophilic liquids such as hydrocarbons. Examples of hydrophobic polymers include polyethylene, polypropylene, PVC, polysulfone, and PTFE. In another example, a hydrophilic polymer may be impermeable with regard to lipophilic liquids, but may have some permeability with regard to aqueous liquids. Examples of hydrophilic polymers include cellulose polymers and poly(vinyl alcohol).
As noted above, the woven structure 620 includes at least one ply containing at least one plurality of microfluidic channels 630. The woven structure 620 may include more than one ply containing microfluidic channels. For a microvascular system that includes the optional fibers (i.e. 640), the woven structure 620 also may include at least one ply containing a plurality of fibers without any microfluidic channels and/or may include at least one ply containing a plurality of microfluidic channels 630 without any fibers. The fibers may be present as tows, also referred to as yarns, which are assemblies of from 100 to 12,000 individual fibers.
Optional fibers (i.e. 640) may include a material having an aspect ratio (diameter:length) of at least 1:10, including at least 1:100 and at least 1:1,000. If present, the optional fibers preferably include reinforcing fibers that, when added to a solid polymer matrix, increase the strength of the matrix relative to the pure polymer. Reinforcing fibers may include an inorganic and/or an organic material. Examples of fibrous reinforcing materials include graphite fibers, ceramic fibers, metal fibers, and polymer fibers. Examples of graphite reinforcing fibers include THORNEL® 25 (Cytec, Tempe, Ariz.) and MODMOR® (Morganite, United Kingdom). Examples of ceramic reinforcing fibers include metal oxide fibers such as titanium oxide fibers, zirconium oxide fibers and aluminum oxide fibers; silica fibers; and glass fibers, such as E-glass fibers and S-glass fibers. Examples of metal fibers include steel fibers, tungsten fibers, beryllium fibers, and fibers containing alloys of these metals. Examples of polymer fibers include polyester fibers, nylon fibers, rayon fibers, and polyaramid fibers, such as KEVLAR® 49 (DuPont).
The woven structure 620 may be a two-dimensional (2D) structure, in which the ply includes threads oriented in two different directions in substantially a single plane. The woven structure 620 may be a three-dimensional (3D) structure, in which the ply includes threads oriented in two different directions in substantially a single plane, and further includes threads oriented in a third direction that is substantially orthogonal to the plane. An individual “thread” in the woven structure 620 may be a microfluidic channel 630 or a structure 640, which may be an individual fiber, a fiber tow, or a microfluidic channel of a second plurality of channels.
The microfluidic channels 630 (and optionally 640) may include substantially tubular channels having a diameter less than 1,000 micrometers. The term “substantially tubular” means that the majority of the cross-sectional periphery of the channel through the substrate matrix is curved in shape. Curved can include circular, elliptic, rounded, arched, parabolic and other curved shapes. The average diameter of the substantially tubular channels preferably is from 0.1 to 1,000 micrometers, from 10 to 750 micrometers, from 20 to 500 micrometers, or from 50 to 250 micrometers. The microfluidic channels 630 may have a length of at least 1 centimeter.
At least a portion of the microfluidic channels 630 can be independent, existing in the matrix 610 without any interconnect with another channel. In one example, all of the microfluidic channels 630 in a microvascular system 600 are independent, and the system does not include a microfluidic network. In this example, any fluid in an individual microfluidic channel 630 is not in fluid communication with a fluid in another microfluidic channel.
The microfluidic channels 630 in the polymeric matrix 610 can affect the structural properties of the matrix, and the type and magnitude of the resulting structural property changes may depend on the properties of the channels and their configuration in the matrix. For example, it may be desirable for the microfluidic channels 630 to have a minimum channel spacing and a maximum channel diameter, which may help to minimize any decrease in the strength of the matrix.
Methods of Making a Microvascular System from Partially Degradable Polymeric Fibers
Forming 710 a composite that includes a solid polymeric matrix and a plurality of partially degradable polymeric fibers in the matrix may include combining a matrix precursor with a plurality of partially degradable polymeric fibers, and then solidifying the matrix precursor to form a solid polymer matrix. The method may further include forming the partially degradable polymeric fibers and/or the matrix precursor.
The matrix precursor may be any substance that can form a solid polymer matrix when solidified. The matrix precursor may be substantially homogeneous, or it may include other substances, such as fillers and/or viscosity modifiers. For example, a matrix precursor may include particles that can change the viscosity of the precursor and/or can change the properties of the polymeric matrix formed from the precursor. Examples of particles that may be present in the matrix precursor include plastic particles and non-plastic particles, such as ceramics, glasses, semiconductors, and metals.
In one example, the matrix precursor includes a monomer and/or prepolymer that can polymerize to form a polymer. The sacrificial fibers and optionally other ingredients may be mixed with the monomer or prepolymer. The matrix precursor may then be solidified by polymerizing the monomer and/or prepolymer of the matrix precursor to form the solid polymer matrix.
Examples of monomers and/or prepolymers that can polymerize to form a polymer include cyclic olefins; unsaturated monomers such as acrylates, alkylacrylates (including methacrylates and ethacrylates), styrenes, isoprene and butadiene; lactones (such as caprolactone); lactams; epoxy-functionalized monomers, prepolymers or polymers; functionalized siloxanes; and two-part precursors for polymers such as polyethers, polyesters, polycarbonates, polyanhydrides, polyamides, formaldehyde polymers (including phenol-formaldehyde, urea-formaldehyde and melamine-formaldehyde), and polyurethanes. Polymerization of a matrix precursor may include crosslinking of monomers and/or prepolymers to form an insoluble polymer network. Crosslinking may be performed by a variety of methods, including the addition of chemical curing agents, exposure to light or other forms of radiation, or heating. If a chemical curing agent is used, it may be added to the matrix precursor before or after it is combined with the sacrificial fibers.
In another example, the matrix precursor includes a polymer in a matrix solvent. The polymer may be dissolved or dispersed in the matrix solvent to form the matrix precursor, and the sacrificial fibers and optionally other ingredients then mixed into the matrix precursor. The matrix precursor may be solidified by removing at least a portion of the matrix solvent from the composition to form the solid polymer matrix.
In another example, the matrix precursor includes a polymer that is at a temperature above its melting temperature. The polymer may be melted to form the matrix precursor and then mixed with the sacrificial fibers and optionally other ingredients. The matrix precursor may be solidified by cooling the composition to a temperature below the melt temperature of the polymer to form the solid polymer matrix.
Forming 710 preferably includes contacting the partially degradable polymeric fibers with a matrix precursor at a temperature below the degradation temperature of the thermally degradable polymeric core. Preferably the partially degradable polymeric fibers are contacted with a matrix precursor at a temperature between 30° C. and 250° C., including temperatures between 50° C. and 200° C., between 75° C. and 175° C., and between 100° C. and 150° C. In one example, forming 710 includes contacting the partially degradable polymeric fibers with a matrix precursor that includes a monomer and/or prepolymer, and heating the matrix precursor and the partially degradable polymeric fibers for a time sufficient to polymerize the monomer and/or prepolymer. In another example, forming 710 includes contacting the partially degradable polymeric fibers with a matrix precursor that includes a polymer that is at a temperature above its melting temperature.
The partially degradable fibers include a thermally degradable polymeric core having a degradation temperature of at most 250° C., and a coating surrounding at least a portion of the core, where at least a portion of the coating does not thermally degrade at temperatures below 275° C. The partially degradable fibers may be as described above for partially degradable fiber 100.
Heating 720 the composite to a temperature of from 100 to 250° C. and maintaining 730 the composite at a temperature of from 100 to 250° C. for a time sufficient to form degradants from the thermally degradable polymeric cores of the partially degradable polymeric fibers may include, for example, placing the composite in an oven. The degradants preferably have an average molecular weight less than 500 Daltons, and preferably are in a gas phase.
Removing 740 the degradants from the composite may include contacting at least a portion of a surface of the composite with a vacuum source. Removing 740 the degradants from the composite may include contacting at least a portion of a surface of the composite with a pressurized fluid, such as a gas. Use of a pressurized fluid or a vacuum may facilitate removal of gaseous degradants. The composite may be maintained at a temperature of from 100 to 250° C. during the removal, or the temperature of the composite may be raised or lowered prior to or during the removal. Removing 740 the degradants from the composite may occur simultaneously with the heating 720 and/or maintaining 730 of the composite, or the removing may occur after the maintaining 730 of the composite.
Optionally introducing 750 a fluid into at least a portion of the microfluidic channels may include any of a variety of methods for introducing a fluid into a microfluidic channel. In one example, the fluid may be injected into one or more channels. In another example, one or more channel openings may be placed in contact with a reservoir of the fluid. The fluid may then flow through the channels through capillary action.
The solid polymer matrix 810 may include a polymeric material, and may include other ingredients in addition to the polymeric material, as described above for solid polymer matrix 510 of
The partially degradable fiber 850 should be strong enough to survive a mechanical weaving process to survive being combined with a matrix precursor. The partially degradable fiber 850 also should remain solid during solidification of the matrix precursor into a polymeric matrix. For solidification by polymerization and/or curing, the partially degradable fiber 850 preferably should remain solid at temperatures up to 180° C. The thermally degradable polymeric core 860 of the partially degradable fiber 850 also should be easily removed from a polymeric matrix by degradation to volatile degradants at higher temperatures. The thermally degradable polymeric core 860 also should have degradation and volatilization temperatures within a narrow range between the highest matrix solidification temperatures and the lowest thermal degradation temperatures of the polymeric matrix (200-240° C.). Preferably, the degradation temperature of the thermally degradable polymeric core 860 is at most 250° C. More preferably, the degradation temperature of the core is at most 220° C., and more preferably is at most 180° C.
The first channel 920 may include a first fluid, and the second channel 930 may include a second fluid different from the first fluid. As channels 920 and 930 are in physical contact, the level of communication between the first and second fluids is determined by the permeabilities of the channel walls 924 and 934. If both channel walls are permeable to both fluids, then the first and second fluids can combine, forming a mixture of the fluids in each channel. If both channel walls are permeable only to the first fluid and/or to an ingredient of the first fluid, then the first fluid may permeate through the channel walls and combine with the second fluid. In this example, the second channel 930 can contain a mixture of the first and second fluids, while the first channel 920 is depleted of the first fluid and/or maintains the first fluid at a reduced fluid pressure. If both channel walls are impermeable to both fluids, then the first and second fluids can flow through their respective microfluidic channels without mixing with each other. The first and second channel walls 924 and 934 may include the same polymer, or they may include different polymers.
The microvascular system 900 may be formed from a composite material 940 including the solid polymeric matrix 910, a first partially degradable fiber 950 in the solid polymeric matrix, and a second partially degradable fiber 960 in the solid polymeric matrix. The first partially degradable fiber 950 includes a first thermally degradable polymeric core 952 and a first coating 954 surrounding at least a portion of the core. The second partially degradable fiber 960 includes a second thermally degradable polymeric core 962 and a first coating 964 surrounding at least a portion of the core. The microvascular system 900 may be formed from the composite material 940 by heating the composite to a temperature of from 100 to 250° C., maintaining the composite at a temperature of from 100 to 250° C. for a time sufficient to form degradants from the thermally degradable polymeric cores 952 and 962, and removing the degradants from the composite to provide microfluidic channels 920 and 930.
The first and second thermally degradable polymeric cores 952 and 962 may include the same polymer, or they may include different polymers. Preferably the first and second cores are the same material, as this can provide for removal of both cores simultaneously. The first and second coatings 924 and 934 may include the same polymer, or they may include different polymers.
The composite material 940 may be formed by placing the first partially degradable fiber 950 and the second partially degradable fiber 960 in a desired configuration, contacting the fibers with a matrix precursor, and solidifying the matrix precursor to form the polymeric matrix 910. The partially degradable fibers (i.e. 950) may be formed by depositing a coating 954 on at least a portion of an external surface of a thermally degradable polymeric fiber 952.
Forming 1010 a composite that includes a solid polymeric matrix and a woven structure in the matrix may include combining a matrix precursor with the partially degradable polymeric fibers, and then solidifying the matrix precursor to form a solid polymer matrix. The method may further include forming the partially degradable polymeric fibers and/or the matrix precursor.
Forming 1010 may include forming the woven structure by weaving the plurality of partially degradable polymeric fibers to form a single ply. In one example, an arrangement of warp threads in a first orientation may be held in tension, and weft threads then may be directed sinusoidally in a second orientation through the warp threads. Preferably the second direction is transverse to the first orientation. In this example, the resulting ply is a 2D woven structure.
In another example, an arrangement of warp threads in a first orientation may be held in tension. Weft threads then may be directed in a second orientation over, under and/or through the warp threads, where the second direction preferably is transverse to the first orientation. Z-threads then may be directed through the warp and weft threads, preferably in an orientation that is orthogonal to a plane formed by the weft and warp threads. The Z-threads may be directed through the weft and warp threads sinusoidally. The warp, weft and/or Z-threads may include partially degradable polymeric fibers. In this example, the resulting ply is a 3D woven structure.
Forming 1010 may include forming the woven structure by weaving the plurality of partially degradable polymeric fibers with a second plurality of partially degradable polymeric fibers and/or with reinforcing fibers to form a single ply. In one example, the warp threads may include the plurality of partially degradable polymeric fibers, and the weft threads may include a second plurality of partially degradable polymeric fibers and/or reinforcing fibers. In another example, the warp threads may include a second plurality of partially degradable polymeric fibers and/or reinforcing fibers, and the weft threads may include the plurality of partially degradable polymeric fibers. In these examples, the resulting plies are 2D woven structures.
In another example, an arrangement of warp threads in a first orientation may be held in tension, weft threads then may be directed in a second orientation over, under and/or through the warp threads, where the second direction preferably is transverse to the first orientation, and Z-threads then may be directed through the warp and weft threads, preferably in an orientation that is orthogonal to a plane formed by the weft and warp threads. The Z-threads may be directed through the weft and warp threads sinusoidally. At least one of the warp, weft and/or Z-threads may include the partially degradable polymeric fibers, and the remaining threads may include a second plurality of partially degradable polymeric fibers and/or reinforcing fibers. In this example, the resulting ply is a 3D woven structure.
Forming 1010 may include inserting the plurality of partially degradable polymeric fibers into a ply of woven a second plurality of partially degradable polymeric fibers and/or reinforcing fibers. In one example, a partially degradable polymeric fiber is stitched into a woven ply of fibers, such as by repeatedly piercing the ply with a needle attached to a partially degradable polymeric fiber, and forming a sinusoidal trace of the partially degradable polymeric fiber that traverses the thickness of the ply. In this example, a pattern of the first plurality of partially degradable polymeric fibers may be formed along the length and width of the woven ply.
In one example, the plurality of partially degradable polymeric fibers and a second plurality of partially degradable polymeric fibers and/or reinforcing fibers may be arranged into two- or three-dimensional woven preforms. The position, length, diameter, and curvature of the partially degradable polymeric fibers and/or reinforcing fibers may be varied to meet desired design criteria.
Forming 1010 includes combining the partially degradable polymeric fibers and a matrix precursor. The matrix precursor may be as described with regard to forming 710 of
Heating 1020 the composite to a temperature of from 100 to 250° C. and maintaining 1030 the composite at a temperature of from 100 to 250° C. for a time sufficient to form degradants from the thermally degradable polymeric cores may include, for example, placing the composite in an oven. The degradants preferably have an average molecular weight less than 500 Daltons, and preferably are in a gas phase. Removing 1040 the degradants from the composite may include contacting at least a portion of a surface of the composite with a vacuum source or with a pressurized fluid. The heating 1020, maintaining 1030 and removing 1040 may be as described above for heating 720, maintaining 730 and removing 740 of
Optionally introducing 1050 a fluid into at least a portion of the microfluidic channels may include any of a variety of methods for introducing a fluid into a microfluidic channel, as described above for introducing 750 of
The presence of partially degradable polymeric fibers in a woven fiber preform can provide seamless fabrication of microvascular composites that are both strong and multifunctional. Preferably the hollow channels produced in the composites are high-fidelity inverse replicas of the original fibers' diameters and trajectories. Use of methods 700 and/or 1000 can provide microvascular fiber-reinforced composites with channels over one meter in length that then can be filled with a variety of fluids including aqueous solutions, organic solvents, and liquid metals.
Methods 700 and 1000 are examples of a method referred to as Vaporization of Sacrificial Components (VaSC). The VaSC methods can provide composite materials that include microfluidic channels having a range of channel curvatures and diameters, allowing the construction of a wide variety of network architectures. The methods also can provide composite materials that include microfluidic channels that are interconnected and/or branched.
When incorporated into a matrix of another material, a thermally degradable polymeric core containing a poly(hydroxyalkanoate) including an alkali earth metal or a transition metal, where the concentration of the metal in the fiber matrix is at least 0.1 wt %, preferably may be removed by heating at 200° C. The heating and removal may occur over the course of several minutes to several hours. Preferably the heating and removal are completed in at most 24 hours, at most 5 hours, at most 3 hours, or at most 2 hours. Details regarding the formation, degradation and removal of poly(hydroxyalkanoate) fibers is described, for example, in U.S. patent application Ser. No. 13/416,002, filed Mar. 9, 2012, with inventors Esser-Kahn et al., which is incorporated herein by reference.
The clearing of lactide from channels formed by degradation of PLA fibers including an alkali earth metal or a transition metal typically may result in a very low number of obstructions. Hidden defects in the channels may be present, and may be caused by complex channel geometries. Defects may be detected by calculating a theoretical value for pressure drop according to the Hagen-Pouiselle relation and comparing the prediction with a measured pressure head for the channels. A negligible difference from between these values indicates geometric uniformity and substantially complete channel clearing.
Partially degradable polymeric fibers having a thermally degradable polymeric core that includes a poly(hydroxyalkanoate) including an alkali earth metal or a transition metal, where the concentration of the metal in the fiber matrix is at least 0.1 wt %, preferably are compatible with fiber preform fabrication. Preferably the single fiber tension strength of a partially degradable polymeric fiber exceeds the threshold stress of 23 MPa applied during automated weaving. Preferably the single fiber tension strength of a partially degradable polymeric fiber is at least 30 MPa, at least 50 MPa, at least 75 MPa, or at least 100 MPa.
Uses of Microvascular Systems
Microvascular networks capable of independent fluid flow and/or controlled mixing between fluids are relevant for a range of applications in microfluidics and self-healing systems. A variety of properties may be obtained with a single microvascular system by selection of one or more fluids for introduction to the microchannels. The variation in properties can be obtained without varying the composite's form factor. Examples of materials properties that may be affected by the fluid in the microchannels of the composites include thermal management, electro-magnetic signature, electrical conductivity tuning, and chemical reactivity.
A microvascular system that includes independent microfluidic channels having independent fluid flow may include modified surfaces within some or all of the microfluidic channels. For example, one plurality of interconnected microfluidic channels in a system may have a hydrophilic surface at the interior of its channel walls, while another plurality of interconnected microfluidic channels in a system may have a hydrophobic surface at the interior of its channel walls. Hydrophilic and/or hydrophobic surfaces at the interior of microfluidic channel walls may be formed by any of a variety of known techniques, including those listed above with regard to applying a surface treatment to the solid polymeric coating as part of the depositing (240, 350). Hydrophilic and/or hydrophobic surfaces at the interior of microfluidic channel walls may be formed using photocleavable self-assembled monolayers (SAMs) as described in Zhao et al., J. Am. Chem. Soc. 124(19), 2002, 5284-85. It may also be desirable to modify the interior of microfluidic channels in microvascular systems that do not include independent channels.
One example of a microvascular system having permeable channel walls is a water purification system. A microvascular water purification system includes a first plurality of microfluidic channels and a second plurality of microfluidic channels, where the first and second channels are separated by channel walls containing a nanoporous polymer. A first stream of water having a high concentration of dissolved salts is introduced into the first plurality of channels and flows through the first channels as a pressure is applied. A second stream of water having a low or negligible concentration of dissolved salts is introduced into the second plurality of channels. The osmotic pressure difference between the two liquids causes water to pass from the second stream into the first stream, diluting the first stream and reducing the concentration of dissolved salts in the first stream.
Another example of a microvascular system having permeable channel walls is an energy production system. An energy production system includes a first plurality of microfluidic channels and a second plurality of microfluidic channels, where the first and second channels are separated by channel walls containing an ionic separator. A cathode fluid is introduced into the first plurality of channels and flows through the first channels as a pressure is applied. An anode fluid is introduced into the second plurality of channels and flows through the second channels as a pressure is applied. Ions can pass between the fluids through the ionic separator, creating a flow of charge that can be collected on the opposite sides of the first and second pluralities of microfluidic channels. The collected charge flow can then be converted into a conventional electrical current.
Microporous Films
It has also been discovered that microporous films may be made from coating precursors that include a thermally degradable polymeric material and a thermally stable material having a degradation temperature higher than the degradation temperature of the thermally degradable polymeric material. A coating precursor is cast into a film that is subject to depolymerization of the thermally degradable polymeric material, to produce a microporous film. Preferably, the microporous film has a thickness of from 3 μm to 50 μm, and more preferably of from 5 μm to 30 μm. Preferred average pore sizes are between 50 nm to 10 μm, and more preferred average pore sizes range between 100 nm to 5 μm.
The thermally degradable polymeric material preferably has a degradation temperature below 280° C., and preferably has a degradation temperature of at most 250° C. Preferably the thermally degradable polymeric material has a degradation temperature between 100 and 250° C. Preferably the thermally degradable polymeric material has a degradation temperature of at most 220° C., of at most 180° C., of at most 150° C., or of at most 100° C. The thermally degradable polymeric material may include a poly(hydroxyalkanoate). Examples of poly(hydroxyalkanoate)s include poly(3-hydroxybutyrate) (P3HB), poly(4-hydroxybutyrate) (P4HB), poly(3-hydroxy-valerate) (PHV), polycaprolactone, poly(lactic acid) (PLA), poly(glycolic acid) (PGA), and copolymers of the monomeric units of these polymers.
Preferably the poly(hydroxyalkanoate) has a weight average molecular weight (Mw) of at least 2,000, and a degradation temperature below 280° C. More preferably, the poly(hydroxyalkanoate) has a degradation temperature of at most 250° C. Optionally, the depolymerization temperature of poly(hydroxyalkanoate)s such as PLA may be reduced by blending the poly(hydroxyalkanoate) with an alkaline earth metal and/or a transition metal. Preferably, the concentration of the metal in the film is at least 0.1 percent by weight (wt %). Preferably the concentration of the metal in the film is at least 0.2 wt %, at least 0.5 wt %, at least 1 wt %, at least 2 wt %, at least 2.5 wt %, at least 3 wt %, at least 5 wt %, at least 7 wt %, or at least 10 wt %. The concentration of the metal in the film may be from 0.1 to 10 wt %, from 0.2 to 7 wt %, from 0.5 to 5 wt %, or from 1 to 3 wt %. Preferably the metal is present in the film as MgO, CaO, BaO, SrO, tin(II) acetate, tin(II) oxalate, tin(II) octoate, or scandium triflate (Sc(OTf)3). More preferably the metal is present in the film as strontium oxide, tin(II) oxalate or tin(II) octoate.
When the film is heated to the degradation temperature of the thermally degradable polymeric material, the thermally degradable polymeric material will degrade to form degradants that can be removed, providing a microporous film containing the thermally stable material. In instances where the thermally degradable polymeric material has a degradation temperature of at most 250° C., the thermally stable material does not thermally degrade at temperatures below 250° C. Preferably, the thermally stable material does not thermally degrade at temperatures below 275° C., at temperatures below 280° C., at temperatures below 300° C., at temperatures below 325° C., or at temperatures below 350° C.
The thermally stable material may include a thermally stable polymeric material having a degradation temperature higher than the degradation temperature of the poly(hydroxyalkanoate), for example a polyamide such as nylon; a polyester such as poly(ethylene terephthalate) and polycaprolactone; a polycarbonate; a polyether; an epoxy polymer; an epoxy vinyl ester polymer; a polyimide such as polypyromellitimide (for example KAPTON®); a phenol-formaldehyde polymer such as bakelite; an amine-formaldehyde polymer such as a melamine polymer; a polysulfone; a poly(acrylonitrile-butadiene-styrene) (ABS); a polyurethane; a polyolefin such as polyethylene, polystyrene, polyacrylonitrile, a polyvinyl, polyvinyl chloride and poly(DCPD); a polyacrylate such as poly(ethyl acrylate); a poly(alkylacrylate) such as poly(methyl methacrylate); a polysilane such as poly(carborane-silane); and/or a polyphosphazene.
The thermally stable polymeric material may include an elastomer, such as an elastomeric polymer, an elastomeric copolymer, an elastomeric block copolymer, and/or an elastomeric polymer blend. Examples of elastomer polymers include polyolefins, polysiloxanes such as poly(dimethylsiloxane) (PDMS), polychloroprene, and polysulfides; examples of copolymer elastomers may include polyolefin copolymers and fluorocarbon elastomers; examples of block copolymer elastomers may include acrylonitrile block copolymers, polystyrene block copolymers, polyolefin block copolymers, polyester block copolymers, polyamide block copolymers, and polyurethane block copolymers; and examples of polymer blend elastomers include mixtures of an elastomer with another polymer.
The thermally stable material may include other ingredients in addition to the thermally stable polymeric material. For example, the thermally stable material may contain one or more particulate fillers, stabilizers, antioxidants, flame retardants, plasticizers, colorants and dyes, fragrances, or adhesion promoters. One type of adhesion promoter that may be present includes substances that promote adhesion between the thermally stable material and the thermally degradable material, and substances that promote adhesion between the thermally stable material and a polymeric matrix in which the thermally degradable material is contained.
In instances where the thermally stable material includes a polyimide, the Mw of the polyimide is at least 2,000. Soluble polyimides are preferred, such as the commercially available MATRIMID® 5218 (Lindberg & Lund A S, Ski, Norway) P84® (Evonik Industries, Essen, Germany), and mixtures thereof. Microporous polyimide films, such as the PI films of
Methods of Making Microporous Films
Preferably, the coating precursor is solidified at a temperature below the degradation temperature of the thermally degradable poly(hydroxyalkanoate). The solidification of the coating precursor to form a film may include removal of solvent from the precursor and/or chemical reaction (i.e. curing) of the precursor. Examples of solidification temperatures include 30° C., 50° C., 75° C., 100° C., 125° C., 150° C. and 180° C. Optionally, a surface treatment may be applied to the film. Examples of surface treatments include functionalization of the film by contacting the film with an oxidizing or reducing atmosphere or by contacting the film with a liquid containing a functionalizing reagent. Examples of surface treatments include applying an adhesion promoter to the film.
Method 2200 further includes heating 2224 the film to a temperature of from 100 to 250° C., maintaining 2226 the film at a temperature of from 100 to 250° C. for a time sufficient to form degradants from the poly(hydroxyalkanoate), and removing 2228 the degradants from the film to provide a microporous film. The degradants preferably have an average molecular weight less than 500 Daltons. Method 2220 may also include interposing 2232 the product microporous film between the positive electrode and the negative electrode of an energy-storage device, such as a lithium ion battery, to provide a separator between the positive electrode materials and the negative electrode materials.
The depolymerization temperature of poly(hydroxyalkanoate)s such as PLA may be reduced by the presence in the film of an alkaline earth metal and/or a transition metal. Preferably the concentration of the metal in the film is at least 0.2 wt %, at least 0.5 wt %, at least 1 wt %, at least 2 wt %, at least 2.5 wt %, at least 3 wt %, at least 5 wt %, at least 7 wt %, or at least 10 wt %. The concentration of the metal in the film may be from 0.1 to 10 wt %, from 0.2 to 7 wt %, from 0.5 to 5 wt %, or from 1 to 3 wt %. Preferably the metal is present in the film as MgO, CaO, BaO, SrO, tin(II) acetate, tin(II) oxalate, tin(II) octoate, or scandium triflate (Sc(OTf)3). More preferably the metal is present in the film as strontium oxide, tin(II) oxalate or tin(II) octoate.
In one example, a metal selected from the group consisting of an alkali earth metal and a transition metal may be included in the coating precursor. In another example, method 2220 may include incorporating 2230 the metal in the film through an infusion process. A representative infusion process includes contacting the film with a composition including a fluorinated fluid, and a metal selected from the group consisting of an alkali earth metal and a transition metal, maintaining the film and the composition together at a temperature and for a time sufficient to provide a concentration of the metal in the film of at least 0.1 wt %, and separating the film and the fluorinated fluid. In one example, films may be infused with a tin(II) oxalate (SnOx) catalyst present in an aqueous trifluoroethanol (TEE) mixture.
In a set of representative examples, a coating precursor includes a monomer and/or prepolymer that can polymerize to form a polymer, such as a thermally stable polymer as described above with regard to the thermally stable polymeric material. The coating precursor may then be solidified by polymerizing the monomer and/or prepolymer of the precursor to form the film. Examples of monomers and/or prepolymers that can polymerize to form a polymer include cyclic olefins; unsaturated monomers such as acrylates, alkylacrylates (including methacrylates and ethacrylates), styrenes, isoprene and butadiene; lactones (such as caprolactone); lactams; epoxy-functionalized monomers, prepolymers or polymers; functionalized siloxanes; and two-part precursors for polymers such as polyethers, polyesters, polycarbonates, polyanhydrides, polyamides, formaldehyde polymers (including phenol-formaldehyde, urea-formaldehyde and melamine-formaldehyde), and polyurethanes. Polymerization of a coating precursor may include crosslinking of monomers and/or prepolymers to form an insoluble polymer network. Crosslinking may be performed by a variety of methods, including the addition of chemical curing agents and/or exposure to radiation such as infrared radiation (IR; i.e. heat), visible light, or ultraviolet radiation (UV).
The following examples are provided to illustrate one or more preferred embodiments of aspects of the present application. Numerous variations can be made to the following examples that lie within the scope of the present application.
Materials & Procedures
PLA pellets (Mw=339,000) for forming fibers by solution spinning were used as received from Purac Biomaterials. Catalyst tin(II) octoate was obtained from Sigma-Aldrich. Trifluoroethanol (TEE) was obtained from Halogen Inc. Polyimide resin was obtained from Alfa Aesar. Other chemicals were all obtained from Sigma-Aldrich unless otherwise noted.
Diglycidyl ether of bisphenol A resin (DGEBA or EPON® 828 was used as received from Miller-Stephenson (Danbury, Conn.), and the curing agent EPIKURE® 3300 was used as received from Hexion (Columbus, Ohio). Epoxy samples were prepared using a mass ratio of 22.7 parts per hundred (pph) EPIKURE® 3300 to EPON® 828.
Fiber surface morphology and fiber removal in epoxy matrices were imaged using a Leica DMR Optical Microscope at various magnifications. Image) software was used to measure fiber diameters from acquired images for each batch of fibers produced and to measure the fraction of PLA fiber removed.
Environmental Scanning Electron Microscopy (ESEM, Philips XL30ESEM-FEG) was used to image cross-sections of the holomatrix and to image empty channels. SEM images were acquired after sputter-coating the sample surface with carbon or gold-palladium, and were collected using backscattered electrons. Selected area elemental analysis was performed by EDS (Energy Dispersive X-ray Spectroscopy, attached to the SEM) with a 20 kV electron source and spot size of 3.0 nm.
An Xradia BioCT (MicroXCT-400) was used to image the apomatrix at 40 keV (8 W power and 200 μA current) at a 4× objective for 5 s exposure times. Rotation intervals were 0.25° for a complete 360° scan. Images were visualized in 3D with XM3Dviewer and reconstructed in 3D using XMReconstructor. Reconstructed images were reproduced in Amira to enhance the color and contrast.
A PLA solution was prepared by dissolving 6 g of PLA pellets in dichloromethane at room temperature, and then removing solvent to provide a solution volume of 35 mL. Catalysts (tin(II) oxalate particles or tin(II) octoate liquid) were blended into the viscous PLA solution to provide a 10 wt % tin equivalence to PLA. The mixture was stirred for half an hour to disperse the catalyst, resulting in a spinning solution.
A spin chamber was pre-heated to 55° C., and 10 mL of the spinning solution was transferred to the chamber. The solution was conditioned in the spin chamber for 5 minutes, and then conditioned outside the chamber for additional 5 minutes before extrusion, allowing the solution to become more concentrated. The spinning solution was then extruded at 55° C. through the chamber at an extrusion speed of 8 cm/hr. The solution passed through a spinneret having a diameter from 0.2 mm to 1 mm, forming a single fiber. Two heating chambers below the spinneret provided additional heat to further evaporate the solvent. The extruded fiber filament was collected on a Teflon bobbin without applying additional stress, and was then air-dried at 50° C. The diameter of the fibers after drying was dependent on the diameter of the spinneret used in the spinning process. A spinneret diameter of 0.25 mm provided a final fiber diameter of 0.14±0.02 mm, a spinneret diameter of 0.50 mm provided a final fiber diameter of 0.42±0.03 mm, and a spinneret diameter of 1.00 mm provided a final fiber diameter of 0.75±0.05 mm.
SEM analysis of the fibers confirmed a uniform distribution of the SnOc in the spun PLA fiber, which is believed to provide a uniform catalyzed depolymerization reaction upon heating, resulting in rapid clearing of the channel formed from degradation and removal of the fiber core.
The mechanical properties of the spun PLA fibers could be changed by cold-drawing the spun fibers. Cold-drawing fibers may provide an increase in tensile strength, which is theorized to be due to alignment of the individual polymer chains within the fiber during the drawing process. WAXS analysis of PLA fibers that were cold-drawn after being spun was consistent with an increase in polymer chain alignment within these fibers, as the degree of orientation of pure spun PLA fiber (no catalyst) increased from 0% when no drawing was performed to 23% when cold-drawing was performed. Spun PLA fibers were drawn to different draw ratios, and their failure strengths were studied by a single fiber tension test. Cold-drawing appeared to significantly increase the fiber strength, whereas the presence of SnOc catalyst did not appear to affect fiber failure strength significantly. As the measured fiber failure strengths were greater than 23 MPa, the fibers were expected to survive the weaving process without significant failure.
Thermally degradable PLA fibers according to Example 1 were coated with a polysiloxane. A thermally degradable PLA fiber was unwound using a tensioner, and then passed through a bath containing a coating precursor containing a liquid copolymer of dimethylsiloxane (DMS) and (epoxycyclohexyl)ethylmethylsiloxane (ECMS), and containing the cationic polymerization initiator (p-isopropylphenyl)(p-methlyphenyl) iodonium tetrakis(pentafluorophenyl)borate. The cationic initiator can initiate the reaction of the epoxy groups in the poly(ECMS-co-DMS) when subjected to UV irradiation.
The fiber was then pulled through a syringe needle tip that had an inner diameter greater than the diameter of the fiber, providing a uniform layer of the coating precursor on the exterior surface of the fiber. UV radiation was then applied to the coating precursor on the fiber, curing the poly(ECMS-co-DMS) into a crosslinked polysiloxane. The resulting coated fiber was collected on a take-up drum.
The thickness of the coating correlated with the difference between the fiber diameter and the inner diameter of the syringe needle tip through which the fiber was pulled after passing through the bath. Table 1 lists a variety of fiber diameters, syringe needle tip inner diameters, and resulting coated fiber diameters.
The thickness of the coating was relatively uniform along the length of the coated fiber.
Coated fibers according to Example 2 were embedded in an EPON® 828: EPIKURE® 3300 epoxy thermoset matrix. The coated fibers were held straight in RTV Silicone molds before filling the mold with epoxy. EPON® 828 epoxy resin and a cycloaliphatic amine curing agent EPIKURE® 3300 were mixed at a ratio of 100:22.7 parts by weight and degassed until air bubbles ceased to form. The post-curing cycle involved heating the specimens at 82° C. for 90 minutes followed by 150° C. for an additional 90 minutes. The cured epoxy thermoset composites were carefully trimmed before thermal treatment to expose fiber ends.
A composite was formed according to Example 3, where the composite included the epoxy thermoset matrix, and two coated PLA fibers in the matrix. The two coated fibers each included a thermally degradable PLA core and a polysiloxane coating. The two coated fibers were arranged perpendicularly and in physical contact at their intersection. After the epoxy was cured, the composite was heated in a sealed vacuum oven (Fisher Isotemp 283) at 200° C. under vacuum (1 torr) for 2 hours, resulting in degradation and removal of the PLA fiber cores.
A composite was formed according to Example 3, except that the solid polymer matrix was poly(dimethylsiloxane) (PDMS) formed using the two-component siloxane kit Sylgard® 184 (DOW CORNING), which contained a mixture of hydroxyl terminated polydimethylsiloxane (HOPDMS) with polydiethylsiloxane (PDES). The composite included the PDMS matrix and two coated PLA fibers in the matrix. The two coated fibers each included a thermally degradable PLA core and a polysiloxane coating. The two coated fibers were in physical contact along the length at which the fibers were interwoven. After the PDMS was cured, the composite was heated in a sealed vacuum oven (Fisher Isotemp 283) at 200° C. under vacuum (1 torr) for 2 hours, resulting in degradation and removal of the PLA fiber cores.
A coating precursor was formed from a mixture of PLA and the polyester poly(ethylene terephthalate) (PET). A liquid mixture was prepared containing 6 weight percent (wt %) PET and 4 wt % PLA in a solvent that was a 70:30 mixture of dichloromethane and trifluoroacetic acid. The liquid mixture was cast into a film by spin-coating at 500 rpm. The film was then soaked in dichloromethane to remove the PLA.
A coating precursor was formed from a mixture of PLA and a polyimide. The polyimide was a soluble thermoplastic polyimide having a chemical name of 1,3-isobenzofurandione, 5,5′-carbonylbis-, polymer with 1- (or 3-) (4-aminophenyl)-2,3-dihydro-1,3,3 (or 1,1,3)-trimethyl-1H-inden-5-amine (CAS#62929-02-6). A solution was prepared containing from 1-2 wt % polyimide and from 1-1.5 wt % PLA in chloroform. The solution was cast into a film either by spin-coating or by contacting a layer of the solution with a doctor blade. The resulting polymer blend film had a thickness of from 5 to 30 μm.
In another example, a coating precursor was formed from a mixture of PLA and a polyimide in a binary solvent. A solution was prepared containing from 1-2 wt % polyimide and from 1-1.5 wt % PLA in a solvent that was a 10:1 mixture of chloroform and dioxane. As described above, the solution was cast into a film and heated in a sealed vacuum oven (Fisher Isotemp 283) at 200° C. under vacuum (1 torr) for 2 hours, resulting in degradation and removal of the PLA phase.
The coating precursor of Example 6 was formed as solution having a PI:PLA ratio 40:60 (wt/wt) in chloroform. The PI was a 1,3-isobenzofurandione having a molecular weight of about 38 kDa, and the PLA of about 55 KDa. The solution was cast into a film either by spin coating or by contacting a film of the solution with a doctor blade, and the film was left to dry for 10 minutes. The resulting polymer blend film was heated in a sealed vacuum oven to a temperature of 280° C., removing the PLA and resulting in microporous polyimide films having a thickness of 5 to 30 μm.
Button lithium-ion cells were prepared with a mesocarbon microbeads (MCMB) graphite powder (Enerland, Korea) as anode material, Li(Ni1/3Co1/3Mn1/3)O2 (NMC) as cathode material, and LiPF6 in ethylene carbonate (EC) as solvent. Cathodes and anodes were cut to the appropriate size using a 1.59 punch. A first set of batteries featured microporous polyimide separators having a thickness of 20 μm, and a second set of control batteries were fitted with CELGARD® 2325 (Celgard, Charlotte, N.C.), a type of traditional, commercially available trilayer (PP/PE/PP) separator membranes. The cells with the microporous polyimide separator exhibited impedance and discharge capacity values very close to those of coin cells featuring the Celgard® 2325. This is illustrated in the linear sweep voltammograms (LSV) of
The thermal shrinkage of the microporous polyimide separators was assessed by changes in size (as measured by length and width) following heat treatment at various temperatures for 30 minutes.
A coating precursor was formed from a mixture of a soluble polyimide (Matrimid® 5218, number average molecular weight (Mn) 38,000; Mw 73,000) and PLA having a Mn of 55,400 (Natureworks, Minnetonka, Minn.). A solution was prepared containing 2-2.5 wt % polyimide, 1-1.5 wt % PLA, and 0.2-0.4 wt % tin(II) octoate in chloroform. Sacrificial fibers were dip-coated with the solution, leaving a coating containing a mixture of phase-separated polyimide and PLA.
In another example, sets of two PLA fibers held at a fixed proximity were dip-coated into a solution containing 2-2.5 wt % PI, 1-1.5 wt % PLA, and 0.2-0.4 wt % tin(II) octoate in chloroform.
To provide a clear and more consistent understanding of the specification and claims of this application, the following definitions are provided.
The term “polymeric” means a substance that includes a polymer.
The term “polymer” means a substance containing more than 100 repeat units. The term “polymer” includes soluble and/or fusible molecules having long chains of repeat units, and also includes insoluble and infusible networks. The term “prepolymer” means a substance containing less than 100 repeat units and that can undergo further reaction to form a polymer. Unless otherwise specified, polymer molecular weights are given in Daltons.
The term “matrix” means a continuous phase in a material.
The term “matrix precursor” means a composition that will form a polymer matrix when it is solidified. A matrix precursor may include a monomer and/or prepolymer that can polymerize to form a solid polymer matrix. A matrix precursor may include a polymer that is dissolved or dispersed in a solvent, and that can form a solid polymer matrix when the solvent is removed. A matrix precursor may include a polymer at a temperature above its melt temperature, and that can form a solid polymer matrix when cooled to a temperature below its melt temperature.
The term “woven structure” means a single ply of an assembly of threads, where the threads are oriented in at least 2 directions within the ply.
The term “microfluidic channel” means a substantially tubular structure having a diameter less than 1,000 micrometers.
The term “microfluidic network” means a plurality of channels having a plurality of interconnects, where at least a portion the channels have a dimension less than 1,000 micrometers.
The term “fluid communication” means that two objects are in an orientation, and within a sufficient proximity to each other, such that fluid can flow from one object to the other. The term “fluid” means a substance in the liquid or gaseous state. In one example, if a microfluidic channel embedded in a matrix is in fluid communication with a surface of the matrix, then fluid can flow from the channel onto the surface.
While various embodiments of the present application have been described, it will be apparent to those of ordinary skill in the art that other embodiments and implementations are possible within the scope of the present application. Accordingly, the present application is not to be restricted except in light of the attached claims and their equivalents.
This application claims the benefit of U.S. Provisional Application No. 61/708,149 entitled “Partially Degraded Fibers And Microvascular Materials Formed From The Fibers” filed Oct. 1, 2012, which is incorporated by reference in its entirety.
This invention was made with government support under contract numbers FA9550-10-1-0255, awarded by the Air Force Office of Scientific Research, and DOE ANL 9F-31921, awarded by the Energy Frontier Research Centers (EFRC). The government has certain rights in the invention.
| Number | Name | Date | Kind |
|---|---|---|---|
| 6766817 | da Silva | Jul 2004 | B2 |
| 7569625 | Keller et al. | Aug 2009 | B2 |
| 20030119398 | Bogdanovich | Jun 2003 | A1 |
| 20070087198 | Dry | Apr 2007 | A1 |
| 20080003433 | Mikami | Jan 2008 | A1 |
| 20080305343 | Toohey | Dec 2008 | A1 |
| 20090191402 | Beiermann et al. | Jul 2009 | A1 |
| 20130065042 | Esser-Kahn et al. | Mar 2013 | A1 |
| Number | Date | Country |
|---|---|---|
| 2007005657 | Jan 2007 | WO |
| Entry |
|---|
| Esser-Kahn, A. P., Thakre, P. R., Dong, H., Patrick, J. F., Vlasko-Vlasov, V. K., Sottos, N. R., Moore, J. S. and White, S. R. (2011), Three-Dimensional Microvascular Fiber-Reinforced Composites. Adv. Mater., 23: 3654-3658. doi:10.1002/adma.201100933, Published Jul. 15, 2011. |
| Celgard, LLC; Polypore Company, “Celgard 2325—Product Information”, 2012, Publisher: Celgard, LLC.; A Polypore Company. |
| E.I. Du Pont De Nemours and Company, “DuPont Kapton: Polyimide Film”, 2012, Publisher: E.I. du Pont de Nemours and Company. |
| E.I. Du Pont De Nemours and Company, “DuPOnt Fuel Cells: DuPont Nafion PFSA Membranes”, 2009, Publisher: E.I. du Pont de Nemours and Company. |
| Momentive Specialiaty Chemicals Inc., “EPON Resin 828”, 2005, Publisher: Momentive Specialiaty Chemicals Inc. |
| De Espinosa, Lucan Montero et al., “Plant oils: The perfect renewable resource for polymer science?!”, 2011, pp. 837-852, vol. 47, Publisher: European Polymer Journal. |
| OSHA and ANSI, “Material Safety Data Sheet—According to OSHA and ANSI”, May 28, 2011, Publisher: OSHA and ANSI. |
| Momentive Technical Data Sheet, “Epikure Curing Agent 3300”, Aug. 2007, Publisher: Momentive Specialiaty Chemicals Inc. |
| Momentive Specialiaty Chemicals Inc., “Epikure Epoxy Curing Agents”, 2013, Publisher: Momentive Specialty Chemicals Inc. |
| Bin Zhao et al., “Control and Applications of Immiscible Liquids in Microchannels”, 2002. |
| Toohey, Kathleen S. et al., “Delivery of Two-Part Self-Healing Chemistry via Microvascular Networks,” Advanced Functional Materials, vol. 19, 2009, pp. 1399-1405. |
| Toohey, Kathleen S. et al., “Self-Healing Materials With Microvascular Networks,” Nature Materials, vol. 6, Aug. 2007, pp. 581-585. |
| Number | Date | Country | |
|---|---|---|---|
| 20140162519 A1 | Jun 2014 | US |
| Number | Date | Country | |
|---|---|---|---|
| 61708149 | Oct 2012 | US |