Patent Application
20210144994
The present disclosure relates to particles with an antimicrobial surface. Various embodiments of the teachings herein include materials for producing a coating and/or processes for producing particles having an antimicrobial surface.
Surfaces having an antimicrobial action have hitherto been formed by spherical particles. Here, the antimicrobially acting metals, metal oxides or metal oxide mixtures are frequently processed to give nanoparticles and then mixed into paints, surface coating compositions or polymer materials. These antimicrobially acting particles can utilize the UV component of light in order to form germ-killing materials. On the other hand, antimicrobial surfaces are produced on the basis of the electrochemical behavior of metals which form microelectrochemical cells in the presence of moisture and due to the microelectric fields display a germ-killing effect.
These metals are either electrodeposited or applied by physicochemical processes (PVD, CVD, sputtering or sol-gel processes).
The present disclosure describes particles having a microbial effect and also materials having an antimicrobial action, by means of which a good microbial effect can be achieved independently of the ambient conditions as well as processes for producing such antimicrobial particles. For example, some embodiments include articles having an antimicrobial surface, characterized in that the particles are equipped with a layer (12, 13) which contains both antimony-tin oxide and manganese oxide.
In some embodiments, the particles have the form of flakes and/or platelets and/or needles (11).
In some embodiments, the layer +11 consists of an inner sublayer (12) of antimony-tin oxide and a porous outer sublayer (13) of manganese oxide.
As another example, some embodiments include a material for producing a coating or a component, comprising a matrix material and particles (16) for embedding in a matrix to be formed from the matrix material, characterized in that the particles (16) have the structure as described herein.
In some embodiments, the matrix material consists of a granulated polymer.
In some embodiments, the particles (16) are attached to the surface of the granulated polymer.
In some embodiments, the matrix material consists of a surface coating composition in which the particles (16) are dispersed.
In some embodiments, the matrix material is present in ionized form in an electrolyte, with the particles (16) being dispersed in the electrolyte.
As another example, some embodiments include a process for producing particles as described herein, characterized in that particles coated with antimony-tin oxide are used and these are wet-chemically coated with manganese oxide using a symproportionation-precipitation process, with the following steps being run through in the order indicated: suspension of the particles (16) in water, introduction of the particle suspension obtained in this way into a manganese(II) nitrate solution, setting of a pH of 8 by introduction of ammonia, dropwise addition of potassium permanganate solution with continual stirring, and filtering-off of the coated particles.
As another example, some embodiments include a process for producing particles as described herein, characterized in that particles coated with antimony-tin oxide are used and these are coated with manganese oxide using a process for atomic layer deposition (ALD), with the following steps being run through in the order indicated: deposition of manganese precursors as first reactant, introduction of water vapor as second reactant, and oxidation of the manganese precursor in the presence of oxygen.
In some embodiments, the process is carried out in a fluidized-bed reactor.
The working examples described below are embodiments of the teachings herein. In the working examples, the components described for the embodiments are in each case individual features of the disclosure which should be viewed as independent of one another and also develop the teachings further independently of one another and should therefore also be regarded, either individually or in a combination other than that shown, as constituent part of the teachings. Furthermore, the embodiments described can also be supplemented by further features, as described above, of the disclosure. In the figures:
Some embodiments of the present disclosure include particles equipped with a layer which contains both antimony-tin oxide and manganese oxide. Such a composition of the material of the layer on the particles displays an excellent antimicrobial action. For this purpose, studies have been carried out and have given the following results.
The precipitates were painted onto a glass support and the material surfaces were tested for antimicrobial effectiveness according to the standard ASTM E 2180-01. Gram-positive bacteria, Staphylococcus aureus ATOC 6538, and Gram-negative bacteria, Escherichia coli ATOC 8739, were used as test organisms. Immediately after initial drying of the cells on the surfaces (0 h), a significant reduction in the bacteria is observed, which is attributable to rapid inactivation of the germs and pronounced biocidal effectiveness of MnO2/ATO on titanium dioxide needles in a moist medium. After an incubation time of four hours, 99.99% of the germs had been killed, which indicates that an antimicrobial action is also displayed under dry conditions.
Three parallel batches were contaminated for each material and also each point in time of sampling. The following control was also carried out: 0.2 ml of the germ suspension was transferred directly into a screw-cap test tube containing 10 ml of TSB and worked up further as above; this gave information about the efficiency of flushing of germs from the test surfaces.
The following samples were examined:
1) comparative sample SnO2 on titanium dioxide needles; hereinafter referred to as SnO2; and
2) antimicrobial particles SnO2/MnO2 on titanium dioxide needles; hereinafter referred to as SnO2/MnO2.
Three parallel batches were contaminated for each material and also each point in time of sampling. The following control was also carried out: 0.2 ml of the germ suspension was transferred directly into a screw-cap test tube containing 10 ml of TSB and worked up further as above; this gave information about the efficiency of flushing of germs from the test surfaces. Table 1 reports the KBE recovered from the surfaces at the different times for Escherichia coli. Table 2 shows the corresponding results for Staphylococcus aureus. Table 3 shows the total numbers of germs applied to the surfaces, while table 4 shows the germs recovered from the different material surfaces at the different incubation times, based on the total numbers of germs applied to the surfaces.
In some embodiments, the particles have the shape of flakes and/or platelets and/or needles. These particle shapes have a large aspect ratio. In other words, these particle shapes have a comparatively large surface area which is available for coating relative to the mass. A comparatively strong antimicrobial action can therefore be achieved with minimal use of material, since the surface area of said layer is of importance for this antimicrobial action.
In some embodiments, the layer consists of an inner sublayer of antimony-tin oxide and a porous outer sublayer of manganese oxide. Particles which have already been coated by manufacturers with antimony-tin oxide can be used as semifinished parts for coating with manganese oxide. The layer system is, owing to the porosity, nevertheless suitable for producing the described antimicrobial properties because the antimony-tin oxide is effective due to the porosity of the manganese oxide.
In the following, the manganese oxide will also be referred to as pyrolusite. The term “pyrolusite” should in the context of the present disclosure be understood as a group of minerals comprising the possible manganese oxides. The antimony-tin oxide will hereinafter also be abbreviated to ATO.
In some embodiments, there is a material for producing a coating, which comprises a matrix material and particles for embedding in a matrix which can be formed from this matrix material in different ways. In some embodiments, the particles have the above-described structure, i.e. they have a layer containing both antimony-tin oxide and manganese oxide. In some embodiments, the layers produced from this material likewise have antimicrobial properties since the particles built into the layer have this property at least at the surface of the component produced or the coating.
In some embodiments, the matrix material can consist of a granulated polymer. Granulated polymers are used in industry for producing polymer parts on a large scale. For this purpose, the granulated polymers are melted and processed in suitable machines to give polymer parts (for example by injection molding). Here, the particles can be built into the matrix of the component as it is being formed. This advantageously gives rise to antimicrobial properties at the surface of the component.
In some embodiments, the particles, which are very much smaller than the grains of the granulated polymer, may be attached to the surface of the granulated polymer, i.e. to the grains of the granulated polymer. This can result in the particles being able to be embedded reliably in the component to be produced. The concentration of particles to be achieved in the component to be produced (or in a polymer coating to be produced) can also be set by the occupation of the surface of the grains of the granulated polymer.
In some embodiments, the matrix material can consist of a surface coating composition in which the particles are dispersed. Surface coating compositions are used on a large scale for coating components, giving a surface coating composition layer by evaporation of a solvent of the surface coating composition and a pigment of the surface coating composition being fixed to the surface. Part of this pigment is the above-described particles having an antimicrobial action, with this action also being able to be utilized on the surface of the surface coating composition layer.
In some embodiments, the matrix material to be present in ionized form in an electrolyte, with the particles being dispersed in the electrolyte. In this way, it is possible to produce a coating on a component by an electrochemical route, with the dispersed particles being incorporated into this coating. During electrolytic coating, the matrix material is deposited from the electrolyte onto the component to be coated. This expediently makes it possible to produce, for example, metallic layers whose antimicrobial properties are improved by incorporation of the particles.
All materials which have been described in more detail above are also suitable for producing components or layers in such a way that the antimicrobial properties are retained even when the surface is worn. This can be explained by the fact that the particles are provided in the entire matrix of the component or of the coating and for this reason fresh particles, whose antimicrobial properties can be brought to bear when the particles are exposed, are continually exposed when material is removed from the surface.
In some embodiments, there is process in which particles which have previously been coated with antimony-tin oxide are used and these are wet-chemically coated with manganese oxide using what is known as a symproportionation-precipitation process, with the following steps being run through in the order indicated: suspension of the particles in water, introduction of the particle suspension obtained in this way into a manganese(II) nitrate solution, setting of a pH of 8 by introduction of ammonia, dropwise addition of potassium permanganate solution with continual stirring (over up to 4 hours), and filtering-off of the coated particles. An economical process for producing the particles already described in more detail above is provided thereby.
In some embodiments, there is process in which particles coated with antimony-tin oxide are used and these are coated with manganese oxide using a process for atomic layer deposition (also referred to as ALD). Here, the following steps are run through in the order indicated: deposition of manganese precursors as first reactant, introduction of water vapor as second reactant, and oxidation of the manganese precursor in the presence of oxygen.
In some embodiments, this process can be carried out using a fluidized-bed reactor. The use of the ALD process has the advantage that very thin layers can be deposited with high precision thereby. As a result, the catalytic properties of the antimicrobial layer can be obtained with minimal consumption of material.
Further particular teachings of the disclosure are described below with reference to the drawing. Identical or corresponding elements of the drawing are in each case provided with the same reference numerals and are only repeatedly described to the extent that there are differences between the individual figures.
An antimicrobial layer can be produced by means of the following measures. Two metal oxides are provided as antimicrobially active substances on a support material. The metal oxides are selected on the basis of their electrochemical behavior, taking into account the standard electrode potentials as shown in
Standard potential of tin:
Sn4++2e⇔Sn2+0.15 V
Sn2++2e⇔Sn−0.14 V
Particle geometries having high aspect ratios, e.g., needles, flakes, platelets, may be selected as support materials. Titanium dioxide needles are selected as working example. Antimicrobially active surfaces can be produced on titanium dioxide needles by wet chemical or physicochemical processes (e.g. atomic layer deposition). Titanium dioxide needles which have previously been provided with an antimony-tin oxide layer are obtainable with various length and width ratios from the company Ishihara. For coating, titanium dioxide needles with the designation FT1000, which are 0.13 μm wide and 1.68 μm long (see
In some embodiments, the particles are produced, for example, by means of wet chemical production of antimicrobial surfaces composed of metal oxides on titanium dioxide needles. On the titanium dioxide needles (needles 11 in
For this purpose, needles are suspended in water. The TiO2 needle suspension is slowly added while stirring to a manganese(II) nitrate solution. When the entire suspension is present in the manganese(II) nitrate solution, a pH of 8 is set by means of ammonia. Potassium permanganate solution is subsequently added dropwise to the TiO2—Mn(II)-NO3 mixture. This mixture of TiO2 needles, Mn(NO3)2, NH3 and KMnO4 is stirred for a number of hours. The titanium dioxide needles coated with pyrolusite are filtered off and washed. The precipitate is dried for 24 hours overnight at 110° C. in the presence of air. It is then calcined at 425° C. for a number of hours.
Pyrolusite is deposited on the ATO of the titanium dioxide needles by symproportionation of the components manganese(II) nitrate and permanganate by precipitation according to equation 1.
3Mn2++2MnO4−+2H2O=5MnO2+4H+ Equation 1
An intermediate oxidation state is formed from a higher oxidation state and a lower oxidation state of two Mn atoms by simultaneous oxidation of Mn2+ and reduction of Mn7+.
In some embodiments, the production of the coated particles is, as an alternative, also successfully effected by physicochemical deposition. An alternative to wet-chemical coating is, for example, atomic layer deposition (ALD). Here, the needles are coated with manganese oxide from the gas phase via manganese precursors and water vapor as second reactants. As manganese precursors, it is possible to use bis(ethylcyclopentadienyl)manganese(II) or bis(N,N-diisopropylpentylamidinato)manganese(II).
Process sequence: The titanium dioxide needles having an ATO layer are placed in a fluidized-bed reactor (FBR). Such a fluidized-bed reactor is depicted in
To overcome the agglomeration forces between the needles, supplementary methods are necessary for a fluidized state to be established. Vibration of the fluidized bed can be effected by ultrasonic transducers 18 which are installed on the outer wall of the FBR and are controlled and regulated by means of an ultrasound generator 19. When the titanium dioxide needles are present in the reactor, a fine vacuum of 10−3 mbar is set in the reactor by means of a pump. This means that the air is pumped out. The needles are then brought into a fluidized state by introduction of inert gas. In the fluidized state, the reactor space is heated to from 140 to 230° C. by thermal radiation. For this purpose, a heating sleeve 20 is present outside the reactor.
Mn(CpEt)2 is firstly stored in a bubbler 22 as protection against atmospheric oxygen and atmospheric moisture and secondly heated to 80-90° C. by means of a thermostatic bath (not shown). The bubbler 22 is equipped with a feed tube and a offtake tube 23. Carrier gas (nitrogen) goes via the feed tube into the bubbler and mixes there with the Mn(CpEt)2 vapor. The nitrogen precursor vapor leaves the bubbler via the offtake tube 23 and is pneumatically conveyed with the aid of valves through the offtake tube into the FBR. The Mn(CpEt)2 flow into the FBR is monitored and controlled by means of the vapor pressure of the precursor and the regulated flow of the N2 carrier gas in such a way that a monolayer of Mn(CpEt)2 is chemisorbed onto the ATO surface (not depicted, cf.
In a second step, excess Mn(CpEt)2 gas molecules are removed and the FBR is flushed with nitrogen.
In a third step, water vapor is conveyed as second reactant from a stock vessel 24 through a conduit 25 into the FBR. The water vapor immediately reacts with the Mn(CpEt)2 complex to form manganese oxide and the volatile ethylcyclopentadiene. The fragmentation of the Mn(CpEt)2 complex occurs between the manganese atom and the negatively charged, aromatic five-membered ring system.
In a fourth step, the volatile ethylcyclopentadiene and the excess water vapor are removed. The vacuum vessel and the coated needles are flushed with nitrogen.
The deposition processes described and the two flushing/evacuation processes between the layer-forming steps comprise a deposition cycle which is repeated a number of times. Each individual process proceeds to completion. The Mn(CpEt)2 and the water vapor are introduced sequentially into the FBR chamber and chemisorbed on the ATO surface of the titanium dioxide needles until the entire ATO surface is occupied. No further adsorption processes then take place. The duration of the individual steps is selected so that the component which has just been introduced reacts in an adequate time with the ATO surface and the excess vapor and also the by-products are removed from the vacuum chamber 21. The adsorption time of Mn(CpEt)2, the dissociation time into MnO and ethylcyclopentadiene and flushing times between the layer-forming processes are in the order of seconds. In this way of carrying out the process, the surface reactions limit themselves, so that a reproducible manganese oxide layer is deposited as outer sublayer 13 having a calculatable composition. The manganese oxide deposited grows with each subsequent cycle.
The number of process cycles necessary, the time for which the coating reactants act and the amount of bis(ethylcyclopentadienyl)manganese(II) and water vapor per unit area and cycle depend on the size (width and length) and number of the titanium dioxide needles and layer thickness of the manganese dioxide.
The reaction (equation 2) of Mn(CpEt)2 with water vapor is:
Mn(CpEt)2+H2O=MnO+2HCpEt Equation 2
The titanium dioxide needles coated with manganese(II) oxide are subsequently calcined at 425° C. in the presence of atmospheric oxygen for a number of hours in order to obtain pyrolusite.
| Number | Date | Country | Kind |
|---|---|---|---|
| 18167217.1 | Apr 2018 | EP | regional |
This application is a U.S. National Stage Application of International Application No. PCT/EP2019/054949 filed Feb. 28, 2019, which designates the United States of America, and claims priority to EP Application No. 18167217.1 filed Apr. 13, 2018, the contents of which are hereby incorporated by reference in their entirety.
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/EP2019/054949 | 2/28/2019 | WO | 00 |