Patent Application
20190023992
This application claims the benefit under 35 USC 119(a) of Korean Patent Applications No. 10-2017-0091553 filed on Jul. 19, 2017, and No. 10-2018-0012794 filed on Feb. 1, 2018, in the Korean Intellectual Property Office, the entire disclosures of which are incorporated herein by reference for all purposes.
The present disclosure relates to a particle including at least one an atomic-scale channel formed on a surface of the particle or on a surface and inside of the particle; a catalyst including the particle, particularly a catalyst for efficient and selective electrochemical conversion of carbon dioxide into high value-added C2+ fuel; and a method of preparing the particle.
A chemical reaction accelerated by a catalyst consists of (1) adsorption of a reactant to a catalytic reaction site, (2) occurrence of a reaction, and (3) desorption of a product from the surface of the catalyst. Therefore, if the adsorption specificity of the surface of the catalyst is changed, the activity and selectivity of the chemical reaction may also be greatly changed.
Accordingly, research has been mainly directed to controlling the adsorption specificity of a catalyst by increasing a catalytic reaction site in order to improve the catalytic performances such as activity and selectivity, but a technology for atomically controlling reaction sites on or inside a catalyst based on adsorption/desorption energy of a reactant or intermediate product has been rarely researched.
Meanwhile, one of major greenhouse gases that cause global warming is carbon dioxide. Carbon dioxide is mainly generated by combustion of fossil fuels, and every year, billions of tons of carbon dioxide is emitted. Accordingly, countries around the world are accelerating the development of a technology for converting carbon dioxide into high value-added fuels or industrial chemicals using electrochemical and/or photochemical methods in order to reduce the emission of carbon dioxide (Korean Patent Laid-open Publication No. 2014-0012017, etc.).
However, the carbon dioxide conversion technology has many limitations for commercial use, such as efficiency, selectivity, and conversion rate. The carbon dioxide conversion technology is basically a catalytic reaction, and most of the problems (high-priced precious metal catalyst, low catalytic performances, and rapid catalytic degradation, etc.) that hinder the commercial use are caused by the catalyst.
Accordingly, in order to commercialize the carbon dioxide conversion technology, the development of a catalyst that enables the production of a high value-added product with high efficiency and excellent selectivity for a long time by supplying a little energy is primarily demanded.
In view of the foregoing, the present disclosure provides a particle including at least one an atomic-scale channel formed on a surface of the particle or on a surface and inside of the particle; a catalyst including the particle, particularly a catalyst for efficient and selective electrochemical conversion of carbon dioxide into high value-added C2+ fuel; and a method of preparing the particle.
However, problems to be solved by the present disclosure are not limited to the above-described problems. Although not described herein, other problems to be solved by the present disclosure can be clearly understood by those skilled in the art from the following descriptions.
A first aspect of the present disclosure provides a particle including at least one atomic-scale channel, the at least one atomic-scale channel being formed on a surface of the particle, or on a surface and inside of the particle.
A second aspect of the present disclosure provides a catalyst including the particle including at least one atomic-scale channel according to the first aspect, wherein the at least one atomic-scale channel is formed on a surface of the particle, or on a surface and inside of the particle, and wherein an inner surface of the at least one atomic-scale channel comprised in the particle includes a reduced metal.
A third aspect of the present disclosure provides a method of preparing the particle including at least one atomic-scale channel according to the first aspect, the method including forming the at least one atomic-scale channel on a surface of the particle, or on a surface and inside of the particle by electrochemical lithiation of a metal compound-containing particle, followed by delithiation, wherein a dimension of a width of the at least one atomic-scale channel is controlled by adjusting a degree of the lithiation, and wherein at least a portion of a surface, or a surface and inside of the metal compound-containing particle is reduced during the lithiation to form the at least one atomic-scale channel, and an inner surface of the at least one atomic-scale channel comprised in the particle includes the metal reduced from the metal compound.
In exemplary embodiments of the present disclosure, the particle according to the present disclosure includes at least one atomic-scale channel on a surface of the particle, or on a surface and inside of the particle, and a width of the at least one atomic-scale channel can be controlled in angstrom (A) unit.
In exemplary embodiments of the present disclosure, the particle according to the present disclosure includes at least one atomic-scale channel whose width can be controlled in angstrom unit on a surface of the particle or on a surface and inside of the particle, and, thus, the at least one atomic-scale channel can form a strong and stable bond with a reactant(s) and/or intermediate product(s) of a catalytic reaction, which makes the particle useful as a catalyst.
In exemplary embodiments of the present disclosure, the catalyst includes at least one atomic-scale channel which can form a strong and stable bond with a reactant(s) and/or intermediate product(s) of a catalytic reaction, and, thus, a current density and a Faradaic efficiency are remarkably high and the activity and/or selectivity of the catalyst is also high.
In exemplary embodiments of the present disclosure, the catalyst can act as a catalyst for electrochemical reduction of an oxygen atom-containing material, particularly for reduction of carbon dioxide, sulfur oxides (SOx), or nitrogen oxides (NOx).
In exemplary embodiments of the present disclosure, the catalyst includes the at least one atomic-scale channel controlled in angstrom unit, and, thus, a selectivity for high value-added C2+ hydrocarbons product prepared by the reduction or electrochemical reduction of the carbon dioxide can be remarkably increased, in comparison to that using a particle without the at least one atomic-scale channel.
In the detailed description that follows, embodiments are described as illustrations only since various changes and modifications will become apparent to those skilled in the art from the following detailed description. The use of the same reference numbers in different figures indicates similar or identical items.
Hereinafter, examples of the present disclosure will be described in detail with reference to the accompanying drawings so that the present disclosure may be readily implemented by those skilled in the art. However, it is to be noted that the present disclosure is not limited to the examples but can be embodied in various other ways. In drawings, parts irrelevant to the description are omitted for the simplicity of explanation, and like reference numerals denote like parts through the whole document.
Through the whole document, the term “connected to” or “coupled to” that is used to designate a connection or coupling of one element to another element includes both a case that an element is “directly connected or coupled to” another element and a case that an element is “electronically connected or coupled to” another element via still another element.
Through the whole document, the term “on” that is used to designate a position of one element with respect to another element includes both a case that the one element is adjacent to the other element and a case that any other element exists between these two elements.
Further, through the whole document, the term “comprises or includes” and/or “comprising or including” used in the document means that one or more other components, steps, operation and/or existence or addition of elements are not excluded in addition to the described components, steps, operation and/or elements unless context dictates otherwise. Through the whole document, the term “about or approximately” or “substantially” is intended to have meanings close to numerical values or ranges specified with an allowable error and intended to prevent accurate or absolute numerical values disclosed for understanding of the present disclosure from being illegally or unfairly used by any unconscionable third party. Through the whole document, the term “step of” does not mean “step for”.
Through the whole document, the term “combination of” included in Markush type description means mixture or combination of one or more components, steps, operations and/or elements selected from a group consisting of components, steps, operation and/or elements described in Markush type and thereby means that the disclosure includes one or more components, steps, operations and/or elements selected from the Markush group.
Through this whole specification, a phrase in the form “A and/or B” means “A or B, or A and B”.
Through this whole specification, the term “RHE” refers to a reversible hydrogen electrode, and the term “CO2RR” refers to an electrochemical reduction of carbon dioxide.
Hereinafter, embodiments and examples of the present disclosure will be described in detail with reference to the accompanying drawings. However, the present disclosure may not be limited to the following embodiments, examples, and drawings.
A first aspect of the present disclosure provides a particle including at least one atomic-scale channel, the at least one atomic-scale channel being formed on a surface of the particle, or on a surface and inside of the particle.
In an exemplary embodiment of the present disclosure, a width of the at least one atomic-scale channel may be less than about 1 nm. For example, the width of the at least one atomic-scale channel may be less than about 1 nm, about 9 Å or less, about 8 Å or less, about 7 Å or less, about 6 Å or less, about 5 Å or less, about 4 Å or less, about 3 Å or less, or about 2 Å or less, but may not be limited thereto. Further, for example, the width of the at least one atomic-scale channel may be about 7 Å or less.
In an exemplary embodiment of the present disclosure, the width of the at least one atomic-scale channel may be from about 1 Å or more to less than about 1 nm, but may not be limited thereto. For example, the width of the at least one atomic-scale channel may be from about 1 Å or more to less than about 1 nm, from about 1 Å or more to about 9 Å or less, from about 1 Å or more to about 8 Å or less, from about 1 Å or more to about 7 Å or less, from about 1 Å or more to about 6 Å or less, from about 1 Å or more to about 5 Å or less, from about 1 Å or more to about 4 Å or less, from about 1 Å or more to about 3 Å or less, from about 1 Å or more to about 2 Å or less, from about 2 Å or more to less than about 1 nm, from about 2 Å or more to about 9 Å or less, from about 2 Å or more to about 8 Å or less, from about 2 Å or more to about 7 Å or less, from about 2 Å or more to about 6 Å or less, from about 2 Å or more to about 5 Å or less, from about 2 Å or more to about 4 Å or less, from about 2 Å or more to about 3 Å or less, from about 3 Å or more to less than about 1 nm, from about 3 Å or more to about 9 Å or less, from about 3 Å or more to about 8 Å or less, from about 3 Å or more to about 7 Å or less, from about 3 Å or more to about 6 Å or less, from about 3 Å or more to about 5 Å or less, from about 3 Å or more to about 4 Å or less, from about 4 Å or more to less than about 1 nm, from about 4 Å or more to about 9 Å or less, from about 4 Å or more to about 8 Å or less, from about 4 Å or more to about 7 Å or less, from about 4 Å or more to about 6 Å or less, from about 4 Å or more to about 5 Å or less, from about 5 Å or more to less than about 1 nm, from about 5 Å or more to about 9 Å or less, from about 5 Å or more to about 8 Å or less, from about 5 Å or more to about 7 Å or less, from about 5 Å or more to about 6 Å or less, from about 6 Å or more to less than about 1 nm, from about 6 Å or more to about 9 Å or less, from about 6 Å or more to about 8 Å or less, from about 6 Å or more to about 7 Å or less, from about 7 Å or more to less than about 1 nm, from about 7 Å or more to about 9 Å or less, from about 7 Å or more to about 8 Å or less, from about 8 Å or more to less than about 1 nm, from about 8 Å or more to about 9 Å or less, or from about 9 Å or more to less than about 1 nm, but may not be limited thereto. Further, for example, the width of the at least one atomic-scale channel may be from about 5 Å or more to about 6 Å or less.
In an exemplary embodiment of the present disclosure, an inner surface of the at least one atomic-scale channel included in the particle may include a reduced metal. In an exemplary embodiment of the present disclosure, a surface between the channels included in the particle may include the reduced metal. In an exemplary embodiment of the present disclosure, the inner surface of the at least one atomic-scale channel included in the particle and the other surface of the particle may include the reduced metal, but may not be limited thereto.
In an exemplary embodiment of the present disclosure, the atomic-scale channel on the surface of the particle among the at least one atomic-scale channel may be open in the surface of the particle and may have a three-dimensional shape when observed in an atomic-scale and may have a one-dimensional or two-dimensional shape when observed in a nano-scale, but may not be limited thereto.
In an exemplary embodiment of the present disclosure, the at least one atomic-scale channel or the inner space of the channel is a space formed in an atomic scale. The at least one atomic-scale channel or the inner space of the channel may be referred to as an atomic-scale interspacing, an atomic-scale interlayer, or an atomic-scale interplanar spacing, based on both inner sides of the atomic-scale channel, but may not be limited thereto.
In an exemplary embodiment of the present disclosure, the at least one atomic-scale channel may have a regular or irregular shape and may be separated from or connected to each other, but may not be limited thereto.
In an exemplary embodiment of the present disclosure, the at least one atomic-scale channel included in the particle may be formed by a process including electrochemical lithiation of a metal compound-containing particle, followed by delithiation, wherein the inner surface of the at least one atomic-scale channel may include the reduced metal formed by reduction of the metal compound during the lithiation.
In an exemplary embodiment of the present disclosure, a dimension of the width of the at least one atomic-scale channel may be controlled by a cut-off voltage of the electrochemical lithiation of the metal compound-containing particle, but may not be limited thereto.
In an exemplary embodiment of the present disclosure, the metal compound may be a compound including one or at least two metal elements selected from the group consisting of Mg, Al, Au, Ag, Cd, Co, Cr, Cu, In, Ir, Mo, Nb, Ni, Os, Pd, Pt, Rh, Ru, Sn, Ti, V, W, Zn, Sc, Y, Zr, Hf, Ta, Mn, Fe, Tc, and Re, but may not be limited thereto. In an exemplary embodiment of the present disclosure, the metal may be used without limitation as long as it has a standard reduction potential higher than that of lithium, but may not be limited thereto.
In an exemplary embodiment of the present disclosure, the metal compound may include an oxide of one or at least two metals selected from the group consisting of Mg, Al, Au, Ag, Cd, Co, Cr, Cu, In, Ir, Mo, Nb, Ni, Os, Pd, Pt, Rh, Ru, Sn, Ti, V, W, Zn, Sc, Y, Zr, Hf, Ta, Mn, Fe, Tc, and Re.
In an exemplary embodiment of the present disclosure, the reduced metal may include one or at least two metals selected from the group consisting of Mg, Al, Au, Ag, Cd, Co, Cr, Cu, In, Ir, Mo, Nb, Ni, Os, Pd, Pt, Rh, Ru, Sn, Ti, V, W, Zn, Sc, Y, Zr, Hf, Ta, Mn, Fe, Tc, and Re, but may not be limited thereto. In an exemplary embodiment of the present disclosure, the metal may be used without limitation as long as it has a standard reduction potential higher than that of lithium, but may not be limited thereto, but may not be limited thereto.
In an exemplary embodiment of the present disclosure, an average diameter of the particle is not particularly limited. For example, the particle may have an average diameter of from nanometer scale to micrometer scale, but may not be limited thereto. For example, the average diameter of the particle may be about 10 μm or less, about 1 μm or less, about 500 nm or less, about 300 nm or less, about 100 nm or less, from about 30 nm to about 500 nm, from about 30 nm to about 400 nm, from about 30 nm to about 300 nm, from about 30 nm to about 200 nm, from about 30 nm to about 100 nm, from about 30 nm to about 80 nm, from about 30 nm to about 60 nm, from about 30 nm to about 50 nm, from about 50 nm to about 500 nm, from about 50 nm to about 400 nm, from about 50 nm to about 300 nm, from about 50 nm to about 200 nm, from about 50 nm to about 100 nm, from about 50 nm to about 80 nm, from about 50 nm to about 60 nm, from about 60 nm to about 500 nm, from about 60 nm to about 400 nm, from about 60 nm to about 300 nm, from about 60 nm to about 200 nm, from about 60 nm to about 100 nm, from about 60 nm to about 80 nm, from about 80 nm to about 500 nm, from about 80 nm to about 400 nm, from about 80 nm to about 300 nm, from about 80 nm to about 200 nm, or from about 80 nm to about 100 nm, but may not be limited thereto.
In an exemplary embodiment of the present disclosure, a volume density of the at least one atomic-scale channel may be in a range of a ratio of from about 0.01 to about 0.2 per unit volume of the particle, but may not be limited thereto. For example, the volume density of the at least one atomic-scale channel may be in a range of a ratio of from about 0.01 to about 0.2, from about 0.01 to about 0.15, from about 0.01 to about 0.1, from about 0.01 to about 0.08, from about 0.01 to about 0.06, from about 0.01 to about 0.04, from about 0.01 to about 0.02, from about 0.02 to about 0.2, from about 0.02 to about 0.15, from about 0.02 to about 0.1, from about 0.02 to about 0.08, from about 0.02 to about 0.06, from about 0.02 to about 0.04, from about 0.04 to about 0.2, from about 0.04 to about 0.15, from about 0.04 to about 0.1, from about 0.04 to about 0.08, from about 0.04 to about 0.06, from about 0.06 to about 0.2, from about 0.06 to about 0.15, from about 0.06 to about 0.1, from about 0.06 to about 0.08, from about 0.08 to about 0.2, from about 0.08 to about 0.15, or from about 0.08 to about 0.1 per unit volume of the particle, but may not be limited thereto.
A second aspect of the present disclosure provides a catalyst including the particle including at least one atomic-scale channel according to the first aspect, wherein the at least one atomic-scale channel is formed on a surface of the particle, or on a surface and inside of the particle, and wherein an inner surface of the at least one atomic-scale channel comprised in the particle includes a reduced metal.
Detailed descriptions on the second aspect of the present disclosure, which overlap with those on the first aspect of the present disclosure, are omitted hereinafter, but the descriptions of the first aspect of the present disclosure may be identically applied to the second aspect of the present disclosure, even though they are omitted hereinafter.
In an exemplary embodiment of the present disclosure, a width of the at least one atomic-scale channel may be less than about 1 nm. For example, the width of the at least one atomic-scale channel may be less than about 1 nm, about 9 Å or less, about 8 Å or less, about 7 Å or less, about 6 Å or less, about 5 Å or less, about 4 Å or less, about 3 Å or less, or about 2 Å or less, but may not be limited thereto. Further, for example, the width of the at least one atomic-scale channel may be about 7 Å or less.
In an exemplary embodiment of the present disclosure, the width of the at least one atomic-scale channel may be from about 1 Å or more to less than about 1 nm, but may not be limited thereto. For example, the width of the at least one atomic-scale channel may be from about 1 Å or more to less than about 1 nm, from about 1 Å or more to about 9 Å or less, from about 1 Å or more to about 8 Å or less, from about 1 Å or more to about 7 Å or less, from about 1 Å or more to about 6 Å or less, from about 1 Å or more to about 5 Å or less, from about 1 Å or more to about 4 Å or less, from about 1 Å or more to about 3 Å or less, from about 1 Å or more to about 2 Å or less, from about 2 Å or more to less than about 1 nm, from about 2 Å or more to about 9 Å or less, from about 2 Å or more to about 8 Å or less, from about 2 Å or more to about 7 Å or less, from about 2 Å or more to about 6 Å or less, from about 2 Å or more to about 5 Å or less, from about 2 Å or more to about 4 Å or less, from about 2 Å or more to about 3 Å or less, from about 3 Å or more to less than about 1 nm, from about 3 Å or more to about 9 Å or less, from about 3 Å or more to about 8 Å or less, from about 3 Å or more to about 7 Å or less, from about 3 Å or more to about 6 Å or less, from about 3 Å or more to about 5 Å or less, from about 3 Å or more to about 4 Å or less, from about 4 Å or more to less than about 1 nm, from about 4 Å or more to about 9 Å or less, from about 4 Å or more to about 8 Å or less, from about 4 Å or more to about 7 Å or less, from about 4 Å or more to about 6 Å or less, from about 4 Å or more to about 5 Å or less, from about 5 Å or more to less than about 1 nm, from about 5 Å or more to about 9 Å or less, from about 5 Å or more to about 8 Å or less, from about 5 Å or more to about 7 Å or less, from about 5 Å or more to about 6 Å or less, from about 6 Å or more to less than about 1 nm, from about 6 Å or more to about 9 Å or less, from about 6 Å or more to about 8 Å or less, from about 6 Å or more to about 7 Å or less, from about 7 Å or more to less than about 1 nm, from about 7 Å or more to about 9 Å or less, from about 7 Å or more to about 8 Å or less, from about 8 Å or more to less than about 1 nm, from about 8 Å or more to about 9 Å or less, or from about 9 Å or more to less than about 1 nm, but may not be limited thereto. Further, for example, the width of the at least one atomic-scale channel may be from about 5 Å or more to about 6 Å or less.
In an exemplary embodiment of the present disclosure, an inner surface of the at least one atomic-scale channel included in the particle may include a reduced metal. In an exemplary embodiment of the present disclosure, a surface between the channels included in the particle may include the reduced metal. In an exemplary embodiment of the present disclosure, the inner surface of the at least one atomic-scale channel included in the particle and the other surface of the particle may include the reduced metal, but may not be limited thereto.
In an exemplary embodiment of the present disclosure, the atomic-scale channel on the surface of the particle among the at least one atomic-scale channel may be open in the surface of the particle and may have a three-dimensional shape when observed in an atomic-scale and may have a one-dimensional or two-dimensional shape when observed in a nano-scale, but may not be limited thereto.
In an exemplary embodiment of the present disclosure, the at least one atomic-scale channel or the inner space of the channel is a space formed in an atomic scale. The at least one atomic-scale channel or the inner space of the channel may be referred to as an atomic-scale interspacing, an atomic-scale interlayer, or an atomic-scale interplanar spacing, based on both inner sides of the atomic-scale channel, but may not be limited thereto.
In an exemplary embodiment of the present disclosure, the at least one atomic-scale channel may have a regular or irregular shape and may be separated from or connected to each other, but may not be limited thereto.
In an exemplary embodiment of the present disclosure, the at least one atomic-scale channel included in the particle may be formed by a process including electrochemical lithiation of a metal compound-containing particle, followed by delithiation, wherein the inner surface of the at least one atomic-scale channel may include the reduced metal formed by reduction of the metal compound.
In an exemplary embodiment of the present disclosure, a dimension of the width of the at least one atomic-scale channel may be controlled by a cut-off voltage of the electrochemical lithiation of the metal compound-containing particle, but may not be limited thereto.
In an exemplary embodiment of the present disclosure, in the catalyst, the particle may act as a catalyst for reduction of an oxygen atom-containing material, but may not be limited thereto. The catalyst may act as a catalyst for reduction of an oxygen atom-containing material in the phase of gas or liquid, but may not be limited thereto.
In an exemplary embodiment of the present disclosure, the oxygen atom-containing material may include carbon dioxide, sulfur oxides (SOx), or nitrogen oxides (NOx), but may not be limited thereto. Further, the oxygen atom-containing material may include carbon dioxide.
In an exemplary embodiment of the present disclosure, the reduction may be performed by electrochemical reduction, but may not be limited thereto.
In an exemplary embodiment of the present disclosure, an activity and/or a selectivity of the catalyst may be controlled by a dimension of the width of the at least one atomic-scale channel comprised in the particle.
In an exemplary embodiment of the present disclosure, the width of the at least one atomic-scale channel before and after the reduction with the catalyst may be maintained constant, but may not be limited thereto.
In an exemplary embodiment of the present disclosure, the metal compound may be a compound including one or at least two metal elements selected from the group consisting of Mg, Al, Au, Ag, Cd, Co, Cr, Cu, In, Ir, Mo, Nb, Ni, Os, Pd, Pt, Rh, Ru, Sn, Ti, V, W, Zn, Sc, Y, Zr, Hf, Ta, Mn, Fe, Tc, and Re, but may not be limited thereto. In an exemplary embodiment of the present disclosure, the metal may be used without limitation as long as it has a standard reduction potential higher than that of lithium, but may not be limited thereto, but may not be limited thereto.
In an exemplary embodiment of the present disclosure, the metal compound may include an oxide of one or at least two metals selected from the group consisting of Mg, Al, Au, Ag, Cd, Co, Cr, Cu, In, Ir, Mo, Nb, Ni, Os, Pd, Pt, Rh, Ru, Sn, Ti, V, W, Zn, Sc, Y, Zr, Hf, Ta, Mn, Fe, Tc, and Re.
In an exemplary embodiment of the present disclosure, the reduced metal may include one or at least two metals selected from the group consisting of Mg, Al, Au, Ag, Cd, Co, Cr, Cu, In, Ir, Mo, Nb, Ni, Os, Pd, Pt, Rh, Ru, Sn, Ti, V, W, Zn, Sc, Y, Zr, Hf, Ta, Mn, Fe, Tc, and Re, but may not be limited thereto. In an exemplary embodiment of the present disclosure, if the metal has a standard reduction potential higher than that of lithium, the metal may be used without limitation as long as it is known as having a targeted catalytic performance, but may not be limited thereto.
In an exemplary embodiment of the present disclosure, an average diameter of the particle is not particularly limited. For example, the particle may have an average diameter of from nanometer scale to micrometer scale, but may not be limited thereto. For example, the average diameter of the particle may be about 10 μm or less, about 1 μm or less, about 500 nm or less, about 300 nm or less, about 100 nm or less, from about 30 nm to about 500 nm, from about 30 nm to about 400 nm, from about 30 nm to about 300 nm, from about 30 nm to about 200 nm, from about 30 nm to about 100 nm, from about 30 nm to about 80 nm, from about 30 nm to about 60 nm, from about 30 nm to about 50 nm, from about 50 nm to about 500 nm, from about 50 nm to about 400 nm, from about 50 nm to about 300 nm, from about 50 nm to about 200 nm, from about 50 nm to about 100 nm, from about 50 nm to about 80 nm, from about 50 nm to about 60 nm, from about 60 nm to about 500 nm, from about 60 nm to about 400 nm, from about 60 nm to about 300 nm, from about 60 nm to about 200 nm, from about 60 nm to about 100 nm, from about 60 nm to about 80 nm, from about 80 nm to about 500 nm, from about 80 nm to about 400 nm, from about 80 nm to about 300 nm, from about 80 nm to about 200 nm, or from about 80 nm to about 100 nm, but may not be limited thereto.
In an exemplary embodiment of the present disclosure, a volume density of the at least one atomic-scale channel may be in a range of a ratio of 0.01 to 0.2 per unit volume of the particle, but may not be limited thereto. For example, the volume density of the at least one atomic-scale channel may be in a range of a ratio of from about 0.01 to about 0.2, from about 0.01 to about 0.15, from about 0.01 to about 0.1, from about 0.01 to about 0.08, from about 0.01 to about 0.06, from about 0.01 to about 0.04, from about 0.01 to about 0.02, from about 0.02 to about 0.2, from about 0.02 to about 0.15, from about 0.02 to about 0.1, from about 0.02 to about 0.08, from about 0.02 to about 0.06, from about 0.02 to about 0.04, from about 0.04 to about 0.2, from about 0.04 to about 0.15, from about 0.04 to about 0.1, from about 0.04 to about 0.08, from about 0.04 to about 0.06, from about 0.06 to about 0.2, from about 0.06 to about 0.15, from about 0.06 to about 0.1, from about 0.06 to about 0.08, from about 0.08 to about 0.2, from about 0.08 to about 0.15, or from about 0.08 to about 0.1 per unit volume of the particle, but may not be limited thereto.
In an exemplary embodiment of the present disclosure, the width of the at least one atomic-scale channel may be about 7 Å or less, and the selectivity for C2+ hydrocarbons product prepared by the reduction, particularly electrochemical reduction, of the carbon dioxide using the particle as the catalyst may be increased, in comparison to that using a particle without the at least one atomic-scale channel. For example, the selectivity for the C2+ hydrocarbons product may be about 40% or more, about 50% or more, about 60% or more, about 70% or more, about 80% or more, or about 90% or more. Further, when the catalyst is actually prepared, the selectivity for the C2+ hydrocarbons product may vary depending on the number, shape, width, length, or depth of the at least one atomic-scale channel formed in the particle included in the catalyst. For example, the selectivity for the C2+ hydrocarbons product may be affected by a carbon-carbon coupling efficiency which varies depending on the number, shape, width, length, or depth of the at least one atomic-scale channel formed in the particle, but may not be limited thereto.
In an exemplary embodiment of the present disclosure, the width of the atomic-scale channel of the particle may be from about 5 Å or more to about 6 Å or less, and the selectivity for the C2+ hydrocarbons product formed by the reduction, particularly electrochemical reduction, of the carbon dioxide using the particle as the catalyst may be increased, in comparison to that using a particle without the at least one atomic-scale channel. For example, the selectivity for the C2+ hydrocarbons product may be about 40% or more, about 50% or more, about 60% or more, about 70% or more, about 80% or more, or about 90% or more. Further, when the catalyst is actually prepared, the selectivity for the C2+ hydrocarbons product may vary depending on the number, shape, width, length, or depth of the at least one atomic-scale channel formed in the particle included in the catalyst. For example, the selectivity for the C2+ hydrocarbons product may be affected by the carbon-carbon coupling efficiency which varies depending on the number, shape, width, length, or depth of the at least one atomic-scale channel formed in the particle, but may not be limited thereto.
In an exemplary embodiment of the present disclosure, the particle according to the present disclosure includes at least one atomic-scale channel whose width can be controlled in angstrom (A) unit on a surface of the particle or on a surface and inside of the particle, and, thus, the at least one atomic-scale channel can form a strong and stable bond with a reactant(s) and/or intermediate product(s) of a catalytic reaction, which makes the particle very useful as a catalyst.
In an exemplary embodiment of the present disclosure, the catalyst includes at least one atomic-scale channel or gap which can form a strong and stable bond with a reactant(s) and/or intermediate product(s) of a catalytic reaction, and, thus, a current density and a Faradaic efficiency are remarkably high and the activity and/or selectivity of the catalyst is also remarkably high, which make └ the catalyst advantageous.
In an exemplary embodiment of the present disclosure, the catalyst can act as a catalyst particularly for electrochemical reduction of an oxygen atom-containing material and thus can act as a catalyst for reduction of carbon dioxide, sulfur oxides (SOx), or nitrogen oxides (NOx).
In an exemplary embodiment of the present disclosure, a method of electrochemical conversion of carbon dioxide may use the catalyst of the second aspect of the present disclosure. The catalyst including the particle including at least one atomic-scale channel according to the first aspect, wherein the at least one atomic-scale channel is formed on a surface of the particle, or on a surface and inside of the particle, and wherein an inner surface of the at least one atomic-scale channel comprised in the particle includes a reduced metal. For example, the width of the atomic-scale channel of the particle is 7 Å or less, but may not be limited thereto.
In an exemplary embodiment of the present disclosure, the catalyst includes the at least one atomic-scale channel controlled in angstrom unit, and, thus, a selectivity for a C2+ hydrocarbons product prepared by the reduction of the carbon dioxide can be remarkably increased, in comparison to that using a particle without the at least one atomic-scale channel.
In an exemplary embodiment of the present disclosure, an electrochemical reduction of carbon dioxide with the catalyst may be a method of producing a C2+ organic compound by electrochemically reducing carbon dioxide using an electrode including the catalyst for reduction of carbon dioxide. Herein, the C2+ organic compound may include an organic compound of from C2 to C4, and for example, the organic compound of from C2 to C4 may include ethylene, propylene, butylene, ethanol, propanol, butanol, or acetates, but may not be limited thereto. Specifically, the organic compound of C2 or more may include ethylene and/or ethanol.
In the electrochemical reduction according to an exemplary embodiment of the present disclosure, a loading amount of the catalyst on the electrode may be from about 1 μg/cm2 to about 50 μg/cm2, preferably from about 5 μg/cm2 to about 20 μg/cm2, and more preferably from about 11 μg/cm2 to about 20 μg/cm2. The catalyst may be loaded by drop-casting a solution containing the catalyst on an electrode or glassy carbon substrate, but may not be limited thereto.
In the electrochemical reduction according to an exemplary embodiment of the present disclosure, a voltage applied to the electrode during the electrochemical reduction may be from about −0.7 V to about −1.5 V and preferably from about −0.7 V to about −1 V based on a RHE (V vs RHE), but may not be limited thereto. For example, the voltage applied to the electrode may be from about −0.7 V to about −1.5 V, from about −0.7 V to about −1.2 V, from about −0.7 V to about −1 V, from about −0.7 V to about −0.9 V, from about −0.9 V to about −1.5 V, from about −0.9 V to about −1.2 V, from about −0.9 V to about −1 V, from about −1 V to about −1.5 V, or from about −1 V to about −1.2 V based on a reversible hydrogen electrode, but may not be limited thereto.
The electrochemical reduction of carbon dioxide according to an exemplary embodiment of the present disclosure may be performed using any cell structures, electrolytes, and counter electrodes known as being used for electrochemical reduction of carbon dioxide to produce a C2+ product. For example, the electrochemical reduction of carbon dioxide may be performed using a reduction tub including a separator that separates a cathode region and an anode region; a cathode which is an electrode including the catalyst for reduction of carbon dioxide and arranged in the cathode region; a cathode electrolyte in contact with the cathode in the cathode region and saturated with carbon dioxide; an anode arranged in the anode region; and an anode electrolyte in contact with the anode. In this case, fresh electrolytes may be injected to the cathode region and the anode region through inlets, respectively, and the electrolytes and reaction products after the reaction may be discharged through outlets. The separator may be an ion-exchange membrane, and the ion-exchange membrane may be a cation-exchange membrane or an anion-exchange membrane. The anode, the cathode electrolyte, and the anode electrolyte may use, without limitation, any anode materials, cathode electrolyte materials, and anode electrolyte materials known as being used for electrochemical reduction of carbon dioxide. For example, the anode may include precious metals such as platinum, rhodium, gold, and the like and/or precious metal oxides, but may not be limited thereto. For example, the cathode electrolyte and the anode electrolyte may be identical to or different from each other, and the cathode electrolyte and the anode electrolyte may be liquid electrolytes. For example, the liquid electrolytes may be aqueous or non-aqueous liquid electrolytes. Examples of the liquid cathode electrolyte may include non-aqueous or aqueous liquid electrolytes including a bicarbonate, carbonate, sulfate, phosphate, borate, chloride, bromide, and other organic/inorganic salts of an alkali metal or ammonium hydroxide, but may not be limited thereto. Examples of the liquid anode electrolyte may include non-aqueous or aqueous liquid electrolytes including a hydroxide, inorganic acid, organic acid, or halide of an alkali metal or ammonium hydroxide, but may not be limited thereto. A solvent for the non-aqueous liquid electrolyte may be any organic solvent known as being used for electrochemical reduction of carbon dioxide, and representative examples thereof may include ionic liquids such as nitrile-based solvents, e.g., acetonitrile, alcohol-based solvents, e.g., methanol, ether-based solvents, e.g., dimethyl ether, and imidazolium-based solvents, but may not be limited thereto.
A third aspect of the present disclosure provides a method of preparing the particle including at least one atomic-scale channel according to the first aspect, including forming the at least one atomic-scale channel on a surface of the particle, or on a surface and inside of the particle by electrochemical lithiation of a metal compound-containing particle, followed by delithiation, wherein a dimension of a width of the at least one atomic-scale channel is controlled by adjusting a degree of the lithiation, and at least a portion of a surface, or a surface and inside of the metal compound-containing particle is reduced during the lithiation to form the at least one atomic-scale channel, and wherein an inner surface of the at least one atomic-scale channel comprised in the particle includes the metal reduced from the metal compound.
Detailed descriptions on the third aspect of the present disclosure, which overlap with those on the first aspect of the present disclosure, are omitted hereinafter, but the descriptions of the first aspect of the present disclosure may be identically applied to the third aspect of the present disclosure, even though they are omitted hereinafter.
In an exemplary embodiment of the present disclosure, an inner surface of the at least one atomic-scale channel included in the particle may include a reduced metal. In an exemplary embodiment of the present disclosure, a surface between the channels included in the particle may include the reduced metal. In an exemplary embodiment of the present disclosure, the inner surface of the at least one atomic-scale channel included in the particle and the other surface of the particle may include the reduced metal, but may not be limited thereto.
In an exemplary embodiment of the present disclosure, the atomic-scale channel on the surface of the particle among the at least one atomic-scale channel may be open in the surface of the particle and may have a three-dimensional shape when observed in an atomic-scale and may have a one-dimensional or two-dimensional shape when observed in a nano-scale, but may not be limited thereto.
In an exemplary embodiment of the present disclosure, the at least one atomic-scale channel or the channel is a space formed in an atomic scale. The at least one atomic-scale channel or the inner space of the channel may be referred to as an atomic-scale interspacing, an atomic-scale interlayer, or an atomic-scale interplanar spacing, based on both inner sides of the atomic-scale channel, but may not be limited thereto.
In an exemplary embodiment of the present disclosure, the at least one atomic-scale channel may have a regular or irregular shape and may be separated from or connected to each other, but may not be limited thereto.
In an exemplary embodiment of the present disclosure, the at least one atomic-scale channel included in the particle may be formed by a process including electrochemical lithiation of a metal compound-containing particle, followed by delithiation, wherein the inner surface of the at least one atomic-scale channel may include the reduced metal formed by reduction of the metal compound during the lithiation.
In an exemplary embodiment of the present disclosure, the lithiation may include applying a constant current and a cut-off voltage of from more than 0 V to about 3 V or less using an electrochemical cell, and the cut-off voltage may be based on Li/Li+, but may not be limited thereto. For example, the cut-off voltage may be from more than 0 V or to about 3 V or less, from more than 0 V to less than about 3 V, from more than 0 V to about 2.5 V or less, from more than 0 V to about 2 V or less, from more than 0 V to about 1.5 V or less, from more than 0 V to about 1.4 V or less, from more than 0 V to about 1.2 V or less, from more than 0 V to about 1 V or less, from more than 0 V or to about 0.8 V or less, from more than 0 V to about 0.6 V or less, from more than 0 V to about 0.4 V or less, from more than 0 V to about 0.2 V or less, from about 0.2 V or more to about 3 V or less, from about 0.2 V or more to less than about 3 V, from about 0.2 V or more to about 2.5 V or less, from about 0.2 V or more to about 2 V or less, from about 0.2 V or more to about 1.5 V or less, from about 0.2 V or more to about 1.4 V or less, from about 0.2 V or more to about 1.2 V or less, from about 0.2 V or more to about 1 V or less, from about 0.2 V or more to about 0.8 V or less, from about 0.2 V or more to about 0.6 V or less, from about 0.2 V or more to about 0.4 V or less, from about 0.4 V or more to about 3 V or less, from about 0.4 V or more to less than about 3 V, from about 0.4 V or more to about 2.5 V or less, from about 0.4 V or more to about 2 V or less, from about 0.4 V or more to about 1.5 V or less, from about 0.4 V or more to about 1.4 V or less, from about 0.4 V or more to about 1.2 V or less, from about 0.4 V or more to about 1 V or less, from about 0.4 V or more to about 0.8 V or less, from about 0.4 V or more to about 0.6 V or less, from about 0.6 V or more to about 3 V or less, from about 0.6 V or more to less than about 3 V, from about 0.6 V or more to about 2.5 V or less, from about 0.6 V or more to about 2 V or less, from about 0.6 V or more to about 1.5 V or less, from about 0.6 V or more to about 1.4 V or less, from about 0.6 V or more to about 1.2 V or less, from about 0.6 V or more to about 1 V or less, from about 0.6 V or more to about 0.8 V or less, from about 0.8 V or more to about 3 V or less, from about 0.8 V or more to less than about 3 V, from about 0.8 V or more to about 2.5 V or less, from about 0.8 V or more to about 2 V or less, from about 0.8 V or more to about 1.5 V or less, from about 0.8 V or more to about 1.4 V or less, from about 0.8 V or more to about 1.2 V or less, from about 0.8 V or more to about 1V or less, from about 1 V or more to about 3 V or less, from about 1V or more to less than about 3 V, from about 1V or more to about 2.5 V or less, from about 1V or more to about 2 V or less, from about 1V or more to about 1.5 V or less, from about 1V or more to about 1.4 V or less, from about 1V or more to about 1.2 V or less, from about 1.2 V or more to about 3 V or less, from about 1.2 V or more to less than about 3 V, from about 1.2 V or more to about 2.5 V or less, from about 1.2 V or more to about 2 V or less, from about 1.2 V or more to about 1.5 V or less, from about 1.2 V or more to about 1.4 V or less, from about 1.4 V or more to about 3 V or less, from about 1.4 V or more to less than about 3 V, from about 1.4 V or more to about 2.5 V or less, from about 1.4 V or more to about 2 V or less, or from about 1.4 V or more to about 1.5 V or less, but may not be limited thereto. For example, the cut-off voltage may be from more than 0 V to about 1.5 V or less, from more than 0 V to about 1 V or less, from more than 0 V to about 0.5 V or less, from about 0.5 V or more to about 1.5 V or less, from about 0.5 V or more to about 1V or less, from about 1 V or more to about 1.5 V or less, or from about 1V or more to about 1.4 V or less. Further, for example, the cut-off voltage may be from about 1V or more to about 1.4 V or less.
In an exemplary embodiment of the present disclosure, the width of the at least one atomic-scale channel may be controlled by a cut-off voltage of the electrochemical lithiation of the metal compound-containing particle. This means that an average width of the at least one atomic-scale channel may be controlled specifically by a cut-off voltage upon a constant current discharge (lithiation), i.e., a voltage at which lithiation is cut off.
In an exemplary embodiment of the present disclosure, the electrochemical lithiation of the metal compound-containing particle may include: a) preparing an electrochemical cell including a first electrode in which a layer including the metal compound is formed on a current collector, a second electrode formed of metallic lithium, a separator positioned between the first electrode and the second electrode, and an electrolyte; and b) performing lithiation by applying a constant current and a cut-off voltage of from more than 0 V to about 3 V or less or from more than 0 V to less than about 3 V using the prepared electrochemical cell.
In an exemplary embodiment of the present disclosure, the electrochemical cell in the step a) may correspond to a conventional lithium half-cell including a metal compound-containing particle as an active material, and the lithiation in the step b) may correspond to a constant current discharge in the conventional lithium half-cell. Therefore, the cut-off voltage may be based on a potential referenced to Li/Li+. Accordingly, since the electrochemical cell in the step a) corresponds to a lithium half-cell, the first electrode may be prepared by a method of preparing an electrode for a conventional lithium secondary cell by using the metal compound-containing particle on the current collector as an active material.
In an exemplary embodiment of the present disclosure, the first electrode may be prepared by coating and drying a slurry including the metal compound-containing particle and an organic binder on the current collector. The organic binder may use any material as long as it has been typically used in an electrode for a lithium secondary cell and may be a polymer which does not chemically react with a liquid electrolyte. For example, the organic binder may be selected from the group consisting of polyvinylidene fluoride, a polyvinylidene fluoride-hexafluoropropylene copolymer, a polyvinylidene fluoride-trichloroethylene copolymer, polymethylmethacrylate, polyacrylonitrile, polyvinylpyrrolidone, polyvinylacetate, a polyethylene-vinyl acetate copolymer, polyethylene oxide, cellulose acetate, cellulose acetate butyrate, cellulose acetate propionate, cyanoethyl pullulan, cyanoethyl polyvinyl alcohol, cyanoethyl cellulose, cyanoethyl sucrose, pullulan, carboxyl methyl cellulose, a styrene-butadiene copolymer, an acrylonitrile-styrene-butadiene copolymer, polyimide, polytetrafluoroethylene, and combinations thereof, but may not be limited thereto. Further, the current collector may be formed of a conductive material such as graphite, graphene, titanium, copper, platinum, aluminum, nickel, silver, gold, and the like, but may not be limited thereto.
In an exemplary embodiment of the present disclosure, the second electrode may be a film or foil of metallic lithium, but may not be limited thereto. Further, the separator may use any microporous membrane used for the conventional lithium secondary cell.
In an exemplary embodiment of the present disclosure, the electrolyte may use, without limitation, any conventional non-aqueous electrolyte that readily conducts lithium ions in a conventional lithium secondary cell. For example, the non-aqueous electrolyte may contain a non-aqueous solvent and a lithium salt, and the lithium salt contained in the electrolyte may include a salt that supplies a lithium cation and one or more anions selected from NO3−, N(CN)2−, BF4−, ClO4−, PF6−, (CF3)2PF4−, (CF3)3PF3−, (CF3)4PF2−, (CF3)5PF−, (CF3)6P−, CF3CO2−, CH3CO2−, SCN−, (CF3CF2SO2)2N−, and the like, but may not be limited thereto.
In an exemplary embodiment of the present disclosure, the solvent in the electrolyte may use any solvent without limitation as long as it has been typically used as a non-aqueous liquid electrolyte in a lithium secondary cell. For example, the solvent may be selected from the group consisting of carbonate-based solvents such as ethylene carbonate, propylene carbonate, 1,2-butylene carbonate, 2,3-butylene carbonate, 1,2-pentylene carbonate, 2,3-pentylene carbonate, vinylene carbonate, dimethyl carbonate, and diethyl carbonate, formate-based solvents such as methyl formate, ethyl formate, propyl formate, and butyl formate, ether-based solvents such as dimethyl ether, diethyl ether, dipropyl ether, and methyl ethyl ether, acetate-based solvents such as methyl acetate, ethyl acetate, and propyl acetate, γ-butyrolactone, 2-methyl-γ-butyrolactone, 3-methyl-γ-butyrolactone, and combinations thereof, but may not be limited thereto.
In an exemplary embodiment of the present disclosure, the step b) may be lithiation of the metal compound-containing particle using the prepared electrochemical cell. Specifically, the lithiation in the step b) may be the lithiation under conditions of a constant current and a cut-off voltage of from more than 0 V to about 3 V or less or from more than 0 V to less than about 3 V using the prepared electrochemical cell.
In an exemplary embodiment of the present disclosure, in the lithiation under the constant current condition, it is advantageous to perform low-current lithiation in order to perform uniform lithiation to the entire surface of the metal compound-containing particle and suppress desorption and removal of a reduced metal from the nanoparticle surface by rapid and partial lithiation and in order to ensure atomic-scale gaps to have a narrow size distribution. Specifically, for example, a current during the low-current lithiation may be desirably from about 1 mA/g to about 20 mA/g (amount of current per 1 g of metal oxide nanoparticles).
In an exemplary embodiment of the present disclosure, after the lithiation in the step b) is performed, recovering the lithiated nanoparticles from the first electrode may be further performed. The recovery may be performed using a solvent that dissolves the organic binder of the first electrode and a solid-liquid separation, but may not be limited thereto.
In an exemplary embodiment of the present disclosure, the delithiation may be performed through acid-washing, and an acid for the acid-washing may use, without limitation, any typical acid used for selectively removing lithium oxide and/or lithium, but may not be limited thereto. For example, the acid may be formic acid or acetic acid, but the kind of the acid used for the acid-washing may not be limited thereto.
In an exemplary embodiment of the present disclosure, the width of the at least one atomic-scale channel may be controlled to less than about 1 nm. For example, the width of the at least one atomic-scale channel may be controlled to less than about 1 nm, about 9 Å or less, about 8 Å or less, about 7 Å or less, about 6 Å or less, about 5 Å or less, about 4 Å or less, about 3 Å or less, or about 2 Å or less, but may not be limited thereto. Further, the width of the at least one atomic-scale channel may be controlled to about 7 Å or less.
In an exemplary embodiment of the present disclosure, the width of the at least one atomic-scale channel may be from about 1 Å or more to less than about 1 nm, but may not be limited thereto. For example, the width of the at least one atomic-scale channel may be from about 1 Å or more to less than about 1 nm, from about 1 Å or more to about 9 Å or less, from about 1 Å or more to about 8 Å or less, from about 1 Å or more to about 7 Å or less, from about 1 Å or more to about 6 Å or less, from about 1 Å or more to about 5 Å or less, from about 1 Å or more to about 4 Å or less, from about 1 Å or more to about 3 Å or less, from about 1 Å or more to about 2 Å or less, from about 2 Å or more to less than about 1 nm, from about 2 Å or more to about 9 Å or less, from about 2 Å or more to about 8 Å or less, from about 2 Å or more to about 7 Å or less, from about 2 Å or more to about 6 Å or less, from about 2 Å or more to about 5 Å or less, from about 2 Å or more to about 4 Å or less, from about 2 Å or more to about 3 Å or less, from about 3 Å or more to less than about 1 nm, from about 3 Å or more to about 9 Å or less, from about 3 Å or more to about 8 Å or less, from about 3 Å or more to about 7 Å or less, from about 3 Å or more to about 6 Å or less, from about 3 Å or more to about 5 Å or less, from about 3 Å or more to about 4 Å or less, from about 4 Å or more to less than about 1 nm, from about 4 Å or more to about 9 Å or less, from about 4 Å or more to about 8 Å or less, from about 4 Å or more to about 7 Å or less, from about 4 Å or more to about 6 Å or less, from about 4 Å or more to about 5 Å or less, from about 5 Å or more to less than about 1 nm, from about 5 Å or more to about 9 Å or less, from about 5 Å or more to about 8 Å or less, from about 5 Å or more to about 7 Å or less, from about 5 Å or more to about 6 Å or less, from about 6 Å or more to less than about 1 nm, from about 6 Å or more to about 9 Å or less, from about 6 Å or more to about 8 Å or less, from about 6 Å or more to about 7 Å or less, from about 7 Å or more to less than about 1 nm, from about 7 Å or more to about 9 Å or less, from about 7 Å or more to about 8 Å or less, from about 8 Å or more to less than about 1 nm, from about 8 Å or more to about 9 Å or less, or from about 9 Å or more to less than about 1 nm, but may not be limited thereto. Further, for example, the width of the at least one atomic-scale channel may be from about 5 Å or more to about 6 Å or less.
In an exemplary embodiment of the present disclosure, the metal compound may be a compound including one or at least two metal elements selected from the group consisting of Mg, Al, Au, Ag, Cd, Co, Cr, Cu, In, Ir, Mo, Nb, Ni, Os, Pd, Pt, Rh, Ru, Sn, Ti, V, W, Zn, Sc, Y, Zr, Hf, Ta, Mn, Fe, Tc, and Re, but may not be limited thereto. In an exemplary embodiment of the present disclosure, the metal may be used without limitation as long as it has a standard reduction potential higher than that of lithium, but may not be limited thereto.
In an exemplary embodiment of the present disclosure, the metal compound may include an oxide of one or at least two metals selected from the group consisting of Mg, Al, Au, Ag, Cd, Co, Cr, Cu, In, Ir, Mo, Nb, Ni, Os, Pd, Pt, Rh, Ru, Sn, Ti, V, W, Zn, Sc, Y, Zr, Hf, Ta, Mn, Fe, Tc, and Re.
In an exemplary embodiment of the present disclosure, the reduced metal may include one or at least two metals selected from the group consisting of Mg, Al, Au, Ag, Cd, Co, Cr, Cu, In, Ir, Mo, Nb, Ni, Os, Pd, Pt, Rh, Ru, Sn, Ti, V, W, Zn, Sc, Y, Zr, Hf, Ta, Mn, Fe, Tc, and Re, but may not be limited thereto. In an exemplary embodiment of the present disclosure, the metal may be used without limitation as long as it has a standard reduction potential higher than that of lithium, but may not be limited thereto.
In an exemplary embodiment of the present disclosure, an average diameter of the particle is not particularly limited. For example, the particle may have an average diameter of from nanometer scale to micrometer scale, but may not be limited thereto. For example, the average diameter of the particle may be about 10 μm or less, about 1 μm or less, about 500 nm or less, about 300 nm or less, about 100 nm or less, from about 30 nm to about 500 nm, from about 30 nm to about 400 nm, from about 30 nm to about 300 nm, from about 30 nm to about 200 nm, from about 30 nm to about 100 nm, from about 30 nm to about 80 nm, from about 30 nm to about 60 nm, from about 30 nm to about 50 nm, from about 50 nm to about 500 nm, from about 50 nm to about 400 nm, from about 50 nm to about 300 nm, from about 50 nm to about 200 nm, from about 50 nm to about 100 nm, from about 50 nm to about 80 nm, from about 50 nm to about 60 nm, from about 60 nm to about 500 nm, from about 60 nm to about 400 nm, from about 60 nm to about 300 nm, from about 60 nm to about 200 nm, from about 60 nm to about 100 nm, from about 60 nm to about 80 nm, from about 80 nm to about 500 nm, from about 80 nm to about 400 nm, from about 80 nm to about 300 nm, from about 80 nm to about 200 nm, or from about 80 nm to about 100 nm, but may not be limited thereto.
In an exemplary embodiment of the present disclosure, a volume density of the at least one atomic-scale channel may be in a range of a ratio of from about 0.01 to about 0.2 per unit volume of the particle, but may not be limited thereto. the volume density of the at least one atomic-scale channel may be in a range of a ratio of from about 0.01 to about 0.2, from about 0.01 to about 0.15, from about 0.01 to about 0.1, from about 0.01 to about 0.08, from about 0.01 to about 0.06, from about 0.01 to about 0.04, from about 0.01 to about 0.02, from about 0.02 to about 0.2, from about 0.02 to about 0.15, from about 0.02 to about 0.1, from about 0.02 to about 0.08, from about 0.02 to about 0.06, from about 0.02 to about 0.04, from about 0.04 to about 0.2, from about 0.04 to about 0.15, from about 0.04 to about 0.1, from about 0.04 to about 0.08, from about 0.04 to about 0.06, from about 0.06 to about 0.2, from about 0.06 to about 0.15, from about 0.06 to about 0.1, from about 0.06 to about 0.08, from about 0.08 to about 0.2, from about 0.08 to about 0.15, or from about 0.08 to about 0.1 per unit volume of the particle, but may not be limited thereto.
Hereinafter, example embodiments are described in more detail by using Examples, but the present disclosure may not limited to the Examples.
1. Methods
(1) Density Functional Theory (DFT) Calculations
All the DFT calculations using the slab models were performed using the dispersion-corrected PBE-D2 functional and the projector augmented wave pseudopotentials with a 400 eV cut-off basis set, as implemented in the Vienna Ab-initio Simulation Package (VASP). To accelerate the convergence for energies using self-consistent field (SCF) iterations, the Gaussian-smearing technique (smearing temperatures kBT=0.1 eV for slabs and 0.01 eV for molecules) was employed, after which all calculated energy values were extrapolated to kBT=0. The reciprocal space for the slab was sampled by a Monkhorst-Pack k-point net of 3×3×1, whereas only the gamma point was sampled for the molecular calculations. The models were prepared from a face-centred cubic copper bulk structure with a lattice parameter of 3.615 Å. To prevent interactions between the periodic replicas along the z-direction, a vacuum separation of at least 15 Å between adjacent images was used for the slab calculations and a 20 Å×20 Å×20 Å box was used for the molecular calculations. Spin-polarized wave functions were also used for all the surface calculations, whereas spin-restricted wave functions were used for H2, H2O, and CO2. During the geometry optimization, the copper atoms in the top layer of the upper surface and those in the bottom layer of the lower surface were fixed. Although in the initial structure the distance of d between the two surfaces is set to be a target value, it would be slightly different from the value by less than 0.2 Å after optimization, depending on the identity of the adsorbate. The energetics reported here are based on electronic energies. For example, the binding energy of *COOH is given by BE (*COOH)=E (*COOH)−E (*)−E (CO2)−0.5×E (H2). Therefore, a more negative value of BE denotes the stronger adsorption.
(2) Preparation of Copper Oxide Particle with the Controlled Width of Atomic-Scale Channels
CuOx (EPRUI Nanoparticles & Microspheres Co. Ltd.) was cleaned by annealing under argon at 150° C. for 3 h before the experiments. The lithiated CuOx nanoparticles were prepared using the following procedures described in our previous work. At first, CuOx nanoparticles were mixed with 5 wt % polyvinylidene fluoride (PVDF) dispersed in N-methyl-2-pyrrolidinone (NMP). Next, the black slurry was uniformly coated onto a Cu foil and dried overnight in a vacuum oven at 80° C. A coin-type cell with the Li foil as the counter electrode and 1 M LiPF6 dissolved in a mixture of ethyl carbonate (EC) and diethyl carbonate (DEC) as the electrolyte (1/1=v/v) were used for the electrochemical lithiation. The test cells with nanomaterials were assembled with a separator (Celgard) and an electrolyte solution in an Ar-filled glove box. The lithiation process was monitored using a VSP potentiostat (Bio-logic) to maintain the static current of 10 mA g−1. After the lithiation process is carried out, the resulting samples produced at each process step were washed with acetone, water, and 1 mM acetic acid solution to remove residual electrolytes, Li2O, and solid electrolyte interlayers.
(3) Operando Analysis
The electrochemical cell was prepared with the three electrodes, electrolyte, CO2 gas bubbling, and polyimide window. The samples were casted on the PTFE coated carbon papers with a 5 wt % of Nafion binder and applied −0.9 V vs. RHE under CO2 bubbling after 2 times linear sweep voltammetry. During CO2RR, operando X-ray absorption spectroscopy (XAS) analyses including the XANES and the EXAFS measurements were performed at 10C beam line, where a Si(111) double crystal monochromator was used for the synchrotron radiation and Cu K-edge spectra obtained in the transmission mode were analyzed using the Athena software with the IFEFFIT library.
(4) Measurements of the Electrochemical Reduction of CO2
Lithiated Cu2O nanoparticles were spin coated onto a glassy carbon substrate, which was then used as the cathode for electroreduction of CO2 in a 0.1 M CsHCO3 solution. The reason for using Cs+ cations is described elsewhere. The electrolyte was first sparged with CO2 to attain a pH of 6.8. Electrochemical measurements were conducted using a Biologic SP-300 potentiostat. Ambient-pressure CO2 electrolysis was carried out in a custom-made, gas-tight electrochemical cell made of polycarbonate and fitted with Viton O-rings. The configuration of the electrochemical cell is such that the working electrode is parallel to the counter electrode (platinum foil) to ensure a uniform potential distribution across the surface. The geometric surface area for both of the electrodes was 1 cm2. The average mass loading of samples on working electrode is 80 μL (equal to ˜10 μg cm−2), which was measured using a XP2U ultra-microbalance (d=0.1 μg, Mettler Toledo). In order to optimize the catalytic activity, mass loading of catalyst solutions was controlled from 50 to 150 μL. A Selemion AMV anion-exchange membrane (110 μm thick) was used to separate the anodic and cathodic compartments. Each of the compartments in this cell contained a small volume of electrolyte (1.3 mL each) to concentrate the liquid products and, therefore, increase the detection limits. The headspace of the cathodic compartment was approximately 3 mL. Before conducting electrolysis of CO2, the electrolyte in the cathodic compartments was purged with CO2 for at least 15 min. During electrolysis, CO2 was bubbled through the electrolyte at a flow rate of 5 sccm to prevent CO2 depletion. The flow rate of CO2 was controlled with a mass flow controller (Alicat Scientific), and the gas was first humidified with water by passing it through a water-filled bubbler to minimize evaporation of the electrolyte. For all experiments, a platinum foil was used as the counter electrode and an Ag/AgCl electrode (leak free series) from Innovative Instruments, Inc. was used as the reference electrode. Data were converted to the RHE reference scale using the following equation of
E vs. RHE=E vs. Ag/AgCl+0.197 V+0.0591×pH
To ensure the accuracy of the reference electrodes, calibration was performed with a homemade, reversible hydrogen electrode. Prior to any electrolysis, the solution resistance was first determined using electrochemical impedance spectroscopy by scanning from 1 MHz to 10 Hz. For all reported CVs and electrolysis, measurements were made with the potentiostat set to compensate for 85% of the measured IR drop.
2. Results
The inventors demonstrate here based on density functional theory (DFT) calculations and experimental measurements that atomic-level control of particle interspacing can be used to influence the activity and selectivity of Cu nanoparticles for the electrochemical CO2RR. DFT calculations of the binding energy of intermediates involved in CO2RR on Cu(100) and Cu(111) surfaces are found to depend on the atomic-scale spacing, ds, between such surfaces. When ds=5-6 Å, the binding energies for adsorbed intermediates, such as *COOH, *CO, *CHO, and *CHOH, reach a maximum and the formation of C—C bonds via the reactions *CHO+*CO→*CHOCO and *CHO+*CHO→*CHOCHO is highly favored. Since *CHOCO and *CHOCHO are precursors to ethylene and ethanol, these calculations suggest that the rates of formation of these products will be maximized for ds=5-6 Å. Motivated by these findings, atomic-scale spaces between Cu particles were created by subjecting CuOx nanoparticles to electrochemical lithiation followed by removal of the lithium oxide deposited and electrochemical reduction of CuOx to Cu. Analysis of TEM images confirmed that lithiation produced the desired interparticle spacings, and operando X-ray absorption near edge structure (XANES) and extended X-ray absorption fine structure (EXAFS) spectra demonstrated that all the oxidized Cu states are reduced to the metallic phase during CO2RR. Particles having inter-particle spacing of 5-6 Å exhibit a significantly higher current density and an FE of nearly 80% to C2+ products, higher than that reported for unmodified CuOx-derived Cu. our theoretical and experimental investigations strongly support the conclusion that atomic-level control of inter-particle spacing favorably influences the activity and selectivity of Cu nanoparticles for the electrochemical CO2RR.
(1) Density Functional Theory Calculations
DFT calculations of the binding energies for various species hypothesized to be involved in both the CO2RR and the hydrogen evolution reaction (HER) were carried out with the aim of identifying the effects of atomic-scale spacing between Cu surfaces on the electrochemical reduction of CO2. Copper nanoparticles with different atomic-scale spaces between them were simulated using a model consisting of two three-layer Cu (100) and Cu (111) (3×3) slabs, where the surfaces are separated by the distance ds (
The binding energies (BEs) for *COOH, *CO, *CHO, *CHOH, and *H, which are adsorbed species thought to be involved in the CO2RR and the HER, were determined as a function of ds. As illustrated in
Further, the inventors examined next whether the value of ds affects the energetics of C—C bond formation. Since *CO and *CHO are the early stage intermediates for CO2RR and therefore their concentrations are expected to be higher than the others, we evaluated the changes of the reaction energies for C—C coupling, *CHO+*CO→*CHOCO. The inventors found that the two reaction energies depend strongly on ds and that minimum values relative to open Cu(100) and Cu(111) surfaces occur at ds=5.0 and 6.0 Å, respectively (
To understand why atomic-scale spacing between the Cu(100) and Cu(111) surfaces helps to stabilize adsorbed species, we carried out a Bader analysis of the charge transfer from the two surfaces. The inventors found that the enhancement in adsorption strength for adsorbed species is due to charge transfer from the second layer to the adsorbate. For example, for *CO, the second layer donates 0.15 electron to the adsorbate compared to 0.38 electron from the first layer, and for *CHOCO, the second layer donates 0.65 electron to the adsorbate, which is similar to the amount donated by the first layer (0.60 electron), and as indicated by
(2) Preparation of Copper Oxide Particle with the Controlled Width of Atomic-Scale Channels
The theoretical findings shown in
The evolution of the CuOx surface morphology during lithiation is illustrated in
The morphological evolution determined by analysis of TEM images is given in
(3) Catalytic Activity and Selectivity for CO2RR
The catalytic activity and selectivity for CO2RR was evaluated by conducting ambient-pressure CO2 electrolysis under a constant potential for several hours.
To minimize the pH changes in the vicinity of the cathode, a 0.1 M CsHCO3 solution was used as the electrolyte and the cathode potential was kept below −0.9 V vs RHE. The inventors have shown previously that hydrated Cs+ cations can buffer pH changes occurring near the catalyst surface under conditions of considerable electrolyte polarization and, thereby, help to increase the amount of CO2 available for electrochemical reaction. The inventors have demonstrated that for cathode potentials more positive than −0.9 V vs RHE, hydrated Cs+ cations present in the out Helmholtz layer imposes a local electric field that enhances formation of C—C bonds via coupling of adsorbed CO or adsorbed CO and HCO. Evidence for the absence of mass transfer effects is given by the identical Tafel slopes observed for samples of CuOx that had been lithiated to different degrees.
The inventors also note that repeated lithiation cycles (5, 10 and 20 cycles) resulted in a CO2RR activity similar to that achieved after step V (
Since the catalyst activity and selectivity have been reported to depend on the catalyst mass loading, the inventors explored the effect of catalyst mass loading on the selectivity to C2+ products using CuOx with ds=5˜6 Å. Catalysts were prepared by drop-casting 50 μL to 150 μL of the catalyst-containing solution onto the glassy carbon substrate. The measured activities and FE for C2+ products are shown in
The inventors also found that the performance of CuOx with ds=5-6 Å, shown in
The reactivity towards C—C coupling during CO2RR is consistent with the binding energy of CO on the Cu surface. The binding energy of CO was probed by temperature-programmed desorption (TPD) and the results are presented in
All catalyst samples were characterized after CO2RR in order to determine whether other parameters besides, ds, contribute to the enhanced activity and selectivity of Cu for the CO2RR. Ex-situ TEM showed that none of the samples exhibited a significant change in morphology after CO2RR. Likewise, the magnitude of ds remained relatively constant after CO2RR. The stability of ds is also reflected in the stability of the current density observed for several hours under applied potential (
Another factor that could affect the catalytic properties of Cu is the density of grain boundaries (GBs). We compared the surface density of GBs determined from an analysis of TEM images. The inventors found that the GB surface density increased at steps I and II, but the density decreased sharply at step Ill (Figure S. The trends with expected reactivity parameters summarized in
The experimental and theoretical work presented here provides convincing evidence that atomic-level control of the interlayer spacing (ds) between Cu nanoparticles can be used to achieve high activity and C2+ product selectivity for CO2RR. The inventors' DFT calculations reveal that parallel Cu(100) and Cu(111) surfaces spaced ˜5-6 Å apart exhibit maximum binding of important CO2RR intermediates and promote C—C bond formation. Such spacing can be created by lithiating CuOx nanoparticles and then removing the Li2O deposited. Cu nanoparticles with values of ds=5-6 Å result in an approximately 12-fold increase in the current density relative to Cu particles obtained from CuOx without lithiation and a Faradaic efficiency to C2+ products of over 78%.
The above description of the example embodiments is provided for the purpose of illustration, and it would be understood by those skilled in the art that various changes and modifications may be made without changing technical conception and essential features of the example embodiments. Thus, it is clear that the above-described example embodiments are illustrative in all aspects and do not limit the present disclosure. For example, each component described to be distributed can be implemented in a combined manner.
The scope of the inventive concept is defined by the following claims and their equivalents rather than by the detailed description of the example embodiments. It shall be understood that all modifications and embodiments conceived from the meaning and scope of the claims and their equivalents are included in the scope of the inventive concept.
| Number | Date | Country | Kind |
|---|---|---|---|
| 10-2017-0091553 | Jul 2017 | KR | national |
| 10-2018-0012794 | Feb 2018 | KR | national |