Patent Application
20160111076
This invention relates to the building sound absorption material, especially to a particulate sound absorption board and preparation method.
Sound absorption material refers to the material that can absorb the incident sound under the action of its porosity, thin film or resonance, and can be divided into porous sound absorption material and resonance sound absorption structure based on its physical property and sound absorption way.
The structural feature of porous sound absorption material is that there are a large number of interconnected and outward micropores in the material, and its sound absorption principle is that the entry of sound wave into the material pore will vibrate tiny fibers of air and material in the pore, and result in friction and viscous resistance, and sound energy is converted into heat energy and absorbed. Fiber material and plaster material are widely used in the engineering, in which the former includes glass wool, mineral wool or various sound absorption boards or sound absorption components mainly made from such materials; the latter includes microporous brick and particulate slag sound absorption brick.
Porous plaster sound absorption material has many varieties, and is divided into slag sound absorption brick, expanded perlite sound absorption brick, pottery clay sound absorption brick and environmentally-friendly sandstone sound absorption board, etc. due to the difference of raw materials. Although the said sound absorption material has many varieties, such materials are not widely applied for its low porosity, low sound absorption coefficient and unsatisfactory sound absorption effect due to the limitation of manufacturing method, pore-forming mechanism and structure strength. For example, the patent (application no.: 201210398344.3) discloses an environmentally-friendly sandstone sound absorption board which is that natural round sand or natural colorful round sand and epoxy resin glue are pressed as the board after mixture to form the base layer, and expanded perlite particle and epoxy resin glue are pressed on the board after mixture to form the light material layer on which the gridding cloth is pressed to act as tensile strength and skeleton. The said sound absorption board is composed of four-layer structure, i.e. base layer, light material layer, gridding cloth layer and decoration surface layer, and featured by complicated structure, plenty of manufacturing processes and high cost. The pore-forming mechanism of base layer and light material layer in the environmentally-friendly sandstone sound absorption board is that the natural pore arising from the evaporation of water molecule and the curing of epoxy resin glue plays a role in sound absorption. Since the pore arising from the evaporation of water molecule is intermittent and random, the porosity is unpredictable, and most of pores arising from the evaporation of water molecule are closed pores that can't ventilate and store air. Such closed pore does not have sound absorption function, so its sound absorption coefficient is uncertain, and sound absorption effect is unsatisfactory. The dosage of binding agent is increased with the increase in specific surface area between sands due to the irregularity of external surface of the sand, so the cost of the said sound absorption board remains high, and its promotion and application are also affected.
The shortcomings above still need to be improved.
The purpose of this invention is to provide a particulate sound absorption board and its preparation method based on the shortage of prior art, which can guarantee the structure strength of sound absorption board, improve the sound absorption coefficient of sound absorption board, and obtain better sound absorption effect.
In order to achieve the above purpose, this invention provides a particulate sound absorption board which is composed of binding agent and sound absorption particle. The external surface of sound absorption particle is covered with a layer of binding agent, and the angularity coefficient of sound absorption particle covered with binding agent is less than 1.3; the said sound absorption particle consists of skeleton particle and filling particle, in which the former is used for sound absorption board skeleton, and the latter flows into the pore between skeleton particles to form sound absorption pore.
Further, the average diameter of cross section of the above sound absorption pore is 0.06-0.09 mm, preferably 0.07 mm.
Further, the diameter of the said skeleton particle is 0.8-1 mm, and the diameter of the said filling particle is 0.15 mm; the weight ratio of the said skeleton particle and filling particle is 80-90:10-15. In order to select more particles with angularity coefficient of less than 1.5, and improve the speed of material selection, the said sound absorption particle is selected from sand, ceramsite and recycled building waste particle.
To guarantee the binding strength and cohesive force of paricles, the said binding agent is extracted from epoxy resin, phenolic resin, urea resin and furfuryl alcohol resin.
The particulate sound absorption board of this invention is formed by splicing two kinds of particles of different diameters, and its sound absorption mechanism is that the entry of sound wave into the sound absorption board produces friction between the air in the pore and the external surface of particle, and the sound energy is converted into heat energy through friction, and the consumption of sound energy can be promoted with the increase in the length of pore so as to improve sound absorption effect. As we know, the pore formed between particles is divided into closed pore, semi-connected pore and connected pore. Closed pore can't store air and ventilate, and does not have sound absorption function, so semi-connected pore and connected pore should be preferred for the purpose of achieving better sound absorption effect. The particulate sound absorption board provided in this invention has such excellent sound absorption structure, and its skeleton is formed by closely splicing skeleton particles (larger diameter particles), and the pore between skeletons is filled with filling particles (smaller diameter particles) so as to form a specific micropore structure required for sound absorption. When micropore diameter of such structure is 0.07 mm, the structure has excellent sound absorption property, including connected pore that can store air and ventilate and semi-connected pore that can store air, but can't ventilate.
According to the experimental analysis and research conducted by the inventor for a long time, there are three factors affecting the sound absorption property of particulate sound absorption board, i.e. length, shape (width) and quantity of pore formed between particles. The length of pore is related to the thickness of sound absorption board which has an influence on sound absorption effect when the shape of pore in the particulate sound absorption board is determined. The thicker the particle board is, the greater the flow resistance, and the larger the sound absorption bandwidth. In view of economy and application range, the thickness of particle board is better 10 mm≈50 mm.
When particles of the same diameter are used, the total porosity formed is fixed, i.e. 0.472, which is nothing to do with particle diameter. It is just that the pore between particles is narrowed down with the decrease in particle diameter, and the number of pores is increasing, but the porosity is unchanged, which means the porosity limit of sound absorption board formed by closely splicing particles is 0.472. Sound absorption effect, however, is not the best when the porosity is maximized. As shown in
When particles of the same diameter are used, its pore is formed between five mutually contacted particles. Theoretically, the maximum cross section area Sx of the said pore 10 should be the cross section area of the pore formed between three mutually contacted particles, as shown in
S
x=(triangle area S)−3×arch area Si
S=(R×CON30°)×(R×SIN30°=0.433R2
Sector 9 area=(60/360)×3.14×R=0.523R2
S
1=(0.523−0.433)R2=0.09 R2
S
x
=S−3×S1=(0.433−3×0.09)R2=0.163 R2
Hence, the area of pore is directly proportional to the square of particle radius, which means the larger the particle diameter is, the greater the area of pore formed.
After several experiments, the inventor finds that the sound absorption coefficient of φ0.3 mm (60-70-mesh screen) sand is relatively better when the sound absorption board is made from particles of the same diameter. According to the above formula, the area Sx of such pore is 0.163 R2=0.163×0.15×0.15=0.00367 mm2, and its diameter is 0.069 mm.
When small diameter particles are inserted into large diameter particles, we know through calculation that the cross section area S2 of the pore is as follows when a small diameter particle is inserted into the pore formed between five large particles:
S
2=3.14r2=3.14×(0.155R)2=3.14×0.024R2=0.075R2
When the diameter of pore is larger, the sound absorption peak is smaller, and frequency channel is narrower. When the diameter of pore is equal to 0.069 mm, the sound absorption coefficient is maximized. When the pore is further narrowed, the intermediate frequency is poorer. Therefore, the pore with the diameter of 0.07 mm is the best sound absorption pore.
When the diameter of large particle is 0.8 mm, S2=0.012 mm2, which is equivalent to the addition of three small round pores with the diameter of 0.07 mm. It means that the pore formed by filling small particles into 0.8 mm large particles is the same as the pore formed from 0.3 mm particles. Hence, its sound absorption property is better.
When the diameter of the pore is 0.07 mm, the quantity of pore is increased by 3 times, and sound absorption coefficient is reduced at a single peak, and sound absorption property of the whole frequency channel is increased.
Hence, after several experiments, the inventor confirms that the width of the pore formed by filling φ0.15 mm particles into φ0.8-1 mm diameter particles is appropriate for high and low frequency sound absorption effect. The best mixture ratio of this invention is as follows: 80-90 skeleton particles (φ0.8-1 mm) and 10-15 filling particles (φ0.15 mm).
To ensure the pore formed between particles is uniform, the roundness requirements of particles are also very important. Theoretically, the pore formed is maximized when spherical particles are spliced, but the shape of particle used is actually irregular, so the pore formed when irregular particles are spliced, on one hand, will become smaller, and on the other hand, will be partially blocked to form “closed pore”. Hence, the total porosity of particulate sound absorption board will become smaller, and many “closed pores” useless for sound absorption will be generated to reduce the acoustic performance of particulate sound absorption board. Therefore, controlling the roundness of particle is very important.
Theoretically, the roundness of particle is represented by angularity coefficient, which is obtained based on the ratio of actual specific surface area of particle and specific surface area of corresponding ideal sphere. Hence, it can represent the derivation degree of particle shape from sphere, which means the larger the angularity coefficient, the more irregular the particle shape, and the more deviated from sphere. To obtain larger porosity and sound absorption pore, the angularity coefficient of particles required for the preparation of sound absorption board should be less than 1.3 so as to ensure the particle is round as far as possible. When the diameter of large particle is 0.8 mm, and 0.15 mm particles are inserted, the area S2 of the pore formed is 0.12 mm, which is equivalent to the addition of three small round pores with the diameter of 0.07 mm. But actual angularity coefficient of particles is generally less than 1.5, so the roundness of particles is adjusted by applying binding agent on the external surface of particles. Particles covered with binding agent are basically round, and its angularity coefficient should be up to 1.3.
Further, to reduce coating thickness, and ensure particles are rounded, the angularity coefficient of sound absorption particle should be less than 1.5. Hence, the selection of the particle with angularity coefficient of less than 1.5 can ensure the thickness of binding agent on the external surface is 0.1-0.2 mm when the angularity coefficient of coated particles is up to 1.3 for the purpose of achieving the best acoustic performance. If the coating (binding agent) is too thick, “teardrops” with be formed on the surface of particles under the action of gravity, and excess teardrops will block the pore, and affect the acoustic performance of particulate sound absorption board; if the coating is too thin, particles won't be rounded easily, and it is difficult to form larger binding area, and binding strength is insufficient. The thickness of binding agent is 0.1-0.2 mm, which can guarantee the binding strength of particles, reduce the dosage of binding agent, and reduce cost.
Meanwhile, to form the skeleton by closely splicing sound absorption board particles, and avoid the reduction of porosity of sound absorption board since the pore formed between particles is blocked by binding agent, this invention also provides the preparation method of above particulate sound absorption board, including the following steps:
Wherein, the covering thickness of binding agent on the surface of particles in step (1) is 0.1-0.2 mm.
Such thickness can guarantee the coated particles have necessary binding strength, and prevent the pore from being blocked by thick binding agent so as to reduce the sound absorption property of sound absorption board.
In step (1), the addition amount of binding agent is 3%-10% by weight of block particle.
In step (2), the addition amount of curing agent is determined based on the type and addition amount of binding agent selected.
Preferably, the top of sealing device is connected to the dust collector which shall be first started when compressed air is pumped into the sealing device to remove the mud and dust from raw materials of block particles, and facilitate the uniform coating of particles.
Meanwhile, to ensure particles are firmly spliced, and prevent the pore formed between particles from being blocked by excess binding agent, the component of binding agent and preparation technology of sound absorption board are also very important. The inventor calculates the binding area between particles, and further determines the addition amount of binding agent in the sound absorption board based on the total binding strength required for sound absorption board obtained from calculation, which can prevent the pore formed between particles from being blocked by excess binding agent, reduce the porosity of sound absorption board, save the usage amount of binding agent, and reduce usage cost.
The two-stage manufacturing technology (i.e. coating, curing and then shaping) of sound absorption board of this invention is that particles are uniformly covered with a layer of 0.1-0.2 mm thick binding agent on the surface, and mixed with curing agent and then mutually spliced. Such preparation technology also can prevent the pore formed between particles from being blocked by excess binding agent. Meanwhile, the coating of sound absorption particles of this invention has two advantages: (1) further improve the angularity coefficient of particles to ensure particles are basically spherical, and facilitate the formation of sound absorption pore in the block. In this invention, the sound absorption is achieved by the pore formed by closely splicing particles, so if particles are spherical, it is useful to improve its porosity, but particles are basically multilateral, so angular particles on the surface can be wrapped to be basically spherical; (2) uniform film can form greater binding surface 6 to obtain better mechanical property, as shown in
Hence, the particulate sound absorption board and its preparation method provided in this invention can guarantee the structure strength of sound absorption board, improve the sound absorption coefficient of sound absorption board, and obtain better sound absorption effect.
Legend: 1. skeleton; 2. connected pore; 3. semi-connected pore; 4. sound absorption particle; 5. binding agent; 6. binding surface; 7. triangle; 8. arch; 9. sector; 10. pore; 11. skeleton particle; 12. filling particle.
To clearly understand the purpose, technical scheme and beneficial effect, this invention will be further described below in combination with specific embodiments and drawings, but the protection scope of this invention is not limited to the following embodiments.
As shown in
The strength and sound absorption effect of the said sound absorption board are inspected, and inspection results are shown in the table below.
The strength and sound absorption effect of the said sound absorption board are inspected, and inspection results are shown in the table below.
The strength and sound absorption effect of the said sound absorption board are inspected, and inspection results are shown in the table below.
See embodiment 1 for specific operation. It is just that the angularity coefficient of particles selected in step 1 is less than 1.8. Upon inspection, the average thickness of binding agent on the external surface of coated particles is 0.07 mm, and the angularity coefficient of coated particles is less than 1.5.
See embodiment 1 for specific operation. It is just that the angularity coefficient of particles selected in step 1 is less than 1.8. To ensure the angularity coefficient of coated particles is less than 1.3, and dosage of binding agent is increased to 10.5 kg in step 3. Upon inspection, the average thickness of binding agent on the external surface of coated particles is 0.25 mm.
See embodiment 1 for specific operation. It is just that the mixture ratio (the mixture ratio of skeleton particle is unchanged, but the mixture ratio of filling particle is reduced) of raw materials in step 2 is changed as follows: 90 kg φ0.8 mm particles and 8 kg φ0.15 mm particles. According to the calculation, the dosage of binding agent is 2.94 kg.
See embodiment 1 for specific operation. It is just that the mixture ratio (the mixture ratio of skeleton particle is unchanged, but the mixture ratio of filling particle is increased) of raw materials in step 2 is changed as follows: 90 kg φ0.8 mm particles and 20 kg φ0.15 mm particles. According to the calculation, the dosage of binding agent is 3.3 kg.
See embodiment 1 for specific operation. It is just that the mixture ratio (the mixture ratio of filling particle is unchanged, but the mixture ratio of skeleton particle is reduced) of raw materials in step 2 is changed as follows: 60 kg φ0.8 mm particles and 10 kg φ0.15 mm particles. According to the calculation, the dosage of binding agent is 2.1 kg.
See embodiment 1 for specific operation. It is just that the mixture ratio (the mixture ratio of filling particle is unchanged, but the mixture ratio of skeleton particle is increased) of raw materials in step 2 is changed as follows: 100 kg φp0.8 mm particles and 10 kg φ0.15 mm particles.
According to the calculation, the dosage of binding agent is 3.3 kg.
See embodiment 1 for material selection. It is just that its preparation method is to directly mix, stir and pressurize sound absorption particles, binding agent and curing agent.
See embodiment 1 for specific operation. It is just that only 100 kg φ0.8 mm particles are selected.
We compare embodiments and comparative embodiments in this invention as well as the strength and sound absorption effect of commonly used environmentally-friendly sandstone sound absorption brick, expanded perilite sound absorption brick and pottery clay sound absorption brick. See the table below for details:
It can be seen from above results that embodiments 1-3 are the best implementation mode of technical scheme of this invention with high strength, good sound absorption effect and less binding agent dosage, and superior to existing environmentally-friendly sandstone sound absorption brick, expanded perilite sound absorption brick and pottery clay sound absorption brick; it fails to achieve better sound absorption effect even if comparative embodiments 1 and 2 lower the roundness requirements for particles, and comparative embodiments 3-6 correspondingly change the mixture ratio of skeleton particles and filling particles; it still fails to obtain better sound absorption effect when general all-mixed preparation method is used (comparative embodiment 7). In comparative embodiment 8, the sound absorption board is made from particles of the same diameter, but its sound absorption effect and sound absorption bandwidth can't be compared with this invention.
Hence, the technical effect of this invention is achieved based on particle roundness requirements, selection of grading and unique preparation method.
| Number | Date | Country | Kind |
|---|---|---|---|
| 201410347735.1 | Jul 2014 | CN | national |
This application is a continuation in part application of PCT application PCT/CN2014/089802, filed on Oct. 29, 2014, which claims the benefit of priority from Chinese Patent Application No. 201410347735.1, filed on Jul. 22, 2014, the content of which is incorporated herein by reference in its entirety.
| Number | Date | Country | |
|---|---|---|---|