Patent Application
20120260982
1. Field of the Invention
The present invention relates to a paste composition for an electrode, a photovoltaic cell element and a photovoltaic cell.
2. Background Art
Generally, electrodes are formed on a light-receiving surface and a back surface of a silicon photovoltaic cell. In order to efficiently extract electrical energy that has been converted in a photovoltaic cell from incident light, it is necessary that the electrodes have sufficiently low volume resistivity and form a favorable ohmic contact with a Si substrate. In particular, in the case of an electrode formed on a light-receiving surface, the width of wires tends to be reduced, and the aspect ratio of the electrode tends to be increased in order to suppress the loss in the amount of incidence of sunlight to a minimum.
An electrode for a light-receiving surface of a photovoltaic cell is typically produced by forming a p-type silicon layer by performing texture (asperity) formation on a light-receiving surface of a p-type silicon substrate, and thermally diffusing phosphorus etc. at high temperature; applying a conductive composition onto the p-type silicon layer by screen printing or the like; and sintering the same in the atmosphere at 800° C. to 900° C. The conductive composition for forming a light-receiving surface electrode contains a conductive metal powder, glass particles and various additives.
As the conductive metal powder, a silver powder is typically used. The reasons therefor include that silver particles have a low volume resistivity of 1.6×10−6 Ω·cm; that silver particles can be sintered via self-reduction under the aforementioned conditions; that silver particles can form a favorable ohmic contact with a silicon substrate; and that a solder material exhibits excellent wettability with respect to electrodes made of silver particles, whereby tab wires, that electrically connect photovoltaic cell elements with each other, are favorably attached during module formation in which photovoltaic cell elements are sealed with a glass substrate or the like.
As described above, a conductive composition containing silver particles exhibits favorable properties as an electrode for photovoltaic cells. Meanwhile, since silver is a noble metal and is expensive itself, and also in view of resource issues, proposals of a paste material to replace a silver-containing conductive composition have been desired. Copper, which is utilized as a semiconductor wiring material, is one of materials viewed as an alternative for silver. Copper is in abundant supply and is low in price, i.e., approximately a hundredth of that of silver. However, since copper is a material that easily oxidizes at a high temperature of 200° C. or higher in the atmosphere, it is difficult to form an electrode according to the processes described above.
In order to eliminate such a drawback of copper, for example, Japanese Patent Application Laid-Open (JP-A) Nos. 2005-314755 and 2004-217952 disclose copper particles that do not oxidize during high-temperature sintering, the copper particles being imparted with oxidation resistance through various techniques.
However, copper particles such as described above exhibit oxidation resistance at a temperature of up to 300° C., and are mostly oxidized at high temperatures of from 800° C. to 900° C. Therefore, the copper particles still have not been practically utilized in electrodes for photovoltaic cells. Further, there is a problem in that additives or the like, which are added to impart oxidation resistance to copper particles, disturb sintering of the copper particles during sintering and, as a result, electrodes with low resistance, such as those made of silver, cannot be obtained.
As another technique of suppressing oxidization of copper, there is a special process of sintering a conductive composition, in which copper is used as a conductive metal powder, in an atmosphere of nitrogen, etc.
However, this technique requires an environment that is sealed completely with an atmospheric gas such as described above, in order to thoroughly suppress oxidization of copper particles, which is not suitable for mass production of photovoltaic cell elements from a viewpoint of production costs.
Another problem to overcome in applying copper for electrodes for photovoltaic cells is ohmic contact properties of copper with respect to a silicon substrate. Namely, even if an electrode of copper can be formed without oxidation during high-temperature sintering, interdiffusion of copper and silicon may be caused as a result of direct contact of copper with a silicon substrate, and a reactant phase of copper and silicon (Cu3Si) may be formed at an interface of the electrode and the silicon substrate.
Formation of Cu3Si may occur within a region of several μm from the interface of the silicon substrate, which may cause cracking on the Si substrate side. Further, Cu3Si may penetrate through an n-type silicon layer that is formed previously on the silicon substrate, thereby deteriorating semiconductor performances (pn-junction properties) of the photovoltaic cell. In addition, the formed Cu3Si may lift up an electrode made of copper and inhibit adhesiveness of the electrode with respect to the silicon substrate, thereby reducing the mechanical strength of the electrode.
The present invention was made in view of the problems described above and aims to provide a paste composition for an electrode, which can suppress oxidization of copper during sintering, form an electrode with low resistivity, and form a copper-containing electrode in which formation of a reactant phase of copper and a silicon substrate is suppressed and that has a favorable ohmic contact. The present invention also aims to provide a photovoltaic cell element and a photovoltaic cell having an electrode formed with the paste composition for an electrode.
The inventors have made intensive studies in order to overcome the aforementioned problems and, as a result, completed the present invention. Specifically, the present invention encompasses the following aspects.
A first aspect of the present invention is a paste composition for an electrode containing phosphorus-containing copper alloy particles, tin-containing particles, glass particles, a solvent and a resin.
The paste composition for an electrode preferably has a phosphorus content in the phosphorus-containing copper alloy particles of from 6 mass % to 8 mass %.
The tin-containing particles preferably comprise at least one selected from tin particles or tin alloy particles with a tin content of 1 mass % or more.
The glass particles preferably have a glass softening point of 650° C. or less and a crystallization initiation temperature of more than 650° C.
In the paste composition for an electrode, the content of the tin-containing particles is preferably from 5 mass % to 70 mass %, with respect to the total content of the phosphorus-containing copper alloy particles and the tin-containing particles, which is defined as 100 mass %.
The paste composition for an electrode preferably further contains silver particles, and more preferably, the content of the silver particles is from 0.1 mass % to 10 mass % with respect to the total content of the phosphorus-containing copper alloy particles, the tin-containing particles and the silver particles, which is defined as 100 mass %.
In the paste composition for an electrode, the total content of the phosphorus-containing copper alloy particles, the tin-containing particles and the silver particles is preferably from 70 mass % to 94 mass %, the content of the glass particles is preferably from 0.1 mass % to 10 mass %, and the total content of the solvent and the resin is preferably from 3 mass % to 29.9 mass %.
A second aspect of the present invention is a photovoltaic cell element including an electrode formed on a silicon substrate, the electrode being formed by sintering the paste composition for an electrode which has been applied to the silicon substrate.
The electrode preferably contains a Cu—Sn alloy phase and a Sn—P—O glass phase, and more preferably, the Sn—P—O glass phase is positioned between the Cu—Sn alloy phase and the silicon substrate.
A third aspect of the present invention is a photovoltaic cell including the photovoltaic cell element, and a tab wire that is positioned on the electrode of the photovoltaic cell element.
According to the present invention, it is possible to provide a paste composition for an electrode, which can suppress oxidization of copper during sintering, form an electrode with low resistivity, and form a copper-containing electrode in which formation of a reactant phase between copper and the silicon substrate is suppressed and that has a favorable ohmic contact. It is also possible to provide a photovoltaic cell element, and a photovoltaic cell having an electrode formed from the paste composition for an electrode.
Exemplary embodiments of the present invention will be described in detail based on the following drawings, wherein:
In the present specification, the term “process” refers not only to an independent process but also to a process that cannot be clearly distinguished from another process, insofar as an intended result of the process can be attained. Further, a numerical range expressed by “A to B” refers to a range including A and B as the minimum value and the maximum value, respectively.
With regard to the amount of components of a composition, when plural substances corresponding to the same component exist in the composition, the amount of the component refers to the total amount of the plural substances, unless otherwise specified.
[Paste Composition for Electrode]
The paste composition for an electrode according to the present invention contains at least one kind of phosphorus-containing copper alloy particles, at least one kind of tin-containing particles, at least one kind of glass particles, at least one kind of a solvent, and at least one kind of a resin. By using a paste composition having a constitution as described above, oxidation of copper during sintering in the atmosphere can be suppressed and an electrode with low resistivity can be formed. Further, formation of a reactant phase of copper and a silicon substrate can be suppressed and a favorable ohmic contact between a formed electrode and the silicon substrate can be obtained.
(Phosphorus-Containing Copper Alloy Particles)
The paste composition for an electrode contains at least one kind of phosphorus-containing copper alloy particles. As a phosphorus-containing copper alloy, a brazing material referred to as a copper-phosphorus brazing alloy (phosphorus concentration: approximately 7 mass % or less) is known. Although a copper-phosphorus brazing alloy is used also as a jointing material of copper and copper, by using phosphorus-containing copper alloy particles in the paste composition for an electrode according to the present invention, an electrode that exhibits excellent oxidation resistance and a low volume resistivity can be formed, by means of a reducing property of phosphorus with respect to oxidized copper. Furthermore, effects of enabling sintering an electrode at low temperature, thereby reducing processing costs, can be achieved.
From the viewpoints of oxidation resistance and low resistivity, the content of phosphorus in the phosphorus-containing copper alloy according to the present invention is preferably from 6 mass % to 8 mass %, more preferably from 6.3 mass % to 7.8 mass % or less, and further preferably from 6.5 mass % to 7.5 mass % or less. If the phosphorus content in a phosphorus-containing copper alloy is 8 mass % or less, even lower resistivity can be attained, and efficiency in production of phosphorus-containing copper alloy particles can be favorable. Further, if the phosphorus content is 6 mass % or more, even more excellent oxidation resistance can be attained.
The phosphorus-containing copper alloy particles are an alloy containing copper and phosphorus, but may contain other atoms. Examples of other atoms include Ag, Mn, Sb, Si, K, Na, Li, Ba, Sr, Ca, Mg, Be, Zn, Pb, Cd, Tl, V, Sn, Al, Zr, W, Mo, Ti, Co, Ni and Au.
The content of other atoms in the phosphorus-containing copper alloy particles may be, for example, 3 mass % or less of the phosphorus-containing copper alloy particles, and is preferably 1 mass % or less from the viewpoints of oxidation resistance and low resistivity.
In the present invention, the phosphorus-containing copper alloy particles may be used singly or in a combination of two or more kinds.
Although the particle size of the phosphorus-containing copper alloy particles is not particularly restricted, the particle size at an accumulated weight of 50% (hereinafter, also abbreviated as “D50%”) is preferably from 0.4 μm to 10 μm, and more preferably from 1 μm to 7 μm. If the particle size is 0.4 μm or more, oxidation resistance can be improved more efficiently. If the particle size is 10 μm or less, the contact area between phosphorus-containing copper alloy particles, or the contact area between phosphorus-containing copper alloy particles and tin-containing particles as described later, in an electrode, can be increased, whereby resistivity can be lowered more efficiently. The particle size of phosphorus-containing copper alloy particles can be measured with a particle size distribution analyzer (MICROTRAC MT3300, trade name, manufactured by Nikkiso Co., Ltd.).
The shape of the phosphorus-containing copper alloy particles is not particularly restricted, and it may be any of quasispherical, flat, blocky, platy, scaly, etc. From the viewpoints of oxidation resistance and low resistivity, the phosphorus-containing copper alloy particles preferably have a quasispherical, flat or platy shape.
The content of the phosphorus-containing copper alloy particles in the paste composition for an electrode is not particularly restricted. From the viewpoint of low resistivity, the content in the paste composition for an electrode is preferably from 20 mass % to 85 mass %, more preferably from 25 mass % to 80 mass %, and further preferably from 30 mass % to 75 mass %.
Phosphorus-containing copper alloys can be produced by an ordinary method. Phosphorus-containing copper alloy particles can be produced from a phosphorus-containing copper alloy, in which the amount of phosphorus has been adjusted, by an ordinary method of preparing a metal powder, such as a water atomization method. Details of the water atomization method may be referred to descriptions in Kinzoku Binran (Metals Handbook, published by Maruzen Co., Ltd.), etc.
More specifically, desired phosphorus-containing copper alloy particles can be produced by melting a phosphorus-containing copper alloy and making the same into a powder by spraying from nozzles, and then drying and classifying the obtained powder. Further, phosphorus-containing alloy particles having a desired particle diameter can be obtained by appropriately selecting the conditions for classification.
(Tin-Containing Particles)
The paste composition for an electrode according to the present invention contains at least one kind of tin-containing particles. By containing tin-containing particles, in addition to phosphorus-containing copper alloy particles, an electrode with low resistivity can be formed in a sintering process described below.
It is considered, for example, that phosphorus-containing copper alloy particles and tin-containing particles react with each other in a sintering process, whereby an electrode composed of a Cu—Sn alloy phase and a Sn—P—O glass phase is formed. It is believed that the Cu—Sn alloy phase form a compact bulk in the electrode, which functions as a conductive layer, and an electrode with low resistivity is formed.
The compact bulk refers to a structure in which Cu—Sn alloy phases in massive form closely contact each other in a three-dimensional continuous manner.
Further, in the event an electrode is formed with the paste composition for an electrode according to the present invention on a substrate containing silicon (hereinafter also referred to “silicon substrate”), an electrode that exhibits high adhesion with respect to the silicon substrate can be formed, and a favorable ohmic contact between the electrode and the silicon substrate can be achieved.
It is considered, for example, that phosphorus-containing copper alloy particles and tin-containing particles react with each other in a sintering process, whereby an electrode composed of a Cu—Sn alloy phase and a Sn—P—O glass phase is formed. Since the Cu—Sn alloy phase is a compact bulk, the Sn—P—O glass phase is formed between the Cu—Sn alloy phase and the silicon substrate. As a result, it is believed that adhesion of the Cu—Sn alloy phase with respect to the silicon substrate is improved. Further, since the Sn—P—O glass phase functions as a barrier layer that inhibits interdiffusion of copper and silicon, it is believed that a favorable ohmic contact between an electrode formed by sintering and a silicon substrate can be achieved. More specifically, it is considered that a favorable ohmic contact can be obtained while suppressing formation of a reaction phase (Cu3Si), which is formed when an electrode containing copper is contacted directly with silicon and heated, and maintaining adhesion with respect to the silicon substrate without deteriorating the semiconductor performances (e.g. pn-junction properties).
Such effects are generally expressed in cases in which an electrode is formed on a substrate containing silicon with a paste composition for an electrode according to the present invention, and there is no particular restriction on the type of the substrate containing silicon. Examples of the substrate containing silicon include silicon substrates for photovoltaic cells and silicon substrates for other semiconductor devices than photovoltaic cells.
Specifically, according to the present invention, in which phosphorus-containing copper alloy particles and tin-containing particles are combined in the paste composition for an electrode, an electrode that exhibits a low volume resistivity and excellent oxidation resistance can be formed by utilizing the reducing property of phosphorous atoms with respect to oxidized copper in the phosphorus-containing copper alloy particles. Next, through reaction between the phosphorus-containing copper alloy particles and the tin-containing particles, a conductive layer composed of a Cu—Sn alloy phase, and an Sn—P—O glass phase, are formed while maintaining the low volume resistivity. It is thus considered, for example, that the two characteristic mechanisms can be attained during sintering by the Sn—P—O glass phase that functions as a barrier layer that prevents interdiffusion of copper and silicon, i.e., suppressed formation of a reactant phase between the electrode and the silicon substrate, and formation of a favorable ohmic contact with a copper electrode.
The tin-containing particles are not particularly restricted, insofar as that are particles containing tin. Among the tin-containing particles, at least one kind selected from tin particles or tin alloy particles is preferred, and at least one kind selected from tin particles or tin alloy particles in which the tin content is 1 mass % or more is more preferred.
There purity of tin in tin particles is not particularly restricted. For example, the purity of tin particles may be 95 mass % or more, preferably 97 mass % or more, and more preferably 99 mass % or more.
The type of the tin alloy particles is not particularly restricted, insofar as that are alloy particles containing tin. Among the tin alloy particles, from the viewpoints of the melting point and reactivity with phosphorus-containing copper alloy particles, tin alloy particles in which the tin content is 1 mass % or more are preferable, tin alloy particles in which the tin content is 3 mass % or more are more preferable, tin alloy particles in which the tin content is 5 mass % or more are further preferable, and tin alloy particles in which the tin content is 10 mass % or more are especially preferable.
Examples of the tin alloy particles include particles of an Sn—Ag alloy, an Sn—Cu alloy, an Sn—Ag—Cu alloy, an Sn—Ag—Sb alloy, an Sn—Ag—Sb—Zn alloy, an Sn—Ag—Cu—Zn alloy, an Sn—Ag—Cu—Sb alloy, an Sn—Ag—Bi alloy, an Sn—Bi alloy, an Sn—Ag—Cu—Bi alloy, an Sn—Ag—In—Bi alloy, an Sn—Sb alloy, an Sn—Bi—Cu alloy, an Sn—Bi—Cu—Zn alloy, an Sn—Bi—Zn alloy, an Sn—Bi—Sb—Zn alloy, an Sn—Zn alloy, an Sn—In alloy, an Sn—Zn—In alloy, and an Sn—Pb alloy.
Among the tin alloy particles, tin alloy particles of Sn-3.5Ag, Sn-0.7Cu, Sn-3.2Ag-0.5Cu, Sn-4Ag-0.5Cu, Sn-2.5Ag-0.8Cu-0.5Sb, Sn-2Ag-7.5Bi, Sn-3Ag-5Bi, Sn-58Bi, Sn-3.5Ag-3In-0.5Bi, Sn-3Bi-8Zn, Sn-9Zn, Sn-52In, Sn-40Pb, etc. have a melting point that is equal to or lower than that of Sn (232° C.). Consequently, these tin alloy particles are suitable because they melt at an early stage of sintering and cover the surfaces of phosphorus-containing copper alloy particles, thereby enabling uniform reaction with the phosphorus-containing copper alloy particles. The above expression of tin alloy particles refers to, in a case of Sn-AX-BY-CZ, that tin alloy particles contain A mass % of element X, B mass % of element Y, and C mass % of element Z.
In the present invention, tin-containing particles may be used singly or used in a combination of two or more kinds.
The tin-containing particles may further contain other atoms that may be unavoidably incorporated therein. Examples of the other atoms that are unavoidably incorporated include Ag, Mn, Sb, Si, K, Na, Li, Ba, Sr, Ca, Mg, Be, Zn, Pb, Cd, Tl, V, Al, Zr, W, Mo, Ti, Co, Ni, and Au.
The content of other atoms in the tin-containing particles may be, for example, 3 mass % or less of the tin-containing particles, and from the viewpoints of the melting point and reactivity with phosphorus-containing copper alloy particles, the content of other atoms is preferably 1 mass % or less.
Although the particle size of the tin-containing particles is not particularly restricted, the particle size at an accumulated weight of 50% (hereinafter, also abbreviated as “D50%”) is preferably from 0.5 μm to 20 μm, more preferably from 1 μm to 15 μm, and further preferably from 5 μm to 15 μm. If the particle size is 0.5 μm or more, oxidation resistance of tin-containing particles by themselves can be improved. If the particle size is 20 μm or less, the contact area with phosphorus-containing copper alloy particles, which exist in the electrode, can be increased, thereby allowing reaction with the phosphorus-containing copper alloy particles to progress effectively.
The shape of the tin-containing particles is not particularly restricted, and may be any of quasispherical, flat, blocky, platy, scaly, etc. From the viewpoints of oxidation resistance and low resistivity, the tin-containing particles preferably have a quasispherical, flat, or platy shape.
The content of the tin-containing particles in the paste composition for an electrode according to the present invention is not particularly limited. Among others, When the total content of the phosphorus-containing copper alloy particles and the tin-containing particles is defined as 100 mass %, the content of the tin-containing particles is preferably from 5 mass % to 70 mass %, more preferably from 7 mass % to 65 mass %, and further preferably from 9 mass % to 60 mass %.
If the content of the tin-containing particles is 5 mass % or more, more uniform reaction with the phosphorus-containing copper alloy particles can be caused. If the content of the tin-containing particles is 70 mass % or less, a sufficient volume of Cu—Sn alloy phase can be formed, and the volume resistivity of an electrode can be further lowered.
(Glass Particles)
The paste composition for an electrode according to the present invention contains at least one kind of glass particles. If the paste composition for an electrode contains glass particles, adhesion between an electrode portion and a substrate is improved during sintering. Further, especially in the formation of an electrode on a light-receiving surface side of a photovoltaic cell, a silicon nitride film, which is an antireflection coating, is removed by so called fire-through during sintering, and an ohmic contact between an electrode and a silicon substrate is obtained.
From the viewpoints of adhesion with respect to a substrate and reduction in resistivity, the glass particles preferably contain glass having a glass softening point of 650° C. or less and a crystallization initiation temperature of higher than 650° C. The glass softening point is measured by an ordinary method with a thermal mechanical analyzer (TMA), and the crystallization initiation temperature is measured by an ordinary method with a thermogravimetric-differential thermal analyzer (TG-DTA).
In the event that the paste composition for an electrode according to the present invention is used for an electrode formed on the light-receiving surface side of a photovoltaic cell, glass particles that are used commonly in the art can be used without particular restriction, as long as that can remove an antireflection coating by softening or melting at an electrode forming temperature, oxidizing the silicon nitride film to which the glass particles contact, and taking in the oxidized silicon dioxide.
Typically, glass particles to be contained in a paste composition for an electrode are composed of glass containing lead, since the material can efficiently take in silicon dioxide. Examples of glass containing lead include those described in Japanese Patent No. 3050064, which can be suitably used in the present invention.
Considering environmental impact, lead-free glass, which does not substantially contain lead, is preferably used in the present invention. Examples of the lead-free glass include those described in paragraphs No. [0024] to [0025] of Japanese Patent Application Laid-Open No. 2006-313744, and those described in Japanese Patent Application Laid-Open No. 2009-188281, and any one of such lead-free glass may be selected appropriately and used in the present invention.
If the paste composition for an electrode according to the present invention is used for an electrode other than that formed on a light-receiving surface side of a photovoltaic cell, for example, for a back-surface output electrode, or a through-hole electrode or a back-surface electrode for a back-contact type photovoltaic cell element, inclusion of a material that is necessary for fire through, such as lead, can be omitted by using glass particles containing glass having a glass softening point of 650° C. or less, and a crystallization initiation temperature of higher than 650° C.
Examples of the glass component of the glass particles to be used in the paste composition for an electrode according to the present invention include silicon dioxide (SiO2), phosphorus oxide (P2O5), aluminum oxide (Al2O3), boron oxide (B2O3), vanadium oxide (V2O5), potassium oxide (K2O), bismuth oxide (Bi2O3), sodium oxide (Na2O), lithium oxide (Li2O), barium oxide (BaO), strontium oxide (SrO), calcium oxide (CaO), magnesium oxide (MgO), beryllium oxide (BeO), zinc oxide (ZnO), lead oxide (PbO), cadmium oxide (CdO), tin oxide (SnO), zirconium oxide (ZrO2), tungsten oxide (WO3), molybdenum oxide (MoO3), lanthanum oxide (La2O3), niobium oxide (Nb2O5), tantalum oxide (Ta2O5), yttrium oxide (Y2O3), titanium oxide (TiO2), germanium oxide (GeO2), tellurium oxide (TeO2), lutetium oxide (Lu2O3), antimony oxide (Sb2O3), copper oxide (CuO), iron oxide (FeO), silver oxide (AgO) and manganese oxide (MnO).
Among these, at least one kind selected from the group consisting of SiO2, P2O5, Al2O3, B2O3, V2O5, Bi2O3, ZnO and PbO is preferably used as the glass component. Specific examples include those including, as a glass component, SiO2, PbO, B2O3, Bi2O3 and Al2O3. These glass particles can effectively lower the softening point. Further, since wettability with respect to phosphorus-containing copper alloy particles, or silver particles that are optionally included, can be improved, sintering among the particles in the sintering process is promoted and an electrode with even lower resistivity can be formed.
Meanwhile, from the viewpoint of low contact resistivity, glass particles containing phosphorus pentoxide (phosphate glass, P2O5 glass particles) are preferable, and glass particles containing vanadium pentoxide and phosphorus pentoxide (P2O5—V2O5 glass particles) are more preferable. By containing vanadium pentoxide, oxidation resistance is further improved and resistivity of an electrode is further lowered. This is considered to be because of reduction in the softening point of the glass as a result of further containing, for example, vanadium pentoxide. If glass particles containing phosphorus pentoxide and vanadium pentoxide (P2O5—V2O5 glass particles) are used, the content of vanadium pentoxide in the total mass of the glass is preferably 1 mass % or more, and more preferably from 1 mass % to 70 mass %.
Although the particle size of the glass particles used in the present invention is not particularly restricted, the particle size at an accumulated weight of 50% (D50%) is preferably from 0.5 μm to 10 μm, and more preferably from 0.8 μm to 8 μm or less. If the particle size is 0.5 μm or more, workability in producing the paste composition for an electrode can be improved. If the particle size is 10 μm or less, the particles can be dispersed homogeneously in the paste composition for an electrode. As a result, fire-through can be efficiently caused in a sintering process, and adhesion with respect to a silicon substrate can be improved.
The shape of the glass particles is not particularly restricted, and may be any of quasispherical, flat, blocky, platy, scaly, etc. From the viewpoints of oxidation resistance and low resistivity, the glass particles preferably have a quasispherical, flat, or platy shape.
The content of the glass particles in the total mass of the paste composition for an electrode is preferably from 0.1 mass % to 10 mass %, more preferably from 0.5 mass % to 8 mass %, and further preferably from 1 mass % to 8 mass %. If the content of the glass particles is within the range, oxidation resistance, reduction in resistivity of an electrode, and reduction in contact resistance can be attained more effectively, and reaction between the phosphorus-containing copper alloy particles and the tin-containing particles can be promoted.
(Solvent and Resin)
The paste composition for an electrode according to the present invention contains at least one kind of solvent and at least one kind of resin. By including a solvent and a resin, liquid properties (such as viscosity or surface tension) of the paste composition for an electrode according to the present invention can be adjusted to suitable liquid properties according to a method of applying the paste composition to a silicon substrate, etc.
The solvent is not particularly restricted, and examples thereof include a hydrocarbon solvent, such as hexane, cyclohexane, and toluene; a chlorinated hydrocarbon solvent, such as dichloroethylene, dichloroethane, and dichlorobenzene; a cyclic ether solvent, such as tetrahydrofuran, furan, tetrahydropyran, pyran, dioxane, 1,3-dioxolane, and trioxane; an amide solvent, such as N,N-dimethylformamide, and N,N-dimethylacetamide; a sulfoxide solvent, such as dimethylsulfoxide, and diethylsulfoxide; a ketone solvent, such as acetone, methyl ethyl ketone, diethylketone, and cyclohexanone; an alcohol compound, such as ethanol, 2-propanol, 1-butanol, and diacetone alcohol; a polyhydric alcohol ester solvent, such as 2,2,4-trimethyl-1,3-pentanediol monoacetate, 2,2,4-trimethyl-1,3-pentanediol monopropiolate, 2,2,4-trimethyl-1,3-pentanediol monobutyrate, 2,2,4-trimethyl-1,3-pentanediol monoisobutyrate, 2,2,4-triethyl-1,3-pentanediol monoacetate, ethylene glycol monobutyl ether acetate, and diethylene glycol monobutyl ether acetate; a polyhydric alcohol ether solvent, such as butyl cellosolve, diethylene glycol monobutyl ether, and diethylene glycol diethyl ether; a terpene solvent, such as α-terpinene, α-terpineol, myrcene, allo-ocimene, limonene, dipentene, α-pinene, β-pinene, terpineol, carvone, ocimene, and phellandrene, and mixtures of these solvents.
From the viewpoint of coating properties and printing properties of the paste composition for an electrode according to the present invention, when it is applied to a silicon substrate, the solvent is preferably at least one selected from a polyhydric alcohol ester solvent, a terpene solvent, and a polyhydric alcohol ether solvent, and at least one selected from a polyhydric alcohol ester solvent and a terpene solvent is more preferable.
According to the present invention, the solvents may be used singly or in a combination of two or more kinds.
A resin used commonly in the art can be used without particular restriction, insofar as it can be thermally decomposed during sintering. Specific examples of the resin include a cellulosic resin, such as methylcellulose, ethylcellulose, carboxymethylcellulose, and nitrocellulose; polyvinyl alcohols; polyvinylpyrrolidones; an acrylic resin; a vinyl acetate/acrylic ester copolymer; a butyral resin such as polyvinyl butyral; an alkyd resin, such as a phenol modified alkyd resin, and a castor oil fatty acid modified alkyd resin; an epoxy resin; a phenol resin; and a rosin ester resin.
From the viewpoint of a property of disappearance during sintering, at least one selected from a cellulosic resin or an acrylic resin is preferable as the resin used in the present invention.
In the present invention, the resin may be used singly or in a combination of two or more kinds.
The weight-average molecular weight of the resin according to the present invention is not particularly restricted. The weight-average molecular weight is preferably from 5,000 to 500,000, and more preferably from 10,000 to 300,000. If the weight-average molecular weight of the resin is 5,000 or more, increase in viscosity of the paste composition for an electrode can be suppressed. The increase in viscosity is considered to be, for example, caused by aggregation of particles due to insufficient steric repulsion when the resin is adsorbed to phosphorus-containing copper alloy particles and tin-containing particles. If the weight-average molecular weight of the resin is 500,000 or less, aggregation of the resin in a solvent is suppressed, and increase in viscosity of the paste composition for an electrode can be suppressed.
In addition, if the weight-average molecular weight of the resin is 500,000 or less, increase in a combustion temperature of the resin can be suppressed. As a result, when the paste composition for an electrode is subjected to sintering, remaining of the resin as a foreign material due to incomplete combustion can be suppressed, and an electrode having even lower resistivity can be obtained.
The contents of the solvent and the resin in the paste composition for an electrode according to the present invention can be selected appropriately, depending on the desired liquid properties and the type of the solvent and the resin. For example, the total content of the solvent and the resin in the total mass of the paste composition for an electrode is preferably from 3 mass % to 29.9 mass %, more preferably from 5 mass % to 25 mass %, and further preferably from 7 mass % to 20 mass %.
If the total content of the solvent and the resin is within the range, application suitability of the paste composition for an electrode to a silicon substrate may become favorable, and an electrode having a desired width and a height can be formed easier.
Further, in the paste composition for an electrode according to the present invention, from the viewpoints of oxidation resistance and low resistivity of an electrode, it is preferred that the total content of the phosphorus-containing copper alloy particles and the tin-containing particles is from 70 mass % to 94 mass %, the content of the glass particles is from 0.1 mass % to 10 mass %, and the total content of the solvent and the resin is from 3 mass % to 29.9 mass %; it is more preferred that the total content of the phosphorus-containing copper alloy particles and the tin-containing particles is from 74 mass % to 88 mass % or less, the content of the glass particles is from 0.5 mass % to 8 mass % or less, and the total content of the solvent and the resin is from 7 mass % to 20 mass % or less; and it is further preferred that the total content of the phosphorus-containing copper alloy particles and the tin-containing particles is from 74 mass % to 88 mass %, the content of the glass particles is from 1 mass % to 8 mass %, and the total content of the solvent and the resin is from 7 mass % to 20 mass %.
(Silver Particles)
The paste composition for an electrode according to the present invention preferably further includes silver particles. By including silver particles, oxidation resistance can be further improved and resistivity of an electrode can be further lowered. In addition, separation of Ag particles in an Sn—P—O glass phase, which is formed by reaction between the phosphorus-containing copper alloy particles and the tin-containing particles, further improves the ohmic contact between a Cu—Sn alloy phase in an electrode layer and a silicon substrate. Moreover, when a photovoltaic cell module is formed, an effect of improving the solder jointing property can be obtained.
The silver that constitutes the silver particles may further contain other atoms that may be unavoidably incorporated therein. Examples of the other atoms include Sb, Si, K, Na, Li, Ba, Sr, Ca, Mg, Be, Zn, Pb, Cd, Tl, V, Sn, Al, Zr, W, Mo, Ti, Co, Ni, and Au.
The content of the other atoms in the silver particles may be, for example, 3 mass % or less of the silver particles, and from the viewpoints of the melting point and reduction in resistivity of an electrode, the content of the other atoms is preferably 1 mass % or less.
Although the particle size of the silver particles used in the present invention is not particularly restricted, the particle size at an accumulated weight of 50% (D50%) is preferably from 0.4 μm to 10 μm, and more preferably from 1 μm to 7 μm. If the particle size is 0.4 μm or more, oxidation resistance is improved more effectively. If the particle size is 10 μm or less, the contact area between the silver particles and the phosphorus-containing copper alloy particles and the tin-containing particles, in an electrode, can be increased, and the resistivity can be lowered more effectively.
The shape of the silver particles is not particularly restricted, and may be any of quasispherical, flat, blocky, platy, scaly, etc. From the viewpoints of oxidation resistance and low resistivity, the silver particles preferably have a quasispherical, flat, or platy shape.
Further, in the event that the paste composition for an electrode according to the present invention contains silver particles, the content of the silver particles is preferably from 0.1 mass % to 10 mass %, more preferably from 0.5 mass % to 8 mass %, when the total content of the phosphorus-containing copper alloy particles, the tin-containing particles, and the silver particles, is defined as 100 mass %.
In the paste composition for an electrode according to the present invention, from the viewpoints of oxidation resistance, reduction in resistivity of an electrode, and application suitability to a silicon substrate, the total content of the phosphorus-containing copper alloy particles, the tin-containing particles and the silver particles in the paste composition for an electrode is preferably from 70 mass % to 94 mass %, and more preferably from 74 mass % to 88 mass %. If the total content of the phosphorus-containing copper alloy particles, the tin-containing particles and the silver particles is 70 mass % or more, a favorable viscosity for application of the paste composition for an electrode can be obtained easily. If the total content of the phosphorus-containing copper alloy particles, the tin-containing particles and the silver particles is 94 mass % or less, unevenness during application of the paste composition for an electrode can be more effectively suppressed.
If the paste composition for an electrode according to the present invention further contains silver particles, from the viewpoints of oxidation resistance and low resistivity of an electrode, it is preferred that the total content of the phosphorus-containing copper alloy particles, the tin-containing particles and the silver particles is from 70 mass % to 94 mass %, the content of the glass particles is from 0.1 mass % to 10 mass %, and the total content of the solvent and the resin is from 3 mass % to 29.9 mass %; it is more preferred that the total content of the phosphorus-containing copper alloy particles, the tin-containing particles and the silver particles is from 74 mass % to 88 mass % or less, the content of the glass particles is from 0.5 mass % to 8 mass %, and the total content of the solvent and the resin is from 7 mass % to 20 mass %; and it is further preferred that the total content of the phosphorus-containing copper alloy particles, the tin-containing particles and the silver particles is from 74 mass % to 88 mass %, the content of the glass particles is from 1 mass % to 8 mass %, and the total content of the solvent and the resin is from 7 mass % to 20 mass %.
(Flux)
The paste composition for an electrode may further include at least one kind of flux. By including a flux, an oxidized film, which is formed on surfaces of phosphorus-containing copper alloy particles, can be removed and a reducing reaction of phosphorus-containing copper alloy particles during sintering can be promoted. Further, melting of the tin-containing particles during sintering is also promoted, whereby reaction with the phosphorus-containing copper alloy particles is promoted. As a result, oxidation resistance can be further improved and resistivity of an electrode to be formed can be further lowered. Moreover, an effect of enhancing the adhesion between an electrode material and a silicon substrate can be obtained.
The flux used in the present invention is not particularly restricted, insofar as it is capable of removing an oxidized film formed on surfaces of phosphorus-containing copper alloy particles, and promoting melting of the tin-containing particles. Preferred examples of the flux include a fatty acid, a boric acid compound, a fluoride compound, and a fluoroborate compound.
More specifically, examples of the flux include lauric acid, myristic acid, palmitic acid, stearic acid, sorbic acid, stearolic acid, propionic acid, boron oxide, potassium borate, sodium borate, lithium borate, potassium fluoroborate, sodium fluoroborate, lithium fluoroborate, potassium bifluoride, sodium bifluoride, lithium bifluoride, potassium fluoride, sodium fluoride, and lithium fluoride.
Among them, from the viewpoints of heat resistance during a process of sintering an electrode material (i.e., a property of not volatilizing at a low temperature stage of sintering) and supplementary oxidation resistance for phosphorus-containing copper alloy particles, examples of the especially preferred flux include potassium borate and potassium fluoroborate.
According to the present invention, the flux may be used singly or in a combination of two or more kinds.
In the event that the paste composition for an electrode according to the present invention contains a flux, from the viewpoints of allowing the phosphorus-containing copper alloy particles to effectively exhibit oxidation resistance and promoting melting of the tin-containing particles, and also from the viewpoint of lowering the porosity at a portion at which the flux is removed after the completion of sintering an electrode material, the content of the flux in the total mass of the paste composition for an electrode is preferably from 0.1 mass % to 5 mass %, more preferably from 0.3 mass % to 4 mass %, further preferably from 0.5 mass % to 3.5 mass %, yet further preferably from 0.7 to 3 mass %, and particularly preferably from 1 mass % to 2.5 mass %.
(Other Components)
The paste composition for an electrode according to the present invention may include other components that are commonly used in the art, in addition to the components as described above, as necessary. Examples of the other components include a plasticizer, a dispersant, a surfactant, an inorganic binder, a metal oxide, a ceramic, and an organometallic compound.
The method for producing the paste composition for an electrode according to the present invention is not particularly restricted. For example, the paste composition for an electrode according to the present invention can be produced by dispersing/mixing phosphorus-containing copper alloy particles, tin-containing particles, glass particles, solvent and resin, and optionally silver particles, etc., with an ordinary dispersing/mixing method.
The dispersing/mixing method is not particularly restricted, and may be selected from ordinary dispersing/mixing methods.
(Method for Producing Electrode with Paste Composition for Electrode)
In the method for producing an electrode with the paste composition for an electrode according to the present invention, an electrode can be formed at a desired portion by applying the paste composition for an electrode to a portion at which an electrode is to be formed, and drying and sintering the paste composition for an electrode. By using the paste composition for an electrode, an electrode with low resistivity can be formed even if a sintering treatment is carried out in the presence of oxygen (e.g. in the atmosphere).
Specifically, for example, in the event that an electrode for a photovoltaic cell is formed with the paste composition for an electrode, the paste composition for an electrode is applied to a silicon substrate in a desired shape, dried and sintered, whereby an electrode for a photovoltaic cell with low resistivity can be formed in a desired shape. By using the paste composition for an electrode, an electrode with low resistivity can be formed even if a sintering treatment is carried out in the presence of oxygen (e.g. in the atmosphere). Further, when an electrode is formed on a silicon substrate, the electrode exhibits excellent adhesion with respect to the silicon substrate and a favorable ohmic contact can be attained.
Examples of the application method of the paste composition for an electrode include a screen printing method, an inkjet method and a dispenser method. From the viewpoint of productivity, a screen printing method is preferable.
If the paste composition for an electrode according to the present invention is applied by screen printing, the paste composition for an electrode preferably has a viscosity in a range of from 20 Pa·s to 1000 Pa·s. The viscosity of the paste composition for an electrode is measured with a Brookfield HBT viscometer at 25° C.
The application amount of the paste composition for an electrode can be selected appropriately, according to the size of an electrode to be formed. The application amount of the paste composition for an electrode may be, for example, from 2 g/m2 and 10 g/m2, and preferably from 4 g/m2 and 8 g/m2.
With regard to the conditions for heat treatment (sintering) for forming an electrode with the paste composition for an electrode according to the present invention, heat treatment conditions that are common in the art may be employed.
Although the heat treatment temperature (sintering temperature) is typically from 800° C. to 900° C., in the event where the paste composition for an electrode according to the present invention is used, heat treatment conditions at lower temperatures may be applied. For example, an electrode that exhibits favorable properties can be formed at a heat treatment temperature of from 450° C. to 850° C.
Further, the heat treatment time may be selected appropriately according to the heat treatment temperature, etc., and may be, for example, from 1 second to 20 seconds.
The heat treatment equipment may be appropriately selected from those that can heat up to a temperature within the range as described above, and examples thereof include an infrared heating oven and a tunnel oven. An infrared heating oven, in which electrical energy is input directly to a heated material in the form of electromagnetic waves and is converted to thermal energy, is high in efficiency and capable for performing rapid heating in a short time. Further, since no combustion product is generated and heating is carried out in a non-contact manner, contamination of an electrode to be formed can be prevented. A tunnel oven, in which sintering is carried out during conveying a sample in an automatic and continuous manner from an inlet to an outlet, is capable of carrying out heating uniformly by dividing the oven and controlling the conveying speed. From the viewpoint of photovoltaic performances of a photovoltaic cell element, a tunnel oven is suitable for carrying out the heat treatment.
[Photovoltaic Cell Element and Method for Producing the Same]
A photovoltaic cell element according to the present invention includes an electrode formed by sintering the paste composition for an electrode that has been applied onto a silicon substrate. As the result, a photovoltaic cell element that exhibits favorable characteristics can be obtained, and superior productivity of the photovoltaic cell element can be achieved.
In the present specification, the term “photovoltaic cell element” refers to an element including a silicon substrate having a pn-junction formed thereon, and an electrode formed on the silicon substrate. The term “photovoltaic cell” refers to an assembly that includes an electrode for a photovoltaic cell element having a tab wire provided thereon, which may be plural photovoltaic cell elements that are connected to each other via tab wires, and is sealed with a sealing resin or the like.
In the following, specific examples of the photovoltaic cell element according to the present invention will be described with reference to the drawings. However, the present invention is not limited thereto.
As outlined in
Next, a method for forming a light-receiving surface electrode 4 provided on the light-receiving surface side as outlined in
A light-receiving surface electrode 4 and a back-surface power output electrode 6 are formed with the paste composition for an electrode according to the present invention. The back-surface collecting electrode 5 is formed with an aluminum electrode paste composition containing a glass powder.
A first example of the method for forming a light-receiving surface electrode 4, a back-surface collecting electrode 5, and a back-surface power output electrode 6, includes applying the paste composition by screen printing, etc. to form desired patterns, respectively, drying the same, and sintering the same simultaneously in the atmosphere at approximately 450° C. to 850° C. According to the present invention, by using the paste composition for an electrode, an electrode that exhibits superior resistivity and contact resistivity can be formed even if sintering is carried out at a relatively low temperature.
At that time, on the light-receiving surface side, glass particles contained in the paste composition for an electrode, which forms a light-receiving surface electrode 4, and an antireflection layer 3 are allowed to react (also referred to as fire-through). As a result, the light-receiving surface electrode 4 and an n+ diffusion layer 2 are electrically connected (ohmic contact).
According to the present invention, since a light-receiving surface electrode 4 is formed with the paste composition for an electrode, oxidation of copper is suppressed even though copper is included as a conductive metal. Therefore, a light-receiving surface electrode 4 with low resistivity can be formed at a high yield.
In the present invention, the electrode is preferably formed by including a Cu—Sn alloy phase and an Sn—P—O glass phase, and more preferably, the Sn—P—O glass phase is positioned between the Cu—Sn alloy phase and a silicon substrate (not illustrated). In that way, reaction between copper and a silicon substrate is suppressed, and an electrode that exhibits low resistance and superior adhesion can be formed.
On the back surface side, aluminum, which is contained in an aluminum electrode paste composition that forms a back-surface collecting electrode 5, diffuses into the back surface of a p-type silicon substrate 1 during sintering, thereby forming a p+ diffusion layer 7. In that way, an ohmic contact is obtained between the p-type silicon substrate 1 and a back-surface collecting electrode 5, and a back-surface power output electrode 6.
A second example of the method for forming a light-receiving surface electrode 4, a back-surface collecting electrode 5, and a back-surface power output electrode 6, includes performing printing with an aluminum electrode paste composition forming a back-surface collecting electrode 5, drying the same, and then sintering the same in the atmosphere at approximately 750° C. to 850° C., thereby forming a back-surface collecting electrode 5; and subsequently performing printing with the paste composition for an electrode according to the present invention on each of the light-receiving surface side and the back surface side, drying the same, and then sintering the same in the atmosphere at approximately 450° C. to 650° C., thereby forming a light-receiving surface electrode 4 and a back surface power output electrode 6.
This method is effective from the viewpoints as set forth below. Specifically, if sintering of an aluminum electrode paste is performed to form a back-surface collecting electrode 5 at a temperature of 650° C. or less, there may be cases in which formation of a p+ diffusion layer is insufficient and due to insufficient sintering of aluminum particles and insufficient diffusion of aluminum into the p-type silicon substrate 1, depending on the composition of the aluminum paste.
In such cases, formation of an ohmic contact between the p-type silicon substrate 1 on the back surface and the back-surface collecting electrode 5, or the back-surface power output electrode 6, may be insufficient. As a result, photovoltaic performances of a photovoltaic cell element may be lowered. Consequently, it is preferable to form the back-surface collecting electrode 5 at a sintering temperature that is suitable for an aluminum electrode paste composition (e.g. 750° C. to 850° C.), and subsequently form the light-receiving surface electrode 4 and the back-surface power output electrode 6 by performing printing with the paste composition for an electrode according to the present invention, drying the same, and then sintering the same at a relatively low temperature (450° C. to 650° C.).
In a photovoltaic cell element having a structure shown in the perspective view of
Next, the through-holes formed in the above process are filled with the paste composition for an electrode according to the present invention by a printing method or an inkjet method. Further, printing is performed on the light-receiving surface side with the paste composition for an electrode according to the present invention into a grid form. A composition layer, which constitutes through-hole electrodes 9 and light-receiving surface collecting electrodes 8, is thus formed.
It is preferred to use a paste having an optimal composition for each process of filling and printing, such as viscosity. However, the filling and the printing may be carried out at once with a paste having the same composition.
On the back surface side, an n+ diffusion layer 2 and a p+ diffusion layer 7, which prevent recombination of carriers, are formed. The n+ diffusion layer 2, which is formed on the light-receiving surface side, portions surrounding the through holes and the back surface side, is formed so that it covers, in a continuous manner, from the light-receiving surface side to the portions surrounding the through holes, and from the portions surrounding the through holes to the back surface side. The n+ diffusion layer 2 may be formed on respective portions in different steps, or may be formed in the same step. Examples of impurity elements for forming the p+ diffusion layer 7 include boron (B) and aluminum (Al). The p+ diffusion layer 7 may be formed by, for example, exercising a thermal diffusion treatment with boron as a diffusion source during a production process of a photovoltaic cell element, prior to forming the antireflection coating 13. Alternatively, in a case in which aluminum is used, the p+ diffusion layer 7 may be formed by performing printing with an aluminum paste and sintering the same on the opposite surface side during the printing process.
On the back surface side, as shown in a plan view of
Followed by drying and sintering the paste composition in the atmosphere at approximately 450° C. to 850° C., light-receiving surface collecting electrodes 8, through-hole electrodes 9, and back surface electrodes 10 and 11 are formed. In a case in which an aluminum electrode is used for either one of back surface electrodes, as mentioned above, it is also possible to form one of the back surface electrodes by performing printing and sintering of an aluminum paste, and subsequently perform printing, filling and sintering of the paste composition for an electrode according to the present invention, thereby forming light-receiving surface collecting electrodes 8, through-hole electrodes 9, and the other one of back surface electrodes, from the viewpoints of sintering properties of aluminum and ohmic contact properties of the back surface electrodes and the p+ diffusion layer 7.
A photovoltaic cell element, having a structure shown as a perspective view of
A photovoltaic cell element, shown as a perspective view of
Applications of the paste composition for an electrode according to the present invention are not limited to photovoltaic cell electrodes as described above, and suitable examples thereof include electrode wiring and shield wiring for plasma displays, ceramic capacitors, antenna circuits, sensor circuits of various types, and heat radiating materials for semiconductor devices.
In particular, the paste composition for an electrode according to the invention can be favorably used for forming electrodes on a substrate containing silicon.
[Photovoltaic Cell]
A photovoltaic cell according to the present invention includes at least one of the photovoltaic cell element and a tab wire that is positioned on an electrode of the photovoltaic cell element. The photovoltaic cell may have a structure that includes plural photovoltaic cell elements that are connected to each other with tab wires, and is sealed with a sealing material.
The tab wire and the sealing material are not particularly restricted, and may be selected from any products that are common in the art.
The present invention will be described more specifically with reference to the examples. However, the present invention is not limited thereto. The expressions “part” and “%” are by mass, unless otherwise specified.
(a) Preparation of Paste Composition for Electrode
Phosphorus-containing copper alloy particles containing 7 mass % of phosphorus were prepared by an ordinary method, and were melted and powderized by a water atomization process. Then, the powder was dried and classified. The classified powder was blended, and subjected to deoxidation and dehydration treatments, thereby preparing phosphorus-containing copper alloy particles containing 7 mass % of phosphorus. The particle size (D50%) of the phosphorus-containing copper alloy particles was 5.0 μm, and the shape was quasispherical.
A glass (hereinafter, also referred to “G01”) composed of silicon dioxide (SiO2) (3 parts), lead oxide (PbO) (60 parts), boron oxide (B2O3) (18 parts), bismuth oxide (Bi2O3) (5 parts), aluminum oxide (Al2O3) (5 parts), and zinc oxide (ZnO) (9 parts) was prepared. The obtained G01 had a softening point of 420° C., and the crystallization temperature was above 650° C.
With the obtained G01, particles having a particle size (D50%) of 2.5 μm were produced. The shape of the particles was quasispherical.
The obtained phosphorus-containing copper alloy particles (39.9 parts), tin particles (Sn: particle size (D50%) of 10.0 μm; purity of 99.9%) (41.5 parts), G01 particles (4.1 parts), terpineol (Ter) (14.1 parts), and ethylcellulose (EC) (0.4 parts) were blended and milled in an agate mortar for 20 minutes, thereby preparing a paste composition for an electrode 1.
(b) Production of Photovoltaic Cell Element
A p-type semiconductor substrate having a thickness of 190 μm, in which an n+ diffusion layer and an antireflection coating (silicon nitride film) were formed on the textured light-receiving surface, was prepared. A specimen having the size of 125 mm×125 mm was obtained from the p-type semiconductor substrate. On the light-receiving surface, the paste composition for an electrode 1, obtained in the above process, was provided by a screen printing method to form an electrode pattern as shown in
Next, an electrode pattern as shown in
The pattern of the back-surface power output electrode, formed with the paste composition for an electrode 1, was constituted of two electrodes each having the size of 123 mm×5 mm. The printing conditions (screen mesh size, printing speed, and printing pressure) were adjusted appropriately so that the thickness of the back surface power output electrode after sintering was 20 μm. The aluminum electrode paste was provided by printing on the whole surface except for the back surface power output electrodes, thereby forming a back-surface collecting electrode pattern. The printing conditions for the aluminum electrode paste were adjusted appropriately so that the thickness of the back-surface collecting electrode after sintering was 30 μm. The specimen was placed in an oven heated to 150° C. for 15 minutes, and the solvent was allowed to evaporate.
Next, the p-type semiconductor substrate was subjected to a heat treatment (sintering) with a tunnel oven (single-line conveyer WB tunnel oven, manufactured by Noritake Co., Limited) in the atmosphere for a retention time of 10 seconds at a maximum sintering temperature of 800° C., thereby preparing a photovoltaic cell element 1 having a desired electrode formed thereon.
A photovoltaic cell element 2 was produced in a similar manner to Example 1, except that the sintering conditions for forming an electrode was changed from 10 seconds at a maximum temperature of 800° C. to 8 seconds at a maximum temperature of 850° C.
A photovoltaic cell element 3 was produced in a similar manner to Example 1, except that a paste composition for an electrode 3 was produced by changing the phosphorus content of the phosphorus-containing copper alloy particles from 7 mass % to 6 mass %.
A photovoltaic cell element 4 was produced in a similar manner to Example 3, except that the sintering conditions for forming an electrode was changed from 10 seconds at a maximum temperature of 800° C. to 12 seconds at a maximum temperature of 750° C.
A photovoltaic cell element 5 was produced in a similar manner to Example 1, except that a paste composition for an electrode 5 was produced by changing the phosphorus content of the phosphorus-containing copper alloy particles from 7 mass % to 8 mass %.
A photovoltaic cell element 6 was produced in a similar manner to Example 1, except that a paste composition for an electrode 6 was prepared by changing the particle size (D50%) of the phosphorus-containing copper alloy particles from 5.0 μm to 1.5 μm.
A photovoltaic cell element 7 was produced in a similar manner to Example 1, except that a paste composition for an electrode 7 was prepared by changing the contents of the phosphorus-containing copper alloy particles and the tin-containing particles to 56.3 parts and 25.1 parts, respectively.
A photovoltaic cell element 8 was produced in a similar manner to Example 1, except that a paste composition for an electrode 8 was prepared by changing the contents of the phosphorus-containing copper alloy particles and the tin-containing particles to 73.0 parts and 8.4 parts, respectively.
A photovoltaic cell element 9 was produced in a similar manner to Example 1, except that a paste composition for an electrode 9 was prepared by using tin alloy particles composed of Sn-58Bi (Sn alloy containing 58 mass % of Bi) instead of the tin-containing particles (Sn), and by changing the particle size (D50%) to 15.0 μm.
A photovoltaic cell element 10 was produced in a similar manner to Example 1, except that a paste composition for an electrode 10 was produced by using tin alloy particles composed of Sn-4Ag-0.5Cu (Sn alloy containing 4 mass % of Ag and 0.5 mass % of Cu) instead of the tin particles (Sn), and that the particle size (D50%) was 8.0 μm.
A photovoltaic cell element 11 was produced in a similar manner to Example 1, except that a paste composition for an electrode 11 was produced by changing the particle size (D50%) of the tin-containing particles from 10.0 μm to 6.0 μm.
A photovoltaic cell element 12 was produced in a similar manner to 1, except that a paste composition for an electrode 12 was prepared by adding silver particles (Ag; particle size (D50%) 3.0 μm; purity 99.5%). More specifically, the contents of the components were changed to 37.9 parts for the phosphorus-containing copper alloy particles, 39.5 parts for the tin particles, 4.0 parts for the silver particles, 4.1 parts for the G01 particles, 14.1 parts for terpineol, and 0.4 parts for ethyl cellulose.
A photovoltaic cell element 13 was produced in a similar manner to Example 1, except that a paste composition for an electrode 13 was prepared by adding silver particles (Ag; particle size (D50%) 3.0 μm). More specifically, the contents of the components were changed to 36.9 parts for the phosphorus-containing copper alloy particles, 38.4 parts for the tin particles, 6.1 parts for the silver particles, 4.1 parts for the G01 particles, 14.1 parts for terpineol, and 0.4 parts for ethyl cellulose.
A paste composition for an electrode 14 was produced in a similar manner to Example 1, except that the content of the G01 particles was changed. More specifically, the contents of the components were changed to 38.3 parts for the phosphorus-containing copper alloy particles, 39.9 parts for the tin particles, 7.8 parts for the G01 particles, 13.5 parts for terpineol, and 0.4 parts for ethyl cellulose.
A photovoltaic cell element 15 was produced in a similar manner to Example 1, except that a paste composition for an electrode 15 was produced by changing the composition of the glass particles from G01 to G02 as described below.
A glass G02 was prepared such that the content of vanadium oxide (V2O5) was 45 parts, phosphorus oxide (P2O5) was 24.2 parts, barium oxide (BaO) was 20.8 parts, antimony oxide (Sb2O3) was 5 parts, and tungsten oxide (WO3) was 5 parts. The softening point of the glass G02 was 492° C., and the crystallization initiation temperature was above 650° C.
With the obtained glass G02, G02 particles having a particle size (D50%) of 2.5 μm was prepared. The shape was quasispherical.
A photovoltaic cell element 16 was produced in a similar manner to Example 1, except that a paste composition for an electrode 16 was prepared changing the solvent from terpineol to diethylene glycol monobutyl ether (BC), and changing the resin from ethyl cellulose to poly(ethyl acrylate) (EPA).
More specifically, the contents of the components were changed to 39.9 parts for the phosphorus-containing copper alloy particles, 41.5 parts for the tin particles, 4.1 parts for the G01 particles, 12.3 parts for diethylene glycol monobutyl ether, and 2.2 parts for poly(ethyl acrylate).
Paste compositions for an electrode 17 to 20 were prepared in a similar manner to Example 1, respectively, by changing the phosphorus content, the particle size (D50%) and the content of the phosphorus-containing copper alloy particles; the composition, the particle size (D50%) and the content of the tin-containing particles; the content, the type and the content of the glass particles; the type and the content of the solvent; and the type and the content of the resin, to that as shown in Table 1.
With the obtained paste compositions for an electrode 17 to 20, photovoltaic cell elements 17 to 20, on which an intended electrode was formed, were produced in a similar manner to Example 1, respectively, except that the temperature and the treatment time for the heat treatment were changed to that as shown in Table 1.
A p-type semiconductor substrate having a thickness of 190 μm, in which an n+ diffusion layer and an antireflection coating (silicon nitride film) were formed on the textured light-receiving surface, was prepared. A specimen having the size of 125 mm×125 mm was cut out from the p-type semiconductor substrate. Thereafter, on the back surface of the p-type semiconductor substrate, a back-surface collecting electrode pattern was formed by printing with an aluminum electrode paste. The back-surface collecting pattern was formed on the entire region except for portions on which the back-surface power output electrode was formed, as shown in
Next, an electrode pattern as shown in
Next, the p-type semiconductor substrate was subjected to a heat treatment (sintering) with a tunnel oven (single-line conveyer WB tunnel oven, manufactured by Noritake Co., Limited) in the atmosphere for a retention time of 10 seconds at a maximum sintering temperature of 650° C., thereby preparing a photovoltaic cell element 1 having a desired electrode formed thereon.
A photovoltaic cell element 22 was produced in a similar manner to Example 21, except that the paste composition for an electrode 5 was used for forming the light-receiving surface electrode and the back-surface power output electrode.
A photovoltaic cell element 23 was produced in a similar manner to Example 21, except that the paste composition for an electrode 9 was used for forming the light-receiving surface electrode and the back-surface power output electrode, and that the sintering conditions for forming the electrodes were changed from 10 seconds at a maximum temperature of 650° C. to 10 seconds at a maximum temperature of 620° C.
A photovoltaic cell element 24 having a structure as shown in
Specifically, through-holes penetrating from the light-receiving surface side to the back surface side, and having a diameter of 100 μm, were formed in the p-type silicon substrate with a laser drill. Further, a texture, an n+ diffusion layer, and an antireflection coating were formed on the light-receiving surface side, in this order. The n+ diffusion layer was formed also on inner sides of the through holes and a portion of the back surface. Then, the through-holes were filled with the paste composition for an electrode 1 by an inkjet method, and a grid pattern was formed with the paste composition for an electrode 1 on the light-receiving surface side.
On the back surface side, a striped pattern shown in
During sintering, a p+ diffusion layer was formed by allowing aluminum to diffuse into the p-type silicon substrate, at a portion on which the aluminum electrode paste was formed.
A photovoltaic cell element 25 was produced in a similar manner to Example 24, except that the light-receiving surface collecting electrode, the through-hole electrode, and the back surface electrode were formed from the paste composition for an electrode 12.
A photovoltaic cell element 26 was produced in a similar manner to Example 24, except that the sintering condition for forming the electrode was changed from 10 seconds at a maximum temperature of 800° C. to 8 seconds at a maximum temperature of 850° C.
A photovoltaic cell element 27 was produced in a similar manner to Example 24, except that the light-receiving surface collecting electrode, the through-hole electrode, and the back surface electrode were formed with the paste composition for an electrode 9.
A paste composition for an electrode 28 was prepared in a similar manner to Example 1, except that the glass particles were changed from the G01 particles to G03 particles.
A glass G03 was prepared to have a composition in which silicon dioxide (SiO2) was 13 parts, boron oxide (B2O3) was 58 parts, zinc oxide (ZnO) was 38 parts, aluminum oxide (Al2O3) was 12 parts, and barium oxide (BaO) was 12 parts. The softening point of the obtained glass G03 was 583° C., and the crystallization initiation temperature was above 650° C.
With the obtained glass G03, G03 particles having a particle size (D50%) of 2.5 μm were obtained. The shape thereof was quasispherical.
Subsequently, a photovoltaic cell element 28, having a structure as shown in
A photovoltaic cell element 29 was produced in a similar manner to Example 28, except that the sintering conditions for forming an electrode was changed from 10 seconds at a maximum temperature of 800° C. to 8 seconds at a maximum temperature of 850° C.
With the paste composition for an electrode 28, a photovoltaic cell element 30, having a structure as shown in
A paste composition for an electrode 31 was prepared in a similar manner to Example 5, except that the glass particles were changed from the G01 particles to the G03 particles. With the paste composition for an electrode 31, same a photovoltaic cell element 31 having the structure shown in
A paste composition 32 for an electrode was prepared in a similar manner to Example 12, except that the glass particles were changed from the glass G01 particles in Example 12 to the glass G03 particles. A photovoltaic cell element 32 having a structure shown in
A paste composition for an electrode C1 was prepared in a similar manner to Example 1, except that the components were changed so that the phosphorus-containing copper alloy particles and the tin-containing particles were not used, as shown in Table 1.
A photovoltaic cell element C1 was produced in a similar manner to Example 1, except that the paste composition for an electrode C1.
Paste compositions for an electrode C2 to C4, in which phosphorus-containing copper alloy particles having different phosphorus contents were used and tin-containing particles were not used, were prepared.
Photovoltaic cell elements C2 to C4 were produced in a similar manner to Comparative Example 1, except that the paste compositions for an electrode C2 to C4, respectively.
A paste composition for an electrode C5 was prepared in a similar manner to Example 1, except that copper particles (purity: 99.5%, particle size (D50%): 5.0 μm, content: 39.9 parts) were used instead of the phosphorus-containing copper alloy particles, and that the contents of the components were changed, as shown in Table 1.
A photovoltaic cell element C5 was produced in a similar manner to Comparative Example 1, except that the paste composition for an electrode C5 was used.
A photovoltaic cell element C6 was produced in a similar manner to Example 24, except that the light-receiving surface collecting electrode, the through-hole electrodes, and the back surface electrodes were formed with the paste composition for an electrode C1.
A photovoltaic cell element C7 was produced in a similar manner to Example 28, except that the paste composition for an electrode 28 was changed to the paste composition for an electrode C1.
A photovoltaic cell element C8 was produced in a similar manner to Example 30, except that the paste composition for an electrode 28 was changed to the paste composition for an electrode C1.
[Evaluation]
Evaluation of the photovoltaic cell elements was carried out with a combination of artificial sunlight (WXS-155S-10, trade name, manufactured by Wacom Electric Co., Ltd.) and a current-voltage (I-V) analyzer (I-V CURVE TRACER MP-160, trade name, manufactured by EKO Instruments Co., Ltd.).
Jsc (short circuit current), Voc (open-circuit voltage), FF (fill factor), and Eff (conversion efficiency), which indicate photovoltaic performances of a photovoltaic cell, were obtained by measurements according to JIS-C-8912, JIS-C-8913 and JIS-C-8914. The measured values of photovoltaic cell elements with a double-surface electrode structure were reduced to relative values, based on the measure values for Comparative Example 1 (photovoltaic cell element C1) that are defined as 100.0. The results are shown in Table 2. In Comparative Example 2, evaluation was not possible to carry out due to increased resistivity of the electrode caused by oxidation of copper particles.
Further, a cross-section of the light-receiving surface electrodes, formed by sintering the paste composition for an electrode, was observed with a scanning electron microscope (MINISCOPE TM-1000, trade name, manufactured by Hitachi, Ltd.) with an acceleration voltage of 15 kV, and the existence or nonexistence of a Cu—Sn alloy phase and an Sn—P—O glass phase in the electrode, and the location of the Sn—P—O glass phase. The results are shown in Table 2.
As is seen from Table 2, the photovoltaic performances observed in Comparative Examples 3 to 5 were inferior to that of Comparative Example 1.
This is considered, for example, that Comparative Example 4, not including tin-containing particles, caused interdiffusion of a silicon substrate and copper during sintering, thereby deteriorating the pn-junction characteristic in the substrate. It is also considered that Comparative Example 5, in which phosphorus-containing copper alloy particles were not used and pure copper (phosphorus content: 0 mass %) was used, caused oxidation of copper particles prior to reacting with tin-containing particles during sintering, whereby a Cu—Sn alloy phase was not formed and resistance of the electrode was increased.
On the other hand, the photovoltaic performances of the photovoltaic cell elements of Examples 1 to 23 were substantially equal to that of Comparative Example 1. In particular, the photovoltaic cell elements 21 to 23, although the paste compositions for an electrode were sintered at a relatively low temperature (620 to 650° C.), exhibited high photovoltaic performances. Further, it was observed that a Cu—Sn alloy phase and an Sn—P—O glass phase were present in the light-receiving surface electrodes, and that the Sn—P—O glass phase was formed between the Cu—Sn alloy phase and the silicon substrate.
The measured value of the back-contact type photovoltaic cell elements having the structure of
As is seen from the results shown in Table 3, the photovoltaic performances of the photovoltaic cell elements of Examples 24 to 27 were substantially equal to that of Comparative Example 6. Further, it was observed that a Cu—Sn alloy phase and an Sn—P—O glass phase were present in the light-receiving surface electrodes, and that the Sn—P—O glass phase was formed between the Cu—Sn alloy phase and the silicon substrate.
The measured value of the back-contact type photovoltaic cell elements having the structure of
As is seen from the results shown in Table 4, the photovoltaic performances of the photovoltaic cell elements of Examples 28 to 29 were substantially equal to that of the photovoltaic cell element according to Comparative Example 7. Further, it was observed that a Cu—Sn alloy phase and an Sn—P—O glass phase were present in the back side electrodes formed by sintering the paste composition for an electrode, and that the Sn—P—O glass phase was formed between the Cu—Sn alloy phase and the silicon substrate.
The measured value of the back-contact type photovoltaic cell elements having the structure of
As is seen from the results shown in Table 5, the photovoltaic performances of the photovoltaic cell elements of Examples 30 to 32 were substantially equal to that of the photovoltaic cell element according to Comparative Example 8. Further, it was observed that a Cu—Sn alloy phase and an Sn—P—O glass phase were present in the back side electrodes formed by sintering the paste composition for an electrode, and that the Sn—P—O glass phase was formed between the Cu—Sn alloy phase and the silicon substrate.
The disclosure of Japanese Patent Application No. 2011-090519 is herein incorporated by reference by reference. All publications, patent applications, and technical standards mentioned in this specification are herein incorporated by reference to the same extent as if each individual publication, patent application, or technical standard was specifically and individually indicated to be incorporated by reference.
This application claims priority under 35 USC 119(e) from U.S. Provisional Application No. 61/475,435, the disclosure of which is incorporated by reference herein.
| Number | Date | Country | |
|---|---|---|---|
| 61475435 | Apr 2011 | US |